DE102004041725B3

DE102004041725B3 - Green body producing device for dental application, has set of electrodes applicable in respective recesses, and another set of electrodes through which direct separation of particles of suspension takes place

Info

Publication number: DE102004041725B3
Application number: DE200410041725
Authority: DE
Inventors: Uwe Dr. Böhm; Wilhelm Heim
Original assignee: Hafner & Co Gold und Silb GmbH; C Hafner GmbH and Co KG
Current assignee: Hafner & Co Gold und Silb GmbH; C Hafner GmbH and Co KG
Priority date: 2004-08-28
Filing date: 2004-08-28
Publication date: 2005-12-08
Anticipated expiration: 2024-08-29

Abstract

The device has a set of electrodes (3a-3c) applicable in respective recesses of a form. Another set of electrodes (5`, 5``) through which direct separation of particles of a suspension takes place. The electrode (3c) has a casing, where interior of the casing is introduced with liquids. The electrode (5``) has a round bar that is insertable in one of the recesses. An independent claim is also included for a device for producing a green body for dental application.

Description

Die Erfindung betrifft eine Vorrichtung und ein Verfahren zur Herstellung eines Grünkörpers, insbesondere für dentale Anwendungen, aus welchem ein Formkörper mittels Sintern herstellbar ist, wobei der Grünkörper durch elektrophoretische Abscheidung von Partikeln aus einer Suspension gebildet wird, indem die Partikel auf einer in der Suspension angeordneten porösen Form abgeschieden werden, deren Form mit der Form des herzustellenden Grünkörpers korreliert ist und die mindestens eine mit einer elektrisch leitenden Flüssigkeit gefüllte Ausnehmung aufweist, in der eine Elektrode für die elektrophoretische Abscheidung der Partikel der Suspension auf die poröse Form angeordnet ist, wobei die Vorrichtung mindestens eine Elektrode aufweist, die in die entsprechende Ausnehmung der porösen Form einsetzbar ist.The The invention relates to an apparatus and a method for the production a green body, in particular for dental Applications from which a shaped body produced by sintering is, wherein the green body by electrophoretic deposition of particles from a suspension is formed by placing the particles on a suspension porous Form are deposited, the shape of which with the shape of the produced Green body correlates is and the at least one with an electrically conductive liquid filled Has recess in which an electrode for the electrophoretic deposition the particle of the suspension is arranged on the porous mold, wherein the device has at least one electrode which fits into the corresponding one Recess of the porous Form is usable.

Ein derartiges Verfahren sowie ein zur Durchführung des Verfahrens geeignete Vorrichtung ist aus der älteren Anmeldung DE 103 20 936.0 der Anmelderin sowie der EP 0 200 242 bekannt.Such a method and a device suitable for carrying out the method are known from the earlier application DE 103 20 936.0 the applicant and the EP 0 200 242 known.

Das bekannte Verfahren sowie die bekannte Vorrichtung eignen sich insbesondere zur Herstellung eines vollkeramischen Grünkörpers für dentale Anwendungen, insbesondere für einen metallfreien vollkeramischen dentalen Zahnersatz, welcher sich in der jüngeren Vergangenheit als alternative Versorgung zur Vollmetall- sowie Verbundrestauration in der Kronen- und Brückenprothetik etabliert hat. Hierbei erfolgt zur Vermeidung von durch Bläschen geöffneter großer Poren im Grünkörper die elektrophoretische Abscheidung nicht mehr direkt auf eine Elektrode (die dann die Form des herzustellenden Grünkörpers haben muß), sondern auf einer porösen Form, die als eine zwischen den beiden Elektroden angeordnete poröse Membran fungiert und die Form des herzustellenden Grünkörpers aufweist. Nach Anlegen einer elektrischen Gleichspannung an die beiden Elektroden findet eine Abscheidung und somit Formgebung eines Grünkörpers an der porösen Membran statt.The known methods and the known device are particularly suitable for producing a all-ceramic green body for dental applications, in particular for one metal-free all-ceramic dental restorations, which are in the younger ones Past as an alternative supply for full metal and composite restorations in crown and bridge prosthetics has established. This is done to avoid being opened by bubbles greater Pores in the green body the electrophoretic deposition no longer directly on an electrode (which must then have the shape of the green body to be produced), but on a porous Shape, as a arranged between the two electrodes porous membrane acts and has the shape of the green body to be produced. After donning a DC electrical voltage to the two electrodes a deposition and thus shaping of a green body on the porous membrane instead.

