DE1942780A1 - Chemical embossing process for the production of jewelry plates - Google Patents
Chemical embossing process for the production of jewelry platesInfo
- Publication number
- DE1942780A1 DE1942780A1 DE19691942780 DE1942780A DE1942780A1 DE 1942780 A1 DE1942780 A1 DE 1942780A1 DE 19691942780 DE19691942780 DE 19691942780 DE 1942780 A DE1942780 A DE 1942780A DE 1942780 A1 DE1942780 A1 DE 1942780A1
- Authority
- DE
- Germany
- Prior art keywords
- pattern
- printing ink
- hardening
- plastic
- plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
EIDAl SANGYO KABUSHiKl KAISHA, 33, Hirabayashi-Minami~chö Sumiyoshi-ku, Osaka, JapanEIDAl SANGYO KABUSHiKl KAISHA, 33, Hirabayashi-Minami ~ chö Sumiyoshi-ku, Osaka, Japan
Chemisches Prägeverfahren zur Herstellung von SchmuckplattenChemical embossing process for the production of jewelry plates
Die Erfindung betrifft ein Verfahren zum Herstellen verschiedener, eine unregelmäßige Oberfläche aufweisender Muster auf einer Schmuckplatte oder anderen Gegenständen vermittels eines chemischen Prägeverfahrens und insbesondere ein chemisches Verfahren "für ein Prägen, durch das auf einer gekrümmten oder ebenen Oberfläche industrieller Güter, wie Schmuckplatten oder Möbeln undweiteren Materialien verschiedene, eine unregelmäßige Oberfläche aufweisende Muster hergestellt werden können.The invention relates to a method for producing various, a pattern having an irregular surface on a jewelry plate or other objects a chemical embossing process and in particular a chemical one Method "for an embossing, by which on a curved or flat surface of industrial goods, such as decorative plates or furniture and other materials patterns having an irregular surface can be produced.
Nach dem Stand der Technik sind Muster mit unregelmäßiger Oberfläche auf einer Schmuckplattevermlttels eines der im folgenden beschriebenen Verfahren hergestellt worden.According to the prior art, patterns with an irregular surface on a jewelry plate are one of the im has been prepared following the method described.
Hierbei handelt es sich einmal um ein Prägeverfahren unter Anwenden einer ein unregelmäßiges Oberflächenmuster aufweisenden Metallwalze, die auf die Platte zur Einwirkung gebracht wird, auf die eine weiche, plastische Folie aufgeklebt ist, welche aufgrund verschiedener Muster eine schmückende Wirkung ausübt oder um das Prägeverfahren, das so ausgeführt wird, daß auf die Platte eine schmückende Folie aufgebracht wird, die zuvor mit einem Kunstharz versehen worden ist, anschließend eine Metallplatte aufgebracht wird, die ein unregelmäßiges Oberflächenmuster aufweist, sowie abschließend die Platte unter Erwärmen und Zusammendrücken zwecks Verformen in eine heiße Presse eingeführt wird.This is, on the one hand, an embossing process using an irregular surface pattern Metal roller, which is brought into action on the plate, on which a soft, plastic film is glued which has a decorative effect due to different patterns or the embossing process that is carried out so that a decorative film is applied to the plate, which is previously provided with a synthetic resin has been, then a metal plate is applied, which has an irregular surface pattern, and finally the plate is introduced into a hot press with heating and compression for the purpose of deforming will.
