DE102005013387A1

DE102005013387A1 - Nail file has handle and file sheet and file sheet is made up of feldspar porcelain whereby file sheet comprises abrasive surface and file is formed in one-piece from porcelain

Info

Publication number: DE102005013387A1
Application number: DE200510013387
Authority: DE
Inventors: Georg Dr. Winterstein; Günther Burgold
Original assignee: Zwilling JA Henckels AG
Current assignee: Zwilling JA Henckels AG
Priority date: 2005-03-23
Filing date: 2005-03-23
Publication date: 2006-09-28

Abstract

The nail file has a handle (2) and a file sheet (1). The file sheet is made up of feldspar porcelain whereby the file sheet comprises an abrasive surface. The file is formed in one-piece from porcelain. The abrasive surface is formed as a coating. An independent claim is also included for method for the production of files.

Description

Die Erfindung betrifft eine Nagelfeile, umfassend einen Handgriff und ein Feilenblatt sowie ein Verfahren zu dessen Herstellung.The The invention relates to a nail file comprising a handle and a file sheet and a method for its production.

Nagelfeilen der eingangs genannten Art sind aus dem Stand der Technik hinreichend bekannt. So ist beispielsweise aus der WO 99/02064 eine Nagelfeile aus Glas bekannt, wobei das Feilenblatt zur Erzeugung einer rauen Oberfläche geätzt ist. Nachteilig an einer solchen Nagelfeile ist, dass die Einstellung der Oberflächenrauigkeit durch Ätzen technisch gesehen relativ aufwändig ist. Um die Bruchgefahr einer solchen Feile zu minimieren, besitzt das Blatt einen verhältnismäßig dicken Rand. Mit einer solchen Feile ist es infolgedessen unkomfortabel unter dem Nagel zu feilen.Nail filing of the type mentioned are sufficient from the prior art known. For example, from WO 99/02064 a nail file made of glass, wherein the file blade to produce a rough surface etched is. The disadvantage of such a nail file is that the setting of surface roughness by etching technically relatively complex is. To minimize the risk of breakage of such a file owns the sheet a relatively thick Edge. As a result, with such a file it is uncomfortable to file under the nail.

Darüber hinaus ist aus dem Gebrauchsmuster DE 200 18 434 eine weitere gläserne Nagelfeile bekannt, die sich von der zuvor beschriebenen Nagelfeile allein dadurch unterscheidet, dass der Griffbereich mit Erhebungen versehen ist, um die Handhabbarkeit dieser Nagelfeile zu verbessern.In addition, from the utility model DE 200 18 434 Another glass nail file known, which differs from the previously described nail file alone in that the grip area is provided with projections to improve the handling of this nail file.

Aus dem DE 297 02 530 U1 ist des Weiteren eine sogenannte handhabungsgerechte Keramikfeile bekannt. Hierbei ist insbesondere bekannt, die Herstellung des Feilenblattes aus Keramik vorzunehmen, wobei der Handgriff verschwenkbar an dem Feilenblatt angeordnet ist. Dies vor dem Hintergrund, dass erkannt wurde, dass Keramikfeilen materialbedingt von hoher Sprödigkeit sind, und dass beim Herausnehmen einer derartigen Keramikfeile bzw. einer Feile mit einem Keramikblatt aus einem Köcher es zu einem Verkanten des Feilenblattes kommen kann, was unmittelbar zu einem Bruch des Feilenblattes führt. Die Anordnung eines schwenkbaren Handgriffes an dem Feilenblatt ist technisch gesehen allerdings relativ aufwändig und verteuert eine derartige Feile unnötig. Würde man eine ausreichende Stabilität trotz hoher Sprödigkeit erzielen wollen, würde das Blatt relativ dick und damit unförmig werden, was das Feilen unter dem Nagel erschwert.From the DE 297 02 530 U1 Furthermore, a so-called handling-compatible ceramic file is known. In this case, it is in particular known to carry out the production of the file blade made of ceramic, wherein the handle is arranged pivotably on the file blade. This against the background that it has been recognized that ceramic files are due to the material of high brittleness, and that when removing such a ceramic file or a file with a ceramic sheet from a quiver it can lead to tilting of the file blade, leading directly to a fracture of the file blade leads. However, the arrangement of a pivotable handle on the file blade is technically relatively complex and expensive such a file unnecessary. If you wanted to achieve sufficient stability despite high brittleness, the sheet would be relatively thick and thus misshapen, which makes filing under the nail difficult.

