DE1965151A1 - Moisture-proof layers for building purposes - Google Patents
Moisture-proof layers for building purposesInfo
- Publication number
- DE1965151A1 DE1965151A1 DE19691965151 DE1965151A DE1965151A1 DE 1965151 A1 DE1965151 A1 DE 1965151A1 DE 19691965151 DE19691965151 DE 19691965151 DE 1965151 A DE1965151 A DE 1965151A DE 1965151 A1 DE1965151 A1 DE 1965151A1
- Authority
- DE
- Germany
- Prior art keywords
- building
- recesses
- furrows
- thermoplastic
- friction surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
ng. Walter Meissner Dipi.-ing. Herbert Tischerng. Walter Meissner Dipi.-ing. Herbert Tischer
1 BERLIN 33, Herbertstraße 22 MÜNCHEN1 BERLIN 33, Herbertstrasse 22 MUNICH
DANIEL GEORGE NUZUM, Edenville, Perrybank Arklow, Wicklow, IrlandDANIEL GEORGE NUZUM, Edenville, Perrybank Arklow, Wicklow, Ireland
Feuchtigkeitsdichte Lagen für BauzweckeMoisture-proof sheets for building purposes
Die Erfindung betrifft Baumaterialien und insbesondere feuchtigkeitsdichte Lagen für Bauzwecke.The invention relates to building materials and, more particularly, to moisture-proof sheets for building purposes.
Die derzeitigen feuchtigkeitsdichten Lagen aus Polyäthylen und Filz für Bauzwecke sind ait einer Reihe Nachteile behaftet, z.B. Mörtel und Steine, die auf feuchtigkeitsdichte Lagen aus Polyäthylen aufgebracht werden, neigen dazu zu gleiten und somit ergeb en sich Schwierigkeiten bezüglich der Lageanordnung der Steine auf derartigen feuchtigkeitsdichten Lagen.The current moisture-proof polyethylene sheets and felt for building purposes have a number of disadvantages, e.g. mortar and stones, which are impervious to moisture Polyethylene layers are applied, tend to slide and thus there are difficulties with regard to the positional arrangement of the stones on such moisture-proof layers.
Eine der Erfindung zugrundeliegende Aufgab e besteht somit darin, diese Nachtelle zu mildern, die mit herkömmlichen feuchtigkeitsdichten Lagen verbinden sind.One of the tasks underlying the invention is thus to mitigate these disadvantages with conventional ones connect moisture-proof layers.
Erfindungsgemäß wird ein Baumaterial geschaffen in Form einer thermoplastischen Folie, die auf einer oder beiden Seiten eine Reiboberfläche für die Aufnahme und das Festhalten des Mörtels und/oder anderer Baumaterialien aufweist.According to the invention, a building material is created in the form of a thermoplastic film that has a friction surface on one or both sides for receiving and holding the Has mortar and / or other building materials.
Die Reiboberfläche kann in Form einer Mehrzahl von Ausnehmungen, Furchen oder dgl. vorliegen, die in dem Folienmaterial ausgebildet sind. The friction surface can be in the form of a plurality of recesses, grooves or the like , which are formed in the sheet material .
Erfindungsgemäß wird ebenfalls eine feuchtigkeitsdichte Lage für Bauzwecke .geschaffen und erfindungsgemäß wird insbesondere ein Verfahren zum Herstellen einer feuchtigkeitsdichten in einem Bauwerk vorgeschlagen, wobei eine Schicht einer thermo plastischen Folie während des Aufbaues des Gebäudes eingsetzt wird, wobei die Folie eine Reibungeoberfläche an einer oder According to the invention, a moisture-proof layer for building purposes is also created and according to the invention, in particular, a method for producing a moisture-proof layer in a building is proposed, a layer of a thermoplastic film being used during the construction of the building, the film having a friction surface on one or the other
009827/H03009827 / H03
19851511985 151
beiden Selten derselben besitzt, die dazu dient den Mörtel und/oder anderes Baumaterial, wie dies zum Aufbau des Gebäudes angewandt wird, aufzunehmen und festzuhalten. Vorteilhafter7 .weise wird die Reiboberfläche durch eine Mehrzahl längsseitig Seite-an-Seite vorliegender Ausnehmungen oder d§l. in der Folie gebildet.both seldom owns the same, which is used for the mortar and / or other building material, as used to construct the building, to pick up and hold. Advantageous7 . In some cases, the friction surface is provided by a plurality of recesses or d§l. in the Foil formed.
