DE102020119683A1 - Process for manufacturing a component using additive manufacturing - Google Patents

Process for manufacturing a component using additive manufacturing Download PDF

Info

Publication number
DE102020119683A1
DE102020119683A1 DE102020119683.0A DE102020119683A DE102020119683A1 DE 102020119683 A1 DE102020119683 A1 DE 102020119683A1 DE 102020119683 A DE102020119683 A DE 102020119683A DE 102020119683 A1 DE102020119683 A1 DE 102020119683A1
Authority
DE
Germany
Prior art keywords
oxide
compound
und
oder
zinc
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE102020119683.0A
Other languages
German (de)
Inventor
Stefan Eibl
Philipp Matthes
Bernhard Häupler
Helmut Bleier
Meike Schmidt
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Rehau Industries SE and Co KG
Original Assignee
Rehau AG and Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Rehau AG and Co filed Critical Rehau AG and Co
Publication of DE102020119683A1 publication Critical patent/DE102020119683A1/en
Pending legal-status Critical Current

Abstract

Die Erfindung betrifft ein Verfahren zur Herstellung eines Bauteils im Wege der additiven Fertigung, insbesondere durch selektives Lasersintern, wobei als Grundmaterial ein pulverförmiger Werkstoff eingesetzt wird. Erfindungsgemäß wrid dem pulverförmigen Werkstoff vor der Bauteilherstellung mindestens eine antimikrobiell wirkende Substanz zugesetzt, die sich während der additiven Fertigung thermisch stabil verhält.The invention relates to a method for producing a component by means of additive manufacturing, in particular by selective laser sintering, with a powdered material being used as the base material. According to the invention, at least one substance with an antimicrobial effect is added to the powdered material before the component is manufactured, which substance is thermally stable during additive manufacturing.

Description

Die Erfindung betrifft ein Verfahren zur Herstellung eines Bauteils im Wege der additiven Fertigung, insbesondere durch selektives Lasersintern, wobei als Grundmaterial ein pulverförmiger Werkstoff eingesetzt wird.The invention relates to a method for producing a component by means of additive manufacturing, in particular by selective laser sintering, a powdery material being used as the base material.

Das Lasersintern gehört zur Gruppe der generativen Schichtbauverfahren. Hierbei wird das Werkstück sukzessive Schicht für Schicht aufgebaut, wobei die Bauplattform nach und nach nach unten verfahren wird. Durch die Wirkung der Laserstrahlen ist es möglich, praktisch beliebige dreidimensionale Geometrien zu erzeugen, wobei insbesondere auch Hinterschneidungen kein fertiungstechnisches Problem darstellen. Dadurch lassen sich Werkstücke erzeugen, die mittels konventioneller mechanischer oder gießtechnischer Verfahren nicht herstellbar sind.Laser sintering belongs to the group of generative layer construction processes. Here, the workpiece is built up successively, layer by layer, with the construction platform being moved downwards one by one. The effect of the laser beams makes it possible to produce practically any three-dimensional geometries, with undercuts in particular not representing a manufacturing problem. This makes it possible to produce workpieces that cannot be produced using conventional mechanical or casting processes.

Der Erfindung liegt die Aufgabe zugrunde, ein Verfahren zur Herstellung eines Bauteils im Wege der additiven Fertigung derart weiter zu entwickeln, dass sich hierdurch neue Anwendungsbereiche ergeben.The invention is based on the object of further developing a method for manufacturing a component by means of additive manufacturing in such a way that this results in new areas of application.

Erfindungsgemäß wird diese Aufgabe dadurch gelöst, dass dem pulverförmigen Werkstoff vor der Bauteilherstellung mindestens eine antimikrobiell wirkende Substanz zugesetzt wird, die sich während der additiven Fertigung thermisch stabil verhält. Die Erfindung beruht hierbei auf der Erkenntnis, das die thermische Belastung von Zusatzstoffen bei der additiven Fertigung wesentlich kurzzeitiger und damit geringer ist als bei konventionellen Herstellungsverfahren, beispielsweise der Extrusion oder dem Spritzgießen von Kunststoffen. Erfindungsgemäß lassen sich somit insbesondere solche antimikrobiell wirkende Substanzen verwenden, die z.B. für eine Extrusion oder einen Spritzgießprozess aufgrund der damit verbundenen hohen thermischen Belastung ungeeignet sind.According to the invention, this object is achieved in that at least one antimicrobial substance is added to the powdery material before the component is manufactured, which substance is thermally stable during additive manufacturing. The invention is based on the knowledge that the thermal load on additives in additive manufacturing is much shorter and therefore less than in conventional manufacturing processes, for example extrusion or injection molding of plastics. According to the invention, substances with an antimicrobial effect can be used which are unsuitable, for example, for an extrusion or an injection molding process due to the associated high thermal load.

Im Stand der Technik sind antibakterielle, pulverförmige Agents bekannt, die durch chemische Synthese vergleichsweise aufwändig hergestellt werden müssen. Die Herstellung umfasst ein mehrstufiges Verfahren sowie den Einsatz von organischen Lösungsmitteln Entsprechende Ansätze sind aus den Druckschriften EP 3 266 613 A1 , EP 3 231 833 A1 und EP 3 231 831 A1 bekannt. In EP 3 363 849 A1 ist eine Ansatz beschrieben, dessen antibakterielle Wirkung auf kostenintensiven organischen Silbersalzen basiert. Zweckmäßigerweise enthält die antimikrobiell wirkende Substanz daher mindestens eine anorganische Metallverbindung und/oder mindestens ein elementares Metall. Die Herstellung der vorgenannten anorganischen Metallverbindungen ist vergleichsweise einfach, wobei insbesondere mindestens ein(e) undotiertes und/oder dotiertes Metalloxid und/oder Metallhydroxid und/oder Metallmischoxid und/oder elementare Metallverbindung und/oder Metallphosphatverbindung und/oder Metallnitratverbindung und/oder Metallphosphatverbindung und/oder Metallsulfat- und/oder Metallsulfonatverbindung und/oder Metallphosphatglas und/oder eine Koordinationsverbindung mit einer organischen Ligandensphäre verwendet werden kann. Gemäß einem bevorzugten Ausführungsbeispiel der Erfindung wird als undotiertes Metalloxid Zinkperoxid und/oder Zinkoxid und/oder Kupferoxid und/oder Eisenoxid und/oder Titandioxid und/oder Silberoxid und/oder Platinoxid und/oder Palladiumoxid und/oder Rhodiumoxid und/oder Rutheniumoxid und/oder osmiumoxid und/oder Manganoxid und/oder als Metallhydroxid Calciumhydroxid und/oder ein Hydroxid des Eisens und/oder Kupfers und/oder Mangans und/oder Zinks und/oder Titans und/oder Platins und/oder Rutheniums und/oder Osmiums und/oder Silbers verwendet.In the prior art, antibacterial, powdery agents are known which have to be produced in a comparatively complex manner by chemical synthesis. The production comprises a multi-stage process and the use of organic solvents. Corresponding approaches can be found in the publications EP 3 266 613 A1 , EP 3 231 833 A1 and EP 3 231 831 A1 known. In EP 3 363 849 A1 describes an approach whose antibacterial effect is based on cost-intensive organic silver salts. The antimicrobial substance therefore expediently contains at least one inorganic metal compound and / or at least one elemental metal. The production of the aforementioned inorganic metal compounds is comparatively simple, with in particular at least one undoped and / or doped metal oxide and / or metal hydroxide and / or metal mixed oxide and / or elemental metal compound and / or metal phosphate compound and / or metal nitrate compound and / or metal phosphate compound and / or metal sulfate and / or metal sulfonate compound and / or metal phosphate glass and / or a coordination compound with an organic ligand sphere can be used. According to a preferred embodiment of the invention, the undoped metal oxide is zinc peroxide and / or zinc oxide and / or copper oxide and / or iron oxide and / or titanium dioxide and / or silver oxide and / or platinum oxide and / or palladium oxide and / or rhodium oxide and / or ruthenium oxide and / or osmium oxide and / or manganese oxide and / or as metal hydroxide calcium hydroxide and / or a hydroxide of iron and / or copper and / or manganese and / or zinc and / or titanium and / or platinum and / or ruthenium and / or osmium and / or silver used.