Der Erfindung liegt daher die Aufgabe zugrunde, eine Nagelfeile zu schaffen, die gegenüber Feilen gemäß dem Stand der Technik eine geringere Sprödigkeit aufweist.Of the Invention is therefore based on the object to provide a nail file, the opposite files according to the state the technique has a lower brittleness having.

Eine solche Feile zeichnet sich erfindungsgemäß dadurch aus, dass zumindest das Feilenblatt aus einem Feldspat-Porzellan ausgebildet ist, wobei das Feilenblatt eine abrasive Oberfläche aufweist. Die Sprödigkeit von Keramikfeilen resultiert im Wesentlichen daher, dass Keramik als Werkstoff eine Vielzahl von Poren aufweist. Dem gegenüber ist ein aus Feldspat-Porzellan hergestelltes Feilenblatt von geringerer Sprödigkeit, weist allerdings dennoch eine größere Härte auf. Das heißt, eine Feile mit einem Feilenblatt aus Feldspat-Porzellan ist aufgrund der erhöhten Stabilität wesentlich handhabungsfreundlicher, was sich insbesondere in einem gegenüber einer Keramikfeile vergleichsweise dünnen Blatt mit ebenfalls einem dünnen Rand niederschlägt. Mit einer solchen Feile kann auch bequem unter dem Nagel gefeilt werden. Außerdem ist aufgrund der schlankeren Ausführen einer Porzellanfeile eine solche Feile auch vom Design her ansprechender als eine Keramikfeile.A Such file is characterized according to the invention by the fact that at least the file blade is formed from a feldspar porcelain, wherein the File blade an abrasive surface having. The brittleness of ceramic files essentially results from that ceramic as material has a plurality of pores. Opposite is a file made of feldspar porcelain of less brittleness, nevertheless has a higher hardness. This means, a file with a blade of feldspar porcelain is due the heightened stability much easier to handle, which is especially in one across from a ceramic file comparatively thin sheet with also one thin Edge precipitates. With such a file can also be filed conveniently under the nail become. Furthermore is one due to the slimmer running of a porcelain file Such a file is also more appealing in design than a ceramic file.

Weitere vorteilhafte Merkmale sowie ein Verfahren zur Herstellung einer Porzellanfeile aus Feldspan-Porzellan sind den Unteransprüchen zu entnehmen.Further advantageous features and a method for producing a Porcelain file made of feldspar porcelain are the dependent claims remove.

So ist insbesondere vorgesehen, dass die Feile einteilig aus Feldspat-Porzellan ausgebildet ist, dass also sowohl der Handgriff als auch das Feilenblatt aus Feldspat-Porzellan einteilig hergestellt sind. Die einteilige Herstellung einer solchen Feile aus Feldspat-Porzellan ist wesentlich kostengünstiger, als ein Feilenblatt mit einem gesonderten Handgriff zu versehen, ohne dass hierunter die Handhabbarkeit leitet.So In particular, it is provided that the file is integrally formed from feldspar porcelain is that so both the handle and the file blade off Feldspar porcelain are made in one piece. The one-piece production Such a file of feldspar porcelain is much cheaper than to provide a file sheet with a separate handle, without that hereunder manages the handling.

In Bezug auf die abrasive Oberfläche ist nach einem weiteren vorteilhaften Merkmal der Erfindung vorgesehen, dass die abrasive Oberfläche als Beschichtung auf dem Feilenblatt angeordnet ist. Hieraus wird deutlich, dass der Grundkörper, und hier insbesondere das Feilenblatt, aus einer reinen Feldspat-Porzellanmasse bestehen kann, und die Beschichtung zur Erzeugung einer abrasiven Oberfläche erst in einem nachfolgenden Arbeitsgang aufgebracht wird. Vorstellbar wäre hingegen auch, abrasive Medien unmittelbar in die Porzellanmasse mit einzubringen, um auf diese Weise aufgrund des Materials eine abrasive Oberfläche zu schaffen. Eine solche Vorgehensweise hätte allerdings den Nachteil, dass durch die abrasiven Mittel, die in einem solchen Fall in der Porzellanmasse eingelagert wären, die Gefügestruktur des Feldspat-Porzellans derart gestört wäre, dass das Sprödbruchverhalten einer solchen Feile erheblich zunimmt.In Reference to the abrasive surface is provided according to a further advantageous feature of the invention, that the abrasive surface is arranged as a coating on the file sheet. This will become clearly that the main body, and here in particular the file sheet, from a pure feldspar porcelain mass can exist, and the coating to produce an abrasive surface is applied only in a subsequent operation. imaginable would be contrary Also, to introduce abrasive media directly into the porcelain mass, to create an abrasive surface due to the material in this way. Such an approach would have however, the disadvantage that due to the abrasive agents that in In such a case would be embedded in the porcelain mass, the microstructure of the feldspar porcelain would be so disturbed that the brittle fracture behavior such a file increases considerably.

