CZ280306B6 - Silicate solution for treating elevation plasters - Google Patents

Silicate solution for treating elevation plasters Download PDF

Info

Publication number
CZ280306B6
CZ280306B6 CS922851A CS285192A CZ280306B6 CZ 280306 B6 CZ280306 B6 CZ 280306B6 CS 922851 A CS922851 A CS 922851A CS 285192 A CS285192 A CS 285192A CZ 280306 B6 CZ280306 B6 CZ 280306B6
Authority
CZ
Czechia
Prior art keywords
weight
solution
silica
silica solution
silicate
Prior art date
Application number
CS922851A
Other languages
Czech (cs)
Inventor
Lubomír Ing. Mrázek
Miroslav Ing. Dr. Nedorost
Libor Pala
Original Assignee
Lubomír Ing. Mrázek
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lubomír Ing. Mrázek filed Critical Lubomír Ing. Mrázek
Priority to CS922851A priority Critical patent/CZ280306B6/en
Publication of CZ285192A3 publication Critical patent/CZ285192A3/en
Publication of CZ280306B6 publication Critical patent/CZ280306B6/en

Abstract

Pro silkátování fasád byl vyzkoušen nový křemičitý roztok sestávající ze směsi draselného vodního skla, koloidního oxidu křemičitého o hmotnostním poměru SíO.sub.2 .n./ K.sub.2.n.O 2,5 až 6, výhodně 4 až 5 o sušině 5 až 20 procent hmotnostních, výhodně 10 až 15 procent hmotnostních, stabilizovaný 0,02 až 0,5 procenty hmotnostními výhodně 0,05 až 0,1 procent hmot. difosforečnanem draselným. Pro zlepšení vlastností silikátového nátěru přidávají se do křemičitého roztoku ještě hydrofobní přísady na bázi polyorganosiloxanů, akrylátové disperze, neionogenní smáčedlo a aglicidní a fungicidní ochranné látky. Silikátování fasád křemičitým roztokem se nejvíce používá u starých vyspravených omítek s nestejnoměrnou nasákavostí a pevností, jako přednátěr při aplikaci silikátorových barev. Při samotným použití se křemičitý roztok částečně hydrofobilizuje, aby byl odolnější vůči povětrnostnímu namáhaní. Pokrok v řešení spočívá v tom, že silikátování fasád s tímto novým křemičitýŕA new siliceous solution consisting of a mixture of potassium waterglass, colloidal silicon dioxide with a weight ratio of 2.5 to 6, preferably 4 to 5, dry matter 5 was tested for silking of the facades. up to 20 percent by weight, preferably 10 to 15 percent by weight, stabilized by 0.02 to 0.5 percent by weight, preferably 0.05 to 0.1 percent by weight; with potassium pyrophosphate. To improve the properties of the silicate coating, hydrophobic additives based on polyorganosiloxanes, acrylate dispersions, nonionic surfactants and aglicides and fungicides are added to the silica solution. Silicate the facades with siliceous solution is the most used in old repaired plasters with uneven water absorption and strength, as a pre-coating when applying silicone paints. During use, the silica solution is partially hydrophobised to be more resistant to weathering. Progress in the solution lies in the fact that silicate facades with this new silica

Description

Křemičitý roztok pro silikátování omítekSilicate solution for silicate plasters

Oblast technikyTechnical field

Vynález se týká úpravy vápenocementové omítky silikátováním pomocí křemičitého roztoku připraveného na bázi draselného vodního skla, koloidního oxidu křemičitého, difosforečnanového stabilizátoru s fungicidní a algicidní ochranou neionogenním smáčedlem, popřípadě s hydrofobními přísadami a akrylátovou nebo styrenakrylátovou disperzí.The invention relates to the treatment of a lime-cement plaster by silicate using a silica solution prepared on the basis of potassium water glass, colloidal silica, a pyrophosphate stabilizer with fungicidal and algicidal protection with a nonionic surfactant, optionally with hydrophobic additives and acrylate or styrene acrylate dispersion.

