DE102004038558A1 - Flexible tubing for hot and cold liquids and other media, e.g. in heating and sanitary systems, has an innermost layer of high-density polyethylene and an adjacent layer of low-density polyethylene - Google Patents

Flexible tubing for hot and cold liquids and other media, e.g. in heating and sanitary systems, has an innermost layer of high-density polyethylene and an adjacent layer of low-density polyethylene Download PDF

Info

Publication number
DE102004038558A1
DE102004038558A1 DE102004038558A DE102004038558A DE102004038558A1 DE 102004038558 A1 DE102004038558 A1 DE 102004038558A1 DE 102004038558 A DE102004038558 A DE 102004038558A DE 102004038558 A DE102004038558 A DE 102004038558A DE 102004038558 A1 DE102004038558 A1 DE 102004038558A1
Authority
DE
Germany
Prior art keywords
flexible hose
layer
layers
hose according
polyethylene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE102004038558A
Other languages
German (de)
Inventor
Juergen Hoeppner
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to DE102004038558A priority Critical patent/DE102004038558A1/en
Publication of DE102004038558A1 publication Critical patent/DE102004038558A1/en
Withdrawn legal-status Critical Current

Abstract

Flexible co-extruded polyethylene tubing for hot and cold liquids and other media, in which the innermost layer is based on high-density polyethylene and the adjacent layer is based on low-density polyethylene. Flexible tubing (1) with at least two layers for pipes for hot and cold media such as liquids, suspensions or aerosols, in which (a) the individual layers are formed by extruding polyethylene-based compound(s), (b) the compound (I) for the innermost layer (3) has an average density of 0.920-0.960 (preferably 0.925-0.948) g/cm3> and a melt flow index of 0.3-4 (preferably 0.3-2) g/10 min and (c) the compound (II) for the layer (2) next to layer (3) has an average density of 0.800-0.915 (preferably 0.860-0.910) g/cm3> and a melt flow index of 0.3-4 (preferably 0.3-2) g/10 min.

Description

Die Erfindung betrifft einen flexiblen Schlauch für Verbindungsschläuche zum Transport von heißen und kalten Medien wie Flüssigkeiten, Suspensionen oder Aerosolen aus mindestens zwei Schichten.The The invention relates to a flexible hose for connecting hoses for Transport of hot and cold media such as liquids, suspensions or aerosols of at least two layers.

Bekannte Schläuche der eingangs genannten Art werden aus einem Polymermaterial, insbesondere Polyethylenverbindungen hergestellt und bestehen aus einer oder mehreren funktionalen Schichten, wobei die jeweils zur Herstellung der einzelnen Schichten verwendeten Polymermaterialien, die in Extrusions- oder Coextrusionsanlagen zu Schläuchen und Rohren verarbeitet werden, annähernd die gleiche Dichte aufweisen. Zur Verwendung zum Transport von heißen Fluiden, insbesondere zur Verwendung als Heizrohre und als Verbindungsschläuche im Heizungs- und Sanitärbereich müssen diese Schläuche hohe Anforderungen an die Wärme-, Chemikalien und Alterungsbeständigkeit erfüllen.Known hoses of the type mentioned are made of a polymer material, in particular Polyethylene compounds produced and consist of one or several functional layers, each being for manufacturing the individual layers of polymer materials used in extrusion or co-extrusion equipment to hoses and pipes are processed, have approximately the same density. For use in transporting hot fluids, especially for use as heating pipes and as connecting hoses in the heating and sanitary area have to do this hoses high demands on the heat, Chemicals and aging resistance fulfill.

Ein Nachteil der bekannten Schläuche besteht darin, daß aufgrund der hohen Anforderungen an die Beständigkeit in der Regel bei der Verwendung von Polyethylenen nur solche mit hoher Dichte, nämlich mit einer Dichte von 0,920-0,960 g/cm3, zur Herstellung der Schläuche eingesetzt werden können. Diese verleihen den unter Verwendung dieser Polymere hergestellten Schläuchen jedoch eine nur sehr geringe Flexibilität. Insbesondere Schläuche aus Polyethylenverbindungen weisen eine hohe Steifigkeit aufgrund der hohen Dichte des verwendeten Polyethylenmaterials auf.A disadvantage of the known hoses is that due to the high demands on the resistance in the rule when using polyethylenes only those with high density, namely with a density of 0.920-0.960 g / cm 3 , can be used for the production of the hoses , However, these impart only very little flexibility to the hoses made using these polymers. In particular, hoses made of polyethylene compounds have a high rigidity due to the high density of the polyethylene material used.

