DE1919358A1 - Heat insulating material - Google Patents

Heat insulating material

Info

Publication number
DE1919358A1
DE1919358A1 DE19691919358 DE1919358A DE1919358A1 DE 1919358 A1 DE1919358 A1 DE 1919358A1 DE 19691919358 DE19691919358 DE 19691919358 DE 1919358 A DE1919358 A DE 1919358A DE 1919358 A1 DE1919358 A1 DE 1919358A1
Authority
DE
Germany
Prior art keywords
insulating material
material according
heat insulating
reinforcement layer
plastic film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE19691919358
Other languages
German (de)
Inventor
Clough Philip James
Steeves Robert Wesley
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Saint Gobain Abrasives Inc
Original Assignee
Norton Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Norton Co filed Critical Norton Co
Publication of DE1919358A1 publication Critical patent/DE1919358A1/en
Pending legal-status Critical Current

Description

595>2-69/Dr.v.B/Bru-Gase P-755
U.S.Ser.No. 722,226
filed: April 10, I968595> 2-69 / Dr.vB / Bru-Gase P-755
USSer.No. 722.226
filed: April 10, I968

Norton Company, 70 Memorial Drive, Cambridge,Mass.,Norton Company, 70 Memorial Drive, Cambridge, Mass.,

(V.St.A.)(V.St.A.)

Wärmeisolierendes MaterialHeat insulating material

Die vorliegende Erfindung betrifft ein wärmeisolierendes Material, insbesondere ein wärmeisolierendes Flächenmaterial für leichte Schutzbekleidung, Decken, Planen u.dgl., mit zwei Kunststoffolien, zwischen denen eine Verstärkungsschicht angeordnet ist und von denen mindestens eine auf der der anderen Kunststoffolie zugewandten Seite mit einer dünnen, im Vakuum aufgebrachten Metallschicht versehen ist.The present invention relates to a heat-insulating material, in particular a heat-insulating sheet material For light protective clothing, blankets, tarpaulins and the like., With two plastic films, between which a reinforcing layer is arranged and of which at least one on the the side facing the other plastic film is provided with a thin metal layer applied in a vacuum.

Es ist bekannt, wärmeisolierende Flächenmaterialien der oben angegebenen Art für leichte Wetterschutzbekleidung, Decken und Planen zu verwenden. Die bekannten wärmeisolierenden Flächenmaterialien haben sich zwar für manche* relativ eng begrenzte Zwecke als brauchbar erwiesen, konnten sich jedoch bisher nicht allgemein durchsetzen, was vermutlich auf die sich teilweise widersprechenden Anforderungen, die an solche Materialien gestellt werden, zurückzuführen ist, nämlich kleines Gewicht, geringe Dicke, niedrige Kosten einerseits und Dauerhaftigkeit, Festigkeit, guter Zusammenhalt der einzelnen Schichten und geeignete Textur.It is known, heat insulating sheet materials of the type specified above for light weather protection clothing, blankets and tarpaulins. The well-known heat insulating Flat materials have proven to be useful for some * relatively narrowly limited purposes, but have so far been able to do so not generally enforce what is presumably based on partially contradicting requirements that are placed on such materials, namely low weight, low thickness, low cost on the one hand and durability, Firmness, good cohesion of the individual layers and suitable texture.

909843/1330909843/1330

— On.- On.

Gemäss einem eigenen älteren Vorschlag besteht die Verstärkungsschicht aus einer webfreien Anordnung von sich im wesentlichen kreuzenden Pasern und beide Kunststoffolien sind auf ihrer der Verstärkungsschicht zugewandten Innenseite mit einer aufgedampften Metallisierung versehen.According to an older proposal of our own, the reinforcement layer consists of a web-free arrangement of itself essentially crossing pasers and both plastic films are on their inside facing the reinforcing layer with a provided with vapor-deposited metallization.

