DE1771288C3 - - Google Patents
Info
- Publication number
- DE1771288C3 DE1771288C3 DE19681771288 DE1771288A DE1771288C3 DE 1771288 C3 DE1771288 C3 DE 1771288C3 DE 19681771288 DE19681771288 DE 19681771288 DE 1771288 A DE1771288 A DE 1771288A DE 1771288 C3 DE1771288 C3 DE 1771288C3
- Authority
- DE
- Germany
- Prior art keywords
- transfer
- pores
- film
- flowable
- color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Die Erfindung betrifft ein Verfahren zur Herstellung eines Übertragungsmaterials, das einen Kunstttoffilm mit einer Vielzahl von Poren und fließfähiger Übertragungsfarbe in diesen Poren aufweist, bei dem ein Gemisch aus Übertragungsfarbe, filmbildendem Polymerem und Lösungsmittel für das Polymere ausgebildet wird, eine Schicht dieses Gemisches auf einen Träger aufgebracht wird, das Lösungsmittel verdampft und der so gebildete Film von dem Träger abgezogen wird. Gegebenenfalls kann dieses Übertragungsmaterial eine Trägerschicht aufweisen, die nach der Herstellung auf die äußere Oberfläche des gebildeten Films aufgetragen wird.The invention relates to a method for producing a transfer material comprising a plastic film having a plurality of pores and flowable transfer paint in these pores, in which a mixture of transfer ink, film-forming polymer and solvent for the polymer is formed is, a layer of this mixture is applied to a support, the solvent evaporates and the film thus formed is peeled off from the support. Optionally, this transmission material have a backing layer which, after manufacture, is applied to the outer surface of the formed Film is applied.
Schwammartige Ubertragungsmaterialien, die eine poröse Harzmatrix und in den Poren dieser Matrix vorliegende Übertragungsfarbe aufweisen, sowie ihre Herstellung sind bekannt und ziemlich weit entwickelt (DT-AS 1213438). Die Mattschicht ist grundsätzlich eine Schicht aus einem filmbildenden Harz, das poröse Struktur aufweist, und in den Poren dieses schwammartigen Matrixmaterials wird ein fließfähiges Markierungsmaterial bzw. eine Übertragungsfarbe schwammartig festgehalten. Dieses Matrixübertragungsmaterial kann durch mehrere bekannte Verfahren auseebildet werden und das erhaltene ProduktSponge-like transfer materials that have a porous resin matrix and present in the pores of this matrix transfer color, as well as their Manufacture are known and quite well developed (DT-AS 1213438). The matte layer is fundamental a layer of a film-forming resin having a porous structure and in the pores of the same Sponge-like matrix material becomes a flowable one Marking material or a transfer color held in a spongy manner. This matrix transfer material can be formed by several known methods and the product obtained
kann eint zusätzliche Trägerschicht aufweisen.can have an additional carrier layer.
Bei dem bekannten Verfahren wird im allgemeinen die Matrixstruktur aus entsprechenden Rohmaterialien so ausgebildet, daß sie die fließfähige Farbe ein-In the known method, the matrix structure is generally made from appropriate raw materials designed in such a way that they incorporate the flowable color
schließt. Meist wird der Harzkörper der Matrix zu Beginn in einem Lösungsmittel für das Harz gelöst oder in einem Dispergiermittel dispergiert und die flüssigen oder sonstigen Farbmaterialien werden in dieser Lösung dispergiert. Die Lösung wird dann auf eine Un-closes. Usually the resin body of the matrix is initially dissolved or in a solvent for the resin dispersed in a dispersant and the liquid or other coloring materials are in this solution dispersed. The solution is then
terlage aufgebracht und die Matrixübertragungsschicht wird gebildet, indem lediglich die Materialien, die das Harz lösen oder solvatisieren, entfernt herden. Bei dieser Arbeitsweise sowie auch bei anderen bekannten Arbeitsweisen hat das erhaltene Produkt Poren, die im wesentlichen vollständig mit der fließfähigen Übertragungsfarbe gefüllt sind.applied and the matrix transfer layer is formed by only the materials, that dissolve or solvate the resin focusses away. In this procedure, as well as in other known procedures, the product obtained has pores, which is essentially completely with the flowable Transfer color are filled.
