CS259644B1 - Lubrication for treatment of glass fibers - Google Patents

Lubrication for treatment of glass fibers Download PDF

Info

Publication number
CS259644B1
CS259644B1 CS872584A CS258487A CS259644B1 CS 259644 B1 CS259644 B1 CS 259644B1 CS 872584 A CS872584 A CS 872584A CS 258487 A CS258487 A CS 258487A CS 259644 B1 CS259644 B1 CS 259644B1
Authority
CS
Czechoslovakia
Prior art keywords
lubrication
glass fibers
weight
polyester resin
molecular weight
Prior art date
Application number
CS872584A
Other languages
Czech (cs)
Other versions
CS258487A1 (en
Inventor
Zdenek Bogdan
Jaroslav Faltys
Original Assignee
Zdenek Bogdan
Jaroslav Faltys
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zdenek Bogdan, Jaroslav Faltys filed Critical Zdenek Bogdan
Priority to CS872584A priority Critical patent/CS259644B1/en
Publication of CS258487A1 publication Critical patent/CS258487A1/en
Publication of CS259644B1 publication Critical patent/CS259644B1/en

Abstract

Řešení se týká oboru povrchové úpravy skleněných vláken přímou lubrikací, která nemusí být z vláken odstraňována. Lubrikace spočívá v tom, že jako její filmotvorné složky je použito kombinace polyvinylacetátu s nasycenou nízkomolekulární polyesterovou pryskyřicí v hmotnostním poměru 1 ku 1 až 5 ku 1. Jako vazného prostředku může být použito buď 0,1 až 3. % hmot. organokřemičitých sloučenin nebo 0,5 až 5 % hmot. chromového komplexu kyseliny metakrylovéThe solution relates to the field of surface treatment of glass fibers by direct lubrication, which does not have to be removed from the fibers. The lubrication consists in the fact that as its film-forming components a combination of polyvinyl acetate with a saturated low molecular weight polyester resin is used in a weight ratio of 1 to 1 to 5 to 1. As a binding agent, either 0.1 to 3. % by weight of organosilicon compounds or 0.5 to 5 % by weight of chromium complex of methacrylic acid can be used.

Description

Vynález, se týká lubrikace pro úpravu skleněných vláken, obsahující vodnou disperzi filmotvorných složek, mazacích složek, tenzidu, vazného a antistatického prostředku a regulátoru pH.The invention relates to a lubrication for treating glass fibers, comprising an aqueous dispersion of film-forming components, lubricating components, a surfactant, a binding and antistatic agent, and a pH regulator.

