DE102018004943A1 - Preservative-free pigment paste - Google Patents

Preservative-free pigment paste Download PDF

Info

Publication number
DE102018004943A1
DE102018004943A1 DE102018004943.5A DE102018004943A DE102018004943A1 DE 102018004943 A1 DE102018004943 A1 DE 102018004943A1 DE 102018004943 A DE102018004943 A DE 102018004943A DE 102018004943 A1 DE102018004943 A1 DE 102018004943A1
Authority
DE
Germany
Prior art keywords
pigment paste
pigment
weight
paste
siliconate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE102018004943.5A
Other languages
German (de)
Inventor
Ingo Hörsting
Jan Leusmann
Dietmar Erber
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Brillux GmbH and Co KG
Original Assignee
Brillux GmbH and Co KG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Brillux GmbH and Co KG filed Critical Brillux GmbH and Co KG
Priority to DE102018004943.5A priority Critical patent/DE102018004943A1/en
Priority to EP19733717.3A priority patent/EP3810709A1/en
Priority to PCT/EP2019/066507 priority patent/WO2019243593A1/en
Publication of DE102018004943A1 publication Critical patent/DE102018004943A1/en
Pending legal-status Critical Current

Abstract

Eine Pigmentpaste enthaltend, jeweils bezogen auf das Gesamtgewicht der Pigmentpaste, 1 bis 75 Gew.% Pigment, 0,1 bis 10 Gew.% Silikonat, 0,5 bis 30 Gew.% Netzmittel und 15 bis 75 Gew.% Wasser, wobei der pH Wert der Pigmentpaste von 10 bis 14 beträgt sowie ein Verfahren zur Herstellung einer solchen Pigmentpaste, ein Überzugsmittel enthaltend mindestens ein Beschichtungsmittel und mindestens eine solche Pigmentpaste und ein Verfahren zur Herstellung eines Überzugsmittels werden beschrieben.A pigment paste containing, based in each case on the total weight of the pigment paste, 1 to 75% by weight of pigment, 0.1 to 10% by weight of siliconate, 0.5 to 30% by weight of wetting agent and 15 to 75% by weight of water, the The pH value of the pigment paste is from 10 to 14 and a method for producing such a pigment paste, a coating agent containing at least one coating agent and at least one such pigment paste and a method for producing a coating agent are described.

Description

Die Erfindung betrifft eine Pigmentpaste zum Abtönen eines Beschichtungsmittels, ein Verfahren zur Herstellung der Pigmentpaste sowie ein Überzugsmittel enthaltend Beschichtungsmittel und Pigmentpaste. Die Erfindung betrifft ferner ein Verfahren zur Herstellung eines Überzugsmittels unter Verwendung der Pigmentpaste und die Verwendung von Silikonat zur Stabilisierung und/oder Erhöhung der Lagerstabilität von Pigmentpasten.The invention relates to a pigment paste for tinting a coating agent, a process for producing the pigment paste and a coating agent containing coating agents and pigment paste. The invention further relates to a method for producing a coating composition using the pigment paste and the use of siliconate for stabilizing and / or increasing the storage stability of pigment pastes.

Pigmentpasten zum Abtönen von Beschichtungsmitteln, wie beispielsweise Farben und Lacken, sind grundsätzlich bekannt. Pigmentpasten werden üblicherweise durch Dispergieren von Pigmenten und gegebenenfalls Füllstoffen und anderen geeigneten Materialien hergestellt und vor dem Einsatz mit dem abzutönenden Beschichtungsmittel vermischt. Derartige Farbmischsysteme sind herkömmlichen Beschichtungsmitteln insbesondere im Hinblick auf Bevorratung und Logistik überlegen. Abgetönte Beschichtungsmittel enthalten mindestens ein Beschichtungsmittel und mindestens eine Pigmentpaste. Abgetönte Beschichtungsmittel werden auch als Überzugsmittel bezeichnet.Pigment pastes for tinting coating agents, such as paints and lacquers, are generally known. Pigment pastes are usually produced by dispersing pigments and, if appropriate, fillers and other suitable materials and mixed with the coating agent to be tinted before use. Color mixing systems of this type are superior to conventional coating materials, particularly with regard to storage and logistics. Tinted coating compositions contain at least one coating composition and at least one pigment paste. Tinted coating agents are also referred to as coating agents.

Im Vergleich zum Zumischen pulverförmiger Pigmente zu einem Beschichtungsmittel haben Pigmentpasten den Vorteil, dass sich diese einfach und homogen verteilen lassen und gut zu dosieren sind. Weiter vorteilhaft ist, dass sie keinen Farbstaub enthalten, da dieser beim Zumischen leicht die Umgebung verunreinigt. Schließlich können Pigmentpasten auf die erwünschte Farbstärke eingestellt und daher auf einfache Weise über das Volumen in ein Beschichtungsmittel wie beispielsweise eine Kunststoffdispersionsfarbe eindosiert und eingerührt werden.Compared to adding powdered pigments to a coating agent, pigment pastes have the advantage that they can be distributed easily and homogeneously and are easy to dose. It is also advantageous that they do not contain paint dust, since this easily contaminates the environment when mixed. Finally, pigment pastes can be adjusted to the desired color strength and can therefore be metered in and mixed in in a simple manner via the volume into a coating agent such as, for example, a plastic emulsion paint.

Grundsätzlich können Pigmentpasten zum Abtönen von ganz unterschiedlichen Beschichtungsmitteln eingesetzt werden. Ein bedeutender Bereich ist hierbei das Abtönen von Kunststoffdispersionsfarbe, auch bekannt als Dispersionsfarbe. Dispersionsfarben enthalten üblicherweise relativ große Mengen an organischchemischen Bestandteilen, insbesondere an Kunstharzpolymeren, insbesondere in Form von Kunstharzdispersionen.In principle, pigment pastes can be used to tint very different coating agents. An important area here is the tinting of plastic emulsion paint, also known as emulsion paint. Dispersion paints usually contain relatively large amounts of organic chemical components, in particular synthetic resin polymers, in particular in the form of synthetic resin dispersions.

Um eine ausreichende Lagerstabilität zu gewährleisten, benötigen Dispersionsfarben und/oder Pigmentpasten üblicherweise Konservierungsmittel, insbesondere Biozide, wie Isothiazolinone. Diese können jedoch insbesondere bei Allergikern Reizungen und Hautirritationen hervorrufen.In order to ensure adequate storage stability, emulsion paints and / or pigment pastes usually require preservatives, in particular biocides, such as isothiazolinones. However, these can cause irritation and skin irritation, especially in allergy sufferers.

In den vergangenen Jahren sind Dispersionsfarben entwickelt worden, die auf Konservierungsmittel verzichten. In den Druckschriften EP 1 297 079 B1 , DE 1 031 910 , DE 10 2014 013 455 A1 und DE 10 2016 002 221 A1 werden jeweils Dispersionsfarben beschrieben, die ohne Konservierungsmittel auskommen. Allerdings wird in keiner dieser Druckschriften eine Pigmentpaste beschrieben, die auf Konservierungsmittel, insbesondere Biozide wie Isothiazolinon, verzichtet. Somit muss auf konservierungsmittelhaltige Pigmentpasten zurückgegriffen werden, um diese konservierungsmittelfreien Dispersionsfarben abzutönen.In recent years, emulsion paints have been developed that do without preservatives. In the pamphlets EP 1 297 079 B1 . DE 1 031 910 . DE 10 2014 013 455 A1 and DE 10 2016 002 221 A1 are described in each case emulsion paints that do not require preservatives. However, none of these publications describe a pigment paste that does without preservatives, in particular biocides such as isothiazolinone. This means that pigment pastes containing preservatives have to be used to tint these preservative-free emulsion paints.

Aus diesem Grund können die oben beschriebenen Dispersionsfarben nicht konservierungsmittelfrei abgetönt werden. Durch den Einsatz einer konservierungsmittelhaltigen Pigmentpaste wird somit Konservierungsmittel in die Dispersionsfarbe eingebracht und die abgetönte Dispersionsfarbe eignet sich nicht mehr für die Anwendung für Allergiker.For this reason, the emulsion paints described above cannot be tinted without preservatives. By using a pigment paste containing preservatives, preservatives are introduced into the emulsion paint and the tinted emulsion paint is no longer suitable for use by allergy sufferers.

Die Herstellung einer konservierungsmittelfreien Pigmentpaste erscheint allerdings aus mehreren Gründen schwieriger als die Herstellung einer konservierungsmittelfreien Dispersionsfarbe.However, the production of a preservative-free pigment paste appears more difficult than the production of a preservative-free emulsion paint for several reasons.

Das hängt zunächst damit zusammen, dass Pigmentpasten deutlich stärker in ihren Zusammensetzungen und Konzentrationen variieren als Dispersionsfarben. Die Menge an Pigment und Wasser kann in größeren Bereichen variieren als für Dispersionsfarben üblich und folglich können Pigmentpasten auch eine größere Varianz in ihrer Viskosität aufweisen. Eine weitere besondere Herausforderung an Pigmentpasten im Vergleich zu Dispersionsfarben liegt in der hohen Flexibilität, die Pigmentpasten bereitstellen müssen. Die Pigmentpasten sollen flexibel mit ganz unterschiedlichen Farben, Lacken oder Putzen vermischt werden können. Hierfür muss die Pigmentpaste eine gute Mischbarkeit und Kompatibilität mit unterschiedlichen Beschichtungsmitteln aufweisen. Die Beschichtungsmittel weisen teilweise bedeutende Unterschiede in ihrer Zusammensetzung und ihrem pH Wert auf. Daher ist ein solches Maß an Mischbarkeit und Kompatibilität der Pigmentpasten schwer zu erreichen.This is due to the fact that pigment pastes vary significantly more in their compositions and concentrations than emulsion paints. The amount of pigment and water can vary in larger ranges than usual for emulsion paints and consequently pigment pastes can also have a greater variance in their viscosity. Another particular challenge with pigment pastes compared to emulsion paints is the high flexibility that pigment pastes have to provide. The pigment pastes should be able to be mixed flexibly with very different colors, varnishes or plasters. For this, the pigment paste must have good miscibility and compatibility with different coating agents. The coating compositions sometimes have significant differences in their composition and pH. Such a degree of miscibility and compatibility of the pigment pastes is therefore difficult to achieve.