Um einen Abscheidekörper mit einer möglichst gleichmäßigen Wanddicke und einer hohen Homogenitäi zu erhalten, ist es bei dem bekannten Verfahren erforderlich, dass insbesondere die in der Ausnehmung der porösen Form angeordnete Elektrode so ausgebildet und/oder angeordnet ist, dass sie überall denselben Abstand zur Oberfläche der porösen Form hat.Around a separation body with one as possible uniform wall thickness and a high homogeneity To obtain, it is necessary in the known method that in particular, the electrode arranged in the recess of the porous mold is designed and / or arranged to be the same everywhere Distance to the surface the porous one Has shape.

Das bekannte Verfahren und die bekannte Vorrichtung wurden bis jetzt erfolgreich zur elektrophoretischen Herstellung von Kronen verwendet. Eine elektrophoretische Abscheidung von Brücken ist mit der bekannten Vorrichtung und dem bekannten Verfahren aber noch nicht möglich, da aufgrund der im vorstehenden Absatz beschriebenen Bedingungen eine hinreichende Wandstärke und/oder die erforderliche Homogenität des Grünkörpers über die gesamte Ausdehnung des Brückengerüsts und insbesondere in einem Brückenzwischenbereich nicht erzielbar sind.The known methods and the known device have been so far successfully used for the electrophoretic production of crowns. A Electrophoretic deposition of bridges is known Device and the known method but not yet possible because due to the conditions described in the preceding paragraph adequate wall thickness and / or the required homogeneity of the green body over the entire extent of the bridge framework and especially in a bridge area are not achievable.

Aus der DE 102 51 369 ist ein Verfahren zur Herstellung vollkeramischer Brückengerüste in der Zahntechnik mittels Elektrophorese bekannt, wobei zwischen zwei Stümpfen eines Arbeitsmodels ein elektrisch leitendes oder leitend gemachtes Plättchen eingebracht wird, dass die beiden Stümpfe berührt, wobei während der Elektrophorese das Plättchen mit dem Pluspol verbunden ist. Hierdurch soll in 45–60 Sekunden ein Brückenzwischenglied gleichzeitig mit dem Plättchen hergestellt werden können. Die Form ist hier aus einem elektrisch leitenden Material gefertigt und bildet somit eine Elektrode für den elektrophoretischen Abscheidevorgangs aus. Es erfolgt also bei diesem Verfahren wiederum eine direkte Abscheidung auf die Elektrode, nicht aber, wie bei dem vorstehend beschriebenen Verfahren, auf eine poröse Membran. Dieses Verfahren ermöglicht somit zwar eine Herstellung eines Brückengerüst durch elektrophoretische Abscheidung, weist aber wiederum die bekannten Nachteile einer Direkt-Abscheidung auf, welche durch die elektrophoretische Membran-Abscheidung vermieden werden sollen.From the DE 102 51 369 is a method for producing all-ceramic bridge frameworks in dental technology by means of electrophoresis, wherein between two stumps of a working model, an electrically conductive or conductive made platelets is introduced that touches the two stumps, wherein the plate is connected to the positive pole during electrophoresis. This should be able to be made in 45-60 seconds, a bridge link at the same time with the platelets. The mold is here made of an electrically conductive material and thus forms an electrode for the electrophoretic deposition process. Thus, in this method, again a direct deposition on the electrode takes place, but not, as in the method described above, on a porous membrane. Although this method thus makes it possible to produce a bridge framework by electrophoretic deposition, it again has the known disadvantages of direct deposition, which are to be avoided by the electrophoretic membrane deposition.