Skleněná vlákna se vyrábějí tak, že se roztavená sklovina přesně stanoveného složení odtahuje vysokou rychlostí z určitého počtu trysek umístěných ve dně platinové tavící pícky. Takto vyrobená skleněná vlákna se sdružují pomocí sdružovacího zařízení do pramene rovnoběžných vláken a navíjejí se na otáčivý buben. Pro umožnění dalšího textilního zpracování se vlákna povrchově upravují lubrikacemi, které se aplikují již při jejich tažení a tvarování ve formě vodných roztoků nebo emulzí. V moderních výrobnách vláken se nejčastěji setkáváme s lubrikacemi přímými — plastikářskými a nepřímými — textilními. Rozdíl mezi nimi je v tom, že přímé lubrikace tvoří funkční složku vláken 1 výrobků z nich, kdežto nepřímé lubrikace chrání vlákna jen dočasně, umožňují pouze jejich textilní zpracování do tkanin a potom jsou z nich odstraněny vypráním nebo vypálením. Přímé lubrikace předávají pramenům skleněných vláken soudržnost při zpracování a určují výsledný charakter rovingu s ohledem na další technologie zpracování, jako je výroba sklolaminátů metodou přesného navíjení, tažení profilů, výroba sklolaminátů sekáním rovingů při strojním nanášení nebo výroba sklolaminátů kontaktním laminováním rovingových tkanin. Pro uvedené technologické aplikace je nutno doposud skleněná vlákna upravovat různými lubrikacemi, které jim předávají požadované vlastnosti. Používá se dvou až tří lubrikací lišících se koncentračně i obsahově s ohledem na výsledný charakter rovingu. Běžně se používají přímé lubrikace o obecném složeni:Glass fibers are produced by drawing molten glass of precisely defined composition at high speed from a certain number of nozzles located in the bottom of a platinum melting furnace. The glass fibers produced in this way are combined using a combining device into a strand of parallel fibers and wound onto a rotating drum. To enable further textile processing, the fibers are surface-treated with lubrications that are applied during their drawing and shaping in the form of aqueous solutions or emulsions. In modern fiber production plants, we most often encounter direct — plastic — and indirect — textile lubrications. The difference between them is that direct lubrications form a functional component of the fibers and products made from them, while indirect lubrications protect the fibers only temporarily, only allowing their textile processing into fabrics and then are removed from them by washing or burning. Direct lubrications impart cohesion to the glass fiber strands during processing and determine the resulting character of the roving with respect to other processing technologies, such as the production of fiberglass by the method of precise winding, drawing profiles, the production of fiberglass by cutting rovings during machine application or the production of fiberglass by contact lamination of roving fabrics. For the above technological applications, it is still necessary to treat the glass fibers with various lubrications that impart the required properties to them. Two to three lubrications are used, differing in concentration and content with respect to the resulting character of the roving. Direct lubrications with a general composition are commonly used:

% hmot.% wt.

filmotvorná složka filmmaking component 3,0 c 3.0 c iž J from J 0.0 0.0 vazná složka binding component 0,1 0.1 until 5,0 5.0 mazací složka lubricant 0,01 0.01 until 2.0 2.0 tenzid surfactant 0,0 0.0 until 0,5 0.5 antistatické látky antistatic agents 0,0 0.0 until 1,0 1.0 regulátory pH pH regulators 0,0 0.0 until 0,3 0.3 voda water do 100,0 up to 100.0

Z filmotvorných látek, jejichž funkce spočívá v tom, že chrání povrch skleněných vláken a slepí je v jeden pramen, jsou uváděny polyesterové pryskyřice (francouzský pat. č. 1 255 793 a č. 1 350 771, pat. USA č. 3 428 518), případně modifikované olejem (francouzský pat. č. 1191102), dále epoxidové pryskyřice (francouzský patent čís. 2 110 469 a č. 2 318 833, japonský patent č. 7 705 391), nebo polyvinylacetátové disperze (pat. USA č. 3 116 192 a č. 3 969 299 a japonský pat. č. 7 635 799], butadienstyrenové latexy (pat. USA č. 3 025 588, pat. NSR č. 1052 354) a kopolyméry etylénoxidu a propylenoxidu, případně nízkomolekulární sminoamidové nebo aminoimidové pryskyřice.Film-forming substances, whose function is to protect the surface of glass fibers and glue them into one strand, include polyester resins (French Pat. No. 1,255,793 and No. 1,350,771, US Pat. No. 3,428,518), possibly modified with oil (French Pat. No. 1,191,102), epoxy resins (French Pat. No. 2,110,469 and No. 2,318,833, Japanese Pat. No. 7,705,391), or polyvinyl acetate dispersions (US Pat. No. 3,116,192 and No. 3,969,299 and Japanese Pat. No. 7,635,799), butadiene-styrene latexes (US Pat. No. 3,025,588, German Pat. No. 1052 354) and copolymers of ethylene oxide and propylene oxide, or low molecular weight aminoamide or aminoimide resins.