Sofern ein dotiertes Metalloxid zum Einsatz kommt, so eignet sich hierfür im Rahmen der Erfindung insbesondere

  • - Zinkoxid mit den elementaren Metallen Fe und/oder Ag und/oder Pt und/oder Pd und/oder Rh und/oder Ru und/oder Au und/oder Os und/oder Mn und/oder Cu und/oder Ti und/oder AI und/oder Mg und/oder den Metalloxiden Eisenoxid und/oder Silberoxid und/oder Kupferoxid und/oder Titandioxid und/oder Aluminiumoxid und/oder Magnesiumoxid und/oder Calciumoxid als Dotierungspartner und/oder
  • - Titandioxid mit Fe und/oder Ag und/oder Cu und/oder Zn und/oder Pt und/oder Pd und/oder Rh und/oder Ru und/oder Au und/oder Os und/oder Mn und/oder AI und/oder Eisenoxid und/oder Silberoxid und/oder Kupferoxid und/oder Zinkdioxid und/oder Aluminiumoxid und/oder Magnesiumoxid und/oder Calciumoxid als Dotierungspartner und/oder
  • - Kupferoxid mit Fe und/oder Ag und/oder Ti und/oder Zn und/oder Pt und/oder Pd und/oder Rh und/oder Ru und/oder Au und/oder Os und/oder Mn und/oder AI und/oder Eisenoxid und/oder Silberoxid und/oder Zinkoxid und/oder Titandioxid und/oder Aluminiumoxid und/oder Magnesiumoxid und/oder Calciumoxid als Dotierungspartner und/oder
  • - Eisenoxid mit Ag und/oder Ti und/oder Zn und/oder Pt und/oder Pd und/oder Rh und/oder Ru und/oder Au und/oder Os und/oder Mn und/oder AI und/oder Kupferoxid und/oder Silberoxid und/oder Zinkoxid und/oder Titandioxid und/oder Aluminiumoxid und/oder Magnesiumoxid und/oder Calciumoxid als Dotierungspartner und/oder
  • - Silberoxid mit Fe und/oder Cu und/oder Ti und/oder Zn und/oder Pt und/oder Pd und/oder Rh und/oder Ru und/oder Au und/oder Os und/oder Mn und/oder AI und/oder Eisenoxid und/oder Kupferoxid und/oder Zinkoxid und/oder Titandioxid und/oder Aluminiumoxid und/oder Magnesiumoxid und/oder Calciumoxid als Dotierungspartner und/oder
  • - Platinoxid mit Ag und/oder Ti und/oder Zn und/oder Fe und/oder Pd und/oder Rh und/oder Ru und/oder Au und/oder Os und/oder Mn und/oder Cu und/oder AI und/oder Kupferoxid und/oder Silberoxid und/oder Zinkoxid und/oder Titandioxid und/oder Aluminiumoxid und/oder Magnesiumoxid und/oder Manganoxid und/oder Rhodiumoxid und/oder Palladiumoxid und/oder Rutheniumoxid und/oder Calciumoxid als Dotierungspartner und/oder
  • - Palladiumoxid mit Ag und/oder Ti und/oder Zn und/oder Pt und/oder Fe und/oder Rh und/oder Ru und/oder Au und/oder Os und/oder Mn und/oder Cu und/oder AI und/oder Kupferoxid und/oder Silberoxid und/oder Zinkoxid und/oder Titandioxid und/oder Aluminiumoxid und/oder Magnesiumoxid und/oder Manganoxid und/oder Rhodiumoxid und/oder Platinoxid und/oder Rutheniumoxid und/oder Calciumoxid als Dotierungspartner und/oder
  • - Rhodiumoxid mit Ag und/oder Ti und/oder Zn und/oder Pt und/oder Fe und/oder Pd und/oder Ru und/oder Au und/oder Os und/oder Cu und/oder Mn und/oder AI und/oder Kupferoxid und/oder Silberoxid und/oder Zinkoxid und/oder Titandioxid und/oder Aluminiumoxid und/oder Magnesiumoxid und/oder Manganoxid und/oder Rhodiumoxid und/oder Platinoxid und/oder Rutheniumoxid und/oder Calciumoxid als Dotierungspartner und/ode
  • - Rutheniumoxid mit Ag und/oder Ti und/oder Zn und/oder Pt und/oder Fe und/oder Pd und/oder Rh und/oder Au und/oder Os und/oder Cu und/oder Mn und/oder AI und/oder Kupferoxid und/oder Silberoxid und/oder Zinkoxid und/oder Titandioxid und/oder Aluminiumoxid und/oder Magnesiumoxid und/oder Manganoxid und/oder Rhodiumoxid und/oder Platinoxid, Rutheniumoxid Calciumoxid als Dotierungspartner und/oder
  • - Osmiumoxid mit Ag und/oder Ti und/oder Zn und/oder Pt, Fe, Pd, Rh, Au, Ru, Mn, Cu, AI / Kupferoxid, Silberoxid, Zinkoxid, Titandioxid, Aluminiumoxid, Magnesiumoxid, Manganoxid, Rhodiumoxid, Platinoxid, Rutheniumoxid Calciumoxid als Dotierungspartner, und/oder
  • - Manganoxid mit Ag, Ti, Zn, Pt, Fe, Pd, Rh, Au, Ru, Os, Cu, AI / Kupferoxid, Silberoxid, Zinkoxid, Titandioxid, Aluminiumoxid, Magnesiumoxid, Manganoxid, Rhodiumoxid, Platinoxid, Rutheniumoxid Calciumoxid als Dotierungspartner verwendet wird.
If a doped metal oxide is used, it is particularly suitable for this within the scope of the invention
  • - Zinc oxide with the elemental metals Fe and / or Ag and / or Pt and / or Pd and / or Rh and / or Ru and / or Au and / or Os and / or Mn and / or Cu and / or Ti and / or Al and / or Mg and / or the metal oxides iron oxide and / or silver oxide and / or copper oxide and / or titanium dioxide and / or aluminum oxide and / or magnesium oxide and / or calcium oxide as doping partner and / or
  • - Titanium dioxide with Fe and / or Ag and / or Cu and / or Zn and / or Pt and / or Pd and / or Rh and / or Ru and / or Au and / or Os and / or Mn and / or Al and / or iron oxide and / or silver oxide and / or copper oxide and / or zinc dioxide and / or aluminum oxide and / or magnesium oxide and / or calcium oxide as doping partner and / or
  • - Copper oxide with Fe and / or Ag and / or Ti and / or Zn and / or Pt and / or Pd and / or Rh and / or Ru and / or Au and / or Os and / or Mn and / or Al and / or iron oxide and / or silver oxide and / or zinc oxide and / or titanium dioxide and / or aluminum oxide and / or magnesium oxide and / or calcium oxide as doping partner and / or
  • - Iron oxide with Ag and / or Ti and / or Zn and / or Pt and / or Pd and / or Rh and / or Ru and / or Au and / or Os and / or Mn and / or Al and / or copper oxide and / or silver oxide and / or zinc oxide and / or titanium dioxide and / or aluminum oxide and / or magnesium oxide and / or calcium oxide as doping partner and / or
  • - Silver oxide with Fe and / or Cu and / or Ti and / or Zn and / or Pt and / or Pd and / or Rh and / or Ru and / or Au and / or Os and / or Mn and / or Al and / or iron oxide and / or copper oxide and / or zinc oxide and / or titanium dioxide and / or aluminum oxide and / or magnesium oxide and / or calcium oxide as doping partner and / or
  • - Platinum oxide with Ag and / or Ti and / or Zn and / or Fe and / or Pd and / or Rh and / or Ru and / or Au and / or Os and / or Mn and / or Cu and / or Al and / or copper oxide and / or silver oxide and / or zinc oxide and / or titanium dioxide and / or aluminum oxide and / or magnesium oxide and / or manganese oxide and / or rhodium oxide and / or palladium oxide and / or ruthenium oxide and / or calcium oxide as doping partner and / or
  • - Palladium oxide with Ag and / or Ti and / or Zn and / or Pt and / or Fe and / or Rh and / or Ru and / or Au and / or Os and / or Mn and / or Cu and / or Al and / or copper oxide and / or silver oxide and / or zinc oxide and / or titanium dioxide and / or aluminum oxide and / or magnesium oxide and / or manganese oxide and / or rhodium oxide and / or platinum oxide and / or ruthenium oxide and / or calcium oxide as doping partner and / or
  • - Rhodium oxide with Ag and / or Ti and / or Zn and / or Pt and / or Fe and / or Pd and / or Ru and / or Au and / or Os and / or Cu and / or Mn and / or Al and / or copper oxide and / or silver oxide and / or zinc oxide and / or titanium dioxide and / or aluminum oxide and / or magnesium oxide and / or manganese oxide and / or rhodium oxide and / or platinum oxide and / or ruthenium oxide and / or calcium oxide as doping partner and / or
  • - Ruthenium oxide with Ag and / or Ti and / or Zn and / or Pt and / or Fe and / or Pd and / or Rh and / or Au and / or Os and / or Cu and / or Mn and / or Al and / or copper oxide and / or silver oxide and / or zinc oxide and / or titanium dioxide and / or aluminum oxide and / or magnesium oxide and / or manganese oxide and / or rhodium oxide and / or platinum oxide, ruthenium oxide and / or calcium oxide as a doping partner
  • - Osmium oxide with Ag and / or Ti and / or Zn and / or Pt, Fe, Pd, Rh, Au, Ru, Mn, Cu, Al / copper oxide, silver oxide, zinc oxide, titanium dioxide, aluminum oxide, magnesium oxide, manganese oxide, rhodium oxide, platinum oxide , Ruthenium oxide calcium oxide as a doping partner, and / or
  • - Manganese oxide with Ag, Ti, Zn, Pt, Fe, Pd, Rh, Au, Ru, Os, Cu, Al / copper oxide, silver oxide, zinc oxide, titanium dioxide, aluminum oxide, magnesium oxide, manganese oxide, rhodium oxide, platinum oxide, ruthenium oxide calcium oxide used as doping partner will.