Es ist daher Aufgabe der vorliegenden Erfindung, eine Vorrichtung und ein Verfahren der eingangs genannten Art derart weiterzubilden, dass auf der Grundlage einer elektrophoretischen Abscheidung auf eine poröse Membran eine zumindest dreigliedrige Brücke herstellbar ist.It is therefore an object of the present invention, an apparatus and to develop a method of the type mentioned above in such a way that based on electrophoretic deposition on a porous one Membrane an at least three-membered bridge can be produced.

Diese Aufgabe wird durch die erfindungsgemäße Vorrichtung dadurch gelöst, dass die Vorrichtung mindestens eine weitere Elektrode aufweist, durch die eine direkte Abscheidung der Partikel der Suspension auf die mindestens eine weitere Elektrode erfolgt.These The object is achieved by the device according to the invention in that the device has at least one further electrode a direct deposition of the particles of the suspension on the at least one further electrode takes place.

Zur Lösung der oben genannten Aufgabe sieht das erfindungsgemäße Verfahren vor, dass die Herstellung eines Teilbereichs des Grünkörpers durch eine direkte Abscheidung der Partikeln auf eine außerhalb der porösen Form angeordnete weitere Elektrode erfolgt.to solution The above-mentioned object provides the method according to the invention that the production of a portion of the green body by a direct deposition of the particles on an outside the porous one Form arranged further electrode takes place.

Durch erfindungsgemäßen Maßnahmen wird in vorteilhafter Art und Weise ein Verfahren und eine Vorrichtung geschaffen, welche es erlauben, auch mehrteilige Brückenglieder durch eine elektrophoretische Membran-Abscheidung, unterstützt von einer elektrophoretischen Direkt-Abscheidung auf die weitere Elektrode, herzustellen, so dass in vorteilhafter Art und Weise die Vorteile einer Membran-Abscheidung auch in der Brückenprothetik genutzt werden können.By measures according to the invention, a method and a device is provided in an advantageous manner, which also allow multi-part bridge members by a elektrophoreti membrane deposition, supported by an electrophoretic direct deposition on the other electrode to produce, so that in an advantageous manner, the advantages of a membrane deposition can also be used in the bridge prosthetics.

Vorteilhafte Weiterbildungen der Erfindung sind Gegenstand der Unteransprüche.advantageous Further developments of the invention are the subject of the dependent claims.

Weitere Einzelheiten und Vorteile sind den Ausführungsbeispielen zu entnehmen, die im folgenden anhand der Figuren beschrieben werden. Es zeigen:Further Details and advantages can be seen in the exemplary embodiments. which are described below with reference to the figures. Show it:

1: Ein erstes Ausführungsbeispiel einer Vorrichtung zur Durchführung des Verfahrens, 1 A first exemplary embodiment of an apparatus for carrying out the method

2: das Ausführungsbeispiel der 1 zusammen mit einer Form, 2 : the embodiment of 1 along with a shape,

3: einen Längsschnitt durch das erste Ausführungsbeispiel der 2, 3 a longitudinal section through the first embodiment of 2 .

4: das in eine Gegenelektrode eingetauchte Ausführungsbeispiel der 1, 4 the immersed in a counter electrode embodiment of the 1 .

5: ein zweites Ausführungsbeispiel einer Vorrichtung, 5 : a second embodiment of a device,

6: ein drittes Ausführungsbeispiel einer Vorrichtung, und 6 a third embodiment of a device, and

7: das dritte Ausführungsbeispiel zusammen mit einer Form. 7 the third embodiment together with a mold.

