DE19749085A1 - Soil substrate with low mobility of harmful substances from clarified sludge and thermally activated clay - Google Patents

Soil substrate with low mobility of harmful substances from clarified sludge and thermally activated clay

Info

Publication number
DE19749085A1
DE19749085A1 DE19749085A DE19749085A DE19749085A1 DE 19749085 A1 DE19749085 A1 DE 19749085A1 DE 19749085 A DE19749085 A DE 19749085A DE 19749085 A DE19749085 A DE 19749085A DE 19749085 A1 DE19749085 A1 DE 19749085A1
Authority
DE
Germany
Prior art keywords
clay
activated clay
sewage sludge
substrate
thermally activated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19749085A
Other languages
German (de)
Inventor
Marc Hohmann
Hans Hohmann
Christian Kaps
Fred Rotter
Bernhard Sourell
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZIEGELWERK NORDHAUSEN DIPL ING
Original Assignee
ZIEGELWERK NORDHAUSEN DIPL ING
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZIEGELWERK NORDHAUSEN DIPL ING filed Critical ZIEGELWERK NORDHAUSEN DIPL ING
Priority to DE19749085A priority Critical patent/DE19749085A1/en
Publication of DE19749085A1 publication Critical patent/DE19749085A1/en
Withdrawn legal-status Critical Current

Abstract

Harmful substances are immobilized in a sludge-based soil substrate by the incorporation of thermally activated clay. A soil substrate with a low mobility of harmful substances and a high biologically available nutrient content comprises clarified sludge and thermally activated clay, which have been sedimented together with water.

Description

Es ist bekannt, Klärschlamm zum Zwecke seiner besseren Verwertung in der Landwirtschaft mit Ton zu mischen.It is known sewage sludge for the purpose of its better recovery in the Mix agriculture with clay.

In der Patentschrift DE 195 15 488 C1 ist beispielsweise ein Verfahren zum Verarbeiten von Klärschlamm angegeben, bei dem zum Abtöten von im Klärschlamm enthaltenen Bakterien ein körniger und erhitzter Ton zum kurzfristigen Erhitzen der Mischung eines teilentwässerten Klärschlammes mit einem mineralischen Rohstoff zugegeben wird. Dabei soll dieser erhitzte Ton durch Brennen zumindest teilweise sein Kristallwasser verloren haben und aus einen Schrühbrand stammen, das heißt einem Brand bei 500 bis 700°C in oxidierender Brennatmosphäre. Nachteilig dabei ist, daß die Schwermetalladsorbtionsfähigkeit reversibel bleibt und es auch wegen Fehlen der flüssigen Phase keine irreversible Einbindung gibt.In the patent DE 195 15 488 C1, for example, a method for Processing of sewage sludge stated in which to kill in the Sludge contained a grainy and heated clay to bacteria short-term heating of the mixture of a partially dewatered sewage sludge is added to a mineral raw material. This should be this heated tone by burning at least partially have lost its water of crystallization and come from a biscuit brand, that is a fire at 500 to 700 ° C. in an oxidizing firing atmosphere. The disadvantage here is that the Heavy metal adsorption capacity remains reversible and it also because of Absence of the liquid phase gives no irreversible involvement.

In der DE 44 19 280 C1 wird ein Verfahren zum Verarbeiten von Klärschlamm beschrieben bei dem einem teilentwässerten Klärschlamm eine Teilmenge eines zumindest teilweise kalzinierten Tones zugegeben wird. Dabei wird als vorteilhaft angesehen, daß die Tonmineralien durch Brennen zumindest teilweise ihr Kristallwasser verloren haben und daß solche zumindest graduell kalzinierten Tone auf Grund noch vorhandener Reaktionsflächen eine Schwermetall - Adsorptionsfähigkeit besitzen. Der Nachteil dieses Verfahrens ist jedoch, daß die adsorbierten Schwermetalle auch wieder desorbiert werden können, es kommt also zu keiner echten Einbindung. In DE 44 19 280 C1 discloses a method for processing Sewage sludge described in the case of a partially dewatered sewage sludge a subset of at least partially calcined clay added becomes. It is considered advantageous that the clay minerals Burn at least partially have lost their water of crystallization and that such at least gradually calcined clays due to still existing Reaction surfaces have a heavy metal - adsorption capacity. The Disadvantage of this method, however, is that the adsorbed heavy metals can be desorbed again, so it comes to no real Integration.  

