CS265461B1 - Sizing agent - Google Patents
Sizing agent Download PDFInfo
- Publication number
- CS265461B1 CS265461B1 CS862323A CS232386A CS265461B1 CS 265461 B1 CS265461 B1 CS 265461B1 CS 862323 A CS862323 A CS 862323A CS 232386 A CS232386 A CS 232386A CS 265461 B1 CS265461 B1 CS 265461B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- sizing
- styrene
- mixtures
- native
- acrylic acid
- Prior art date
Abstract
šlichtovaoího prostředku ke šlichtování přízí z chemických a nativních vláken a jejich směsí sestávajícího ze sodné nebo draselné soli kopolymeru styrenu, maleinanhydridu a kyseliny akrylové, esterifikovaného dvou až pěti funkčními C2-5 alkoholy nebo jejich směsí lze využít ve všech textilních závodech pro příze z chemických a nativních vláken a jejich směsi, určené pro zpracování tkací technikou v bavlnářském, lnářském a vlnařském průmyslu.sizing agent for sizing yarn of chemical and native fibers; mixtures thereof consisting of sodium or potassium salts of a styrene-maleic anhydride copolymer and acrylic acid esterified two to five functional C2-5 alcohols or their blends can be used in all textile fabrics chemical and native yarn plants fibers and mixtures thereof for processing weaving technique in cotton, flax and wool industry.
Description
Předmětem vynálezu je šlichtovaeí prostředek určený pro šlichtování přízí z chemických a nativních vláken a jejich směsí, zpracovaných tkací technikou, pozůstávající z kopolymeru styrenu, maleinanhydridu a kyseliny akrylové, esterifikovaného dvou až pěti funkčními alkoholy a neutralizovaného hydroxidem alkalického kovu. a<».· přtThe present invention relates to a sizing composition for sizing yarns of chemical and native fibers and mixtures thereof, processed by a weaving technique, consisting of a copolymer of styrene, maleic anhydride and acrylic acid, esterified with two to five functional alcohols and neutralized with an alkali metal hydroxide. and <»
W:thjW: th j
Šlichtování je pracovní operace v jejímž průběhu se na osnóvní nitě v přípravě' pro tkaní nanáSí nativní a syntetické polymery případně jejich směsi za účelem zpevnění a uhlazení, což je podmínkou pro technicky a ekonomicky vyhovující zpracovatelnost.Sizing is a process during which native and synthetic polymers, or mixtures thereof, are applied to the warp threads in the weaving preparation for consolidation and smoothing, which is a precondition for technically and economically satisfactory processability.
Významnou skupinu mezi šlichtovacími prostředky tvoří kopolymery styrenu (USA patent č. 4 246.755, 2 872 436, čs. AO 197 640).An important group among sizing agents is styrene copolymers (U.S. Pat. No. 4,246,755, 2,872,436, AO 197,640).
Nevýhodou těchto prostředků je nedostatečná adheze k vláknu, což má nepříznivý technologický dopad zejména při zpracování osnov na vysokovýkonných tkacích strojích. Nevyhovující je rovněž biologická rozložitelnost v odpadních vodách, což je závažný nedostatek z hlediska současných ekologických požadavků.The disadvantage of these compositions is the insufficient adhesion to the fiber, which has an unfavorable technological impact, especially when processing the warps on high-performance weaving machines. Biodegradability in waste water is also unsatisfactory, a serious shortcoming in terms of current environmental requirements.
Výše uvedené nevýhody řeší prostředek dle vynálezu pozůstávající ze sodné nebo draselné soli kopolymeru styrenu, maleinanhydridu a kyseliny akrylové (v molárním poměru 1:0,9:0,09 až 1:1,1:0,4), esterifikovaného vztaženo na mol styrenu 0,9 až 1,2 mol dvou až pěti funkčního alkoholu s 2 až 5 atomy uhlíku nebo jejich směsí (například pentaerythritem, glycerinem nebo glykolem).The above disadvantages are solved by a composition according to the invention consisting of the sodium or potassium salt of a copolymer of styrene, maleic anhydride and acrylic acid (in a molar ratio of 1: 0.9: 0.09 to 1: 1.1: 0.4), esterified based on mol of styrene 0.9 to 1.2 moles of two to five functional C 2 to C 5 alcohols or mixtures thereof (for example, pentaerythritol, glycerin or glycol).
Adheze se obvykle vyjadřuje jako hodnota deformační práce ošlichtováných přástů. Biologická rozložitelnost se vyjadřuje poměrem BSK5:CHSK. Při poměru BSK5:CHSKŽ0,1 jsou přípravky považovány za biologicky odbouratelné aktivovanými kaly. Poměr BSK5:CHSK, zjištěný u prostředku podle vynálezu, znamená podstatné zlepšení čietitelnosti odpadních vod z textilních závodů.Adhesion is usually expressed as the value of the deformation work of the seamed yarns. Biodegradability is expressed as BOD5: COD ratio. At a BOD5: COD1.1 ratio, the preparations are considered biodegradable by activated sludge. The BOD5: COD ratio found with the composition according to the invention means a substantial improvement in the legibility of the waste water from textile plants.
Porovnáním hodnot adheze a biologické rozložitelnosti pro celou paletu prostředků tohoto typu (lišící se druhem vícefunkčního alkoholu, používaného pro esterifikací) bylo zjištěno, že jednotlivé naměřené hodnoty se pohybují v úzkém rozmezí. Soubor typických hodnot je uveden v tabulce.By comparing the adhesion and biodegradability values for a whole range of formulations of this type (differing in the type of multifunctional alcohol used for esterification), it was found that the individual measured values were within a narrow range. A set of typical values is given in the table.