Jako mazacích látek v přímých lubrikacích je používáno převážně kationaktívních látek, které velmi dobře lnou k anionaktivnímu povrchu skleněných vláken. Jsou to amidy mastných nenasycených i nasycených kyselin, kde kyselá skupina obsahuje 4 až 24 atomy uhlíku, zejména kyselina pelargonová, kyselina stearová, kyselina palmitová nebo kyselina olejová. Zvláště se osvědčila mazadla, která vznikla reakcí tetraetylénpentaminu či dietyléntriaminu s mastnými kyselinami, jako kyselinou stenrovou nebo kyselinou olejovou.As lubricants in direct lubrication, mainly cationic substances are used, which adhere very well to the anionic surface of glass fibers. These are amides of unsaturated and saturated fatty acids, where the acid group contains 4 to 24 carbon atoms, especially pelargonic acid, stearic acid, palmitic acid or oleic acid. Lubricants formed by the reaction of tetraethylenepentamine or diethylenetriamine with fatty acids, such as stearic acid or oleic acid, have proven particularly effective.

Vazných prostředků, které jsou schopny zprostředkovat vazbu na mezních plochách mezi sklem a laminačuí pryskyřicí, je uváděna celá řada. Patří sem silanové a siloxanové látky, jako např. vinyl-, alkoxy-, amino-, epoxy-, acyloxy-, nebo metakryl-sllany, mající na druhé straně hydrolyzovatelné skupiny alkoxy nebo halogenové, jako gama-metakryloxypropyltrimetoxysilan, gama-aminopropyltrletoxysilan nebo gama-glycidoxypropyltrimetoxysilan.A wide variety of coupling agents are reported that are capable of mediating bonding at the interfaces between glass and laminating resin. These include silane and siloxane substances, such as vinyl, alkoxy, amino, epoxy, acyloxy, or methacrylic silanes, having on the other side hydrolyzable alkoxy or halogen groups, such as gamma-methacryloxypropyltrimethoxysilane, gamma-aminopropyltrimethoxysilane, or gamma-glycidoxypropyltrimethoxysilane.

Další skupinou vazných prostředků jsou komplexní sloučeniny Wernerova typu, kde trojmocný atom jádra např. chrómu je koordinován s organickou sloučeninou, jako je např. kyselina metakrylová za vzniku dichlorchrommetakrylátu. Tento produkt v jistých kombinacích působí též jako antistatický prostředek při povrchových úpravách skleněných vláken.Another group of binding agents are complex compounds of the Werner type, where a trivalent atom of the core, e.g. chromium, is coordinated with an organic compound, such as methacrylic acid, to form dichlorochromium methacrylate. This product, in certain combinations, also acts as an antistatic agent in the surface treatment of glass fibers.

Za účelem lepší smáčivosti a rozprostíratelnosti na povrchu skleněných vláken při velkých odtahových rychlostech jsou lubrikace doplněny o tenzidy typu alkyl-fenolpolyglykol-éteru nebo etylénoxidovaných aduktů kationaktivní povahy.For better wettability and spreadability on the surface of glass fibers at high draw-off speeds, the lubrications are supplemented with surfactants of the alkylphenolpolyglycol ether type or ethylene-oxidized adducts of cationic nature.

Jako regulátorů pH, jehož hodnota se má u přímých lubrikací pohybovat v rozmezí pH 3 až 5, je používáno kys. octové, eventuálně vodného roztoku amoniaku.Acetic acid, or possibly an aqueous solution of ammonia, is used as a pH regulator, the value of which should be in the range of pH 3 to 5 for direct lubrication.