Dosavadní stav technikyBACKGROUND OF THE INVENTION

Silikátování omítek s nestejnomérou nasákavostí, různě porézním a pevným podkladem je známé a provádí se ponejvíce u starých vyspravených omítek zředěným roztokem speciálně připraveného draselného vodního skla s vysokým mol. poměrem SiO2/K2O = 5 až 7. Silikátováním se omítka zpevní a stává se stejnoměrně propustnou a teprve potom se může přikročit k natírání silikátovou barvou. Protože speciální draselné vodní sklo s vysokým mol. poměrem SiO2/K2O se v tuzemsku nevyrábí a jeho dovoz ze zahraničí je velmi nákladný, bylo úkolem nalézt jiný vhodný křemičitý roztok pro silikátování omítek.Silicate rendering of plasters with uneven absorbency, porous and solid substrates is known and is carried out mostly on old repaired plasters with a dilute solution of specially prepared high molten potassium water glass. With a SiO 2 / K 2 O ratio of 5 to 7. The silicate coating strengthens and becomes evenly permeable before painting with silicate paint. Because special potassium water glass with a high mol. the SiO 2 / K 2 O ratio is not produced in the Czech Republic and its import from abroad is very expensive, the task was to find another suitable silica solution for silicate plasters.

V patentové literatuře se řeší problém výroby silikátového pojivá fasádní nátěrové hmoty ve spisech CH 637 989, GB 2 010 876, ČS patentu 275 380. Podle CH 637 989, GB 2 010 876 se připravuje minerální pojivo pro nátěry ze směsi draselného a sodného vodního skla s přísadou velmi jemného práškového hydratovaného oxidu křemičitého, vody a metyltrimetoxysilanu intenzivním vířivým mícháním při zvýšené teplotě až suspenze oxidu křemičitého přejde v sol. Přitom metyltrimetoxysilan zhydrolyzuje na metylsilanol a stabilizuje vzniklý sol se zvýšeným mol. poměrem SiO2/K2O. ČS patent 275 380 se týká fasádní nátěrové hmoty se zvýšenou odolností vůči špinění a plynovým exhalacím. Vyznačuje se tím, že obsahuje styrenakrylátovou nebo akrylátovou disperzi a vodní sklo s vápencem a siloxidem (práškový SiO2) s hydrofobní přísadou metylsiloxanem.The patent literature solves the problem of the production of silicate binder facade paints in the documents CH 637 989, GB 2 010 876, CZ patent 275 380. According to CH 637 989, GB 2 010 876 a mineral binder is prepared for coating from a mixture of potassium and sodium water glass with the addition of very fine hydrated silica powder, water and methyltrimethoxysilane by vigorous vortexing at elevated temperature until the silica suspension becomes sol. In this case, methyltrimethoxysilane hydrolyzes to methylsilanol and stabilizes the resulting sol with an increased mol. The ratio of SiO 2 / K 2 O. The CS patent 275 380 relates to a facade paint with increased resistance to staining and gas exhalations. It is characterized in that it contains a styrene acrylate or acrylate dispersion and a water glass with limestone and siloxide (powdered SiO 2 ) with a hydrophobic additive methylsiloxane.

Podstata vynálezuSUMMARY OF THE INVENTION

Na základě experimentálních zkoušek bylo s překvapením zjištěno, že je možné pro výrobu křemičitého roztoku použít i draselné vodní sklo s nízkým mol. poměrem SiO2/K2 = 2,8 až 3,3, když se jeho mol. poměr zvýší přídavkem roztoku koloidního oxidu křemičitého a současně se stabilizuje pomocí K4P2O7, aby nenastala gelace SiO2 během skladování v silné alkalickém prostředí.Based on experimental tests, it has surprisingly been found that low moles potassium water glass can also be used for the production of the silica solution. SiO 2 / K 2 ratio = 2.8 to 3.3 when its mol. the ratio is increased by the addition of a colloidal silica solution and at the same time stabilized with K 4 P 2 O 7 to avoid SiO 2 gelation during storage in a strong alkaline environment.