Es wurde nun gefunden, daß überraschenderweise eine bessere Schriftdichte während des Gebrauchs des Übertragungsmateriais unter normalen Druck- undIt has now been found that, surprisingly, better font density during use of the Transfer materials under normal pressure and
so Schreibbedingungen erreicht werden kann, wenn die ursprünglich in den Poren vorliegende Menge der Übertragungsfarbe vermindert wird.so writing conditions can be achieved when the the amount of transfer ink originally present in the pores is reduced.
Erfindungsgemäß wird daher ein verhältnismäßig großer Anteil des in den Poren der Matrix vorliegen-According to the invention, a relatively large proportion of the material present in the pores of the matrix is therefore
a5 den Materials als Teil der Herstellung eines Übertragungsmaterials vor dem ersten normalen Gebrauch dieses Übertragungsmaterials zum Drucken oder Schreiben entfernt. Im allgemeinen wird die gewünschte Druckqualität dann erhalten, wenn die Entfernung in einem Teil der Matrixschicht erfolgt, in dem eine wesentliche Erhöhung der durchschnittlichen Größe des Porenvolumens vorliegt.a 5 removed the material as part of the manufacture of a transfer material prior to the first normal use of that transfer material for printing or writing. In general, the desired print quality is obtained if the removal takes place in a part of the matrix layer in which there is a substantial increase in the average size of the pore volume.
In der DT-AS 1771287 wird ein ähnliches Übertragungsmaterial vorgeschlagen, in welchem eineA similar transmission material is used in DT-AS 1771287 suggested in which a
kleine Menge der Übertragungsfarbe aus den Poren entfernt ist, so daß die Einwirkung der Umgebungsbedingungen nicht bewirkt, daß flüssige Übertragungsfarbe an die Oberfläche des Obertragungsmaterials gepreßt wird.small amount of the transfer paint is removed from the pores, so that the exposure to environmental conditions does not cause liquid transfer ink to adhere to the surface of the transfer material is pressed.
Gegenstand der Erfindung ist ein Verfahren zur Herstellung eines Übertragungsmaterials, das einen Kunststoffilm mit einer Vielzahl von Poren und fließfähiger Übertragungsfarbe in diesen Poren sowie gegebenenfalls eine Trägerschicht aufweist, durch Aus-The invention is a method for producing a transfer material that has a Plastic film with a multitude of pores and flowable transfer paint in these pores as well as optionally has a carrier layer, by
bildung eines Gemisches aus Übertragungsfarbe, filmbildendem Polymerem und Lösungsmittel für das Polymere, Aufbringen einer Schicht dieses Gemisches auf einen Träger, Verdampfen des Lösungsmittels und Abziehen von dem Träger und gegebenenfalls Auf-Formation of a mixture of transfer ink, film-forming polymer and solvent for the Polymers, applying a layer of this mixture to a support, evaporating the solvent and Peel off from the carrier and, if necessary,
j0 tragen eines bleibenden Trägerfilms auf die äußere Oberfläche des gebildeten Films, das dadurch gekennzeichnet ist, daß man bei der Ausbildung des Gemisches aus Übertragungsfarbe, filmbildendem Polymerem und Lösungsmittel einen Bestandteil mit merklich geringerer Flüchtigkeit, der jedoch verdampfbar ist, zusetzt und aus dem wie vorstehend gebildeten, Übertragungsfarbe enthaltenden Kunststoffilm diesen Bestandteil mit geringerer Flüchtigkeit aus den Poren verdampft, so daß eine unvollständigej 0 wear a permanent carrier film on the outer surface of the film formed, which is characterized in that, in the formation of the mixture of transfer ink, film-forming polymer and solvent, a component with noticeably lower volatility, but which is vaporizable, is added and from the like The plastic film formed above and containing the transfer color evaporates this component with lower volatility from the pores, so that an incomplete
Füllung der Poren mit Übertragungsfarbe erreicht wird.Filling the pores with transfer paint is achieved.