Außerdem sind die Lagerungsanforderungen an Pigmentpasten deutlich höher als die Lagerungsanforderung an Dispersionsfarben. Pigmentpasten müssen üblicherweise für deutlich längere Zeiträume gelagert werden, da sie oft unregelmäßig zum Abtönen von Farben eingesetzt werden und nicht wie fertige Farben relativ zügig aufgebraucht werden. Dort unterliegen diese einer Belastung durch Schädlinge aus der Luft in Kombination mit der hohen Luftfeuchtigkeit im Mischbehälter. Zudem wird Pigmentpasten im Mischautomaten beim Abpumpen zusätzlich weiterer Luftsauerstoff zugefügt, der in der Paste durch das permanente Mischen zudem gut verteilt wird. Der zugefügte Luftsauerstoff kann Schädlinge miteinbringen und deren Wachstum fördern. Beim Abpumpen eines Teils der Paste im Mischautomaten setzt sich zudem an den oberen Innenseiten des Behälters in dem die Paste im Mischautomaten vorliegt, ein hochkonzentrierter, feuchter, pulverförmiger Absatz der Paste ab, der ein hervorragender Nährboden für Schädlinge darstellt. Deshalb enthalten Pigmentpasten üblicherweise neben einem höheren Gehalt an Topfkonservierern auch Fungizide zur Vermeidung von Befall im Mischbehälter. In addition, the storage requirements for pigment pastes are significantly higher than the storage requirements for emulsion paints. Pigment pastes usually have to be stored for significantly longer periods, since they are often used irregularly to tint colors and are not used up relatively quickly like finished colors. There they are exposed to pests from the air in combination with the high humidity in the mixing container. In addition, pigment pastes are added in the automatic mixer when pumping out additional atmospheric oxygen, which is also well distributed in the paste due to the permanent mixing. The added atmospheric oxygen can bring pests and promote their growth. When pumping out part of the paste in the automatic mixer, a highly concentrated, moist, powdery deposit of the paste is deposited on the upper inside of the container in which the paste is present, which is an excellent breeding ground for pests. Therefore, pigment pastes usually contain not only a higher level of in-can preservatives, but also fungicides to prevent infestation in the mixing container.

Aufgrund der deutlich längeren Lagerzeiten stellt sich bei Pigmentpasten auch die Schwierigkeit, dass die Pigmente über deutlich längere Zeiträume den Bedingungen in der Paste ausgesetzt sind als in einer Dispersionsfarbe. Die in den Druckschriften EP 1 297 079 B1 , DE 1 031 910 , DE 10 2014 013 455 A1 und DE 10 2016 002 221 A1 beschriebenen konservierungsmittelfreien Dispersionsfarben benötigen ein stark alkalisches Milieu um den Befall durch Schädlinge zu verhindern. In einer konzentrierten und über lange Zeiträume anzuwendenden Paste stellt sich die Gefahr, dass die Pigmentpaste in der Form nicht dauerhaft stabil und in allen erforderlichen Qualitäten kontinuierlich kompatibel ist.Due to the significantly longer storage times with pigment pastes, there is also the difficulty that the pigments are exposed to the conditions in the paste for significantly longer periods than in an emulsion paint. The ones in the pamphlets EP 1 297 079 B1 . DE 1 031 910 . DE 10 2014 013 455 A1 and DE 10 2016 002 221 A1 The preservative-free emulsion paints described require a strongly alkaline environment in order to prevent infestation by pests. In a concentrated paste that can be used over a long period of time, there is a risk that the pigment paste will not be permanently stable in the form and will be continuously compatible in all the required qualities.

Die vorliegende Erfindung stellt sich somit die Aufgabe, eine konservierungsmittelfreie Pigmentpaste bereitzustellen, die über Zeiträume von mindestens sechs Monaten ohne jeglichen Qualitätsverlust und ohne Schädlingsbefall zum Abtönen eines Beschichtungsmittels, insbesondere in Farbmischautomaten, einsetzbar ist.The present invention therefore has as its object to provide a preservative-free pigment paste which can be used over a period of at least six months without any loss of quality and without pest infestation for tinting a coating agent, in particular in automatic paint mixers.

Die vorliegende Erfindung stellt sich weiterhin die Aufgabe, eine konservierungsmittelfreie Pigmentpaste bereitzustellen, die flexibel zum Abtönen von unterschiedlichen Beschichtungsmitteln genutzt werden kann.The present invention further has the object of providing a preservative-free pigment paste which can be used flexibly for tinting different coating agents.

Des Weiteren stellt sich die Erfindung die Aufgabe, eine konservierungsmittelfreie Pigmentpaste bereitzustellen, die in Mischbehältern von Mischautomaten im Wesentlichen ohne Qualitätsverlust und im Wesentlichen ohne Schädlingsbefall zum Abtönen von Beschichtungssystemen eingesetzt werden kann.Furthermore, the object of the invention is to provide a preservative-free pigment paste which can be used in mixing containers of automatic mixers essentially without loss of quality and essentially without pest infestation for tinting coating systems.

Alle oder einige dieser Aufgaben werden erfindungsgemäß durch die Pigmentpaste von Anspruch 1, das Verfahren nach Anspruch 11, das Verfahren nach Anspruch 13, das Überzugsmittel nach Anspruch 15, sowie die Verwendung nach Anspruch 17 gelöst.All or some of these objects are achieved according to the invention by the pigment paste of claim 1, the method according to claim 11, the method according to claim 13, the coating agent according to claim 15, and the use according to claim 17.

Vorteilhafte Ausgestaltungen der Erfindung sind in den abhängigen Ansprüchen angegeben und werden nachfolgend im Einzelnen erläutert.Advantageous embodiments of the invention are specified in the dependent claims and are explained in detail below.

Die erfindungsgemäße Pigmentpaste enthält, jeweils bezogen auf das Gesamtgewicht der Pigmentpaste,

  1. a. 1 bis 75 Gew.% Pigment,
  2. b. 0,1 bis 10 Gew.% Silikonat,
  3. c. 0,5 bis 30 Gew.% Netzmittel,
  4. d. 15 bis 75 Gew.% Wasser,
wobei der pH Wert der Pigmentpaste von 10 bis 14 beträgt.The pigment paste according to the invention contains, based in each case on the total weight of the pigment paste,
  1. a. 1 to 75% by weight pigment,
  2. b. 0.1 to 10% by weight of siliconate,
  3. c. 0.5 to 30% by weight of wetting agent,
  4. d. 15 to 75% by weight of water,
the pH value of the pigment paste is from 10 to 14.

Überraschend hat sich gezeigt, dass eine Pigmentpaste enthaltend, jeweils bezogen auf das Gesamtgewicht der Pigmentpaste, 1 bis 75 Gew.% Pigment, 0,1 bis 10 Gew.% Silikonat, 0,5 bis 30 Gew.% Netzmittel und 15 bis 75 Gew.% Wasser, wobei der pH Wert der Pigmentpaste von 10 bis 14 beträgt, lagerungsbeständig ist für Zeiträume von über 6 Monaten im Wesentlichen ohne Verlust an Farbqualität. Die erfindungsgemäße Pigmentpaste benötigt hierzu keine Konservierungsmittel. Selbst im hochkonzentrierten, feuchten, pulverförmigen Absatz der Paste an den oberen Innenseiten des Behälters in dem die Paste im Mischautomaten vorliegt, tritt bei der erfindungsgemäßen Paste kein Schädlingsbefall ein. Die erfindungsgemäße Pigmentpaste lässt sich zudem mit ganz unterschiedlichen Beschichtungsmitteln kombinieren und einfach vermischen. Die erfindungsgemäße Pigmentpaste eignet sich hervorragend zum Abtönen von konservierungsmittelfreien Dispersionsfarben. Mit der erfindungsgemäßen Pigmentpaste können folglich konservierungsmittelfreie Dispersionsfarben und andere konservierungsmittelfreie Beschichtungsmittel abgetönt werden.Surprisingly, it has been found that a pigment paste containing, based in each case on the total weight of the pigment paste, 1 to 75% by weight of pigment, 0.1 to 10% by weight of siliconate, 0.5 to 30% by weight of wetting agent and 15 to 75% by weight % Water, the pH value of the pigment paste being from 10 to 14, is storage-stable for periods of more than 6 months, essentially without loss of color quality. The pigment paste according to the invention does not require any preservatives for this. Even in the highly concentrated, moist, powdery paragraph of the paste on the upper inner sides of the container in which the paste is present in the automatic mixer, no pest infestation occurs with the paste according to the invention. The pigment paste of the invention can also be combined with very different coating agents and simply mixed. The pigment paste according to the invention is outstandingly suitable for tinting preservative-free Emulsion paints. Preservative-free emulsion paints and other preservative-free coating agents can consequently be tinted with the pigment paste according to the invention.