Podstatou křemičitého roztoku pro silikátování vápenocementových omítek je zředěný směsný roztok draselného vodního skla a koloidního oxidu křemičitého o mol. poměru SiO2/K2O = 3,5 až 9, výhodně 6 až 8 o sušině 5 až 20 % hmot., výhodné 10 až 15 % hmot., vztaženo pouze na tyto dvé složky, 0,01 až 0,5 % hmot, difosforečnanu draselného a/nebo 0,1 až 3 % hmot., výhodné 0,5 ažThe essence of the silica solution for silicate lime-cement plasters is a diluted mixed solution of potassium water glass and colloidal silica with a mol. SiO 2 / K 2 O ratio = 3.5 to 9, preferably 6 to 8, 5 to 20% by weight, preferably 10 to 15% by weight, based on the two components only, 0.01 to 0.5% % of potassium pyrophosphate and / or 0.1 to 3 wt.%, preferably 0.5 to 3 wt

-1CZ 280306 B6 % hmot, aktivní hydrofobní substance, vybrané ze skupiny zahrnující polyorganosiloxany obsahující ve vodě rozpustné alkalické soli dimetyl-, difenyl-, metyl-, fenyl-silanolátu nebo elastomery polydimetylsiloxanů ve formě vodné emulze, popřípadě s přídavkem 0,5 až 10 % hmot., výhodně 2 až 5 % hmot, akrylátové nebo styrenakrylátové disperze. Zbytek do 100 % hmot, tvoří odsolená voda.% By weight of active hydrophobic substance selected from the group consisting of polyorganosiloxanes containing water-soluble alkali salts of dimethyl-, diphenyl-, methyl-, phenyl-silanolate or elastomers of polydimethylsiloxanes in the form of an aqueous emulsion, optionally with the addition of 0.5 to 10 % of acrylate or styrene acrylate dispersion. The remainder to 100% by weight is desalinated water.

Příprava křemičitého roztoku podle vynálezu se děje pouhým míšením uvedených složek. Do odsolené vody se nejprve rozpustí K4P2°7 a P°tom se Postupné přidají roztok koloidního oxidu křemičitého, roztok vodního skla, popřípadě hydrofobní látka nebo akrylátová disperze. Pro snížení povrchového napětí se přidá do křemičitého roztoku malé množství neionogenního smáčedla a ochranná fungicidní a algicidní látka, nejlépe zředěný alkalický roztok komplexu mědi s alkalickou solí N,N bis-2-hydroxyetylaminooctové.The preparation of the silica solution according to the invention is carried out simply by mixing said components. To demineralized water are initially dissolved K 4 P 2 and P ° 7 ° with the axis P lable added a solution of colloidal silica, waterglass solution, or a hydrophobic substance or acrylate dispersion. To reduce the surface tension, a small amount of a nonionic surfactant and a protective fungicidal and algicidal agent, preferably a dilute alkaline solution of the copper complex with the N, N bis-2-hydroxyethylaminoacetic acid alkali salt, are added to the silica solution.

Upravuje-li se zdivo pouze jedním nebo dvěma nátěry, přidá se do posledního nátěru malé množství hydrofobní látky a akrylátové nebo styrenakrylátové disperze, aby nátěr odpuzoval vodu a prodloužila se jeho životnost. Použije-li se křemičitý roztok jako přednátěr pro nanášení silikátové barvy nehydrofobizuje se, ale může obsahovat malé množství akrylátové nebo styrenakrylátové disperze pro zlepšení skladovatelnosti a zpracovatelnosti nátěru.If the masonry is treated with only one or two coats, a small amount of hydrophobic substance and an acrylate or styrene acrylate dispersion are added to the last coat to repel the water and extend its life. When a silica solution is used as a leaching agent for silicate paint application, it does not hydrophobize but may contain a small amount of acrylate or styrene acrylate dispersion to improve the shelf life and processability of the coating.

