DE1569086C3 - Pre-coating compound for polyester films - Google Patents
Pre-coating compound for polyester filmsInfo
- Publication number
- DE1569086C3 DE1569086C3 DE19641569086 DE1569086A DE1569086C3 DE 1569086 C3 DE1569086 C3 DE 1569086C3 DE 19641569086 DE19641569086 DE 19641569086 DE 1569086 A DE1569086 A DE 1569086A DE 1569086 C3 DE1569086 C3 DE 1569086C3
- Authority
- DE
- Germany
- Prior art keywords
- polyester
- film
- adhesion
- acid
- polyester films
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Die vorliegende Erfindung bezieht sich auf Vorbeschichtungsmassen für Polyesterfolien, insbesondere solche, die die Haftung zusätzlich aufgebrachter Beschichtungen verbessern.The present invention relates to precoat compositions for polyester films, in particular those that ensure the adhesion of additionally applied coatings improve.
Wegen ihrer Transparenz, Haltbarkeit und Festigkeit sind Folien aus Polyestern, z. B. aus Polyäthylenterephthalat, als Trägermaterialien für verschiedene Schichten sehr geschätzt. Die Folien sind wasserabstoßend und gehen verhältnismäßig schlecht eine chemische Verbindung ein, so daß ihre Beschichtung Schwierigkeiten bereitet. Zur Verbesserung der Haftung zwischen aufgebrachter Schicht und Polyesterunterlage sind bereits physikalische und chemische Verfahren angewendet worden, jedoch waren die damit erzielten Erfolge gering. So ist z. B. vorgeschlagen worden, die Folien mit einem Sandstrahl zu behandeln, um so ihre Oberfläche aufzurauhen und zu vergrößern.Because of their transparency, durability and strength, films made of polyesters, e.g. B. made of polyethylene terephthalate, highly valued as a carrier material for various layers. The foils are water-repellent and enter a chemical compound relatively poorly, so that their coating Causes difficulties. To improve the adhesion between the applied layer and the polyester base Physical and chemical processes have already been used, but they were with it successes achieved low. So is z. B. has been proposed to treat the foils with a sandblast so as to roughen their surface and to enlarge.
Nach diesem Verfahren wird die Haftung zwar geringfügig verbessert, jedoch sind die dafür aufgewandten Kosten hoch und das Verfahren führt darüberhinaus zu einer Verminderung der Transparenz. Eine chemische Behandlung der Folien mit Säuren oder Oxydationsmitteln bewirkt zwar, daß die Folien sich leichter beschichten lassen, doch wird der Erfolg durch die während des Beschichtungsvorgangs einwirkende Wärme und Reibung wieder verringert.Adhesion is slightly improved after this process, but the used for it are Costs are high and the process also leads to a reduction in transparency. A chemical treatment of the foils with acids or oxidizing agents causes the foils can be coated more easily, but success is achieved through the during the coating process heat and friction are reduced again.
Auf dem Gebiet des Verklebens zweier vorgebildeter Oberflächen, von denen mindestens eine aus Polyäthylenterephthalat besteht, ist es bekannt, die Oberflächen mit einem flüssigen Film aus Dichloressigsäure oder einer konzentrierten Lösung einer anderen Chloressigsäure zu überziehen und aufeinander zu pressen (deutsche Auslegeschrift 10 03 889).In the field of bonding two pre-formed surfaces, of which at least one is made Polyethylene terephthalate, it is known, the surfaces with a liquid film of dichloroacetic acid or a concentrated solution of another chloroacetic acid and coated on top of each other to press (German Auslegeschrift 10 03 889).
Um die Haftung von Beschichtungen auf der Oberfläche von Polyesterfolien zu verbessern, ist die technische Lehre für das Verkleben von vorgebildeten Oberflächen aus Polyäthylenterephthalat jedoch nicht zu verwenden, da die Aufgabenstellung völlig anders ist.To the adhesion of coatings on the surface Improving polyester films is the technical teaching for gluing preformed ones However, surfaces made of polyethylene terephthalate should not be used, as the task is completely different is.
