DE102004008018A1 - Grains to absorb household pet urine formed from glass foam wetted with water and then coated with bentonite and dried - Google Patents
Grains to absorb household pet urine formed from glass foam wetted with water and then coated with bentonite and dried Download PDFInfo
- Publication number
- DE102004008018A1 DE102004008018A1 DE102004008018A DE102004008018A DE102004008018A1 DE 102004008018 A1 DE102004008018 A1 DE 102004008018A1 DE 102004008018 A DE102004008018 A DE 102004008018A DE 102004008018 A DE102004008018 A DE 102004008018A DE 102004008018 A1 DE102004008018 A1 DE 102004008018A1
- Authority
- DE
- Germany
- Prior art keywords
- granules
- grains
- absorbent
- light
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
Die Erfindung betrifft ein Verfahren zur Herstellung eines insbesondere flüssigen Tierabfall absorbierenden Streumittels für Haustiere.The The invention relates to a process for the preparation of a particular liquid Animal waste absorbing bedding material for pets.
Ein
solches Verfahren ist beispielsweise durch die
Darüber hinaus
ist es allgemein bekannt, wasserquellfähigen Natriumbentonitton in
Verbindung mit einer Tierabfall absorbierenden Zusammensetzung einzusetzen,
wie dies im Rahmen der
Im
Rahmen der
Durch
die
Die bekannten Vorgehensweisen haben sich grundsätzlich bewährt, was die Flüssigkeitsaufnahmefähigkeit des eingesetzten Tonminerals und dessen Agglomeration angeht, um einzelne Klumpen aus einer zugehörigen Abfallbox entfernen zu können. Allerdings sind die bekannten marktfähigen Produkte relativ schwer, weil ihr Schüttgewicht im Bereich von ca. 1 kg/l liegt. Das erschwert die Handhabung und auch den Transport für den Endverbraucher. – Hier will die Erfindung insgesamt Abhilfe schaffen.The known procedures have basically proven, what the fluid absorbency of the clay mineral used and its agglomeration, to single lumps from an associated To remove waste box. However, the known marketable products are relatively heavy, because of their bulk density in the range of about 1 kg / l. This complicates the handling and also the transport for the end user. - Here The invention aims to provide a total remedy.
Der Erfindung liegt das technische Problem zugrunde, ein Verfahren zur Herstellung eines Streumittels für Haustiere anzugeben, mit dessen Hilfe ein Leichtstreu kostengünstig produziert werden kann, welches mit den gleichen positiven Eigenschaften wie die bisherigen Streumittel ausgerüstet ist.Of the Invention is the technical problem underlying a method for Production of a gritter for Indicate pets, with the help of which a light litter produced cost-effectively can be, which with the same positive characteristics as the previous scattering agent is equipped.
Zur Lösung dieser technischen Problemstellung ist Gegenstand der Erfindung ein Verfahren zur Herstellung eines insbesondere flüssigen Tierabfall absorbierenden Streumittels für Haustiere, wonach Körner eines Leichtgranulates mit einem Schüttgewicht von unter 300 g/l, insbesondere Schaumglasgranulates, mit einem Absorptionsmittel gegebenenfalls unter Flüssigkeitszugabe gemischt und anschließend getrocknet werden, so dass die jeweiligen Körner des Leichtgranulates bzw. Schaumglasgranulates mit einer Absorptionsmittelbeschichtung vorgegebener Dicke umhüllt werden.to solution This technical problem is the subject of the invention a method for producing a particular liquid animal waste absorbing Gritters for Pets, after which grains a light granulate with a bulk density of less than 300 g / l, in particular foam glass granules, optionally with an absorbent with addition of liquid mixed and then be dried so that the respective grains of light granules or Foam glass granules with an absorbent coating predetermined Thickness wrapped become.
