CS269912B1 - Means for anti-inflammatory vaccination of ash - Google Patents

Means for anti-inflammatory vaccination of ash Download PDF

Info

Publication number
CS269912B1
CS269912B1 CS876652A CS665287A CS269912B1 CS 269912 B1 CS269912 B1 CS 269912B1 CS 876652 A CS876652 A CS 876652A CS 665287 A CS665287 A CS 665287A CS 269912 B1 CS269912 B1 CS 269912B1
Authority
CS
Czechoslovakia
Prior art keywords
parts
weight
ash
acid salts
oxides
Prior art date
Application number
CS876652A
Other languages
Czech (cs)
Other versions
CS665287A1 (en
Inventor
Josef Dipl Tech Coufal
Frantisek Vegricht
Ivan Ing Dana
Original Assignee
Josef Dipl Tech Coufal
Frantisek Vegricht
Ivan Ing Dana
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Josef Dipl Tech Coufal, Frantisek Vegricht, Ivan Ing Dana filed Critical Josef Dipl Tech Coufal
Priority to CS876652A priority Critical patent/CS269912B1/en
Publication of CS665287A1 publication Critical patent/CS665287A1/en
Publication of CS269912B1 publication Critical patent/CS269912B1/en

Abstract

Účelem prostředku je omezeni plynných sirnýoh exhalátů vznikajíoioh v topenií- ® tíoh průmyslovýoh, převážně energetiokýoh j kotlů, se současným snížením koefioientu zanesení teplosměnnýoh plooh těohto kotlů ze strany spalin. Uvedeného účinku se doj sáhuje prostředkem složeným z 1 až 1,5 hmotnostníoh dílů oxidů zinku, z 3 až 5 hmotnostních dílů solí kyseliny fosforečná, z 0,5 až 1,5 hmotnostníoh dílů oxidů mědi a to vSe doplněno na 1OO hmotnostních dílů solemi kyseliny chlorovodíková. Při použitá se prostředek dávkuje do spalovacího prooesu, kde očkuje vznikájíoí pope— loviny.The purpose of the agent is to reduce gaseous sulfur exhalates generated in the heating of industrial, mainly energy-generating boilers, with a simultaneous reduction in the coefficient of fouling of the heat exchange surfaces of these boilers from the flue gases. The stated effect is achieved by an agent composed of 1 to 1.5 parts by weight of zinc oxides, 3 to 5 parts by weight of phosphoric acid salts, 0.5 to 1.5 parts by weight of copper oxides, all supplemented to 100 parts by weight with hydrochloric acid salts. When used, the agent is dosed into the combustion process, where it inoculates the resulting ash.

Description

Vynález se týká prostředku k protiexhalátovému snížení obsahu oxidů síry v plynných exhalátech vznikajících spalováním fosilních paliv v topeništích průmyslových kotlů se současným snížením koeficientu zanesení teplosměnnýoh ploch těchto kotlů popelovinari ze strany spalin.The invention relates to a means for reducing the content of sulfur oxides in gaseous exhalates produced by the combustion of fossil fuels in the furnaces of industrial boilers, while simultaneously reducing the coefficient of clogging of the heat exchange surfaces of these boilers with ash from the flue gases.

Dosavadní známé technologie spalování fosilních paliv v topeništích průmyslových kotlů od sebe ve většině případů oddělují proces snížení exhalátů oxidů síry a proces snížení koeficientu zanesení teplosměnnýoh ploch. Vzrůst koeficientu zanesení ve svém důsledku zvySuje tvorbu oxidů síry předevěím zpětným sáláním nánosů popelovin do topeniště za současného snížení ůěinnosti kotelní Jednotky. Tím se také zvySuJe spotřeba paliva pro požadovaný výkon a tedy zvyšuje tvorbu dalších siraýoh exhalátů. Při nasazení suché aditivní metody odsíření, například přidáváním práškového uhličitanu vápenatého do topeniště, pak dochází ke snižování účinnosti odsiřovacího procesu. Uvádí se 15 až 20 £ využitého uhličitanu vápenatého. U kotelních Jednotek s teplotou v topeništi nad 1000 °C je to způsobeno mimo Ji- ‘ né i spókáním povrchu aktivních částic protože je známo, že vápenné přísady snižují teplotu měknutí popelovin. Tím vlastně dochází ke značné redukoi plochy, na které probíhá reakce vázání síry.The currently known technologies of burning fossil fuels in industrial boiler furnaces in most cases separate the process of reducing sulfur oxide exhalations and the process of reducing the fouling coefficient of heat exchange surfaces. The increase in the fouling coefficient consequently increases the formation of sulfur oxides, primarily by the back-radiation of ash deposits into the furnace, while simultaneously reducing the efficiency of the boiler unit. This also increases the fuel consumption for the required output and thus increases the formation of additional sulfur exhalations. When using a dry additive desulfurization method, for example by adding powdered calcium carbonate to the furnace, the efficiency of the desulfurization process is reduced. It is reported that 15 to 20% of the calcium carbonate used is used. In boiler units with a temperature in the furnace above 1000 °C, this is caused, among other things, by the sintering of the surface of the active particles, since it is known that lime additives reduce the softening temperature of ash. This actually results in a significant reduction in the surface area on which the sulfur binding reaction takes place.