009825/1111009825/1111
Wenn es sich jedoch z.B. um das Muster einer Holzmaserung handelt; bei dem Porenmuster in die unregelmäßige Oberfläche eingeformt werden, sind diese Huster so klein und* zahlreich, daß es außerordentlich schwierig ist, mit den Metallwalzen und Formen zu arbeiten, wobei erhebliche Herstellungskosten und Verkaufspreise der Schmuckplatte resultieren. Weiterhin ist es technisch unmöglich gewesen, die angegebene Prägearbeit mit sehr kleinen Mustern aufgedruckt auf die Platte und ausgeformt in ein unregelmäßiges Oberflächenmuster herzustellen. Die gedruckten Muster fallen gewöhnlich nicht mit den vorgesehenen unregelmäßigen Oberflächeneigenschaften zusammen, so daß die fertige Platte ein ganz anderes Aussehen als ein natürliches Hihlzbrett besitzt und somit ein ansprechendes Aussehen nicht gegeben ist*However, if it is, for example, a wood grain pattern acts; where pore patterns are molded into the irregular surface, these coughs are so small and * numerous that it is extremely difficult to deal with Metal rollers and molds work, with significant manufacturing costs and sales prices of the jewelry plate result. Furthermore, it has been technically impossible to print the specified embossing with very small patterns onto the plate and molded into an irregular surface pattern. The printed samples fall usually not with the intended irregular surface properties together, so that the finished panel has a completely different appearance than a natural heating board possesses and therefore does not have an appealing appearance *
Weiterhin wird zur Zeit ein Prägeverfahren angewandt, bei dem im allgemeinen ein ausgewähltes Muster zuvor auf die Oberfläche der Platte miteiner Druckfarbe im Gemisch mit einem Material aufgedruckt wird, das einen durchscheinenden Kunststoff abstößt, und im Anschluß hieran wird der durchscheinende Kunststoff aufgebracht, so daß der Kunststoff an jeder Seite von dem oberen Teil des aufgedruckten Anteils abgestoßen wird, wodurch in der Schicht des harzartgen Films das unregelmäßige Oberflächenmuster ausgebildet wird. Da jedoch der auf die Platte aufgebrachte Kunststoff nicht in einem kontinuierlichen Zustand verbleiben kann, da derselbe abgestoßen und getrennt über dem gedruckten Teil zerschnitten wird, bewegt sich die harzartige Anstrichmasse unregelmäßig teilweise bis zu einer Stelle weitentfernt von der Stelle über dem gedruckten Teil, das aus Linien und Punkten besteht, so daß die unregelmäßig vergrößerten, dreidimensionalen unregelmäligen Muster nicht genau mit den gedrückten Mustern übereinstimmen und sich ein sehr wenig vorteilhaftes Aussehen der Gegenstände ergibt.Furthermore, an embossing process is currently used at generally a selected pattern is previously applied to the surface of the plate with an ink mixed with it is imprinted on a material that repels a translucent plastic, and then the translucent Plastic applied so that the plastic is on each side from the top of the printed portion is repelled, whereby the irregular surface pattern is formed in the resinous film layer. However, since the plastic applied to the plate cannot remain in a continuous state, it is the same is repelled and cut separately over the printed part, the resinous paint moves irregular partially up to a point far from the point above the printed part made up of lines and Points, so that the irregularly enlarged, three-dimensional irregular pattern does not exactly match the printed pattern and become a very results in a less favorable appearance of the objects.
008826/1111008826/1111
Der Erfindung liegt nun die Aufgabe zugrunde, ein chemishes Verfahren zu schaffen, das es ohne Anwenden der oben angegebenen metallischen Abdeckplatte oder Prägewalze mit dreidimensional unregelmäßiger Oberfläche ermöglicht, die Prägemuster auf der Oberfläche des Gegenstandes mit gekrümmter oder ebener Fläche auszuführen, so daß es möglich wird, in großen Mengen und billig schmückende, gedruckte und dreidimensional unregelmäßige Porenmuster, wie bei Hartholzschnitten oder die dreidimensional uneegelmäßigen Muster von Textilien, wie z.B. gewobenen und gestrickten Gegenständen und ebenfalls verschiedene Arten an Figuren und Buchstaben herzustellen.The invention is now based on the object of a chemical Method of creating it without applying the above metallic cover plate or embossing roller with a three-dimensional irregular surface enables the embossing pattern on the surface of the object with a curved or flat surface, so that it becomes possible in large quantities and cheap decorative, printed and three-dimensional irregular pore patterns, as in hardwood cuts or the three-dimensional irregular patterns of textiles such as woven and knitted objects and also make different types of figures and letters.
Das erfindungsgemäße Verfahren ist nun dadurch gekennzeichnet, daß verschiedene Bilder mit der Druckfarbe ausgebildet werden, die einen Härtungsverzögerer oder -beschleuniger enthält, und zwar- auf der Oberfläche eines entsprechenden Gegenstandes und sodann hierauf der härtende Kunststoff aufgebracht wird.The method according to the invention is now characterized in that that various images are formed with the printing ink containing a hardening retarder or accelerator, namely- on the surface of a corresponding object and then the hardening plastic is applied thereon.