Zur Erhöhung der Flexibilität derartiger Schläuche ist bereits in der EP 1 415 802 offenbart, niedrigdichte Polyethylenverbindungen, nämlich Polyethylenverbindungen mit einer Dichte von 0,800-0,915 g/cm3, zur Herstellung der Schläuche zu verwenden. Derart hergestellte Schläuche weisen im Gegensatz zu den bislang bekannten, unter Verwendung der hochdichten Polyethylenverbindungen hergestellten Schläuchen eine höhere Flexibilität und verbesserte Elastizität auf, wobei jedoch nicht in jedem Fall die mechanische, thermische und chemische Stabilität erreicht wird, die die unter Verwendung von Polymeren hoher Dichte hergestellten Schläuche aufweisen. Folglich können die unter Verwen dung niedrigdichter Polyethylenverbindungen hergestellten Schläuche nur bedingt im Heißwasser- und Chemikalienbereich eingesetzt werden.To increase the flexibility of such hoses is already in the EP 1 415 802 discloses to use low density polyethylene compounds, namely polyethylene compounds having a density of 0.800-0.915 g / cm 3 , for the manufacture of the hoses. Hoses produced in this way, in contrast to hitherto known hoses produced using the high-density polyethylene compounds, have higher flexibility and improved elasticity, but do not always achieve the mechanical, thermal and chemical stability inherent in using high density polymers have produced hoses. Consequently, the hoses produced using low-density polyethylene compounds can only be used to a limited extent in hot water and chemicals.

Der Erfindung liegt daher die Aufgabe zugrunde, unter Beibehaltung der aus der Verwendung hochdichter Polyethylenverbindungen resultierenden Wärme-, Chemikalien- und Alterungsbeständigkeit ein flexibles Rohr, bzw. eine Schlauchleitung zu schaffen, welche eine nur geringe Biegesteifigkeit und Knickneigung zeigt.Of the Invention is therefore based on the object, while maintaining the resulting from the use of high density polyethylene compounds heat, chemical and aging resistance flexible tube, or to create a hose, which is a shows only low bending stiffness and bending tendency.

Die Erfindung löst die Aufgabe durch einen flexiblen Schlauch mit den Merkmalen des Anspruchs 1. Vorteilhafte Weiterbildungen der Erfindung sind in den Unteransprüchen angegeben.The Invention solves the task through a flexible hose with the characteristics of Claim 1. Advantageous developments of the invention are in the dependent claims specified.

Wesentlich für die Erfindung ist, dass der Schlauch aus mindestens zwei Schichten besteht, wobei ein Polymer auf Polyethylenbasis zur Herstellung einer innersten Schicht eine höhere Dichte aufweist als ein Polymer auf Polyethylenbasis zur Herstellung einer an die innerste Schicht angrenzenden Schicht. Unter der innersten Schicht wird dabei im Rahmen der Anmeldung die Schicht des Schlauchs verstanden, die in Kontakt mit dem zu führenden Medium steht.Essential for the Invention is that the tube consists of at least two layers, wherein a polyethylene-based polymer for producing an innermost one Layer a higher one Has density as a polyethylene-based polymer for production a layer adjacent to the innermost layer. Under the innermost Layer is understood in the context of the application, the layer of the tube, which in contact with the leading Medium stands.

In Abhängigkeit von dem Einsatzzweck des erfindungsgemäßen Schlauchs kann dieser auch eine oder mehrere weitere Schichten aufweisen, die wiederum an die an die innerste Schicht angrenzende Schicht angrenzen. Im Falle der Verwendung eines Polymers auf Polyethylenbasis zur Herstellung der weiteren Schichten, kann dessen Dichte höher, niedriger oder gleich der Dichte des für die darunter liegende Schicht verwendeten Materials sein.In dependence of the purpose of the hose according to the invention this can also be a or more layers, which in turn to the the innermost layer adjacent to adjacent layer. In case of Use of a polyethylene-based polymer for the production of further layers, its density can be higher, lower or equal the density of for the underlying layer used material.

Erfindungsgemäß weist die Verbindung zur Bildung der innersten Schicht eine Dichte von 0,92-0,96 g/cm3 und einen Schmelzindex von 0,3-4 g/10 min, vorzugsweise eine mittlere Dichte von 0,925-0,946 g/cm3 und einen Schmelzindex von 0,3-2 g/10 min auf. Demgegenüber weist die an die innerste Schicht angrenzende Schicht erfindungsgemäß eine mittlere Dichte von 0,8-0,915 g/cm3 und einen Schmelzindex von 0,3-4 g/min, vorzugsweise eine mittlere Dichte von 0,860-0,910 g/cm3 und einen Schmelzindex von 0,3-2 g/10 min auf.According to the invention, the composition for forming the innermost layer has a density of 0.92-0.96 g / cm 3 and a melt index of 0.3-4 g / 10 min, preferably an average density of 0.925-0.946 g / cm 3 and a melt index of 0.3-2 g / 10 min. In contrast, the layer adjacent to the innermost layer according to the invention has an average density of 0.8-0.915 g / cm 3 and a melt index of 0.3-4 g / min, preferably a mean density of 0.860-0.910 g / cm 3 and a Melt index of 0.3-2 g / 10 min.

Diese und die im folgenden aufgeführten Dichtangaben beziehen sich auf Messungen nach ISO 1183. Die Angaben zum Schmelzindex beziehen sich auf Messungen nach ISO 113, 190°/2,16 kg.These and the following seal specifications refer to measurements according to ISO 1183. The melt index refer to measurements according to ISO 113, 190 ° / 2.16 kg.

