DE1948017A1 - Luminescent screen production by sediment- - ation in presence of tanning agents - Google Patents

Luminescent screen production by sediment- - ation in presence of tanning agents

Info

Publication number
DE1948017A1
DE1948017A1 DE19691948017 DE1948017A DE1948017A1 DE 1948017 A1 DE1948017 A1 DE 1948017A1 DE 19691948017 DE19691948017 DE 19691948017 DE 1948017 A DE1948017 A DE 1948017A DE 1948017 A1 DE1948017 A1 DE 1948017A1
Authority
DE
Germany
Prior art keywords
sedimentation
tanning
liquid
luminescent screen
additive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE19691948017
Other languages
German (de)
Inventor
Johann Hemm
Otto Dipl-Chem Marzel
Uwe Dipl-Phys Ritter
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Licentia Patent Verwaltungs GmbH
Original Assignee
Licentia Patent Verwaltungs GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Licentia Patent Verwaltungs GmbH filed Critical Licentia Patent Verwaltungs GmbH
Priority to DE19691948017 priority Critical patent/DE1948017A1/en
Publication of DE1948017A1 publication Critical patent/DE1948017A1/en
Pending legal-status Critical Current

Abstract

Luminescent screen production by sedimentation in presence of tanning agents. Additive with tanning activity which pref. leaves no residue on heating to 450 degrees C in presence of O2, pref. 0.2-5% tannin solution, is added to sedimentation liquid (II), pref. 0.1-1 (0.2)% polyvinyl alcohol solution, in process for producing a luminescent screen, particularly for cathode ray tubes, by depositing a fluorescent substance introduced in (II) on to a luminescent screen support placed below (II). Adhesion of fluorescent substance to support is achieved without adding water glass to (II), thus preventing diminution of light output by presence of silicic acid in luminescent screen.

Description

"Verfahren zum Herstellen eines Leuchtschirmes" Die Erfindung betrifft ein Verfahren zum Herstellen eines Leuchtschirmes insbesondere für Kathodenstrahlröhren nach dem Sedimentationsprinzip, bei dem sich ein leuchtstoff, der in eine über dem Leuchtschirmträger stehende Sedimentationsflüssigkeit eingebracht wird, auf dem Leuchtschirm träger absetzt. "Method of Making a Luminous Screen" The invention relates to a method for producing a fluorescent screen, in particular for cathode ray tubes according to the sedimentation principle, in which there is a fluorescent substance, which is in an above the Luminous screen support standing sedimentation liquid is introduced on the Luminescent screen carrier separates.

Sedimentationsverfahren zur Herstellung von teuchtsohirmen für Kathodenstrahlröhren sind bekannt. Um db Haftfestigkeit des Leuchtstoffes auf dem Leuchtschirmträger zu erh6-hen, ist es üblich, der Sedimentationsflussigkeit Wasserglas zuzusetzen. Die ausscheidende Kieselsäure bewirkt eine verbesserte Haftung der Leuchtstoffpartikelchen auf dem Leuchtschirmträger. Es ist aber auch bekannt, daß in dem Leuchtschirm vorhandene Kieselsäure nicht entfernt werden kann, wodurch sich eine Verringerung der Lichtausbeute des Leuchtschirmes ergibt.Sedimentation process for the production of moisture screens for cathode ray tubes are known. To db adhesive strength of the phosphor on the screen support To increase it, it is customary to add water glass to the sedimentation liquid. The precipitating silica improves the adhesion of the phosphor particles on the Screen mount. But it is also known that in that Silica present in the fluorescent screen cannot be removed, resulting in a Reduction in the light output of the fluorescent screen results.

Der vorliegenden Erfindung liegt die Aufgabe zugrunde ein neuartiges Verfahren der eingangs genannten Art anzugeben, das Leuchtachirme guter Haftfähigkeit zu erzielen gestattet, wobei Schädigungen des Leuchtstoffes weitgehend vermieden werden.The present invention is based on the object of a novel one Specify the method of the type mentioned at the outset, the fluorescent screen with good adhesion allowed to achieve, with damage to the phosphor largely avoided will.

Gemäß der Ertlndung wird vorgeschlagen, daß der Sedimentationsflüssigkeit ein Zusatz mit Gerbwirkung zugesetzt wird.According to the Ertlndung it is proposed that the sedimentation liquid an additive with a tanning effect is added.

