CS249223B1 - Fast-hardening building mixture especially for wrapping filling - Google Patents
Fast-hardening building mixture especially for wrapping filling Download PDFInfo
- Publication number
- CS249223B1 CS249223B1 CS92385A CS92385A CS249223B1 CS 249223 B1 CS249223 B1 CS 249223B1 CS 92385 A CS92385 A CS 92385A CS 92385 A CS92385 A CS 92385A CS 249223 B1 CS249223 B1 CS 249223B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- cement
- construction
- weight
- fast
- mixture
- Prior art date
Description
Tento vynález sa zaoberá rýchlotvrdnúcou stavebnou zmesou, najma na plnenie obalov na budovanie stavebných konštrukcii alebo ich prvkov.The present invention is concerned with a rapid-hardening building composition, in particular for filling construction building packages or elements thereof.
Pri výstavbě niektorých banských alebo podzemných inžinierskych stavieb, najma v obťažných geologických podmienkach je potřebné zakladať viacvýlomy pri razení chodieb alebo budovat spevňujúcu náplň, připadne iné konštrukčné prvky bez akejkotvek mechanizácie, pričom sa nemóžu použit klasické spósoby vykonávania betonářských práč, ako je například ukladanie betónovej zmesi do debnenia alebo nanášanie suchého striekaného betonu. Přitom sa požaduje, aby budovaná část konštrukcie bola z hmoty, ktorá rýchlo nadobúda pevnost, aby bránila zosuvu alebo zasypaniu budovaného diela málo pevnou horninou.In the construction of some mining or underground engineering constructions, especially in difficult geological conditions, it is necessary to create multi-breakthroughs in tunneling or to build a reinforcing fill, or other construction elements without any mechanization, and conventional methods of concreting works such as concrete for formwork or application of dry sprayed concrete. In doing so, it is desired that the construction part of the structure be made of a material that quickly acquires strength in order to prevent the building work from sliding or falling into the low-strength rock.
Uvedené problémy rieši čs. AO č. 247 281. Jeho podstatou je, že do budovaného prvku alebo konštrukcie sa ukládá suchá rýchlotvrdnúca zmes, zabalená do obalov, například vriec umelohmotovej tkaniny, ktorá sa priamo v obale aktivuje polievaním a prevlhčovaním vodou, například napuštěním vody do prepichnutého obalu.These problems are solved by MS. AO č. 247 281. It is based on the fact that a dry quick-hardening composition, packed in containers, for example a bag of plastic fabric, is put into the element or structure being constructed, which is activated directly in the container by watering and moistening with water, for example by impregnating water into the punctured container.
Z čs. AO č. 222 863 je známa rýchlotvrdnúca hydraulická zmes, pozostávajúca — — uvedené v dieloch hmotnostných — zo 100 dielov hlinitanového cementu, 3 až 30 dielov mletého vápna a/alebo vápenného hydrátu, 3 až 30 dielov mletého vápenca s obsahom najmenej 50 % hmotnostných častíc menších ako 45 μΐη, 0,1 až 5 dielov regulátora tuhnutia, pozostávajúceho z organickej kyseliny, obsahujúcej najmenej dve karboxylové skupiny a/alebo z rozpustného síranu dvojmocného- kovu a/alebo z anionaktívnej sulfonovanej organickej zlúčeniny, a připadne 5 až 900 dielov portlandského alebo trosikoportlandského cementu a/alebo až 800 dielov plniva.Z čs. AO č. 222 863 is a known rapid-hardening hydraulic mixture consisting of - stated in parts by weight - 100 parts of aluminous cement, 3 to 30 parts of ground lime and / or lime hydrate, 3 to 30 parts of ground limestone containing at least 50% by weight particles smaller than 45 0.1 to 5 parts of a solidification regulator consisting of an organic acid containing at least two carboxyl groups and / or of a soluble divalent metal sulphate and / or of an anionic sulphonated organic compound, and optionally 5 to 900 parts of Portland or Trosicoportland cement, and / or up to 800 parts of filler.
Ako anionaktívnu sulfonovanú organická zlúčeninu bolo podta AO č. 222 863 možné použit například dinaftylmetándisulfonan sodný a ako organická kyselinu, obsahujúcu najmenej dve karboxylové skupiny, například kyselinu etyléndiamíntetraoctovú, vinnu alebo citrónová.As anionic sulfonated organic compound, AO no. 222 863 can be used, for example, sodium dinaphthylmethanedisulfonate and as an organic acid containing at least two carboxylic groups, for example ethylenediaminetetraacetic acid, tartaric acid or citric acid.