Erfindungsgemäß wird ebenfalls ein neuartiges Verfahren zum Herstellen eines Materials für Bauzwecke geschaffen, das darin besteht, daß ein thermoplastisches Material aus einem ringförmigen Strangpreßwerkzeug herkömmlicher Form extrudiert wird und ist dadurch gekennzeichnet, daß eine Mehrzahl von Seite-an-Seite vorliegenden Ausnehmungen oder dgl. vorgesehen ist, die sich längsseitig in axialer Richtung des Strangpreßwerkzeuges erstrecken und an dem Werkzeugring oder Werkzeugdorn oder an beiden vorliegen, so daß das aus dem ringförmigen Strangpreßwerkzeug stranggepreßte Material mit einer Mehrzahl Seiten-anSeite ausnehmungen oder dgl. versehen wird.According to the invention, a novel method for producing a material for building purposes is also provided that is contained therein consists in extruding a thermoplastic material from an annular extrusion die of conventional shape and is characterized in that a plurality of side-by-side recesses or the like. Is provided, which are extend longitudinally in the axial direction of the extrusion tool and on the tool ring or tool mandrel or on both are present, so that the material extruded from the annular extrusion die is provided with a plurality of side-by-side recesses or the like.
Das in dieser Weise ausgebildete röhrenförmige Material kann für das Ausbilden von Leitungen für die Aufnahme von Strömungsmitteln angewandt werden. So wurde z.B. gefunden, daß das Material besonders zweckmäßig ist für Leitungen, die frischluft in Bergwerken zuführen.The tubular material formed in this way can for the formation of conduits for the reception of fluids. For example, it was found that the Material is particularly useful for pipes that supply fresh air in mines.
Nach einem weiteren erfindungsgemäßen Merkmal wird ein ringförmiges Strangpreßwerkzeug vorgeschlagen, das eine Mehrzahl an Seite-an-Seite Ausnehmungen oder dgl. aufweist, die sich längsseitig in axialer Richtung des Strangpreßwerkzeuges erstrecken und über die gesamte innere zyllnderförmige Oberfläche des Werkzeugringes oder über die gesamte zylinderförmige Oberfläche des Werkzeugdorns oder über beide hin verlaufen .According to a further inventive feature, an annular extrusion die is proposed which has a plurality has side-by-side recesses or the like, which extend longitudinally in the axial direction of the extrusion tool and run over the entire inner cylindrical surface of the tool ring or over the entire cylindrical surface of the tool mandrel or over both.
Die Erfindung wird im folgenden beispielsweise unter Bezugnahme auf die beigefügten Zeichnungen erläutert:The invention is explained below, for example, with reference to the accompanying drawings:
—3 --3 -
■009827/U03■ 009827 / U03
ORIGINALORIGINAL
Flg. 1 1st ein Endaufriß eines Strangpreßwerkzeuges, wie es zum Herställen eines erfindungsgemäßen Baumaterials angewandt wird, wobei hier drei verschiedene abgewandelte Ausführungsformen des Strangpreßwerkzeuges wiedergegeben sind.Flg. 1 is an end elevation of an extrusion die as used in Manufacture of a building material according to the invention is used, here three different modified embodiments of the Extrusion tool are reproduced.
Fig. 2 zeigt ein röhrenförmiges Material, wie es vermittels des Strangpreßwerkzeuges nach Fig. 1 hergestellt worden ist.Fig. 2 shows a tubular material, as it is by means of Extrusion die according to Fig. 1 has been produced.
Fig. 3 zeigt eine erfindungsgemäß vorgesehene Folie in Form eines länglichen Streifens.3 shows a film provided according to the invention in the form of an elongated strip.
Fig. 4 zeigt, wie das Material nach der Fig. 3 zum Ausbilden einer feuchtigkeitsdichten Lage in einem Bauwerk angewandt werden kann.FIG. 4 shows how the material according to FIG. 3 is used to form a moisture-proof layer in a building can be used.
Unter Bezugnahme auf die Fig. 1 ist dort ein Strangpreßwerkzeug im Endaufriß so gezeigt, daß dasselbe ein Ringteil 1 mit einer mittleren öffnung aufweist, die einen Dorn 2 aufnimmt. Somit begrenzen die innere zylinderförmige Oberfläche 3 des Ringteils 1 und die zylinderförmige Oberfläche 4 des Doms 2 zusammen eine ringförmige Strangpreßöffnung 5.Referring to Fig. 1, there is shown an extrusion tool in end elevation so that it is a ring member 1 with a has central opening which receives a mandrel 2. Consequently delimit the inner cylindrical surface 3 of the ring part 1 and the cylindrical surface 4 of the dome 2 together an annular extrusion orifice 5.