Leichtgranulat meint im Rahmen der Erfindung also eine granulare Masse mit einem Schüttgewicht von unter 300 g/l, insbesondere von weniger als 200 g/l. Vorzugsweise liegt das Schüttgewicht des Leichtgranulates sogar unterhalb von 100 g/l. Ergänzend beträgt die Korngröße weniger als 15 mm Korndurchmesser, wobei insbesondere eine Körnung mit einer Korngröße von 10 mm und weniger an Durchmesser bevorzugt wird. Meistens liegt die Korngröße sogar in einem Bereich unterhalb von 5 mm Korndurchmesser.easy granules means in the context of the invention thus a granular mass with a bulk weight less than 300 g / l, in particular less than 200 g / l. Preferably is the bulk density of light granules even below 100 g / l. In addition, the grain size is less as 15 mm grain diameter, in particular a grain with a Grain size of 10 mm and less diameter is preferred. Most of the time it lies Grain size even in a range below 5 mm grain diameter.
Dabei kommt es ergänzend darauf an, ein Leichtgranulat zur Verfügung zu stellen, welches preiswert in ausreichender Menge beschafft werden kann, sich mit dem betreffenden Absorptionsmittel problemlos beschichten lässt und im Übrigen Unverträglichkeiten mit dem (flüssigen) Tierabfall vermeidet. In diesem Zusammenhang hat sich insbesondere ein anorganisches Granulat mit den angegebenen Schüttgewichten von regelmäßig unterhalb von 300 g/l auf Glasbasis als besonders geeignet bewährt, wenngleich auch andere Materialien denkbar sind und von der Erfindung umfasst werden, solange sie in granularer Form mit der angegebenen Obergrenze des Schüttgewichtes vorliegen.there it comes in addition on it to provide a light granules, which is inexpensive can be procured in sufficient quantity to deal with the concerned Absorbant easily coat and incidentally incompatibilities with the (liquid) Animal waste avoids. In this context, in particular an inorganic granulate with the stated bulk densities from regularly below of 300 g / l based on glass proven to be particularly suitable, although Other materials are conceivable and encompassed by the invention as long as they are in granular form with the specified upper limit of bulk density available.
Das Leichtgranulat bzw. Schaumglasgranulat mag dabei über einen Restwassergehalt von weniger als 35 Gew.-% verfügen und kann aus Recyclingglas, synthetischem Glas, mineralischem Glas natürlichen Ursprungs oder Gemischen derselben hergestellt werden. Zu diesem Zweck kann das betreffende Glas mit beispielsweise einer wässrigen Alkalimetallhydroxyd-Lösung und/oder einer Alkalimetallsilicat-Lösung als wässrige Suspension bei Temperaturen von 60° C bis 120° C reagiert werden. Das erhaltene Reaktionsprodukt wird dann üblicherweise als viskose Masse ausgetragen, granuliert und solange abgekühlt, bis eine feste Granulatkörnung vorliegt. Anschließend wird das Granulat durch Erhitzen aufgebläht, wobei das Erhitzen in ein oder mehreren Stufen erfolgen kann. Nach dem beschriebenen Blähvorgang liegt das Leichtgranulat auf Glasbasis mit dem gewünschten Schüttgewicht von deutlich weniger als 300 g/l vor.The light granules or foam glass granules may have a residual water content of less than 35 wt .-% and may be made of recycled glass, synthetic glass, mineral glass of natural origin or mixtures thereof. For this purpose, the glass in question can be reacted with, for example, an aqueous alkali metal hydroxide solution and / or an alkali metal silicate solution as an aqueous suspension at temperatures of 60 ° C. to 120 ° C. The resulting reaction product is then usually discharged as a viscous mass, granulated and cooled until a solid Granulatkörnung exists. Subsequently, the granules are inflated by heating, wherein the heating can take place in one or more stages. After the described blowing process, the light granules are based on glass with the desired bulk density of significantly less than 300 g / l before.
Üblicherweise werden die Körner des Leichtgranulates bzw. Schaumglasgranulates während oder nach dem Trocknen zur Verbesserung der Abriebfestigkeit der Absorptionsmittelbeschichtung mittels eines Bindemittels (beispielsweise Bentonitsuspension) besprüht. Sofern jedoch die Abriebfestigkeit schon von vornherein gegeben ist und sich als ausreichend erweist, mag selbstverständlich auf einen solchen Sprühvorgang verzichtet werden. Das gilt auch für einen abschließenden Siebvorgang, mit dessen Hilfe die beschichteten Körner des Leichtgranulates bzw. Schaumglasgranulates nach dem Trocknen sowie gegebenenfalls dem Besprühen gesiebt werden. Denn auch dieser Klassifizierungsvorgang ist als Option anzusehen.Usually become the grains of light granules or foam glass granules during or after drying to improve the abrasion resistance of the absorbent coating by means of a binder (for example Bentonitsuspension) sprayed. Provided However, the abrasion resistance is given from the outset and of course proves to be sufficient, of course, on such a spraying process be waived. This also applies to a final screening process, with the help of which the coated grains of light granules or Foam glass granules after drying and optionally the spray be sifted. Because even this classification process is as Option to watch.