Infolge der erfindungsgemäßen Ausgestaltung erfüllen die einzelnen Schichten unterschiedliche Anforderungen an den herzustellenden Schlauch. Die aus einem hochdichten Material bestehende innerste Schicht bewirkt die vorteilhaften Eigenschaften des Schlauchs hinsichtlich der Spannungs-, Temperatur-, Chemikalien- und Alterungsbeständigkeit. Die an die innerste Schicht angrenzende Schicht, welche aus einer weicheren, niedrigdichten Polyethylenverbindung gebildet ist, beeinflußt die Knickneigung und Flexibilität positiv.As a result of the embodiment according to the invention, the individual layers meet different requirements for the hose to be produced. The innermost layer made of a high-density material effects the advantageous properties of the hose in terms of stress, temperature, chemical and aging resistance. The layer adjacent to the innermost layer, which is formed of a softer, low density polyethylene compound, affects the Kinkiness and flexibility positive.

Der erfindungsgemäße Schlauch erfüllt somit sowohl die geforderten Anforderungen an die Wärme-, Chemikalien- und Alterungsbeständigkeit und weist zudem eine hohe Flexibilität auf, so dass sich der erfindungsgemäße Schlauch vielfältig verwenden läßt. Die gewählten Polyethylenverbindungen lassen sich zudem mit konventionellen Verfahren, bspw. in einem Extrusionsprozeß, in besonders einfacher Weise zu Rohren und Schläuchen verarbeiten, so daß eine besonders einfache und kostengünstige Herstellung der Schläuche möglich ist.Of the hose according to the invention Fulfills Thus, both the required requirements for the thermal, chemical and aging resistance and also has a high flexibility on, so that the hose according to the invention use manifold leaves. The selected Polyethylene compounds can also be prepared by conventional methods for example in an extrusion process, process in a particularly simple manner to pipes and hoses, so that a particularly simple and inexpensive Production of the hoses possible is.

Nach einer besonders vorteilhaften Weiterbildung der Erfindung handelt es sich bei den für die innerste Schicht des Schlauchs eingesetzten Polyethylenverbindungen um Ethylen/Okten-1 Copolymere, die aufgrund der Seitenkettenlängen die Alterungsstabilität und die mechanischen Eigenschaften in besonders positiver Weise beeinflussen.To a particularly advantageous embodiment of the invention it is at the for the innermost layer of the tube used polyethylene compounds ethylene / octene-1 copolymers, which due to the side chain lengths the aging stability and the mechanical properties in a particularly positive way influence.

Nach einer besonderen Ausgestaltung der Erfindung weist die innerste Schicht dabei eine mittlere Wandstärke von 1-75% der gesamten Wandstärke, vorzugsweise eine mittlere Wandstärke von 10-50% der Gesamtwandstärke des zwei- oder mehrlagig aufgebauten Schlauchs auf. Der gemäß dieser Weiterbildung hergestellte Schlauch weist eine optimale Abstimmung zwischen den mechanischen Eigenschaften wie Flexibilität, Elastizität und Reißfestigkeit einerseits und der Temperatur-, Chemie- und Alterungsbeständigkeit andererseits auf.To a particular embodiment of the invention, the innermost Layer thereby an average wall thickness of 1-75% of the total Wall thickness, preferably an average wall thickness of 10-50% of the total wall thickness of the two- or multi-layered hose on. The according to this Continuing manufactured hose exhibits optimal tuning between mechanical properties such as flexibility, elasticity and tear resistance on the one hand and the temperature, chemical and aging resistance on the other hand.

Besonders vorteilhafterweise weist die innerste Schicht eine mittlere Wandstärke von 0,1-5 mm, vorzugsweise eine mittlere Wandstärke von 0,3-1,8 mm auf. Derartige Wandstärken erweisen sich als besonders vorteilhaft bei der Verarbeitung der eingesetzten Polyethylenverbindungen und tragen zudem erheblich zur mechanischen und thermischen Stabilität der Schläuche bei.Especially Advantageously, the innermost layer has an average wall thickness of 0.1-5 mm, preferably an average wall thickness of 0.3-1.8 mm. such wall thickness prove to be particularly advantageous in the processing of used polyethylene compounds and also contribute significantly for the mechanical and thermal stability of the hoses.

Gemäß einer weiteren vorteilhaften Ausgestaltung der Erfindung sind bei der Verwendung mehrerer Verbindungen auf Polyethylenbasis diese untereinander homogen mischbar. Gemäß dieser Weiterbildung der Erfindung lassen sich die Schichten optimal aneinander anpassen. Zudem werden die Variationsmöglichkeiten hinsichtlich der mechanischen Eigenschaften der Schläuche einerseits und der Beständigkeit andererseits gesteigert.According to one Another advantageous embodiment of the invention are in the Use of several compounds based on polyethylene with each other homogeneously miscible. According to this Development of the invention, the layers can optimally together to adjust. In addition, the variations in terms of the mechanical properties of the hoses on the one hand and the durability on the other hand increased.