Alternativ oder ergänzend hierzu liegt es ebenso im Rahmen der Erfindung, dass eine Koordinationsverbindung mit einer organischen Ligandensphäre mit Ag und/oder Ti und/oder Zn und/oder Pt und/oder Fe und/oder Pd und/oder Rh und/oder Au und/oder Ru und/oder Mn und/oder AI und/oder Cu als Koordinationszentrum und wenigstens einer organischen Verbindung (ungeladen und/oder ionisch), welche die Elemente, ausgewählt aus C und/oder N und/oder O und/oder S und/oder P und/oder Si und/oder Sb und/oder As und/oder F und/oder Cl und/oder Br und/oder I umfaßt, verwendet wird.Alternatively or in addition to this, it is also within the scope of the invention that a coordination compound with an organic ligand sphere with Ag and / or Ti and / or Zn and / or Pt and / or Fe and / or Pd and / or Rh and / or Au and / or Ru and / or Mn and / or Al and / or Cu as the coordination center and at least one organic compound (uncharged and / or ionic) which contains the elements selected from C and / or N and / or O and / or S and / or P and / or Si and / or Sb and / or As and / or F and / or Cl and / or Br and / or I is used.

Im Rahmen der Erfindung liegt es ferner generell, dass die antimikrobiell wirkende Substanz als elementares Metall Ag und/oder Cu und/oder Fe und/oder Pt und/oder Pd und/oder Rh und/oder Os und/oder Au enthält. Weiterhin liegt es im Rahmen der Erfindung, dass als antimikrobiell wirkende Substanz ergänzend oder alternativ zur anorganischen Metallverbindung bzw. zum elementaren Metall mindestens eine organische Verbindung und/oder mindestens eine polymere Verbindung enthält. Sofern eine organische Verbindung zum Einsatz kommt, so eignet sich hierfür insbesondere eine quaternäre Ammoniumverbindung und/oder quaternäre Phosphoniumverbindung und/oder Pyridopyrazindion-Verbindung (z.B. beschrieben in WO2020/053654 ) und/oder ein Adefovir-Derivat (z.B. von der Fa. Gilead® Sciences), bspw. Adefovir dipivoxil [9-[2-[[bis[(pivaloyloxy)methoxy]phosphinyl]-methoxy]ethyl]adenin und/oder Tenofovir und/oder [(2R)-1-(6-aminopurin-9-yl)propan-2-yl]oxymethylphosphonsäure und/oder Tenofoviralafenamid (z.B. beschrieben in US2019/0216831 ) und/oder Enmetazobactam und/oder Tazobactam und/oder Triaazaacenaphthalene und/oder 3-(Trimethoxysilyl)propyl-N-octadecyl-N,N-dimethylammoniumchlorid und/oder 3-(Trimethoxysilyl)propyl-N-octadecyl-N,N-dimethylammoniumchlorid und/oder 3-(Trimethoxysilyl)propyl-N-tetradecyl-N,N-dimethylammoniumchlorid und/oder 3-(Trimethoxysilyl)propyl-N,N-didecyl-N-methylammoniumchlorid und/oder 3-(Trihydoxysilyl)propyl-N-octadecyl-N,N-dimethylammoniumchlorid und/oder Triclosan und/oder eine 10H-Benzo[G]pteridin-2,4-dion-Verbindung und/oder eine Flavin-Verbindung und/oder Selendiaryl-Verbindung und/oder Porphyrin-Verbindung und/oder Phthalocyanin-Verbindung und/oder Phenothiazinium-Verbindung und/oder Phenoxazinium-Verbindung und/oder Phenalen-1-on-Verbindung und/oder Zinkpyrithion-Verbindung.It is also generally within the scope of the invention that the antimicrobial substance contains Ag and / or Cu and / or Fe and / or Pt and / or Pd and / or Rh and / or Os and / or Au as elemental metal. Furthermore, it is within the scope of the invention that as an antimicrobial substance, in addition to or as an alternative to the inorganic metal compound or the elemental metal, it contains at least one organic compound and / or at least one polymeric compound. If an organic compound is used, a quaternary ammonium compound and / or quaternary phosphonium compound and / or pyridopyrazinedione compound (for example described in WO2020 / 053654 ) and / or an adefovir derivative (for example from Gilead® Sciences), for example adefovir dipivoxil [9- [2 - [[bis [(pivaloyloxy) methoxy] phosphinyl] methoxy] ethyl] adenine and / or tenofovir and / or [(2R) -1- (6-aminopurin-9-yl) propan-2-yl] oxymethylphosphonic acid and / or tenofovir alafenamide (eg described in US2019 / 0216831 ) and / or enmetazobactam and / or tazobactam and / or triaazaacenaphthalenes and / or 3- (trimethoxysilyl) propyl-N-octadecyl-N, N-dimethylammonium chloride and / or 3- (trimethoxysilyl) propyl-N-octadecyl-N, N- dimethylammonium chloride and / or 3- (trimethoxysilyl) propyl-N-tetradecyl-N, N-dimethylammonium chloride and / or 3- (trimethoxysilyl) propyl-N, N-didecyl-N-methylammonium chloride and / or 3- (trihydoxysilyl) propyl-N -octadecyl-N, N-dimethylammonium chloride and / or triclosan and / or a 10H-benzo [G] pteridine-2,4-dione compound and / or a flavin compound and / or selenium diaryl compound and / or porphyrin compound and / or phthalocyanine compound and / or phenothiazinium compound and / or phenoxazinium compound and / or phenalen-1-one compound and / or zinc pyrithione compound.