In der belgischen Patentschrift 6 21521 werden Schichten mit antistatischer Ausrüstung geschützt, die sich auf der Rückseite eines photographischen Silberfilms befinden. Den Schichten selbst kommt keine haftvermittelnde Rolle zu, da auf ihnen keine weiteren Überzüge aufgebracht werden. Da sie sogar auf Grund möglicher Eigenfarbe während der Entwicklung des Silberfilms entfernt werden müssen, um unerwünschte Farbverschiebungen zu vermeiden, mischt man ihnen alkalilösliche Harze bei, die den Entwicklungsvorgang erleichtern.In the Belgian patent 6 21521 layers with an antistatic finish are protected, the are on the back of a silver photographic film. None of the shifts themselves come Adhesion-promoting role too, since no further coatings are applied to them. Since they even on Because of possible inherent color must be removed during the development of the silver film in order to avoid undesired To avoid color shifts, alkali-soluble resins are mixed in, which facilitate the development process facilitate.
In der USA.-Patentschrift 28 93 896 wird ein Verfahren beschrieben, daß die chemische Behandlung von Polyesterfolien mit Halogenfettsäuren in einem Lösungsmittel ohne Zusatz von Bindemitteln beinhaltet. US Pat. No. 28 93 896 describes a process that involves chemical treatment of polyester films with halogen fatty acids in a solvent without the addition of binders.
Ein großer Nachteil dieses Verfahrens besteht darin, daß die einmal erzielte »Aufrauhung« der Oberfläche, die das ursprünglich geringe Haftvermögen erhöht, durch die während des Beschichtungsvorgangs einwirkende Wärme und Reibung wesentlich beeinträchtigt wird.A major disadvantage of this method is that once the "roughening" of the Surface that increases the originally low level of adhesion due to the coating process acting heat and friction is significantly impaired.
Folien, die auf die oben angegebene Weise vorbehandelt wurden, sind außerdem nur begrenzt lagerfähig, weil die Aktivierung der Oberfläche langsam abklingt, und müssen deshalb sofort weiterverarbeitet werden.Films that have been pretreated in the manner specified above can also only be stored for a limited time, because the activation of the surface slowly decays and must therefore be processed further immediately will.
In der USA.-Patentschrift 27 76 219 und in der beligischen Patentschrift 6 13 317 werden Substrierungen für konventionelle Silberhalogenid enthaltende Gelatineschichten beschrieben. In der ersten Schrift handelt es sich um Vorstriche aus perhalogenierten Essigsäuren, Gelatine und Cellulosenitrat für Filmträger auf Basis Celluloseester, in der zweiten sind Rezepturen auf Polyäthylenterephthalat als Filmträger abgestimmt, wobei vorzugsweise Trifluoressigsäure, Polyvinylidenchlorid und Gelatine zur Anwendung gelangen.In the United States patent specification 27 76 219 and in the Belgian patent specification 6 13 317 are subbing for conventional gelatin layers containing silver halide. In the first Scripture is about primers made of perhalogenated acetic acids, gelatine and cellulose nitrate for film base based on cellulose ester, in the second are recipes based on polyethylene terephthalate as Film support matched, preferably trifluoroacetic acid, polyvinylidene chloride and gelatin for Application.
Die sich aus der andersartigen Aufgabenstellung, nämlich Haftvermittlung zwischen organophilen FiImträgern und hydrophilen Silberhalogenid/Gelatineschichten, ergebende neue technische Lehre ist jedoch für die Lösung der dieser Erfindung zu Grunde liegenden Aufgabe nicht zu verwenden.The result of the different task, namely the mediation of adhesion between organophilic film carriers and hydrophilic silver halide / gelatin layers, however, emerging new technical teaching is not to be used for the solution of the problem on which this invention is based.
Aus der älteren deutschen Auslegeschrift 12 39 851From the older German interpretation 12 39 851
4.0 ist bekannt, daß die Behandlung von Polyäthylenterephthalatfilmträgern mit Trichloressigsäure auch ohne Zusatz von Chromsäure als Oxidationsmittel eine Erhöhung der Oberflächenaffinität bewirkt. Harze, wie z. B. Nitrocellulose, Celluloseacetat und Polyacrylsäureester, können den Trichloressigsäurelösungen beigefügt und auf diese Weise direkt auf der Oberfläche verankert werden. Gegenüber dieser grenzt sich die vorliegende Erfindung in der Wahl ihrer Harze bzw. Lösungsmittel und in der mit PoIyesterfolie reagierenden Substanzen ab.4.0 is known to treat polyethylene terephthalate film supports with trichloroacetic acid causes an increase in the surface affinity even without the addition of chromic acid as an oxidizing agent. Resins such as B. nitrocellulose, cellulose acetate and polyacrylic acid esters, the trichloroacetic acid solutions attached and anchored directly on the surface in this way. Compared to this The present invention is limited in the choice of its resins or solvents and in that with polyester film reacting substances.