Nach einer weiteren vorteilhaften Ausgestaltung der Erfindung handelt es sich bei den Verbindungen um eine einzige oder eine Mischung aus Verbindungen auf Polyethylenbasis, welche jeweils unter Verwendung von Ziegler-Natta, Metallocen- oder Constrained-Geometric-catalyst (CGC) single side Katalysatoren hergestellt sind. Die Hinzunahme einer bestimmten Menge an Ziegler-Natta katalysierten Polyethylenverbindungen zu aus anderen Katalyseverfahren gewonnenen Polyethylenverbindungen steigert die positiven Eigenschaften des erfindungsgemäßen Schlauchs in ergänzender Weise. Die verwendbaren Ziegler-Natta katalysierten Verbindungen weisen eine hohe Temperaturbeständigkeit und Festigkeit auf. Bei einer ggf. anschließend durchgeführten Co-Vernetzung bleibt die lamellare festigkeitssteigernde Kristallitstruktur der Ziegler-Natta katalysierten Verbindungen erhalten.To a further advantageous embodiment of the invention the compounds are a single or a mixture polyethylene-based compounds, each using from Ziegler-Natta, metallocene or constrained geometric catalyst (CGC) single side catalysts are made. The addition of a certain amount of Ziegler-Natta catalyzed polyethylene compounds from other catalytic processes obtained polyethylene compounds increases the positive properties of the hose according to the invention in supplementary Wise. The useful Ziegler-Natta catalyzed compounds exhibit a high temperature resistance and strength on. In case of subsequent co-networking remains the lamellar strength-enhancing crystallite structure of Ziegler-Natta catalyzed compounds.

Nach einer besonders vorteilhaften Ausgestaltung der Erfindung sind eine oder mehrere der Schichten mit einem Vernetzungsgrad von 45-75% an jeder Stelle der Schicht vernetzt. Durch diese Vernetzung wird die Temperatur- und Druckbeständigkeit in ergänzender Weise verbessert, wobei gleichzeitig die notwendige Flexibilität erhalten bleibt. Durch diese Weiterbildung der Erfindung wird das Einsatzspektrum des erfindungsgemäßen Schlauchs in ergänzender Weise erhöht.To A particularly advantageous embodiment of the invention are a or more of the layers having a degree of crosslinking of 45-75% networked every part of the shift. Through this networking, the Temperature and pressure resistance in supplementary Improved manner, while maintaining the necessary flexibility remains. By this development of the invention is the range of applications of the hose according to the invention in supplementary Way increased.

Die Vernetzung kann grundsätzlich mit verschiedenen, dem Fachmann geläufigen Verfah ren, wie beispielsweise durch das Vernetzen mit Silanen oder peroxydische Vernetzen durchgeführt werden. Nach einer weiteren Ausgestaltung der Erfindung ist die Vernetzung der Schichten durch Bestrahlung mit Elektronen hergestellt.The Networking can basically with various, familiar to those skilled procedural ren, such as by crosslinking with silanes or peroxidic crosslinking. To A further embodiment of the invention is the networking of Layers produced by irradiation with electrons.

Die Vernetzung mittels Elektronenstrahlungen stellt ein kostengünstiges und schnelles Vernetzungsverfahren dar. Ferner weist es den Vorteil auf, dass im Gegensatz zum chemischen Vernetzen auf potentiell gesundheitsschädliche Additive verzichtet werden kann, die sich beim Vernetzen in der/den Schicht/en des Schlauches einlagern und im Gebrauch als Trinkwasserschlauch mit dem Trinkwasser herausgespült und beim Verzehr durch den menschlichen Körper aufgenommen werden können.The Networking by means of electron beams represents a cost-effective and fast crosslinking process. Furthermore, it has the advantage on that, unlike chemical crosslinking on potentially harmful additives can be omitted, the crosslinking in the / the layer / s of the hose and in use as a drinking water hose flushed out with the drinking water and can be absorbed by the human body when ingested.

Der grundsätzlich zwei- oder mehrschichtige Aufbau des erfindungsgemäßen Schlauchs ermöglicht die Anpassung der Schläuche an verschiedenen Einsatzbereiche, bei denen eine oder mehrere zusätzliche Schichten besondere Eigenschaften aufweisen können, die den Einsatz des erfindungsgemäßen Schlauchs unter den jeweiligen Anforderungen ermöglichen.Of the in principle two- or multi-layered construction of the hose according to the invention allows the adaptation of the hoses in various applications where one or more additional Layers may have special properties, the use of the hose according to the invention under the respective requirements.

Eine weitere Schicht kann ferner auch als Dekorschicht ausgeführt werden, die dem erfindungsgemäßen Schlauch beispielsweise ein besonderes Aussehen und/oder eine besondere Oberflächenstruktur verleiht. Nach einer besonders vorteilhaften Ausgestaltung der Erfindung sind eine oder mehrere der Schichten farbig und/oder transparent ausgestaltet.A further layer can also be carried out as a decorative layer, the hose of the invention For example, a special appearance and / or a special surface structure gives. According to a particularly advantageous embodiment of the invention one or more of the layers are colored and / or transparent.

Eine farbige Ausgestaltung kann dabei einerseits zur Verbesserung des äußeren Erscheinungsbilds beitragen und andererseits als Abschirmung vor schädlichem UV-Licht dienen. Die farbliche Gestaltung kann dabei durch Beimischung von farbgebenden und/oder UV-Licht reflektierenden oder -absorbierenden Zusätzen in die Verbindung zur Herstellung der jeweiligen Schicht erfolgen.A Colored design can on the one hand to improve the external appearance on the other hand as a shield against harmful ones Serve UV light. The color scheme can by admixing of coloring and / or UV light reflective or absorbing additives in the compound to Production of the respective layer done.

