DE1783189B2 - PROCESS FOR MANUFACTURING COCK WITH LOW APPEARABLE SPECIFIC WEIGHT - Google Patents

PROCESS FOR MANUFACTURING COCK WITH LOW APPEARABLE SPECIFIC WEIGHT

Info

Publication number
DE1783189B2
DE1783189B2 DE19661783189 DE1783189A DE1783189B2 DE 1783189 B2 DE1783189 B2 DE 1783189B2 DE 19661783189 DE19661783189 DE 19661783189 DE 1783189 A DE1783189 A DE 1783189A DE 1783189 B2 DE1783189 B2 DE 1783189B2
Authority
DE
Germany
Prior art keywords
coal
coke
mixture
coking
highly volatile
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE19661783189
Other languages
German (de)
Other versions
DE1783189A1 (en
DE1783189C3 (en
Inventor
Hugo Dipl.-Ing. Dr.-Ing. 6680 Heinitz; Petak Heinrich Dipl.-Ing. 6603 Sulzbach Lohrmann
Original Assignee
Ausscheidung aus: 15 71 672 Saarbergwerke AG, 6600 Saarbrücken
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ausscheidung aus: 15 71 672 Saarbergwerke AG, 6600 Saarbrücken filed Critical Ausscheidung aus: 15 71 672 Saarbergwerke AG, 6600 Saarbrücken
Priority to DE19661783189 priority Critical patent/DE1783189C3/en
Priority claimed from DE19661783189 external-priority patent/DE1783189C3/en
Publication of DE1783189A1 publication Critical patent/DE1783189A1/en
Publication of DE1783189B2 publication Critical patent/DE1783189B2/en
Application granted granted Critical
Publication of DE1783189C3 publication Critical patent/DE1783189C3/en
Expired legal-status Critical Current

Description

Ergebnisse erzielt werden können.Results can be achieved.

Gemäß den im folgenden beschriebenen Ausgestaltungen der Erfindung können die Eigenschaften des Kokses mehr in diese oder in jene Richtung gelenkt werden.According to the configurations described below According to the invention, the properties of the coke can be steered more in this or that direction will.

Koks mit verhältnismäßig geringem scheinbaren spez. Gewicht und besonders hoher Reaktionsfähigkeit erhält man, wenn Flammkohle, Braunkohle, hochfiüchtige Kokskohle, Torf, mit bekannten Mitteln, z. B. durch Voroxydation, der Backfähigkeit beraubte hochfiüchtige Kokskohle oder ein unterhalb 4500C erzeugtes und wieder erstarrtes Schmelzprodukt aus einer solchen hochflüchtigen Kokskohle oder Koks oder Schwelkoks aus einer oder einer Mischung der genannten Kohlen oder eine Mischung von zwei oder mehreren der genannten Stoffe in feingemahlener Form mit 10 bis 40%, vorzugsweise 10 bis 20%, feingemahlenem Steinkohlenteerpech oder hochschmelzendem Bitumen aus der Erdölindustrie oder der Kohleextraktion vermengt wird und die Mischung auf eh.e Körnung von 100% unter 3 mm, mindestens 90% unter 2 mm und mindestens 50% unter 1 mm aufgemahlen, durch Stampfen auf 035 bis 1,05 t/m3 verdichtet und bei normaler Verkokungstemperatur verkokt wird.Coke with a relatively low apparent spec. Weight and particularly high reactivity are obtained when flame coal, lignite, highly volatile coking coal, peat, with known means, e.g. B. by pre-oxidation, the bakeability deprived of high volatile coking coal or a below 450 0 C produced and solidified melt product from such a highly volatile coking coal or coke or low temperature coke from one or a mixture of said coals or a mixture of two or more of the substances mentioned in finely ground Form is mixed with 10 to 40%, preferably 10 to 20%, finely ground coal tar pitch or high-melting bitumen from the petroleum industry or coal extraction and the mixture to a grain size of 100% below 3 mm, at least 90% below 2 mm and at least 50 % ground below 1 mm, compacted by tamping to 035 to 1.05 t / m 3 and coked at normal coking temperature.