Dem Ziel einer erhöhten Stabilität des Feilenblattes wird des Weiteren dadurch Rechnung getragen, dass das Feilenblatt im Querschnitt mit gewölbter Unter- und Oberseite ausgebildet ist, also eine im Querschnitt etwa ovale Kontur besitzt. Durch diese Formgebung erhält die Feile eine gegenüber einer flachen Feile erhöhte Stabilität.the Goal of an elevated stability of the file sheet is further taken into account by the fact that the file blade in cross-section with arched lower and upper side is formed, so has a cross-sectionally approximately oval contour. By this shaping receives the file opposite a flat file increased Stability.

Bereits an anderer Stelle wurde dargelegt, dass die abrasive Oberfläche im Wege einer Glasur auf den Feilenkörper bzw. auf das Feilenblatt aufgebracht wird. In diesem Zusammenhang ist vorgesehen, dass eine solche Glasur bzw. die Beschichtung Korund aufweist. Hierbei ist insbesondere vorgesehen, dass der Anteil an Korund zwischen 30 % und 65 %, bezogen auf die Gesamtfeststoffmasse, aus Glasurpulver und Korund liegt. Hierbei erhöht sich die Rauigkeit mit steigendem Korundanteil in der Glasur. Die Glasur besteht demzufolge im Wesentlichen aus Wasser, Glasurpulver und Korund, wobei das Glasurpulver Anteile von Kaolin, Quarzsand und Feldspat aufweist. Eine Glasur in flüssiger Form wird auch als "Schlicker" bezeichnet.It has already been stated elsewhere that the abrasive surface is applied by way of a glaze on the file body or on the file sheet. In this context, it is provided that such a glaze or the coating has corundum. In this case, it is provided in particular that the proportion of corundum is between 30% and 65%, based on the total solids mass, of glaze powder and corundum. This increases the roughness with increasing corundum content in the glaze. Accordingly, the glaze consists essentially of water, glaze powder and corundum, the glaze powder having fractions of kaolin, quartz sand and feldspar. A glaze in liquid form is also called "slip".

Darüber hinaus können zur Feineinstellung der Rauigkeit der abrasiven Oberfläche Korunde unterschiedlicher Körnung Verwendung finden, bzw. auch Gemische aus Korunden unterschiedlicher Körnung.Furthermore can for fine adjustment of the roughness of the abrasive surface corundum different grain size Use, or mixtures of corundums different Grain.

Es hat sich daher darüber hinaus weiterhin als vorteilhaft herausgestellt, wenn der Glasurschlicker einen Anteil an Zelluloselösung aufweist. Die Zelluloselösung bewirkt eine bessere Haftung der Korundanteile in der fertigen Glasur. Darüber hinaus verhindert die Zelluloselösung in dem Glasurschlicker ein zu schnelles Absetzen der festen Bestandteile; der Schlicker wird viskoser. Hieraus wird deutlich, dass die Handhabung des Schlickers durch die Zelluloselösung erhöht wird.It has therefore about it furthermore, it has been found to be advantageous if the glaze slip a proportion of cellulose solution having. The cellulose solution causes a better adhesion of the corundum in the finished glaze. About that In addition, the cellulose solution prevents in the glaze slip too fast settling of the solid constituents; the slip becomes more viscous. From this it becomes clear that the handling of the slip is increased by the cellulose solution.

