DE1069056B - - Google Patents
Info
- Publication number
- DE1069056B DE1069056B DENDAT1069056D DE1069056DA DE1069056B DE 1069056 B DE1069056 B DE 1069056B DE NDAT1069056 D DENDAT1069056 D DE NDAT1069056D DE 1069056D A DE1069056D A DE 1069056DA DE 1069056 B DE1069056 B DE 1069056B
- Authority
- DE
- Germany
- Prior art keywords
- clay
- brick
- frost
- expanded clay
- rotary kiln
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
Herstellung frostbeständiger keramischer Baukörper Es ist schon verschiedentlich vorgeschlagen worden, die Frostbeständigkeit von Baukörpern aus gebranntem Ton, wie z. B. Mauerziegel, Dachziegel usw., durch Beimischung von Quarzsand zu verbessern.Manufacture of frost-resistant ceramic structures It's been different it has been proposed to assess the frost resistance of structures made of baked clay, such as B. Bricks, roof tiles, etc., to be improved by adding quartz sand.
Andere Vorschläge erstrecken sich auf Zusätze von verbrennbaren Stoffen, wie z. B. gemahlener Kohle, kohlenstoffreiche Aschen oder Schlacken, Sägespäne usw., die dem Ziegelton beigemischt werden.Other proposals extend to the addition of combustible substances, such as B. ground coal, carbon-rich ashes or slag, sawdust, etc., which are mixed with the brick clay.
Sowohl der Zusatz von Quarzsand als auch die Beimischung von verbrennbaren Stoffen sollen dem Zweck dienen, den Hohlraumaufbau des Ziegelscherbens dahingehend zu beeinflussen, daß die im Scherben vorhandenen Feinstkapillaren von Makroporen durchsetzt werden, in die das Eis bei seiner Ausdehnung eindringen kann, wodurch eine Gefügezerstörung verhindert werden soll.Both the addition of quartz sand and the admixture of combustible ones Fabrics should serve the purpose of building up the cavity in the broken brick to influence that the fine capillaries of macropores present in the body be penetrated into which the ice can penetrate as it expands, whereby a structural destruction is to be prevented.
Die mit Zusatz von Sand erzielten Ergebnisse sind jedoch unbefriedigend und gewisse Verbesserungen mehr zufällig, da die notwendige Abstimmung des Sandes hinsichtlich der Menge und der Korngröße auf den Ton praktisch nicht möglich ist; andererseits infolge des Quarzwachstums während des Brandes Gefügeauflockerungen und innere Spannungen hervorgerufen werden.However, the results obtained with the addition of sand are unsatisfactory and certain improvements more accidentally, since the necessary tuning of the sand in terms of the amount and grain size on the clay is practically impossible; on the other hand, as a result of the quartz growth during the fire, loosening of the structure and internal tensions are created.
Der Zusatz von verbrennbaren Stoffen, die beim Brand des Ziegeltones ausbrennen und Hohlräume hinterlassen, bringt ebenfalls kein befriedigendes Ergebnis, da die entweichenden Verbrennungsgase ihrerseits zusätzliche Feinstkapillaren bilden, die die erstrebte Wirkung zum Teil wieder aufheben, zudem das Gefüge des Scherbens auflockern und damit eine Verringerung der Festigkeit verursachen. Andere Vorschläge gehen dahin, Schachtofen-Blähton oder Blähschiefer als Zusatz zu verwenden, jedoch mit dem Ziel, das Gewicht der gebrannten Körper herabzusetzen.The addition of combustible substances when the brick clay burns burn out and leave cavities, also does not bring a satisfactory result, since the escaping combustion gases in turn form additional fine capillaries, which partially cancel the desired effect, as well as the structure of the body loosen up and thus cause a reduction in strength. Other suggestions are going to use shaft furnace expanded clay or expanded slate as an additive, however with the aim of reducing the weight of the burned bodies.
Schachtofen-Blähton ist gekennzeichnet durch eine völlig offene, poröse und zerklüftete Oberfläche seiner Einzelkörner, die sich zwangläufig aus dem Herstellungsvorgang im Schachtofen sowie durch den anschließenden Brechvorgang ergibt. Seine Verwendung als Zusatz zu Ziegelton verleiht dem gebrannten Ziegel zwar ein geringeres Gewicht, läßt diesen andererseits aber frostempfindlicher werden, da infolge der offenen Porigkeit des Schachtofen-Blähtons der Anteil des saugfähigen Porenraumes des Ziegels ansteigt.Shaft furnace expanded clay is characterized by a completely open, porous and jagged surface of its individual grains, inevitably resulting from the manufacturing process in the shaft furnace as well as through the subsequent crushing process. Its use as an additive to brick clay gives the fired brick a lower weight, On the other hand, it makes it more sensitive to frost because of the open Porosity of the expanded clay shaft kiln is the proportion of the absorbent pore space in the brick increases.