Ein Koks von sehr geringem scheinbaren spez. Gewicht und extrem hoher Reaktionsfähigkeit wird erhalten, wenn Flammkohle, Braunkohle, hochfiüchtige Kokskohle, Torf, mit bekannten Mitteln, z. B. durch Voroxydation, der Backfähigkeit beraubte hochflüchtige Kokskohle oder ein unterhalb 4 SO0C erzeugtes und wieder erstarrtes Schmelzprodukt aus einer solchen hochflüchtigen Kokskohle oder eine Mischung aus den genannten Stoffen mit 10 bis 60% eines in bekannter Weise erzeugten, im Schüttgewicht besonders niedrigen Kokses oder Schwelkokses aus Flammkohle, Braunkohle, Torf oder hochflüchtiger Kokskohle und mit 10 bis 30%, vorzugsweise 10 bis 20%, feingemahlenem Steinkohlenteerpech oder hochschmelzendem Bitumen aus der Erdölindustrie oder der Kohleextraktion vermengt wird und die Mischung durch Stampfen auf 0,70 bis 0,95 t/m3 verdichtet und bei normaler Verkokungstemperatur verkokt wird.A coke of very little apparent spec. Weight and extremely high reactivity is obtained when flame coal, lignite, highly volatile coking coal, peat, by known means, e.g. B. by pre-oxidation, highly volatile coking coal deprived of the ability to bake or a melt product produced below 4 SO 0 C and solidified again from such a highly volatile coking coal or a mixture of the substances mentioned with 10 to 60% of a coke produced in a known manner, particularly low in bulk density or smoldering coke from flame coal, lignite, peat or highly volatile coking coal and with 10 to 30%, preferably 10 to 20%, finely ground coal tar pitch or high-melting bitumen from the petroleum industry or coal extraction is mixed and the mixture is tamped to 0.70 to 0.95 t / m 3 is compressed and coked at normal coking temperature.

Einen Koks mit geringem scheinbaren spez. Gewicht und mäßiger Reaktionsfähigkeit erhält man, wenn nicht- oder schwachbackende bituminöse Stoffe, wie Braunkohle oder Flammkohle, mit 10 bis 40% eines im Schüttgewicht niedrigen Kokses oder Schwelkokses aus Flammkohle, Braunkohle, Torf oder Fettkohle oder Mischungen dieser Stoffe und mit backender Kokskohle gemischt, die Mischung durch Stampfen auf 0,70 bis 0,95 t/m3 verdichtet und bei normaler Verkokungstemperatur verkokt wird.A coke with low apparent spec. Weight and moderate reactivity are obtained if non-baked or weakly baked bituminous substances, such as lignite or flame coal, are mixed with 10 to 40% of a coke with a low bulk density or low-density coke made from flame coal, lignite, peat or fat coal or mixtures of these substances and mixed with baking coking coal, the mixture is compacted by tamping to 0.70 to 0.95 t / m 3 and coked at normal coking temperature.

Die Erfindung unterscheidet sich demgemäß von dem vorbekannten Stand der Technik im ganzen durch die Erkenntnis, daß sich unter umfangreicher Verwendung von weniger wertvollen Ausgangsstoffen mit verkokungstechnisch extremen Eigenschaften und unter Anwendung des Stampfverfahrens verhältnismäßig wertvolle, beispielsweise für die Elektrometallurgie geeignete Kokse, erzeugen lassen, wobei deren Eigenschaften auch in einem interessanten Maße steuerbar sind.The invention accordingly differs from the previously known prior art as a whole by the Realization that with extensive use of less valuable starting materials with coking technology extreme properties and relatively valuable when using the ramming process, for example for electrometallurgy suitable cokes, can be produced, with their properties also to an interesting extent are controllable.