Auf diese Weise wird ein Übertragungsmaterial erhalten, bei dem unter dem Schreibdruck ein Fluß von Übertragungsfarbe an die Oberfläche stattfindet.In this way, there is obtained a transfer material in which, under the writing pressure, a flow of Transfer color to the surface takes place.
Dieses Material ist daher relativ häufig benutzbar und liefert dichtere Schriftbilder.This material can therefore be used relatively frequently and provides denser typefaces.
Dies scheint darauf zurückzuführen zu sein, daß die teilweise gefüllten Poren, die erhebliche leere Be-This seems to be due to the fact that the partially filled pores, the considerable empty loading
reiche aufweisen, eine Entstehung einer beträchtlichen Bewegung und einer erheblichen kinetischen Energie der festen Markierungspigmente und gegebenenfalls der Farbstoffe ermöglichen, die anderweitig nicht erzielbar ist und die ermöglicht, daß sich eine größere Menge dieses Farbmittels zur Schreiboberfläche hin bewegt. Ein erfindungsgemäßes Übertragungsmaterial ist beim Schreiben und bei anderen Druckanwendungen, bei denen nur ein geringer Schreibdruck erzeugt wird, besonders brauchbar. Die Anwendung von geringem Schreibdruck ist im allgemeinen erwünscht, da hierdurch ein geringerer Verschleiß des Bands und eine geringere Einprägung des beschriebenen Materials erfolgt, so daß die Erfindung für die meisten Anwendungszwecke vorteilhaft ist.rich, a development of considerable movement and considerable kinetic Energy of the solid marking pigments and, if necessary, of the dyes allow the otherwise is not achievable and allows that a larger amount of this colorant to the writing surface moved towards. One transfer material of the present invention is in writing and others Printing applications that generate little writing pressure are particularly useful. the The use of low writing pressure is generally desirable, as this results in less wear of the tape and a lesser impression of the material described, so that the invention is advantageous for most purposes.
Vorzugsweise wird bei dem erfinduugsgemäßen Verfahren ein solcher Anteil des Bestandteils mit merklich geringerer Flüchtigkeit als das Lösungsmittel zugesetzt, daß nach Entfernung dieses Anteils das Volumen des Durchschnitts der Poren zu weniger als 85%, vorzugsweise zu etwa 75%, mit fließfähiger Übertragungsfarbe gefüllt ist.Preferably, in the case of the according to the invention Process such a proportion of the component having a markedly lower volatility than the solvent added that after removing this portion the volume of the average of the pores to be less than 85%, preferably about 75%, is filled with flowable transfer ink.
Mit Ausnahme der nachfolgend beschriebenen Einzelheiten können die erfindungsgemäßen Überschicht durch Aufbringen und Entfernen des Lösungsmittelshergestellt. Erfindungsgemäß ist dai Material von geringer, jedoch merklicher Flüchtigkeit, vorzugsweise ein synthetisches Kerosin (beschriebenWith the exception of the details described below, the overcoat according to the invention can prepared by applying and removing the solvent. The material is according to the invention of low but noticeable volatility, preferably a synthetic kerosene (described
in Rompp, Chemielexikon, 6. Aufl. 1966, Seite 3017, Stichwort »Isopar«). Es ist als Anteil im Rest der Mischung der Rohmaterialien enthalten und wird als Anteil des Restes der Mischung aufgebracht. Das Volumen des flüssigen Farbanteils der Mischung, ein-in Rompp, Chemielexikon, 6th edition. 1966, page 3017, keyword »Isopar«). It is and is included as a proportion in the remainder of the mixture of raw materials applied as a proportion of the remainder of the mixture. The volume of the liquid color component of the mixture, one
,o schließlich der Pigmente der Farbe, wird so gewählt, daß es etwa 3/4 des Volumens der Kombination von flüssiger Farbe und zugesetztem synthetischem Kerosin ausmacht., o finally the pigments of the color, is chosen to be about 3/4 of the volume of the combination of liquid paint and added synthetic kerosene.
Es ist besonders vorteilhaft, wenn man bei der Her-It is particularly advantageous if you
j5 stellung des Übertragungsmaterials die Porosität so einstellt, daß die Poren zumindest 2/3 des Gesamtvolumens des Übertragungsmaterials nahe der zum Schreiben zu verwendenden Oberfläche des Übertragungsmaterials ausmachen.j 5 position of the transfer material so adjusting the porosity, the pores at least 2/3 of of the total volume of the transfer material close to the writing surface to be used in the transfer material.