Unabhängig von der Art und Form des Gegenstandes wird gegebenenfalls ein Füllmittel auf die Oberfläche desselben aufgebracht, um *so zuvor die Oberfläche glatt zu machen. Sodann erfolgt ein Trocknen und nach Aufkleben von Folien aus dünnem Papier auf diese Oberfläche zwecks Glätten derselben wird der Grundüberzug mit den üblichen Grundanstrichfarben aufgebracht, wie es erforderlich ist, und nach dem Aufdrucken der Grundmuster mit herkömmlicher Druckfarbe werden die oben angegebenen dreidimensionalen, unregelmäßigen Muster und Buchstaben aufgedrückt, wobei die Druckfarbe ein das Erhärten des Kunststoffes verzögerndes Mittel enthält und sodann ein abschließender Überzug, wie z.B. ein Überzug aus einem durchsichtigen oder durchscheinenden Polyester-Kunststoff gleichmäßig aufgebracht und unter Erhärten desselben getrocknet, wird.Regardless of the type and shape of the item, if necessary a filler is applied to the surface of the same in order to make the surface smooth beforehand. Then drying takes place and after gluing films of thin paper to this surface for the purpose of smoothing the same the base coat is applied with the usual base paints as required and after printing the basic pattern with conventional ink becomes the above-mentioned three-dimensional irregular pattern and printed letters, the printing ink containing an agent which retards the hardening of the plastic, and then a final cover, such as a cover made of a clear or translucent polyester plastic applied evenly and dried while hardening, will.
In dem oben angegebenen Fall wird das Erhärten des Anteils, über dem mit der Druckfarbe überzogenen Teil, die mit dem Härtungsverzögerer vermischt ist, aufgrund des VorliegensIn the above-mentioned case, the hardening of the portion above the portion coated with the printing ink, which is covered with the Cure retarder is mixed due to the presence
- 4 009825/1111 - 4 009825/1111
dieses Verzögerers verzögert werden, während das andere Teil glatt gehärtet wird, so daß ein Einschrumpfen während des Härtens erfolgt und der Kunstharzanstrich, der auf demjenigen Anteil aufgebracht ist, wo das Härten verzögert wird, wird in Richtung auf das eingeschrumpfte Teil gezogen, so daß die Dicke der Überzugsschicht nnter Ausbilden von Vertiefungen erheblich verringert wird.this retarder will be delayed while the other part is cured smooth so that shrinkage occurs during curing and the resin paint applied to that Proportion applied where curing is delayed is drawn towards the shrunk part, so that the thickness of the coating layer to form pits is reduced significantly.
In umgekehrter Weise ergibt sich dann, wenn konvexe Muster ausgebildet werden sollen, daß der Druckfarbe ein Härtungsbeschleuniger zugesfetzt wird, so daß der Kunststoff über dieser Druckfarbe schneller erhärtet als an jeder Seite deselben, und der Kunststoff oder das Kunstharz an diesem Anteil wird demjenigen an dem anderen Teil unter Ausbilden eines VorSprungs anziehen und an jeder Seite so verringert werden, daß sich eine diesbezügliche Vertiefung ergibt. Wenn als die Kunststoff-Anstrichmasse, die auf diese Oberfläche aufgebracht wird, ein ungesättigter Polyester angewandt wird, nimmt man als Härtungsverzögerer Hydrochinon, Pikrinsäure, Nitrobenzol und dgl. und als Härtungsbeschleuniger Benzoylperoxid, Dimethylanilin, Methylathylketonperoxid, usw.Conversely, if convex patterns are to be formed, a curing accelerator is added to the printing ink, so that the plastic overflows this printing ink hardens faster than on either side of the same, and the plastic or synthetic resin on this Participation is given to the person in the other part under training of a projection and thus reduced on each side that there is a corresponding deepening. If than the plastic paint applied to that surface is applied, an unsaturated polyester is used, hydroquinone is used as a hardening retarder, Picric acid, nitrobenzene and the like and, as a hardening accelerator, benzoyl peroxide, dimethylaniline, methyl ethyl ketone peroxide, etc.
Die Erfindung wird im folgenden beispielsweise unter Bezugnahme auf die beigefügte Zeichnung erläutert:The invention is explained below, for example, with reference to the accompanying drawing:
Fig. 1 ist ein längsseitiger Schnitt eines Teils des Gegenstandes, der einer vorbereitenden Behandlung, wie einem überziehen mit einem Füllmittel, überziehen mit einer Grundfarbe und Aufdrucken eines gefärbten Musters unterzogen worden ist.Fig. 1 is a longitudinal section of part of the article, that of a preparatory treatment such as coating with a filler, coating with a base color and has been subjected to printing of a colored pattern.