Es hat sich gezeigt, daß ein Zusatz von in der Sedimentationsflüssigkeit löslichen und gerbenden Stoffen beeito in geringer Beimengung die Haftfestigkeit des Leuchtstoffes auf dem Leuchtschirmträger außerordentlich erhöht. Diese erhöhte Haftfestigkeit tritt bereits sohon während des Absetzens des Leuchtstoffes ein, was den großen Vorteil mit sich bringt, daß bei dem Abgießen der Sedimentationsflüssigkeit die niedergeschlagene Leuchtstoffschicht nicht beschädigt wird. Es ist dadurch möglich, das Abgießen der Sedimentationsflüssigkeit durchzuführen, weil die Gefahr wesentlich verringert ist, daß durch die abfließende Flüssigkeit Leuohtstoffteilohen aus der niedergeschlagenen Schicht herausgerissen werden.It has been shown that an addition of in the sedimentation liquid Soluble and tanning substances and in small admixtures the adhesive strength of the phosphor on the screen carrier is extremely increased. This increased Adhesion already occurs during the deposition of the fluorescent material, which has the great advantage that when pouring off the sedimentation liquid the deposited phosphor layer is not damaged. It is thereby possible pouring off the sedimentation liquid perform because the risk is significantly reduced that the outflowing liquid will cause particles of fluorescent material be torn from the depressed layer.

Anhand eines bevorzugten Ausführungsbeispiels der Erfindung wird der Anmeldungsgegenstand nachfolgend näher erklärt.Based on a preferred embodiment of the invention, the The subject of the application is explained in more detail below.

Als Sedimentationsflüssigkeit, die über dem Leuchtschirmträger steht, der bevorzugt die Frontscheibe einer Kathodenstrahlröhre ist, wird eine Sedimenttionslösung aus 0,1 %iger bis 1 %iger, insbesondere etwa 0,2 %iger Polyvinylalkohol-Lösung verwendet. Dieser wird als Gerbmittel eine 0,2 bis 1 %ige, insbesondere etwa 0,5 %ige Tannin-Lösung zugesetzt, und zwar in einer Menge von etwa 2 bis 30 % der Gesamtflüssigkeitsmenge. Dieser Sedimentationslösung wird der Leuchtstoff zugesetzt, der sich infolge seiner pulverförmigen Struktur aus der Suspension nun auf der Oberfläche des Leuchtschlrmträgers absetzt. Die Absetzzeit kann von einer halben bis zu mehreren Stunden dauern.As a sedimentation liquid that stands over the screen support, which is preferably the faceplate of a cathode ray tube, becomes a sedimentation solution from 0.1% to 1%, in particular about 0.2%, polyvinyl alcohol solution. As a tanning agent, this is a 0.2 to 1%, in particular about 0.5%, tannin solution added, in an amount of about 2 to 30% of the total amount of liquid. This sedimentation solution is added to the phosphor, which is due to its powdery structure from the suspension now on the surface of the Leuchtschlrmträgers settles. The settling time can take from half an hour to several hours.

Nach erfolgtem Absetzen des leuchtstoffes wird die Sedimentationsflüssigkeit abgegossen, wobei nun keine besonderen Maßnahmen beachtet werden müssen, weil der Leuohtstoff fest auf dem Leuchtschirmträger haftet. Danach wird der Beuchtschirm in an sich bekannter Weise weiterbehandelt, d. h.After the luminescent material has settled, the sedimentation liquid becomes poured off, but now no special measures have to be observed because of the Leuohtstoff adheres firmly to the screen carrier. After that, the belly screen further treated in a manner known per se, d. H.

also, getrocknet und dann bei etwa 4300 C über eine Zeit von etwa einer halben bis zwei Stunden ausgeheizt. Auoh danaoh zeigt der leuohtschirm noch eine ausgezeichnete Haftung auf dem Leuchtschirmträger und es ist keinerlei Beschädigung des Leuchtstoffes durch die Sedimentationsiösung festzustellen.so, dried and then at about 4300 C for a time of about half an hour to two hours. Auoh danaoh the leuoh screen still shows excellent adhesion to the screen support and there is no damage whatsoever determine the phosphor through the sedimentation solution.

Wenngleich als bevorzugtes Gerbmittel Tannin verwendet wird, so kann es auch zweckmäßig sein, noch andere Gerbmittel zu verwenden. Geeignet erscheinen z. B. höher molekulare Abkämmlinge der Gallussäure sow@ Ellagen-Gerbstoffe (2. B.Although tannin is used as the preferred tanning agent, it can it may also be expedient to use other tanning agents. Appear suitable z. B. higher molecular combs of gallic acid and Ellagen tannins (2. B.

