DE102006037534A1 - Thermoplastic product, useful for producing soft plastic component, comprises a first polar thermoplastic component with coherent bond to a second thermoplastic component having styrene-based thermoplastic elastomer and polyolefin - Google Patents

Thermoplastic product, useful for producing soft plastic component, comprises a first polar thermoplastic component with coherent bond to a second thermoplastic component having styrene-based thermoplastic elastomer and polyolefin Download PDF

Info

Publication number
DE102006037534A1
DE102006037534A1 DE200610037534 DE102006037534A DE102006037534A1 DE 102006037534 A1 DE102006037534 A1 DE 102006037534A1 DE 200610037534 DE200610037534 DE 200610037534 DE 102006037534 A DE102006037534 A DE 102006037534A DE 102006037534 A1 DE102006037534 A1 DE 102006037534A1
Authority
DE
Germany
Prior art keywords
thermoplastic
product according
component
styrene
polyolefin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
DE200610037534
Other languages
German (de)
Inventor
Dagmar Dr. Koppler
Manuela Gehringer
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Allod Werkstoff GmbH and Co KG
Original Assignee
Allod Werkstoff GmbH and Co KG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Allod Werkstoff GmbH and Co KG filed Critical Allod Werkstoff GmbH and Co KG
Priority to DE200610037534 priority Critical patent/DE102006037534A1/en
Priority to DE200750003616 priority patent/DE502007003616D1/en
Priority to AT07786542T priority patent/ATE466120T1/en
Priority to PCT/EP2007/006874 priority patent/WO2008017423A2/en
Priority to EP20070786542 priority patent/EP2054227B1/en
Publication of DE102006037534A1 publication Critical patent/DE102006037534A1/en
Priority to US12/367,636 priority patent/US20090197107A1/en
Priority to US13/193,193 priority patent/US8647748B2/en
Ceased legal-status Critical Current

Abstract

Thermoplastic product comprises a first polar engineering thermoplastic component with coherent bond to a second thermoplastic component, which comprises a styrene-based thermoplastic elastomer and a polyolefin. An independent claim is included for producing a composite product with selective electroplating using a hard plastic component and a soft plastic component, where for the production of the soft plastic component, a thermoplastic component from styrene-based elastomer and polyolefin is used, comprising providing an injection mold for the composite product, injection molding of the composite product and selective electroplating of the composite product.

Description

Die Erfindung betrifft ein thermoplastisches Erzeugnis.The The invention relates to a thermoplastic product.

Es ist bekannt, dass durch Kombination von SEES (Polystyrol-poly(ethylen/butylen)-polystyrol) mit polaren thermoplastischen Elastomeren, wie TPE-E (thermoplastische Polyesterelastomere) oder TPU (thermoplastische Polyurethane) gute Verbundhaftungen an technischen Thermoplasten, wie ABS (Acrylnitril-Butadien-Styrol-Copolymere), ABS/PC (Acrylnitril-Butadien-Styrol-Copolymere/Polycarbonat), PC (Polycarbonat) und PMMA (Polymethylmethacrylat) möglich sind. Entsprechende Erzeugnisse werden beispielsweise in USP 5 149 589 beschrieben.It is known that by combining SEES (polystyrene-poly (ethylene / butylene) -polystyrene) with polar thermoplastic elastomers such as TPE-E (thermoplastic polyester elastomers) or TPU (thermoplastic polyurethanes) good adhesion to engineering thermoplastics such as ABS (acrylonitrile Butadiene-styrene copolymers), ABS / PC (acrylonitrile-butadiene-styrene copolymers / polycarbonate), PC (polycarbonate) and PMMA (polymethylmethacrylate) are possible. Corresponding products are for example in USP 5,149,589 described.

Es ist ferner bekannt, dass thermoplastische Elastomere auf der Basis von SEES/PP (Polystyrol-poly(ethylen/butylen)-polystyrol/Polypropylen) ausgezeichnete Verbundhaftungen zu polyolefinischen Werkstoffen, wie Polypropylen oder Polyolefin aufweisen. Auch transparente Materialien dieser Zusammensetzung sind bekannt.It It is also known that thermoplastic elastomers are based on of SEES / PP (polystyrene-poly (ethylene / butylene) -polystyrene / polypropylene) excellent adhesion to polyolefinic materials, such as polypropylene or polyolefin. Also transparent materials of this composition are known.