Fig. 2 ist eine vergrößerte längsseitige Ansicht des Teils nach Fig. 1, auf das die dreidimensional unregelmäßigen Muster unter Anwenden der Druckfarbe aufgedruckt sind, die in der Lage ist, die Polymerisation des Kunststoff-Anstrichs zu verhindern.FIG. 2 is an enlarged longitudinal view of the part of FIG. 1 onto which the three-dimensionally irregular Patterns are printed using the printing ink, which is able to polymerize the plastic paint to prevent.
Fig. 3 ist eine vergrößerte längsseitige Ansicht im Schnitt des Teils nach der Fig. 2, auf das ein abschließender überzug mit einem durchsichtigen Kunstharz-Anstrich aufgebracht worden ist, der polymerisiert werden kann.Figure 3 is an enlarged, longitudinal sectional view of the portion of Figure 2 having a final coating thereon has been applied with a clear synthetic resin paint that can be polymerized.
0 0 9 8 2 5/11110 0 9 8 2 5/1111
,Fig. 4 zeigt in vergrößertem längsseitigen Schnitt ein Teil des fertigen Gegenstandes, der vermittels des erfindungsgemäßen Prägeverfahrens darauf ausgebildet ein dreidimensional unregelmäßiges Muster besitzt., Fig. 4 shows a part in an enlarged longitudinal section of the finished object, which is formed thereon by means of the embossing method according to the invention, a three-dimensional has an irregular pattern.
Zunächst wird ein überziehen mit dem Füllmittel als vorbereitende Behandlung zum Glätten der Oberfläche von Sperrholz in üblicher Weise ausgeführt. Anstelle des Füllmittels können auch dünne Folien, z.B. aus dünnem Papier, Textilgut, Kunststoff and weiteren Materialien auf die Oberfläche der Platte aufgebracht werden und diesesvorbereitende Glätten kann in dem Fall in Fortfall kommen, wo es sich um eine harte Platte mit einer bereits vorliegenden glitten Oberfläche handelt. Nach dem Glätten der Oberfläche wird der Grundüberzug mit einer herkömmlichen Anstrichfarbe mit Holzeinfärbung aufgebracht und sodann getrocknet. Sodann werden die gewählten Schmuckmuster aus.Holztexturierung auf die Oberfläche der Platte mit einer herkömmlichen Druckfarbe aufgedruckt. In dem Fall einer Holzmusterung entsprechend dem obigen Beispiel wird der entsprechende der Fig. 1 einer Vorbehandlung auf seiner Oberfläche unterworfene Gegenstand wieter durch Aufdrucken der schön gefärbten Hchlzmaserungsmusterung des natürlichen Holzes weiterverarbeitet. Diese Arbeiten werden in herkömmlicher Weise ausgeführt und sind nicht neuartig. Sodann setzt jedoch das erfindungsgemäße Verfahren ein, wie es im folgenden erläutert ist.First, a coating with the filler is used as a preparatory step Treatment for smoothing the surface of plywood carried out in the usual way. Instead of the filler, you can also thin foils, e.g. made of thin paper, textiles, plastic and other materials on the surface of the plate can be applied and this preparatory smoothing can be omitted in the case where the plate is hard acts with an already existing sliding surface. After smoothing the surface, the base coat is applied a conventional paint with wood coloring and then dried. Then the elected Wood texturing on the surface of the Plate printed with a conventional printing ink. In the case of a wood pattern according to the example above the corresponding object of FIG. 1 subjected to a pretreatment on its surface is again carried out Imprint of the beautifully colored wood grain pattern of the processed from natural wood. This work is carried out in a conventional manner and is not novel. Then, however, the method according to the invention begins, as is explained below.