Die Erfindung geht von der bekannten Erkenntnis aus, daß ein Baukörper dann frostbeständig ist, wenn der; Quotient aus Wasseraufnahme bei Wasserlagerung unter Normaldruck zu Wasseraufnahme unter Vakuum = 0,80 ist und somit darauf beruht, daß der Anteil wassersaugender Poren im Verhältnis zum gesamten Porenraum möglichst klein ist.The invention is based on the known knowledge that a building is frost-resistant if the; Quotient from water absorption during water storage under normal pressure to water absorption under vacuum = 0.80 and is therefore based on that the proportion of water-sucking pores in relation to the total pore space as possible is small.
Die Erfindung bezweckt, den für die Herstellung keramischer Baukörper verwendeten Ziegelton durch Beigabe geeigneter Stoffe in seiner Gefügestruktur dahingehend zu beeinflussen, daß der Sättigungswert des Scherbens = 0,80f wird und dieser damit die Eigenschaft der Frostbeständigkeit erhält, ohne daß die Nachteile der beschriebenen Vorschläge eintreten.The invention aims for the production of ceramic structures used brick clay by adding suitable substances in its structure to influence that the saturation value of the body = 0.80f and this with it the property of frost resistance is retained without the disadvantages of the described Proposals occur.
Das wesentliche Merkmal besteht in der Maßnahme, dem Ausgangsmaterial für die Herstellung der in Rede stehenden Baukörper vor der Formgebung gebrannten Drehofen-Blähton feiner Körnung, beispielsweise der Korngruppe 0 bis 3 mm, in geringen Mengen beizumischen. Die Höhe des Zusatzes richtet sich dabei nach dem ursprünglichen Sättigungswert des Ziegelscherbens und schwankt je nach Art des verwendeten Ausgangsmaterials.The essential feature is the measure, the starting material Fired for the production of the building structure in question before shaping Rotary kiln expanded clay of fine grain size, for example the grain group 0 to 3 mm, in small amounts Mix in quantities. The amount of the addition depends on the original Saturation value of the broken brick and fluctuates depending on the type of raw material used.
Beispielsweise ist bei einem Sättigungswert des frostunbeständigen Scherbens von 0,86 ein Zusatz von 8 Gewichtsprozent Drehofen-Blähton erforderlich, um den Sättigungswert auf 0,79 zu senken und den Scherben frostbeständig zu machen.For example, at a saturation value, the frost-unstable For shards of 0.86, an addition of 8 percent by weight of rotary kiln expanded clay is required, to lower the saturation value to 0.79 and to make the shards resistant to frost.
Diese überraschend günstige Wirkung beruht auf der besonderen Eigenschaft des Drehofen-Blähtons, dessen Einzelkorn eine gesinterte, dichte Oberfläche besitzt und kein Wasser aufnimmt, während das innere Gefüge makroporös ist, wobei die Einzelporen von elastischen Zellwänden getrennt sind. Der in den Kapillaren des Scherbens entstehende Eisdruck wird deshalb unwirksam, was durch das elastische Verhalten der zwischen den Makroporen befindlichen Zellwände bedingt ist.This surprisingly favorable effect is based on the special property of the rotary kiln expanded clay, the single grain of which has a sintered, dense surface and does not absorb water, while the inner structure is macroporous, with the individual pores are separated by elastic cell walls. The one that arises in the capillaries of the body Ice pressure is therefore ineffective, which is due to the elastic behavior of the between cell walls located in the macropores.
Die Verwendung von Drehofen-Blähton zur Herstellung frostbeständiger keramischer Baukörper kann beispielsweise wie folgt gehandhabt werden: Dem Ausgangsmaterial wird, gegebenenfalls nach vorheriger Trocknung und Mahlung, die erforderliche Menge gekörnten Drehofen-Blähtons zugesetzt, beides im Zwangsmischer innig vermischt, sodann das fertige Gemisch in bekannter Weise im Trockenpreßverfahren geformt, getrocknet und gebrannt. Sofern die Verformung im Naßpreßverfahren erfolgt, empfiehlt es sich, den gekörnten Drehofen-Blähton vor der Vermischung mit der Ziegeltonmasse so weit anzufeuchten, daß er einen Feuchtigkeitsgehalt von etwa 6 Gewichtsprozent aufweist. Nach erfolgter Vermischung mit dem Ziegelton wird das fertige Gemisch in bekannter Weise geformt, getrocknet und gebrannt.The use of rotary kiln expanded clay to produce frost-resistant Ceramic structures can be handled as follows, for example: The starting material becomes, if necessary after previous drying and grinding, the required amount granulated rotary kiln expanded clay added, both intimately mixed in the compulsory mixer, then the finished one Mixture in a known manner in the dry pressing process shaped, dried and fired. If the deformation takes place in the wet pressing process, it is advisable to use the granular expanded clay before mixing with the brick clay mass to moisten so that it has a moisture content of about 6 percent by weight having. After mixing with the brick clay is the finished mixture shaped, dried and fired in a known manner.
Claims (1)