Weiterhin wird in Kunststoffe 1/2005, Seiten 34-36, beschrieben, dass mit Materialien auf Basis von S-SB-S (partiell ungesättigtes Styrol/Butadien-Blockcopolymer), das unter der Marke Styroflex® vertrieben wird, Haftungen an PC, PMMA und MARS (Methylmethacrylat-Acrylnitiril/Butadien-Styrol-Copolymere) erzielt werden können. Dieses Material weist eine Härte von 85 Shore A auf. Für viele Anwendungen im Dichtungssektor wird dies als zu hart angesehen und es ist für viele Anwendungen im Außenbereich aufgrund der vorhandenen Doppelbindungen nicht einsetzbar.Furthermore, pages 34-36 that with materials based on S-SB-S (partially unsaturated styrene / butadiene block copolymer), which is marketed under the brand name Styroflex ®, liabilities of PC, PMMA is in Kunststoffe 1/2005, as described, and MARS (methyl methacrylate-acrylonitrile / butadiene-styrene copolymers) can be achieved. This material has a hardness of 85 Shore A. For many applications in the sealing sector this is considered to be too hard and it is not suitable for many outdoor applications due to the existing double bonds.

Der Stand der Technik weist ferner allgemein folgende Nachteile auf.

  • – Transparente Polymercompounds mit ausgezeichneten Verbundhaftungen an amorphen, technischen Thermoplasten mit guten Bewitterungseigenschaften sowie Shore-Härten unter 70 Shore A sind nicht möglich.
  • – Die Modifizierung von SEES mit TPE-E oder TPU sowie die Kompatibilisierung durch säuremodifiziertes SEES oder modifiziertes PP (Polypropylen) ist aufwändig und schwierig. Bei speziellen Bauteilen kann es durch den mehrphasigen Aufbau zu Delamination in der Nähe des Angusses kommen.
  • – Durch die Abmischung mit zur Hydrolyse neigenden polaren thermoplastischen Elastomeren, wie TPE-E oder TPU, müssen die Materialien vorgetrocknet werden.
  • – Ein Einsatz als Dichtungswerkstoff bei Temperaturen über 70°C ist bei haftungsmodifizierten Materialien des Standes der Technik nicht möglich.
The prior art also generally has the following disadvantages.
  • - Transparent polymer compounds with excellent adhesion to amorphous, engineering thermoplastics with good weathering properties and Shore hardnesses below 70 Shore A are not possible.
  • - The modification of SEES with TPE-E or TPU as well as the compatibilization by acid-modified SEES or modified PP (polypropylene) is complex and difficult. With special components, the multi-phase structure can lead to delamination near the gate.
  • By mixing with hydrolysis-prone polar thermoplastic elastomers such as TPE-E or TPU, the materials must be pre-dried.
  • - A use as a sealing material at temperatures above 70 ° C is not possible with adhesion-modified materials of the prior art.

Die Aufgabe vorliegender Erfindung besteht darin, die genannten Nachteile des Standes der Technik zu überwinden.The Object of the present invention is the disadvantages mentioned of the prior art overcome.

Überraschenderweise wurde gefunden, dass die Aufgabe durch ein thermoplastisches Erzeugnis gelöst wird, das dadurch gekennzeichnet ist, dass es einen ersten polaren technischen Thermoplasten mit stoffschlüssiger Verbindung mit einem zweiten Thermoplasten umfasst, der ein styrolbasierendes thermoplastisches Elastomer und ein Polyolefin umfasst.Surprisingly It was found that the task by a thermoplastic product solved which is characterized in that it is a first polar technical thermoplastics with integral connection with a second thermoplastic, which is a styrene-based thermoplastic Elastomer and a polyolefin comprises.

Hierbei beträgt in einer bevorzugten Ausführungsform der kristalline Anteil im styrolbasierenden thermoplastischen Elastomer höchstens 20 Gew.-% des Elastomers.in this connection is in a preferred embodiment the crystalline fraction in the styrene-based thermoplastic elastomer at the most 20% by weight of the elastomer.