Durch das Anwenden einer herkömmlichen Druckmaschine werden lediglich die dreidimensional unregelmäßigen Musterungen, wie die Poren und die Texturierung des Hartholzes aufgedruck, und zwar unter Anwenden einer Druckfarbe, die mit einem oder mehreren Härtungsverlaögerern oder Polymerisationsinhibitoren, wie Hydrochinon, butyliertes Hydroxytoluol asw. und Antioxidantien, wie Distearylthiopropionat, 2-Mercaptobenzimidazol usw. vermischt, die in der Lage sind, die Polymerisation des abschließenden harzartigen Überzuges zu verzögern. Dieser Zustand ist in der Fig. 2 gezeigt. Auf der Oberfläche der Platte, auf der das dreidimensional unregelmäßige Muster 2, wie das Porenmuster aufgedruckt ist,By using a conventional printing machine, only the three-dimensional irregular patterns, like the pores and texturing of the hardwood, using a printing ink that matches one or more hardening retarders or polymerization inhibitors, like hydroquinone, butylated hydroxytoluene asw. and antioxidants such as distearyl thiopropionate, 2-mercaptobenzimidazole, etc. mixed, which are able to to delay the polymerization of the final resinous coating. This state is shown in FIG. On the surface of the plate on which the three-dimensional irregular pattern 2, like the pore pattern, is printed
€09825/1 111 " 6 "€ 09825/1 111 " 6 "
I O T ί- / U »-»I O T ί- / U »-»
mit einem abschließenden, durchsichtigen, harzartigen Überzug 3 z.B. aus Polyester versehen, der, wie in der Fig. 3 gezeigt, polymerisiert werden kann. Sodann erfolgt ein Erwärmen und Härten. EinHärten kann natürlich auch , bei Normaltemperatur oder durch Beaufschlagen radioaktiver Strahlen erfolgen. Bei dem Ausbilden des gehärteten Überzugsfilms vermittels eines Härtngsverfahrens, wie einer Polymerisation oder Kondensations-Polymerisation wird lediglich das dreidimensional unregelmäßige Musterteil A, wie die oben angegebenen Porenmuster des Holzes, siehe die Fig. 4, mit der Spezialdruckfarbe überzogen, die in der Lage ist, die PS)Iymerisation zu verzögern. Somit wird das Härten der harzartigen Anstrichmasse an diesem Musterteil Ά lediglich verzögert, während alle anderen Teile keinerlei Verzögerung erfahren, da die Überzugsschicht und das die Holzmaserung aufweisende Muster beide mit herkömmlicher Druckfarbe überzogen sind.provided with a final, transparent, resin-like coating 3, for example made of polyester, which, as in FIG Fig. 3, can be polymerized. This is followed by heating and curing. Hardening can of course also take place at normal temperature or by exposure to radioactive rays. In forming the cured coating film by a curing method such as polymerization or condensation polymerization only becomes the three-dimensional irregular pattern part A like those mentioned above The pore pattern of the wood, see Fig. 4, coated with the special printing ink which is capable of polymerizing the PS) to delay. Thus, the hardening of the resinous paint on this pattern part Ά is only delayed while all other parts experience no delay, since the coating layer and that having the wood grain Patterns are both coated with conventional printing ink.
Wenn das Teil, wo sich der Härtungsvorgang abspielt und das Teil, wo die Härtung verzögert wird, in Berührung miteinander wie weiter oben ausgeführt, vorliegen, wird sich eine derartige Ungleichmäßigkeit des Härtens und somit Zusammenhaftens ergeben, wie es in der Fig1. 4 gezeigt ist, und die harzartige Anstrichmasse an dem Muster A wird in Richtung auf das Teil gezogen, wo sich das Härten an beiden Seiten abspielt, während der abschließend aufgebrachte durchsichtige überzug auf der Oberfläche mit Ausnahme des Musters A gehärtet wird, so daß eine dicke, durchscheinende, harzartige Überzugsschicht darauf ausgebildet wird und zwischen denselben eine tiefe Ausnehmung 4 in dem Muster A in genau der richtigen Lage vorliegt, ohne daß sich eine Diskrepanz bezüglich der durchscheinenden, harzartigen, abschlißenden Überzugsschicht ergibt. In dieser Weise werden die dreidimensional-unregelmäßigen Muster ausgebildet, wodurch sich ein elegantes und schmückendes Muster der Platte ergibt, die auch einem Naturholz bezug- ■' lieh des Griffs entspricht.When the part where the curing takes place and the part where hardening is retarded, each running in contact as above are present, to such an unevenness of curing and thus sticking together result is, as. In Figure 1 4 is shown, and the resinous paint on the pattern A is drawn towards the part where curing is taking place on both sides, while the finally applied clear coating on the surface except for the pattern A is cured so that a thick one , translucent resinous coating layer is formed thereon and there is a deep recess 4 therebetween in the pattern A in just the correct position without causing any discrepancy in the translucent resinous final coating layer. In this way, the three-dimensional, irregular patterns are formed, resulting in an elegant and decorative pattern of the plate, which also corresponds to a natural wood related to the handle.