Im Gegensatz dazu ist bei dem vorliegenden wärmeisolierenden Material gegebenenfalls nur eine der beiden Kunststofffolien auf der der anderen Kunststoffolie zugewandten Seite mit einer dünnen im Vakuum aufgebrachten Metallschicht versehen, die Verstärkungsschicht enthält eine Kunststoffolie und der zwischen der Metallschicht und der Außenseite eirier der Folien befindliche Teil des Materials hat für Infrarotstrahlung im Wellenlängenbereich zwischen 30 000 und 90 000 8 eine 80# übersteigende Durchlässigkeit. In contrast to this, in the case of the present heat-insulating material, only one of the two plastic films may be present on the side facing the other plastic film with a thin metal layer applied in a vacuum, which The reinforcement layer contains a plastic film and the one between the metal layer and the outside of the film Part of the material has a permeability exceeding 80 # for infrared radiation in the wavelength range between 30,000 and 90,000 8.

Die beiden äußeren Kunststoffolien sind zwar selbsttragend, sie können sich jedoch gegebenenfalls schon bei massiger Zugbeanspruchung dehnen. Mit der Metallschicht auf der der anderen Folie zugewandten Seite der einen Folie ist die Verstärkung* schicht mit den Folien über deren wirksame Fläche verbunden.und mindestens eine, vorzugsweise beide Kunststoffolien haben für Infrarotstrahlung im Wellenlängenbereich zwischen 80 000 und 90 000 8 eine 80% übersteigende Durchlässigkeit.The two outer plastic films are self-supporting, but they can expand even under moderate tensile stress. With the metal layer on the side facing the other film side of a film is the gain * layer with the films about their effective area verbunden.und at least one, preferably both plastic films have in excess of infrared radiation in the wavelength range from 80,000 to 90,000 8 is a 80% Permeability.

Gemäss einer Ausgestaltung der Erfindung enthält die Verstärkungsschicht eine Kunststoffolie, die dicker ist als jede der beiden äusseren Kunststoffolien oder die Verstärkungsschicht besteht aus einer solchen Kunststoffolie.According to one embodiment of the invention, the contains Reinforcement layer a plastic film that is thicker than either of the two outer plastic films or the reinforcement layer consists of such a plastic film.

Bei einer speziellen Ausfuhrungsform der Erfindung ist nur eine der beiden äußeren Kunststoffolien metallisiert und die andere äußere Kunststoffolie hat ebenso wie die Verstärkungsschicht die oben angegebene Infrarotdurchlässigkeit.In a special embodiment of the invention only one of the two outer plastic films is metallized and the other outer plastic film has the same as the reinforcement layer the infrared transmittance given above.

909843/1330909843/1330

mm ^i-. mm ^ i-.

Gemäss einer Weiterbildung der Erfindung ist die Verstärkungsschicht perforiert, so daß zwischen den äußeren Folien Lufttaschen gebildet werden, die die Isolierfähigkeit des Materials erhöhen.According to a further development of the invention, the reinforcement layer is perforated so that between the outer foils Air pockets are formed, which increase the insulating capacity of the material.

Die äußeren Kunststoffolien stellen einen abriebfesten, dauerhaften Träger und Schutz für die reflektierende Metallschicht und Metallschichten dar und lassen praktisch die ganze Infrarotstrahlung vom menschlichen Körper zur innen angeordneten reflektierenden Metallschicht durch und übertragen die refle tierte Strahlung wieder zurück zum menschlichen Körper.The outer plastic films provide an abrasion-resistant, permanent support and protection for the reflective metal layer and metal layers and allow practically all of the infrared radiation from the human body to the inside reflective metal layer and transmit the reflected radiation back to the human body.

Vorzugsweise wird für das vorliegende Flächenmaterial Polyäthylen verwendet, das im Vakuum mit Aluminium bedampft worden ist. Die Kunststoffolie hat eine 80;i übersteigende Durchlässig keit für das ferne Infrarot, insbesondere des Viellenlängenbereichs zwischen 80 000 und 90 000 S, was dem Strahlungsmaximum bei der Temperatur des menschlichen Körpers entspricht, gleichzeitig ist das Reflexionsvermögen der Grenzfläche Kunststoff-Metall sowie der anderen Metalloberfläche für die vom Kunststoff durchgelassene Infrarotstrahlung sehr groß.Preferably, polyethylene is used for the present sheet material, which has been vapor-deposited with aluminum in a vacuum is. The plastic film has a permeability exceeding 80; i for the far infrared, in particular of the multi-length range between 80,000 and 90,000 S, which is the radiation maximum at the Temperature of the human body, at the same time is the reflectivity of the plastic-metal interface as well the other metal surface is very large for the infrared radiation transmitted by the plastic.