Damit ist es nunmehr möglich, auch mit unpolaren thermoplastischen Elastomeren auf Basis von Styrolelastomeren in Kombination mit Polyolefinen Haftung an polaren technischen Thermoplasten, wie ABS, ABS/PC, PC oder PMMA zu erreichen.In order to is it now possible also with non-polar thermoplastic elastomers based on styrene elastomers in combination with polyolefins adhesion to polar engineering thermoplastics, such as ABS, ABS / PC, PC or PMMA.

Ein geringer kristalliner Anteil im styrolbasierenden thermoplastischen Elastomer kann durch geeignete Auswahl von im Handel befindlichen Styrolelastomeren aus der Gruppe der SEES mit hohem Seitenkettenanteil erreicht werden. Entsprechende Handelsprodukte sind beispielsweise Kraton® MD 6932, Kraton® MD 6924 oder Kraton® RP 6945.A low crystalline content in the styrenic based thermoplastic elastomer can be achieved by appropriate selection of commercially available styrene elastomers from the high side chain SEES group. Corresponding commercial products are, for example, Kraton® MD 6932, Kraton® MD 6924 or Kraton® RP 6945.

Eine weitere Möglichkeit hierbei besteht in der Auswahl von SEPS (Polystyrolpoly(ethylen/propylen)-polystyrol), das ebenfalls aufgrund seines molekularen Aufbaus ein amorphes Weichsegment besitzt. Entsprechende Handelsprodukte werden unter dem Handelsnamen Septon® vertrieben.Another possibility here is the selection of SEPS (polystyrene poly (ethylene / propylene) polystyrene), which also has an amorphous soft segment due to its molecular structure. Corresponding commercial products are marketed under the trade name Septon ®.

Des Weiteren kann die Kristallisation des Weichsegments bei Einsatz von üblichen SEES-Typen, wie Kraton® G1651, oder von SEEPS (Polystyrolpoly(ethylen-ethylen/propylen)-polystyrol), beispielsweise vertrieben unter der Bezeichnung Septon® 4055, durch α-Olefine, beispielsweise vertrieben unter dem Handelsnamen Engage®, oder durch ataktische Polypropylene, beispielsweise vertrieben unter dem Handelsnamen Rextac®, verhindert werden.Furthermore, the crystallization of the soft segment when using conventional SEES types, such as Kraton ® G1651, or SEEPS (Polystyrolpoly (ethylene-ethylene / propylene) -polystyrene), for example sold under the name Septon ® 4055, by α-olefins, for example sold under the trade name Engage ®, or by atactic polypropylene, for example, sold under the trade name Rextac ® can be prevented.

Dem zweiten Thermoplasten können weitere Polyolefine, ausgewählt aus der Gruppe der Homo- oder Copolymere, insbesondere PP und PE (Polyethylen) in einer Menge von bis zu 70% zugesetzt werden.the second thermoplastics can other polyolefins selected from the group of homopolymers or copolymers, in particular PP and PE (Polyethylene) are added in an amount of up to 70%.

Des Weiteren kann dem zweiten Thermoplasten ein maleinsäureanhydridmodifiziertes Polyolefin oder spezielle Styrolelastomere, die beispielsweise unter dem Handelsnamen Orevac® CA 100 oder Kraton® FG 1901 vertrieben werden, zugesetzt werden.Further, the second thermoplastic polyolefin is a maleic anhydride or special styrene elastomers are sold for example under the trade name Orevac ® CA 100 or Kraton ® FG 1901 are added.

Weiterhin können Weichmacher aus der Gruppe der paraffinischen oder technischen Öle in einer Menge von bis zu 60 Gew.-% des zweiten Thermoplasten zugesetzt werden.Farther can Plasticizers from the group of paraffinic or industrial oils in one Amount of up to 60 wt .-% of the second thermoplastic may be added.

Der zweite Thermoplast kann handelsübliche Füll- und/oder Verstärkungsstoffe, wie Calciumcarbonat, Talkum, Bariumsulfat, Metalloxide, -hydroxide oder Kieselsäure in einer Menge von bis zu 80 Gew.-% enthalten.Of the second thermoplastic can be commercially available Filling and / or Reinforcing materials, such as calcium carbonate, talc, barium sulfate, metal oxides, hydroxides or silica contained in an amount of up to 80 wt .-%.

