DE1669311A1 - Sprayable coating agent for the production of corrosion protection coatings to be melted - Google Patents
Sprayable coating agent for the production of corrosion protection coatings to be meltedInfo
- Publication number
- DE1669311A1 DE1669311A1 DE19681669311 DE1669311A DE1669311A1 DE 1669311 A1 DE1669311 A1 DE 1669311A1 DE 19681669311 DE19681669311 DE 19681669311 DE 1669311 A DE1669311 A DE 1669311A DE 1669311 A1 DE1669311 A1 DE 1669311A1
- Authority
- DE
- Germany
- Prior art keywords
- coating agent
- production
- melted
- corrosion protection
- sprayable coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
Verspritzbares Beschichtungsmittel zur Herstellung aufzuschmelzender Korrosionsschutzüberzüge Die Erfindung bezieht sich auf ein versgritzbares Beschichtungsmittel zur Herstellung aufzuschmelzender, dickschichtiger Korrosionsschutzüberzü:ge. Das Beschichtungsmittel ist in erster Linie zur Herstellung von Überzügen. auf Metallen bestimmt.Verspritzbares coating compositions for producing aufzuschmelzender corrosion protection coatings The invention relates to a coating agent for producing versgritzbares aufzuschmelzender, high build Korrosionsschutzüberzü: ge. The coating agent is primarily used for the production of coatings. determined on metals.
Der Schutz durch Überzüge auf Metalloberflächen durch-Kunststoffe ist bekannt. Alle bekannten Verfahren weisen jedoch je nach dem Verwendungszweck gewisse Nachteile auf. So lassen sich lösungsmittelhaltige Lacke, vor allem als Einbrennlacke, nur in begrenzter Schichtstärke auftragen. Um bei dicken Schichten eine blasenfreieOberfläche zu erzielen, war es erforderlich, die Lacke so hoch zu pigmentieren, daß der entstandene Film meist den Anforderungen nicht genügte.The protection provided by coatings on metal surfaces through plastics is known. However, all known methods have depending on the intended use certain disadvantages. Solvent-based paints, especially as Stoving enamels, only apply in a limited layer thickness. To with thick layers To achieve a bubble-free surface it was necessary to make the lacquers so high pigment that the resulting film mostly did not meet the requirements.
Ferner ist es bekannt, dicke Schichten mit lösungsmittelfreien Isocyanat- bzw. Epoxysystemen herzustellen.. Diese Werkstoffe sind aber verhältnismäßig kostspielig, so daß ihre Anwendung für viele Zwecke nicht wirtschaftlich ist. Auch bereitet die Verarbeitung Schwierigkeiten, da diese Stoffe gewöhnlich als Zweikomponentenmaterial Verwendung finden. Bekannt ist es auch, preiswerte Überzüge auf der Basis hochpigmentierter, weichmacherhaltiger PVC-Massen herzustellen. Diese Beschichtungenzeigten aber den Nachteil, daß bei Dicken bis ca. 500w eine schlechte Haftung auftrat und daß diese Schichten aufgrund der sehr hohen Pigmentierung und der verwendeten Grundmaterialiengegen mechanische-Beanspruchungen sehr-empfindlich waren. Diese Eigenschaft wird durch oft ungenügende Ausgelierung bei niederer Temperatur noch verstärkt:.It is also known to apply thick layers with solvent-free isocyanate or to produce epoxy systems .. These materials are relatively expensive, so that their application is not economical for many purposes. Also prepare the Processing difficulties, as these fabrics are usually two-component materials Find use. It is also known to use inexpensive coatings the basis of highly pigmented, plasticizer-containing PVC compounds. These Coatings, however, had the disadvantage that at thicknesses of up to approx Adhesion occurred and that these layers due to the very high pigmentation and The base materials used are very sensitive to mechanical stresses was. This property is often caused by insufficient gelation at low temperatures reinforced:
