DE19527923A1 - Double-sided pressure-sensitive adhesive material eliminating need for pretreatment - has foam base contg. microballoons, esp. polyurethane foam contg. polymer microballoons, useful in car construction, e.g. for bonding strips to bodywork - Google Patents

Double-sided pressure-sensitive adhesive material eliminating need for pretreatment - has foam base contg. microballoons, esp. polyurethane foam contg. polymer microballoons, useful in car construction, e.g. for bonding strips to bodywork

Info

Publication number
DE19527923A1
DE19527923A1 DE19527923A DE19527923A DE19527923A1 DE 19527923 A1 DE19527923 A1 DE 19527923A1 DE 19527923 A DE19527923 A DE 19527923A DE 19527923 A DE19527923 A DE 19527923A DE 19527923 A1 DE19527923 A1 DE 19527923A1
Authority
DE
Germany
Prior art keywords
sensitive adhesive
pressure
adhesive material
foam
material according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19527923A
Other languages
German (de)
Inventor
Edgar Lindner
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lohmann GmbH and Co KG
Original Assignee
Lohmann GmbH and Co KG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lohmann GmbH and Co KG filed Critical Lohmann GmbH and Co KG
Priority to DE19527923A priority Critical patent/DE19527923A1/en
Publication of DE19527923A1 publication Critical patent/DE19527923A1/en
Withdrawn legal-status Critical Current

Abstract

In double-sided pressure-sensitive adhesive material with a foam base, the foam contains microballoons (I).

Description

Die Erfindung betrifft ein doppelseitig haftklebend ausge­ rüstetes Haftklebematerial mit einem Träger auf Schaum­ stoffbasis.The invention relates to a double-sided pressure-sensitive adhesive Equipped pressure-sensitive adhesive material with a carrier on foam material base.

Um Unebenheiten oder größere Dicketoleranzen zu überbrücken, die in vielen zu verklebenden Teilen vorhanden sind, werden in der Regel Haftklebematerialien mit einem Träger auf Schaumstoffbasis eingesetzt, z. B. in der Automobilindu­ strie zur Befestigung von Leisten auf Karosserieblech. Eine ausreichende Festigkeit einer solchen Verbindung ist nur zu erreichen, wenn der zur Ausrüstung des Haftklebematerials verwendete Haftklebstoff eine optimale Verbindung zum Schaumstoffträger besitzt. Ansonsten kommt es zu einer Ab­ lösung des Klebstoffs vom Trägermaterial, sobald eine Schäl- oder Scherbelastung auf das Klebebandsystem ausgeübt wird.To bridge unevenness or larger thickness tolerances, which are present in many parts to be bonded, are usually pressure-sensitive adhesives with a carrier used on foam base, z. B. in the automotive industry Strike for attaching strips on body panel. A sufficient strength of such a compound is only too reach when to the equipment of the pressure-sensitive adhesive material used pressure-sensitive adhesive an optimal connection to Has foam carrier. Otherwise it comes to an Ab Solution of the adhesive from the substrate as soon as a Peel or shear stress applied to the adhesive tape system becomes.

Derartige Nachteile weisen beim Stand der Technik Haftkle­ bematerialien mit Trägerschäumen auf Basis von Polyethylen, Polyurethan oder Polyarylat auf.Such disadvantages in the prior art include pressure sensitive adhesives materials with carrier foams based on polyethylene, Polyurethane or polyarylate.

Als Haftklebstoffe kommen dabei solche auf Basis von Acryl­ at-, Silikon-, Polyurethan- oder Kautschukklebern zum Ein­ satz.As pressure-sensitive adhesives are those based on acrylic At-, silicone, polyurethane or rubber adhesives to Ein sentence.

Die so aufgebauten Haftklebematerialien erfüllen aufgrund ihres Schaumcharakters die Forderung, Unebenheiten oder Dickentoleranzen bei zu verklebenden Werkstücken auszuglei­ chen. Nachteilig erweist sich jedoch die schwache Haftung der verwendeten Haftklebstoffe zum Trägerschaum. Deshalb müssen die eingesetzten Schaumstoffträger vor der Beschich­ tung zusätzlich vorbehandelt werden. Als wirkungsvollste Methode zur Vorbehandlung von Trägermaterialien wird in der Industrie die Coronavorbehandlung eingesetzt. Dies hat nachteilig zur Folge, daß eine Coronavorbehandlung als zu­ sätzlicher Schritt in den Beschichtungsprozeß integriert werden muß.The pressure-sensitive adhesive materials thus constructed meet due to its foam character the requirement of bumps or Thickness tolerances for workpieces to be bonded auslei chen. However, the disadvantage is the weak adhesion the pressure-sensitive adhesives used to the carrier foam. That's why must the foam carrier used before Beschich additionally pretreated. As the most effective Method for the pretreatment of support materials is used in the Industry used the corona pretreatment. this has disadvantageous consequence that a Coronavorbehandlung than to additional step integrated into the coating process must become.