Die Zusammensetzung der Mischung von Rohmaterialien, aus der die Übertragungsschicht durch Aufbringen und Entfernen des Alkohollösungsmittels hergestellt wird, kann die folgende sein: 6 Gewichtsteile Nylon, 5 Gewichtsteile Holzmehl, 16 Gewichts- The composition of the mixture of raw materials, from which the transfer layer by applying and removing the alcohol solvent can be the following: 6 parts by weight nylon, 5 parts by weight wood flour, 16 parts by weight
tragungsmaterialien im allgemeinen wie in der oben I5 teile fließfähige Farbe (einschließlich Pigmenten), rib dth Alhift 1213438 5 Gihil hih Ki Z olltädiSupport materials in general as in the above I5 parts flowable paint (including pigments), rib dth Alhift 1213438 5 Gihil hih Ki Z olltädi
5 Gewichtsteile synthetisches Kerosin. Zur vollständigen Lösung oder Solvatisierung oder Dispersion aller Komponenten wird ausreichend denaturierter Äthylalkohol verwendet. Die flüssige Farbe ist die einzige Komponente in dieser Zusammensetzung, die mehr als einen Bestandteil aufweist. Die flüssige Farbe kann aus den folgenden Bestandteilen bestehen:5 parts by weight synthetic kerosene. To the full Solution or solvation or dispersion of all components becomes sufficiently denatured ethyl alcohol used. The liquid paint is the only component in this composition that is more as a component. The liquid paint can consist of the following components:
beschriebenen deutschen Auslegeschrift 1213438 beschrieben oder wie in der obengenannten Patentanmeldung beschrieben oder gemäß anderen Arbeitsweisen auf dem Gebiet der Matrix-Übertragungsmaterialien hergestellt werden. Im allgemeinen ist der Körper der Matrix oder schwammartigen Schicht gemäß der Erfindung Nylon, vermischt mit merklichen Mengen fein verteiltem Füllstoff. Nylon ist auf Grund seiner Festigkeit und Beständigkeit gegen die Einschneidewirkung unter dem direkten Aufschlag einer 35 Schwarzpigment 1686 (Farbstoff-Type bevorzugt. Es hat sich auch im allgemeinen als notwendig bei der Herstellung von Schreiibmaschinenbändern erwiesen, eine Trägerschicht vorzusehen, und diese Trägerschicht sollte im allgemeinen keineGerman Auslegeschrift 1213438 described or as described in the above-mentioned patent application or prepared according to other working methods in the field of matrix transfer materials. In general, the body of the matrix or sponge-like layer according to the invention is nylon mixed with appreciable amounts of finely divided filler. Nylon is due to its strength and resistance to the Einschneidewirkung under the direct impact of a 35 black pigment preferably 1686 (dye-Type. It has also been found in general to be necessary in the production of Schreiibmaschinenbändern to provide a backing layer, and this carrier layer generally should none
flüssige Farbe und keine anderen Bestandteile in einer 40 Nigrosinbase N, 2 Gewichtsteile ausreichenden Menge, um die Trägerschicht bezüglich ölsäure) des Einschneidens von auftreffenden Typen zu schwächen, enthalten. Bei Kohlepapieren schützt die Rückseitenschicht das darauf befindliche Papierblatt davor, von dem darunter befindlichen Übertragungsmedium 45 bedruckt zu werden.liquid paint and no other ingredients in an amount of 40 Nigrosine Base N, 2 parts by weight sufficient to weaken the carrier layer with respect to oleic acid) of the incision of impacting types. In the case of carbon papers, the backing layer protects the paper sheet located thereon from being printed on by the transfer medium 45 located below.