Bei der transparenten Ausgestaltung weisen die Kristallite des für diese Schicht eingesetzten Werkstoffs auf Polyethylenbasis eine Größe auf, welche kleiner ist als die halbe Wellenlänge des sichtbaren Lichtspektrums.at the transparent design, the crystallites of the for this One layer of polyethylene-based material used, which is less than half the wavelength of the visible light spectrum.

Nach einer weiteren Ausgestaltung der Erfindung kann eine oder mehrere der Schichten auch aus einer metallisierten und/oder farbig bedruckten Kunststoffolie bestehen. Die Verwendbarkeit derartiger Kunststoffolien steigert die Gestaltungsmöglichkeiten des Schlauchs, wobei der Einsatz von Folien besonders kostengünstig möglich ist.To Another embodiment of the invention may include one or more the layers also from a metallized and / or color printed plastic film consist. The usability of such plastic films increases the design options the hose, the use of films is particularly cost-effective.

Die oben charakterisierten Materialien auf Polyethylenbasis zur Herstellung eines flexiblen Schlauches können grundsätzlich innerhalb der erfindungsgemäßen Parameter so gewählt werden, dass eine ausreichende Temperatur- und Druckbeständigkeit des erfindungsgemäß hergestellten Schlauchs vorliegt.The polyethylene-based materials characterized above for production a flexible hose can in principle within the parameters according to the invention so chosen be that sufficient temperature and pressure resistance of the invention produced Hose is present.

Falls jedoch eine Steigerung der Temperatur- und Druckbeständigkeit des erfindungsgemäßen Schlauchs für den Einsatz unter erhöhten Temperatur- und Druckeinflüssen erforderlich ist, können hierfür geeignete Maßnahmen getroffen werden. So kann nach einer besonders vorteilhaften Weiterbildung der Erfindung eine oder mehrere der Schichten als Armierung ausgebildet sein, die vorzugsweise aus Fasern und/oder Fasergewebe aus synthetischen und/oder metallischem Material gebildet ist. Die Verbindung der Armierung mit der darüber und/oder darunter liegenden Schicht kann dabei beliebig, beispielsweise durch formschlüssiges und/kraftschlüssiges Verbinden erfolgen.If but an increase in temperature and pressure resistance of the hose according to the invention for the Use under elevated Temperature and pressure influences is required therefor appropriate measures to be hit. Thus, according to a particularly advantageous development of the invention, one or more of the layers formed as a reinforcement preferably made of fibers and / or synthetic fiber and / or metallic material is formed. The connection of Reinforcement with the above and / or underlying layer can be arbitrary, for example, by positive and / non-positive connection respectively.

Nach einer weiteren Ausgestaltung der Erfindung ist eine oder mehrere der Schichten eine Diffusionssperrschicht, insbesondere eine Sauerstoffdiffusionssperrschicht, die vorzugsweise aus einer Ethylenvinylalkohol-Copolymer-Verbindung gebildet ist, welche den Austausch von Stoffen zwischen dem im Schlauch geförderten Medium und der Umgebung bzw. umgekehrt verhindert. Nach einer besonderen Ausgestaltung der Erfindung weist die Ethylenvinylalkohol-Copolymer-Verbindung dabei einen Ethylenanteil von 35-45 Mol%, vorzugsweise 41 Mol% auf.To Another embodiment of the invention is one or more the layers have a diffusion barrier layer, in particular an oxygen diffusion barrier layer, preferably made of an ethylene-vinyl alcohol copolymer compound is formed, which is the exchange of substances between the in the hose funded Medium and the environment or vice versa prevented. After a special design The invention features the ethylene vinyl alcohol copolymer compound while an ethylene content of 35-45 mol%, preferably 41 mol%.

Nach einer besonders vorteilhaften Ausgestaltung der Erfindung ist eine oder mehrere der Schichten eine Haftvermittlerschicht, die vorzugsweise aus einer funktionalisierten Poythylenverbindung, insbesondere einer mit Maleinsäureanhydrid gepfropften funktionalisierten Polyethylenverbindung gebildet ist.To a particularly advantageous embodiment of the invention is a or more of the layers, a primer layer, preferably from a functionalized Poythylenverbindung, in particular a with maleic anhydride grafted functionalized polyethylene compound is formed.

Nachstehend wird ein Ausführungsbeispiel der Erfindung anhand einer Zeichnung erläu tert. In der Zeichnung zeigt:below is an embodiment of Invention erläu reference to a drawing. In the drawing shows:

1 Eine Schnittansicht eines zweischichtigen Schlauches. 1 A sectional view of a two-layer hose.

Ein in 1 dargestellter flexibler Schlauch 1 weist eine innerste Schicht 3, die in Kontakt mit dem zu transportierenden Medium steht, und eine an die innerste Schicht 3 angrenzende Schicht 2 auf, wobei eine Verbindung auf Polyethylenbasis zur Herstellung der innersten Schicht 3 eine hohe Dichte aufweist. Eine Verbindung auf Polyethylenbasis zur Herstellung der an die innerste Schicht 3 angrenzenden Schicht 2 weist eine niedrige Dichte auf.An in 1 illustrated flexible hose 1 has an innermost layer 3 which is in contact with the medium to be transported, and one to the innermost layer 3 adjacent layer 2 on, wherein a polyethylene-based compound for producing the innermost layer 3 has a high density. A polyethylene-based compound for making the innermost layer 3 adjacent layer 2 has a low density.