Nach »Glückauf« I960, S. 997 -1006, sind reaktionsfähige Kokse bereits bekannt. Sie sind jedoch nicht aus weniger wertvollen Ausgangsstoffen mit extremen Eigenschaften hergestellt. Auch Grosskinsky: »Handbuch des Kokereiwesens«, Bd. 1, 1955, S. 440, kann lediglich entnommen werden, daß scheinbare spezifische Koksgewichte von 0# bis 1,0 bekannt sind; Ober die Herstellung ist nichts gesagtAccording to "Glückauf" 1960, pp. 997-1006, are reactive Coke already known. However, they are not made from less valuable raw materials with extreme ones Properties made. Grosskinsky: "Handbuch des Kokereiwesens", Vol. 1, 1955, p. 440, it can only be seen that apparent coke specific weights of 0 # to 1.0 are known; Nothing is said about the production

Nach den DT-PS 3 67 893, 3 78 690 und 3 93 702 ist zwar die Verwendung weniger wertvoller Ausgangs-S stoffe mit extremen Eigenschaften — Braunkohle und Pech, gegebenenfalls noch weitere Kohle — bekannt, aber eicht zur Herstellung von Koks für die Stahlindustrie, sondern zur Herstellung von Koksbriketts für den Haushalt, deren Eigenschaften mit denen des in der Stahlindustrie benötigten Kokses nicht vergleichbar sind. In der DT-PS 6 77 418 geht es darum, höhersiedende aliphatische Kohlenwasserstoffe in den Ausgangsstoffen für eine Kohledestillation unterzubringen, um bei dieser Destillation mehr Benzol zu erhalten.According to DT-PS 3 67 893, 3 78 690 and 3 93 702 it is true that the use of less valuable output S substances with extreme properties - lignite and pitch, possibly other coal - known, but used to make coke for that Steel industry, but for the production of coke briquettes for the household, their properties with those of the coke required in the steel industry are not comparable. DT-PS 6 77 418 is about to accommodate higher-boiling aliphatic hydrocarbons in the raw materials for a coal distillation, to get more benzene in this distillation.

Der Koks ist Nebensache, über seine Eigenschaften wird nichts Wesentliches gesagt Die DT-PS 7 17 314 bezieht sich auf Briketts, die insbesondere in südlichen Ländern die seinerzeit dort immer noch im Haushalt verwendete und viel zu wertvolle Holzkohle ersetzen sollten. Auch hier sind die Eigenschaften der Erzeugnisse nicht vergleichbar. Die DT-PS 8 54 644 betrifft zwar die primäre Kokserzeugung unter Verwendung schlecht verkokbarer Kohlen und erwähnt auch, daß bei der üblichen Koksherstellung die zerkleinerte Kohle in die Kokskammern eingeschüttet oder eingestampft wird. Sie offenbart aber zwischen dem ersichtlich nur der Vollständigkeit halber erwähnten Stampfverfahren und der später besprochenen Verwendung schlechter verkokender Kohlen keinen Zusammenhang. Die — tatsächlich auch nie durchgeführte — Verwendung von Braunkohle oder vergleichbarer Kohle zur Herstellung von Koks unter Anwendung des Stampfverfahrens ist der DT-PS 8 54 644 nicht zu entnehmen. Erst recht nicht gibt die DT-PS 8 54 644 eine Lehre in Richtung der speziellen und angesichts der Ausgangsstoffe im ganzen erstaunlich guten Eigenschaften der nach der Erfindung darüber hinaus viel einfacher hergestellten Kokse. Nach der DT-PS 8 30 635 entsteht wiederum kein Koks, der dem erfindungsgemäßen Koks vergleichbar sein könnte.The coke is secondary, nothing essential is said about its properties. DT-PS 7 17 314 refers to briquettes that were still in the household, especially in southern countries used and should replace much too valuable charcoal. Here, too, are the properties of the products not comparable. DT-PS 8 54 644 concerns the primary coke production using poorly cokable coals and also mentions that in the usual coke production, the crushed coal in the Coking chambers is poured or pulped. But it reveals only the evident between the For the sake of completeness, the ramming method mentioned and the use discussed later are worse coking coals no connection. The - actually never carried out - use of Lignite or comparable coal for the production of coke using the ramming process not to be found in DT-PS 8 54 644. The DT-PS 8 54 644 certainly does not teach a lesson in the direction of the special and in view of the starting materials on the whole surprisingly good properties of the according to the invention in addition, cokes made in a much simpler manner. According to DT-PS 8 30 635 again no coke is produced, the could be comparable to the coke according to the invention.