Bei einer bevorzugten Ausführungsform der Erfindung bilden zwei metallisierte äußere Polyäthylenfolien, deren metallisierte Oberflächen einander zugewandt sind, also innen liegen, mit einer Verstärkungsschicht aus Polyäthylen eine Schichtstruktur; die verstärkende Polyäthylenschient ist mit den beiden Metall schichten entweder durch Klebstoff oder durch Warmeverschweißung verbunden, so daß ein. einheitliches Produkt vorliegt.In a preferred embodiment of the invention form two metallized outer polyethylene foils, the metallized surfaces of which face each other, i.e. are inside, a layer structure with a reinforcement layer made of polyethylene; the reinforcing polyethylene rail is with the two metal layers either by glue or by heat welding connected so that a. uniform product is available.

Die Verstärkungsfolie soll dicker sein als die beiden äußeren Folien. Bei einer typischen Ausführungsform beträgt die Dicke der beiden äußeren Folien jeweils etwa 25/Um und die Dicke der Verstärkungsschicht etwa 50 ,um. Das gesamte Produkt ist dann etwa 100 ,um dick, so daß es eher gefaltet und auf einer kleineren Fläche bzw. in einem kleineren Raum aufbexiahrt werden 'The reinforcement film should be thicker than the two outer foils. In a typical embodiment, the thickness of the two outer foils each about 25 / um and the Thickness of the reinforcement layer about 50 µm. The entire product is then about 100 µm thick, making it more likely to be folded and on one side can be opened in a smaller area or in a smaller room '

'909843/1330'909843/1330

Ϊ - - IΪ - - I.

kann als es in dieser Grössenordnung mit den bekannten Materialien nicht möglich war.can than it in this order of magnitude with the known materials was not possible.

Die verstärkende Kunststoffschicht kann mechanisch oder thermisch mit Ausnehmungen versehen werden, z.B. indem man ein regelmässiges Lochmuster einschmilzt, wobei die offene Fläche 25 bis 75$ der Oberfläche betragen kann; die hierdurch gebildeten Lufttaschen erhöhen die Wärmeisolationsfähigkeit des Materials, ohne aaß dadurch die Festigkeit des Materials nennenswert beeinträchtigt wird.The reinforcing plastic layer can be mechanically or thermally provided with recesses, e.g. by a regular hole pattern melts down, with the open area Can be $ 25 to $ 75 of surface area; the resulting Air pockets increase the thermal insulation properties of the material, without aass, the strength of the material is noticeably impaired.

Bei einer anderen Ausführungsform der Erfindung ist nur eine der äußeren Folien Metallisiert. Die die Verstärkungsschicht bildende Folie besteht aus Polyäthylen, sie hat jedoch wie die äußeren Folien eine 80& übersteigende Durchlässigkeit für Infrarotstrahlung im Bereich von 80 000 bis 90 000 8. Das Material kann daher, trotzdem es nur eine Metallisierung aufweist, beidseitig verwendet werden. Um eine solche beidseitige Verwendung zu ermöglichen, ist es jedoch wichtig, daß die gegebenenfalls für die Verbindung der Verstärkungsschicht mit den Außenfolien verwendeten Klebstoffschichten aussergewöhnlich dünn und In another embodiment of the invention is only one of the outer foils is metallized. The film forming the reinforcement layer is made of polyethylene, but it has like the outer foils a permeability exceeding 80% for Infrared radiation in the range of 80,000 to 90,000 8. The material can therefore be used on both sides even though it only has one metallization. To such a mutual use To enable it, however, it is important that any adhesive layers used for connecting the reinforcing layer to the outer foils are exceptionally thin and

transparent sind. ·. .are transparent. ·. .