Výše uvedené nedostatky podstatně zmírňují prostředek podle vynálezu Jehož podstata spočívá v tom, že je složen ze směsi o obsahu 1 až 1,5 hmotnostních dílů oxidů zinku, s výhodou oxidu zinečnatého (ZnO), z 3 až 5 hmotnostních dílů solí kyseliny fosforečné, s výhodou fosforečnanu sodného (NayO^), z 0,5 až 1,5 hmotnostních dílů oxidů mědi, s výhodou oxidu měďnatého (CuO), a to vše doplněno na 100 hmotnostních dílů solemi kyseliny chlorovodíkové, s výhodou 35 až 45 hmotnostních dílů chloridu amonného (NH^Cl) a 46 až 60,5 hmotnostních dílů chloridu sodného (NaCl) a .chlorIdu draselného (KC1) v surovém stavu.The above-mentioned shortcomings are significantly alleviated by the composition according to the invention, the essence of which lies in the fact that it is composed of a mixture containing 1 to 1.5 parts by weight of zinc oxides, preferably zinc oxide (ZnO), 3 to 5 parts by weight of phosphoric acid salts, preferably sodium phosphate (Na2O3), 0.5 to 1.5 parts by weight of copper oxides, preferably copper oxide (CuO), and all this supplemented to 100 parts by weight with hydrochloric acid salts, preferably 35 to 45 parts by weight of ammonium chloride (NH2Cl) and 46 to 60.5 parts by weight of sodium chloride (NaCl) and potassium chloride (KCl) in the raw state.

Při použití se prostředek dávkuje do spalovacího prooesu, kde očkuje vznikající popělo viny.When used, the agent is dosed into the combustion process, where it inoculates the resulting ash.

Výhodou prostředku podle vynálezu Je předevěím to, že vyvolává zvýšenou vyzbu síry na popeloviny a chemická aditiva za současného narušování kondenzačních řetězců křemičitanů v popelovináoh, projevující se absencí skelné fáze popelovin v Její základní podobě. Tím dojde i ke snížení pevnosti popelovin projevující se mimo jiné i zlepšením rozpojování pevné fáze popelovin.The advantage of the composition according to the invention is primarily that it causes increased sulfur deposition on the fly ash and chemical additives while simultaneously disrupting the condensation chains of silicates in the fly ash, manifested by the absence of the glass phase of the fly ash in its basic form. This also results in a reduction in the strength of the fly ash, manifested, among other things, by improving the separation of the solid phase of the fly ash.

Ve svém důsledku toto nasazení působí systémově na oelý spalovací trakt kotle, nebol nejenom snižuje emiee oxidů síry, ale snižuje i ztráty v přestupu tepla snížením koeficientu zanesení teplosměnnýoh ploch popelovinami ze strany spalin. Snížená mechanická pevnost pep*levin usnadňuje čistění moderními metodami, například působením akustického tlaku, tím ovlivňuje nepřímo teplotu spalovacího prooesu směrem k nižěím hodnotám a tím také umožňuje průběh hoření blížíoí se podmínkami fluidnímu spalování. Včetně odpovídající vazby síry na popelovlny, předevěím na oxid vápenatý vzniklý kalcinací malých množství uhličitanu vápenatého, který Je v mnoha druzíoh vysokopopelnatého uhlí obsažen. Zvyšuje se i vazba síry na křemičitany obdobně jako je tomu u simatých sklářských kmenů a strusek.As a result, this application has a systemic effect on the entire combustion tract of the boiler, as it not only reduces the emission of sulfur oxides, but also reduces heat transfer losses by reducing the coefficient of clogging of heat exchange surfaces with ash from the flue gas side. The reduced mechanical strength of the ash facilitates cleaning by modern methods, for example, by the action of acoustic pressure, thereby indirectly affecting the temperature of the combustion process towards lower values and thus also enabling the course of combustion approaching the conditions of fluidized combustion. Including the corresponding binding of sulfur to ash clouds, especially to calcium oxide formed by calcination of small amounts of calcium carbonate, which is contained in many other high-ash coals. The binding of sulfur to silicates also increases, similar to that of glass-making slags and slags.

Výhodou prostředku podle vynálezu je i to, že jej lze kombinovat, nebo jím doplnit některé známé metody odsíření, které tak intenzifikuje. Především jej lze kombinovat se suchou aditivní metodou odsíření, v níž zlepšuje využití dávkovaného uhličitanu vápenatého. 'The advantage of the composition according to the invention is that it can be combined with or supplemented with some known desulfurization methods, which it intensifies. In particular, it can be combined with the dry additive desulfurization method, in which it improves the utilization of dosed calcium carbonate. '

Podstata vynálezu bude blíže osvětlena v dále uvedených příkladech, které však neomezují rozsah vynálezu. Díly v příkladech uváděné Jsou hmotnostní.The invention will be further illustrated in the following examples, which do not, however, limit the scope of the invention. The parts in the examples are by weight.