K4P2°7 zabraňuje gelování SiO2 během skladování a současně zlepšuje tvrdnutí a pevnost nátěru. Příčina tvrdnutí křemičitého nátěru není zcela objasněna a bude podrobena dalšímu studiu. Pravděpodobně uvolněná kyselina křemičitá z vodního skla účinkem vzdušného oxidu uhličitého reaguje s koloidním oxidem křemičitým za vzniku vysokomolekulárních kondenzačních produktů, které se při tvrdnutí zesiťují a vytvoří s omítkou pevný nátěr. Bylo zjištěno, že samotný koloidní oxid křemičitý není vhodný pro silikátování omítek, protože nátěr špatně tvrdne a je i po delší době měkký. K 4 P 2 ° 7 prevents the gelling of SiO 2 during storage and at the same time improves the hardening and strength of the coating. The cause of the hardening of the silica coating is not fully understood and will be subjected to further study. Probably released waterglass silicic acid reacts with colloidal silica under the action of airborne carbon dioxide to produce high molecular weight condensation products that crosslink when hardened to form a solid coating with the plaster. It has been found that colloidal silicon dioxide alone is not suitable for silicate plasters because the coating hardens and is soft even after a long time.

Příklady provedeni vynálezuDETAILED DESCRIPTION OF THE INVENTION

Příklad 1Example 1

Do 700 g odsolené vody se rozpustí za míchání 0,7 g K4P2O7 a potom se postupné přidá 150 g roztoku koloidního oxidu křemičitého o koncentraci 30 % hmot., 150 g roztoku draselného vodního skla o mol. poměru SiO2/K2O = 3,3, hustoty = 1,35 g/cm3, 0,5 g neionogenního smáčedla Slovasol 3520 - R a 12 ml roztoku mědi v komplexu se Syntronem - D (dihydroxyetylglycinu), odpovídající 0,05 g mědi.To 700 g of desalinated water, 0.7 g of K 4 P 2 O 7 is dissolved with stirring, and then 150 g of a 30 wt.% Colloidal silica solution, 150 g of a potassium waterglass solution of mol. SiO 2 / K 2 O ratio = 3.3, density = 1.35 g / cm 3 , 0.5 g of Slovasol 3520-R nonionic surfactant and 12 ml of copper solution complexed with Syntron-D (dihydroxyethylglycine) corresponding to 0, 05 g copper.

Příklad 2Example 2

Postup podle příkladu 1 s tím rozdílem, že se přidá navíc g Lukofobu 39 (vodný roztok draselných solí metyl a fenyl silanolátu).The procedure of Example 1, except that an additional g of Lukofob 39 (an aqueous solution of potassium salts of methyl and phenyl silanolate) was added.

-2CZ 280306 B6-2GB 280306 B6

Přiklad 3Example 3

Postup podle příkladu 1 s tím rozdílem, že se přidá navíc 6 g silikonové emulze Lukopren - E 7620 (elastomer na bázi polydimetylsiloxanu).The procedure of Example 1 except that an additional 6 g of Lukopren-E 7620 silicone emulsion (polydimethylsiloxane-based elastomer) was added.

Příklad 4Example 4

Postup podle příkladu 1 s tím rozdílem, že se přidá navíc 50 g Sokratu 2403 LX (kopolymer styrenakrylátové disperze).The procedure of Example 1, except that an additional 50 g of Sratrat 2403 LX (styrene acrylate dispersion copolymer) was added.

Průmyslová využitelnostIndustrial applicability

Křemičitý roztok se nejčastěji používá pro silikátování starých vyspravených omítek s nestejnoměrnou nasákavostí a pevností jako přednátěr při aplikaci silikátových nátěrových barev i k jejich ředění. Použije-li se křemičitý roztok jako samotný nátěr, je účelné, aby byl hydrofobizován polyorganosiloxany, popřípadě upraven akrylátovou nebo styrenakrylátovou disperzí. Pokrok řešení spočívá v tom, že silikátování omítek s novým křemičitým přípravkem se provádí s poměrně nízkými náklady a není třeba používat speciální draselné vodní sklo s vysokým mol. poměrem SiO2/K2O = 5 až 7.The silicate solution is most often used to silicate old repaired plasters with uneven absorbency and strength as a primer for the application of silicate paints and their dilution. If the silica solution is used as the coating itself, it is expedient to be hydrophobized with polyorganosiloxanes, optionally treated with an acrylate or styrene acrylate dispersion. Progress of the solution consists in the fact that the silicate of the plasters with the new silica preparation is carried out at relatively low cost and there is no need to use a special potassium water glass with a high mol. SiO 2 / K 2 O ratio = 5 to 7.