Im Rahmen der Erfindung kommt also nicht (mehr) ein Tonmineral als Hauptbestandteil des Streumittels zum Einsatz, welches zuvor bestimmte Modifikationen erfahren hat. Vielmehr greift die vorgestellte Lehre auf Körner eines Leichtgranulates zurück, die dann mit dem eigentlichen Absorptionsmittel beschichtet werden. Die jeweiligen Körner des Streumittels bestehen also in ihrem Innern aus dem betreffenden Leichtgranulat, während außen nur eine mehr oder minder dünne Schicht des Absorptionsmittels vorliegt. Diese Absorptionsmittelbeschichtung findet in einer Schichtdicke von regelmäßig 0,1 bis 3 mm, insbesondere 0,1 bis 2 mm Verwendung. Die Körner des Leichtgranulates mögen im Ausgangsmaterial eine Körnung von 0,1 bis 10 mm, insbesondere 0,1 bis 5 mm, vorzugsweise 0,5 bis 2 mm aufweisen. Anders ausgedrückt, verfügt der Körnerkern über die angegebenen Durchmesserwerte zwischen 0,1 bis 10 mm, insbesondere 0,1 bis 5 mm, vorzugsweise 0,5 bis 2 mm. Dagegen liegt der Körnermantel in der angegebenen Schichtdicke von regelmäßig 0,1 bis 3 mm, insbesondere 0,1 bis 2 mm vor. Dadurch werden rein rechnerisch Körner mit Durchmessern bis zu 13 mm hergestellt.in the The scope of the invention is therefore not (more) a clay mineral than Main component of the gritter used, which previously had certain modifications has experienced. Rather, the teaching presented on grains one of Light granules back, which are then coated with the actual absorbent. The respective grains of the scattering agent thus consist in their interior of the relevant Light granules while Outside just a more or less thin one Layer of the absorbent is present. This absorbent coating finds in a layer thickness of regularly 0.1 up to 3 mm, in particular 0.1 to 2 mm use. The grains of the Like light granulates in the starting material a grain size from 0.1 to 10 mm, in particular 0.1 to 5 mm, preferably 0.5 to 2 mm. In other words, has the kernel over the specified diameter values between 0.1 to 10 mm, in particular 0.1 to 5 mm, preferably 0.5 to 2 mm. In contrast, the grain coat is in the specified layer thickness of regularly 0.1 to 3 mm, in particular 0.1 to 2 mm before. As a result, grains are purely calculated Diameters up to 13 mm.
Das Leichtgranulat bzw. Schaumglasgranulat mag aus beispielsweise Abfallglas, synthetischem oder auch mineralischem Glas hergestellt sein, wobei die betreffende Aufzählung nicht vollständig ist. Grundsätzlich können beliebige Absorptionsmittel Verwendung finden, die mit den Körnern des Schaumglasgranulates in der beschriebenen Art und Weise eine Verbindung einzugehen in der Lage sind.The Light granules or foam glass granules may consist of, for example, waste glass, be made of synthetic or mineral glass, wherein the relevant list not completely is. in principle can Any absorbent can be used with the grains of foam glass granules in the manner described to make a connection in are able.
Dabei haben sich Absorptionsmittel auf Tonmineralbasis, insbesondere Dreischicht-Tonminerale, als besonders günstig erwiesen. Denn solche Tonminerale verfügen über eine äußerst ausgeprägte Quellfähigkeit, die den flüssigen Tierabfall aufzunehmen in der Lage ist. Gleichzeitig agglomerieren die erfindungsgemäßen Körner zu leicht handhabbaren Klumpen, die einwandfrei aus einer zugehörigen Streubox entfernt werden können. Die Eigenschaften sind also vergleichbar mit denjenigen, die von herkömmlichen Streumitteln zur Verfügung gestellt werden.there have clay-based absorbents, especially three-layer clay minerals, as a particularly cheap proved. Because such clay minerals have an extremely pronounced swelling capacity, the liquid To be able to absorb animal waste. Simultaneously agglomerate the grains according to the invention easy-to-handle lumps, which properly from an associated litter box can be removed. The properties are therefore comparable to those of usual Scattering available be put.