Ohne an eine bestimmte Theorie gebunden sein zu wollen, scheint das Zusammenwirken des Netzmittels mit dem Silikonat in der Pigmentpaste die Paste ausreichend vor dem Befall durch Schädlinge zu schützen, ohne dabei die Pigmente oder andere Bestandteile der Paste langfristig zu schädigen, und trotzdem eine Paste zu ergeben, die über breite Konzentrationsbereiche der anderen Bestandteile in der Paste sowie mit einer großen Anzahl unterschiedlicher Beschichtungsmittel kompatibel ist. Ohne die erfindungsgemäßen Gehalte an Netzmittel und Silikonat haben Pigmentpasten entweder nicht ausreichend langanhaltende konservierende Wirkung oder sie sind nicht über breite Konzentrationsbereiche der anderen Bestandteile in der Paste sowie mit einer großen Anzahl unterschiedlicher Beschichtungsmittel kompatibel. Ein solches Zusammenwirken von Netzmittel und Silikonat war zuvor ausgehend vom Stand der Technik nicht zu erwarten.Without wishing to be bound by any particular theory, the interaction of the wetting agent with the siliconate in the pigment paste seems to adequately protect the paste from pest infestation, without thereby causing long-term damage to the pigments or other constituents of the paste, and still a paste result that is compatible over a wide range of concentrations of the other constituents in the paste and with a large number of different coating agents. Without the wetting agent and siliconate contents according to the invention, pigment pastes either do not have a sufficiently long-lasting preservative effect or are not compatible over wide concentration ranges of the other constituents in the paste and with a large number of different coating agents. Such interaction of wetting agent and siliconate was not previously to be expected based on the prior art.

Silikonate gemäß der Erfindung sind insbesondere Verbindungen mit der Formel M(OSi(R)(OH)2)y, wobei M ein Alkalimetall oder ein Erdalkalimetall, y 1 oder 2 und R ein Kohlenwasserstoffrest mit 1 bis 10 Kohlenstoffatomen, insbesondere ein C1- bis C6-Alkylrest, ist. Erdalkali- oder Alkalimetallsilikonate können beispielsweise durch Umsetzen von Alkylsilantriol mit einem Erdalkali- oder Alkalimetallhydroxid erhalten werden. Die Herstellung von Lösungen von Silikonaten, insbesondere wässrigen Lösungen, ist beispielsweise in der DE 1 031 910 beschrieben.Silicates according to the invention are in particular compounds having the formula M (OSi (R) (OH) 2 ) y , where M is an alkali metal or an alkaline earth metal, y 1 or 2 and R is a hydrocarbon radical having 1 to 10 carbon atoms, in particular a C 1 - to C 6 alkyl. Alkaline earth metal or alkali metal siliconates can be obtained, for example, by reacting alkylsilanetriol with an alkaline earth metal or alkali metal hydroxide. The production of solutions of siliconates, in particular aqueous solutions, is for example in the DE 1 031 910 described.

In den Verbindungen M(OSi(R)(OH)2)y, die für das erfindungsgemäße Silikonat in Frage kommen, kann das Alkalimetall oder das Erdalkalimetall M insbesondere ausgewählt sein aus der Gruppe bestehend aus Lithium, Natrium, Kalium, Magnesium, Calcium, Strontium, Barium und Mischungen davon. Vorzugsweise ist M ausgewählt aus der Gruppe bestehend aus Lithium, Natrium, Kalium und Mischungen davon. Der Kohlenwasserstoffrest R ist vorzugsweise ausgewählt aus der Gruppe bestehend aus Methyl-, Ethyl-, n-Propyl-, iso-Propyl-, n-Butyl-, iso-Butyl-, tert-Butyl, n-Pentyl-, iso-Pentyl-, tert-Pentyl-, Neopentyl-, Phenyl-, Aryl-, und Cyclohexyl-. Bevorzugt ist der Kohlenwasserstoffrest R ein C1- bis C6-Alkylrest, insbesondere ausgewählt aus der Gruppe bestehend aus Methyl-, Ethyl-, n-Propyl-, iso-Propyl-, n-Butyl-, iso-Butyl-, tert-Butyl, n-Pentyl-, iso-Pentyl-, tert-Pentyl- und Neopentyl-. Bevorzugt ist der Kohlenwasserstoffrest R Methyl-. Weiter bevorzugt ist das Silikonat der erfindungsgemäßen Pigmentpaste ausgewählt aus der Gruppe bestehend aus Lithiummethylsilikonat, Natriummethylsilikonat und Kaliummethylsilikonat. Am bevorzugtesten ist das Silikonat Kaliummethylsilikonat. Diese Silikonate, insbesondere Kaliummethylsilikonat ergeben homogene Oberflächen und sind gut handhabbar.In the compounds M (OSi (R) (OH) 2 ) y which are suitable for the siliconate according to the invention, the alkali metal or the alkaline earth metal M can in particular be selected from the group consisting of lithium, sodium, potassium, magnesium, calcium, Strontium, barium and mixtures thereof. M is preferably selected from the group consisting of lithium, sodium, potassium and mixtures thereof. The hydrocarbon radical R is preferably selected from the group consisting of methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl, tert-butyl, n-pentyl, iso-pentyl , tert-pentyl, neopentyl, phenyl, aryl, and cyclohexyl. The hydrocarbon radical R is preferably a C 1 -C 6 -alkyl radical, in particular selected from the group consisting of methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl, tert- Butyl, n-pentyl, iso-pentyl, tert-pentyl and neopentyl. The hydrocarbon radical R is preferably methyl. The siliconate of the pigment paste according to the invention is further preferably selected from the group consisting of lithium methyl siliconate, sodium methyl siliconate and potassium methyl siliconate. Most preferably, the siliconate is potassium methyl siliconate. These siliconates, especially potassium methyl siliconate, result in homogeneous surfaces and are easy to handle.

Das Silikonat ist in der erfindungsgemäßen Pigmentpaste in einer Menge von 0,1 bis 10 Gew.-% enthalten, bezogen auf das Gesamtgewicht der Pigmentpaste. Bevorzugt enthält die erfindungsgemäße Pigmentpaste 0,1 bis 7 Gew.%, weiter bevorzugt 0,2 bis 3 Gew.%, bevorzugter 0,3 bis 2 Gew.%, noch bevorzugter 0,3 bis 1 Gew.% und besonders bevorzugt 0,3 bis 0,9 Gew.% Silikonat, jeweils bezogen auf das Gesamtgewicht der Pigmentpaste. Pigmentpasten mit einem solchen Anteil an Silikonat zeigen eine ausgezeichnete Lagerstabilität, bei der auch über einen Zeitraum von über 6 Monaten kein Qualitätsverlust beobachtbar ist. Über den gleichen Zeitraum ist auch kein Befall durch Pilze oder andere biologische Schädlinge zu beobachten.The silicone paste is contained in the pigment paste according to the invention in an amount of 0.1 to 10% by weight, based on the total weight of the pigment paste. The pigment paste according to the invention preferably contains 0.1 to 7% by weight, more preferably 0.2 to 3% by weight, more preferably 0.3 to 2% by weight, even more preferably 0.3 to 1% by weight and particularly preferably 0, 3 to 0.9% by weight of siliconate, in each case based on the total weight of the pigment paste. Pigment pastes with such a proportion of siliconate show excellent storage stability, in which no loss of quality can be observed even over a period of more than 6 months. No infection by fungi or other biological pests was observed over the same period.

Die Pigmentpaste enthält erfindungsgemäß 1 bis 75 Gew.% Pigment. Hierbei kommen verschiedene Substanzen als Pigmente infrage. Bevorzugt ist das Pigment ausgewählt aus der Gruppe bestehend aus Titandioxid, Eisenoxidgelb, Arylid (Monoazo), Bismutvanadat, (Di-)Arylide, Azokondensationspigmente, Pyranthone, Isoindoline, Anthrachinone, Derivate von Dioxazinen, Perinone, Naphtol-AS-Derivate, Perylene, Chinacridone, Indanthrene, Phthalocyanine, Rutil-Zinn-Zink, Chinacridone, Diketo-pyrrolo-pyrrol, Eisenoxidrot, Phthalocyaninblau, Dioxazin, Kobaltblau, Ultramarinblau, Phthalocyaningrün, Chromoxidgrün, Kobaltgrün, Farbruss, Eisenoxidschwarz, Pyrazolo-Chinazolon, Naphtol-AS-Monoazopigment, Pigment Violet 23, und Mischungen davon.According to the invention, the pigment paste contains 1 to 75% by weight of pigment. Various substances can be used as pigments. The pigment is preferably selected from the group consisting of titanium dioxide, iron oxide yellow, arylide (monoazo), bismuth vanadate, (di) arylides, azo condensation pigments, pyranthones, isoindolines, anthraquinones, derivatives of dioxazines, perinones, naphtol-AS derivatives, perylenes, quinacridones , Indanthrene, phthalocyanine, rutile-tin-zinc, quinacridone, diketo-pyrrolo-pyrrole, iron oxide red, phthalocyanine blue, dioxazine, cobalt blue, ultramarine blue, phthalocyanine green, chromium oxide green, cobalt green, color black, iron oxide black, pyrazolo-quinazolone, monhtazo-pigmentation, naphtholophenone, naphtholophenone, naphthazopmentone Violet 23, and mixtures thereof.