In den 1 bis 4 ist ein erstes Ausführungsbeispiel einer allgemein mit 1 bezeichneten Vorrichtung zur elektrophoretischen Abscheidung eines Grünkörpers auf einer porösen Form 2 (siehe dazu 2) dargestellt, welche mittels dentaltechnisch gängiger Methoden von zwei durch eine Zahnlücke getrennte Zahnstümpfen abgeformt wurde. Die Form 2 stellt also das Positivmodel einer Brückenprothetik dar und weist somit den Positivabdruck zweier Zahnstümpfe Z1 und Z2 auf, die bei der fertigen Prothetik durch ein Brückenzwischenglied verbunden sein sollen, welches sich über den Bereich Z' der Form 2 erstreckt. Vorzugsweise ist die Form 2 aus einem gießfähigen, aushärtenden und porösen Dublierwerkstoff, z. B. Kunststoff, Metallverbindungen oder Gips, insbesondere expandierenden Dentalgips, ausgebildet. In der Form 2 sind drei Ausnehmungen 2a, 2b, 2c eingebracht, deren Funktion weiter unten noch erläutert wird.In the 1 to 4 is a first embodiment of a generally with 1 designated device for electrophoretic deposition of a green body on a porous mold 2 (see 2 ), which was molded by means of common dental technology methods of two separated by a tooth gap tooth stumps. Form 2 thus represents the positive model of a bridge prosthesis and thus has the positive impression of two tooth stumps Z1 and Z2, which should be connected in the finished prosthetics by a bridge intermediate, which extends over the area Z 'of the mold 2 extends. Preferably, the shape 2 from a pourable, hardening and porous duplicating material, eg. As plastic, metal compounds or gypsum, in particular expanding dental gypsum formed. In the shape 2 are three recesses 2a . 2 B . 2c whose function will be explained below.

Die Vorrichtung 1 weist nun – wie am besten aus 1 ersichtlich ist – drei Elektroden 3a–3c auf, welche in die Ausnehmungen 2a–2c der Form 2 einbringbar sind. Die in 1 linke, erste Elektrode 3a taucht dabei in die Ausnehmung 2a und die in 1 rechte, zweite Elektrode 3b in die Ausnehmung 2b ein. Die mittlere Elektrode 3c ist nicht – wie die Elektroden 3a und 3b – bügelförmig ausgebildet, sondern ist als Hülse 4 mit einem im Durchmesser vergrößerten Bereich 4a und in einem im Durchmesser verringerten Bereich 4b ausgebildet, wobei der Übergang zwischen den beiden Bereichen 4a, 4b als Stufe 4c ausgestaltet ist.The device 1 now shows - how best 1 it can be seen - three electrodes 3a - 3c on which in the recesses 2a - 2c the form 2 can be introduced. In the 1 left, first electrode 3a dives into the recess 2a and the in 1 right, second electrode 3b into the recess 2 B one. The middle electrode 3c is not - like the electrodes 3a and 3b - Formed bow-shaped, but is as a sleeve 4 with an enlarged diameter area 4a and in a reduced diameter area 4b formed, with the transition between the two areas 4a . 4b as a stage 4c is designed.

Durch diese Stufe 4c wird dabei die Eindringtiefe der Hülse 4 in die Ausnehmung 2c begrenzt. Vorzugsweise ist der Durchmesser der Ausnehmung 2c auf den Außendurchmesser der Hülse 4 der dritten Elektrode 3c derart abgestimmt, dass die Hülse 4 fest in der Ausnehmung 2c steckt, jedoch mit mässigem Kraftaufwand aus ihr entfernbar ist. Eine derartige Ausgestaltung besitzt den Vorteil, dass durch die Hülse 4 der dritten Elektrode 3c die Form 2 ohne zusätzliche Halterung in der Vorrichtung 1 gehalten werden kann. Natürlich ist es auch möglich, die dritte Elektrode 3c nicht als Hülse 4, sondern als Bügel auszuführen und die Form 2 durch eine zusätzliche, ggf. auch vorrichtungsexterne Halterung festzuhalten.Through this stage 4c is the penetration depth of the sleeve 4 into the recess 2c limited. Preferably, the diameter of the recess 2c on the outer diameter of the sleeve 4 the third electrode 3c tuned so that the sleeve 4 firmly in the recess 2c but it can be removed with moderate effort. Such a configuration has the advantage that through the sleeve 4 the third electrode 3c form 2 without additional support in the device 1 can be held. Of course it is also possible to use the third electrode 3c not as a sleeve 4 but to perform as a temple and the shape 2 hold by an additional, possibly also device external holder.