Gemäß der Erfindung wird die Haftung von Beschichtungen auf der Oberfläche von Polyesterfolien dadurch verbessert, daß man die Polyesteroberfläche zuerst mit einer Vorbeschichtungsmasse beschichtet, die aus einer Lösung aufgebracht wird, die in einem Lösungsmittel eine mit der Polyesterfolie reagierende Substanz und außerdem ein Harz enthält, das sowohl mit der Polyesteroberfläche als auch mit der später aufzubringenden Schicht verträglich ist.According to the invention, the adhesion of coatings to the surface of polyester films improved by first coating the polyester surface with a precoat, which is applied from a solution which reacts with the polyester film in a solvent Substance and also contains a resin, which both with the polyester surface and with the later to be applied layer is compatible.
6" Die erfindungsgemäße Vorbeschichtungsmasse ist dadurch gekennzeichnet, daß sie als mit Poiyesterfolien reagierende Substanz eine oder mehrere aus der Gruppe Trichloressigsäure, Monochloressigsäure, Trifluoressigsäure oder Benzophenon und als film- 6 "The precoating compound according to the invention is characterized in that it contains one or more from the group of trichloroacetic acid, monochloroacetic acid, trifluoroacetic acid or benzophenone as the substance that reacts with polyester films and
bildendes Harz Polyvinylbutyral, Polyvinylformal, Celluloseacetatbutyrat von niedriger Viskosität, Polyvinylchlorid oder Poly-(methylvinyläther-monobenzyimaleatester) enthält.forming resin polyvinyl butyral, polyvinyl formal, cellulose acetate butyrate of low viscosity, polyvinyl chloride or poly (methyl vinyl ether monobenzyimaleate ester) contains.
3 43 4
Die erfindungsgemäße Vorbeschichtungsmasse Das nachfolgende Beispiel dient dazu, die vorlie-The Precoating Compound According to the Invention The following example serves to illustrate the present
kann auf die Polyesterfolie durch Eintauchen, Auf- gende Erfindung zu erläutern,can be dipped onto the polyester film to explain the invention,
bürsten, Aufsprühen, Aufbringen mit Walzen oder . . .brushing, spraying, application with rollers or. . .
mit Hilfe einer Auftragsvorrichtung aufgebracht und "applied with the help of an application device and "
anschließend getrocknet werden. 5 Eine Polyäthylenterephthalatfolie wurde mit derare then dried. 5 A polyethylene terephthalate film was with the
Die vorteilhaft erhöhte Haftung, die die erfindungs- folgenden Lösung beschichtet:The advantageously increased adhesion that coats the solution according to the invention:
gemäße Vorbeschichtungsmasse gegenüber Polyester- Polyvinylbutyral Igappropriate precoating compound compared to polyester-polyvinylbutyral Ig
folien besitzt, wurde mit Hilfe eines einfachen Klebe- Benzylalkohol 100 ccFoils, was made with the help of a simple adhesive benzyl alcohol 100 cc
streifentests festgestellt. Dazu wird ein selbstkleben- Mischung aus Methylethylketon strip tests noted. This is done using a self-adhesive mixture of methyl ethyl ketone
der Klebestreifen gleichmäßig und fest auf die Schicht io und denaturiertem Alkohol (2:1) 20 ccthe adhesive strip evenly and firmly on the layer of io and denatured alcohol (2: 1) 20 cc
aufgeklebt und mit einem plötzlichen Ruck nach oben Trichloressissäure 12 g entfernt. Läßt sich die Schicht dabei nicht von derglued on and with a sudden jerk upwards trichloressic acid 12 g removed. If the layer cannot be removed from the
Polyesteroberfläche abtrennen, dann ist die Haftung Die erzielte Haftung war ausgezeichnet. Auch mitSeparate the polyester surface, then the adhesion. The adhesion achieved was excellent. Also with
mit ausgezeichnet zu bewerten. Polyvinylformal erhielt man sehr gute Resultate.to be rated as excellent. Polyvinyl formal gave very good results.
Claims (1)