Der Anteil an Pigment in der Paste variiert in großen Bereichen. Dies hängt zum einen mit der gewünschten Farbe der Paste zusammen, zum anderen mit der Farbstärke des Pigments. Bevorzugte Mengenbereiche von Pigment in der Paste sind 5 bis 70 Gew.%, vorzugsweise 10 bis 65 Gew.%, weiter bevorzugt 20 bis 55 Gew.% und besonders bevorzugt 30 bis 50 Gew.% Pigment.The proportion of pigment in the paste varies widely. This is due on the one hand to the desired color of the paste, and on the other hand to the color strength of the pigment. Preferred quantitative ranges of pigment in the paste are 5 to 70% by weight, preferably 10 to 65% by weight, more preferably 20 to 55% by weight and particularly preferably 30 to 50% by weight of pigment.

Üblicherweise werden anorganische Pigmente in größeren Mengen eingesetzt als organische Pigmente. Gemäß einer bevorzugten Ausführungsform enthält die Pigmentpaste von 20 bis 75 Gew.% eines anorganischen Pigments, bevorzugt von 40 bis 70 Gew.% eines anorganischen Pigments. Gemäß einer weiteren bevorzugten Ausführungsform enthält die Pigmentpaste von 1 bis 50 Gew.%, bevorzugt von 1 bis 20 Gew.% eines organischen Pigments. Gemäß einer weiteren bevorzugten Ausführungsform enthält die Pigmentpaste von 20 bis 75 Gew.%, bevorzugt von 40 bis 70 Gew.% eines anorganischen Pigments und von 1 bis 20 Gew.%, bevorzugt von 1 bis 10 Gew.% eines organischen Pigments.Inorganic pigments are usually used in larger quantities than organic pigments. According to a preferred embodiment, the pigment paste contains from 20 to 75% by weight of an inorganic pigment, preferably from 40 to 70% by weight of an inorganic pigment. According to a further preferred embodiment, the pigment paste contains from 1 to 50% by weight, preferably from 1 to 20% by weight an organic pigment. According to a further preferred embodiment, the pigment paste contains from 20 to 75% by weight, preferably from 40 to 70% by weight of an inorganic pigment and from 1 to 20% by weight, preferably from 1 to 10% by weight of an organic pigment.

Gemäß einer Ausführungsform werden bevorzugt anorganische Pigmente eingesetzt. Beispiele für anorganische Pigmente sind Oxide wie Titandioxid, Eisenoxide, z.B. P.Y. 42, P.R. 101, P.Bk. 11, Chromoxidgrün, z.B. P.G. 17, Chromeisenoxide, z.B. P.Br. 29, Mischphasenpigmente z.B. Cobaltoxide Blau P.B. 28 und Grün P.G. 50, Bismutvanadat P.Y. 184, Rutil-Zinn-Zink P.O. 216, Rutil-Zinn-Zink-Titan P.Y. 213, Silikate, z.B. Ultramarinblau P.B. 29 und Kohlenstoff, z.B. Ruß P.Bk. 7.In one embodiment, inorganic pigments are preferably used. Examples of inorganic pigments are oxides such as titanium dioxide, iron oxides, e.g. P.Y. 42, P.R. 101, P.Bk. 11, chrome oxide green, e.g. P. G. 17, chrome iron oxides, e.g. P.Br. 29, mixed phase pigments e.g. Cobalt Oxide Blue P.B. 28 and Grün P.G. 50, bismuth vanadate P.Y. 184, rutile-tin-zinc P.O. 216, rutile-tin-zinc-titanium P.Y. 213, silicates, e.g. Ultramarine blue P.B. 29 and carbon, e.g. Carbon black P.Bk. 7th

Gemäß einer weiteren Ausführungsform werden bevorzugt organische Pigmente eingesetzt. Beispiele für organische Pigmente sind Azopigmente, z.B. Arylidgelb (Monoazo) P.Y. 74, Polycyclische Pigmente, z.B. Chinacridone P.R. 122, Perinone P.O. 43, Pyrazolo-Chinazolon P.O. 67, Diketo-Pyrrolo-Pyrrol (DPP) P.R. 254, Dioxazine P.V. 23 und Metallkomplexpigmente, z.B. Kupferphthalocyanine Blau P.B. 15:3 und Grün P.G. 7.According to a further embodiment, organic pigments are preferably used. Examples of organic pigments are azo pigments, e.g. Arylid Yellow (Monoazo) P.Y. 74, polycyclic pigments, e.g. Chinacridone P.R. 122, Perinone P.O. 43, pyrazolo-quinazolone P.O. 67, Diketo-Pyrrolo-Pyrrole (DPP) P.R. 254, Dioxazine P.V. 23 and metal complex pigments, e.g. Copper phthalocyanine blue P.B. 15: 3 and Green P.G. 7th

Die für die Beispiele verwendeten Bezeichnungen der anorganischen und organischen Pigmente entsprechen den Generic Names des Colour Index der British Society of Dyers and Colourists.The names of the inorganic and organic pigments used for the examples correspond to the generic names of the Color Index of the British Society of Dyers and Colorists.

Gemäß einer weiteren Ausführungsform werden Mischungen von anorganischen und organischen Pigmenten eingesetzt.According to a further embodiment, mixtures of inorganic and organic pigments are used.

Durch die Verwendung der angeführten Pigmente können farbige Pigmentpasten hergestellt werden, die im Wesentlichen das ganze Farbspektrum abdecken.By using the pigments listed, colored pigment pastes can be produced that cover essentially the entire color spectrum.

Neben den Komponenten Pigment, Silikonat und Wasser kann die erfindungsgemäße Pigmentpaste Füllstoff enthalten. Die Pigmentpaste kann insbesondere 0,01 bis 60 Gew.% oder 0,01 bis 50 Gew.% oder 0,01 bis 40 Gew.% oder 0,01 bis 30 Gew.%, jeweils bezogen auf das Gesamtgewicht der Pigmentpaste, Füllstoff enthalten. Der Füllstoff kann aus der Gruppe bestehend aus Carbonaten, Sulfaten, Oxiden und Mischungen davon ausgewählt sein. Insbesondere kann der Füllstoff aus der Gruppe bestehend aus Dolomit, Bariumsulfat, Feldspat, Quarz, Calciumcarbonat, Glimmer, Kaolin, kalziniertes Kaolin, Talkum, Ton, Silika, Diatomeenerde und Mischungen davon ausgewählt sein. Gemäß einer Ausführungsform ist der Füllstoff Calciumcarbonat. Derartige Füllstoffe ergeben Pigmentpasten mit einer guten Verarbeitbarkeit.In addition to the components pigment, siliconate and water, the pigment paste according to the invention can contain filler. The pigment paste can contain, in particular, 0.01 to 60% by weight or 0.01 to 50% by weight or 0.01 to 40% by weight or 0.01 to 30% by weight, in each case based on the total weight of the pigment paste, of filler , The filler can be selected from the group consisting of carbonates, sulfates, oxides and mixtures thereof. In particular, the filler can be selected from the group consisting of dolomite, barium sulfate, feldspar, quartz, calcium carbonate, mica, kaolin, calcined kaolin, talc, clay, silica, diatomaceous earth and mixtures thereof. In one embodiment, the filler is calcium carbonate. Such fillers result in pigment pastes with good processability.

Calciumcarbonat kann dabei in verschiedener Form, beispielsweise in Form von Kreide oder Calcit eingesetzt werden.Calcium carbonate can be used in various forms, for example in the form of chalk or calcite.

Gemäß einer bevorzugten Ausführungsform enthält die Pigmentpaste zumindest einen Füllstoff. Gemäß einer anderen bevorzugten Ausführungsform enthält die Pigmentpaste keinen Füllstoff. Der Einsatz von Füllstoffen in der Paste hängt von der Gesamtzusammensetzung der Paste ab. Grundsätzlich kann der Preis der Paste durch den Einsatz von Füllstoffen gesenkt werden. Allerdings kann es durch den Einsatz von Füllstoff auch zu Schwierigkeiten in der Kompatibilität der Komponenten in der Paste kommen, insbesondere kann sich der Füllstoff im Mischautomaten absetzen. Über Füllstoffe können außerdem zusätzliche Sporen ins System eingetragen werden. Zudem haben Füllstoffe negative Auswirkungen auf glänzende Systeme und reduzieren im Allgemeinen die Witterungsstabilität des Überzugmittels.According to a preferred embodiment, the pigment paste contains at least one filler. According to another preferred embodiment, the pigment paste contains no filler. The use of fillers in the paste depends on the overall composition of the paste. In principle, the price of the paste can be reduced by using fillers. However, the use of filler can also lead to difficulties in the compatibility of the components in the paste, in particular the filler can settle in the automatic mixer. Additional spores can also be added to the system via fillers. In addition, fillers have negative effects on glossy systems and generally reduce the weathering stability of the coating agent.