CS 269 9t2 BtCS 269 9t2 Bt

Příklad 1Example 1

Prostředek byl složen z 1 dílu oxidu zinečnatého, z 3 dílů fosforečnanu sodného, z 1 dílu oxidu měňnatého, ze 40 dílů ohloridu amonného a 55 dílů chloridu sodného a. chloridu draselného. Získaná směs byla přiváděna do spalovacího procesu v množství 200 g- na tunu paliva, kterým bylo vysokopopelnaté hnědé uhlí spalované v práškovém topeništi- Mezi oxidy získanými z paliva bylo 2,6 % CaO a 1,77 5^ SO^. Během dávkování přípravku· bylo ve strusoe zjištěno 2,8 CaO a 1,19 % soj, před dávkováním etruská obsahovala 2,82 CaO a 1,01 % SOyThe composition consisted of 1 part zinc oxide, 3 parts sodium phosphate, 1 part manganese oxide, 40 parts ammonium chloride and 55 parts sodium chloride and potassium chloride. The resulting mixture was fed into the combustion process in an amount of 200 g per ton of fuel, which was high-ash brown coal burned in a pulverized furnace. Among the oxides obtained from the fuel were 2.6% CaO and 1.775 SO. During the dosing of the composition, 2.8 CaO and 1.19% SO were found in the slurry, before dosing the Etruscan contained 2.82 CaO and 1.01% SO.

Příklad 2Example 2

Prostředek ve složení jako v příkladu 1 byl použit v laboratorním pokusu simulujícím proces slinutí popelovin vznikajících při nasazení suché aditivní metody odsíření. Je známo, že uhličitan vápenatý snižuje teplotu mčknutí popelovin s následnou tvorbou * tvrdých a sklovitých strusek. Prostředek podle vynálezu byl přidán do hnědého uhlí v množství odpovídajícím 100 g prostředku na tunu paliva. Obsah uhličitanu vápenatého byl v palivu zvýšen na 10 £ a smšs všech zúčastněných komponentů byla rozemleta a homogenizována a následně v laboratorní píooe vystavena teplotě 1200 °C. Po vyhoření paliva byla vzniklá struska zchlazena. Měla jemně krystalickou strukturu se snadným rozpojováním. Obsah oxidů ve strusoe nebyl zjišíován. .The composition of the agent as in Example 1 was used in a laboratory experiment simulating the process of sintering of fly ash resulting from the use of a dry additive desulfurization method. It is known that calcium carbonate reduces the softening temperature of fly ash with the subsequent formation of * hard and glassy slags. The agent according to the invention was added to brown coal in an amount corresponding to 100 g of the agent per ton of fuel. The calcium carbonate content in the fuel was increased to 10 £ and the mixture of all the components involved was ground and homogenized and subsequently exposed to a temperature of 1200 °C in a laboratory furnace. After the fuel burned out, the resulting slag was cooled. It had a finely crystalline structure with easy separation. The oxide content in the slag was not determined. .

Claims (1)

Prostředek k protiexhalátovému očkování popelovin snižující tvorbu oxidů síry především průmyslových kotlů spalujících pevná fosilní paliva se současným účinkem na snížení koeficientu zanesení teplosměnných ploch ze strany spalin, vyznačený tím, že Je složen z 1 až 1,5 hmotnostních dílů oxidů zinku, s výhodou oxidu zinečnatého ZnO, z 3 až 5 hmotnostních dílů solí kyseliny fosforečné, s výhodou fosforečnanu sodného Na^PO^, z 0,5 až 1,5 hmotnostních dílů oxidů mědi, s výhodou oxidu mědnatého CuO a to vše doplněno na 100 hmotnostních dílů solemi kyseliny chlorovodíkové, s výhodou 35 až 45 hmotnostních dílů chloridu amonného NH^Cl a 46 až 60,5 hmotnostních dílů ohloridu sodného NaCl a chloridu draselného KC1 v surovém stavu.An agent for anti-exhalation inoculation of ash, reducing the formation of sulfur oxides, especially in industrial boilers burning solid fossil fuels, with a simultaneous effect on reducing the fouling coefficient of heat exchange surfaces from the flue gas side, characterized in that it is composed of 1 to 1.5 parts by weight of zinc oxides, preferably zinc oxide ZnO, 3 to 5 parts by weight of phosphoric acid salts, preferably sodium phosphate Na^PO^, 0.5 to 1.5 parts by weight of copper oxides, preferably cupric oxide CuO, and all of this supplemented to 100 parts by weight with hydrochloric acid salts, preferably 35 to 45 parts by weight of ammonium chloride NH^Cl and 46 to 60.5 parts by weight of sodium chloride NaCl and potassium chloride KC1 in the raw state.
CS876652A 1987-09-14 1987-09-14 Means for anti-inflammatory vaccination of ash CS269912B1 (en)