Dementsprechend kann Beispiel 1 der obengenannten deutschen Auslegeschrift 1213438 oder die speziellein Verbindung mit Fig. 1 der obengenanntenAccordingly, example 1 of the above-mentioned German Auslegeschrift 1213438 or the particularly in connection with Figure 1 of the above
und Ruß-Zusammensetzung)
2451L Schwarzpigment (Farbstoff- und Ruß-Zusammensetzung) Nigrosinoleat (1 Gewichtsteiland carbon black composition)
2451L black pigment (dye and carbon black composition) nigrosine oleate (1 part by weight
Methylviolett-BaseMethyl violet base
gemischte Octylester von ölsäuremixed octyl esters of oleic acid
Gewichtsprozent 6,0 10,0Weight percent 6.0 10.0
63,063.0
3,03.0
18,018.0
100,0100.0
In dem durch das obige Verfahren gebildeten Endprodukt beträgt das mittlere Porenvolumen nahe der Oberfläche, das von der Farbe während der normalenIn the final product formed by the above process, the mean pore volume is close to Surface that is different from the color during normal
-r ~ „ „ Schreibarbeitsgänge übertragen wird, zumindest das-r ~ "" writing jobs is transferred, at least that
Patentanmeldung beschriebene Ausführungsform als 5o Doppelte des Volumens der Nylon- und Füllstoffgrundsätzliche Beschreibung der spezielleren Aspekte phase und wahrscheinlich tatsächlich erheblich mehr der bevorzugten erfindungsgemäßen Ausführungs- "Patent application described embodiment as 50 double the volume of nylon and filler basic description of the more specific aspects phase and probably actually considerably more of the preferred embodiments of the invention "
form mit Ausnahme der dargelegten oder ersichtlichen Unterschiede angesehen werden. Ein Holzmehlfüllstoff ist auch hier der bevorzugte Füllstoff. Das 55 gemäß diesen beiden Verfahren erzeugte Band liefert nicht ganz so dichte Abbildungen, wie sie erwünscht sind, wenn es als Schreibmaschinenband in Schreibmaschinen, die mit nur geringem Aufschlagdruck arbeiten, verwendet wird, wie beispielsweise bei den be- 6o es in^der genannten Patentanmeldung beschrieben ist. kannten Schreibkopf-Schreibmaschinen. Um die Das Papier bewegt sich durch eine Kammer, in der erhaltene Schriftdichte merklich zu erhöhen, werden das Lösungsmittel, der Äthylalkohol, ziemlich rasch die folgenden Arbeitsweisen während der Herstellung verdampft wird. In der gleichen Kammer, jedoch mit des Schreibmaschinenbandes angewendet. viel geringerer Rate, wird auch das synthetische Kero-form with the exception of the differences outlined or evident. Wood flour filler is also the preferred filler here. The 55 according to these two produced tape method provides not quite as dense pictures as they are desirable when it is used as a typewriter ribbon in typewriters which operate with little impact pressure, such as at the loading 6o it ^ said patent application is described. knew stylus typewriters. The paper moves through a chamber in which the resulting font density is noticeably increased, the solvent, the ethyl alcohol, is evaporated fairly quickly during manufacture using the following procedures. In the same chamber but used with the typewriter tape. much lower rate, the synthetic kero-
In die Mischung von Rohmaterialien, aus der das 65 sin, das gegenüber Äthylalkohol schwerer flüchtig ist, Übertragungsmaterial hergestellt wird, wird eine verdampft. Die Fördergeschwindigkeit der Papierun-Flüssigkeit von verhältnismäßig niedriger Flüchtigkeit terlage durch die Kammer braucht nicht merklich hereineebracht. Dann wird eine feste Übertragung- abgesetzt zu werden. Es besteht kein wirklicher ZweiIn the mixture of raw materials from which the 65 sin, which is less volatile than ethyl alcohol, Transfer material is produced, one is vaporized. The speed of conveyance of the paper un-liquid Of relatively low volatility, the material through the chamber does not need to be noticeably brought in. Then a fixed transfer will be discontinued. There is no real two
ais das Zweifache dieses Volumens.ais twice this volume.