Praktische Versuche haben gezeigt, dass die Pigmentpaste besonders gut mit Beschichtungsmitteln vermischt werden kann, wenn die Füllstoffpartikel klein sind. Vorteilhafterweise weisen die Füllstoffpartikel der erfindungsgemäßen Pigmentpaste eine Größe von weniger als 100 µm, insbesondere weniger als 80 µm, bevorzugt von 0,1 bis 50 µm, weiter bevorzugt von 1 bis 30 µm auf. Verfahren zur Bestimmung der Partikelgröße sind dem Fachmann bekannt. Beispielsweise kann die Partikelgröße mittels Grindometer nach DIN EN ISO 1524 , insbesondere nach DIN EN ISO 1524:2013-06 , bestimmt werden. Dabei bezieht sich die Partikelgröße der Füllstoffe insbesondere auf die maximale Agglomeratgröße in der Pigmentpaste.Practical tests have shown that the pigment paste can be mixed particularly well with coating agents if the filler particles are small. The filler particles of the pigment paste according to the invention advantageously have a size of less than 100 μm, in particular less than 80 μm, preferably from 0.1 to 50 μm, more preferably from 1 to 30 μm. Methods for determining the particle size are known to the person skilled in the art. For example, the particle size can be determined using a grindometer DIN EN ISO 1524 , especially after DIN EN ISO 1524: 2013-06 , be determined. The particle size of the fillers relates in particular to the maximum agglomerate size in the pigment paste.

Ferner kann die Partikelgröße, insbesondere die Partikelgrößenverteilung, auch mittels Transmissionselektronenmikroskopie bestimmt werden.Furthermore, the particle size, in particular the particle size distribution, can also be determined by means of transmission electron microscopy.

Bevorzugt wird die Partikelgröße mittels Grindometer nach DIN EN ISO 1524:2013-06 bestimmt.The particle size is preferably determined using a grindometer DIN EN ISO 1524: 2013-06 certainly.

Die Pigmentpaste enthält zudem mindestens ein Netzmittel. Das Netzmittel dient als Antiflockungsmittel, welches das Ausflocken der suspendierten Partikel aus der Paste verhindert. Zudem wird durch das Netzmittel die Verteilung der Pigmentpaste in dem Beschichtungsmittel verbessert. The pigment paste also contains at least one wetting agent. The wetting agent serves as an anti-flocculant, which prevents the suspended particles from flocculating out of the paste. In addition, the distribution of the pigment paste in the coating agent is improved by the wetting agent.

Überraschenderweise weisen Pigmentpasten mit den erfindungsgemäßen Gehalten an Netzmittel und Silikonat eine gute Kompatibilität der Bestandteile der Pigmentpaste selbst sowie der Pigmentpaste mit dem abzutönenden Beschichtungsmittel auf.Surprisingly, pigment pastes with the contents of wetting agent and siliconate according to the invention have good compatibility of the constituents of the pigment paste itself and of the pigment paste with the coating agent to be tinted.

Der Anteil des Netzmittels an der Pigmentpaste kann in weiten Bereichen variieren und richtet sich grundsätzlich nach der gewünschten Viskosität der Pigmentpaste. Die jeweils geeignete Menge an Netzmittel hängt dabei von der Art des eingesetzten Netzmittels, von der Menge und Art des eingesetzten Pigments sowie von den gegebenenfalls vorhandenen weiteren Bestandteile der Pigmentpaste ab.The proportion of the wetting agent in the pigment paste can vary within a wide range and depends in principle on the desired viscosity of the pigment paste. The appropriate amount of wetting agent depends on the type of wetting agent used, on the amount and type of pigment used and on any other constituents of the pigment paste that may be present.

Üblicherweise können bereits mit einem Netzmittelanteil von 0,5 bis 30 Gew.%, vorzugsweise 0,5 bis 25 Gew.%, weiter bevorzugt von 1 bis 20 Gew.%, weiter bevorzugt von 1 bis 15 Gew.%, weiter bevorzugt von 2 bis 12 Gew.%, besonders bevorzugt von 4 bis 10 Gew.%, jeweils bezogen auf das Gesamtgewicht der Pigmentpaste, hervorragende Ergebnisse erzielt werden. Ein höherer Anteil an Netzmittel an der Pigmentpaste als 30 Gew.% kann zu einer unerwünschten glänzenden Oberfläche des mit Pigmentpaste abgetönten Beschichtungsmittels führen. Bei dem Verzicht oder dem Einsatz von zu wenig Netzmittel kann es vorkommen, dass nicht sämtliches Pigment in die Paste eingebunden wird, welches dann nicht oder nur eingeschränkt zur Deckkraft beiträgt.Usually a wetting agent content of from 0.5 to 30% by weight, preferably 0.5 to 25% by weight, more preferably from 1 to 20% by weight, more preferably from 1 to 15% by weight, more preferably from 2 up to 12% by weight, particularly preferably from 4 to 10% by weight, based in each case on the total weight of the pigment paste, excellent results can be achieved. A higher proportion of wetting agent in the pigment paste than 30% by weight can lead to an undesirable glossy surface of the coating agent tinted with pigment paste. If you do not use or use too little wetting agent, it may happen that not all of the pigment is incorporated into the paste, which then does not contribute to the opacity or only to a limited extent.

Beispiele für Netzmittel sind Diethylmaleat, Tallöl, Polyethylenpolyamin, Reaktionsprodukte aus Tallöl und Polyethylenpolyamin, Polyether, Polyetherphosphat, Polyethylenglykolmonomethylether, ortho-Kresylglycidylether, 2-Ethylhexylglycidylether, Block-Copolymere, Ammoniumsalze von Acrylatcopolymeren, Polyetherpolysiloxan, Polyoxyethylen-(2)-stearylalkohol, Polyester, fettsäuremodifizierte Polyester und Mischungen davon.Examples of wetting agents are diethyl maleate, tall oil, polyethylene polyamine, reaction products from tall oil and polyethylene polyamine, polyether, polyether phosphate, polyethylene glycol monomethyl ether, ortho-cresyl glycidyl ether, 2-ethyl hexyl glycidyl ether, block copolymers, ammonium salts of acrylate copolymers, 2-polyether-polyoxy-siloxane, polyether-polyoxy-siloxane, polyether-polyoxy-siloxane, fatty acid modified polyesters and mixtures thereof.

Der pH Wert der Pigmentpaste beträgt erfindungsgemäß von 10 bis 14, bevorzugt von 10 bis 12, weiter bevorzugt von 10,4 bis 11,6. Besonders bevorzugt beträgt der pH Wert der Pigmentpaste mehr als 10,4 und weniger als 11,5. Es wurde gefunden, dass Pigmentpasten mit den angegebenen pH Werten auch bei einer Lagerung über mehrere Monate keine oder nur geringfügige Verfärbungen aufweisen, selbst wenn sie im Wesentlichen frei von Konservierungsmitteln sind. „Im Wesentlichen frei von Konservierungsmitteln“ bedeutet dabei, dass die Pigmentpaste Konservierungsmittel höchstens in Spuren, insbesondere in einer Menge von weniger als 2 ppm enthält. Mit dem oben beschriebenen pH Wert wird das optimale Gleichgewicht getroffen zwischen dem Verhindern des Befalls durch Schädlinge und der Stabilität der Komponenten in der Paste.According to the invention, the pH of the pigment paste is from 10 to 14, preferably from 10 to 12, more preferably from 10.4 to 11.6. The pH value of the pigment paste is particularly preferably more than 10.4 and less than 11.5. It has been found that pigment pastes with the stated pH values show no or only slight discoloration even when stored for several months, even if they are essentially free of preservatives. “Essentially free of preservatives” means that the pigment paste contains preservatives at most in traces, in particular in an amount of less than 2 ppm. The pH value described above strikes the optimal balance between preventing pest infestation and the stability of the components in the paste.

Erfindungsgemäße Pigmentpasten mit derartigen pH Werten haben den zusätzlichen Vorteil, auch ohne besondere Vorkehrungen hinsichtlich des Arbeitsschutzes verwendet werden zu können.Pigment pastes according to the invention with such pH values have the additional advantage that they can also be used without special precautions with regard to occupational safety.

Der pH Wert kann beispielsweise durch Zugabe von alkalischen Substanzen, auch Alkalisteller genannt, eingestellt werden. Beispiele für alkalische Substanzen sind Alkalimetallhydroxide wie Litihium-, Natrium- und/oder Kaliumhydroxid, Erdalkalimetallhydroxide wie Magnesium-, Calcium-, und/oder Bariumhydroxid, Ammoniumhydroxid und/oder Ettringit (Ca6[Al(OH)6]2(SO4 × 26 H2O)).The pH can be adjusted, for example, by adding alkaline substances, also known as alkaline adjusters. Examples of alkaline substances are alkali metal hydroxides such as lithium, sodium and / or potassium hydroxide, alkaline earth metal hydroxides such as magnesium, calcium and / or barium hydroxide, ammonium hydroxide and / or ettringite (Ca 6 [Al (OH) 6 ] 2 (SO 4 × 26 H 2 O)).

Das Xonotlit weist vorzugsweise ein monoklines Kristallsystem auf (Xonotlitmonoklin). Es hat sich gezeigt, dass Xonotlit und/oder Ettringit in besonders vorteilhafter Weise in Kombination mit dem in der erfindungsgemäßen Pigmentpaste enthaltenen Silikonat eingesetzt werden können. Insbesondere weisen Pigmentpasten, die neben Silikonat Xonotlit und/oder Ettringit als Alkalisteller enthalten, eine erhöhte pH-Stabilität auf.The xonotlite preferably has a monoclinic crystal system (xonotlite monoclin). It has been shown that xonotlite and / or ettringite can be used in a particularly advantageous manner in combination with the siliconate contained in the pigment paste according to the invention. In particular, pigment pastes which, in addition to siliconate, contain xonotlite and / or ettringite as alkali plates, have increased pH stability.