Bezüglich der Hülse 4 ist noch auszuführen, dass es bevorzugt wird, dass der im Durchmesser geringere Bereich 4b der Hülse 4 eine Vielzahl von Bohrungen (nicht gezeigt) aufweist, durch die in den Innenraum 4' der Hülse 4 eingebrachte Ausgleichsflüssigkeit in die Form 2 eindringen kann. Durch die Verwendung einer elektrisch leitenden Ausgleichsflüssigkeit wird dann ein sehr guter elektrischer Kontakt zwischen der Hülse 4 und der Oberfläche der Ausnehmung 2c hergestellt.Regarding the sleeve 4 is still to be executed, that it is preferred that the smaller diameter portion 4b the sleeve 4 a plurality of bores (not shown) through which in the interior 4 ' the sleeve 4 introduced compensation fluid in the mold 2 can penetrate. By using an electrically conductive equalizing fluid then a very good electrical contact between the sleeve 4 and the surface of the recess 2c produced.

An dieser Stelle soll noch angemerkt werden, dass es natürlich auch möglich ist, eine oder beide der Elektroden 3a, 3b wie die dritte Elektrode 3c, also mit einer Hülse 4, auszubilden. Selbstverständlich ist es auch möglich, die dritte Elektrode 3c bügelförmig auszubilden. Auch eine beliebige Kombination von draht- oder bügelförmigen Elektroden und Hülsen-Elektroden ist möglich.It should also be noted at this point that it is of course also possible, one or both of the electrodes 3a . 3b like the third electrode 3c So with a sleeve 4 to train. Of course it is also possible, the third electrode 3c form bow-shaped. Any combination of wire or bow-shaped electrodes and sleeve electrodes is possible.

Die Vorrichtung 1 weist nun des weiteren eine weitere Elektrode 5 auf, die – wie am besten aus den 2 und 3 ersichtlich – die Form 2 im Bereich Z' zwischen den beiden Zahnstümpfen Z1 und Z2 umschließt. Die weitere Elektrode 5 ist vorzugsweise lösbar in der Vorrichtung 1 aufgenommen. Bei dem hier beschriebenen Ausführungsbeispiel wird dies dadurch erreicht, dass die Hülse 4 der dritten Elektrode 3c eine Bohrung 6 aufweist, in welche ein Ende 5' der weiteren Elektrode 5 einschiebbar und dort mittels eines Arretierelements 7, z. B. einer Feststellschraube, in einer definierten Lage fixierbar ist. Durch eine derartige Ausgestaltung wird – wie weiter unten noch beschrieben wird – das Einsetzen der Form 2 in die Vorrichtung 1 erleichtert.The device 1 now has another further electrode 5 on, which - as best of the 2 and 3 apparent - the form 2 in the area Z 'between the two tooth stubs Z1 and Z2 encloses. The further electrode 5 is preferably detachable in the device 1 added. In the embodiment described here, this is achieved in that the sleeve 4 the third electrode 3c a hole 6 has, in which an end 5 ' the further electrode 5 insertable and there by means of a locking element 7 , z. B. a locking screw, can be fixed in a defined position. By such a configuration is - as will be described below - the onset of the mold 2 into the device 1 facilitated.

Die Funktionsweise der Vorrichtung 1 ist nun wie folgt: Nachdem die Form 2 in bereits bekannter Art und Weise als Positivmodel der herzustellenden Brückenprothetik aus einem entsprechenden porösen Material gefertigt und die Ausnehmungen 2a–2c ausgebildet wurden, werden die Elektroden 3a–3c in die Ausnehmungen 2a–2c eingeführt und eine elektrisch leitende Ausgleichsflüssigkeit wird in die Ausnehmungen 2a und 2b sowie in die Hülse 4 eingebracht. Diese Ausgleichsflüssigkeit läßt man dann etwa 1–10 Minuten, insbesondere 3–5 Minuten einwirken, wobei während der Einwirkzeit ggf. Ausgleichsflüssigkeit insbesondere in die Hülse 4 nachgefüllt werden muß.The operation of the device 1 is now as follows: After the form 2 manufactured in a known manner as a positive model of the bridge prosthesis to be produced from a corresponding porous material and the recesses 2a - 2c were formed, the electrodes are 3a - 3c in the recesses 2a - 2c introduced and an electrically conductive compensating fluid is in the recesses 2a and 2 B as well as in the sleeve 4 brought in. This leveling liquid is allowed to act for about 1-10 minutes, in particular 3-5 minutes, during the exposure time, if necessary, compensation fluid in particular in the sleeve 4 must be refilled.

