DE1541772B2 - DEVICE FOR DETERMINING THE MAGNETIC SPECIFIC SIZES OF FERROMAGNETIC SAMPLES USING A CHANGING FIELD - Google Patents

Description

The invention relates to a device for determining the magnetic parameters (Induction, intensity of magnetization, field strength and magnetic reversal loss) of ferromagnetic Samples in the form of rods with, for example, circular or rectangular or ring-shaped Cross section in a slowly changing alternating field, e.g. B. an electromagnet or electrical steel panels - or ribbons with small thickness and large width in a rapidly changing alternating field, z. B. an open magnetizing coil by means of an induction double measuring coil and a field strength double measuring coil.

In the field of magnetic metrology of magnetic materials, there are two types of material characteristic of the measuring method to be used:

I. Materials with a permanent magnet character,
II. Materials with a soft magnetic character.

I. Permanent Magnet Materials

The basis is the hysteresis loop with the characteristic values:

B _max = maximum induction at H _max = maximum field strength,
Bj _max = maximum intensity of magnetization

at H _max ,

B _r = remanence at H = O,
H _ic = coercive field strength at B _t = 0,
H _c = coercive field strength at B = 0.

For a magnetic material with a hard character, rods with a round or rectangular or ring-shaped cross-section are clamped between the large-area poles of an electromagnet and slowly magnetized up and down using known methods wound around the sample with w turns and connected to a flux meter, whose deflection voltage u _F is proportional to the time integral of the induction voltage

u _F

= J u _B dt = Yi-F (B, - B _{f = 0} ) '

and thus also proportional to the respective induction B or its increase or decrease.

The second variable H is detected directly on the sample by means of a Hall probe which supplies a voltage u _H proportional to the field. The hysteresis loop B = / (H) is written by connecting the u _F and u _H voltages to an XF recorder.

Is the% value of the fluxmeter a proportional voltage derived from the Hall probe voltage u _H c · u _H counter switched, the intensity of magnetization B ₁ occurs according to the "-

B ₁ = B- μΗ

According to the French Patent 1,145,316 it is shown how by means of simple field strength coil W ₁₁ · F ₁₁ above and below the strip or panel, the field strength H and by means of a simple, the band or panel surrounding induction coil w _g · F _B, the Induction B can be determined.

The measuring equations for the stresses are:
1. Field strength H

F ₁₁ ■ dy ^ H / dt

or

\ u _H · dt = w _u - F _n ■ B ₀ = w _H ■ F ₁₁ ■ μ ₀ Η.

2. Induction B
u _B = w _B · F _B ■
or

dB

German

Su _B dt = w _B F _B -B ^ w ₁₃

B ₁ ),

where B ₀ = air induction, B _; = Intensity of magnetization.

According to another known method, the voltage u _{L of} an air-core coil next to the sample is switched in a correspondingly large manner opposite the induction coil voltage u _B , so that the internal induction (intensity of the magnetization) B is also maintained.

The measurement accuracy of the known methods depends more or less on the measurement accuracy of the Hallsondenkreises and on the agreement of the air field strength of the field coil in the sample. Experience has shown that the accuracies are not very high. Above all, the Hall probe often needs to be checked and corrected. The field coil has a relatively small cross-section so that it can be brought close enough to the sample. An improvement in the accuracy of the measured values in the stability of the measuring coil combination and in the interchangeability of the samples is achieved in a device for determining the magnetic parameters according to the type described in that, according to the invention, both the induction double measuring coils and the field strength double measuring coils the sample in a homogeneous Surround the area in a ring, the coil system of at least three concentric coils with the cross-sections F ₁ , F ₂ , F ₃ and the number of turns W ₁ , ^W 2> ^W 3 ( ^{counting from the} inside to the outside) and that the condition for the field coil pair is W ₁ = W ₂ and for the coil pair of the intensity of the magnetization, the condition W ₁ F ₁ = W ₃ F _{3 is} met and that the second coil F ₂ W _{2 of} the first coil F ₁ W ₁ and to measure the intensity of the field strength measurement Magnetization, the third coil F ₃ W _{3 of} the first coil F ₁ W ₁ is switched on.

The double measuring coil pairs are connected to one another on one side in such a way that they are connected in opposite directions and their final voltage is equal to the difference between the individual coil voltages.

The winding areas of the individual coils and the associated voltages are from the inside out

W ₁ F ₁ ,

1. U ₁ «2

The cross-section of the tape or panel is F ₀ .

In order to obtain the list of the voltage _{equations, the induction B must be split into the parts B 0} and Bi , then the equations are:

dß ₀ dB, -

2. U ₂ = W ₂ F ₂ - £ - + W ₂ F ₀ - ^ -

3. _{Ui =}

dB ₀

_o _

From the counter connection of w ₂ - we then get

₁ and W ₁ - w ₃

1. Field strength μΗ = B ₀

u ₂ - u, = [W ₂ F ₂ - W ₁ F ₁ )

dB ₀ dt

under the condition

W ₂ F ₀ = W ₁ F ₀ , i.e. H. w ₂ = W ₁ .