G0 9825/11 1 1G0 9825/11 1 1
ORlQiNAL JNSPPC-™ORlQiNAL JNSPPC- ™
— "7 —- "7 -
Im obigen Ausführungsbeispiel erfährt die Oberfläche der Platte ein vorbereitendes Glätten, und das Aufdrucken wird direkt auf die so verbereitete Oberfläche ausgeführt. Nach anderen Ausführungsbeispielen jedoch werden die schmückenden, gefärbten Muster der Holzmaserung und Textur mit einer herkömmlichen Druckfarbe auf Papier, Textilgut oder Folien aufgedruckt, und nachdem lediglich das dreidimensional unregelmäßige Musterteil A mit der speziellen harzartigen Druckfarbe bedruckt worden ist, die in der Lage ist, die Polymerisation zu verzögern, wird dieses Papier oder Textilgut oder Folie auf die Oberfläche der Platte als erster Arbeitsschritt aufgeklebt und als nächster Arbeitsschritt kann das abschließende überziehen mit der durchsichtigen, harzartigen Anstrichmasse sowie das Härten und oben angegebene Verformen in der erfindungsgemäßen Weise durchgeführt werden. In the above embodiment, the surface of the plate is given a preparatory smoothing and the printing is carried out executed directly on the surface prepared in this way. According to other embodiments, however, the decorative, stained wood grain pattern and texture with a conventional printing ink on paper, textile or foils printed, and after only the three-dimensional irregular pattern part A with the special resin-like If printing ink has been printed which is able to retard the polymerization, this paper or textile material becomes or film glued to the surface of the plate as the first step and as the next step can do the final coating with the clear, resinous paint as well as hardening and above Deforming can be carried out in the manner according to the invention.
Die Erfindung wird im folgenden anhand einer Reihe spezieller Ausführungsbeispiele erläutert:The invention is explained below with the aid of a number of special exemplary embodiments:
Es wird ein Füllmittel, bestehend aus Polierpulver, Wasser und Gloiopeltis-Leim in einem Gewichtsverhältnis von 65%, 31% und 4% auf die Oberfläche einer 4 mm dicken Furnierplatte aufgebracht und nach dem Trocknen wird ein cremefarbener Oberflächenlack (Zinkweiß, Füllmittel, Nitrocellulose, Äthylacetat, Butylacetat, Methylalkohol und Toluol in einem Gewichtsverhältnis von 15%, 15%, 8%, 10%, 6%, 6% und 38% mit einem gleichen Volumen an Lackverdünnungsmittel verdünnt) erhalten. Nach dem Trocknen wird das Maserungsmuster eines Zelkovalholzes mit einer Druckfarbe auf der Grundlage von Acetylcellulose aufgedruckt, wobei.das Porenmuster des ο Zelkovalholzes mit einer Druckfarbe auf der Grundlage fjy von Acetyleellulose bedruckt wird, wobei 72 Teile an Acetylcellulose und 28 Teile Hydrochinon vorliegen. Sodann wird ot ein durchscheinender, harzartiger Überzug bestehend aus _» 100 Teilen trockenem Polyester-Kunstfetoff, 15 Teilen Styrol, 3* 1 Teil Methyläthylketonperoxid und 1 Teil Kobaltnaphthenat ~~* hierauf aufgebracht. Es erfolgt sodann 10 Minuten lang ein Erwrmen und Hätten bei 8O°c, wodurch eine Schmuckplatte - 8-A filler consisting of polishing powder, water and Gloiopeltis glue in a weight ratio of 65%, 31% and 4% is applied to the surface of a 4 mm thick veneer board and, after drying, a cream-colored surface varnish (zinc white, filler, nitrocellulose, Ethyl acetate, butyl acetate, methyl alcohol and toluene in a weight ratio of 15%, 15%, 8%, 10%, 6%, 6% and 38% diluted with an equal volume of paint thinner). After drying, the grain pattern of a covalent wood is printed with a printing ink based on acetyl cellulose, whereby the pore pattern of the covalent wood is printed with a printing ink based on acetyl cellulose, with 72 parts of acetyl cellulose and 28 parts of hydroquinone being present. Then a translucent, resin-like coating consisting of 100 parts dry polyester plastic, 15 parts styrene, 3 * 1 part methyl ethyl ketone peroxide and 1 part cobalt naphthenate is applied to it. This is followed by 10 minutes of heating and cooling at 80 ° C, which creates a decorative plate - 8-
- 8 mit Zelkoval-Holzmusterung ausgebildet wird.- 8 is formed with zelkoval wood pattern.