Polyvinylacetátové disperze mívají zřídka vlastnosti požadované pro příslušné aplikace. Při použití na přípravu lubrikací, které musí předávat skleněným vláknům vlastnosti požadované od finálního výrobku, je nutná jejich modifikace k dosažení požadované elasticity a rozpustnosti v laminačních pryskyřicích. Tento postup je však velmi omezen, neboť ani látky, které si jsou chemicky velmi podobné, se ne vždy, navzájem mísí. Některá změkčovadla, jako dibutylsebakát, migrují do částic polymeru velmi pomalu i za zvýšených teplot. Možnosti využití vnější plastifikace jsou omezené a hlavní nevýhoda spočívá v migraci změkčovadla na povrch, což se v daném případě může projevit i sníženou rozpustností filmu upravených skleněných vláken v laminační pryskyřici.Polyvinyl acetate dispersions rarely have the properties required for the respective applications. When used for the preparation of lubricants, which must impart to the glass fibers the properties required for the final product, their modification is necessary to achieve the required elasticity and solubility in the laminating resins. However, this procedure is very limited, since even substances that are chemically very similar do not always mix with each other. Some plasticizers, such as dibutyl sebacate, migrate into the polymer particles very slowly even at elevated temperatures. The possibilities of using external plasticization are limited and the main disadvantage lies in the migration of the plasticizer to the surface, which in a given case may also be manifested by a reduced solubility of the film of treated glass fibers in the laminating resin.

Uvedené nevýhody se odstraní nebo podstatně omezí lubrikací pro povrchovou úpravu skleněných vláken podle tohoto vy259644 nálezu, jehož podstata spočívá v tom, že íilmotvornou složkou je polyvinylacetát s nasycenou nízkomolekulární polyesterovou pryskyřicí v hmotnostním poměru 1 ku 1 až o ku 1. Filmotvorná složka, kterou je nasycená nízkomolekulární polyesterová pryskyřice o střední molekulové hmotnosti M„ v rozmezí 1 000 až 2 000 s velikostí částic v rozmezí 0,1 až 5 mikrometrů, má obecný vzorecThe above disadvantages are eliminated or significantly reduced by the lubrication for the surface treatment of glass fibers according to this invention, the essence of which lies in the fact that the film-forming component is polyvinyl acetate with a saturated low-molecular polyester resin in a weight ratio of 1 to 1 to 0 to 1. The film-forming component, which is a saturated low-molecular polyester resin with an average molecular weight M n in the range of 1,000 to 2,000 with a particle size in the range of 0.1 to 5 microns, has the general formula

HOco (c^ coo kde n = 2 až 10, m = 1 až 10, x = 1 až 20, y = 1 až 15.HOco ( c ^ coo where n = 2 to 10, m = 1 to 10, x = 1 to 20, y = 1 to 15.

S výhodou lubrikace obsahuje 0,1 až 1 % hmot. vazného prostředku na bázi organokřemičitých sloučenin, nebo 0,5 až 5 % hmot. vazného a antistatického prostředku na bázi chromového komplexu kyseliny metakrylové.Preferably, the lubrication contains 0.1 to 1% by weight of a binding agent based on organosilicon compounds, or 0.5 to 5% by weight of a binding and antistatic agent based on a chromium complex of methacrylic acid.

Předložený vynález umožňuje vyrábět skleněná vlákna a rovingy pro všechny dříve uvedené technologie zpracování s jedinou lubrikací. Poměr polyvinylacetátu s nasycenou nízkomolekulární polyesterovou pryskyřicí podle vynálezu má velmi příznivý vliv na další zpracovatelnost upravených skleněných vláken. Zvolená nasycená nízkomolekulární polyesterová pryskyřice zvyšuje rozpustnost povrchového filmu lubrikace na skleněných vláknech při laminování, čímž je snížena pracnost laminování, eventuálně zkrácena jeho doba. Organokřemičiťé sloučeniny nebo chromový komplex kyseliny metakrvlové zabezpečují dobré spojení povrchu skleněných vláken s používanou laminační pryskyřicí a zajišťují optimální fyzikálně mechanické vlastnosti výsledných sklolaminátových výrobků.The present invention allows the production of glass fibers and rovings for all previously mentioned processing technologies with a single lubrication. The ratio of polyvinyl acetate to saturated low molecular weight polyester resin according to the invention has a very favorable effect on the further processability of the treated glass fibers. The selected saturated low molecular weight polyester resin increases the solubility of the surface film of lubrication on the glass fibers during lamination, thereby reducing the laboriousness of lamination, possibly shortening its time. Organosilicon compounds or chromium complex of metacrylic acid ensure good bonding of the glass fiber surface with the used lamination resin and ensure optimal physical and mechanical properties of the resulting fiberglass products.