Corilagin) und Catechin-Gerbstoffe. Diese Gerbmittel soll ten aber zweckmäßig bei den üblichen Ausheiztemperaturen, die im allgemeinen nicht über 4500 C liegen, entfernbar sein, d. h. bevorzugt unter Sauerstoffanwesenheit verbrennbar sein. Da der Zusatz der Gerbmittel verhältnismäßig gering sein kann, ist aber auch noch keine störende Verringerung der Leuchtkraft des Leuohtschirmes feststellbar, wenn Gerbzusätze zurückbleiben sollten.Corilagin) and catechin tannins. These tanning agents should, however expedient at the usual bakeout temperatures, which generally do not exceed 4500 C lie, be removable, d. H. preferably combustible in the presence of oxygen be. Since the addition of the tanning agent can be relatively small, it is also no disturbing reduction of the luminosity of the lampshade noticeable yet, if tanning additives should remain.

AS Sedimentationslösung werden gemäß der Erfindung bevorzugt wässrige Lösungen organischer Stoffe, insbesondere eine 0,1 bis 1 %ige Polyvinylalkohol-Lösung, verwendet. De Sedimentationsflüssigkeit soll zweckmäßig kein Wasserglas enthalten.According to the invention, AS sedimentation solutions are preferably aqueous Solutions of organic substances, in particular a 0.1 to 1% polyvinyl alcohol solution, used. The sedimentation liquid should expediently not contain a glass of water.

Claims (7)

P a t e n t a n s p r ü c h e P a t e n t a n s p r ü c h e Verfahren zum Herstellen eines Leuohtsohirmes insbesondere für Kathodenstrahlröhren nach dem Sedimentationsprinzip, bei dem sioh ein Leuohtstoff, der in eine über dem Leuchtschirmträger stehende SedimentationsflUssigkeit ein.Method for producing a lampshade, in particular for cathode ray tubes according to the sedimentation principle, in which sioh a Leuohtstoff, which in a over the Luminous screen carrier a standing sedimentation liquid. gebracht wird, auf dem Leuchtschirmträger absetzt, dadurch gekennzeichnet, daß der SedimentationsflUssigkeit ein Zusatz mit Gerbwirkung zugesetzt wird.is brought, deposited on the screen carrier, characterized in that that an additive with a tanning effect is added to the sedimentation liquid. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß in gerbender Zusatz verwendet wird, der bei erhöhten, jedoch 4500 C nicht Ubersteigenden Temperaturen, vorzugsweise bei Sauerstoffanwesenheit, weitgehend rückstandslos entrernbar ist.2. The method according to claim 1, characterized in that in tanning Additive is used, which at elevated, but not exceeding 4500 C temperatures, preferably in the presence of oxygen, can be removed largely without leaving any residue. 3. Verfahren nach einem oder mehreren der Ansprüche 1 bis 2, dadurch gekennzeichnet, daß als gerbender Zusatz eine 0,2 %ige bis 5 %ige, vorzugsweise 0,3 %ige bis 2,5 %ige, insbesondere eine etwa 0,5 %ige Tanninlösung verwendet wird.3. The method according to one or more of claims 1 to 2, characterized characterized in that the tanning additive is 0.2% to 5%, preferably 0.3% to 2.5%, in particular an approximately 0.5% tannin solution is used. 4, Verfahren nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, daß der Sedimentationsflüssigkeit 2 bis 50 Volumsprozente, insbesondere 5 bis 20 Volumsprozente, einer gerbenden Flüssigkeit zugesetzt werden. 4, method according to one of claims 1 to 3, characterized in that that of the sedimentation liquid 2 to 50 percent by volume, in particular 5 to 20 percent by volume, added to a tanning liquid. 5. Verfahren nach einem oder mehreren der Ansprüche 1 bis 4, dadurch gekennzeichnet, daß als Sedimentationsflüssigkeit eine 0, bis 1 %ige, insbesondere etwa 0,2 %ige Polyvinylalkohol-Lösung verwendet wird.5. The method according to one or more of claims 1 to 4, characterized characterized in that the sedimentation liquid is a 0 to 1%, in particular about 0.2% polyvinyl alcohol solution is used. 6. Verfahren nach einem oder mehreren der Ansprüche 1 bis 5, dadurch gekennzeichnet, daß als Sedimentationsflüssigkeit organische Lösungen undZoder wässrige Lösungen verwendet werden.6. The method according to one or more of claims 1 to 5, characterized characterized in that organic solutions andZ or aqueous Solutions are used. 7. Verfahren naoh einem oder mehreren der Ansprüche 1 bis 6, dadurch gekennzeichnet, daß die Sedimentationsflüs.7. The method naoh one or more of claims 1 to 6, characterized characterized in that the Sedimentationsflüs. sigkeit frei von Wasserglas ist.the liquid is free from water glass.
DE19691948017 1969-09-23 1969-09-23 Luminescent screen production by sediment- - ation in presence of tanning agents Pending DE1948017A1 (en)