Um das Einsetzen der Form 2 in die Vorrichtung 1 zu erleichtern, wurde vorher die weitere Elektrode 5 gelöst und von der übrigen Vorrichtung 1 getrennt oder zumindest soweit nach unten verschoben, dass ein Bügel 5'' der weiteren Elektrode 5 ein Einsetzen der Form 2 in die Vorrichtung 1 nicht behindert. Nach dem Einsetzen der Form 2 wird dann die weitere Elektrode 5 wie aus 2 ersichtlich lagepositioniert, so dass sie unter dem Bereich Z' der Form 2, also desjenigen Bereichs, in dem ein Brückenzwischenglied ausgebildet werden soll, positioniert ist.To the insertion of the form 2 into the device 1 To facilitate, before the further electrode 5 solved and from the rest of the device 1 separated or at least so far moved down that a hanger 5 '' the further electrode 5 an insertion of the mold 2 into the device 1 not disabled. After inserting the mold 2 then becomes the further electrode 5 like out 2 positionally positioned so that they are below the area Z 'of the mold 2 , So that of the area in which a bridge link is to be formed, is positioned.

Die Vorrichtung 1 wird nun zusammen mit der in ihr gehaltenen Form 2 in eine Gegenelektrode 10 eingebracht, welche eine Suspensionskammer 11 aufweist, in der eine Suspension S eingefüllt ist, die die abzuscheidenden Partikel enthält.The device 1 now becomes together with the form held in it 2 in a counter electrode 10 introduced, which is a suspension chamber 11 in which a suspension S is filled, which contains the particles to be deposited.

Dann wird an die Elektroden 3a–3c und 5 und an die Gegenelektrode 10 eine Gleichspannung angelegt. Dies bewirkt, dass im Bereich der Elektroden 3a–3c, welche durch das Material der porösen Form 2 von der Gegenelektrode 10 getrennt sind, eine Membran-Abscheidung der in der Suspension S befindlichen Partikel stattfindet, während im Bereich der weiteren Elektrode 5 ein unmittelbarer Niederschlag der Partikel an der Elektrode 5 stattfindet.Then it's going to the electrodes 3a - 3c and 5 and to the counter electrode 10 a DC voltage applied. This causes in the area of the electrodes 3a - 3c caused by the material of the porous form 2 from the counter electrode 10 are separated, a membrane deposition of the particles located in the suspension S takes place, while in the region of the further electrode 5 an immediate precipitation of the particles on the electrode 5 takes place.

Durch diese Kombination der durch die Elektroden 3a–3c bewirkten Membran-Abscheidung und der durch die weitere Elektrode 5 bewirkten Direkt-Abscheidung ist es somit in vorteilhafter Art und Weise möglich, einen Grünkörper auszubilden, der zwei durch Membran-Abscheidung gewonnene Kappen für die Zahnstümpfe Z1 und Z2 sowie ein im wesentlichen durch eine direkte Abscheidung gewonnenes Brückenzwischenglied zwischen den beiden Kappen für die Zahnstümpfe Z1 und Z2 aufweist. Es ist somit mit der beschriebenen Vorrichtung 1 in vorteilhafter Art und Weise möglich, auch eine Brückenprothetik durch eine Membran-Abscheidung, unterstützt von einer Direkt-Abscheidung im Bereich Z' der weiteren Elektrode 5, herzustellen.Through this combination of the through the electrodes 3a - 3c caused membrane deposition and by the other electrode 5 It is thus advantageously possible to form a green body, the two caps obtained by membrane deposition for the tooth stubs Z1 and Z2, and a bridge intermediate between the two caps for the tooth stubs Z1, obtained essentially by direct deposition and Z2. It is thus with the described device 1 in an advantageous manner, also a bridge prosthesis by a membrane deposition, supported by a direct deposition in the region Z 'of the further electrode 5 to manufacture.

