CZ286988B6 - Process for preparing aluminous cements based on compounds Ca.Ali2Oi3 and CaO.2Al2O3 from ammonia alum - Google Patents

Process for preparing aluminous cements based on compounds Ca.Ali2Oi3 and CaO.2Al2O3 from ammonia alum Download PDF

Info

Publication number
CZ286988B6
CZ286988B6 CZ1997976A CZ97697A CZ286988B6 CZ 286988 B6 CZ286988 B6 CZ 286988B6 CZ 1997976 A CZ1997976 A CZ 1997976A CZ 97697 A CZ97697 A CZ 97697A CZ 286988 B6 CZ286988 B6 CZ 286988B6
Authority
CZ
Czechia
Prior art keywords
cao
ground
preparing
ali2oi3
alum
Prior art date
Application number
CZ1997976A
Other languages
Czech (cs)
Other versions
CZ97697A3 (en
Inventor
Zdeněk Prof. Dr. Ing. Drsc. Šauman
Marie Ing. Brandstillerová
Pavel Ing. Matoušek
Petr Ing. Novák
Original Assignee
Diamo S. P.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Diamo S. P. filed Critical Diamo S. P.
Priority to CZ1997976A priority Critical patent/CZ286988B6/en
Publication of CZ97697A3 publication Critical patent/CZ97697A3/en
Publication of CZ286988B6 publication Critical patent/CZ286988B6/en

Abstract

The invented process for preparing aluminous cements is characterized in that ammonia alum is used as starting material. Ammonia alum is mixed either in initial state or precalcinated at a temperature ranging from 900 to 1000 degC with either calcium carbonate or oxide in molar ratio of CaO : Ali2Oi3 being equal to 1 : 1 to 1 : 2 and the obtained mixture of raw materials is ground, homogenized and optionally subjected to granulation. So treated reaction mixture is subsequently heat treated at temperature range from 1450 to 1650 degC and then ground so that specific surface of the resulting product is at least 300 square meters per one kilogram.

Description

Způsob přípravy hlinitanových cementů na bázi sloučenin CaO.Al2O3 a CaO.2Al2O3 z kamence hlinitoamonnéhoProcess for the preparation of aluminous cements based on CaO.Al 2 O 3 and CaO.2Al 2 O 3 compounds from ammonium alum

Oblast technikyTechnical field

Vynález se týká způsobu výroby hlinitanového cementu přepracováním kamence hlinitoamonného NH4A1(SO4)2.12H2O.BACKGROUND OF THE INVENTION The present invention relates to a process for the production of aluminous cement by reworking alumina alum NH 4 A1 (SO 4 ) 2 .12H 2 O.

Dosavadní stav technikyBACKGROUND OF THE INVENTION

Dosavadní způsoby přípravy sloučenin CaO.Al2O3 a CaO.2Al2O3 vycházejí převážně z tepelného zpracování směsi hlinitých sloučenin na bázi oxidu hlinitého a vápence.The prior art processes for the preparation of CaO.Al 2 O 3 and CaO 2 Al 2 O 3 are mainly based on the heat treatment of a mixture of aluminum compounds based on alumina and limestone.

Využití kamence hlinitoamonného pro výrobu sloučenin CaO.Al2O3 a CaO.2Al2O3 nebylo dosud realizováno ani zvažováno s ohledem na nedostatečný zdroj této hlinité suroviny.The use of ammonium alum for the production of CaO.Al 2 O 3 and CaO 2 Al 2 O 3 has not been realized or considered with regard to the insufficient source of this aluminum raw material.

Podstata vynálezuSUMMARY OF THE INVENTION

Způsob přípravy hlinitanových cementů, jejichž hlavní složky tvoří sloučeniny CaO.Al2O3 a CaO.2Al2O3 podle vynálezu spočívá v tom, že se jako hlinitá surovina použije kamenec hlinitoamonný, jenž se v původním nebo předžíhaný při teplotě 900 až 1000 °C smísí s uhličitanem nebo oxidem vápenatým v molámím poměru CaO:Al2O3 rovném 1:1 až 1:2. Vzniklá surovinová směs se semele, zhomogenizuje, případně podrobí granulaci a poté se tepelně zpracuje v rotační peci při teplotách v rozmezí od 1450 do 1650 °C. Podle zvoleného molámího poměru CaO:Al2O3 a použité teploty výpalu vznikají při jejím tepelném zpracování reakcemi v pevném stavu převážně sloučeniny CaO.Al2O3 a CaO.2Al2O3 doprovázené případně velmi malým podílem fáze 12CaO.7Al2O3. Tepelně zpracovaná směs se semele na měrný povrch vyšší než 300 m2.kg1.Process for preparing alumina cements whose major components are compounds CaO.Al 2 O 3 CaO.2Al 2 O 3 according to the invention consists in that the aluminum material used as alum hlinitoamonný that in the initial or preliminary calcination at a temperature of 900-1000 ° C is mixed with carbonate or calcium oxide in a molar CaO: Al 2 O 3 ratio of 1: 1 to 1: 2. The resulting feedstock mixture is ground, homogenized, optionally granulated and then heat-treated in a rotary kiln at temperatures ranging from 1450 to 1650 ° C. According to the selected molar ratio of CaO: Al 2 O 3 and the temperatures of firing are formed during the thermal treatment by solid state reaction of predominately CaO.Al 2 O 3 CaO.2Al 2 O 3 optionally accompanied by a very small proportion of phase 12CaO.7Al 2 O 3 . The heat treated mixture is ground to a specific surface area of more than 300 m 2 .kg 1 .