Sofern alternativ oder ergänzend als antimikrobielle Substanz eine polymere Verbindung verwendet wird, so eignet sich hierfür insbesondere ein(e) Ethylen-Copolymer mit Aminoalkylgruppenhaltigen (Meth)acrylat-Comonomeren (z.B. beschrieben in WO2019/110205 ) und/oder Poly(hexamethylenbiguanidin)hydrochlorid und/oder Polyaminopropylbiguanidin und/oder Hydroxyalkylcellulose modifiziert mit quaternären Ammoniumgruoppen und/oder Polyquaternium-n-Polymer (n = 4 - 30) und/oder Polyiminocarbonyl-Verbindung und/oder Polyethylenimin-Peptid-Konjugat und/oder Amphotensid und/oder Hydrophobin und/oder alpha-4-[1-tris(2-hydroxyethyl)ammoniumchlorid-2-butenyl]poly[1-dimethylammoniumchlorid-2-butenyl]-omega-tris(2-hdroxyethyl)ammoniumchlorid und/oder Poly[11-(N-piperidyl)undecan-1-(para-toloyl)sulfonat und/oder Poly(oxoethylen(dimethylimino)ethylen(dimethylimino)ethylendichlorid und/oder Poly(oxyethylen(dimethylimino)ethylen(dimethylimino)ethylendichlorid und/oder Poly(dodecyldimethyl(vinylbenzyl))ammoniumchlorid.If, as an alternative or in addition, a polymeric compound is used as the antimicrobial substance is used, an (e) ethylene copolymer with (meth) acrylate comonomers containing aminoalkyl groups (eg described in, for example) is suitable for this purpose WO2019 / 110205 ) and / or poly (hexamethylene biguanidine) hydrochloride and / or polyaminopropyl biguanidine and / or hydroxyalkyl cellulose modified with quaternary ammonium groups and / or polyquaternium-n-polymer (n = 4 - 30) and / or polyiminocarbonyl compound and / or polyethyleneimine-peptide conjugate and / or amphoteric surfactant and / or hydrophobin and / or alpha-4- [1-tris (2-hydroxyethyl) ammonium chloride-2-butenyl] poly [1-dimethylammonium chloride-2-butenyl] omega-tris (2-hydroxyethyl) ammonium chloride and / or poly [11- (N-piperidyl) undecane-1- (para-toloyl) sulfonate and / or poly (oxoethylene (dimethylimino) ethylene (dimethylimino) ethylene dichloride and / or poly (oxyethylene (dimethylimino) ethylene (dimethylimino) ethylene dichloride and / or poly (dodecyldimethyl (vinylbenzyl)) ammonium chloride.

Im Rahmen der Erfindung liegt es ferner, dass die antimikrobiell wirkende Substanz als Flüssigkeit oder Feststoff in und/oder auf einer Trägersubstanz dem pulverförmigen Werkstoff zugesetzt wird. So kann beispielsweise die flüssige oder feststoffförmige antimikrobiell wirkende Substanzen in fester und/oder flüssiger Form als Beschichtung, Niederschlag oder Abscheidung (z.B. aus der Gasphase) geträgert sein auf und/oder infiltriert sein in partikulären porösen Substanzen und/oder Substanzen mit membranartigen Oberflächen und/oder Substanzen mit diffusionsoffenen Oberflächen und/oder Substanzen mit geschlossener Oberfläche, wie z.B. Glashohlkugeln und/oder Glaskugeln und/oder Glimmer und/oder Fasern (z.B. Kaliumtitanatfasern und/oder Kohlefasern und/oder Glasfasern und/oder keramische Fasern), Polymerpartikeln und/oder Zeolithen und/oder Silikaten und/oder Aluminiumoxid und/oder Polymerpulver und/oder Glaspartikeln und/oder Aerosilen und/oder Kreide und/oder Zink-oxid und/oder Titandioxid und/oder Bariumsulfat und/oder Talkum und/oder einem Schichtsilikat.It is also within the scope of the invention that the antimicrobial substance is added to the powdery material as a liquid or solid in and / or on a carrier substance. For example, the liquid or solid-like antimicrobial substances in solid and / or liquid form as a coating, precipitate or deposit (e.g. from the gas phase) can be supported on and / or infiltrated in particulate porous substances and / or substances with membrane-like surfaces and / or substances with diffusion-open surfaces and / or substances with a closed surface, such as hollow glass spheres and / or glass spheres and / or mica and / or fibers (e.g. potassium titanate fibers and / or carbon fibers and / or glass fibers and / or ceramic fibers), polymer particles and / or Zeolites and / or silicates and / or aluminum oxide and / or polymer powder and / or glass particles and / or aerosils and / or chalk and / or zinc oxide and / or titanium dioxide and / or barium sulfate and / or talc and / or a sheet silicate.

