CS240485B1

CS240485B1 - Polypropylene pressure-sensitive tape

Info

Publication number: CS240485B1
Application number: CS623384A
Authority: CS
Inventors: Jan Durinda; Martin Benko; Vincent Rachel; Vladimir Rusnak
Original assignee: Jan Durinda; Martin Benko; Vincent Rachel; Vladimir Rusnak
Priority date: 1984-08-17
Filing date: 1984-08-17
Publication date: 1986-02-13

Abstract

Polypropylénová na tlak citlivá páska obsahujúca vrstvu na tlak citlivého lepidla a polypropylénový nosný materiál vyznačená tým, že v nej ohsiahnutá polypropylénová vrstva je orientovaná dížením v pozdížnom smere pásky v pomere váčšom ako 1:3 a menšom ako 1: 7 a v, priečnom smere pásky v pomere váčšom ako 1:7a menšom ako 1:12.Polypropylene pressure-sensitive tape containing a layer of pressure-sensitive adhesive and a polypropylene carrier material, characterized in that the polypropylene layer covered therein is oriented by stretching in the lateral direction of the tape in a ratio greater than 1:3 and less than 1:7 and in the transverse direction of the tape in a ratio greater than 1:7 and less than 1:12.

Description

240483240483

Vynález sa týká polypropylénovej na tlakcitlivej pásky so zlepšenými vlastnosťami arozšířenou použitelnosťou.The present invention relates to a polypropylene pressure-sensitive tape with improved properties and extended usability.

Pod pojmom na tlak citlivá páska sa ro-žníme kombinácia na tlak citlivého lepidla,nosného materiálu a připadne oddelovacíe-ho nátěru.The pressure-sensitive tape is a combination of a pressure-sensitive adhesive, a carrier material and, optionally, a separating coating.

Pod pojmom na tlak citlivé lepidlo sa ro-zumiě viskoelastický materiál, ktorý je vbezrozpúšťadlovej formě permanentně lep-kavý a spája okamžité váčšinu povrchovpri použití mierneho přítlaku na vytvorenielepeného spoja.The pressure-sensitive adhesive is understood to mean a viscoelastic material which is permanently adhesive in the non-solvent form and connects the instantaneous surface to the use of a slight pressure on the bonded bond.

Pod pojmom nosný materiál sa rozumiemateriál, spravidla plošný, na ktorom je na-nesená vrstva na tlalk citlivého lepidla.The term carrier material is understood to mean a material, typically a sheet, on which a layer of pressure sensitive adhesive pressure is supported.

Pod pojmom oddělovací nátěr sa rozumienátěr nanesený na opačnej straně nosného·materiálu ako je vrstva na tlak citlivého le-pidla zabezpečujúci 1'ahké oddelenie od nana tlak citlivého lepidla.The term separating coating means a coating applied on the opposite side of the carrier material, such as a pressure-sensitive adhesive layer providing easy separation from the pressure-sensitive adhesive.

Pod pojmom polypropylénová na tlak cit-livá páska sa rozumie na tlak citlivá páskaobsahujúca polypropylénový nosný materiál.By polypropylene pressure-sensitive tape is meant a pressure-sensitive tape containing polypropylene support material.

Pod pojmom polypropylénový nosný mate-riál sa rozumie nosný materiál tvořený po-lypropylénovou vrstvou alebo nosný mate-riál obsahujúci polypropylénové vrstvu akoprevažujúcu zložku.By polypropylene carrier material is meant a support material consisting of a polypropylene layer or a support material comprising a polypropylene layer and a predominant component.

Pod pojmom polypropylénová vrstva sarozumie vrstva tvořená prevažne polypropy-lénem.The term "polypropylene layer" refers to a layer formed predominantly of polypropylene.

Na tlak citlivé pásky sú spravidla distri-buované a používané v navinutej formě —— v kotúčoch. Je prirodzené, že dlžka natlak citlivej pásky je řádové váčšia ako jejšířka, i keď to pre vymedzenie pojmu natlak citlivá páska nie je podmienkou.The pressure-sensitive tapes are generally distributed and used in wound form in rolls. Naturally, the pressure of a sensitive tape is magnitude larger than its width, although it is not a prerequisite to define the pressure sensitive tape.