Man will dort einerseits ein brauchbares Gas und andererseits einen brauchbaren Koks erzeugen, und zwar einen Koks, der in Gasgeneratoren zur Erhitzung von Kammern oder Retorten verwendbar ist. Dieses bescheidene Qualitätsergebnis konnte ebenfalls keinerlei Hinweis darauf geben, daß man bei Anwendung der erfindungsgemäßen Maßnahmen aus minderwertigen Ausgangsstoffen metallurgischen Koks herstellen kann. Die DT-PS 1 73 432 betrifft schließlich wieder abweichend von dem erfindungsgemäßen Produkt Gießereikoks, der, wie üblich, aus gut verkokbaren Kohlen, lediglich unter Zusatz von entfettendem, d. h. als Magerungsmittel dienenden, Koksgruß hergestellt werden soll. Weder die Ausgangsstoffe, in denen sich keine nichtbackenden Kohlen einerseits und keine Bindemittel andererseits finden, noch das Erzeugnis stimmen irgendwie mit dem erfindungsgemäßen Verfahren überein.They want to produce a usable gas on the one hand and a usable coke on the other, and a coke that can be used in gas generators for heating chambers or retorts. This A modest quality result could also give no indication of the fact that one was using the Measures according to the invention can produce metallurgical coke from inferior starting materials. DT-PS 1 73 432 finally relates to foundry coke again, in a departure from the product according to the invention, which, as usual, is made from charcoal that can easily be coked, only with the addition of degreasing, d. H. as Lean coke is to be produced. Neither the starting materials, which do not contain any non-baking coals on the one hand and no binding agents on the other hand find nor the product somehow agree with the method according to the invention match.

Ausführungsbeispiele
I.Embodiments
I.

Eine Mischung aus 85% oberster Flammkohle (unter Flammkohle wird eine junge, nicht- oder schwachbakkende hochfiüchtige Kohle verstanden im Gegensatz zu der eine hohe Dilatation aufweisenden Gasflammkohle) mit 40% flüchtigen Bestandteilen und aus 15% zerkleinertem Hartpech mit 50% flüchtigen Bestandtei-A mixture of 85% top flame coal (under flame coal is a young, non-bakery or weakly baked High volatile coal understood in contrast to the high dilation gas flame coal) with 40% volatile components and from 15% crushed hard pitch with 50% volatile components

Ien wurde auf eine Körnung von 100% < 3 mm, 90% < 2 mm und 55% < lmm aufgenr\hlen und in einer Stampfmaschine einer Stampfkokerei auf eine Verdichtung von 1,05 t/m3 gebracht Der erzeugte Stampfkuchen wurde in eine Koksofenkammer mit 181 Fassungsvermögen eingefahren. Die Verkokung wurde bei einer Heizzugtemperatur von 12000C durchgeführt. Der ga,re Kammerinhalt wurde auf übliche Weise ausgestoßen und gelöscht Der gedrückte Koks zeigte ein scheinbares spezifisches Gewicht von 0,90 und eine Reaktionsfähigkeit von 1,50 cm3/g seeIen was granulated to a grain size of 100% <3 mm, 90% <2 mm and 55% <1 mm and brought to a compression of 1.05 t / m 3 in a ramming machine of a stamped coking plant. The stamped cake produced was placed in a coke oven chamber retracted with a capacity of 181. The coking was carried out at a Heizzugtemperatur of 1200 0C. The g a , re chamber contents were ejected and quenched in the usual manner. The pressed coke showed an apparent specific gravity of 0.90 and a reactivity of 1.50 cm 3 / g see

II.II.