Schließlich ist ein verspritzbares, aus einer wässrigen Dispersion eines chemikalienbeständigen, thermoplastischen Kunststoffes mit einem Bindemittel und Zusätzen bestehendes Beschichtungsmittel zur Herstellung aufzuschmelzender Korrosionsschutzüberzüge bekannt geworden. Diese bekannten Be-' schichtungsmittel lieferten aber nur Überzüge relativ geringer Schichtdicke Aufgabe der Erfindung ist ein verspritzbares Beschichtungsmittel zur Herstellung aufzuschmelziander Korrosionsschutzüberzöge, die wie die bekannten Mittel Bindemitteldispersionen und/oder Bindemttellösungen und/oder Bndemittelemulsionen sowie Pigmente und Füllstoffe enthalten, welche die geschilderten Mängel der bekannten Beschichtungsmittel nicht aufweisen, also gut haftend dickschichtig auftragbar sind, bei denen die Aufbringung keine Schwierigkeiten bereitet, die blasenfrei sind und mechanisch allen erforderlichen Beanspruchungen gewachsen sind.Finally, a sprayable, made from an aqueous dispersion of a chemical-resistant, thermoplastic with a binding agent and additions of existing coating agents for the production of anti-corrosive coatings to be melted on known. However, these known coating agents only provided coatings relatively small layer thickness The object of the invention is a sprayable coating agent for the production of fused-on anti-corrosion coatings, like the known ones Means binder dispersions and / or binder solutions and / or binder emulsions as well as pigments and fillers, which the described shortcomings of the known Do not have coating agents, i.e. they can be applied in thick layers with good adhesion, in which the application does not cause any difficulties, which are bubble-free and mechanically are able to withstand all necessary stresses.
Diese Aufgabe wird erfindungsgemäß dadurch gelöst, daß ein oder mehrere in den Mitteln nicht lösliche thermoplastische Kunststoffe in pulverisierter Form mit Korngrößen möglichst nicht über 150 /u zugesetzt sind. Der verwendete thermoplastische Kunststoff kann an sich in anderen Iösungsmitteln-löslich sein. Er soll aber nicht in den für das Verfahren verwendeten Mitteln gelöst oder stark gequollen werden.According to the invention, this object is achieved in that one or more thermoplastics which are insoluble in the agents are added in powdered form with grain sizes not exceeding 150 microns if possible. The thermoplastic plastic used can in itself be soluble in other solvents. However, it should not be dissolved in the agents used for the process or be severely swollen.
Durch das Verfahren gemäß der Erfindung Wird auch erreicht, daß der pulverförmige Kunststoff wie ein Pigment in die Masse eingearbeitet wird und beim Einbrennvorgang seine Bindemitteleigenschaften entwickelt.The method according to the invention also achieves that the powdery plastic like a pigment is incorporated into the mass and when The baking process develops its binder properties.
Die Temperatur beim Einbrennvorgang muß also auf jeden Fall über dem Schmelzpunkt des Kunststoffes liegen.The temperature during the baking process must definitely be above that Melting point of the plastic.
Die Zerkleinerung muß so weit vorgenommen werden,- daß der Kunststoff beim Verspritzen, z.B. bei Anwendung einer "Airless-Pistole" nicht die Düse verstopft. Es ist anderergeits nicht erforderlich, unter 10 @u Korngröße zu zerkleinern. Ein Beschichtungsmittel gemäß der Erfindung kann beispielsweise wie folgt hergestellt werden: 25 Teile einer handelsüblichen Kunstharzdispersion, 10 Teile des pulverisierten thermoplastischen Kunststoffes und 65 Teile verschiedener Pigmente und Füllstoffe werden in" einem Behälter mit einem ächnellrührer so lange gerührt, bis eine gleichmäßige Verteilung aller Bestandteile gegeben ist.The comminution must be carried out to such an extent that the plastic does not clog the nozzle when it is sprayed, for example when using an "airless gun". On the other hand, it is not necessary to shred grain sizes below 10 @u. A coating agent according to the invention can be produced, for example, as follows: 25 parts of a commercially available synthetic resin dispersion, 10 parts of the pulverized thermoplastic and 65 parts of various pigments and fillers are stirred in a container with a constant stirrer until all components are evenly distributed is.
Die Viskosität kann, wenn erforderlich, mit 1 - ¢ Gew.-l Wasser reguliert werden.The viscosity can, if necessary, be regulated with 1 ¢ wt. L of water will.
Als zuzusetzende Kunststoffe haben sich verschiedene Vinylpolymerisate als besonders geeignet erwiesen.Various vinyl polymers have proven to be the plastics to be added proved to be particularly suitable.
Claims (1)