Bei dem Tonmineral kommt üblicherweise Montmorillonit zum Einsatz, welcher den Hauptbestandteil marktüblicher Bentonite darstellt. Im Einzelnen empfiehlt die Erfindung die Verwendung eines Kalzium-Bentonits, eines natürlichen Natrium-Bentonits oder eines technisch aktivierten Natrium-Bentonits. Dabei mag dem Absorptionsmittel bzw. dem Tonmineral oder Bentonit ergänzend ein optischer Aufheller beigefügt sein. Bei diesem optischen Aufheller handelt es sich bevorzugt um Titandioxid, welches auch bei der Papierherstellung als Aufheller Verwendung findet. Bei dem Bindemittel zur Erhöhung der Abriebfestigkeit der Absorptionsmittelbeschichtung handelt es sich in der Regel um Methylzellulose oder auch Wasserglas.at The clay mineral is usually montmorillonite used, which represents the main component of commercial bentonites. In particular, the invention recommends the use of a calcium bentonite, a natural one Sodium bentonite or a technically activated sodium bentonite. there May supplement the absorbent or the clay mineral or bentonite optical brightener attached be. This optical brightener is preferably Titanium dioxide, which is also used as a brightener in papermaking place. In the binder for increasing the abrasion resistance of Absorbent coating is usually methyl cellulose or water glass.
Im Ergebnis wird ein neuartiges Streumittel für Haustiere zur Verfügung gestellt, welches insbesondere flüssigen Tierabfall zu absorbieren in der Lage ist. In diesem Zusammenhang überzeugt das beschriebene Streumittel insbesondere dadurch, dass das Schüttgewicht des Endproduktes weniger als 500 g/l beträgt. Gegenüber herkömmlichen und klumpen bildenden Streumitteln wird also eine Gewichtsreduzierung auf mehr als die Hälfte beobachtet. Das erleichtert nicht nur den Transport enorm, sondern insbesondere auch die Handhabung beim Verbraucher.in the Result, a novel bedding remover will be provided for pets, which in particular liquid Animal waste is able to absorb. In this context, convinced the scattering agent described in particular in that the bulk density of the final product is less than 500 g / l. Compared to conventional and lump forming Scattering will be a weight reduction to more than that half observed. This not only facilitates the transport enormously, but also in particular, the handling of the consumer.
Diese Erfindungsmaßnahme wird insbesondere dadurch erreicht, dass die einzelnen Körner des Streumittels mit einem Schaumglasgranulatkern bzw. Leichtgranulatkern ausgerüstet sind. Derartige Schaumgläser lassen sich vorteilhaft aus Abfallglas oder auch Recyclingglas herstellen. Dabei wird in der Regel ein Abfallglasmehl erzeugt und unter Zugabe eines Treibmittels zu einer viskosen Masse aufbereitet, die durch Erhitzen zum Aufblähen gebracht wird.These invention measure is achieved in particular by the fact that the individual grains of the scattering agent are equipped with a foam glass granulate core or Leichtgranulatkern. Such foam glasses can be advantageously produced from waste glass or recycled glass. In this case, a waste glass powder is usually generated and with the addition of a Propellant prepared to a viscous mass by heating to inflate is brought.
Einzelheiten
einer solchen Schaumglasgranulatherstellung werden in der
Die
einzelnen leichtgewichtigen Körner
werden nun erfindungsgemäß beschichtet,
nämlich
mit dem den flüssigen
Tierabfall aufnehmenden Absorptionsmittel. Dabei hat es sich gezeigt,
dass die an dieser Stelle vorliegende Schichtdicke von 0,1 bis 3
mm der Absorptionsmittelbeschichtung ausreicht, den flüssigen Tierabfall
einwandfrei aufnehmen zu können.