Eine Mischung aus 50% einer auf < 3 mm vermahlenen obersten Flammkohle mit 42% flüchtigen Bestandteilen, aus 30% Schwelkoks mix 14% flüchtigen Bestandteilen einer Körnung von 0—5 mm und einem Schüttgewicht von 0,35 t/m3, der aus einer feingemahlenen hochflüchtigen Kokskohle im Wirbelschichtverfahren hergestellt wurde, und aus 20% feingemahlenem Hartpech mit 50% flüchtigen Bestandteilen wurde innig vermengt und ohne weitere Aufmahlung in einer Stampfmaschine einer Stampfkokerei auf eine Verdichtung von 0,78 t/m3 gebracht. Hierauf wurde der erzeugte Stampfkuchen in eine Koksofenkammer mit 181 Fassungsvermögen eingefahren. Die Verkokung wurde bei einer Heiztugtemperatur von 12000C durchgeführt Der gare Kammerinhalt wurde auf übliche Weise ausgestoßen und gelöscht Der gedrückte Koks zeigte ein scheinbares spezifisches Gewicht von 0,68 und eine Reaktionsfähigkeit von 1,5 cm3/g see.A mixture of 50% of a top flame coal milled to <3 mm with 42% volatile components, of 30% smoldering coke mix 14% volatile components with a grain size of 0-5 mm and a bulk density of 0.35 t / m 3 , the one from a Finely ground highly volatile coking coal was produced in the fluidized bed process, and 20% finely ground hard pitch with 50% volatile components was intimately mixed and brought to a compression of 0.78 t / m 3 without further grinding in a ramming machine of a ram coking plant. The pound cake produced was then moved into a coke oven chamber with a capacity of 181. The coking was carried out at a Heiztugtemperatur of 1200 0 C. The gare chamber content is ejected in the usual manner and erased The pushed coke showed an apparent specific gravity of 0.68 and a reaction capacity of 1.5 cm 3 / g lake.

111.111

Eine Mischung aus 60% Kokskohle von 33% flüchtigen Bestandteilen und aus 20% Kohle von 19% flüchtigen Bestandteilen wird auf eine Körnung < 3mm vermählen und mit 20% eines im Wirbelbett erzeugten Kokses vom Schüttgewicht 030 der Körnung 0 -1 mm und des Gehalts an flüchtigen Bestandteilen von 8% innig vermengt in einer Stampfmaschine einer Stampfkokerei auf eine Verdichtung von 0,80 t/m3 gebracht, in einen Koksofen eingebracht und bei einer Heizzugtemperatur von 12000C verkokt Der fertige Koks wird normal gedrückt und gelöscht. Er besitzt eine Trommelfestigkeit von M 40 = 80, einen Abrieb M 10 = 8,0, ein scheinbares spezifisches Gewicht von 0,80 und eine Reaktionsfähigkeit von 0,50 cm3/g see.A mixture of 60% coking coal with 33% volatile components and 20% coal with 19% volatile components is ground to a grain size <3mm and with 20% of a coke produced in a fluidized bed with a bulk density of 030 with a grain size of 0-1 mm and a content of volatile content of 8% intimately mixed brought 3, is introduced into a coke oven and carbonized at a Heizzugtemperatur of 1200 0 C. The finished coke is pushed and normally deleted in a tamping machine, a tamped coke oven to a compression of 0.80 t / m. It has a drum strength of M 40 = 80, an abrasion M 10 = 8.0, an apparent specific gravity of 0.80 and a reactivity of 0.50 cm 3 / g see.