Bei dem in 1 darstellten Ausführungsbeispiel weist die Verbindung auf Polyethylenbasis zur Herstellung der innersten Schicht 3 eine Dichte von 0,933 g/cm3 auf. Der Schmelzindex der Verbindung beträgt 0,7 g/10 min. Demgegenüber beträgt die Dichte der Verbindung auf Polyethylenbasis zur Herstellung der auf die innerste Schicht 3 aufextrudierten, angrenzenden Schicht 20,905 g/cm3 und der Schmelzindex beträgt 1/10 min. In dem hier dargestellten Ausführungsbeispiel des flexiblen Schlauchs 1 bildet die angrenzende Schicht 2 gleichzeitig die äußerste Schicht des flexiblen Schlauchs 1.At the in 1 illustrated embodiment, the polyethylene-based compound for the production of the innermost layer 3 a density of 0.933 g / cm 3 . The melt index of the compound is 0.7 g / 10 min. On the other hand, the density of the polyethylene-based compound for producing the innermost layer is 3 20.805 g / cm 3 extruded adjacent layer and the melt index is 1/10 min. In the embodiment of the flexible hose shown here 1 forms the adjacent layer 2 at the same time the outermost layer of the flexible hose 1 ,

Die mittlere Wandstärke der innersten Schicht 3 beträgt 28% der Gesamtwandstärke des flexiblen Schlauchs 1. Die Ausgestaltung des Schlauchs 1 kombiniert die Wärme-, Chemikalien- und Alterungsbeständigkeit der innersten Schicht 3 mit der Flexibilität der angrenzenden Schicht 2, so daß insgesamt ein Schlauch 1 bereitgestellt wird, der hohe mechanische, thermische und chemische Beständigkeit bei gleichzeitiger Flexibilität und Knickstabilität aufweist.The mean wall thickness of the innermost layer 3 is 28% of the total wall thickness of the flexible hose 1 , The design of the hose 1 combines the heat, chemical and aging resistance of the innermost layer 3 with the flexibility of the adjacent layer 2 so that a total of one hose 1 is provided, which has high mechanical, thermal and chemical resistance with simultaneous flexibility and buckling stability.

Gemäß einer hier nicht dargestellten Ausführungsform des Schlauches kann dieser eine oder mehrere weitere Schichten aufweisen, die auf der an die innerste Schicht 3 angrenzenden äußersten Schicht 2 angeordnet sind. Zur Herstellung der weiteren Schichten können ebenfalls Verbindungen auf Polyethylenbasis verwendet werden, wobei deren Dichte höher, geringer oder gleich der Dichte des Materials zu Herstellung der angrenzenden Schicht sein kann.According to an embodiment of the hose (not shown here), the hose may have one or more further layers which rest on the innermost layer 3 adjacent outermost layer 2 are arranged. To make the further layers, polyethylene-based compounds may also be used, the density of which may be higher, lower or equal to the density of the material for making the adjacent layer.

Ein mögliches Herstellungsverfahren des Schlauchs 1 wird im folgenden erläutert. Ein flexibler Schlauch 1 wird im Extrusionsverfahren unter Zuhilfenahme eines Extruders hergestellt. Dabei wird dem Extruder die für die innerste Schicht 3 gewählte Verbindung – meist in Form eines Granulats, bei welchem es sich um ein homogenes Granulat oder eine Mischung unterschiedlicher Granulate handeln kann – zugeführt. Die gewählte Verbindung auf Polyethylenbasis wird in eine homogene Schmelze umgewandelt. Im Extruder wird die aufgeschmolzene Verbindung einem angeflanschten Werkzeug in Form des zu extrudierenden Werkzeugs zugeführt. Das Werkzeug enthält einen Fließkanal, der vom Schmelzstrom durchflossen wird und die Schmelze in die gewünschte Schlauchform bringt. Eine erste Verbindung auf Polyethylenbasis zur Herstellung der innersten Schicht des flexiblen Schlauchs 1 weist einen Schmelzindex von 1 und eine Dichte von 0,935 g/cm3 auf.A possible manufacturing process of the hose 1 will be explained below. A flexible one tube 1 is produced in the extrusion process with the aid of an extruder. In this case, the extruder for the innermost layer 3 chosen compound - usually in the form of granules, which may be a homogeneous granules or a mixture of different granules - supplied. The selected polyethylene-based compound is converted to a homogeneous melt. In the extruder, the molten compound is fed to a flanged tool in the form of the tool to be extruded. The tool contains a flow channel through which the melt stream flows and brings the melt into the desired tube shape. A first polyethylene-based compound for making the innermost layer of the flexible hose 1 has a melt index of 1 and a density of 0.935 g / cm 3 .