Die Patentschrift DE 44 15 163 C1 schützt ein Verfahren zum Verarbeiten von Klärschlamm, daß dadurch gekennzeichnet ist, daß dem Klärschlamm kalzinierte oder getemperte Tonmineralien oder Scherben eines keramischen Altmaterials zugemischt werden, wobei der Klärschlamm selbst teilentwässert sein soll. Das erfindungsgemäße Gemenge ist nicht nur hygenisiert, sondern besitzt auch ein reduziertes Gefahrenpotential aufgrund von Adsorption der Schwermetalle durch die Tonminerale. Nachteilig ist auch hier die nur vorübergehende Einbindung der Schwermetalle.The patent DE 44 15 163 C1 protects a method for processing sewage sludge, characterized in that the sewage sludge Calcined or tempered clay minerals or shards of a be mixed with old ceramic material, the sewage sludge itself should be partially dehydrated. The mixture according to the invention is not only Hygenized, but also has a reduced risk potential due to adsorption of the heavy metals by the clay minerals. The disadvantage here is the only temporary integration of Heavy metals.

Der in den Patentansprüchen 1 bis 9 angegebenen Erfindung liegt das Problem zugrunde, die reversible Einbindung der Schwermetalle des Klärschlammes in den Ton irreversibel zu machen und dabei gleichzeitig die Eigenschaften gebrannten Tones zur Konditionierung und Hygenisierung von Klärschlamm zu nutzen. Dieses Problem wird durch die Zugabe von Ton aus alkali- und erdalkalireichen Ziegeltonen, der bei Brenntemperaturen von 550°C-750°C unter reduzierender und wasserdampfangereicherter Brennatmosphäre thermisch aktiviert wurde, und Wasser zum Klärschlamm gelöst.The invention specified in the claims 1 to 9 is the Problem underlying the reversible involvement of the heavy metals of Make sewage sludge irreversible in the clay and at the same time the Properties of fired clay for conditioning and hygenization to use sewage sludge. This problem is caused by the addition of clay from alkali and alkaline earthy brick zones, at firing temperatures from 550 ° C to 750 ° C under reducing and water vapor enriched Combustion atmosphere was thermally activated, and water to sewage sludge solved.

Die mit der Erfindung erzielten Vorteile bestehen insbesondere darin, daß über die Lösungsphase die Schwermetalle, insbesondere Cadmium, statt adsorptiv, d. h. leicht auswaschbar, chemisch und damit stabil gebunden werden und die übrigen Tonbestandteile hygenisierend und nährstoffanreichernd für die Ausbildung eines naturnahen Bodensubstrats wirken.The advantages achieved by the invention are in particular that the heavy metals, in particular cadmium, take place via the solution phase adsorptive, d. H. easily washed out, chemically and thus stably bound and the other constituents of sound are hygenic and Nutrientanreichernd for the formation of a near-natural soil substrate Act.

Ein Ausführungsbeispiel wird im folgenden näher beschrieben:An embodiment will be described in more detail below:

Zur Herstellung eines erfindungsgemäßen Substrates wird kommunaler Klärschlamm mit thermisch aktiviertem Ziegelton versetzt. Der Ziegelton hat die in der folgenden Tabelle angegebene, beispielhafte chemische Zusammensetzung (in Masse-%).To produce a substrate according to the invention becomes municipal Sludge mixed with thermally activated brick clay. The brick sound has the exemplary chemical given in the following table Composition (in% by mass).

Chemische AnalyseChemical Analysis

Elementeelements Masse-%Dimensions-% Na2ONa 2 O 0,30.3 K2OK 2 O 3,73.7 CaOCaO 1,81.8 MgOMgO 3,23.2 SiO2 SiO 2 62,362.3 Al2O3 Al 2 O 3 16,416.4 Fe2O3 Fe 2 O 3 5,25.2 Mn2O3 Mn 2 O 3 0,0830.083 Cr2O3 Cr 2 O 3 0,0170,017 TiO2 TiO 2 0,8440.844 P2O5 P 2 O 5 0,1690.169 SO3 SO 3 0,0150,015

Der Glühverlust dieser beispielhaften Rohtonmischung beträgt ca. 6,2 Masse-%.The loss on ignition of this exemplary raw clay mixture is about 6.2% by weight.

Aus diesem oben beispielhaft aufgeführtem alkali- und erdalkalihaltigen Ziegelton werden üblicherweise bei Temperaturen um 1000°C Ziegelsteine gebrannt. Dieser Brennvorgang erfolgt im allgemeinen, in einem Tunnel­ ofen, unter einer sauerstoffhaltigen Atmosphäre.For this example listed above alkali and alkaline earth metal Brick clay usually becomes bricks at temperatures around 1000 ° C burned. This burning process is generally carried out in a tunnel furnace, under an oxygen-containing atmosphere.