Tatsächlich
werden Wasseraufnahmeraten von deutlich mehr als 100 Gew.-% erreicht,
die sogar noch die angegebe nen Werte in der
Die Erfindungslehre macht also deutlich, dass die bisherigen Streumittel auf Tonmineral- bzw. Bentonitbasis nahezu ausschließlich die äußeren Schichten des jeweiligen Kornes für die Flüssigkeitsaufnahme genutzt haben, wohingegen der innere Kern zumeist keine Flüssigkeit mehr aufgenommen hat. Denn zuvor ist es bereits zu der gewünschten Klumpenbildung gekommen. Auch wird der Zugang zum Körnerkern durch die gequollene äußere Schicht zunehmend erschwert.The Inventions thus make it clear that the previous scattering agents on Tonmineral- or Bentonitbasis almost exclusively the outer layers of the respective grain for the fluid intake whereas the inner core mostly has no liquid has recorded more. Because before it is already the desired lump formation came. Also, access to the kernel core is through the swollen outer layer increasingly difficult.
Diese Erkenntnis nutzt die vorliegende Innovation, indem der innere Körnerkern aus einem leichtgewichtigen Material, nämlich einem Leichtgranulat bzw. Schaumglasgranulat besteht. Das Schaumglas neigt nicht zu Reaktionen mit dem Tierabfall, ist im Übrigen gesundheitlich unbedenklich, so dass dem Einsatz als Streumittel nichts entgegensteht.These Knowledge uses the present innovation by the inner kernel from a lightweight material, namely a light granulate or foam glass granules. The foam glass does not tend to react with the animal waste, by the way Harmless to health, so use as a scattering agent nothing stands in the way.
Das alles wird erreicht bei einem halbierten Schüttgewicht im Vergleich zu marktüblichen Klumpstreus und gleicher Fähigkeit zur Klumpenbildung bzw. Agglomeration.The Everything is achieved with a halved bulk density compared to conventional Klumpstreus and equal ability for clumping or agglomeration.
Beispiel:Example:
Zunächst werden Schaumglasgranulatkörner mit einer Körnung von 0,1 bis ca. 3 mm Korndurchmesser zur Verfügung gestellt. Das Schüttgewicht liegt zwischen 100 g/l und 200 g/l.First, be Foam glass granules with a grain from 0.1 to about 3 mm grain diameter provided. The bulk density is between 100 g / l and 200 g / l.
Die Absorptionsmittelbeschichtung kann auf grundsätzlich zweierlei Art und Weise auf das jeweilige Korn des Schaumglasgranulates aufgebracht werden. In einer ersten Variante werden die einzelnen Körner mit Wasser oder einer anderen geeigneten Flüssigkeit gesättigt und in einen Mischer (z. B. Lödige- oder Eirich-Mischer) gegeben. Ein Eirich-Mischer verfügt bekanntermaßen über einen Granulierteller, welcher mit einem Hochgeschwindigkeits-Rührwerk sowie mit Rührwerk-Flügeln ausgestattet ist. Die Rührwerk-Flügel rotieren mit einer geringeren Geschwindigkeit als der Granulierteller, und zwar in einer zu seiner Drehrichtung entgegengesetzten Richtung.The Absorbent coating can be done in basically two ways be applied to the respective grain of the foam glass granules. In a first variant, the individual grains with water or a other suitable liquid saturated and into a mixer (eg Lödige- or Eirich mixer). An Eirich mixer is known to have a granulating dish, which is equipped with a high-speed agitator and stirrer blades is. The agitator blades rotate at a slower speed than the granulating plate, and indeed in a direction opposite to its direction of rotation.