Příklady provedení vynálezuDETAILED DESCRIPTION OF THE INVENTION

Příklad 1Example 1

Surový kamenec hlinitoamonný produkovaný například sanační technologií odsolování roztoků chemické těžby uranu se předžíhá při teplotě 950 °C. Poté se semele na měrný povrch 360 m2.kg'1. A smíchá s přírodním mletým vápencem obsahujícím více než 90 % CaCO3 v molámím poměru CaO:Al2O3 rovném 1:1,5. Po důkladné homogenizaci se surovinová směs granuluje a následně tepelně zpracuje v rotační peci při teplotě 1500 °C. Výpalek obsahuje zejména sloučeniny CaO.Al2O3 a CaO.2Al2O3, které jsou hlavními složkami hlinitanového cementu. Výsledný produkt - hlinitanový cement - se připraví rozemletím výpalku v kulovém mlýně na měrný povrch 350 m2.kg'1.The crude ammonium alum produced by, for example, the desalination technology of the uranium chemical extraction solutions is preheated at a temperature of 950 ° C. Then grind to a specific surface of 360 m 2 .kg -1 . And it is mixed with natural ground limestone containing more than 90% CaCO 3 in a molar ratio of CaO: Al 2 O 3 of 1: 1.5. After thorough homogenization, the feed mixture is granulated and subsequently heat-treated in a rotary kiln at 1500 ° C. It comprises especially compounds burnout CaO.Al 2 O 3 CaO.2Al 2 O 3, which are major components of alumina cement. The resulting product - aluminous cement - is prepared by grinding the stillage in a ball mill to a specific surface of 350 m 2 .kg -1 .

Příklad 2Example 2

Surový kamenec hlinitoamonný produkovaný například sanační technologií odsolování roztoků chemické těžby uranu se smíchá s přírodním mletým vápencem obsahujícím více než 90 % CaCO3 v molámím poměru CaO:Al2O3 = 1:2. Po důkladné homogenizaci se surovinová směs granuluje a následně tepelně zpracuje v rotační peci při teplotě 1600 °C. Výpalek v tomtoThe crude ammonium alum produced by, for example, the desalination technology of the uranium chemical extraction solutions is mixed with natural ground limestone containing more than 90% CaCO 3 in a molar ratio of CaO: Al 2 O 3 = 1: 2. After thorough homogenization, the raw material mixture is granulated and subsequently heat-treated in a rotary kiln at 1600 ° C. The fudge in this

-1 CZ 286988 B6 případě obsahuje výrazně větší množství sloučeniny CaO.2Al2O3 a menší množství sloučeniny CaO.Al2O3. Výsledný produkt - hlinitanový cement - se získá rozemletím výpalku v kulovém mlýně na měrný povrch 370 m2.kg’1.In this case, it contains a significantly larger amount of the CaO.2Al 2 O3 compound and a smaller amount of the CaO.Al 2 O3 compound. The resulting product - aluminous cement - is obtained by grinding the stillage in a ball mill to a specific surface of 370 m 2 .kg -1 .

Průmyslová využitelnostIndustrial applicability

Vynález lze využít k přípravě hlinitanových cementů z kamence hlinitoamonného. Vynález je výhodné využít zejména pro přepracování kamence hlinitoamonného, vznikajícího jako odpadoío vý produkt, např. při sanaci technologických roztoků hydrochemické těžby kovů, např. uranu, na průmyslově využitelný produkt.The invention can be used to prepare aluminate cements from alum ammonium alum. The invention is particularly advantageous for converting ammonium alum produced as a waste product, for example in the rehabilitation of technological solutions of hydrochemical mining of metals, such as uranium, into an industrially usable product.

Claims (2)

PATENTOVÉ NÁROKYPATENT CLAIMS 1. Způsob přípravy hlinitanových cementů na bázi sloučenin CaO.Al2O3 a CaO.2Al2O3, 20 vyznačující se tím, že se kamenec hlinitoamonný v původním stavu nebo předžíhaný při teplotě 900 až 1000 °C smísí s uhličitanem nebo oxidem vápenatým v molámím poměru CaO:Al2O3 rovnému 1:1 až 1:2 a vzniklá surovinová směs se semele, zhomogenizuje a poté se podrobí tepelnému zpracování v rozmezí teplot 1450 až 1650 °C, po němž se výsledný produkt semele tak, aby jeho měrný povrch činil nejméně 300 m^kg'1.Process for preparing aluminous cements based on CaO.Al 2 O 3 and CaO 2 Al 2 O 3 , 20 characterized in that alum ammonium alum in its original state or preheated at a temperature of 900 to 1000 ° C is mixed with carbonate or calcium oxide in a molar ratio of CaO: Al 2 O3 of 1: 1 to 1: 2 and the resulting feed mixture is ground, homogenized and then subjected to heat treatment in the range of 1450 to 1650 ° C, after which the resulting product is ground to its specific the surface area was at least 300 m ^ kg -1 . 2. Způsob podle nároku 1, vyznačující se tím, že semletá a zhomogenizovaná surovinová směs se před tepelným zpracováním podrobí granulaci.Method according to claim 1, characterized in that the ground and homogenized raw material mixture is subjected to granulation prior to heat treatment.
CZ1997976A 1997-04-01 1997-04-01 Process for preparing aluminous cements based on compounds Ca.Ali2Oi3 and CaO.2Al2O3 from ammonia alum CZ286988B6 (en)