In einem weiteren Verfahrensschritt wird auf die innerste Schicht 3 die angrenzende Schicht 2 extrudiert. Dabei wird dem Extruder die für die angrenzende Schicht 2 gewählte Verbindung zugeführt. Im Anschluß an die Umwandlung in eine homogene Schmelze wird die angrenzende Schicht 2 auf die innerste Schicht 3 aufextrudiert.In a further method step is applied to the innermost layer 3 the adjacent layer 2 extruded. In this case, the extruder for the adjacent layer 2 supplied selected connection. Following conversion to a homogeneous melt, the adjacent layer becomes 2 on the innermost layer 3 extruded.

Die Verbindungen auf Polyethylenbasis zur Herstellung der angrenzenden Schicht 2 weist ebenfalls einen Schmelzindex von 1 auf. Die mittlere Dichte der Verbindung beträgt 0,88 g/cm3.The polyethylene-based compounds for making the adjacent layer 2 also has a melt index of 1. The average density of the compound is 0.88 g / cm 3 .

Claims (17)

Flexibler Schlauch für Verbindungsschläuche zum Transport von heißen und kalten Medien wie Flüssigkeiten, Suspensionen oder Aerosolen bestehend aus mindestens zwei Schichten, dadurch gekennzeichnet, dass – die einzelnen Schichten durch Extrudieren einer oder mehrerer Verbindungen auf Polyethylenbasis gebildet sind, – die eine innerste Schicht (3) bildende Verbindung eine mittlere Dichte von 0,920-0,960 g/cm3 und einen Schmelzindex von 0,3-4 g/10 min., vorzugsweise eine mittlere Dichte von 0,925-0,948 g/cm3 und einen Schmelzindex von 0,3-2 g/10 min. aufweist und – die Verbindung zur Bildung einer an die innerste Schicht (3) angrenzenden Schicht (2) eine mittlere Dichte von 0,800-0,915 g/cm3 und einen Schmelzindex von 0,3-4 g/10 min., vorzugsweise eine mittlere Dichte von 0,860-0,910 g/cm3 und einen Schmelzindex von 0,3-2 g/10 min. aufweist.Flexible hose for connecting hoses for transporting hot and cold media such as liquids, suspensions or aerosols consisting of at least two layers, characterized in that - the individual layers are formed by extruding one or more polyethylene-based compounds, - the one innermost layer ( 3 ) forming compound has an average density of 0.920-0.960 g / cm 3 and a melt index of 0.3-4 g / 10 min., preferably a mean density of 0.925-0.948 g / cm 3 and a melt index of 0.3-2 g / 10 min. and - the compound for forming a to the innermost layer ( 3 ) adjacent layer ( 2 ) has an average density of 0.800-0.915 g / cm 3 and a melt index of 0.3-4 g / 10 min., preferably a mean density of 0.860-0.910 g / cm 3 and a melt index of 0.3-2 g / 10 min. having. Flexibler Schlauch nach Anspruch 1, dadurch gekennzeichnet, dass die die innerste Schicht (3) bildende Verbindung aus einem Ethylen-Okthen-1 Copolymer gebildet ist.Flexible hose according to claim 1, characterized in that the innermost layer ( 3 ) forming compound of an ethylene-octhene-1 copolymer is formed. Flexibler Schlauch nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass die innerste Schicht (3) eine mittlere Wandstärke von 1 bis 75% einer Gesamtwandstärke, vorzugsweise eine mittlere Wandstärke von 10-50% der Gesamtwandstärke des zwei oder mehrlagig aufgebauten Schlauchs (1) aufweist.Flexible hose according to claim 1 or 2, characterized in that the innermost layer ( 3 ) an average wall thickness of 1 to 75% of a total wall thickness, preferably an average wall thickness of 10-50% of the total wall thickness of the two or more layers constructed hose ( 1 ) having. Flexibler Schlauch nach einem der vorangehenden Ansprüche, dadurch gekennzeichnet, dass die innerste Schicht (3) eine mittlere Wandstärke von 0,1-5 mm, vorzugsweise eine mittlere Wandstärke von 0,3-1,8 mm aufweist.Flexible hose according to one of the preceding claims, characterized in that the innermost layer ( 3 ) has an average wall thickness of 0.1-5 mm, preferably an average wall thickness of 0.3-1.8 mm. Flexibler Schlauch nach einem der vorangehenden Ansprüche, dadurch gekennzeich net, dass bei der Verwendung mehrerer Verbindungen auf Polyethylenbasis diese untereinander homogen mischbar sind.Flexible hose according to one of the preceding claims, characterized gekennzeich net that when using multiple connections on Polyethylene base these are mutually homogeneously miscible. Flexibler Schlauch nach einem der vorangehenden Ansprüche, dadurch gekennzeichnet, dass es sich bei den Verbindungen um eine einzige oder eine Mischung aus Verbindungen auf Polyethylenbasis handelt, welche jeweils unter Verwendung von Ziegler-Natta, Metaocen- oder Constrained-Geometric-Catalyst (CGC) single-side Katalysatoren hergestellt sind.Flexible hose according to one of the preceding claims, characterized characterized in that the compounds are a single or a mixture of polyethylene-based compounds, each using Ziegler-Natta, Metaocene or Constrained Geometric Catalyst (CGC) single-side catalysts are made. Flexibler Schlauch nach einem der vorangehenden Ansprüche, dadurch gekennzeichnet, dass die Verbindung zur Herstellung der an die innerste Schicht (3) angrenzenden Schicht (2) aus einer einzigen oder einer Mischung aus Verbindungen auf Polyethylenbasis besteht, welche einen Kristallitschmelzbereich von über 90°, vorzugsweise 95-131°C aufweisen.Flexible hose according to one of the preceding claims, characterized in that the compound for the production of the to the innermost layer ( 3 ) adjacent layer ( 2 ) consists of a single or a mixture of polyethylene-based compounds, which have a crystallite melting range of over 90 °, preferably 95-131 ° C. Flexibler Schlauch nach einem der vorangehenden Ansprüche, dadurch gekennzeichnet, dass eine oder mehrere der Schichten (2, 3) mit einem Vernetzungsgrad von 45-75% an jeder Stelle der Schicht (2, 3) vernetzt sind.Flexible hose according to one of the preceding claims, characterized in that one or more of the layers ( 2 . 