Claims (11)

Patentansprüche: 17Claims: 17 1. Verfahren zum Herstellen von Koks mit geringem scheinbaren spez. Gewicht, dadurch S gekennzeichnet, daß Flammkohle, Braunkohle, hoehflüchtige Kokskohle, Torf, der Backfähigkeit beraubte hoehflüchtige Kokskohle oder ein durch Erhitzung bis zu 4500C erzeugtes Schmelzprodukt aus einer solchen hochflüchtigen Kokskohle oder Koks oder Schwelkoks aus einer oder einer Mischung der genannten Kohle oder eine Mischung von zwei oder mehreren der genannten Stoffe in feingemahlener Form mit feingemahlenem Brikettpech, Hartpech aus Steinkohlenteer oder hochschmelzendem Bitumen aus der Erdölindustrie oder üer Kohleextraktion oder mit backender Kokskohle vermengt wird und die Mischung nachgemahlen, durch Stampfen verdichtet und bei normaler Verkokungstemperatur verkokt wird.1. Process for producing coke with low apparent spec. Weight, characterized in that flammable coal, brown coal, highly volatile coking coal, peat, highly volatile coking coal deprived of the ability to bake or a melt product produced by heating up to 450 0 C from such a highly volatile coking coal or coke or low-temperature coke from one or a mixture of the said coal or a mixture of two or more of the substances mentioned in finely ground form with finely ground briquette pitch, hard pitch from coal tar or high-melting bitumen from the petroleum industry or via coal extraction or with baking coking coal and the mixture is re-ground, compacted by tamping and coked at normal coking temperature. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß der Anteil an Steinkohlenteerpech, Erdölbitumen oder Kohleextraktbitumen in der Mischung 10-40%, vorzugsweise 10-20%, beträgt. 2. The method according to claim 1, characterized in that that the proportion of coal tar pitch, petroleum bitumen or coal extract bitumen in the Mixture is 10-40%, preferably 10-20%. 3. Verfahren nach Anspruch 2, dadurch gekennzeichnet, daß in der Einsatzmischung der Anteil der Körnung unter 3 mm 100%, der Anteil unter 2 mm mindestens 90% und der Anteil unter 1 mm mindestens 50% beträgt.3. The method according to claim 2, characterized in that the proportion of the feed mixture Grain size below 3 mm 100%, the proportion under 2 mm at least 90% and the proportion under 1 mm is at least 50%. 4. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß Flammkohle, Braunkohle, hoehflüchtige Kokskohle, Torf, der Backfäh'gkeit beraubte hoehflüchtige Kokskohle oder ein durch Erhitzung bis zu 45O0C erzeugtes Schmelzprodukt aus einer solchen hochflüchtigen Kokskohle oder eine Mischung aus den genannten Stoffen mit Koks oder Schwelkoks aus Flammkohle, Braunkohle, Torf, Eßkohle oder Kokskohle und mit feingemahlenem Hartpech, Brikettpech aus Steinkohlenteer oder hochschmelzendem Bitumen aus der Erdölindustrie oder aus der Kohlenextraktion vermengt wird und die Mischung durch Stampfen auf 0,70 bis 0,95 t/m3 verdichtet und bei normaler Verkokungstemperatur verkokt wird.4. The method according to claim 1, characterized in that flame coal, lignite, highly volatile coking coal, peat, the bakeability deprived of high volatile coking coal or a melt product produced by heating up to 450 0 C from such a highly volatile coking coal or a mixture of the substances mentioned is mixed with coke or smoldering coke made from flame coal, brown coal, peat, edible coal or coking coal and with finely ground hard pitch, briquette pitch made from coal tar or high-melting bitumen from the oil industry or from coal extraction and the mixture is tamped to 0.70 to 0.95 t / m 3 is compressed and coked at normal coking temperature. 