Nachdem eine braungefärbte ,OberMchenbehandlungsmasse, bestehend aus 16% Pigment, 44% Füllmittel, 15% Aikylphenol-Harzlack, 20% Lack, bestehend aus 1 Teil gekochtem öl und 2 Teilen Kopalharz, und 5% Benzin auf eine Spanplatte aufgebracht und getrocknet werden ist, wird ein entsprechendes Muster des Walnußholzes auf die Spanplatte unter Anwenden einer Druckfarbe auf der Grundlage von Acetylcellulose aufgedruckt, wobei die Druckfarbe 14 Teile Hydrochinon, 4 Teile Dammar-Pflanzengummi, 5 Teile Shellack, 20 Teile Phthalocyaninblau und 50 Teile einer Zylollösung mit 45% Acrylharz enthält. Das Porenmuster des Walnußholzes wird aufgedruckt und sodann der durchscheinende, harzartige überzug, bestehend aus 95 Teilen an der Luft torcknendem Polyesterharz, 1 Teil Methyläthylketonperoxid und 0,5 Teilen Kobaltnaphthenat auf die Oberfläche der Spanpiatee aufgebracht und nach dem Erhärten bei Raumtemperatur wird ' 12 Minuten lang auf 70°C zum Härten erhitzt, so daß sich eine Schmuckplatte mit 3-dimensional unregelmäßigem Muster auf der Oberfläche ergibt, wobei lediglich die Poren vertieft ausgeführt sind und der Rest der Oberfläche relativ dick ist.After a brown-colored, upper treatment mass, consisting of 16% pigment, 44% filler, 15% alkylphenol resin varnish, 20% varnish, consisting of 1 part boiled oil and 2 parts of copal resin and 5% gasoline are applied to a chipboard and dried, becomes a corresponding one Pattern of the walnut wood on the chipboard using an acetyl cellulose-based printing ink printed, the printing ink being 14 parts hydroquinone, 4 parts dammar vegetable gum, 5 parts shellac, 20 parts Contains phthalocyanine blue and 50 parts of a cylinder solution with 45% acrylic resin. The pore pattern of walnut wood is printed on and then the translucent, resin-like coating, consisting of 95 parts, scorching in the air Polyester resin, 1 part methyl ethyl ketone peroxide and 0.5 part cobalt naphthenate on the surface of the Spanpiatee applied and after hardening at room temperature is' heated for 12 minutes at 70 ° C for hardening, so that results in a decorative plate with a 3-dimensional irregular pattern on the surface, whereby only the pores are deepened and the rest of the surface is relatively thick.
Die gefärbten Holzmaserungsmuster werden in einer herkömm-The colored wood grain patterns are
2 liehen Druckfarbe aufdünnes Papier mit 80 g/m aufgedruckt, wobei die Maserung von Zelkovalholz angewandt wird. Es erfolgt das Aufdrucken der Porenmusterung des Holzes unter Anwenden der Drckfarbe, die aus 70 Teilen Acetylcellulose und 30 Teilen Hydrochinon besteht. Das Aufdrucken erfolgt auf eine Furnierplätte in einer Dicke von 3 mm (die Menge der Überzugsdruckfarbe beläuft sich auf 0,5 g/m ). Es2 borrowed printing ink printed on thin paper with 80 g / m, where the grain of zelkoval wood is used. The pore pattern of the wood is printed underneath Apply the printing ink, which is made from 70 parts of acetyl cellulose and 30 parts of hydroquinone. The printing takes place on a veneer plate with a thickness of 3 mm (the amount the coating ink is 0.5 g / m). It
erfplgt sodann ein Trocknen an der Luft. Es werden 50 g/m Anstrichfarbe, bestehend aus 100 Teilen Polyester-Kunststoff, 10 Teilen Styrol, 1 Teil Methyläthylketonperoxid und 1 Teil Kobaltnaphthenat aufgebracht. Nach einem Trocknen,bei Nor-air drying is then required. It becomes 50 g / m Paint, consisting of 100 parts polyester plastic, 10 parts of styrene, 1 part of methyl ethyl ketone peroxide and 1 part Cobalt naphthenate applied. After drying, at North
0098 25/11110098 25/1111
maltemperatur wird 10 Minuten auf 8O°C erftitzt und gehärtet. Hierdurch wird eine schmückende Furnierplatte mit dem Aussehen nach der Fig. 5 hergestellt, wobei jedoch hier der dem Porenmusterteil entsprechende Teil vertieft ist, während der restliche Anteil wie Naturholz konvex und uneben ausgeführt ist.painting temperature is heated to 80 ° C for 10 minutes and hardened. This produces a decorative veneer panel with the appearance of FIG. 5, but here the the part corresponding to the pore pattern part is deepened, while the remaining part is convex and uneven like natural wood is.