Jedným z hlavných použití na tlak citli-vých pások je zatváranie obalov, najmá o-balov z vlnitej lepenky. Nakolko v ostatnomobdobí varastá hmotnost obsahu obalov vl-nitej lepenky, sú povodně používané papie-rové na tlak citlivé pásky a celofánové natlak citlivé pásky nahrádzané páskami, vktorých nosný materiál obsahuje syntetickýpolymér, spravidla polyolefín.One of the main uses of pressure sensitive tapes is the closing of packaging, especially corrugated cardboard. Since, in the past, the vast mass of corrugated cardboard contents, the paper pressure-sensitive tapes used and the cellophane pressures are sensitive tapes replaced by tapes in which the carrier material comprises a synthetic polymer, typically a polyolefin.

Patent AT 337 8Θ1 popisuje papierovú natlak citlivú pásku tvořenu vrstvou sulfáto-vého papiera, vrstvou na tlak citlivého le-pidla na jednej straně papiera a nalamino-vanou, resp. naextrudovanou vrstvou poly-etylénu alebo· polypropylénu.Patent AT 337 8-1 discloses a paper pressure-sensitive tape formed by a layer of sulphate paper, a pressure-sensitive adhesive layer on one side of the paper, and a laminate, respectively. an extruded layer of polyethylene or polypropylene.

Patent US 4 188 439 popisuje na tlak cit-livá pásku tvorenú vrstvami lineárneho po-lyetylénu, rozvětveného polyetylénu, papie-ra a na tlak citlivého: lepidla.U.S. Pat. No. 4,188,439 discloses a pressure sensitive tape formed by layers of linear polyethylene, branched polyethylene, paper and pressure sensitive adhesive.

Patent US 4 188 442 popisuje na tlak cit-livú pásku tvorenú vrstvami rozvětvenéhopolyetylénu, lineárneho polyetylénu, rozvět-veného polyetylénu, papiera a na tlak citli-vého lepidla.U.S. Pat. No. 4,188,442 discloses a pressure-sensitive strip formed of layers of branched polyethylene, linear polyethylene, branched polyethylene, paper and pressure sensitive adhesive.

Hlavným cielom obsahu polyolefínovýchvrstiev v uvedených na tlak citlivých pás-kách je zlepšenie ich mechanických vlast-ností. Je prirodzené, že váčšiu pevnost za- bezpečuje obsah polypropylénovej vrstvynež polyetylénovej vrstvy. V případe vysokej pevnosti na tlak citli-vej pásky v tahu však vzniká problém di-stribúcie pásky na menšie časti, a to najmáv případe distribúcie ručným trháním.The main aim of the polyolefin coating content in said pressure sensitive bands is to improve their mechanical properties. Naturally, the strength of the polypropylene layer is higher than that of the polyethylene layer. However, in the case of high tensile strength of the sensitive tape in tension, there is a problem of distributing the tape to smaller parts, in particular in the case of manual tearing.

Patent US 4 137 362 popisuje polypropylé-nová na tlak citlivú pásku, v ktorej poly-propylénová vrstva je orientovaná dlženímv pozdížnom smere pásky v rozsahu pome-rov 1: 1 až 1: 3 a v priečnom smere páskyv pomere váčšom ako 4. Podlá autorov ci-tovaného· patentu sa tým dosahuje to, že po-lypropylénová na tlak citlivá páska je pev-ná v priečnom smere a súčasne distribuova-tel'ná v pozdížnom smere ručným trháním.Je prirodzené, že táto páska je podlá auto-rov uvedeného patentu určená najmá nazatváranie obalov, a to najmá na zatváraniedebien s klopami tým spésobom, že páskaje namáhaná na tah výlučné vo smere prieč-nom.U.S. Pat. No. 4,137,362 discloses a polypropylene pressure-sensitive tape in which the poly-propylene layer is oriented in a longitudinal direction of the tape in the range of 1: 1 to 1: 3 and in the transverse direction of the tape in a ratio greater than 4. According to the authors The patent claims that the polypropylene pressure-sensitive tape is rigid in the transverse direction and at the same time distributable in the longitudinal direction by manual tearing. The invention is particularly concerned with the closing of the packaging, and in particular with the flap with the flaps, in such a way that the strip is subjected to tension exclusive in the transverse direction.