Aufgabe der Erfindung ist es daher, die Adhäsion zwischen Schaumstoffträger und Haftklebstoff der Haftklebemateria­ lien wesentlich zu verbessern, und zwar bevorzugt unter Vermeidung einer Vorbehandlung der eingesetzten Schaum­ stoffträger.The object of the invention is therefore, the adhesion between Foam carrier and pressure-sensitive adhesive of the pressure-sensitive adhesive material significantly improved, preferably under Prevention of pretreatment of the foam used fabric carrier.

Gelöst wird diese Aufgabe überraschend durch ein doppelsei­ tig haftklebend ausgerüstetes Haftklebematerial mit Schaum­ stoffträger, bei dem der Schaumstoff Mikrohohlkugeln ent­ hält. Besonders geeignet sind Schaumstoffträger auf Poly­ urethan- oder Acrylatbasis, die geschlossen- oder offenzel­ lig sein können. Dabei bewegt sich der Volumenanteil der Zellen zwischen 1 und 50%. Die Mikrohohlkugeln bestehen vorzugsweise aus organischen Materialien. Der maximale Durchmesser der Mikrokugeln liegt zwischen 5 und 350 µm, vorzugsweise bei 10 bis 150 µm. Der Anteil der Mikrokugeln im Schaumstoff beträgt bis zu 50 Vol.-%. Als besonders ge­ eignet haben sich Mikrohohlkugeln auf Polymerbasis erwie­ sen.This task is solved surprisingly by a doppelsei pressure-sensitive adhesive material with foam carrier, in which the foam micro hollow balls ent holds. Foam carriers on poly are particularly suitable urethane or acrylate base, the closed or offenzel can be lig. The volume fraction of the Cells between 1 and 50%. The hollow microspheres exist preferably from organic materials. The maximum Diameter of the microspheres is between 5 and 350 μm, preferably at 10 to 150 μm. The proportion of microspheres in the foam is up to 50 vol .-%. As a particularly ge Micro hollow spheres based on polymers have proven to be suitable sen.

Der zur ein- oder beidseitigen Ausrüstung des Trägermateri­ als einzusetzende Haftkleber kann aus der Gruppe der Acry­ lat-, Silikon-, Polyurethan- oder Kautschukkleber ausge­ wählt werden. Die haftklebenden Flächen können vor Gebrauch durch Abdeckungen geschützt werden.The one- or two-sided equipment of the Trägermateri as to be used pressure-sensitive adhesive can from the group of Acry lat, silicone, polyurethane or rubber adhesive out be chosen. The pressure-sensitive adhesive surfaces can be used before use protected by covers.

Das Haftklebematerial kann noch weitere Schichten umfassen, wie z. B. solche zum Dickenausgleich oder zur Wärmeaktivier­ barkeit.The pressure-sensitive adhesive material may comprise further layers, such as B. those for thickness compensation or heat activator bility.

Die Wirkung der Mikrohohlkugeln beruht darauf, daß ihr Ein­ satz in den Oberflächen des Schaumes die Affinität zu Haft­ klebematerialien erhöht.The effect of the hollow microspheres is based on their Ein set in the surfaces of the foam the affinity to detention increased adhesive materials.

Besonderen Vorteil erlangen erfindungsgemäße Haftklebemate­ rialien in der Automobilindustrie. Hier werden sie in Form von Bändern zur Befestigung von Zierleisten oder Emblemen auf Karosserieblech eingesetzt. Die dabei an das Haftklebe­ material zu stellende Anforderung bezüglich einwandfreier Verankerung des Haftklebstoffs zum Schaumstoffträger ist trotz der bekannten Coronavorbehandlung bei herkömmlichen Haftklebematerialien nicht immer gegeben. Häufig kommt es bei nicht einwandfreier Vorbehandlung des Schaumstoffträ­ gers zu Verankerungsproblemen und der Klebstoff löst sich samt Zierleiste oder Emblem vom Schaumstoff, oder der Schaumstoff löst sich mit Klebstoff und Zierleiste von der Karosserieseite, auf der die zweite Klebstoffseite ver­ bleibt, was Anlaß zu Reklamationen gibt.Particular advantage is achieved by pressure-sensitive adhesives according to the invention rials in the automotive industry. Here they are in shape of tapes for fixing decorative moldings or emblems used on body sheet. The case of the pressure-sensitive adhesive material requirement with regard to flawless  Anchoring of the pressure-sensitive adhesive to the foam carrier is despite the known corona pretreatment in conventional Pressure-sensitive adhesive materials are not always given. Often it comes if not perfect pretreatment of Schaumstoffträ gers to anchoring problems and the adhesive dissolves including trim strip or emblem of the foam, or the Foam dissolves with adhesive and trim from the Body side, on which the second adhesive side ver remains, which gives rise to complaints.

