CZ24184U1 - Composite based on polyurethane sealing compound exhibiting increased wear resistance - Google Patents
Composite based on polyurethane sealing compound exhibiting increased wear resistance Download PDFInfo
- Publication number
- CZ24184U1 CZ24184U1 CZ201226283U CZ201226283U CZ24184U1 CZ 24184 U1 CZ24184 U1 CZ 24184U1 CZ 201226283 U CZ201226283 U CZ 201226283U CZ 201226283 U CZ201226283 U CZ 201226283U CZ 24184 U1 CZ24184 U1 CZ 24184U1
- Authority
- CZ
- Czechia
- Prior art keywords
- wear resistance
- composite
- polyurethane
- increased wear
- composite based
- Prior art date
Description
Oblast techniky
Technické řešení se týká kompozitu na bázi polyuretanové zalévací hmoty se zvýšenou odolností proti opotřebení. Kompozit je tvořen polyuretanovou zalévací hmotou (matrice), do které jsou přidány ve vhodném množství vhodně veliké částice (plnivo) vhodně vybraných nekovových a/nebo kovových materiálů.
Dosavadní stav techniky
Polyuretanová zalévací hmota je dvousložková hmota, sestávající z pryskyřice a tužidla. Sama o sobě má relativně nízkou odolnost proti opotřebení. Tento její nedostatek lze v případě potřeby snadno odstranit přidáním částic dalšího nebo dalších materiálů. Konkrétní výsledné vlastnosti materiálu lze ovlivňovat množstvím přidaných částic, jejich velikostí a také druhem materiálu, ze kterého jsou částice vyrobeny.
Podstata technického řešení
Kompozit na bázi polyuretanové zalévací hmoty se zvýšenou odolností proti opotřebení je tvořen matricí na bázi polyuretanové zalévací hmoty a plnivem ve formě částic, přičemž matrice v kompozitu je nejméně 60 % hmotnostních. Plnivo je tvořeno kombinací směsi nekovových a/nebo kovových částic granátu a/nebo karborunda a/nebo kostěné drtě a/nebo sody a/nebo drcených vajíčkových skořápek a/nebo zirblastu a/nebo litinového granulátu a/nebo ocelové drtě, přičemž v kompozitu je vždy použito nejméně dvou z výše uvedených druhů částic. Největší ze tří rozměrů částic je v rozmezí od 0,05 mm do 5 mm. Měrná hmotnost kompozitu na bázi polyuretanové zalévací hmoty je v rozmezí od 1000 do 4200 kg.m3.
Příklady provedení technického řešení
Příklady složení kompozitu na bázi polyuretanové zalévací hmoty se zvýšenou odolností proti opotřebení:
Příklad 1
- zalévací hmota
- granát
- karborundum % hmotnostních 25 % hmotnostních 15 % hmotnostních.
Příklad 2
- zalévací hmota
- kostěná drť
- soda % hmotnostních 15 % hmotnostních 15 % hmotnostních.
Příklad 3
- zalévací hmota
- drcené vajíčkové skořápky
- litinový granulát % hmotnostních 25 % hmotnostních % hmotnostních.
Příklad 4
- zalévací hmota
- granát
- karborundum
- ocelová drť % hmotnostních 10 % hmotnostních 10 % hmotnostních 10 % hmotnostních.
- 1 CZ 24184 Ul
Příklad 5 - zalévací hmota - kostěná drť - soda - zirblast 65 % hmotnostníchTechnical field
The technical solution relates to a composite based on polyurethane encapsulating material with increased wear resistance. The composite comprises a polyurethane encapsulant (matrix) to which suitably sized particles (filler) of suitably selected non-metallic and / or metallic materials are added in a suitable amount.
BACKGROUND OF THE INVENTION
Polyurethane encapsulating compound is a two-component compound consisting of resin and hardener. It itself has a relatively low wear resistance. This deficiency can be easily eliminated by adding particles of additional or additional materials, if necessary. The specific resulting properties of the material can be influenced by the amount of particles added, their size and the type of material from which the particles are made.
The essence of the technical solution
The polyurethane encapsulated composite with increased wear resistance is comprised of a polyurethane encapsulated matrix and a particulate filler, the matrix in the composite being at least 60% by weight. The filler is a combination of a mixture of non-metallic and / or metal particles of garnet and / or carborundum and / or bone chippings and / or soda and / or crushed egg shells and / or zircblast and / or cast iron granules and / or steel chippings. at least two of the above-mentioned particle types are always used. The largest of the three particle sizes is in the range of 0.05 mm to 5 mm. The specific weight of the polyurethane encapsulating composite is in the range of 1000 to 4200 kg.m 3 .
Examples of technical solution
Examples of composites based on polyurethane encapsulating compound with increased wear resistance:
Example 1
- encapsulating compound
- grenade
- carborundum 25% by weight 15% by weight.
Example 2
- encapsulating compound
- bone chippings
- soda by weight 15% by weight 15% by weight.
Example 3
- encapsulating compound
- crushed egg shells
- cast iron granulate by weight 25% by weight.
Example 4
- encapsulating compound
- grenade
- carborundum
- steel pulp 10% by weight 10% by weight 10% by weight.
- 1 CZ 24184 Ul
Example 5 - encapsulant - bone crumb - soda - zirblast 65% by weightClaims (4)