Gegenstand der Erfindung ist auch ein Verfahren zur Herstellung einer Feile gemäß einem oder mehrerer der voranstehend abgehandelten Merkmale, wobei insbesondere vorgesehen ist, dass der gegossene und getrocknete Porzellanrohling in den Glasurschicker eingetaucht wird, wobei der Glasurschicker einen Anteil an Korund aufweist, wobei nach einem Trockenvorgang die Rohlinge gebrannt werden.object The invention also relates to a method for producing a file according to one or more of the above-discussed features, in particular provided is that the cast and dried porcelain blank is immersed in the glaze, with the glaze having a proportion of corundum, wherein after a drying process the blanks are fired.

Ein anderes Verfahren zur Herstellung einer Feile zeichnet sich dadurch aus, dass der gegossene und getrocknete Rohling gebrannt wird, wobei nach dem Brand dieser gebrannte Porzellanrohling in den Glasurschlicker eingetaucht wird, wobei der Glasurschlicker einen Korundanteil aufweist, und wobei nachfolgend dieser gebrannte, mit einem Schlicker überzogene Porzellanrohling einem zweiten Brand unterzogen wird. Es hat sich gezeigt, dass nach der zweiten Verfahrensvariante hergestellte Nagelfeilen eine etwas dickere Beschichtung aufweisen, da der Glasurschlicker in einer vorgebrannten Feile nicht in dem Maße in die Porzellanrohmasse eindringen kann, wie das bei einem nichtgebrannten Porzellanrohling der Fall ist. Insofern ist nach einem weiteren Merkmal in Bezug auf das erste Verfahren auch vorgesehen, dass vor dem Eintauchen des Porzellanrohlings in den Glasurschlicker der Porzellanrohling ausgiebig in Wasser getränkt wird.One another method of making a file is characterized from that the cast and dried blank is fired, wherein after firing this fired porcelain blank in the glaze slip immersed, wherein the glaze slip has a corundum content, and wherein subsequently this fired, with a slip coated Porcelain blank is subjected to a second fire. It has shown that prepared according to the second process variant nail files a have somewhat thicker coating, since the glaze slip in a pre-burned file not to the extent in the porcelain raw mass can penetrate, as with a non-burned porcelain blank the case is. In this respect is related to another feature on the first procedure also provided that before immersion of the porcelain blank in the glaze slip the porcelain blank extensively soaked in water becomes.

Anhand der Zeichnung wird die Erfindung nachstehend beispielhaft näher erläutert, wobei nachfolgend ebenfalls noch ein Beispiel für eine Glasur aufgeführt ist.Based the drawing, the invention is explained in more detail below, for example, below another example for a glaze listed is.

1 zeigt die Feile in perspektivischer Darstellung; 1 shows the file in perspective view;

2 zeigt einen Schnitt gemäß Linie II-II aus 1 in vergrößerter Darstellung. 2 shows a section along line II-II 1 in an enlarged view.

In der Zeichnung ist eine vollständig aus Feldspat-Porzellan hergestellte Feile erkennbar, wobei sowohl das Feilenblatt 1 als auch der Handgriff 2 einteilig aus Feldspat-Porzellan hergestellt sind. Hierbei ist das Feilenblatt im Querschnitt nach Art eines schlanken Ovals ausgebildet, d. h. die Unter- und die Oberseite des Feilenblattes besitzen eine leichte Wölbung. Wie bei jedem anderen Feilenblatt auch, läuft das Feilenblatt zum Ende hin spitz zu. Der Vorteil der Verwendung eines im Querschnitt flachovalen Feilenblattes besteht darin, dass ein solches Feilenblatt eine höhere Stabilität aufweist, als ein beispielsweise lediglich flaches Feilenblatt. Dennoch kann aufgrund des flachen Randes eines solchen flachovalen Feilenblattes auch die Nagelunterseite gut bearbeitet werden.In the drawing, a file made entirely of feldspar porcelain can be seen, with both the file blade 1 as well as the handle 2 made in one piece from feldspar porcelain. Here, the file sheet is formed in cross section in the manner of a slender oval, ie, the lower and the upper side of the file blade have a slight curvature. As with any other file sheet, the file blade runs towards the end pointed. The advantage of using a flat-section flat-oval file blade is that such a file blade has a higher stability than, for example, only a flat file blade. Nevertheless, due to the flat edge of such a flat oval file blade and the nail base can be edited well.