Diese Nachteile werden beim Einsatz von Haftklebemateria­ lien nach der Erfindung vermieden. Hier werden Ablöse­ erscheinungen nicht beobachtet, und die Beeinflussung der Polarität der Schaumstoffoberfläche durch Zusatz von Mikro­ hohlkugeln scheint für eine gute Verankerung des Haftkleb­ stoffs zum Schaumstoffträger auch ohne Coronavorbehandlung verantwortlich zu sein, worauf die in der Tabelle angegebe­ nen Meßwerte einen Hinweis geben.These disadvantages are the use of pressure-sensitive adhesive materials Lien avoided according to the invention. Here are transfer fees phenomena are not observed, and the influence on the Polarity of the foam surface by addition of micro Hollow balls seems to be a good anchorage of the pressure-sensitive adhesive fabric to foam carrier even without corona pretreatment to be responsible for what is stated in the table give a message to NEN measured values.

Beispielexample

Zur Herstellung eines erfindungsgemäßen PUR-Klebebandes wird ein Gemisch ausFor the preparation of a PUR adhesive tape according to the invention is a mixture of

Gew.-TeileParts by weight ® Impranil HS-62 Gew.-Teile (Aromatisches PUR-Präpolymer der Fa. Bayer)® Impranil HS-62 parts by weight (Aromatic PUR prepolymer from Bayer) 10001000 ® Imprafix HS-C (Vernetzungskomponente auf Aminbasis der Fa. Bayer)® Imprafix HS-C (amine-based crosslinking component from Bayer) 6262 ® Bayderm B-TO schwarz (ketonhaltige Pigmentpräperation d. Fa. Bayer)® Bayderm B-TO black (ketone-containing pigment preparation from Bayer) 4040 ® Levacast Fluid SN (Zurichtmittel auf PUR-Basis der Fa. Bayer)® Levacast Fluid SN (Bayer PUR-based dressing) 10 10   ® Acronal L 700 (Polyacrylsäureester der Fa. BASF)® Acronal L 700 (polyacrylic acid from BASF) 55 ® Tinuvin 765 (UV-Absorber der Fa. Ciba-Geigy)® Tinuvin 765 (UV absorber from Ciba-Geigy) 55 ® Celogen OT (Blasmittel auf Basis von Azodicarbonamid der Fa. Uniroyal)® Celogen OT (blowing agent based on azodicarbonamide from Uniroyal) 2020 ® Dualite M 6017 AE (Hohlkugeln auf Acrylnitrilcopolymerbasis)® Dualite M 6017 AE (acrylonitrile copolymer-based hollow spheres)

® Impranil HS-62 wird in einem Behälter vorgelegt. Unter Rühren werden ® Imprafix HS-C und das ® Bayderm B-TO schwarz zugegeben. Diese Mischung wird 10 Minuten gerührt. Anschließend werden ® Levacast Fluid SN, ® Acronal L 700, ® Tinuvin 765, ® Celogen OT und ® Dualite M 6017 AE zugege­ ben und nochmals 30 Minuten gerührt, bis eine beschichtbare Masse erhalten wird. Diese Masse wird mit Hilfe einer Streichrakel auf ein dehäsiv ausgerüstetes Papier ausge­ strichen und bei einer Temperatur von ca. +160°C geschäumt und anschließend bei der gleichen Temperatur 2 Minuten ge­ trocknet, so daß man eine Schicht mit einer Dicke von ca. 800 µm erhält. Die so hergestellte Schicht wird anschlie­ ßend beidseitig nach Entfernung des dehäsiv ausgerüsteten Papieres mit ca. 70 g/m² eines Polyacrylathaftklebers be­ schichtet. Zum Schutz der Klebstoffschicht wird das Klebe­ band mit einem dehäsiv ausgerüsteten Schutzpapier oder ei­ ner Schutzfolie abgedeckt. ® Impranil HS-62 is placed in a container. Under Stirring ® Imprafix HS-C and the ® Bayderm B-TO black added. This mixture is stirred for 10 minutes. Subsequently, ® Levacast Fluid SN, ® Acronal L 700, ® Tinuvin 765, ® Celogen OT and ® Dualite M 6017 AE added and stirred again for 30 minutes until a coatable Mass is obtained. This mass is using a Streichrakel on a dehäsiv equipped paper out painted and foamed at a temperature of about + 160 ° C and then at the same temperature for 2 minutes ge dries, so that a layer with a thickness of about 800 microns receives. The layer thus produced is subsequently On both sides after removal of the dehäsiv equipped Paper with about 70 g / m² of a polyacrylate adhesive be coated. To protect the adhesive layer is the adhesive tied with a dehäsiv equipped protective paper or egg ner protective film covered.  