Zmes podta čs. AO č. 222 863 sa móže po zabalení do obalov ukladať do stavebných konštrukcii alebo ich prvkov. K hydraulickej aktivácii balenej rýchlotvrdnúcej zmesi je však potřebné intenzívně prepichovanie ihlou alebo zaostřenou perforovanou trubkou a podobné, ktorou sa súčasne privádza tlaková voda.Mixture podta MS. AO č. 222 863 may be placed in building structures or elements thereof after packaging. However, intensively piercing with a needle or a sharpened perforated tube and the like is necessary for the hydraulic activation of the packaged quick-hardening composition, and simultaneously pressurized water is supplied.
Pri zvlášť naliehavých a rizikových prácach v nepřístupných miestach, budovaných v obťažných geologických podmienkach sa prepichovanie obalov nedá prakticky uskutočniť pre zlý přístup k spevňovanému miestu alebo' pre nebezpečie závalu.In particularly urgent and risky work in inaccessible areas built in difficult geological conditions, the puncturing of the packages cannot be practically performed due to poor access to the reinforced area or due to the risk of collapse.
Je všeobecne známe, že v dosledku poréznej štruktúry a nízkej pevnosti prídavok silikátového porézneho kameniva znižuje pevnosti mált a betónov.It is generally known that due to the porous structure and low strength, the addition of silicate porous aggregate reduces the strength of mortars and concrete.
Uvedené nedostatky sa prekvapujúco odstránia u rýchlotvrdnúcej stavebnej zmesi podta vynálezu, určenej najmá do obalov na rýchlu výstavbu, pozostávajúcej z cementu, kameniva a připadne modifikujúcich přísad alebo příměsí. Jej podstatou je, že obsahuje od 15 do 49,5 °/o hmotnostných cementu a od 50,5 do 85 % hmotnostných kameniva, pričom najmenej 0,5 % hmotnostných je uimelé silikátové kamenivo s objemovou hmotnosťou naj viac 1 600 kg . m-3 a obsahom častíc menších ako 2,5 mm najmenej 50 % hmotnostných.Surprisingly, the above-mentioned drawbacks are eliminated in the quick-hardening building composition according to the invention, intended in particular in rapid-construction packages, consisting of cement, aggregates and, optionally, modifying additives or admixtures. Its essence is that it contains from 15 to 49.5% by weight of cement and from 50.5 to 85% by weight of aggregate, with at least 0.5% by weight being a silicate aggregate with a bulk density of not more than 1600 kg. m -3 and a particle content of less than 2,5 mm by at least 50% by weight.
Zmes podta vynálezu sa 1'ahko aktivuje vodou. Ak je zabalená vo vreciach z tkaniny, ktorá prepúšťa vodu, móže byť s výhodou použitá tam, kde sa vyžaduje aktivácia púhym poliatím vodou. Pre také případy aplikácie, kde je možné obal prepichovať a napúšťať vodou, móže byť použitý aj parotesný obal, například z umelohmotovej fólie alebo z tkaniny potiahnutej umelohmotovou fóliou. Aj v takom případe však postačuje menší počet prepichnutí ako u doteraz známých zmesi.The composition of the invention is readily activated with water. When packed in bags of water-permeable fabric, it can advantageously be used where activation by mere pouring of water is required. For such applications where the container can be punctured and impregnated with water, a vapor-proof container can also be used, for example of a plastic film or a plastic film-coated fabric. Even in such a case, however, a smaller number of punctures is sufficient than with the known mixtures.
Ako cement móže byť v zmesi použitý cement na báze slinku portlandského cementu, ako je například portlandský alebo troskoportlandský cement. Tiež móže byť použitý hlinitanový cement alebo zmes hlinitanového cementu a cementu na báze slinku portlandského cementu.As cement, Portland cement clinker cement such as Portland or Troskoportland cement can be used in the mixture. Aluminous cement or a mixture of aluminous cement and Portland cement clinker cement may also be used.
Ako kamenivo sa móžu do zmesi podta vynálezu s výhodou použit běžné druhy kameniv podta ČSN 72 1511 Kamenivo pro stavební účely. Základné ustanovenia, ako sú například tažené riečne kamenivo, drvené karbonátové alebo silikátové kamenivo, ako je například kamenivo, ktoré vznikne pri drvení odpadu z výroby 1'ahčených plynosilikátových tvárnic.As an aggregate, conventional types of aggregates according to ČSN 72 1511 Aggregates for construction purposes can be advantageously used in the mixture according to the invention. Basic provisions, such as drawn river aggregates, crushed carbonate or silicate aggregates, such as aggregates, which arise from the crushing of waste from the manufacture of 1 'lightweight gas silicate blocks.