Außerdem können übliche Additive, wie Antioxidantien, Lichtschutzmittel, Gleitmittel oder Farbstoffe zugegeben werden.In addition, conventional additives, such as antioxidants, light stabilizers, lubricants or dyes added become.

Die Erfindung soll im Folgenden anhand von Beispielen näher erläutert werden.The Invention will be explained in more detail below with reference to examples.

Beispiel 1example 1

Es wird in üblicher Weise ein Polymercompound hergestellt aus 30,3 Gew.-% SEES mit einem Seitenkettenanteil von über 60% (Kraton® RP 6924), 24,2 Gew.-% paraffinisches Weissöl (Primol 382), 3,0 Gew.-% Homopolypropylen (Borealis HD 120 MO), 18,2 Gew.-% copolymerisiertes Polypropylen (Hifax® CA 60A) und 24,3 Gew.-% CaO3 (Calcilit 6G).It is in the usual way a polymer compound made from 30.3 wt .-% SEBS with a side chain content of about 60% (Kraton ® RP 6924), 24.2 wt .-% paraffinic white oil (Primol 382), 3.0 wt. -% homopolymer polypropylene (Borealis HD 120 MO), 18.2 wt .-% of copolymerized polypropylene (Hifax ® CA 60A) and 24.3 wt .-% CaO 3 (CALCILIT 6G).

Beispiel 2Example 2

Es wird in üblicher Weise ein Polymercompound hergestellt aus 84,7 Gew.-% SEES mit einem Seitenkettenanteil von über 60% (Kraton® MD 6932) und 15,3 Gew.-% PP-MAH (Polypropylen-Maleinsäureanhydrid) (Orevac® CA 100).It is in the usual way a polymer compound made from 84.7 wt .-% SEBS with a side chain content of about 60% (Kraton ® MD 6932) and 15.3 wt .-% PP-MAH (polypropylene-maleic anhydride) (Orevac ® CA 100).

Beispiel 3Example 3

Es wird in üblicher Weise ein Polymercompound hergestellt aus 66,7 Gew.-% SEPS (Seeton® 2063), 16,7 Gew.-% copolymerisiertes Polypropylen (Hifax® CA 60A) und 16,6 Gew.-% ataktisches Polypropylen (Rextac® APAO 3585).It is in the usual way a polymer compound made from 66.7 wt .-% SEPS (Seeton ® 2063), 16.7 wt .-% of copolymerized polypropylene (Hifax ® CA 60A) and 16.6 wt .-% atactic polypropylene (Rextac ® APAO 3585).

Vergleichsbeispiel 1Comparative Example 1

Es wird in üblicher Weise ein Polymercompound hergestellt aus 19,2 Gew.-% SEES (Kraton® G1654), 5,8 Gew.-% SEBS-MAH (Kraton® FG 1901), 23,1 Gew.-% paraffinisches Weissöl (Primol 382), 32,7 Gew.-% TPE-E (Hytrel 4068) und 19,2 Gew.% CaCO3 (Calcilit 6G).It is in the usual way a polymer compound made from 19.2 wt .-% SEBS (Kraton ® G1654), 5.8 wt .-% SEBS-MAH (Kraton ® FG 1901), 23.1 wt .-% paraffinic white oil ( Primol 382), 32.7 wt% TPE-E (Hytrel 4068) and 19.2 wt% CaCO 3 (Calcilite 6G).

Vergleichsbeispiel 2Comparative Example 2

Es wird 100-prozentiges S-SB-S (Styroflex® 2G 66) eingesetzt.It is used 100 percent S-SB-S (Styroflex ® 2G 66).