Bei der letzterwähnten Ausführungsform kann gewünschtenfalls die innere Oberfläche der unmetallisierten Aussenfolie bedruckt sein. Der Druck wird dann durch die Folie gegen Abrieb geschützt. Bei dieser Ausführungsform können ausserdem komplentäre Drucke, Farben oder Huster auf die Innenseite der unmetallijsierten Aussenfolie und auf die Verstärkungsfolie gedruckt werden, um einen komplizierten Zweifarbendruck auf einer einzigen Fläche zu vermeiden. Farbstoffe und Druckfarben sollen dabei je-* idoeh so gewählt werden, daß eine möglichst hohe DurchHssigkeitIn the latter embodiment, if desired the inner surface of the unmetallized outer film be printed. The pressure is then applied through the film against abrasion protected. In this embodiment, complementary Prints, colors or coughs on the inside of the unmetallized The outer film and the reinforcement film are printed to make an intricate two-color print on a single Avoid area. Dyes and printing inks should each * should be chosen so that the highest possible permeability

Ifür Infrarotstrahlung gewährleistet ist und die Farbstoffe mit der schlechtesten Durchlässigkeit sollen das offenste Muster biljden, um die übertragung der Strahlung möglichst wenig zu stören.If for infrared radiation is guaranteed and the dyes with the worst permeability should form the most open pattern, in order to disturb the transmission of the radiation as little as possible.

9098-43/1-3309098-43 / 1-330

In der Zeichnung ist das oben beschriebene Ausführungsbeispiel schematisch dargestellt. Bedruckt sind in diesem Falle dann also die Oberflächen der gelochten Verstärkungsfolie und der zweiten Aussenfοlie, die an die diese Folien verbindende dünne Kleberschicht angrenzen.In the drawing, the embodiment described above is shown schematically. Are printed in this So then fall the surfaces of the perforated reinforcement film and the second outer film, the one that connects these films adjoin a thin layer of adhesive.

Die oben erläuterten Ausführungsbeispiele können selbstverständlich in der verschiedensten i'/eise abgewandelt werden, ohne den Rahmen der Erfindung zu überschreiten. Man kann z.B. Polypropylen anstelle von Polyäthylen verwenden. Weiterhin ist es möglich, auch die Aussenseiten der Kunststoffolien zu metallisieren. Die Oberfläche oder Oberflächen können mit Farbstoffen gefärbt, bedruckt oder gemustert werden, solange diese eine hohe Infrarotdurchlässigkeit aufweisen.The exemplary embodiments explained above can of course be modified in a wide variety of ways, without going beyond the scope of the invention. For example, you can use polypropylene instead of polyethylene. Farther it is also possible to metallize the outside of the plastic film. The surface or surfaces can be coated with dyes colored, printed or patterned, as long as they have a high infrared transmission.

909843/ 1330909843/1330

Claims (1)