Der abgeschiedene Grünkörper wird dann zwischen 10 und 60 Minuten auf der porösen Form 2 getrocknet. Dies kann entweder an Luft oder unter kontrollierter Atmosphäre geschehen. Anschließend wird der Grünkörper entformt und weiter, entweder unter Luft oder unter kontrollierter Atmosphäre, getrocknet. Dabei wird die weitere Elektrode 5 vom Grünkörper entfernt. Die Sinterung des Grünkörpers erfolgt also ohne die weitere Elektrode 5 und die poröse Form 2.The deposited green body then becomes on the porous form between 10 and 60 minutes 2 dried. This can be done either in air or under controlled atmosphere. Subsequently, the green body is removed from the mold and further dried, either under air or under controlled atmosphere. In the process, the further electrode becomes 5 removed from the green body. The sintering of the green body thus takes place without the further electrode 5 and the porous form 2 ,

In 5 ist nun ein zweites Ausführungsbeispiel einer Vorrichtung dargestellt, welches zur Herstellung einer mehrgliedrigen Brücke dient. Die Vorrichtung 1' des zweiten Ausführungsbeispiels besteht im wesentlichen aus einer Hintereinanderanordnung von drei Vorrichtungen 1 des ersten Ausführungsbeispiels, so dass diese Vorrichtung 1' nicht mehr näher beschrieben werden muß.In 5 Now, a second embodiment of a device is shown, which serves to produce a multi-unit bridge. The device 1' of the second embodiment consists essentially of a series arrangement of three devices 1 of the first embodiment, so that this device 1' no longer needs to be described in more detail.

In den 6 und 7 ist nun ein drittes Ausführungsbeispiel einer Vorrichtung 1' zur elektrophoretischen Abscheidung eines Grünkörpers dargestellt, welche zwei den Elektroden 3a und 3b entsprechenden Elektroden 3a'' und 3b'' aufweist. Die der Elektrode 5 entsprechende weitere Elektrode 5'' weist einen Rundstab 5a auf, der in eine Ausnehmung 2d der Form 2 – wie aus 7 ersichtlich – eingesetzt ist. Der aus elektrisch leitenden Material gefertigte Rundstab 5a weist eine Bohrung auf, in die eine Gewindestange 5b'' einbringbar ist, die durch die Ausnehmung 2c der Form 2 geführt wird.In the 6 and 7 is now a third embodiment of a device 1' for the electrophoretic deposition of a green body, which two are the electrodes 3a and 3b corresponding electrodes 3a '' and 3b '' having. The electrode 5 corresponding further electrode 5 '' has a round bar 5a on, in a recess 2d the form 2 - like out 7 apparent - is used. The round rod made of electrically conductive material 5a has a hole in which a threaded rod 5b '' can be introduced through the recess 2c the form 2 to be led.

Eine derartige Konstruktion besitzt den Vorteil, dass die weitere Elektrode 5'' besonders leicht in der Form 2 befestigt werden kann, indem der Rundstab 5a in die Ausnehmung 2d der Form 2 eingesetzt und dann mittels der Gewindestange 5b und einer mit ihr zusammenwirkenden Kontermutter 5c an der Form 2 befestigt wird.Such a construction has the advantage that the further electrode 5 '' especially light in shape 2 can be fastened by the round rod 5a into the recess 2d the form 2 inserted and then by means of the threaded rod 5b and a cooperating counter nut 5c at the shape 2 is attached.

Wie aus den 6 und 7 ersichtlich ist, kann am Rundstab 5a der zweiten Elektrode 5'' noch ein oder zwei Abscheideflächen 12a, 12b angeordnet sein, welche den durch den Rundstab 5a bewirkten Abscheideeffekt verstärken.Like from the 6 and 7 can be seen on the round rod 5a the second electrode 5 '' one or two separation surfaces 12a . 12b be arranged, which by the round rod 5a reinforce the effect of separation.