Die Polymercompounds aus den Beispielen und Vergleichsbeispielen werden auf einem Zweischneckencompoundierextruder (Berstorff ZE 50 A) homogenisiert und Zweikomponenten-Verbundkörper auf der Spritzgussmaschine Klöckner-Ferromatik Typ F 110 hergestellt. Hierfür werden ABS-Platten (Polylac 717) mit Abmessungen von 150 mm·100 mm·2 mm flächig mit 2 mm der Mischungen aus den Beispielen überspritzt. Anschließend werden die Schälkräfte vergleichend mit den Mischungen aus allen Beispielen an 20 mm breiten Streifen, mit einem Abzugswinkel von 90° mit Prüfgeschwindigkeiten von 100 mm/Min an einer Zwick Zug-Prüfmaschine 1445 geprüft.The Polymer compounds from the examples and comparative examples homogenized on a twin-screw compounding extruder (Berstorff ZE 50 A) and bicomponent composite bodies on the injection molding machine Klöckner-Ferromatik Type F 110 manufactured. Therefor are ABS plates (Polylac 717) with dimensions of 150 mm x 100 mm x 2 mm flat with 2 mm of the mixtures from the examples oversprayed. Then be Comparing the peeling forces with the mixtures of all examples on 20 mm wide strips, with a take-off angle of 90 ° with test speeds of 100 mm / min on a Zwick tensile testing machine 1445 tested.

Die Mittelwerte der Schälkräfte sind in nachfolgender Tabelle angegeben, sowie die Härte der jeweiligen Mischung. Beispiel 1 Beispiel 2 Beispiel 3 Vergleichsbeispiel 1 Vergleichsbeispiel 2 Härte 55 Shore A 55 Shore A 55 Shore A 56 Shore A 84 Shore A Haftung an ABS 32 MPa 37 MPa 46 MPa 29 MPa 69 MPa The mean values of the peeling forces are given in the following table, as well as the hardness of the respective mixture. example 1 Example 2 Example 3 Comparative Example 1 Comparative Example 2 hardness 55 Shore A 55 Shore A 55 Shore A 56 Shore A 84 Shore A Liability to ABS 32 MPa 37 MPa 46 MPa 29 MPa 69 MPa

Das erfindungsgemäße thermoplastische Erzeugnis weist eine deutlich größere stoffschlüssige Verbundhaftung auf als entsprechende Erzeugnisse im Stand der Technik. Deshalb kann das erfindungsgemäße thermoplastische Erzeugnis beispielsweise als Abdichtung gegen wässrige Medien eingesetzt werden.The thermoplastic according to the invention Product has a significantly greater cohesive bond strength as corresponding products in the prior art. Therefore can the thermoplastic invention Product can be used for example as a seal against aqueous media.

Darüber hinaus hat das erfindungsgemäße thermoplastische Erzeugnis gegenüber dem Stand der Technik auch den Vorteil, dass es zugleich auch transparent sein kann, so dass beispielsweise Designern bisher unbekannte Möglichkeiten eröffnet werden.Furthermore has the thermoplastic according to the invention Product The prior art also has the advantage that it is also transparent at the same time so that designers, for example, previously unknown possibilities open become.

Ein weiterer wesentlicher Vorteil des erfindungsgemäßen thermoplastischen Erzeugnisses besteht darin, dass es auch bei Shore-Härten von 50 Shore A und darunter noch eine gute Verbundhaftung aufweist.One Another significant advantage of the thermoplastic product according to the invention This is also true for Shore hardnesses of 50 Shore A and below still has a good bond adhesion.

Claims (14)