Die weitere Behandlung kann im wesentlichen die gleiche wie die in der DAS 1213438 oder DAS 1771 287 sein, mit Ausnahme der hier beschriebenen oder offensichtlichen Unterschiede. Die obige Mischung von Nylon und den anderen Rohmaterialien für die Übertragungsschicht wird auf eine Arbeitsunterlage aufgebracht, die vorzugsweise Papier ist, wieFurther treatment can be essentially the same as that in DAS 1213438 or DAS 1771 287, with the exception of differences described or obvious here. The above mix of nylon and the other raw materials for the transfer layer is placed on a work pad applied, which is preferably paper, such as
fei, daß der Äthylalkohol weitgehend verdampft wird, während das synthetische Kerosin in großen Mengen zurückbleibt. Anschließend wird eine Trägerschicht in der gewünschten Dicke aus zusätzlichem Nylon, wie in Beispiel 1 der DAS 1213438 und in der DAS 1771287 beschrieben ist, im allgemeinen bis zu einer Trockendichte in der Größenordnung vcn etwa 0,0125 rim aufgebracht. Diese Schicht kann aufgebracht werden, nachdem die gesamte Papierunterlage durch die Auftragsvorrichtung unter Bildung des festen Matrixmaterials hindurchgeführt wurde, indem die Papierunterlage dann als Vorratsrolle zum Eingang des Beschichters gebracht und erneut durch den Beschichter geführt wird, wobei dieses Mal die Auftragsvorrichtung Nylon in einem Gemisch von Äthyl- ι alkohol und Wasser auf die obere Seite des Matrix-Übertragungsmaterials aufträgt.fei that the ethyl alcohol is largely evaporated, while the synthetic kerosene remains in large quantities. This is followed by a backing layer in the desired thickness of additional nylon, as in Example 1 of DAS 1213438 and in DAS 1771287 is described, generally to a dry density in the order of magnitude of about 0.0125 rim applied. This layer can be applied after the entire paper backing through the applicator forming the solid Matrix material was fed through, then the paper backing as a supply roll to the entrance of the coater and passed through the coater again, this time the application device Nylon in a mixture of ethyl alcohol and water on the upper side of the matrix transfer material applies.
Die erfindungsgemäßen Übertragungsmaterialien ergeben eine 25%ige Erhöhung der Intensität der Bildfarbe im Vergleich zu anderen vergleichbaren Übertragungsmaterialien bei dem gleichen Schreibdruck. Durch sorgfältige Analysen wurde festgestellt, daß die Porengröße und andere derartige Faktoren in den erfindungsgemäßen Produkten im wesentlichen die gleiche Größe und Anordnung haben, die für ein Produkt erwartet würden, das aus dem flüssigen Gemisch mit einer Menge an nichtflüchtiger Flüssigkeit hergestellt ist. die das gleiche Volumen wie uie Kombination von flüssiger Farbe und Kerosin aufweist. Das Volumen des Durchschnitts der Poren ist nach der oben beschriebenen bevorzugten Ausführungsform zu etwa 3/4 gefüllt. Die Eigenschaften bezüglich der wiederholten Verwendung als Schreibmaschinenfarbband sind gut. Sorgfältige Analysen haben gezeigt, daß fast nur Spurenmengen an synthetischem Kerosin in dem Endprodukt verbleiben und somit, daß der Mechanismus, der zu der dichteren Schrift führt, nur durch die physikalische Konfiguration der Poren und nicht durch eine Änderung in dem Farbträger auf Grund des Vorhandenseins des synthetischen Kerosins hervorgerufen wird.The transfer materials according to the invention give a 25% increase in the intensity of the image color compared to other comparable transfer materials at the same writing pressure. Through careful analysis, it has been found that the pore size and other such factors in the products of the present invention are essentially the same size and arrangement as would be expected for a product made from the liquid mixture with an amount of non-volatile liquid. which has the same volume as the combination of liquid paint and kerosene. The volume of the average of the pore is filled according to the above described preferred embodiment to about 3/4. The repeated use properties as a typewriter ribbon are good. Careful analysis has shown that almost only trace amounts of synthetic kerosene remain in the final product and thus that the mechanism leading to the denser writing is only through the physical configuration of the pores and not through a change in the color vehicle due to the presence of the synthetic kerosene.