Polypropylénová na tlak citlivá páska po-písaná v uvedenom patente má však viace-ro nevýhod.However, the polypropylene pressure-sensitive tape described in said patent has disadvantages.

Pri použití uvedenej pásky tým sposobom,že po vytvoření lepeného spoja je táto na-máhaná len v priečnom smere, je strihovonamáhaná vrstva na tlak citlivého lepidla,ktará sa, vzhtadom na to, že lepený spoj nieje vo· smere střihového namáhania dosta-točne dlhý, nakolko je ohraničený šířkoupásky, stává najslabším článkom na tlakcitlivej pásky, čo spravidla može viesť k roz-rušeniu lepeného spoja, otvoreniu obalu aznehodnoteniu jeho obsahu.. Případné rie-šenie tejto· nevýhody zvfičšením šířky páskynaráža na skutočnosť, že zváčšenie šířkypásky znamená jednak zváčšenie nákladovna zatváranie obalu, jednak zváčšenie silya práce potrebnej na odvíjanie pásky z ko-túča. Případné riešenie namáhavosti pri odví-janí na tlak citlivej pásky je sice riešitelnépomocou dnes spravidla běžných nástrojovumožňujúcich odvíjanie na tlak citlivej pás-ky z otočného hriadela, tieto nástroje všakspravidla obsahujú element určený na reza-nie pásky, resp. je takýto element bez ťaž-kostí do týčhto nástrojov včlenitelný. Potomovšem odpadá opodstatněnost nízkej pev-nosti v ťahu popísanej na tlak citlivej poly-propylénovej pásky v jej pozdížnom smere. Případné riešenie namáhavosti pri odví-jení na tlak citlivej pásky je sice riešitelnépomocou oddelovaciebo nátěru obsiahnuté-ho v ipáske, jeho vytvorenie však předsta-vuje ďalšiu výrobnú operáciu, a navýše su-roviny na vytvorenie oddelovaciebo nátěrusú vysoko nákladné. Ďalšou nevýhodou polypropylénovej natlak citlivej pásky popísanej v uvedenompatente je jej nízká pevnost v ťahu vo· sme-re pozdížnom daná nízkou mierou orientá-cie polypropylénovej vrstvy dlžením v· tom-to smere. Táto· znemožňuje spolehlivé za- 240483By using said tape in such a way that it is only stretched in the transverse direction after the bonding is formed, the shear-bonded layer is a pressure-sensitive adhesive, due to the fact that the bonded joint is not sufficiently long in the shear stress as it is bounded by the width of the tape, it becomes the weakest link to the pressure-sensitive tape, which can generally lead to the splicing of the bond, the opening of the package, and the non-evaluation of its contents. the cost of closing the packaging, and the strength of the work needed to unwind the tape from the coil. A possible solution to the strain-relieving pressure-sensitive tape is, of course, solvable by today's commonly used tools for unrolling a pressure-sensitive tape from a rotary shaft, but these tools typically contain an element intended to cut the tape or the tape. such an element can be incorporated into these tools without difficulty. Thereafter, the low tensile strength described on the pressure-sensitive polypropylene tape in its longitudinal direction is no longer necessary. The possible solution to the strain on the pressure-sensitive tape is, of course, solved by the separating coating contained in the tape, but its formation is a further manufacturing operation, and in addition, the layers for the formation of the separating coat are highly expensive. A further disadvantage of the polypropylene pressure sensitive tape described in the present invention is its low tensile strength due to the low orientation orientation of the polypropylene layer by stretching in this direction. This makes it impossible for reliable 240483