Gemäß einer Ausführungsform der Erfindung enthält die erfindungsgemäße Pigmentpaste neben Silikonat mindestens einen Alkalisteller in einer Menge von 0,005 bis 3 Gew.%, insbesondere von 0,01 bis 1 Gew.%, bezogen auf die Gesamtzusammensetzung der Pigmentpaste. Insbesondere kann die erfindungsgemäße Pigmentpaste 0,005 bis 3 Gew.%, insbesondere von 0,01 bis 1 Gew.% Kaliumhydroxid, Xonotlit und/oder Ettringit, bezogen auf die Gesamtzusammensetzung der Pigmentpaste, enthalten.According to one embodiment of the invention, the pigment paste according to the invention contains, in addition to siliconate, at least one alkali plate in an amount of 0.005 to 3% by weight, in particular 0.01 to 1% by weight, based on the total composition of the pigment paste. In particular, the pigment paste according to the invention can contain 0.005 to 3% by weight, in particular 0.01 to 1% by weight, of potassium hydroxide, xonotlite and / or ettringite, based on the total composition of the pigment paste.

Gemäß einer Ausführungsform der Erfindung bleibt der pH Wert der erfindungsgemäßen Pigmentpaste über einen Zeitraum von mindestens 4 Wochen, bevorzugt mindestens 8 Wochen, weiter bevorzugt mindestens 12 Wochen, noch weiter bevorzugt mindestens 16 Wochen, noch weiter bevorzugt mindestens 20 Wochen, im Wesentlichen konstant. „Im Wesentlichen konstant“ bedeutet dabei, dass sich der gemessene pH Wert im Rahmen des bei Messungen des pH Werts üblichen Messtoleranzbereichs nicht ändert.According to one embodiment of the invention, the pH of the pigment paste according to the invention remains over a period of at least 4 weeks, preferably at least 8 weeks, more preferably at least 12 weeks, even more preferably at least 16 weeks, even more preferably at least 20 weeks, essentially constant. “Essentially constant” means that the measured pH value does not change within the measurement tolerance range that is customary when measuring the pH value.

Gemäß einer bevorzugten Ausführungsform der Erfindung zeichnet sich die erfindungsgemäße Pigmentpaste ferner dadurch aus, dass sie eine Viskosität von 0,1 bis 12 Pas, vorzugsweise 0,5 bis 8 Pas, besonders bevorzugt von 0,8 bis 5 Pas, gemessen bei 23 °C und bei einer Schergeschwindigkeit von 3 s-1 im Rotationsviskosimeter mit zylindrischer Messgeometrie aufweist. Vorzugsweise weist die Pigmentpaste bei einer Schergeschwindigkeit von 50 s-1 und einer Temperatur von 23 °C im Rotationsviskosimeter mit zylindrischer Messgeometrie eine Viskosität von 0,1 bis 5 Pas, vorzugsweise von 0,2 bis 3 Pas, besonders bevorzugt von 0,35 bis 1,5 Pas, auf.According to a preferred embodiment of the invention, the pigment paste according to the invention is further characterized in that it has a viscosity of 0.1 to 12 Pas, preferably 0.5 to 8 Pas, particularly preferably 0.8 to 5 Pas, measured at 23 ° C. and at a shear rate of 3 s -1 in a rotary viscometer with a cylindrical measuring geometry. The pigment paste preferably has a viscosity of 0.1 to 5 Pas, preferably of 0.2 to 3 Pas, particularly preferably of 0.35 to, at a shear rate of 50 s -1 and a temperature of 23 ° C. in a rotary viscometer with a cylindrical measuring geometry 1.5 Pas, on.

Eine Viskosität von 0,1 bis 8 Pas bei 3 s-1 ist für die Verarbeitbarkeit von Pigmentpasten optimal, da sie eine besonders einfache Vermischung mit gängigen Beschichtungsmitteln erlaubt. Das Dosieren der erfindungsgemäßen Pigmentpaste kann beispielsweise problemlos in handelsüblichen Mischautomaten durchgeführt werden. Die Viskosität der erfindungsgemäßen Pigmentpaste ist insbesondere hoch genug, um zu verhindern, dass sich die in ihr enthaltenen Feststoffe wie Pigmente und/oder Füllstoffe am Boden des Vorratsbehälters im Mischautomaten absetzen. Gleichzeitig ist die Viskosität aber niedrig genug, dass sich die Pigmentpaste in ein Beschichtungsmittel hinreichend genau und reproduzierbar eindosieren lässt.A viscosity of 0.1 to 8 Pas at 3 s -1 is optimal for the processing of pigment pastes, since it allows particularly easy mixing with common coating agents. The pigment paste according to the invention can, for example, be metered without problems in commercially available automatic mixers. The viscosity of the pigment paste according to the invention is particularly high enough to prevent the solids contained therein, such as pigments and / or fillers, from settling on the bottom of the storage container in the automatic mixer. At the same time, the viscosity is low enough that the pigment paste can be dosed into a coating agent with sufficient accuracy and reproducibility.

Die erfindungsgemäße Pigmentpaste kann zudem als weitere Additive Dispergiermittel, Rheologieadditive, Entschäumer und/oder Hydrophobierungsmittel enthalten.The pigment paste according to the invention can also contain, as further additives, dispersants, rheology additives, defoamers and / or water repellents.

Beispiele für Rheologieadditive sind Methylhydroxyethylcellulose, Schichtsilikat wie Smektit und Hectorit, Xanthangummi, Siliciumdioxid, Polyurethanharz, Octan-1-ol (ethoxyliert, 4-EO), Alkoholalkoxylate, Ethylenoxid-Propylenoxid-Copolymere, Maleinsäureanhydrid-Diisobutylen-Copolymere, Polyacryl- und Polymethacrylsäure und deren Salze, Methylcellulosen, Carboxymethylcellulosen, Hydroxymethylcellulosen, Polyurethane, Alkalimetallphosphate, Acrylate und Salze modifizierter Phosphorsäuren, sowie deren Mischungen.Examples of rheology additives are methylhydroxyethyl cellulose, layered silicate such as smectite and hectorite, xanthan gum, silicon dioxide, polyurethane resin, octan-1-ol (ethoxylated, 4-EO), alcohol alkoxylates, ethylene oxide-propylene oxide copolymers, maleic anhydride-diisobutylene copolymers, polyacrylic acid and polyacrylic acid and polyacrylic acid and polyacrylic acid their salts, methyl celluloses, carboxymethyl celluloses, hydroxymethyl celluloses, polyurethanes, alkali metal phosphates, acrylates and salts of modified phosphoric acids, and mixtures thereof.

Beispiele für Entschäumer sind Polyurethanharze, Polyglykole, Triglyceride, Polysiloxan-Polyether-Copolymere und Silikonöle.Examples of defoamers are polyurethane resins, polyglycols, triglycerides, polysiloxane-polyether copolymers and silicone oils.

Beispiele für Hydrophobiermittel sind insbesondere oligomere und polymere Siloxane und Silikonharze.Examples of hydrophobizing agents are, in particular, oligomeric and polymeric siloxanes and silicone resins.

Gemäß einer bevorzugten Ausführungsform ist die erfindungsgemäße Pigmentpaste im Wesentlichen frei von Konservierungsmitteln, insbesondere von Isothiazolinen. „Im Wesentlichen frei von Konservierungsmitteln“ bedeutet dabei, dass die Pigmentpaste Konservierungsmittel höchstens in Spuren, insbesondere in einer Menge von weniger als 2 ppm enthält. Beispiele für Isothiazoline sind Methylisothiazolinon, Chlormethylisothiazolinon, Benzisothiazolinnon, Octylisothiazolinon, Dichloroctylisothiazolinon und Butylbenzisothiazolinon. Vorzugsweise ist die Pigmentpaste frei von ([([(2-dihydro-5-methyl-3(2H)-oxazolyl)-1-methylethoxy]methoxy)methoxy]methanol.According to a preferred embodiment, the pigment paste according to the invention is essentially free of preservatives, in particular isothiazolines. “Essentially free of preservatives” means that the pigment paste contains preservatives at most in traces, in particular in an amount of less than 2 ppm. Examples of isothiazolines are methylisothiazolinone, chloromethylisothiazolinone, benzisothiazolinnone, octylisothiazolinone, dichloroctylisothiazolinone and butylbenzisothiazolinone. The pigment paste is preferably free of ([([(2-dihydro-5-methyl-3 (2H) -oxazolyl) -1-methylethoxy] methoxy) methoxy] methanol.

Die Erfindung stellt ferner ein Verfahren zur Herstellung der erfindungsgemäßen Pigmentpaste bereit, umfassend die Schritte

  1. a. Bereitstellen einer Zusammensetzung enthaltend, jeweils bezogen auf das Gesamtgewicht der Pigmentpaste,
    1. i. 1 bis 75 Gew.% Pigment,
    2. ii. 0,1 bis 10 Gew.% Silikonat,
    3. iii. 0,5 bis 30 Gew.% Netzmittel,
    4. iv. 15 bis 75 Gew.% Wasser,
  2. b. Dispergieren der in a. genannten Komponenten.
The invention further provides a method for producing the pigment paste according to the invention, comprising the steps
  1. a. Providing a composition containing, in each case based on the total weight of the pigment paste,
    1. i. 1 to 75% by weight pigment,
    2. ii. 0.1 to 10% by weight of siliconate,
    3. iii. 0.5 to 30% by weight of wetting agent,
    4. iv. 15 to 75% by weight of water,
  2. b. Disperse the in a. components mentioned.

Vorzugsweise umfasst das Verfahren als weiteren Schritt c., das Einstellen des pH Wertes auf einen Wert von 10 bis 14.As a further step c., The method preferably comprises adjusting the pH to a value of 10 to 14.