Davon abweichend, wird erfindungsgemäß der Ton nur bei einer Temperatur von 650-750°C gebrannt. Das Herstellen von Aktivton erfolgt aus dem oben charakterisierten Rohstoff im gleichen Tunnelofen wie die Ziegelsteinherstellung aber unter Sauerstoffausschluß. Deviating from this, according to the invention, the sound only at one Temperature of 650-750 ° C burned. The production of active sound takes place from the raw material characterized above in the same tunnel kiln as the Brick production but under exclusion of oxygen.  

Dies wird erreicht durch ein kompaktes Setzen der Ziegelrohlinge und/oder Abdecken der Setzstapel, wodurch ein Brennen in den eigenen Entgasungsprodukten, - das heißt in einer wasserdampfhaltigen, CO2- angereicherten, und zumindest teilweise sauerstofffreien Atmosphäre erfolgt. Der Wasserdampf entstammt der Entwässerung der Tonmineralien und das Kohlendioxid der Entsäuerung der Erdalkalikarbonate.This is achieved by a compact setting of the brick blanks and / or covering the setting stacks, whereby a burning in the own degassing, that is carried out in a water vapor-containing, CO 2 - enriched, and at least partially oxygen-free atmosphere. The water vapor originates from the drainage of the clay minerals and the carbon dioxide from the deacidification of the alkaline earth carbonates.

Der so erhaltene aktive Ton enthält umgewandelte Tonminerale und neue Mineralphasen mit aktiven Zentren und teilweise verfügbares Kalium und gebrannten Kalk und Magnesit.The active clay thus obtained contains converted clay minerals and new ones Mineral phases with active centers and partially available potassium and burnt lime and magnesite.

Der Aktivton ist somit in der Lage Schwermetalle irreversibel einzubinden, hygienisierend zu wirken und den in der Regel vorhandenen Kalimangel auszugleichen.The active clay is thus capable of irreversibly incorporating heavy metals, to be sanitizing and the existing Kalimangel usually compensate.

Dieser so gebrannte Ziegelton wird anschließend auf eine Mahlfeinheit von 0,2 bis 0,09 mm aufgemahlen.This fired brick clay is then reduced to a fineness of 0.2 to 0.09 mm ground.

Das so erhaltene Aktivton-Pulver wird dem für die Substratherstellung vorgesehenen Klärschlamm mit einem Masseanteil von 25% (bezogen auf die Trockensubstanz des Klärschlammes) zugegeben. Die Zugabe erfolgt im Klärwerk nach der biologischen Behandlung d. h. nach der Stabilisierung des Klärschlammes. Der stabillisierte Klärschlamm wird in einen externen Behälter/Becken mit einem Rührwerk überführt, mit dem Aktivtonpulver versetzt und zur Reaktion gebracht. Danach kann in üblicher Weise entwässert, gelagert und ausgebracht werden.The thus obtained active clay powder becomes that for substrate production provided sewage sludge with a mass fraction of 25% (based on the dry substance of the sewage sludge) was added. The addition takes place in Wastewater treatment plant after biological treatment d. H. after stabilization of sewage sludge. The stabilized sewage sludge is in an external Transfer container / bowl with a stirrer, with the active clay powder staggered and reacted. After that, in the usual way drained, stored and deployed.

Claims (9)