Es wird eine mit Papier überzogene Furnierplatte, die in ähnlicher Weise wie in ier Fig. 3 gezeigt ist, verarbeitet worden ist, mit 200 xj/m einer Anstrichfarbe überzogen, die aus 100 Teilen Polyester-Kunststoff und 10 Teilen Styrol besteht. Man überläßt sich sodann die Anordnung 1 Minute lang sich selbst bei Raumtemperatur. Im Anschluß hieran wird vermittels eines Resonanz-Transfer-Elektronenbeschleunigers der Firma General Electric Company Inc. mit 4 Mrad Strahlung die Anordnung bestrahlt. Hierdurch wird eine Platte gewonnen, die vertiefte Poren aufweist und weitestgehend einem natürlichen Holzprodukt entspricht.It becomes a paper-covered veneer board that is inserted into in a manner similar to that shown in Fig. 3, coated with 200 xj / m of a paint which consists of 100 parts polyester plastic and 10 parts styrene. The arrangement is then left to oneself for 1 minute long itself at room temperature. This is followed by a resonance transfer electron accelerator from General Electric Company Inc. irradiated the arrangement with 4 Mrad radiation. In this way a plate is obtained which has deepened pores and largely corresponds to a natural wood product.
Druckfarbe auf der Grundlage von Acetylcellulose - 70Acetylcellulose-based printing ink - 70
Hydrochinon 30Hydroquinone 30
durchsichtiges Polyesterharzclear polyester resin
Polyesterharz 100Polyester resin 100
Styrol 10Styrene 10
Methyläthylketonperoxid 1Methyl ethyl ketone peroxide 1
Kobaltnaphthenat 1Cobalt naphthenate 1
Die die Musterung ausbildende Druckfarbe wird für das Ausbilden eines gewünschten Musters auf Papier angewandt, das an der Platte befestigt wird. Sodann wird das Harz auf das Papier unter Ausbilden eines Films aufgebracht.The ink forming the pattern is used for forming of a desired pattern is applied to paper attached to the plate. Then the resin is applied to the Paper is applied to form a film.
Das Harz wird bei Normaltemperatur vorgehärtet und sodann bei 80°c nachgehärtet unter Ausbilden einer eine dreidimensionale schmückende Musterung aufweisenden Platte, wie sie in der Fig. 4 gezeigt ist.The resin is pre-cured at normal temperature and then post-cured at 80 ° C to form a three-dimensional decorative pattern having plate, as shown in FIG.
009825/1 1 1 1009825/1 1 1 1
Die Vorteile des erflndungsgemäBen chemischen Prägeverfahrens bestehen darin, daß es nicht mehr erforderlich ist, eine mechanische Anordnung, wie eine Prägewalze und dgl. anzuwen den, wie dies bei herkömmlichen Arbeitsweisen der Fall ist, und die Herstellungskosten sind wesentlich verringert, so daß sich eine entsprechende Ersparnis ergibt. Es ist eben falls möglich, das erfindungsgemäSe Verfahren im Zusammenhang mit gekrümmten und nicht ebenen Flächen wie z.B. Blumenvasen, Tischgeschirr usw. anzuwenden. The advantages of the chemical embossing process according to the invention are that it is no longer necessary to use a mechanical arrangement such as an embossing roller and the like, as is the case with conventional methods, and the production costs are significantly reduced, so that a corresponding one is required Savings result. It's just if possible to apply the erfindungsgemäSe procedures related to curved and non-planar surfaces, such as flower vases, tableware etc..
Da die harzartigen, das Härten inhibierenden oder das Härten beschleunigenden Mittel in die Druckfarbe und die Anstrich masse eingemischt sind, ergeben sich sehr günstige Ergebnisse. Since the resinous, hardening inhibiting or hardening accelerating agents are mixed into the printing ink and the paint composition, the results are very favorable.
Mit anderen Worten, es ist lediglich das Bedrucken mit der eingefärbten Masse un d das abschließende Oberziehen erforderlich, jedoch ist kein getrenntes Prägeverfahren notwen dig, und es ergeben sich keine Diskrepanzen zwischen den eingefärbten Mustern und den dreidimensional unterschiedlichen Musterungen.In other words, all that is required is the printing with the colored mass and the final coating , but no separate embossing process is necessary, and there are no discrepancies between the colored patterns and the three-dimensionally different patterns.
009826/1111009826/1111
Claims (5)