Die angeführten Schritte a. bis c. können in beliebiger Reihenfolge fachspezifisch durchgeführt werden.The steps listed a. to c. can be carried out subject-specific in any order.

Das im Zusammenhang mit der erfindungsgemäßen Pigmentpaste zum Silikonat Gesagte gilt gleichermaßen auch für das Silikonat des erfindungsgemäßen Verfahrens. The statements made in connection with the pigment paste according to the invention relating to the siliconate apply equally to the siliconate of the method according to the invention.

Das im Zusammenhang mit der erfindungsgemäßen Pigmentpaste zum Pigment Gesagte gilt gleichermaßen auch für das Pigment des erfindungsgemäßen Verfahrens.What has been said about the pigment in connection with the pigment paste according to the invention applies equally to the pigment of the method according to the invention.

Das im Zusammenhang mit der erfindungsgemäßen Pigmentpaste zu Füllstoff Gesagte gilt gleichermaßen auch für Füllstoff des erfindungsgemäßen Verfahrens.The statements made regarding filler in connection with the pigment paste according to the invention apply equally to filler of the method according to the invention.

Das im Zusammenhang mit der erfindungsgemäßen Pigmentpaste zum Netzmittel Gesagte gilt gleichermaßen auch für das Netzmittel des erfindungsgemäßen Verfahrens.The statements made in connection with the pigment paste according to the invention relating to the wetting agent also apply equally to the wetting agent of the method according to the invention.

Das im Zusammenhang mit der erfindungsgemäßen Pigmentpaste zum pH Wert sowie zur alkalischen Substanz Gesagte gilt gleichermaßen auch für den pH Wert sowie für die alkalische Substanz des erfindungsgemäßen Verfahrens.What has been said in connection with the pigment paste according to the invention regarding the pH value and the alkaline substance applies equally to the pH value and to the alkaline substance of the method according to the invention.

Die erfindungsgemäße Pigmentpaste eignet sich hervorragend zum Abtönen von Beschichtungsmitteln. Besonders vorteilhaft ist es hierbei, dass die Pigmentpaste einen äußerst geringen Einfluss auf den Glanz des Farbmischsystems hat. Durch das Vermischen eines Beschichtungsmittels mit einer Pigmentpaste wird das Beschichtungsmittel abgetönt. Dadurch wird ein abgetöntes Beschichtungsmittel erhalten. Abgetönte Beschichtungsmittel werden auch als Überzugsmittel bezeichnet. Überzugsmittel enthalten mindestens eine erfindungsgemäße Pigmentpaste und ein oder mehrere Beschichtungsmittel. Ein weiterer Gegenstand der Erfindung ist somit ein Verfahren zur Herstellung eines Überzugsmittels, in dem mindestens eine erfindungsgemäße Pigmentpaste mit einem oder mehreren Beschichtungsmitteln vermischt wird. Vorzugsweise wird das Vermischen durch Mischautomaten durchgeführt.The pigment paste according to the invention is outstandingly suitable for tinting coating agents. It is particularly advantageous here that the pigment paste has an extremely low influence on the gloss of the color mixing system. The coating agent is tinted by mixing a coating agent with a pigment paste. This gives a tinted coating agent. Tinted coating agents are also referred to as coating agents. Coating agents contain at least one pigment paste according to the invention and one or more coating agents. The invention thus furthermore relates to a process for producing a coating composition in which at least one pigment paste according to the invention is mixed with one or more coating compositions. Mixing is preferably carried out by automatic mixers.

Vorzugsweise wird zur Herstellung des Überzugsmittels maximal ein Anteil von 15 Vol.% Pigmentpaste in das Beschichtungsmittel gemischt. Auf diese Weise wird ein gut streichbares und haltbares Überzugsmittel erhalten, welches selbst dann lange haltbar ist, wenn das Beschichtungsmittel frei von Konservierungsmitteln ist.A maximum of 15% by volume of pigment paste is preferably mixed into the coating composition to produce the coating composition. In this way a readily spreadable and durable coating agent is obtained which is long-lasting even when the coating agent is free from preservatives.

Als Beschichtungsmittel, das oder die mit der mindestens einen erfindungsgemäßen Pigmentpaste vermischt wird oder werden, eignen sich hierbei ganz unterschiedliche Beschichtungsmittel. Als Beschichtungsmittel kommen insbesondere Silikatfarben, Dispersions-Silikatfarben, Lacke, Putze und Kunststoffdispersionsfarben, vorzugsweise Kunststoffdispersionsfarben, in Frage. So kann die erfindungsgemäße Pigmentpaste zum Abtönen von Silikatfarben, Dispersions-Silikatfarben, Lacken, Putzen und Kunststoffdispersionsfarben, vorzugsweise zum Abtönen von Kunststoffdispersionsfarben, eingesetzt werden. Vorzugsweise ist das Beschichtungsmittel konservierungsmittelfrei.Very different coating agents are suitable as coating agents that are or are mixed with the at least one pigment paste according to the invention. Particularly suitable coating agents are silicate paints, dispersion silicate paints, lacquers, plasters and plastic dispersion paints, preferably plastic dispersion paints. Thus, the pigment paste according to the invention can be used for tinting silicate paints, dispersion silicate paints, lacquers, plasters and plastic dispersion paints, preferably for tinting plastic dispersion paints. The coating agent is preferably free of preservatives.

Die Erfindung hat außerdem zum Gegenstand ein Überzugsmittel umfassend mindestens eine erfindungsgemäße Pigmentpaste und mindestens ein Beschichtungsmittel. Vorzugsweise ist das Überzugsmittel im Wesentlichen frei von Konservierungsmitteln.The invention also relates to a coating composition comprising at least one pigment paste according to the invention and at least one coating agent. The coating agent is preferably essentially free of preservatives.

Zudem hat die Erfindung die Verwendung eines Silikonats zur Stabilisierung und/oder Erhöhung der Lagerstabilität von Pigmentpasten zum Gegenstand.The invention also relates to the use of a siliconate for stabilizing and / or increasing the storage stability of pigment pastes.

Die Erfindung wird im Folgenden durch Beispiele näher erläutert, die jedoch nur der Veranschaulichung dienen und nicht limitierend sind.The invention is explained in more detail below by examples, which, however, serve only for illustration and are not limiting.

BeispieleExamples

Eine Pigmentpaste mit der folgenden, in Tabelle 1 wiedergegebenen Formulierung wurde hergestellt durch Mischen der in Tabelle 1 angegebenen Bestandteile, dosierte Angaben jeweils in Gew.%. Bestandteil Formulierung A Diketopyrrolopyrrol- Rotpigment 3 Calciumcarbonat 25 Kaliummethylsilikonat 0,5 Entschäumer 0,2 Netzmittel 4 Rheologieadditive 3,3 Wasser 64 A pigment paste with the following formulation shown in Table 1 was prepared by mixing the constituents listed in Table 1, metered amounts in each case in% by weight. component Formulation A Diketopyrrolopyrrole red pigment 3 calcium carbonate 25 potassium methyl 0.5 defoamers 0.2 wetting agent 4 rheology 3.3 water 64

Die Formulierung A zeigte eine gute Lagerstabilität von mehr als 6 Monaten ohne Verfärbungen und ließ sich gut verarbeiten. Insbesondere zeigte die Formulierung eine gute Mischbarkeit mit Beschichtungsmitteln, insbesondere mit Kunststoffdispersionsfarben. Der pH Wert betrug für Formulierung A nach 6 Monaten 11,2.Formulation A showed good storage stability of more than 6 months without discoloration and was easy to process. In particular, the formulation showed good miscibility with coating agents, in particular with plastic emulsion paints. The pH value for formulation A was 11.2 after 6 months.

ZITATE ENTHALTEN IN DER BESCHREIBUNG QUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of documents listed by the applicant has been generated automatically and is only included for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.

Zitierte PatentliteraturPatent literature cited

  • EP 1297079 B1 [0006, 0011]EP 1297079 B1 [0006, 0011]
  • DE 1031910 [0006, 0011, 0020]DE 1031910 [0006, 0011, 0020]
  • DE 102014013455 A1 [0006, 0011]DE 102014013455 A1 [0006, 0011]
  • DE 102016002221 A1 [0006, 0011]DE 102016002221 A1 [0006, 0011]

Zitierte Nicht-PatentliteraturNon-patent literature cited

  • DIN EN ISO 1524 [0034]DIN EN ISO 1524 [0034]
  • DIN EN ISO 1524:2013-06 [0034, 0036]DIN EN ISO 1524: 2013-06 [0034, 0036]

Claims (17)