1. Bodensubstrat mit geringer Schadstoffmobilität und hohem Nährstoffgehalt das biologisch aktivierbar ist, dadurch gekennzeichnet, daß das Substrat aus üblichen, Klärschlammen und thermisch aktiviertem Ton besteht, beide Bestandteile zusammen mit Wasser gelagert worden sind und daß die Immobilisierung von Schwermetallen größenordnungsgemäß über derjenigen eines Bodensubstrates gleicher Mischung aus nicht oder nicht erfindungsgemäß aktiviertem Ton liegt.1. soil substrate with low pollutant mobility and high nutrient content is biologically activated, characterized in that the substrate consists of conventional sewage sludge and thermally activated clay, both components have been stored together with water and that the immobilization of heavy metals of the order of magnitude above that of a soil substrate same Mixture of not or not inventively activated clay is. 2. Bodensubstrat nach Anspruch 1, dadurch gekennzeichnet, daß ein Substrat infolge der Zugabe von thermisch aktiviertem Ton zu üblichen Klärschlämmen entsteht, welches zur Sicherung der Forderungen der Trinkwasserverordnung insbesondere bezüglich Cadmium geeignet ist.2. soil substrate according to claim 1, characterized in that a substrate due to the addition of thermally activated clay to usual Sewage sludge is produced, which is used to secure the requirements of Drinking Water Ordinance is particularly suitable with respect to cadmium. 3. Verfahren zur Herstellung eines Bodensubstrates nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, daß einem Klärschlamm 5-50 Masse-% (bezogen auf seine Trockenmasse) eines thermisch aktivierten Tones besonderer Feinheit unter Wasserzugabe zugemischt wird, wobei der aktivierte Ton infolge seiner chemischen Zusammensetzung und/oder seiner Vorbehandlung die Schwermetalle des Klärschlammes im Temperaturbereich vorzugsweise von 20 bis 60°C aus wäßrigen Klärschlamm-Ton-Suspensionen irreversibel bindet. 3. A method for producing a soil substrate according to one of previous claims, characterized in that a Sewage sludge 5-50 mass% (based on its dry matter) of a thermally activated clay of special fineness with addition of water mixed with the activated clay due to its chemical Composition and / or its pretreatment the heavy metals of the Sewage sludge in the temperature range preferably from 20 to 60 ° C from aqueous sewage sludge clay suspensions irreversibly binds.   4. Verfahren nach Anspruch 3, dadurch gekennzeichnet, daß der aktivierte Ton aus alkali- und erdalkalireichen Ziegeltonen vorzugsweise bei Brenn­ temperaturen von 550-750°C unter reduzierender und in besonderer Weise wasserdampfangereicherter Brennatmosphäre vorzugsweise so hergestellt wird, daß das kompakt gesetzte Brenngut in seinen eigenen Entgasungsprodukten und unter Beibehaltung eines Temperaturgradienten von 100-200 Grad über der Brenngutmasse garbrennt.4. The method according to claim 3, characterized in that the activated Clay from alkali and alkaline earth-rich Ziegeltonen preferably at Brenn Temperatures of 550-750 ° C under reducing and in particular Way steam-enriched combustion atmosphere preferably so is made that the compact set firing in his own Degassing and while maintaining a temperature gradient from 100-200 degrees above the firing mass. 5. Verfahren nach Anspruch 3 und 4 dadurch gekennzeichnet, daß dem Substrat gezielt Nährstoffe, insbesondere Kalium und Magnesium durch den aktivierten Ton zugeführt werden.5. The method according to claim 3 and 4, characterized in that the Substrate targeted nutrients, especially potassium and magnesium by the be activated sound. 6. Verfahren nach Anspruch 3 bis 5, dadurch gekennzeichnet, daß durch Aufmahlen des aktivierten Tones auf eine vorzugsweise Korngröße von 0,2 bis 0,09 mm dieser als Konditionierungsmittel für Klärschlamm wirkt.6. The method according to claim 3 to 5, characterized in that Milling the activated clay to a preferred grain size of 0.2 to 0.09 mm this acts as a conditioning agent for sewage sludge. 7. Verfahren nach Anspruch 3 bis 6 dadurch gekennzeichnet, daß durch die thermische Behandlung des Tones bei Temperaturen unterhalb des üblichen keramischen Garbrandes und durch seiner Reaktionen mit Klärschlamm im Wasser infolge natürlicher Sukzession ein biologisch aktives Substrat entsteht.7. The method according to claim 3 to 6, characterized in that Thermal treatment of the clay at temperatures below the usual ceramic Garbrandes and by its reactions with Sewage sludge in the water due to natural succession a biologically active Substrate is formed. 8. Verfahren nach Anspruch 3 dadurch gekennzeichnet, daß der aktivierte Ton aus feinstgemahlenem Ziegelbruch, der die Eigenschaften des Tones nach Anspruch 4 aufweist, hergestellt wird.8. The method according to claim 3, characterized in that the activated Clay of finely ground brick breaking, the characteristics of the clay according to claim 4, is produced. 9. Verfahren nach Anspruch 3 bis 8 dadurch gekennzeichnet, daß dem Substrat zusätzlich zum aktivierten Ton geringe Mengen Rohton zugemischt werden.9. The method according to claim 3 to 8, characterized in that the Substrate mixed in addition to the activated clay small amounts of raw clay become.
DE19749085A 1997-10-02 1997-10-02 Soil substrate with low mobility of harmful substances from clarified sludge and thermally activated clay Withdrawn DE19749085A1 (en)