5. Verfahren nach Anspruch 4, dadurch gekennzeichnet, daß der Kohleanteil der Mischung in der Körnung zu 100% unter 3 mm, zu mindestens 90% unter 2 mm und zu mindestens 50% unter 1 mm liegt.5. The method according to claim 4, characterized in that the carbon content of the mixture in the The grain size is 100% less than 3 mm, at least 90% less than 2 mm and at least 50% less than 1 mm. 6. Verfahren nach Anspruch 4 oder 5, dadurch gekennzeichnet, daß der Koks oder Schwelkoks aus Flammkohle, Braunkohle, Torf, Eßkohle oder Kokskohle eine Körnung von 100% unter 5 mm und ein Schüttgewicht von maximal 0,40 t/m3 hat.6. The method according to claim 4 or 5, characterized in that the coke or smoldering coke made of flame coal, lignite, peat, edible coal or coking coal has a grain size of 100% below 5 mm and a bulk density of a maximum of 0.40 t / m 3 . 7. Verfahren nach einem der Ansprüche 4 bis 6, dadurch gekennzeichnet, daß der Anteil an Koks oder Schwelkoks in der Mischung 10 bis 60% beträgt.7. The method according to any one of claims 4 to 6, characterized in that the proportion of coke or smoldering coke in the mixture is 10 to 60%. 8. Verfahren nach einem der Ansprüche 4 bis 7, dadurch gekennzeichnet, daß der Anteil an Brikettpech oder Hartpech aus Steinkohlenteer oder hochschmelzendem Bitumen aus der Erdölindustrie oder der Kohlenextraktion in der Mischung 10 bis 30%, vorzugsweise 10 bis 20%, beträgt.8. The method according to any one of claims 4 to 7, characterized in that the proportion of briquette pitch or hard pitch from coal tar or high-melting bitumen from the petroleum industry or the coal extraction in the mixture is 10 to 30%, preferably 10 to 20%. 9. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß Flammkohle, Braunkohle, Torf, der Backfähigkeit beraubte hochflüchtige Kokskohle oder ein durch Erhitzung bis zu 4500C erzeugtes9. The method according to claim 1, characterized in that flame coal, lignite, peat, highly volatile coking coal deprived of baking ability or one produced by heating up to 450 ° C. 189 Schmelzprodukt aus einer hochflüchtigen Kokskohle mit 5—30% Koks oder Schwelkoks aus Flammkohle, Braunkohle, Torf, Eßkohle oder Kokskohle und mit backender Kokskohle vermengt wird und die Mischung durch Stampfen auf 0,70 bis 0,95 t/m3 verdichtet und bei normaler Verkokungstemperatur verkokt wird. 189 Melted product from a highly volatile coking coal is mixed with 5-30% coke or low-temperature coke from flame coal, lignite, peat, edible coal or coking coal and with baking coking coal and the mixture is compacted by tamping to 0.70 to 0.95 t / m 3 and at normal coking temperature is coked. 10. Verfahren nach Anspruch 9, dadurch gekennzeichnet, daß der Kohleanteil der Mischung in der Körnung zu 100% unter 3 mm, zu mindestens 90% unter 2 mm und zu mindestens 50% unter 1 mm liegt10. The method according to claim 9, characterized in that that the carbon content of the mixture in the grain size is 100% below 3 mm, at least 90% is less than 2 mm and at least 50% less than 1 mm 11. Verfahren nach Anspruch 9 oder 10, dadurch gekennzeichnet, daß der Koks oder Schwelkoks aus Flammkohle, Braunkohle, Torf, Eßkohle oder Kokskohle eine Körnung von 100% unter 5 mm und ein Schüttgewicht von weniger als 0,40 t/m3 hat11. The method according to claim 9 or 10, characterized in that the coke or smoldering coke made of flame coal, lignite, peat, edible coal or coking coal has a grain size of 100% below 5 mm and a bulk density of less than 0.40 t / m 3 Die Erfindung betrifft ein Verfahren zum Herstellen von Koks mit geringem scheinbaren spezifischen Gewicht.The invention relates to a method of making coke with low apparent specificity Weight. Die Anforderungen an die Eigenschaften von Koksen hinsichtlich spezifischem Gewicht und Reaktionsfähigkeit richten sich nach dem Verwendungszweck.The requirements for the properties of cokes in terms of specific weight and reactivity depend on the intended use. Im Hochofen, vor allem im Kupolofen, wird im allgemeinen ein reaktionsschwacher Koks benötigt.In the blast furnace, especially in the cupola, a low-reactivity coke is generally required. Bei der Herstellung von