Claims (7)

1. Křemičitý roztok pro silikátování omítek, vyznačuj ίο i se tím, že sestává ze směsi roztoků draselného vodního skla, vodního roztoku koloidního oxidu křemičitého o molárním poměru SiO2/K2O rovném 3,5 až 9, o sušině 5 až 20 % hmot., vztaženo pouze na tyto dvě složky, 0,01 až 0,5 % hmot, difosforečnanu draselného a/nebo 0,1 až 3 % hmot, aktivní hydrofobní substance, vybrané ze skupiny zahrnující polyorganosiloxany nebo elastomery polydimetylsiloxanu, nebo 0,5 až 10 % hmot, akrylátové, nebo styrenakrylátové disperze, zbytek do 100 % hmot, tvoří odsolená voda.Silica solution for the first silikátování plasters and ίο characterized in that it comprises a mixture of potassium water glass solution, water solution of colloidal silica having a molar ratio SiO 2 / K 2 O is 3.5 to 9, the dry matter of from 5 to 20% by weight, based on the two components only, 0.01 to 0.5% by weight of potassium pyrophosphate and / or 0.1 to 3% by weight of an active hydrophobic substance selected from the group consisting of polyorganosiloxanes or polydimethylsiloxane elastomers, or 0.5 up to 10% by weight of acrylate or styrene acrylate dispersions, the remainder up to 100% by weight being desalinated water. 2. Křemičitý roztok podle nároku 1, vyznačující se tím, že polyorganosiloxany obsahují ve vodě rozpustné alkalické soli dimetyl-, difenyl-, metyl-, fenyl-silanolátu.The silica solution according to claim 1, wherein the polyorganosiloxanes comprise water-soluble alkali salts of dimethyl, diphenyl, methyl, phenyl silanolate. 3. Křemičitý roztok podle nároku 1, vyznačující se tím, že elastomery polydimetylsiloxanu jsou ve formě vodné suspenze.The silica solution of claim 1, wherein the polydimethylsiloxane elastomers are in the form of an aqueous suspension. 4. Křemičitý roztok podle nároku 1, vyznačující se tím, že aktivní hydrofobní substance je použita v množství 0,5 až 1 % hmot, vztaženo na celkovou hmotnost směsi.The silica solution according to claim 1, characterized in that the active hydrophobic substance is used in an amount of 0.5 to 1% by weight, based on the total weight of the mixture. 5. Křemičitý roztok podle nároku 1, vyznačující se tím, že akrylátová nebo styrenakrylátové disperze je obsa-3CZ 280306 B6 žena v množství 2 až 5 % hmot, vztaženo na celkovou hmotnost směsi.The silica solution according to claim 1, wherein the acrylate or styrene acrylate dispersion is present in an amount of 2 to 5% by weight, based on the total weight of the composition. 6.6. Křemičitý roztok podle nároku 1, vyznačující tím, že molární poměr SiO2/K2O je 6 až 8.The silica solution of claim 1, wherein the SiO 2 / K 2 O molar ratio is 6-8. Křemičitý roztok podle nároku 1, vyznačující tím, že sušina tvoří 10 až 15 % hmot.The silica solution according to claim 1, wherein the dry matter comprises 10 to 15 wt. 8. Křemičitý roztok podle nároku 1, vyznačující se tím, že difosforečnan draselný je použit v množství 0,05 až 0,1 % hmot, vztaženo na celkovou hmotnost směsi.8. The silica solution of claim 1 wherein the potassium pyrophosphate is used in an amount of 0.05 to 0.1% by weight based on the total weight of the composition.
CS922851A 1992-09-17 1992-09-17 Silicate solution for treating elevation plasters CZ280306B6 (en)