Entweder die innere Oberfläche 3 des Ringteils 1 oder die Oberfläche 4 des Doms 2 oder beide sind mit Seite-an-Seite angeordneten Ausnehmungen versehen, die sich längsseitig in der axialen Richtung des Strangpreßwerkzeuges erstrecken, wobei die drei möglichen Anordnungen hier weggebrochen durch die Bezugszeichen a, b und c in der Fig. 1 wiedergegeben sind.Either the inner surface 3 of the ring part 1 or the surface 4 of the dome 2 or both are arranged side-by-side Provided recesses which extend longitudinally in the axial direction of the extrusion tool, the three possible arrangements are shown here broken away by the reference symbols a, b and c in FIG.
Wie durch das Bezugszeichen a gezeigt, ist die innere zylinderförmige Oberfläche 3 des Ringteils χ mit Ausnehmungen 6 ausgebildet, wobei die'Ausnehmungen über den gesamten Umfang der zylinderförmigen Oberfläche 3 vorgesehen sind; wobei jedoch die zylinderförmige Oberfläche 4 des Doms 2 glatt 1st. Wie durch das Bezugszeichen b gezeigt, ist andererseits hier äie zylinderförmige Oberfläche 4 dee Doms 2 mit Ausnehiraagen 1 über den gesamten Umfang desselben versehen, wobei eil© innere zylinderförmige Oberfläche 3 des Ringteile 1 glatt let. Wie durch das Bezugszeichen c gezeigt, ist sowohl Sie innere sylinderförmige Oberfläche 3 des Ringteile i als auch die ringförmige Oberfläche t des Dorne 2 mit Ausnehmungen Über ä®ren gesamte Umfange hin versehen.As shown by the reference character a, the inner cylindrical surface 3 of the ring part χ is formed with recesses 6, the recesses being provided over the entire circumference of the cylindrical surface 3; however, the cylindrical surface 4 of the dome 2 is smooth. As shown by the reference character b, on the other hand, here a cylindrical surface 4 of the dome 2 is provided with cutouts 1 over the entire circumference thereof, with the inner cylindrical surface 3 of the ring part 1 being smooth. As shown by the reference character c, both the inner cylindrical surface 3 of the ring part i and the ring-shaped surface t of the mandrel 2 are provided with recesses over the entire circumference.
009827/U03 - 4 -009827 / U03 - 4 -
Wenn ein thermoplastisches Material und insbesondere ein synthetisches Polymer, wie Polyäthylen, Polypropylen oder Polyvinylchlorid aus einem Strangpreßwerkzeug der in der Fig. 1 gezeigten Form stranggepreßt wird, wird ein röhrenförmiges Produkt gebildet, das Ausnehmungen oder Furchen besitzt, die sich in axialer Richtung entweder an den äußeren oder den inneren oder beiden Oberflächen des Rohrs erstrecken.If a thermoplastic material, and especially a synthetic one Polymer, such as polyethylene, polypropylene or polyvinyl chloride, extruded from an extrusion die of the form shown in FIG a tubular product is formed which has recesses or furrows extending in either the axial direction on the outer or inner or both surfaces of the Extend pipe.
Das in dieser Weise gebildete röhrenförmige Material kann in dieser Form zum Ausbilden von Leitungen, wie weiter oben angegeben, herangezogen werden. Gewöhnlich jedoch wird das röhrenförmige Material längsseitig zerschnitten und flachgemacht, so daß ein Streifen eines Folienmaterials ergibt, bei dem sich Ausnehmungen oder Furchen längsseitig zu dem Streifen auf einer oder beiden Oberflächenerstrecken. Die Fig. 2 zeigt ein Stück eines röhrenförmigen Materials 11, das vermittels eines Strangpreßwerkzeuges stranggepreßt worden ist, bei dem ein Ring oder ein Dorn der Form entsprechend dem Bezugszeichen b der Fig. 1 angewandt worden ist, so daß die Ausnehmungen oder Furchen 12 an der inneren Oberfläche vorliegen. Ein röhrenförmiges Material dieser Ausfuhrungsform kann längsseitig längs der Linie A-A zerschnitten werden unter Ausbilden eines Streifens eines Folienmaterials 13, siehe die Fig. 3, wobei die Ausnehmungen oder Furchen 12 sich längsseitig auf einer Oberfläche erstrecken und eine Reibungsoberfläche ergeben.The tubular material formed in this way can be in this Form for forming lines, as indicated above, are used. Usually, however, it becomes tubular Material cut lengthways and flattened so that a strip of film material results in which there are recesses or furrows extending alongside the strip on one or both surfaces. Fig. 2 shows a piece of a tubular Material 11 which has been extruded by means of an extrusion tool, in which a ring or a mandrel of the shape the reference character b of Fig. 1 has been applied so that the recesses or furrows 12 are present on the inner surface. A tubular material of this embodiment can are cut longitudinally along the line A-A to form a strip of a film material 13, see FIG. 3, wherein the recesses or furrows 12 extend longitudinally on a surface and provide a friction surface.