Móžu sa však použit aj iné druhy tahčených silikátových umělých kameniv, například agloporit, vznikajúci pri spekaní a žíhaní konglomerátov alebo výliskov z elektrárenského popolčeka. Je však potřebné, aby najmenej 0,5 % hmotnostných bolo silikátové pórovité kamenivo s objemovou hmotnosťou najviac 1 600 kg . m~3 a s obsahom častíc menších ako 2,5 mm najmenej 50 % hmotnostných. Na tento účel sa móžu s výhodou použit drobné frakcie aglpporitového kameniva, připadne i drobné odpadně frakcie, ktoré vznikajú pri výrobě agloporitu. Móžu sa však použit aj iné druhy umelých 1’ahčených silikátových kameniv, ak vyhovujú uvedeným požiadavkám na objemová hmotnost a na zrnenie.However, other types of pulverized silicate artificial aggregates, such as agloporite, resulting from the sintering and annealing of conglomerates or power fly ash compacts, may also be used. However, it is necessary that at least 0.5% by weight is a silicate porous aggregate with a maximum density of 1600 kg. m- 3 and having a particle content of less than 2,5 mm by at least 50%. For this purpose, it is advantageous to use small fractions of agpporite aggregate, possibly also small waste fractions which are produced in the production of agloporite. However, other types of artificial lightweight silicate aggregates may also be used, provided they comply with the specified density and grain requirements.
Je výhodné, ak rýchlotvrdnúca zmes podlá vynálezu obsahuje aj modifikačné příměsi alebo přísady, ako je zmáčadlo, například dinaftylmetándisulfonan sodný urýchíovač tvrdnutia a tuhnutia cementcw na báze portlandského slinku, ako je síran hlinitý, uhličitan sodný, hlinitan sodný alebo ich kombinácie urýchíovač tvrdnutia a tuhnutia hlinitanového cementu, ako je například mleté vápno alebo vápenný hydrát regulátor tuhnutia hlinitanového cementu, ako je například síran meďnatý, kyselina citrónová alebo etyléndiamíntetraoctová stabilizátor hydratačných produktov hlinitanového cementu, ako je mikromletý vápenec.It is preferred that the quick setting composition of the present invention also comprises modifying ingredients or additives, such as a wetting agent, for example sodium dinaphthylmethane disulfonate, a curing agent based on Portland clinker, such as aluminum sulfate, sodium carbonate, sodium aluminate, or a combination thereof a cement such as ground lime or lime hydrate solidification regulator of an aluminous cement such as copper sulfate, citric acid or ethylenediaminetetraacetic stabilizer of hydrating products of an aluminous cement such as micronized limestone.
Výhody rýchlotvrdnúcej zmesi pódia vynálezu ukazujú následujíce příklady: Příklad 1The following examples illustrate the advantages of the quick curing composition of the invention: Example 1
Boli vyrobené dve suché zmesi; zmes označená A 1 pódia vynálezu a pre porovnáme zmes označená A 2 silikátového, porézneho kameniva podía AO 222 863 nasledujáceho zloženia:Two dry mixes were made; A 1-denoted mixture according to the invention and for a comparison A 2-denoted mixture of silicate, porous aggregate according to AO 222 863 having the following composition:
Zložka Zmes A 1 podlá vynálezu Porovnávacia zmes A 2 portlandský cementComponent A 1 according to the invention Comparative mixture A 2 Portland cement
kamenivo, ktoré bolo vyrobené predrvením odpadu z výroby piynosilikátových tvárnic, obsahujúce 80 % častíc menších ako 2,5 mraaggregates which have been produced by pre-crushing piynosilicate blocks production waste containing 80% of particles smaller than 2,5 mra
Spolu 67,4 kg 57,4 kgTotal 67.4 kg 57.4 kg
Zhomogenizo-vané suché zmesi boli naplněné do -vriec z jutovej tkaniny tak, aby hrubka zmesi vo vreci, uloženom na vodorovná podložku, bola 8 cm. Potom boli obe zabalené zmesi ro-vnako aktivované políevaním vodou po dobu 180 sekúnd.The homogenized dry blends were filled into a jute fabric bag so that the thickness of the blend in the bag placed on a horizontal support was 8 cm. Then, both packaged blends were activated by sieving with water for 180 seconds.
Zmes A 1 podlá vynálezu bola po 30 minutách od poliatia dobré zatvrdnutá a po rozlomení -sa ukázalo, že je po celej hrúbke úplné prevlhčená. Zmes A 1 maia po 30 minutách po poliatí vodou pevnost v tlaku 3 MPa.The mixture A1 according to the invention was well hardened after 30 minutes from the pouring and showed that after breaking it was completely wetted over the entire thickness. The mixture A 1 has a compressive strength of 30 bar after 30 minutes after the water has been poured.