Elektroden oder Kunstkohle stellt sich die Forderung nach einem sehr dichten und reaktionsträgen Koks.When manufacturing electrodes or charcoal, there is a need for a very dense and inert coke. Für die Elektrometallurgie wird übereinstimmend ein leichter Koks verlangt, der in einzelnen Fällen eine geringe Reaktionsfähigkeit haben darf, häufig jedoch eine extrem hohe Reaktionsfähigkeit haben muß.For electrometallurgy, a light coke is consistently required, which in some cases is a may have low responsiveness, but often must have extremely high responsiveness. Der Erfindung liegt die Aufgabe zugrunde, in den letzteren Rahmen fallende Kokse mit geringem scheinbaren spez. Gewicht und mindestens mäßiger Reaktionsfähigkeit herzustellen.The invention is based on the object, falling in the latter framework with little apparent spec. Weight and at least moderate reactivity. Gemäß der Erfindung wird Flammkohle, Braunkohle, hoehflüchtige Kokskohle, Torf, der Backfähigkeit beraubte hoehflüchtige Kokskohle oder ein durch Erhitzung bis zu 4500C erzeugtes Schmelzprodukt aus einer solchen hochflüchtigen Kokskohle oder Koks oder Schwelkoks aus einer oder einer Mischung der genannten Kohlen oder eine Mischung von zwei oder mehreren der genannten Stoffe in feingemahlener Form mit feingemahlenem Brikettpech, Hartpech aus Steinkohlenteer oder hochschmelzendem Bitumen aus der Erdölindustrie oder der Kohleextraktion oder mit backender Kokskohle vermengt und die Mischung wird nachgemahlen, durch Stampfen verdichtet und bei normaler Verkokungstemperatur verkokt.According to the invention, flame coal, lignite, highly volatile coking coal, peat, highly volatile coking coal that has been deprived of baking ability or a melt product produced by heating up to 450 0 C from such a highly volatile coking coal or coke or low-temperature coke from one or a mixture of said coals or a mixture of two or more of the substances mentioned in finely ground form with finely ground briquette pitch, hard pitch from coal tar or high-melting bitumen from the petroleum industry or coal extraction or mixed with baking coking coal and the mixture is re-ground, compacted by pounding and coked at normal coking temperature. Es wurde festgestellt, daß die Dichte von Koksen nicht, wie zunächst anzunehmen wäre, ausschließlich von der Verdichtung des Einsatzes und dem rohstoffbedingten Koksausbringen (Gehalt an fixem Kohlenstoff) abhängig ist: Wie weit die Substanz Klüfte im Koksofen bildet, also in dichteerhöhender Weise schrumpft, läßt sich theoretisch nicht voraussagen; es ist von Fall zu Fall und von Stoff zu Stoff verschieden. Die Reaktionsfähigkeit von Koksen gleicher Ausgarung (d. h. mit gleichem Restgehalt an flüchtigen Bestandteilen) ist zwar primär an die Rohstoffe gebunden, wird jedoch durch Form, Größe und Porosität der Koksstücke mitbestimmt und durch die Art des Verkokungsvorgangs hinsichtlich Dichte des Einsatzes und Heizzugtemperatur weiterhin beeinflußt wobei theoretisch nicht voraussehbareIt has been found that the density of cokes is not, as might initially be assumed, exclusive from the compression of the input and the raw material-related coke output (content of fixed carbon) depends on: How far the substance forms fissures in the coke oven, i.e. shrinks in a density-increasing manner theoretically not predicting oneself; it differs from case to case and from substance to substance. The responsiveness of cokes with the same fermentation (i.e. with the same residual content of volatile constituents) is primary bound to the raw materials, but is also determined by the shape, size and porosity of the coke pieces due to the nature of the coking process in terms of density of the insert and heating cable temperature influenced whereby theoretically unpredictable
DE19661783189 1966-10-01 Process for making coke with low apparent specific gravity Expired DE1783189C3 (en)