Příkladné provedení lubrikace podle vynálezu je objasněno na dvou následujících příkladech provedení.An exemplary embodiment of the lubrication according to the invention is illustrated by the following two exemplary embodiments.

Příklad 1Example 1

Složky lubrikace Lubrication components Chemické složení Chemical composition % hmot. % wt. hlavní filmotvorná složka main film-making component polyvinylacetát ve vodné disperzi s obsahem sušiny 50 % hmot. polyvinyl acetate in aqueous dispersion with a dry matter content of 50% by weight. 5,0 5.0 vedlejší filmotvorná složka secondary filmmaking component polyesterová pryskyřice ve vodné disperzi s obsahem sušiny polypropylenglykolodipátu 50 % hmot. polyester resin in aqueous dispersion with a dry content of polypropylene glycol adipate of 50% by weight. 2,0 2.0 vazný a antistatický prostředek chromový komplex kyseliny metakrylové binding and antistatic agent chromium complex of methacrylic acid 1,2 1.2 tenzid surfactant nonylfenolpolyglykoléter s obsahem 10 °/o sušiny vc vodném roztoku nonylphenol polyglycol ether with a content of 10 °/o dry matter in an aqueous solution 1,0 1.0 mazací složka lubricant produkt získaný reakcí dietvléntriaminu s kyselinou olejovou s obsahem 3,13 % hmot. sušiny ve vodném roztoku product obtained by the reaction of diethyl ether triamine with oleic acid containing 3.13% by weight of dry matter in aqueous solution 2,4 2.4 regulátor pH pH regulator vodný roztok čpavku (1 % hmot. konc.) Aqueous ammonia solution (1% wt. conc.) 2,7 2.7 dispergační složka dispersant deionizovaná voda deionized water 85,7 85.7

Jako nasycené nízkomolekulární polyesterové pryskyřice bylo použito polypropylenglykoadipátu o vzorciPolypropylene glycoadipate with the formula was used as a saturated low molecular weight polyester resin.

COWHAT

-- COO-- COO

o střední molekulové hmotnosti Mn 1 500 a velikosti částic do 2 mikrometrů.with an average molecular weight M n 1,500 and a particle size of up to 2 micrometers.

Lubrikace se připraví smíšením výše uvedených složek v předepsané koncentraci podle běžně známých postupů. Při přípravě lubrikace je však nutno dokonale promísit obě vodné disperze filmotvorných složek, aby nedocházelo k jejich sedimentaci v konečné lubrikaci. Jako dispergační médium je možno použít běžnou pitnou vodu, nebo lépe vodu detonizovanou bez nežádoucích iontů například železa Fe, vápníku Ca apod., které mohou nepříznivě ovlivnit výsledné vlastnosti lubrikace.The lubrication is prepared by mixing the above-mentioned components in the prescribed concentration according to commonly known procedures. However, when preparing the lubrication, it is necessary to mix both aqueous dispersions of the film-forming components thoroughly to prevent their sedimentation in the final lubrication. Ordinary drinking water can be used as a dispersing medium, or better, detonated water without undesirable ions, such as iron Fe, calcium Ca, etc., which can adversely affect the resulting properties of the lubrication.