Vorzugsweise ist die antimikrobiell wirkende Substanz pulverförmig mit einer mittleren Partikelgröße von 0,01 µm bis 150 µm ausgebildet. So kann insbesondere eine nanoskalige mittlere Partikelgröße von 10 nm - 50 nm (z.B. 20 nm - 40 nm) oder alternativ eine mittlere Partikelgröße von 10 µm bis 100 µm, insbesondere 30 bis 70 µm vorteilhaft sein. Das Gewichtsverhältnis von antimikrobiell wirkender Substanz zu pulverförmigem Werkstoff beträgt zweckmäßigerweise 0,2 bis 6 %, insbesondere 0,3 bis 3 %. Sofern nanoskalige Partikel verwendet werden, ist ein entsprechendes Gewichtsverhältnis von 0,1 bis 1 %, vorzugsweise 0,3 bis 0,8 % sinnvoll.The substance with an antimicrobial effect is preferably in powder form with an average particle size of 0.01 μm to 150 μm. In particular, a nanoscale average particle size of 10 nm - 50 nm (e.g. 20 nm - 40 nm) or, alternatively, an average particle size of 10 µm to 100 µm, in particular 30 to 70 µm, can be advantageous. The weight ratio of antimicrobial substance to powdery material is expediently 0.2 to 6%, in particular 0.3 to 3%. If nanoscale particles are used, a corresponding weight ratio of 0.1 to 1%, preferably 0.3 to 0.8%, makes sense.

Vorzugswesie besteht der pulverförmige Werkstoff aus Kunststoff, insbesondere einem Polyamid und/oder einem Polyolefin und/oder einem Polyester und/oder einem thermoplastischen Polyurethan und/oder einem Styrolcopolymer (z.B. ASA und/oder ABS und/oder SAN und/oder SEBS und/oder SEPS und/oder SBS und/oder SMMA) und/oder einem Polyetherimid und/oder einem Polyetheramid und/oder einem Polyetherketon und/oder einem Polyetheretherketon. Alternativ oder ergänzend kann der pulverförmige Werkstoff auch aus einem kunststoffbeschichteten Formsand wobei als Material für die Kunststoffbeschichtung der Formsandpartikel wiederum die vorgenannten Polymere bzw. Polymerkombinationen zum Einsatz kommen können. Im Rahmen der Erfindung liegt es, dass der Blend aus pulverförmigem Werkstoff und antimikrobiell wirkende Substanz mittels eines Dryblend-Verfahrens hergestellt wird, bei dem die Temperatur unterhalb des Erweichungspunktes des pulverförmigen Werkstoffs liegt. Vorzugsweise wird als Laser ein CO2-Laser, ein Nd:YAG-Laser oder ein Faserlaser verwendet.The powdery material preferably consists of plastic, in particular a polyamide and / or a polyolefin and / or a polyester and / or a thermoplastic polyurethane and / or a styrene copolymer (e.g. ASA and / or ABS and / or SAN and / or SEBS and / or SEPS and / or SBS and / or SMMA) and / or a polyetherimide and / or a polyetheramide and / or a polyetherketone and / or a polyetheretherketone. As an alternative or in addition, the powdery material can also consist of a plastic-coated molding sand, the aforementioned polymers or polymer combinations again being able to be used as the material for the plastic coating of the molding sand particles. It is within the scope of the invention that the blend is produced from powdery material and substance with an antimicrobial effect by means of a dryblend process in which the temperature is below the softening point of the powdery material. A CO 2 laser, an Nd: YAG laser or a fiber laser is preferably used as the laser.

Zweckmäßigerweise wird ein pulverförmiger Werkstoff mit einer mittleren Partikelgröße von 1 bis 500 µm, vorzugsweise 10 bis 200 µm, insbesondere 20 bis 100 µm verwendet. Vorzugsweise sind die entsprechenden Partikel zumindest im Wesentlichen rund (d.h. annhähernd kreis- bzw. kugelförmig) ausgebildet.A powdery material with an average particle size of 1 to 500 μm, preferably 10 to 200 μm, in particular 20 to 100 μm, is expediently used. The corresponding particles are preferably at least substantially round (i.e. approximately circular or spherical).

Mit dem erfindungsgemäßen Verfahren lassen sich die verschiedensten Gegenstände herstellen. Besonders bevorzugt sind hierbei Gegenstände, die bei Ihrem bestimmungsgemäßen Gebrauch von vielen verschiedenen Personen angefasst werden, z.B. Griffelemente, insbesondere für Türen, Fenster, Schubladen und dergl..A wide variety of objects can be produced with the method according to the invention. Particularly preferred are objects that are touched by many different people during their intended use, e.g. handle elements, especially for doors, windows, drawers and the like.

Im Folgenden wird die Erfindung anhand eines Ausführungsbeispiels erläutert:

  • Eine Zusammensetzung aus 95 Gew.-% lasersinterfähigem Polyamid-Pulver der Firma Farsoon Technologies mit der Bezeichnung „FS 3300PA PA1212-based powder“ (mittlere Partikelgröße 50 µm) und 5 Gew.-% ZnO2 Pulver mit einer mittleren Partikelgröße von 2 µm wird mittels eines Turbomischers trocken vermischt. Der Blend wird sodann auf einem SLS-Drucker (z.B. einem Farsoon SLS ST252P) zu einem Türgriff verarbeitet werden, welcher eine antimikrobielle Wirkung zeigt. Selbstverständlich wird durch dieses Ausführungsbeispiel die vorbeschriebene Offenbarung, insbesondere hinsichtlich der Nutzung unterschiedlichster antimikrobieller Substanzen, in keiner Weise eingeschränkt.
The invention is explained below using an exemplary embodiment:
  • A composition of 95% by weight of laser-sinterable polyamide powder from Farsoon Technologies with the designation “FS 3300PA PA1212-based powder” (mean particle size 50 µm) and 5% by weight of ZnO2 powder with a mean particle size of 2 µm is produced using a turbo mixer dry mixed. The blend is then processed on an SLS printer (eg a Farsoon SLS ST252P) into a door handle, which has an antimicrobial effect. Of course, the above-described disclosure, in particular with regard to the use of the most varied of antimicrobial substances, is in no way restricted by this exemplary embodiment.

ZITATE ENTHALTEN IN DER BESCHREIBUNGQUOTES INCLUDED IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant was generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.