S tvfiranie obalov, najma autormi citovanéhopatentu uvádzaných lepenkových debien sí.klopami sposobom v súčasnosti normativněv rozvinutých krajinách predpísaným, tojest sposobom, pri ktorom sa páska prele-puje cez rohy obalu, spravidla debny s klo-pami, v dosledku čoho je páska namáhanána tah i v pozdlžnom smere pásky, teda spó-sobom, ktorý zabezpečuje ochranu balené-ho obsahu proti kontaminácii tuhými me-chanickými nečistotami, vodou, hmyzom,připadne hlodavcami. Ďalšou nevýhodou polypropylénové]’ natlak citlivej pásky popísanej v citovanompatente je skutečnost, že v dosledku jejníz-kej pevnosti v tahu v p-ozdlžnom smere pás-ky táto páska nemože byť použitá na za-tváranie o-balov určených pro ťažšie obsa-hy, rozšírenie ktorých rastie s rozvojom vý-roby paůvrstvovej a sedemvrstvovej vlnitejlepenky, nak-oťko Ikonštrukcia tý-chto obalovvyžaduje prelepovanie sposobom, pri ktoromje ina tlak citlivá páska namáhaná na tah vpozdlžnom smere pásky. Z tých istých pří-čin nemože byť táto páska použitá na zatvá-ranie obalov pomocou páskovacích strojov,ktorých použitie v rozvinutých krajináchvýznamné rastie.With the formation of packaging, in particular by the cited inventors of the cardboard boxes mentioned above, in the presently prescribed normative manner, in which the tape is overlapped by the corners of the package, usually crates, as a result of which the tape is strained even by in the longitudinal direction of the tape, that is to say, in a way that protects the packaged contents against contamination with solid mechanical impurities, water, insects, or rodents. A further disadvantage of the polypropylene pressure-sensitive tape described in the cited patent is that, due to its low tensile strength in the β-length direction of the tape, this tape cannot be used to form packages intended for heavier contents, the expansion of which increases with the development of a layered and seven-layered corrugated sheet, since the icon of these packages requires a bonding method in which the other pressure-sensitive tape is subjected to tension in the longitudinal direction of the tape. For the same reasons, this tape cannot be used to close packages with strapping machines, the use of which in significant countries is increasing in use.

Vyššie uvedené nevýhody polypropyléno-vej na tlak citlivej pásky sú odstránené po-lypropylénovou na tlak citlivou páskou po-dlá vynálezu, kterej podstatou je, že v nejobsiahnutá polypropylénová vrstva je orien-tovaná díženim v pozdlžnom smere pásky vpomere vSčšom ako 1:3a menšom ako 1 : 7a v priečnom smere v pomere váčšom ako1:7a menšom ako 1:12. Tým, že polypropylénová na tlak citlivápáska pódia vynálezu obsahuje polypropylé-nová vrstvu orientovaná dlžením v pozdlž-nom smere pásky v pomere váčšom ako 1: 3a menšom ako 1:7 a v priečnom smere'pásky v pomere váčšom ako 1:7a menšomako- 1 : 12 sa v dosledku zvýšenej pevnostitejto pásky v pozdlžnom ismere pásky danejzvýšenou mierou jej oriéntácie v tomto sme-re spĎsobenou zvýšenými pomermi dlženiav tomto smere, odstránia vyššie popísanénevýhody doteraz známej polypropylénové]'na tlak citlivej pásky.The above-mentioned disadvantages of polypropylene pressure-sensitive tape are removed by polypropylene pressure-sensitive tape of the present invention, the principle being that in the most complex polypropylene layer, it is oriented by drawing in the longitudinal direction of the tape at a ratio of greater than 1: 3 and less than 1: 7a in a transverse direction greater than 1: 7 and less than 1:12. In that the polypropylene pressure-sensitive sheet of the present invention comprises a longitudinally stretched polypropylene layer with a length greater than 1: 3 and less than 1: 7 and in the transverse direction the band is greater than 1: 7 and less than 1: 7a. In this respect, the above-described advantages of the prior art polypropylene pressure-sensitive tape are avoided as a result of the increased strength of the tape in the longitudinal tape ratio by the increased degree of orientation in this tape due to the increased draw ratio of this direction.