Im Anschluss an die Mischung der Körner mit Wasser oder der anderen Flüssigkeit wird das Absorptionsmittel bzw. ein Bentonit als Pulver (bzw. ergändend als Bindemittel) zugegeben, wobei gegebenenfalls der bereits beschriebene optische Aufheller, z. B. Titandioxid, in dem Pulver enthalten ist. Im Rahmen des einsetzenden Mischprozesses werden die einzelnen Körner des Schaumglasgranulates mit der gewünschten Absorptionsmittelbeschichtung ausgerüstet. Sobald das Absorptionsmittel die jeweiligen Körner vollständig mit einer Schichtdicke von ca. 0,1 bis 2 mm umhüllt hat und dabei ein fließfähiges Granulat mit einer Körnung zwischen ca. 0,3 mm bis 7 mm entstanden ist, wird der Mischprozess beendet.in the Following the mixture of grains with water or the other liquid is the absorbent or a bentonite powder (or ergaend as Binder) is added, optionally the already described optical brighteners, z. As titanium dioxide, is contained in the powder. As part of the incipient mixing process, the individual grains of the Foam glass granules with the desired Equipped absorbent coating. Once the absorbent the respective grains Completely coated with a layer thickness of about 0.1 to 2 mm, while a flowable granules with a grain between about 0.3 mm to 7 mm, is the mixing process completed.
Alternativ hierzu lassen sich die Körner des Schaumglasgranulates auch trocken in einen Mischer eingeben, wobei zu dieser Trockenmischung eine wässrige Aufschlämmung des Absorptionsmittels bzw. des weißen Betonits, dem gegebenenfalls ein optischer Aufheller zugesetzt ist, gegeben wird. Wie zuvor bereits beschrieben, wird der Mischprozess beendet, wenn ein fließfähiges Granulat unter Berücksichtigung der Absorptionsmittelbeschichtung von 0,1 bis 2 mm entstanden ist.alternative this can be the grains of the foam glass granules also dry in a mixer, wherein to this dry mixture, an aqueous slurry of the absorbent or white Betonits, to which an optical brightener is optionally added, is given. As previously described, the mixing process becomes stopped when a flowable granules considering the absorbent coating of 0.1 to 2 mm is formed.
In jedem Fall wird nach dem beschriebenen Mischprozess überschüssiges Wasser entfernt, indem das noch feuchte Granulat mit Hilfe einer pulverförmigen Mischung aus dem Absorptionsmittel (weißer Bentonit), einem optischen Aufheller sowie gegebenenfalls einem Bindemittel bestäubt wird. Danach erfolgt ein erneutes Mischen für ca. 1 bis 2 Minuten, bis das Granulat keine Agglomerate mehr aufweist.In In any case, after the mixing process described, excess water removed by adding the still moist granules using a powdery mixture from the absorbent (white Bentonite), an optical brightener and optionally one Binder pollinated becomes. Thereafter, a new mixing for about 1 to 2 minutes, until the granules no longer has agglomerates.
Im nächsten Schritt wird das Granulat dann in einem Heißlufttrockner bis auf eine Restfeuchte von 3 bis 10 Gew.-% getrocknet, wobei anschließend zur Verbesserung der Abriebfestigkeit der Absorptionsmittelbeschichtung das noch heiße Granulat mit einer wässrigen Lösung eines Bindemittels (z. B. Methylzellulose oder Wasserglas) besprüht wird.in the next Step the granules then in a hot air dryer down to one Residual moisture of 3 to 10 wt .-% dried, in which case the Improvement of the abrasion resistance of the absorbent coating that's still hot Granules with an aqueous solution a binder (eg methyl cellulose or water glass) is sprayed.
Abschließend wird das getrocknete Granulat auf einer Siebanlage in die gewünschte Kornfraktion abgesiebt.Finally, it will sieved the dried granules on a sieve in the desired grain fraction.
Es
ergeben sich folgende Kennwerte für das neuartige Streumittel:
Schüttgewicht:
445 g/l;
Kornverteilung: 4,0–3,15 mm: 0,9
3,15–2,0 mm:
40,1
2,0–1,0
mm: 51,1
0,5–1,0
mm: 7,9
< 0,
5 mm: 0
Wasseraufnahme nach Westinghouse: Gew.-405 %;
Klumpendurchmesser
ca. 5 bis 10 cm.The following characteristic values for the novel scattering agent result:
Bulk density: 445 g / l;
Grain distribution: 4.0-3.15 mm: 0.9
3.15-2.0 mm: 40.1
2.0-1.0 mm: 51.1
0.5-1.0 mm: 7.9
<0, 5 mm: 0
Water absorption according to Westinghouse: 405% by weight;
Club diameter approx. 5 to 10 cm.
Claims (12)