Zitierte PatentliteraturPatent literature cited

  • EP 3266613 A1 [0005]EP 3266613 A1 [0005]
  • EP 3231833 A1 [0005]EP 3231833 A1 [0005]
  • EP 3231831 A1 [0005]EP 3231831 A1 [0005]
  • EP 3363849 A1 [0005]EP 3363849 A1 [0005]
  • WO 2020/053654 [0008]WO 2020/053654 [0008]
  • US 2019/0216831 [0008]US 2019/0216831 [0008]
  • WO 2019/110205 [0009]WO 2019/110205 [0009]

Claims (15)

Verfahren zur Herstellung eines Bauteils im Wege der additiven Fertigung, insbesondere durch selektives Lasersintern, wobei als Grundmaterial ein pulverförmiger Werkstoff eingesetzt wird, dadurch gekennzeichnet, dass dem pulverförmigen Werkstoff vor der Bauteilherstellung mindestens eine antimikrobiell wirkende Substanz zugesetzt wird, die sich während der additiven Fertigung thermisch stabil verhält.A method for manufacturing a component by means of additive manufacturing, in particular by selective laser sintering, a powdery material being used as the base material, characterized in that at least one antimicrobial substance is added to the powdery material before the component is manufactured, which substance changes thermally during additive manufacturing behaves stably. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass die antimikrobiell wirkende Substanz mindestens eine anorganische Metallverbindung und/oder mindestens ein elementares Metall enthält.Procedure according to Claim 1 , characterized in that the antimicrobial substance contains at least one inorganic metal compound and / or at least one elemental metal. Verfahren nach Anspruch 2, dadurch gekennzeichnet, dass als anorganische Metallverbindung mindestens ein(e) undotiertes und/oder dotiertes Metalloxid und/oder Metallhydroxid und/oder Metallmischoxid und/oder elementare Metallverbindung und/oder Metallphosphatverbindung und/oder Metallnitratverbindung und/oder Metallphosphatverbindung und/oder Metallsulfat- und/oder Metallsulfonatverbindung und/oder Metallphosphatglas und/oder eine Koordinationsverbindung mit einer organischen Ligandensphäre verwendet wird.Procedure according to Claim 2 , characterized in that at least one undoped and / or doped metal oxide and / or metal hydroxide and / or metal mixed oxide and / or elemental metal compound and / or metal phosphate compound and / or metal nitrate compound and / or metal phosphate compound and / or metal sulfate and / or metal sulfonate compound and / or metal phosphate glass and / or a coordination compound with an organic ligand sphere is used. Verfahren nach Anspruch 3, dadurch gekennzeichnet, dass - als undotiertes Metalloxid Zinkperoxid und/oder Zinkoxid und/oder Kupferoxid und/oder Eisenoxid und/oder Titandioxid und/oder Silberoxid und/oder Platinoxid und/oder Palladiumoxid und/oder Rhodiumoxid und/oder Rutheniumoxid und/oder osmiumoxid und/oder Manganoxid und/oder - als dotiertes Metalloxid Zinkoxid mit Fe, Ag, Pt, Pd, Rh, Ru, Au, Os, Mn, Cu, Ti, AI, Mg, Eisenoxid, Silberoxid, Kupferoxid, Titandioxid, Aluminiumoxid, Magnesiumoxid, Calciumoxid als Dotierungspartner und/oder Titandioxid mit Fe, Ag, Cu, Zn, Pt, Pd, Rh, Ru, Au, Os, Mn, AI / Eisenoxid, Silberoxid, Kupferoxid, Zinkdioxid, Aluminiumoxid, Magnesiumoxid, Calciumoxid als Dotierungspartner und/oder Kupferoxid mit Fe, Ag, Ti, Zn, Pt, Pd, Rh, Ru, Au, Os, Mn, AI / Eisenoxid, Silberoxid, Zinkoxid, Titandioxid, Aluminiumoxid, Magnesiumoxid, Calciumoxid als Dotierungspartner und/oder Eisenoxid mit Ag, Ti, Zn, Pt, Pd, Rh, Ru, Au, Os, Mn, AI / Kupferoxid, Silberoxid, Zinkoxid, Titandioxid, Aluminiumoxid, Magnesiumoxid, Calciumoxid als Dotierungspartner, und/oder Silberoxid mit Fe, Cu, Ti, Zn, Pt, Pd, Rh, Ru, Au, Os, Mn, AI / Eisenoxid, Kupferoxid, Zinkoxid, Titandioxid, Aluminiumoxid, Magnesiumoxid, Calciumoxid als Dotierungspartner und/oder Platinoxid mit Ag, Ti, Zn, Fe, Pd, Rh, Ru, Au, Os, Mn, Cu, AI / Kupferoxid, Silberoxid, Zinkoxid, Titandioxid, Aluminiumoxid, Magnesiumoxid, Manganoxid, Rhodiumoxid, Palladiumoxid, Rutheniumoxid, Calciumoxid als Dotierungspartner, und/oder Palladiumoxid mit Ag, Ti, Zn, Pt, Fe, Rh, Ru, Au, Os, Mn, Cu, AI / Kupferoxid, Silberoxid, Zinkoxid, Titandioxid, Aluminiumoxid, Magnesiumoxid, Manganoxid, Rhodiumoxid, Platinoxid, Rutheniumoxid, Calciumoxid als Dotierungspartner, und/oder Rhodiumoxid mit Ag, Ti, Zn, Pt, Fe, Pd, Ru, Au, Os, Cu, Mn, AI / Kupferoxid, Silberoxid, Zinkoxid, Titandioxid, Aluminiumoxid, Magnesiumoxid, Manganoxid, Rhodiumoxid, Platinoxid, Rutheniumoxid, Calciumoxid als Dotierungspartner, und/ode Rutheniumoxid mit Ag, Ti, Zn, Pt, Fe, Pd, Rh, Au, Os, Cu, Mn, AI / Kupferoxid, Silberoxid, Zinkoxid, Titandioxid, Aluminiumoxid, Magnesiumoxid, Manganoxid, Rhodiumoxid, Platinoxid, Rutheniumoxid, Calciumoxid als Dotierungspartner, und/oder Osmiumoxid mit Ag, Ti, Zn, Pt, Fe, Pd, Rh, Au, Ru, Mn, Cu, AI / Kupferoxid, Silberoxid, Zinkoxid, Titandioxid, Aluminiumoxid, Magnesiumoxid, Manganoxid, Rhodiumoxid, Platinoxid, Rutheniumoxid, Calciumoxid als Dotierungspartner, und/oder Manganoxid mit Ag, Ti, Zn, Pt, Fe, Pd, Rh, Au, Ru, Os, Cu, AI / Kupferoxid, Silberoxid, Zinkoxid, Titandioxid, Aluminiumoxid, Magnesiumoxid, Manganoxid, Rhodiumoxid, Platinoxid, Rutheniumoxid, Calciumoxid als Dotierungspartner, und/oder - als Metallhydroxid Calciumhydroxid, ein Hydroxid des Eisens, Kupfers, Mangans, Zinks, Titans, Platins, Rutheniums, Osmiums, Silbers und/oder - eine Koordinationsverbindung mit einer organischen Ligandensphäre mit Ag, Ti, Zn, Pt, Fe, Pd, Rh, Au, Ru, Mn, Al, Cu als Koordinationszentrum und wenigstens einer organischen Verbindung (ungeladen und/oder ionisch), welche die Elemente, ausgewählt aus C, N, O, S, P, Si, Sb, As, F, Cl, Br, I umfaßt, verwendet wird.Procedure according to Claim 3 , characterized in that - as undoped metal oxide zinc peroxide and / or zinc oxide and / or copper oxide and / or iron oxide and / or titanium dioxide and / or silver oxide and / or platinum oxide and / or palladium oxide and / or rhodium oxide and / or ruthenium oxide and / or osmium oxide