Tabelle table

Claims (12)

1. Doppelseitig haftklebend ausgerüstetes Haftklebematerial mit Träger auf Schaumstoffbasis, dadurch gekennzeichnet, daß der Schaumstoff Mikrohohlkugeln enthält.1. Double-sided pressure-sensitive adhesive pressure-sensitive adhesive material with foam-based carrier, characterized in that the foam contains hollow microspheres. 2. Haftklebematerial nach Anspruch 1, dadurch gekennzeich­ net, daß der Schaumstoff ein Polyurethanschaumstoff ist.2. Pressure-sensitive adhesive material according to claim 1, characterized gekennzeich net, that the foam is a polyurethane foam. 3. Haftklebematerial nach Anspruch 1 oder 2, dadurch ge­ kennzeichnet, daß der Schaumstoff geschlossenzellig ist.3. pressure-sensitive adhesive material according to claim 1 or 2, characterized ge indicates that the foam is closed-cell. 4. Haftklebematerial nach Anspruch 1 oder 2, dadurch ge­ kennzeichnet, daß der Anteil der Zellen zwischen 1 und 50 Vol.-% beträgt.4. pressure-sensitive adhesive material according to claim 1 or 2, characterized ge indicates that the proportion of cells is between 1 and 50 Vol .-% is. 5. Haftklebematerial nach einem oder mehreren der vorange­ henden Ansprüche, dadurch gekennzeichnet, daß die Mikro­ hohlkugeln organisches oder anorganisches Material enthal­ ten.5. pressure-sensitive adhesive material according to one or more of the preceding Henden claims, characterized in that the micro hollow balls contain organic or inorganic material th. 6. Haftklebematerial nach einem oder mehreren der vorange­ henden Ansprüche, dadurch gekennzeichnet, daß der Durchmes­ ser der Mikrohohlkugeln zwischen 5 und 350 µm, vorzugsweise zwischen 10 und 150 µm beträgt.6. pressure-sensitive adhesive material according to one or more of the preceding existing claims, characterized in that the diam the hollow microspheres between 5 and 350 microns, preferably between 10 and 150 microns. 7. Haftklebematerial nach einem oder mehreren der vorange­ henden Ansprüche, dadurch gekennzeichnet, daß der Anteil der Mikrohohlkugeln im Schaumstoff bis zu 50 Vol.-% be­ trägt.7. pressure-sensitive adhesive material according to one or more of the preceding existing claims, characterized in that the proportion the hollow microspheres in the foam up to 50 vol .-% be wearing. 8. Haftklebematerial nach einem oder mehreren der vorange­ henden Ansprüche, dadurch gekennzeichnet, daß die Mikro­ hohlkugeln Polymer-Hohlkugeln sind. 8. pressure-sensitive adhesive material according to one or more of the preceding Henden claims, characterized in that the micro hollow spheres are polymer hollow spheres.   9. Haftklebematerial nach einem oder mehreren der vorange­ henden Ansprüche, dadurch gekennzeichnet, daß der Haftkleb­ stoff aus der Gruppe bestehend aus Acrylatklebern, Silikon­ klebern, Polyurethanklebern und Kautschukklebern ausgewählt ist.9. pressure-sensitive adhesive material according to one or more of the preceding existing claims, characterized in that the pressure-sensitive adhesive fabric from the group consisting of acrylate adhesives, silicone selected from adhesives, polyurethane adhesives and rubber adhesives is. 10. Haftklebematerial nach einem oder mehreren der vorange­ henden Ansprüche, dadurch gekennzeichnet, daß der Schaum­ stoff nur einseitig mit Haftkleber beschichtet ist.10. pressure-sensitive adhesive material according to one or more of the preceding Henden claims, characterized in that the foam fabric is only coated on one side with pressure-sensitive adhesive. 11. Haftklebematerial nach einem oder mehreren der vorange­ henden Ansprüche, dadurch gekennzeichnet, daß es mindestens eine Schicht enthält.11. pressure-sensitive adhesive material according to one or more of the preceding existing claims, characterized in that it at least contains a layer. 12. Verwendung des Haftklebematerials nach einem der An­ sprüche 1 bis 11 zur Herstellung von Klebeverbindungen an Teilen im Automobilbau.12. Use of the pressure-sensitive adhesive material according to one of the Proverbs 1 to 11 for the production of adhesive joints on Parts in the automotive industry.
DE19527923A 1995-07-29 1995-07-29 Double-sided pressure-sensitive adhesive material eliminating need for pretreatment - has foam base contg. microballoons, esp. polyurethane foam contg. polymer microballoons, useful in car construction, e.g. for bonding strips to bodywork Withdrawn DE19527923A1 (en)