Häutsächlich auf Grund der verhältnismäßig größeren Löslichkeit von Nylon gegenüber der relativ geringeren Löslichkeit des Farbträgen:, wenn beide in Äthylalkohol vorliegen, ergibt sich eine Schichtung, wie in Fig. 3 der obengenannten DAS 1 771287 und auch in der D AS 1213 438 erörtert ist. Die Schichtung der Poren und des Harzkörpers ist derart, daß mehr Poren und daher mehr Farbe sich an der Oberfläche des Übertragungsmaterials befinden, oie die Oberfläche sein soll, von der auf Papier oder eine andere aufnahmefähige Oberfläche geschrieben wird. Wie bereits erwähnt wurde, weist die bevorzugte erfindungsgemäße Ausführungsform an der Oberfläche, von der aus geschrieben wird, auch ein durchschnittliches Porenvolumen auf, das zumindest doppelt so groß wie das Volumen der kontinuierlichen Phase ist.Mainly due to the relatively greater solubility of nylon compared to the relatively lower solubility Solubility of the paints: if both are present in ethyl alcohol, the result is a stratification, as discussed in Fig. 3 of the above-mentioned DAS 1 771287 and also in D AS 1213 438. The layering the pores and the resin body is such that more pores and therefore more color appear on the surface of the transfer material, oie the surface should be, from which on paper or some other receptive Surface is written. As already mentioned, the preferred according to the invention Embodiment on the surface from which it is written, also an average pore volume that is at least twice the volume of the continuous phase.
Zwei Faktoren, die bei der obengenannten deutschen Patentanmeldung eine Rolle spielen, werden bei dieser bevorzugten Ausführungsform verwendet. Der eine Faktor ist, daß keine Farbe spontan zu der Oberfläche des Produkts gepreßt wird, selbst wenn dieses extremen Bedingungen hoher Feuchtigkeit ausgesetzt wird. Wie in der genannten DT-AS 1 771 287 dargelegt ist, ist Nylon hygroskopisch und quillt durch die absorbierte Feuchtigkeit, wodurch Farbe an die Oberfläche gepreßt wird. Ein schmutziges Schriftbild und schlechte Eigenschaften bezüglich der Handhabung chetungTwo factors that play a role in the above German patent application are in used in this preferred embodiment. One factor is that there is no color spontaneously on the surface of the product is pressed even when exposed to extreme conditions of high humidity will. As set out in the aforementioned DT-AS 1 771 287 Nylon is hygroscopic and swells due to the moisture it absorbs, causing paint to surface is pressed. Dirty typeface and poor handling properties chetung
5 S 5 p
10 . Da erfindungsgemaß große 10 . Since the invention is large
e?nffcnSdurch die Entfernung des Matenals mit n.e? nffcn S by removing the material with n.
SKlSKSiSer durchschnitte Tat sich jedoch in der Praxis gezeigt, daß SKISKSiSer average has shown in practice that
srL kleine Mengen von Farbe in gewissen FallensrL small amounts of paint in certain cases
Sweise um ein in der Praxis durchfuhrbares und S Afbi auf Papier oder ein anderesS wise about something that can be carried out in practice and S Afbi on paper or another
beiden lassen sich leicht trennen.the two are easy to separate.