and / or manganese oxide and / or - as a doped metal oxide zinc oxide with Fe, Ag, Pt, Pd, Rh, Ru, Au, Os, Mn, Cu, Ti, Al, Mg, iron oxide, silver oxide, copper oxide, titanium dioxide, aluminum oxide, magnesium oxide , Calcium oxide as doping partner and / or titanium dioxide with Fe, Ag, Cu, Zn, Pt, Pd, Rh, Ru, Au, Os, Mn, Al / iron oxide, silver oxide, copper oxide, zinc dioxide, aluminum oxide, magnesium oxide, calcium oxide as doping partner and / or copper oxide with Fe, Ag, Ti, Zn, Pt, Pd, Rh, Ru, Au, Os, Mn, Al / iron oxide, silver oxide, zinc oxide, titanium dioxide, aluminum oxide, magnesium oxide, calcium oxide as doping partner and / or iron oxide with Ag, Ti , Zn, Pt, Pd, Rh, Ru, Au, Os, Mn, Al / copper oxide, silver oxide, zinc oxide, titanium dioxide, alumin iumoxid, magnesium oxide, calcium oxide as doping partner, and / or silver oxide with Fe, Cu, Ti, Zn, Pt, Pd, Rh, Ru, Au, Os, Mn, Al / iron oxide, copper oxide, zinc oxide, titanium dioxide, aluminum oxide, magnesium oxide, calcium oxide as doping partner and / or platinum oxide with Ag, Ti, Zn, Fe, Pd, Rh, Ru, Au, Os, Mn, Cu, Al / copper oxide, silver oxide, zinc oxide, titanium dioxide, aluminum oxide, magnesium oxide, manganese oxide, rhodium oxide, palladium oxide, ruthenium oxide , Calcium oxide as doping partner, and / or palladium oxide with Ag, Ti, Zn, Pt, Fe, Rh, Ru, Au, Os, Mn, Cu, Al / copper oxide, silver oxide, zinc oxide, titanium dioxide, aluminum oxide, magnesium oxide, manganese oxide, rhodium oxide, Platinum oxide, ruthenium oxide, calcium oxide as doping partner, and / or rhodium oxide with Ag, Ti, Zn, Pt, Fe, Pd, Ru, Au, Os, Cu, Mn, Al / copper oxide, silver oxide, zinc oxide, titanium dioxide, aluminum oxide, magnesium oxide, manganese oxide , Rhodium oxide, platinum oxide, ruthenium oxide, calcium oxide as doping partner, and / or ruthenium oxide with Ag, Ti, Zn, Pt , Fe, Pd, Rh, Au, Os, Cu, Mn, Al / copper oxide, silver oxide, zinc oxide, titanium dioxide, aluminum oxide, magnesium oxide, manganese oxide, rhodium oxide, platinum oxide, ruthenium oxide, calcium oxide as doping partner, and / or osmium oxide with Ag, Ti, Zn, Pt, Fe, Pd, Rh, Au, Ru, Mn, Cu, Al / copper oxide, silver oxide, zinc oxide, titanium dioxide, aluminum oxide, magnesium oxide, manganese oxide, rhodium oxide, platinum oxide, ruthenium oxide, calcium oxide as a doping partner, and / or manganese oxide with Ag , Ti, Zn, Pt, Fe, Pd, Rh, Au, Ru, Os, Cu, Al / copper oxide, silver oxide, zinc oxide, titanium dioxide, aluminum oxide, magnesium oxide, manganese oxide, rhodium oxide, platinum oxide, ruthenium oxide, calcium oxide as doping partner, and / or - as metal hydroxide calcium hydroxide, a hydroxide of iron, copper, manganese, zinc, titanium, platinum, ruthenium, osmium, silver and / or - a coordination compound with an organic ligand sphere with Ag, Ti, Zn, Pt, Fe, Pd, Rh, Au, Ru, Mn, Al, Cu as coordination center and at least one organic n Compound (uncharged and / or ionic) comprising the elements selected from C, N, O, S, P, Si, Sb, As, F, Cl, Br, I is used. Verfahren nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, dass die antimikrobiell wirkende Substanz als elementares Metall Ag und/oder Cu und/oder Fe und/oder Pt und/oder Pd und/oder Rh und/oder Os und/oder Au enthält.Method according to one of the Claims 1 until 4th , characterized in that the antimicrobial substance contains Ag and / or Cu and / or Fe and / or Pt and / or Pd and / or Rh and / or Os and / or Au as elemental metal. Verfahren nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, dass die antimikrobiell wirkende Substanz mindestens eine organische Verbindung und/oder mindestens eine polymere Verbindung enthält.Method according to one of the Claims 1 until 5 , characterized in that the antimicrobial substance contains at least one organic compound and / or at least one polymeric compound. Verfahren nach Anspruch 6, dadurch gekennzeichnet, dass als organische Verbindung eine quaternäre Ammoniumverbindung und/oder quaternäre Phosphoniumverbindung und/oder Pyridopyrazindion-Verbindung und/oder ein Adefovir-Derivat, bspw. Adefovir dipivoxil [9-[2-[[bis[(pivaloyloxy)methoxy]phosphinyl]-methoxy]ethyl]adenin und/oder Tenofovir und/oder [(2R)-1-(6-aminopurin-9-yl)propan-2-yl]oxymethylphosphonsäure und/oder Tenofoviralafenamid, und/oder Enmetazobactam und/oder Tazobactam und/oder Triaazaacenaphthalene und/oder 3-(Trimethoxysilyl)propyl-N-octadecyl-N,N-dimethylammoniumchlorid und/oder 3-(Trimethoxysilyl)propyl-N-octadecyl-N,N-dimethylammoniumchlorid und/oder 3-(Trimethoxysilyl)propyl-N-tetradecyl-N,N-dimethylammoniumchlorid und/oder 3-(Trimethoxysilyl)propyl-N,N-didecyl-N-methylammoniumchlorid und/oder 3-(Trihydoxysilyl)propyl-N-octadecyl-N,N-dimethylammoniumchlorid und/oder Triclosan und/oder eine 10H-Benzo[G]pteridin-2,4-dion-Verbindung und/oder eine Flavin-Verbindung und/oder Selendiaryl-Verbindung und/oder Porphyrin-Verbindung und/oder Phthalocyanin-Verbindung und/oder Phenothiazinium-Verbindung und/oder Phenoxazinium-Verbindung und/oder Phenalen-1-on-Verbindung und/oder Zinkpyrithion-Verbindung verwendet wird.Procedure according to Claim 6 , characterized in that the organic compound is a quaternary ammonium compound and / or quaternary phosphonium compound and / or pyridopyrazinedione compound and / or an adefovir derivative, for example adefovir dipivoxil [9- [2 - [[bis [(pivaloyloxy) methoxy] phosphinyl) ] -methoxy] ethyl] adenine and / or tenofovir and / or [(2R) -1- (6-aminopurin-9-yl) propan-2-yl] oxymethylphosphonic acid and / or tenofovir alafenamide, and / or enmetazobactam and / or tazobactam and / or triaazaacenaphthalene and / or 3- (Trimethoxysilyl) propyl-N-octadecyl-N, N-dimethylammonium chloride and / or 3- (trimethoxysilyl) propyl-N-octadecyl-N, N-dimethylammonium chloride and / or 3- (trimethoxysilyl) propyl-N-tetradecyl-N, N -dimethylammonium chloride and / or 3- (trimethoxysilyl) propyl-N, N-didecyl-N-methylammonium