-ο--ο- Paten tansprüehe ■ Godfather tansprüehe ■ 1. nivärmeisolierendes I-iaterial, insbesondere Flächen- ^—J
material für leichte Schutzbekleidung, Decken, Planen u.dgl., mit mindestens zwei Xunststoffolien, zwischen denen eine Verstärkuno'sschicht angeordnet ist und von denen mindestens eine auf der der anderen Kunststoffolie zugewandten Seite mit einer dünnen, im Vakuum aufgebrachten Metallschicht versehen, dadurch gekennzeichnet , daß die Verstärkungsschicht eine Kunststoffolie enthält oder aus einer solchen besteht, und daß ! der zwischen der Metallschicht und der Außenseite mindestens einer [ der Folien befindliche Teil des i-iaterials eine 80?i übersteigende ' Durchlässigkeit für Infrarotstrahlung im VJellenlängenbereich zwi- j sehen 80 000 und 90 000 S hat. j1. Level-insulating material, especially surface- ^ - J
material for light protective clothing, blankets, tarpaulins, etc., with at least two plastic films, between which a reinforcement layer is arranged and of which at least one is provided on the side facing the other plastic film with a thin metal layer applied in a vacuum, characterized that the reinforcement layer contains or consists of a plastic film, and that! the part of the material located between the metal layer and the outside of at least one of the foils has a permeability exceeding 80% for infrared radiation in the wavelength range between 80,000 and 90,000 °. j 2.) Wärmeisolierendes Material nach Anspruch I9 j2.) Heat insulating material according to claim I 9 j dadurch gekennzeichnet , daß nur eine der bei den äußeren Kunststoffolien mit einer1 Metallschicht versehen "ist, und daß die Verstärkung schicht eine 80p übersteigende Durchlässig· keit für Infrarotstrahlung im ¥ellenlängenbereich von 80 ooo bis 90 000 8 hat.characterized in that only one of "is provided at the outer plastic films with a 1 metal layer, and that the reinforcing layer is a 80p exceeding Transparent · ness for infrared radiation in the ¥ avelength the range of 80 thousand to 90 000 8 has. 3·) Wärmeisolierendes Material nach Anspruch 1 oder ! 23 dadurch gekennzeichnet^ daß die Kunststoffolie der Verstärkungsschicht dicker als eine oder jede der äußeren Kunststoffolien ist.3 ·) Heat insulating material according to claim 1 or! 2 3 characterized ^ that the plastic film of the reinforcement layer is thicker than one or each of the outer plastic films. 4.) Wärmeisolierendes Material nach Anspruch 3S dadurch "gekennzeichnet, daß die Dicke der Verstärkungsschicht etwa 50 ,um und die Dicke der anderen Kunst- j stoffolien jeweils etwas 25/Um beträgt.4.) Heat-insulating material according to claim 3 S, characterized in that the thickness of the reinforcing layer is about 50 to and the thickness of the other Kunst- j stoffolien each about 25 / um. 909843/133C909843 / 133C j . 5·) viärmeisolierendes Material nach einem der vor-j. 5) thermal insulating material according to one of the j ■j ■ \ hergehenden Ansprüche, dadurch gekennzeichnet, I daß die Verstärkungsschicht perforiert ist. \ previous claims, characterized in that the reinforcement layer is perforated. : 6.) Wärmeisolierendes Material nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, j. daß alle Folien aus Polyäthylen bestehen.: 6.) Heat insulating material according to one of the preceding Claims, characterized in that j. that all foils are made of polyethylene. 7.) Wärmeisolierendes Material nach einem der Ansprüche 1 bis O3 dadurch gekennzeichnet , I daß alle Folien aus Polypropylen bestehen.7.) Heat insulating material according to one of claims 1 to O 3, characterized in that I that all films are made of polypropylene. 8.) Wärmeisolierendes Material nach einem der vor- ! hergehenden Ansprüche ,dadurch gekennzeich-I η e t , daß die Folien miteinander bzw. mit den Metallschichten I durch eine Wärmebehandlung miteinander verschweißt sind.8.) Heat insulating material according to one of the ! previous claims, characterized marked-I η e t that the foils are welded to one another or to the metal layers I by means of a heat treatment. ; 9·) Wärmeisolierendes Material nach Anspruch 2; 9 ·) Heat insulating material according to claim 2 oder Anspruch 2 und einem der Ansprüche 3 bis 8, d a d u r ch gekennzeichnet , daß die der Verstärkungsschicht zugewandte Seite aer unmetallisierten Kunststoffolie und /oder die dieser Kunststoffolie zugewandte Seite der Verstärkungsschicht mit einem bzw. zwei Färbstoffmustern versehen sind. or claim 2 and one of claims 3 to 8, d a d u r ch characterized in that that of the reinforcement layer facing side of the unmetallized plastic film and / or the side of the reinforcement layer facing this plastic film is provided with one or two dye patterns. 9.09843/19.09843 / 1 LeerseiteBlank page
DE19691919358 1968-04-18 1969-04-16 Heat insulating material Pending DE1919358A1 (en)