3 ) with a degree of crosslinking of 45-75% at each point of the layer ( 2 . 3 ) are networked. Flexibler Schlauch nach einem der vorangehenden Ansprüche, dadurch gekennzeichnet, dass die Vernetzung einer oder mehrerer der Schichten (2, 3) durch Bestrahlung mit Elektronen hergestellt ist.Flexible hose according to one of the preceding claims, characterized in that the cross-linking of one or more of the layers ( 2 . 3 ) is produced by irradiation with electrons. Flexibler Schlauch nach einem oder mehreren der vorangehenden Ansprüche, dadurch gekennzeichnet, dass eine oder mehrere der Schichten (2, 3) farbig und/oder transparent ausgestaltet sind.Flexible hose according to one or more of the preceding claims, characterized in that one or more of the layers ( 2 . 3 ) are designed colored and / or transparent. Flexibler Schlauch nach einem oder mehreren der vorangehenden Ansprüche, dadurch gekennzeichnet, dass eine oder mehrere der Schichten aus der metallisierten und/oder farbig bedruckten Kunststoffolie bestehen.Flexible hose after one or more of the previous claims, characterized in that one or more of the layers of the metallized and / or colored printed plastic film. Flexibler Schlauch nach einem der vorangehenden Ansprüche, dadurch gekennzeichnet, dass eine oder mehrere der Schichten eine Armierung ist, die vorzugsweise aus Fa sern und/oder Fasergewebe aus synthetischem und/oder metallischem Material gebildet ist.Flexible hose according to one of the preceding claims, characterized in that one or more of the layers is a reinforcement which is preferably made of fibers and / or fibrous webs of synthetic and / or metallic material. Flexibler Schlauch nach einem der vorangehenden Ansprüche, dadurch gekennzeichnet, dass die Armierung formschlüssig und/oder kraftschlüssig mit der darunter liegenden und/oder darüber liegenden Schicht verbunden ist.Flexible hose according to one of the preceding Claims, characterized in that the reinforcement form-fitting and / or non-positively with connected to the underlying and / or overlying layer is. Flexibler Schlauch nach einem oder mehreren der vorangehenden Ansprüche, dadurch gekennzeichnet, dass die Armierung weder form-, noch stoffschlüssig mit der darunter liegenden und/oder darüber liegenden Schicht verbunden ist.Flexible hose according to one or more of the preceding Claims, characterized in that the reinforcement neither form fit, nor cohesively with connected to the underlying and / or overlying layer is. Flexibler Schlauch nach einem oder mehreren der vorangehenden Ansprüche, dadurch gekennzeichnet, dass eine oder mehrere der Schichten eine Diffusionssperrschicht, insbesondere eine Sauerstoff-Diffusions-Sperrschicht ist, die vorzugsweise aus einer Ethylenvenylalkohol-Copolymer-Verbindung.Flexible hose after one or more of the previous claims, characterized in that one or more of the layers comprises a diffusion barrier layer, In particular, an oxygen diffusion barrier layer is preferably made an ethylene-vinyl alcohol copolymer compound. Flexibler Schlauch nach einem oder mehreren der vorangehenden Ansprüche, dadurch gekennzeichnet, dass die Ethylenvenylalkohol-Copolymer-Verbindung einen Ethylenanteil von 35-45 Mol%, vorzugsweise 41 Mol% aufweist.Flexible hose after one or more of the previous claims, characterized in that the ethylene-vinyl alcohol copolymer compound has an ethylene content of 35-45 mol%, preferably 41 mol%. Flexibler Schlauch nach einem der vorangehenden Ansprüche, dadurch gekennzeichnet, dass eine oder mehrere der Schichten eine Haftvermittlerschicht ist, die vorzugsweise aus einer funktionalisierten Polyethylenverbindung, insbesondere einer mit Malleinsäure anhydrit gepfropften funktionalisierten Polyethylenverbindung gebildet ist.Flexible hose according to one of the preceding Claims, characterized in that one or more of the layers has a Adhesive layer is preferably made of a functionalized Polyethylene compound, in particular anhydrite with malonic acid grafted functionalized polyethylene compound is formed.
DE102004038558A 2004-08-06 2004-08-06 Flexible tubing for hot and cold liquids and other media, e.g. in heating and sanitary systems, has an innermost layer of high-density polyethylene and an adjacent layer of low-density polyethylene Withdrawn DE102004038558A1 (en)