chloride and / or 3- (trihydoxysilyl) propyl-N-octadecyl-N, N-dimethylammonium chloride and / or triclosan and / or a 10H- Benzo [G] pteridine-2,4-dione compound and / or a flavin compound and / or selenium diaryl compound and / or porphyrin compound and / or phthalocyanine compound and / or phenothiazinium compound and / or phenoxazinium compound and / or phenalen-1-one compound and / or zinc pyrithione compound is used. Verfahren nach Anspruch 6 oder 7, dadurch gekennzeichnet, dass als polymere Verbindung ein(e) Ethylen-Copolymer mit Aminoalkylgruppenhaltigen (Meth)acrylat-Comonomeren und/oder Poly(hexamethylenbiguanidin)hydrochlorid und/oder Polyaminopropylbiguanidin und/oder Hydroxyalkylcellulose modifiziert mit quaternären Ammoniumgruoppen und/oder Polyquaternium-n-Polymer (n = 4 - 30) und/oder Polyiminocarbonyl-Verbindung und/oder Polyethylenimin-Peptid-Konjugat und/oder Amphotensid und/oder Hydrophobin und/oder alpha-4-[1-tris(2-hydroxyethyl)ammoniumchlorid-2-butenyl]poly[1-dimethylammoniumchlorid-2-butenyl]-omega-tris(2-hdroxyethyl)ammoniumchlorid und/oder Poly[11-(N-piperidyl)undecan-1-(para-toloyl)sulfonat und/oder Poly(oxoethylen(dimethylimino)ethylen(dimethylimino)ethylendichlorid und/oder Poly(oxyethylen(dimethylimino)ethylen(dimethylimino)ethylendichlorid und/oder Poly(dodecyldimethyl(vinylbenzyl))ammoniumchlorid verwendet wird.Procedure according to Claim 6 or 7th , characterized in that the polymeric compound is an ethylene copolymer with (meth) acrylate comonomers containing aminoalkyl groups and / or poly (hexamethylene biguanidine) hydrochloride and / or polyaminopropyl biguanidine and / or hydroxyalkyl cellulose modified with quaternary ammonium groups and / or polyquaternium-n- Polymer (n = 4 - 30) and / or polyiminocarbonyl compound and / or polyethyleneimine-peptide conjugate and / or amphoteric surfactant and / or hydrophobin and / or alpha-4- [1-tris (2-hydroxyethyl) ammonium chloride-2- butenyl] poly [1-dimethylammonium chloride-2-butenyl] omega-tris (2-hydroxyethyl) ammonium chloride and / or poly [11- (N-piperidyl) undecane-1- (para-toloyl) sulfonate and / or poly (oxoethylene (dimethylimino) ethylene (dimethylimino) ethylene dichloride and / or poly (oxyethylene (dimethylimino) ethylene (dimethylimino) ethylene dichloride and / or poly (dodecyldimethyl (vinylbenzyl)) ammonium chloride is used. Verfahren nach einem der Ansprüche 1 bis 8, dadurch gekennzeichnet, dass die antimikrobiell wirkende Substanz als Flüssigkeit oder Feststoff in und/oder auf einer Trägersubstanz dem pulverförmigen Werkstoff zugesetzt wird.Method according to one of the Claims 1 until 8th , characterized in that the antimicrobial substance is added to the powdery material as a liquid or solid in and / or on a carrier substance. Verfahren nach einem der Ansprüche 1 bis 9, dadurch gekennzeichnet, dass die antimikrobiell wirkende Substanz pulverförmig mit einer mittleren Partikelgröße von 0,01 µm bis 150 µm, vorzugsweise nanoskalig 10 nm - 50 nm, insbesondere 20 nm - 40 nm oder vorzugsweise 10 µm bis 100 µm, insbesondere 30 bis 70 µm ausgebildet ist.Method according to one of the Claims 1 until 9 , characterized in that the antimicrobial substance in powder form with an average particle size of 0.01 µm to 150 µm, preferably nanoscale 10 nm - 50 nm, in particular 20 nm - 40 nm or preferably 10 µm to 100 µm, in particular 30 to 70 µm is trained. Verfahren nach einem der Ansprüche 1 bis 10, dadurch gekennzeichnet, dass das Gewichtsverhältnis von antimikrobiell wirkender Substanz zu pulverförmigem Werkstoff 0,2 bis 6 %, insbesondere 0,3 bis 3 % beträgt.Method according to one of the Claims 1 until 10 , characterized in that the weight ratio of antimicrobial substance to powdery material is 0.2 to 6%, in particular 0.3 to 3%. Verfahren nach einem der Ansprüche 1 bis 11, dadurch gekennzeichnet, dass der pulverförmige Werkstoff aus Kunststoff, insbesondere einem Polyamid und/oder einem Polyolefin und/oder einem Polyester und/oder einem thermoplastischen Polyurethan und/oder einem Styrolcopolymer und/oder einem Polyetherimid und/oder einem Polyetheramid und/oder einem Polyetherketon und/oder einem Polyetheretherketon und/oder einem kunststoffbeschichteten Formsand besteht.Method according to one of the Claims 1 until 11th , characterized in that the powdery material is made of plastic, in particular a polyamide and / or a polyolefin and / or a polyester and / or a thermoplastic polyurethane and / or a styrene copolymer and / or a polyetherimide and / or a polyetheramide and / or a polyetherketone and / or a polyetheretherketone and / or a plastic-coated molding sand. Verfahren nach einem der Ansprüche 1 bis 12, dadurch gekennzeichnet, dass der Blend aus pulverförmigem Werkstoff und antimikrobiell wirkende Substanz mittels eines Dryblend-Verfahrens hergestellt wird, bei dem die Temperatur unterhalb des Erweichungspunktes des pulverförmigen Werkstoffs liegt.Method according to one of the Claims 1 until 12th , characterized in that the blend of powdery material and antimicrobial substance is produced by means of a dryblend process in which the temperature is below the softening point of the powdery material. Verfahren nach einem der Ansprüche 1 bis 13, dadurch gekennzeichnet, dass ein pulverförmiger Werkstoff mit einer mittleren Partikelgröße von 1 bis 500 µm, vorzugsweise 10 bis 200 µm, insbesondere 20 bis 100 µm verwendet wird.Method according to one of the Claims 1 until 13th , characterized in that a powdery material with an average particle size of 1 to 500 µm, preferably 10 to 200 µm, in particular 20 to 100 µm is used. Gegenstand, hergestellt mit einem Verfahren nach einem der Ansprüche 1 bis 14, insbesondere Griffelement.Article produced by a method according to one of the Claims 1 until 14th , in particular handle element.
DE102020119683.0A 2020-06-25 2020-07-27 Process for manufacturing a component using additive manufacturing Pending DE102020119683A1 (en)