TabulkaTable
Stávající šlichtovaeí Prostředek dle vynálezu prostředek na bázi kopolymeru styrenuExisting Sizing Composition The present invention is a styrene copolymer composition
Další výhodou prostředku dle vynálezu je jeho neomezená mísitelnost s jinými šlichtovacími prostředky, zejména se všemi typy škrobů nativních a modifikovaných, polyvinylalkoholem a karboxymethylcelulozou. To umožňuje vytváření směsných šlicht různého typu.A further advantage of the composition according to the invention is its unrestricted miscibility with other sizing agents, in particular all types of native and modified starches, polyvinyl alcohol and carboxymethylcellulose. This allows the formation of mixed sizes of various types.
Použití prostředku dle vynálezu jsou podrobněji osvětlena na příkladech provedení, jimiž však předmět vynálezu není omezen.The use of the composition according to the invention is illustrated in more detail by way of examples, but not by way of limitation.
Přikladl šlichtovaeí prostředek pozůstávající ze sodné soli kopolymeru styren-maleinanhydrid - kyselina akrylová (mol poměr 1:1:0,1), esterifikované 1,09 mol glycerinu.Example 1 is a sizing composition consisting of sodium salt of styrene-maleic anhydride-acrylic acid copolymer (1: 1: 0.1 mole ratio), esterified with 1.09 mole glycerin.
K ošlichtovánl příze 25 tex 100 % bavlna (klasický výpřed) se použije lázně obsahující na 100 1: 6,00 kg šlichtovacího prostředku uvedeného složeníFor sizing 25 tex 100% cotton (classic spun) a bath containing 100 l: 6.00 kg of sizing composition of the following composition is used
Příklad 2Example 2
Slichtovací prostředek pozůstávající z draselné soli kopolymeru styren-maleinanhydrid - kyselina akrylová (mol poměru 1:1:0,2), esterifikované 1 mol glycerinu.Sizing composition consisting of potassium salt of styrene-maleic anhydride-acrylic acid copolymer (1: 1: 0.2 mole) esterified with 1 mole of glycerin.
».».
K ošlichtovánl příze 29,5 tex'40 % VSs/60 % bavlna (BD výpřed) se použije lázeň obsahující na 100 1: 2,5 kg šlichtovacího prostředku uvedeného složeniA bath containing 100 l: 2.5 kg of a sizing composition of the following composition is used to sieve the yarn 29.5 tex -40% VSs / 60% cotton (BD sputter).
Příklad3Example3
Slichtovací prostředek pozůstávající z sodné soli kopolymeru styren-maleinanhydrid kyselina akrylová (mol poměru 1:0,9:0,2) esterifikované 1,1 mol pentaerythritu.Sizing composition consisting of sodium salt of styrene-maleic anhydride acrylic acid (1: 0.9: 0.2 mole) esterified with 1.1 mole of pentaerythrite.
K ošlichtování příze 35,5 tex, 100 % VSs (klasický výpřed) se použije lázně obsahující na 100 1: 2,25 kg šlichtovacího prostředku uvedeného složeníFor sizing 35.5 tex, 100% VSs (classic spin), use a bath containing 100 l: 2.25 kg of sizing composition of the following composition
PřikládáHe attaches
Slichtovací prostředek pozůstávající z draselné soli kopolymeru styren-maleinanhydridSizing agent consisting of the potassium salt of a styrene-maleic anhydride copolymer
- kyselina akrylová (v mol poměru 1:0,9:0,4), esterifikované 1,2 mol pentaerythritu. K ošlichto vání příze 29,5 tex, 40 % VSs/60 % bavlna (klasický výpřed) se použije lázně obsahující na 100 1: 3,00 kg karboxymetylcelulózyacrylic acid (in a ratio of 1: 0.9: 0.4), esterified with 1.2 mol of pentaerythritol. A bath containing 100 l: 3.00 kg of carboxymethylcellulose is used to suture the 29.5 tex, 40% VSs / 60% cotton (classic spin) yarn.
2,00 kg šlichtovacího prostředku uvedeného složení2.00 kg of a sizing composition of this composition
Příklad 5Example 5
Slichtovací prostředek pozůstávající ze sodné soli kopolymeru styren-maleinanhydrid - kyselina akrylová (v mol poměru 1:1,1:0,09), esterifikované 1,18 mol glykolu.Sizing composition consisting of sodium salt of styrene-maleic anhydride-acrylic acid copolymer (in a ratio of 1: 1.1: 0.09 mol), esterified with 1.18 mol of glycol.
K ošlichtování příze 20 tex, 65 % PESs/35 % bavlna (klasický výpřed) se použije lázně obsahující na 100 1: 1,60 kg oxidovaného škrobu bramborovéhoFor sizing 20 tex, 65% PESs / 35% cotton (classic spin), a bath containing 100 l: 1.60 kg of oxidized potato starch is used
7,00 kg šlichtovacího prostředku uvedeného složení7.00 kg of the sizing composition of said composition
Slichtovací prostředek dle vynálezu lze v širokém měřítku využít ve všech textilních závodech, kde se šlichtuji příze z chemických a nativních vláken a jejich směsí určených pro zpracování tkaci technikou v bavlnářském, lnářském a vlnařském průmyslu.The sizing composition according to the invention can be widely used in all textile plants, in which the yarns of chemical and native fibers and their mixtures intended for processing by the weaving technique in the cotton, linen and wool industry are sized.
Claims (2)