Das erzeugte Produkt wird naturhch je nach Wunsch geschnitten und verpackt. Die bevorzugte Form ist fin Schreibmaschinenband für eine SchreibmSiine mit nur einem geringen Schreibaufschlag. ?ur Verwendung wird daher das Übertragungsmate-5a gesch"uztund8auf Spulenoder Rollen zur Verwendung als Schreibmaschinenband aufgerollt. Es is ersichtlich, daß der Bestandteil mit niedriger Flüchtigkeit nicht ein synthetisches Kerosin sein muß. um die Erfindung durchzuführen. Eine Anzahl von Materialien mit verhältnismäßig ««^r RudiUg. keit die die Fähigkeit besitzen, aus dem gebildeten festen Matrixmaterial ausgetrieben zu werden, wurden mit guten Ergebnissen verwendet. Im allgemeinen ist es jedoch bevorzugt, daß der zugegebene Bestandteil nicht hochgradig mit dem flussigen Anteil der , fließfähigen Farbe mischbar ist, da die Entfernung des Bestandteils dann in einer Umgebung, Ae nur verhältnismäßig schlecht zum Verdampfen fuhrt.erfolgen kann. Der Bestandteil mit niedriger Flüchtigkeit SlHe mit der fließfähigen Farbe schwach mischbar sein so daß er zu Beginn die im wesentlichen ebenfalls von dieser Farbe besetzten Poren ^Ht Die Entfernung von Farbe zur Erzielung von merklich an Farbe verarmten Poren kann auch durch andere Arbeitsweisen wie beispielsweise durch eine Druckbehandlung « in einer Schichtanordnung mit einem absorbierenden 55 Material, vorgenommen werden. Eine solche Druckbehandlung wurde ebenfalls durchgeführt. Be. Laboratoriumsversuchen unter Anwendung von Druck und einer absorptionsfähigen Oberfläche zum Abziehen 6o verhältnismäßig großer Mengen der flussigen Farbe in einem Matrix-Übertragungsmatenal wurde eine Erhöhung der Schriftdichte, wie gemäß der obigen Beschreibung der Erfindung erwartet, erzielt.The product produced is naturally cut and packaged as required. The preferred form is a typewriter tape for a typewriter with only a small write charge. Thus, for use, the transfer material 5a is protected and 8 rolled up on spools or reels for use as typewriter tape. It will be appreciated that the low volatility ingredient need not be synthetic kerosene to practice the invention. A number of materials having relatively "" R gels which have the ability to be driven out of the solid matrix material formed have been used with good results, but in general it is preferred that the added ingredient not be highly miscible with the liquid portion of the flowable paint Since the removal of the constituent can then only lead to evaporation relatively poorly in an environment Ht The removal of color to achieve a noticeable amount of color e depleted pores can also be done by other operations such as by a pressure treatment "in a layer arrangement with an absorbent material 55. Such a pressure treatment was also carried out. Be. Laboratory tests using pressure and an absorbent surface to peel off relatively large amounts of the liquid paint in a matrix transfer material resulted in an increase in font density as expected in accordance with the above description of the invention.
Aus den obigen Ausführungen ist ersichtlich daß die hier beschriebenen Merkmale nicht auf die Herbeschränkt sind, wie sie in den -*"·· f-From the above it can be seen that the features described here are not restricted to the ones described in the - * "·· f -
Stei'UngSIOIIII UUWiui.n. ., , .. Incline SIOIIII UUWiui.n. .,, ..
sehen Auslegeschriften 1213438 oder 1771287 beschrieben ist. Insbesondere werden die Matrix-Übcr-see interpretation documents 1213438 or 1771287 described is. In particular, the matrix transfer
tragungsmaterialien häufig durch Aufbringen eines Lehre erfolgen. Auch braucht die Farbe nicht zu alleiWear materials are often done by applying a teaching. Also, the color does not need to be alone
fließfähigen Gemischs von Rohmaterialien auf eine Zeiten flüssig zu sein. So kann dje Farbe ein Gel odeflowable mixture of raw materials to be fluid at a time. So the color can be a gel or a gel
Unterlage, die ein Papier oder eine harzartige Unter- eine andere unter den Umgebungsbedingungen festiA pad that holds a paper or a resinous substrate in place under the ambient conditions
lage sein kann, hergestellt, wobei die Unterlage dau- Substanz sein, solange sie bei Beaufschlagung mit dei ernd als Teil des Endprodukts verbleibt. Die Einstel- 5 Drucken beim Schreiben oder Drucken fließt. Es islocation can be produced, with the pad dur- ing substance as long as it is exposed to the dei ernd remains as part of the final product. The settings 5 printing when writing or printing flows. It is
lung der relativen Menge von Flüssigkeit in den bei ersichtlich, daß die Schichtung der Poren zwischen dedevelopment of the relative amount of liquid in the case can be seen that the stratification of the pores between de
solchen Verfahren gebildeten Poren kann auf ver- Schreiboberfläche und der Trägerschicht kein für di<Pores formed in such a process cannot be used on the writing surface and the carrier layer for di <
schiedenen Wegen gemäß der obigen technischen Erfindung wesentlicher Faktor ist.different ways according to the above technical invention is an essential factor.
Claims (3)