Bei der Durchführung des Verfahrens hat es sich als vorteilhaft herausgestellt, vorzusehen, dass die poröse Form 2 an entsprechenden Stellen mit einem eine Direkt-Abscheidung reduzierenden oder verhindernden Mittel, z. B. mit Wachs, abgedeckt wird. Dies besitzt dann den Effekt, dass in den an die vorgenannten Abdeckungen angrenzenden Flächen eine verstärke Direkt-Abscheidung stattfindet.In carrying out the method, it has been found advantageous to provide that the porous shape 2 at appropriate locations with a direct deposition reducing or preventing agent, e.g. B. with wax, is covered. This then has the effect of increasing direct deposition in the areas adjacent the aforementioned covers.

Claims

Apparatus for producing a green body, in particular for dental applications, from which a shaped body can be produced by means of sintering, wherein the green body is formed by electrophoretic deposition of particles from a suspension (S) onto a porous mold ( 2 ), the device ( 1 ; 1' ) at least one electrode ( 3a - 3c ), which in a recess ( 2a - 2c ) the form ( 2 ), characterized in that the device ( 1 ) at least one further electrode ( 5 ; 5 '' ), by which a direct deposition of the particles of the suspension (S) on the at least one further electrode ( 5 ; 5 '' ) he follows.

Device according to claim 1, characterized in that at least one electrode ( 3a - 3c ) is wire, ironing or sleeve-shaped.

Device according to claim 1 or 2, characterized in that at least one electrode ( 3c ) a sleeve ( 4 ), in whose interior ( 4 ' ) A compensation liquid can be introduced.

Device according to one of the preceding claims, characterized in that at least one further electrode ( 5 ) is formed bow-shaped.

Apparatus according to claim 4, characterized in that at least one further electrode ( 5 '' ) a round rod ( 5a ), which in a correspondingly shaped recess ( 2d ) of the porous form ( 2 ) can be used.

Apparatus according to claim 5, characterized in that the round rod ( 5a ) of the further electrode ( 5 '' ) in the porous form ( 2 ) is lockable.

Device according to one of the preceding claims, characterized in that the further electrode ( 5 ; 5 '' ) detachable in the device ( 1 ) is arranged.

Device according to one of the preceding claims, characterized in that at the further electrode ( 5 '' ) at least one separation surface ( 12a . 12b ) is arranged.

A process for producing a green body, in particular for dental applications, from which a shaped body can be produced by sintering, wherein the green body is formed by electrophoretic depositions of particles from a suspension (S) by the particles on a in the suspension (S) arranged porous Shape ( 2 ) are deposited, whose shape is correlated with the shape of the green body to be produced and the at least one filled with electrically conductive compensating liquid recess ( 2a - 2c ), in each of which an electrode ( 3a - 3c ) for the electrophoretic deposition of the particles of the suspension (S) on the porous form ( 2 ), characterized in that the production of a portion of the green body by a direct deposition of the particles on one outside the porous mold ( 2 ) arranged further electrode ( 5 ; 5 '' ) he follows.

Method according to claim 9, characterized in that the further electrode ( 5 ' ) spaced from the surface of the porous mold ( 2 ) is arranged.

Method according to claim 9, characterized in that the further electrode ( 5 '' ) in a recess receiving it only partially ( 2d ) of the porous form ( 2 ) is arranged.

Method according to one of the preceding claims, characterized in that the electrophoretically deposited green body on the porous mold ( 2 ) is dried or dried.

A method according to claim 12, characterized in that after or during drying, the further electrode ( 5 ; 5 '' ) is removed from the green body.

Method according to one of the preceding claims, characterized in that the electrophoretically deposited green body before sintering of the porous form ( 2 ) is removed.

Method according to one of the preceding claims, characterized in that the porous mold ( 2 ) is covered locally with a direct deposition preventing or at least reducing agent.