Für die Herstellung einer derartigen Feile aus Feldspat-Porzellan wird nun in solcher Weise vorgegangen, dass zunächst die Rohmasse aus Feldspat-Porzellan in eine Form gegossen wird, wobei die zu beschichtenden saugfähigen Porzellanrohlinge vor dem Eintauchen in den Schlicker mit Wasser getränkt werden. Alsdann werden die so beschichteten Feilenrohlinge getrocknet, um nachfolgend bei etwa 1400 °C gebrannt zu werden.For the production Such a file of feldspar porcelain will now be in such Way proceeded that first the raw mass of feldspar porcelain is poured into a mold, wherein the absorbent porcelain blanks to be coated are present immersed in the slurry with water soaked. Then be The so coated filing blanks dried to below at about 1400 ° C to be burned.

Nach einer anderen Verfahrensvariante ist vorgesehen, dass die Feldspat-Porzellanrohlinge zunächst einem ersten Brand bei ca. 1400 °C, unterzogen werden, alsdann in den Glasurschlicker getaucht werden, um dann zum zweiten Mal bei ca. 1400 ° C gebrannt zu werden.To another variant of the method is provided that the feldspar porcelain blanks first a first fire at about 1400 ° C, are then immersed in the glaze slip, to be fired for the second time at about 1400 ° C.

Beispiel für die Rezeptur eines Glasurschlickers:
40 % Anteile Wasser als 2-5 % Zelluloselösung
60 % Gesamtfeststoff, davon 50 % Glasurpulver (Kaolin, Feldspat, Quarzsand) mit körnigen Anteilen und 50 % Korund gegebenenfalls unterschiedlicher Körnung;
geringe Mengen an Entschäumer.Example of the recipe of a glaze slip:
40% water as 2-5% cellulose solution
60% total solids, of which 50% glaze powder (kaolin, feldspar, quartz sand) with granular fractions and 50% corundum, optionally of different grain size;
small amounts of defoamer.

Der Entschäumer verhindert die Bildung von Schaum beim Rühren des Schlickers.Of the defoamers prevents the formation of foam when stirring the slurry.

Der Gesamtfeststoff, bestehend aus pulvriger Glasur und Edelkorund, wird mit dem Wasser und der Zelluloselösung sowie dem Entschäumer vermischt und bildet so den Glasurschlicker. Vor dem Tauchvorgang des Porzellanrohlings wird dieser sogenannte Schlicker gut aufgeführt, um eine gleichmäßige Verteilung der Feststoffe und insbesondere des Korundes in dem Schlicker zu bewerkstelligen.Of the Total solids, consisting of powdery glaze and precious corundum, is mixed with the water and the cellulose solution and the defoamer and thus forms the glaze slip. Before the dipping process of the porcelain blank This so-called slip is well listed to ensure even distribution the solids and especially the corundum in the slurry accomplish.

Claims

Nail file, comprising a handle and a file blade, characterized in that at least the file blade is formed of feldspar porcelain, wherein the file blade has an abrasive surface.

Nail file according to claim 1, characterized that the file is integrally formed of porcelain.

Nail file according to claim 1, characterized that the abrasive surface is designed as a coating.

Nail file according to claim 3, characterized that the coating is made of abrasive embedded in a glaze Elements is formed.

Nail file according to one or more of the preceding Claims, characterized in that the file blade in cross section to Type of a flat oval is formed.

Nail file according to claim 3, characterized the coating has a corundum content.

Nail file according to one or more of the preceding Claims, characterized in that the proportion of corundum between 30 and 65%, based on the total solids mass, of glaze powder and Corundum lies.

Nail file according to one or more of the preceding Claims, characterized in that the corundum has a different grain size.

Nail file according to one or more of the preceding Claims, characterized in that the glaze slip a proportion of cellulose having.

Nail file according to one or more of the preceding Claims, characterized in that the glaze shares of kaolin, quartz sand and feldspar.

Method for producing a file according to or more of the claims 1 to 10, characterized in that the cast and dried Blank made of feldspar porcelain is immersed in a glaze slip, the glaze slip having a corundum, wherein after a drying process Blanks are fired.

Method for producing a file according to or more of the preceding claims 1 to 10, characterized that the cast and dried blank fired from feldspar porcelain After firing, the fired porcelain blank is put into a glaze slip immersed, wherein the glaze slip has a corundum content, and wherein subsequently the fired feldspar porcelain blank a second fire is subjected.

Method according to claim 11, characterized in that that the cast and dried feldspar porcelain blank before Dipping in the glass slurry is soaked in water.

Process according to claims 11 and 12, characterized that the firing temperature is about 1400 ° C.