Tato lubrikace je vhodná pro vlákna vyráběná na platinových pecích s počtem 400 až 1 200 výtokových trysek o průměru vláken 10 až 16 mikrometrů. Takto upravená vlákna s lubrikaci jsou vhodná pro výrobu rovingu, určeného ke zpracování technologií strojním nanášením, vinutím, eventuálně pro výrobu tkanin.This lubrication is suitable for fibers produced in platinum furnaces with 400 to 1,200 nozzles and fiber diameters of 10 to 16 microns. Fibers treated in this way with lubrication are suitable for the production of roving intended for processing by machine application, winding, or eventually for the production of fabrics.

Příklad 2Example 2

Zahrnuje chemické složení v hmotnostní koncentraci uvedené v příkladu 1, pokud se týká hlavní a vedlejší filmotvorné složky, tenzidu a mazací složky; Jako vazný prostředek byl použit v tomto případě 0,2 % hmotu. χ-aminopropyltrietoxysilanu a jako regulátu pH 2 % hmotn. 10% vodného roztoku kyseliny octové. Jako dispergační médium byla použita deionizovaná voda v množství do 100 % hmotn.It includes the chemical composition in the mass concentration given in Example 1, as regards the main and secondary film-forming components, surfactant and lubricant component; In this case, 0.2% by weight of χ-aminopropyltriethoxysilane was used as a binding agent and 2% by weight of 10% aqueous acetic acid solution was used as a pH regulator. Deionized water was used as a dispersing medium in an amount of up to 100% by weight.

Tato úprava je zvláště výhodná pro některé výrobky, například roving a tkaniny pro vyztužování epoxidových pryskyřic.This treatment is particularly advantageous for some products, such as roving and fabrics for reinforcing epoxy resins.

Možná je i záměna silanového vazného prostředku za jiný trifunkční, eventuálně mouofunkční silan s určením pro výztuže laminátů se speciálními požadavky.It is also possible to replace the silane coupling agent with another trifunctional, possibly monofunctional silane intended for reinforcing laminates with special requirements.

Claims (3)

1. Lubrikace pro úpravu skleněných vláken, obsahující vodnou disperzi filmotvorné složky, mazacích složek, tenzidu, vazného a antistatického prostředku a regulátoru pH, vyznačující se tím, že filmotvornou složkou vynalezu je směs polyvlnylacetátu s nasycenou nízkomolekulární polyesterovou pryskyřicí v hmotnostním poměru 1 ku 1 až 5 ku 1, přičemž nasycená polyesterová pryskyřice má obecný vzorec vClaims 1. A glass fiber treatment comprising an aqueous dispersion of a film forming component, lubricating components, surfactant, binder and antistatic agent and a pH regulator, wherein the film forming component of the invention is a mixture of polyvinyl acetate with a saturated low molecular weight polyester resin in a weight ratio of 1 to 1 5 to 1, wherein the saturated polyester resin has the general formula in t kde n = 2 až 10, m = 1 až 10, x = 1 až 20, y = 1 až 15, střední molekulovou hmotnost Mn 1 000 až 2 000 a velikost částic 0,1 až 5 mikrometrů.where n = 2 to 10, m = 1 to 10, x = 1 to 20, y = 1 to 15, average molecular weight M n 1,000 to 2,000 and particle size 0.1 to 5 microns. 2. Lubrikace k povrchové úpravě skleněných vláken podle bodu 1 vyznačující se tím, že obsahuje 0,1 až 1,0 % hmotn. vazného prostředku na bázi organokřemičltých sloučenin.2. A glass fiber finish according to claim 1, comprising 0.1 to 1.0 wt. a binder based on organosilicon compounds. 3. Lubrikace k povrchové úpravě skleněných vláken podle hodu 1, vyznačující se tím, že obsahuje 0,5 až 5 % hmotn. vazného a antistatického prostředku na bázi chromového komplexu kyseliny metakrylové.3. A glass fiber finish according to claim 1, characterized in that it comprises 0.5 to 5 wt. binding and antistatic agent based on chromium methacrylic acid complex.
CS872584A 1987-04-10 1987-04-10 Lubrication for treatment of glass fibers CS259644B1 (en)