Result:

W ₂ -U ₁ = (W ₂ F ₂ - W ₁ F ₁ )

- W ₁ (F ₂ - F ₁ ).

dß ₀

di

2. Intensity of magnetization B, U ₁ - W ₃ = (W ₁ F ₁ - w ₃ l

dB;

di

V ₁ F ₀ - W ₃ F ₀ )

di

under the condition

W ₁ F ₁ = W ₃ F ₃ or W ₁ F ₁ - W ₃ F ₃

= O.

Result:

«I -" 3 = ( ^w i -

dB.

di

Coil pair composed of an opposing coil pair (4-coil system) with the windings W ₁ , W ₂ , w ₃ , w ₄ and the cross-sections F ₁ , F ₂ , F ₃ , F ₄ (counting from the inside out).

The conditions here are W ₁ = w ₂ for the field coil pair and W ₃ F ₃ - W ₄ F ₄ . must be observed for the induction coil pair.

The differential voltage of the field coil pair is under these conditions

U ₂ -U ₁ = w, CF, -f,) ^

and the differential voltage of the induction coil pair

"4 = ( ^W 3 - W ₄ ) F ₀

40

45

In order to achieve an improvement in the accuracy of the measured values, in the stability of the measuring coil combination and in an easy interchangeability of the samples (round, rectangular or ring-shaped rod), not only a pair of coils with the intensity of magnetization B ₁ , but also a pair of coils for Measurement of the field strength H in the homogeneous area wrapped in a ring around the sample with a circular, rectangular or ring-shaped cross-section. Both coil systems are designed in such a way that _{the effect of the air flow in the sample is automatically compensated for during the B r} measurement and the effect of the iron flow in the sample during the H measurement.

For this purpose, both a pair of coils with the intensity of the magnetization and a field W ₃

di

The B _r measurement has a further advantage that only the cross section of the sample is included as a variable.

Instead of a 4-coil system, it is also possible to use a 3-coil system with the number of turns W ₁ , w ₂ , w ₃ (counting from the inside to the outside) and the cross-sections F ₁ , F ₂ , F ₃ . In this 3-coil system, coils 1 and 2 for field strength measurement and coils 1 and 3 for induction measurement are connected in opposition to one another. _{The relationships W 1} = w ₂ for the field strength measurement and W ₁ F ₁ = W ₃ F ₃ for the induction measurement then apply here.

So continue to apply

- U ₁ = W ₁ (F ₂ - F ₁ )

U ₁ - U ₃ = (w, - w ₃ ) F ₀

dß ₀
German

dB, -di

The measuring device for the 4 or 3 coil system consists of two resettable flux meters for the direct display of the induction and field strength values and in connection with an XY recorder for fast recording of the hysteresis loop Bi = f (H).

The invention is explained in more detail with reference to two figures.

In Fig. 1 shows the principle. 1 is a U-shaped electromagnet, for example, which is excited by the current i ″, of the winding 2. The rod sample 3 with the cross section F _{0 is} clamped between the pole shoes NS. The homogeneously magnetized area with constant induction and field strength is indicated by dashed lines. This area is filled in by the 3-coil system 1, 2, 3 as an example.

The field coil pair with the voltage u _H is 1-2. The induction coil pair with the voltage u _B. is 1-3. The counter connection of each pair is indicated in the lower half. B; and H are indicated by flux meters 4 and 5. The XY recorder 6 for recording the hysteresis loop B ₁ - = / (H) is connected to both.

II. Soft magnetic materials

In the case of plasticized materials, such as dynamo or transformer sheet metal with or without grain orientation, the core loss V (W / kg) at a certain maximum induction B _max

and a maximum field strength H ₁ ^ _x in the case of alternating current magnetization, the important parameter. Rolled sheets or strips that have recently been running should be checked immediately before being rolled up into a coil. In a known, practically used embodiment for a continuous strip, the magnetization is carried out by a more or less long current-carrying open magnetization coil, the current of which is set depending on the desired maximum induction. The induction measuring winding surrounds the tape. The magnetizing current cannot be used to measure the field strength because the shear of the open coil is too great. For the Η measurement, for example, a short air-core coil is inserted between the surface of the strip or the board and the upper inner side of the magnetizing coil.

So exactly this well-known two-coil system in the space of a constant field strength with sufficient Good coordination of the coil dimensions with one another, the induction, the field strength, the loss of magnetic reversal If it is also able to measure, the mechanical susceptibility to failure is more sudden when running in Changes in thickness, tears on the edges of the belt and waves in the belt are quite large, so that an uninterrupted measuring activity for weeks is hardly possible.