Pigmentpaste enthaltend, jeweils bezogen auf das Gesamtgewicht der Pigmentpaste, a. 1 bis 75 Gew.% Pigment, b. 0,1 bis 10 Gew.% Silikonat, c. 0,5 bis 30 Gew.% Netzmittel, d. 15 bis 75 Gew.% Wasser, wobei der pH Wert der Pigmentpaste von 10 bis 14 beträgt.Containing pigment paste, in each case based on the total weight of the pigment paste, a. 1 to 75% by weight pigment, b. 0.1 to 10% by weight of siliconate, c. 0.5 to 30% by weight of wetting agent, d. 15 to 75% by weight of water, the pH of the pigment paste being from 10 to 14. Pigmentpaste nach Anspruch 1, dadurch gekennzeichnet, dass sie 0,1 bis 7 Gew.%, insbesondere 0,2 bis 3 Gew.%, 0,3 bis 2 Gew.%, 0,3 bis 1 Gew.% oder 0,3 bis 0,9 Gew.%, jeweils bezogen auf das Gesamtgewicht der Pigmentpaste, Silikonat enthält.Pigment paste after Claim 1 , characterized in that they 0.1 to 7 wt.%, in particular 0.2 to 3 wt.%, 0.3 to 2 wt.%, 0.3 to 1 wt.% or 0.3 to 0.9 % By weight, based in each case on the total weight of the pigment paste, contains siliconate. Pigmentpaste nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass das Pigment ausgewählt ist aus der Gruppe bestehend aus Titandioxid, Eisenoxidgelb, Arylid (Monoazo), Bismutvanadat, (Di-)Arylide, Azokondensationspigmente, Pyranthone, Isoindoline, Anthrachinone, Derivate von Dioxazinen, Perinone, Naphtol-AS-Derivate, Perylene, Indanthrene, Phthalocyanine, Rutil-Zinn-Zink, Chinacridone, Diketo-pyrrolo-pyrrol, Eisenoxidrot, Phthalocyaninblau, Dioxazin, Kobaltblau, Ultramarinblau, Phthalocyaningrün, Chromoxidgrün, Kobaltgrün, Farbruss, Eisenoxidschwarz, Pyrazolo-Chinazolon, Naphtol-AS-Monoazopigment, Pigment Violet 23, und Mischungen davon.Pigment paste according to one of the preceding claims, characterized in that the pigment is selected from the group consisting of titanium dioxide, iron oxide yellow, arylide (monoazo), bismuth vanadate, (di) arylides, azo condensation pigments, pyranthones, isoindolines, anthraquinones, derivatives of dioxazines, perinones , Naphtol-AS derivatives, perylenes, indanthrene, phthalocyanines, rutile-tin-zinc, quinacridones, diketo-pyrrolo-pyrrole, iron oxide red, phthalocyanine blue, dioxazine, cobalt blue, ultramarine blue, phthalocyanine green, chromium oxide green, cobalt green, color black, iron oxide black quinolazole, pyrazole , Naphtol-AS monoazo pigment, Pigment Violet 23, and mixtures thereof. Pigmentpaste nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass das Netzmittel ausgewählt ist aus der Gruppe bestehend aus Diethylmaleat, Tallöl, Polyethylenpolyamin, Reaktionsprodukte aus Tallöl und Polyethylenpolyamin, Polyether, Polyetherphosphat, Polyethylenglykolmonomethylether, ortho-Kresylglycidylether, 2-Ethylhexylglycidylether, Block-Copolymere, Ammoniumsalze von Acrylatcopolymeren, Polyetherpolysiloxan, Polyoxyethylen-(2)-stearylalkohol, Polyester, fettsäuremodifizierte Polyester und Mischungen davon.Pigment paste according to one of the preceding claims, characterized in that the wetting agent is selected from the group consisting of diethyl maleate, tall oil, polyethylene polyamine, reaction products from tall oil and polyethylene polyamine, polyether, polyether phosphate, polyethylene glycol monomethyl ether, ortho-cresyl glycidyl ether, 2-ethylhexyl glycidyl ether, block copolol ether Ammonium salts of acrylate copolymers, polyether polysiloxane, polyoxyethylene (2) stearyl alcohol, polyester, fatty acid-modified polyester and mixtures thereof. Pigmentpaste nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass die Pigmentpaste 0,01 bis 60 Gew.%, insbesondere 0,01 bis 50 Gew.% oder 0,01 bis 40 Gew.% oder 0,01 bis 30 Gew.%, jeweils bezogen auf das Gesamtgewicht der Pigmentpaste, Füllstoff enthält, insbesondere ausgewählt aus der Gruppe bestehend aus Carbonaten, Sulfaten, Oxiden und Mischungen davon.Pigment paste according to one of the preceding claims, characterized in that the pigment paste 0.01 to 60% by weight, in particular 0.01 to 50% by weight or 0.01 to 40% by weight or 0.01 to 30% by weight, each based on the total weight of the pigment paste, contains filler, in particular selected from the group consisting of carbonates, sulfates, oxides and mixtures thereof. Pigmentpaste nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass der pH Wert der Pigmentpaste von 10 bis 12, insbesondere von 10,4 bis 11,6, beträgt.Pigment paste according to one of the preceding claims, characterized in that the pH of the pigment paste is from 10 to 12, in particular from 10.4 to 11.6. Pigmentpaste nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass der pH Wert der Pigmentpaste über einen Zeitraum von mindestens 4 Wochen, insbesondere mindestens 8 Wochen oder mindestens 12 Wochen oder mindestens 16 Wochen oder mindestens 20 Wochen, im Wesentlichen konstant bleibt.Pigment paste according to one of the preceding claims, characterized in that the pH of the pigment paste remains essentially constant over a period of at least 4 weeks, in particular at least 8 weeks or at least 12 weeks or at least 16 weeks or at least 20 weeks. Pigmentpaste nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass die Pigmentpaste als weitere Additive Dispergiermittel-, Rheologieadditive, Entschäumer und/oder Hydrophobierungsmittel enthält.Pigment paste according to one of the preceding claims, characterized in that the pigment paste contains, as further additives, dispersant, rheology additives, defoamers and / or hydrophobizing agents. Pigmentpaste nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass die Pigmentpaste eine Viskosität von 0,1 bis 12 Pas, vorzugsweise 0,5 bis 8 Pas, besonders bevorzugt von 0,8 bis 5 Pas, gemessen bei 23 °C und bei einer Schergeschwindigkeit von 3 s-1 im Rotationsviskosimeter mit zylindrischer Messgeometrie aufweist und/oder dass die Pigmentpaste eine Viskosität von 0,1 bis 5 Pas, vorzugsweise von 0,2 bis 3 Pas, besonders bevorzugt von 0,35 bis 1,5 Pas, gemessen bei 23 °C und bei einer Schergeschwindigkeit von 50 s-1 im Rotationsviskosimeter mit zylindrischer Messgeometrie aufweist.Pigment paste according to one of the preceding claims, characterized in that the pigment paste has a viscosity of 0.1 to 12 Pas, preferably 0.5 to 8 Pas, particularly preferably 0.8 to 5 Pas, measured at 23 ° C and at a shear rate of 3 s -1 in a rotary viscometer with a cylindrical measuring geometry and / or that the pigment paste has a viscosity of 0.1 to 5 Pas, preferably 0.2 to 3 Pas, particularly preferably 0.35 to 1.5 Pas, measured at 23 ° C and at a shear rate of 50 s -1 in a rotary viscometer with a cylindrical measuring geometry. Pigmentpaste nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass die Pigmentpaste im Wesentlichen frei von Konservierungsmitteln ist.Pigment paste according to one of the preceding claims, characterized in that the pigment paste is essentially free of preservatives. Verfahren zur Herstellung einer Pigmentpaste nach einem der Ansprüche 1 bis 10, umfassend a. Bereitstellen einer Zusammensetzung enthaltend, jeweils bezogen auf das Gesamtgewicht der Zusammensetzung, i. 1 bis 75 Gew.% Pigment, ii. 0,1 bis 10 Gew.% Silikonat, iii. 0,5 bis 30 Gew.% Netzmittel, iv. 15 bis 75 Gew.% Wasser, b. Dispergieren der in a. genannten Komponenten.Process for the preparation of a pigment paste according to one of the Claims 1 to 10 , comprising a. Providing a composition containing, in each case based on the total weight of the composition, i. 1 to 75% by weight pigment, ii. 0.1 to 10% by weight siliconate, iii. 0.5 to 30% by weight of wetting agent, iv. 15 to 75% by weight of water, b. Disperse the in a. components mentioned. Verfahren nach Anspruch 11, dadurch gekennzeichnet, dass das Verfahren einen Schritt c., Einstellen des pH Wertes auf einen Wert von 10 bis 14, umfasst.Procedure according to Claim 11 , characterized in that the method comprises a step c., adjusting the pH to a value from 10 to 14. Verfahren zur Herstellung eines Überzugsmittels, dadurch gekennzeichnet, dass mindestens eine Pigmentpaste nach einem der Ansprüche 1 bis 10 mit einem oder mehreren Beschichtungsmitteln vermischt wird.A process for producing a coating composition, characterized in that at least one pigment paste according to one of the Claims 1 to 10 is mixed with one or more coating agents. Verfahren nach Anspruch 13, dadurch gekennzeichnet, dass das Vermischen der Pigmentpaste mit dem oder den Beschichtungsmittel(n) durch einen Mischautomaten durchgeführt wird.Procedure according to Claim 13 , characterized in that the mixing of the pigment paste with the coating agent (s) is carried out by an automatic mixer. Überzugsmittel enthaltend mindestens eine Pigmentpaste nach einem der Ansprüche 1 bis 10 und mindestens ein Beschichtungsmittel.Coating agents containing at least one pigment paste according to one of the Claims 1 to 10 and at least one coating agent. Überzugsmittel nach Anspruch 15, dadurch gekennzeichnet, dass das Überzugsmittel im Wesentlichen frei von Konservierungsmitteln ist.Coating agent after Claim 15 , characterized in that the coating agent is essentially free of preservatives. Verwendung eines Silikonats zur Stabilisierung und/oder Erhöhung der Lagerstabilität von Pigmentpasten.Use of a siliconate to stabilize and / or increase the storage stability of pigment pastes.
DE102018004943.5A 2018-06-22 2018-06-22 Preservative-free pigment paste Pending DE102018004943A1 (en)