Thermoplastisches Erzeugnis, dadurch gekennzeichnet, dass es einen ersten polaren technischen Thermoplasten mit stoffschlüssiger Verbindung mit einem zweiten Thermoplasten umfasst, der ein styrolbasierendes thermoplastisches Elastomer und ein Polyolefin umfasst.Thermoplastic product, characterized in that it comprises a first polar engineering thermoplastic material-bonded compound with a second thermoplastic comprising a styrene-based thermoplastic elastomer and a polyolefin. Thermoplastisches Erzeugnis nach Anspruch 1, dadurch gekennzeichnet, dass der kristalline Anteil im styrolbasierenden thermoplastischen Elastomer höchstens 20 Gew.-% des Elastomers beträgt.Thermoplastic product according to claim 1, characterized characterized in that the crystalline portion in the styrene-based thermoplastic elastomer at most 20 wt .-% of the elastomer. Thermoplastisches Erzeugnis nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass der zweite Thermoplast ein SEES mit einem Seitenkettenanteil von über 60% umfasst.A thermoplastic product according to claim 1 or 2, characterized in that the second thermoplastic is a SEES with a side chain content of over 60%. Thermoplastisches Erzeugnis nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass der zweite Thermoplast ein SEPS mit amorphen Weichsegmenten umfasst.A thermoplastic product according to claim 1 or 2, characterized in that the second thermoplastic is a SEPS comprising amorphous soft segments. Thermoplastisches Erzeugnis nach einem der Ansprüche 1–4, dadurch gekennzeichnet, dass der zweite Thermoplast ataktisches Polypropylen und/oder α-Olefine umfasst.Thermoplastic product according to one of claims 1-4, characterized in that the second thermoplastic is atactic polypropylene and / or α-olefins includes. Thermoplastisches Erzeugnis nach einem der Ansprüche 1–5, dadurch gekennzeichnet, dass der zweite Thermoplast ein Polyolefin enthält, ausgewählt aus der Gruppe der Homo- oder Copolymere.Thermoplastic product according to any one of claims 1-5, characterized characterized in that the second thermoplastic contains a polyolefin selected from the group of homopolymers or copolymers. Thermoplastisches Erzeugnis nach Anspruch 6, dadurch gekennzeichnet, dass das Polyolefin ein Polyethylen- oder Polypropylen-Homo- oder Copolymer ist.Thermoplastic product according to claim 6, characterized characterized in that the polyolefin is a polyethylene or polypropylene homo- or copolymer. Thermoplastisches Erzeugnis nach einem der Ansprüche 1–7, dadurch gekennzeichnet, dass der zweite Thermoplast ein säuremodifiziertes Polypropylen oder ein säuremodifiziertes styrolbasierendes thermoplastisches Elastomer aufweist.Thermoplastic product according to any one of claims 1-7, characterized characterized in that the second thermoplastic is an acid-modified Polypropylene or an acid modified having styrene-based thermoplastic elastomer. Thermoplastisches Erzeugnis nach einem der Ansprüche 1–8, dadurch gekennzeichnet, dass der zweite Thermoplast Weichmacher aus der Gruppe der paraffinischen oder technischen Öle in einer Menge von bis zu 60 Gew.-% des zweiten Thermoplasten aufweist.Thermoplastic product according to any one of claims 1-8, characterized characterized in that the second thermoplastic plasticizer from the Group of paraffinic or technical oils in an amount of up to 60 wt .-% of the second thermoplastic. Thermoplastisches Erzeugnis nach einem der Ansprüche 1–9, dadurch gekennzeichnet, dass der zweite Thermoplast Füll- und/oder Verstärkungsstoffe aufweist.Thermoplastic product according to any one of claims 1-9, characterized characterized in that the second thermoplastic filling and / or reinforcing materials having. Thermoplastisches Erzeugnis nach Anspruch 10, dadurch gekennzeichnet, dass der zweite Thermoplast Calciumcarbonat, Talkum, Bariumsulfat, Metalloxide, Metallhydroxide oder Kieselsäure von bis 80 Gew.-% des zweiten Thermoplasten aufweist.Thermoplastic product according to claim 10, characterized in that the second thermoplastic is calcium carbonate, talc, Barium sulfate, metal oxides, metal hydroxides or silica of to 80 wt .-% of the second thermoplastic. Thermoplastisches Erzeugnis nach einem der Ansprüche 1–11, dadurch gekennzeichnet, dass der zweite Thermoplast Antioxidantien, Lichtschutzmittel, Gleitmittel oder Farbstoffe aufweist.Thermoplastic product according to any one of claims 1-11, characterized characterized in that the second thermoplastic antioxidants, light stabilizers, Has lubricants or dyes. Thermoplastisches Erzeugnis nach einem der Ansprüche 1–12, dadurch gekennzeichnet, dass der erste Thermoplast ein amorpher Thermoplast ist.Thermoplastic product according to any one of claims 1-12, characterized characterized in that the first thermoplastic is an amorphous thermoplastic is. Thermoplastisches Erzeugnis nach einem der Ansprüche 1–13, dadurch gekennzeichnet, dass es spritzgießbar, extrudierbar oder kalandrierbar ist.Thermoplastic product according to any one of claims 1-13, characterized characterized in that it is injection-moldable, extrudable or calendered is.
DE200610037534 2006-08-10 2006-08-10 Thermoplastic product, useful for producing soft plastic component, comprises a first polar thermoplastic component with coherent bond to a second thermoplastic component having styrene-based thermoplastic elastomer and polyolefin Ceased DE102006037534A1 (en)