To remedy these weaknesses, it is useful, even with soft magnetic material for the induction and field strength measurement to take over the 3- or 4-coil system and concentric around the electrical sheet or around the moving belt. The 3 or 4 coil system can continue to be recorded by a short-circuit-free, non-magnetic coil box, which the windings mechanically shields it from the material to be measured and thus prevents damage. The height dimension is chosen so that the measuring coil system is in the coil body of the magnetizing winding of known design can be inserted and attached to it. The solid-free passage room for the tape or the board can be lowered in height as much as it is a allows trouble-free operation. The length of the magnetization can be varied as desired using short coil units in a row be enlarged. Two or more measuring units can also be joined together in the middle be. To achieve the best possible symmetry of the field strength above and below the board or the strip the coil area under the belt can be covered with a friction-resistant insulating plate (glass fiber pressed plate) be designed so strong that the band and center line coincide.

To improve the homogeneity of the field strength in the field coil space, between the magnetization and measuring coil formers above and below, possibly also on the sides, over the entire length and width of highly permeable metal sheets (Armcoeisen) can be inserted. ■

In Fig. Figure 2 is a schematic cross section of the coil assembly of an open magnetizer shown.

7 is the continuous belt or panel;

8 is the free passage room; 65 '

9 is the insulating and carrier plate for the electrical steel sheet inside the magnetization and measuring coil system;

10 is the coil body, for example for a concentric 3-coil measuring system made of non-magnetic Material;

11 is the one pushed over the measuring coil body 10 Bobbin with magnetizing winding;

12 and 13 are attached bobbins with magnetizing windings for extension the magnetization distance. Insulating strips are inserted as a replacement for the measuring coil formers ;

14 are insulating support bodies for the magnetizing coils;
15, 16, 17 is the 3-coil measuring system.

Claims (7)

Patent claims: 1. Device for determining the magnetic parameters (induction, intensity of magnetization, field strength and magnetic reversal loss) of ferromagnetic samples in the form of rods with, for example, circular or rectangular or ring-shaped cross-section in a slowly changing alternating field, e.g. B. an electromagnet or electrical sheet - or strips with small thickness and large width in a rapidly changing alternating field, z. B. an open magnetizing coil by means of an induction double measuring coil and a field strength double measuring coil, characterized in that both the induction double measuring coil and the field strength double measuring coil encircle the sample in the homogeneous area, the coil system of at least three concentric coils with the cross-sections (F ₁ , F ₂ and F ₃ ) and the number of turns (w _u W ₂ , W ₃ ) (counting from the inside out) and that the condition W ₁ = W ₂ for the field coil pair and the condition W ₁ F ₁ for the coil pair of the intensity of the magnetization - W ₃ F _{3 is} observed and that the second coil (F ₂ W ₂ ) of the first coil (F ₁ W ₁ ) for measuring the field strength and the third coil (F ₃ W ₃ ) of the first coil (F ₁ W ₁ ) is connected in the opposite direction. 2. Device for determining the magnetic parameters according to claim 1, characterized in that both the coil of the intensity of the magnetization and the field strength coil each from an opposing pair of coils (4-coil system) with the hosts (W ₁ , W ₂ , W ₃ , W ₄ ) and the cross-sections (F ₁ , F ₂ , F ₃ , F ₄ ) (counting from the inside out) and that here the conditions W ₁ = w ₂ z. B. for the field strength _{coil pair and W 3} F ₃ = W ₄ F ₄ for the induction coil pair are adhered to ^. 3. Measuring device for bars in the slowly changing magnetic field of an electromagnet according to claims 1 to 2, characterized in that both field strength proportional and induction-proportional voltage is also displayed via a low-resetting flux meter or can be recorded as a hysteresis loop using both flux meters and an X-Y recorder. 4. Device for determining the magnetic parameters according to Claims 1 and 2 for electrical steel sheets and electrical steel strips in the alternating field of an open coil, characterized in that both the magnetizing winding and the 3- or 4-coil measuring system supported by telescopic bobbins, with smooth inner walls for ensure an unrestrained flow of the material to be measured. 5. Device for determining the magnetic parameters according to claims 1, 2 and 4, characterized in that the coil system in 1, 3 or more odd-numbered bobbins is divided and the middle the 3 or 4 coil measuring system within its magnetization winding contains or that the coil system is divided into two or more even-numbered bobbins and the two middle ones the 3 or Include 4-coil system within the magnetization winding. 6. Device for determining the magnetic parameters according to claims 1, 2 and 4, 5, characterized in that the lower base of the bobbin is covered with a flat insulating plate (Glass fiber) is designed around the panels or the tape as possible in the middle of the measuring room and to lead without significant slack. 7. Device for determining the magnetic parameters according to claims 1, 2 and 4 to 6, characterized in that highly permeable between the magnetizing coil and the measuring coil system Metal sheets are inserted along the entire length of the magnetizing coil. 1 sheet of drawings 109 534/50