Porovnávacia zmes A 2 maia po rozlomení na povrchu okrajov zatvrdnutá, pre vodu nepriepustnú vrstvu hrubá cca 20 mm, a v střede neprevlhčenú -suchá vrstvu v hrúbke 30 až 40 mm. Středná neprevlhčená vrstva suchej zmesi bola ešte v póvodnom sypkom stave, a preto nemala ešte prakticky žiadnu pevnost' v tlaku. K prevlhčeniu suchej strednej vrstvy a tým aj k jej vytvrdnutiu a nadahudnutiu pevností by halo potřebné viacná-sobné prepichovanie ohaiu zaostřenou perforovanou trubkou, opatřenou prívodom tlakovej vody.After breaking, the comparative composition A 2 has a hardened, water-impermeable layer about 20 mm thick and has a non-moistened, dry layer 30 to 40 mm thick. The middle non-moistened layer of the dry mixture was still in the original bulk state and therefore had virtually no compressive strength yet. To moisten the dry middle layer and thus to cure it and to overheat the strengths, a plurality of punctures with a sharpened perforated pipe provided with a pressurized water supply would be necessary.
Z uvedeného příkladu je zřejmé, že zmes A 1 podlá vynálezu sa podstatné rýchlejšie a 1’ahšie prevlhčuje ako zmes doteraz známa.From the above example, it is apparent that the mixture A1 of the present invention is substantially faster and easier to moisturize than the prior art mixture.
Příklad 2Example 2
Podlá vynálezu boli vyrobené dve zmesi, označené B 1 a B 2 nasledujúceho zloženia:According to the invention, two mixtures were produced, designated B1 and B2, having the following composition:
Zložkacomponent
Zmes B íMixture B 1
Zmes B 2Mixture B 2
Zhomogenizovaná suchá zmes bola plněná do jutových vriec a aktivovaná vodou rovnakým sposobom ako v příklade 1.The homogenized dry mixture was filled into jute bags and activated with water in the same manner as in Example 1.
Obe zmesi podl'a vynálezu boli po 30 minutách od poliatia vodou úplné a riadne v celej hrúbke zatvrdnuté.Both mixtures according to the invention were complete and properly hardened throughout the thickness 30 minutes after the water treatment.
Uvedené příklady však nijako neobmedzujú zloženie zmesi podta vynálezu, například použitím ďalších urýchlovačov tvrdnutia alebo tuhnutia cementu na báze portlandského stinku, použitím kombinácii portlandského alebo troskoportlandského cementu s hlinitanovým cementom, přidáním roznych zmáčadiel, volbou různých druhov kameniva vrátane silikátových 1'ahčených kameniv, kombinácii jednotlivých frakcií a druhov kameniva a podobné.However, these examples do not limit the composition of the composition according to the invention, for example by using other Portland cement stiffeners or curing accelerators, using a combination of Portland or troscortortland cement with aluminous cement, adding various wetting agents, selecting various types of aggregates including silicate aggregates. fractions and types of aggregates and the like.
Zimes podlá vynálezu sa íahšie, rýchlej-The compounds according to the invention are easier, faster
10,0 kg šie a důkladnejšie prevlhčuje v obale. Rýchlotvrdnúca zmes podlá vynálezu zabalená v obale a aktivovaná priamo v budovanom prvku alebo konštrukcii umožňuje výrazné urýchlenie výstavby a zvýšenie bezpečnosti práce, najmá pri budovaní zvlášť náročných stavebných diel v nepriaznivých geologických podmienkách — v sypkých a málo pevných horninách a tiež tam, kde nie je možné použit žiadnu mechanizáciu, alebo kde je nevyhnutné v extrémně krátkých časoch zabezpečit vybudovanie a zatvrdnutie konštrukcie. Rýchlotvrdnúca zmes podta vynálezu je zvlášť výhodná pri spevňovaní viac výrubov vznikajúcich pri razení banských chodieb, kde umožňuje výrazné zvýšit výkon raziaceho stroja, a tiež pri budovaní protivýbuchových a protipožiarnych hrádzí.10.0 kg wider and more moisturized in the packaging. The quick-hardening composition according to the invention packaged in the package and activated directly in the element or structure being built allows a significant acceleration of construction and increased occupational safety, especially when building particularly demanding components in unfavorable geological conditions - in loose and low strength rocks and also where no mechanization or where it is necessary to ensure the construction and hardening of the structure in extremely short times. The quick curing composition of the invention is particularly advantageous in consolidating a plurality of excavations resulting from the mine tunneling, where it enables to significantly increase the performance of the embossing machine, as well as in the construction of explosion and fire dams.
Claims (1)