Bei dem Aufbau eines Gebäudes wird ein Streifenmaterial der in *r Fig. 3 gezeigten Form so angeordnet, daß sich dasselbe waagerecht in einer Wand des Gebäudes längsseitig relativ zu der Wand ersstreckt. Wie in der Fig. 4 gezeigt, wird bei dem Bau eines aus Ziegelsteinen aufgebauten Gebäudes nach Verlegen der unteren Steinlagen 21 eine Lage 22 Streifenmaterials auf die Mörtellage 23 aufgebracht, die über den unteren Steinlagen ausgebreitet wird. Das Streifenmaterial 22 wird so angeordnet, daß die Reibungsoberfläche, wie sie durch die Ausnehmungen oder Furchen gebildet wird, oben liegt. Sodann wird weiterer Mörtel 24 auf die Reibungsoberfläche des Streifenmaterials ausgebreitet für die Aufnahme der nächsten Steinlage 25. Die Reibungsoberfläche dient dazu, den Mörtel der Schicht 24 festzuhalten und jede Gefahr auszuschließen, daß dieserWhen constructing a building, a strip of material is used in * r Fig. 3 arranged so that the same extends horizontally in a wall of the building longitudinally relative to the wall. As shown in Fig. 4, in the construction of a brick building after laying the lower brick layers 21 a layer 22 of strip material is applied to the mortar layer 23, which is spread over the lower stone layers. That Strip material 22 is arranged so that the friction surface, as it is formed by the recesses or furrows, is on top. Additional mortar 24 is then applied to the friction surface of the strip material spread out for the reception of the next stone layer 25. The friction surface serves to the mortar of the To hold layer 24 and to exclude any danger that this
00 9.8 27/U03 -5-00 9.8 27 / U03 -5-
ORtQlUALORtQlUAL
Mörtel und mit ihm die sich anschließenden Steinlagen ins Gleiten kommen.Mortar and with it the adjoining stone layers start to slide.
Die angegebene Konfiguration mit Ausnehmungen und die Anzahl der Ausnehmungen pro Längeneinheit kann stark unterschiedlich für das Anpassen auf spezielle Anwendungsgebiete gestaltet werden. Weiterhin kann ebenfalls die Tiefe oder die Tiefen der Ausnehmungen verändert werden.The specified configuration with recesses and the number of recesses per unit of length can vary widely for the Adapt to special areas of application. Furthermore, the depth or the depths of the recesses can also be used to be changed.
Erfindungsgemäß hergestelltes Material bleibt unter allen Wetterbedingungen schmiegsam und flexibel und wird bei kaltem Wetter nicht einreißen oder Rißbildung zeigen, so daß im Vergleich mit derzeitigen Materialien der Ausschuß bis zu 40% verringert werden kann.Material made in accordance with the invention will remain in all weather conditions pliable and flexible and will not tear or crack in cold weather, so that when compared with current materials the scrap can be reduced up to 40%.
Ein spezielles Material der in der Fig. 3 gezeigten Form kann mit zehn längsseitigen Ausnehmungen pro Zentimeter deren Breite versehen werden und die Tiefe der Ausnehmungen kann sich auf 0,1 mm belaufen, wobei die Dicke des Materials sich auf 0,25 bis 1,25 mm und die Breite auf 2,5 cm bis 1 m beläuft. Das Material kann in Rollenform in Längen bis zu etwa 1600 m Länge geliefert werden. Vorzugsweise ist, wie bereits erwähnt, das in Anwendung kommende thermoplastische Material Polyäthylen, Polypropylen oder Polyvinylchlorid .A special material of the form shown in FIG. 3 can be provided with ten longitudinal recesses per centimeter of their width and the depth of the recesses can be 0.1 mm, the thickness of the material being 0.25 to 1.25 mm and the width is 2.5 cm to 1 m. The material can be supplied in roll form in lengths of up to around 1600 m. As already mentioned, the thermoplastic material used is preferably polyethylene, polypropylene or polyvinyl chloride .
009827/U03009827 / U03
Claims (17)