Dosledkom toho je možnost použitia po-lypropylénové]' na tlak citlivej pásky pódiavynálezu na zatváranie debien s klopamispĎs-obom normativně predpísaným v rozvi-nutých krajinách, na zatváranie obalov sozvýšenou hmotnosťou obsahu, ako i na za-tváranie obalov pomocou páskovacích stro-jov. Tým, že polypropylénová na tlak citlivápáska podlá vynálezu obsahuje polypropy-lénvoú vrstvu orientovaná dlžením v- pozdlž-nom smere pásky v pomere váčšom ako 1: 3a menšom ako 1: 7 a v priečnom smere pás-ky v pomere váčšom ako 1:7a menšom ako1: '12 sa v dosledku zníženej prieťažnostitejto pásky v pozdlžnom smere sposobenejzvýšenými pomermi dlženia v tomto- smere zabezpečí zvýšená stabilita lepeného sp-ojavy-tváraného touto páskou, nakoíko sa znížimiera energie o-bsiahnutej v polypropylé-nové j v-rstve pásky v dosledku jej predíže-nia pri vytváraní lepeného spoja, ktorá ve-die k zmršťovaniu pásky po vytvoření lepe-ného spoja, a teda silovému namáhaniu le-peného spoja. PřikladlLast but not least, it is possible to use polypropylene pressure-sensitive tape of the present invention for closure of clopamisposites prescribed in developed countries, for packaging closure with increased weight, and for wrapping with strapping machines. In that the polypropylene pressure-sensitive sheet according to the invention comprises a polypropylene layer oriented in the longitudinal direction of the tape in a ratio greater than 1: 3 and less than 1: 7 and in the cross-section of the tape in a ratio greater than 1: 7 and less As a result of the reduced elongation of the tape in the longitudinal direction due to the increased draw ratios in this direction, the stability of the bonded adhesive formed by the tape is increased, since the energy absorbed in the polypropylene layer of the tape is reduced as a result. it is reduced by the formation of a bonded joint which leads to the tape shrinking after the bonding has been formed and thus the stress of the bonded joint. Přikladl

Polypropylénová na tlak citlivá páskatvořená vrstvou na tlak citlivého lepidlahrábky 22 μαι na nosnom materiále tvoře-ném vrstvou polypropylénu hrábky 30 ,«morientovanou dlžením v pozdlžnom smerepásky v pomere 1 : 5,4 a v priečnom smerepásky v pomere 1: 9,5. P r i k 1 a d 2Polypropylene pressure-sensitive pressure-sensitive adhesive layer 22 microns on the carrier material of the pea polypropylene layer 30, which is 1: 5.4 in longitudinally stretched longitudinal direction and 1: 9.5 in transverse direction. P r i k 1 and d 2

Polypropylénová na tlak citlivá páska tvo-řená vrstvou na tlak citlivého lepidla -hrůb-ky 27 /un na nosnom materiále tvorenompolypropylénovou vrstvou hrábky 30 μπιorientovanou dlžením v pozdlžnom smerepásky v pomere 1: 5,3 a v priečnom smerepásky v- pomere 1: 8,0. P r i k 1 a d 3Polypropylene pressure-sensitive tape formed by a pressure-sensitive adhesive layer 27 / un on a support material consisting of a polypropylene layer of a rake of 30 µm oriented in a 1: 5.3 ratio in the longitudinal direction and in a 1: 8 cross section 0. P r i k 1 and d 3

Polypropylénová na tlak citlivá páska .tvo-řená na tlak -citlivého lepidla hrůbky 27 μίαna nosnom materiále tvorenom polypropy-lénovou vrstvou hrůbky 30 μΐη orientovanádlžením v pozdlžnom smere pásky v pomere1: 7,'6 a v priečnom smere pásky v pomere1 : 6,2. PřikládáPolypropylene pressure-sensitive tape formed by the pressure-sensitive adhesive of the ridge 27 μία to the support material formed by the polypropylene layer of the ridge 30 μΐη oriented in the longitudinal direction of the tape in the ratio 1: 7, 6 and in the transverse direction of the tape in the ratio 1: 6,2 . Attaches

Polypropylénová na tlak citlivá páska tvo-řená vrstvou na tlak citlivého lepidla hrůb-ky 25 ,ttm na nosnom materiále tvorenompolypropylénovou vrstvou hrůbky 40 μΐη -o-rientovanou dlžením v pozdlžnom smerepásky v pomere 1: 4,1 a v priečnom smerepásky v- pomere 1 :10,6. P r i k 1 a d 5,Polypropylene pressure-sensitive tape formed by a pressure-sensitive adhesive layer at ridge 25, on a support material consisting of a polypropylene layer of 40 μΐη -related lengthwise stretch in a ratio of 1: 4.1 and in a cross-section in a ratio of 1 : 10.6. P r i k 1 a d 5,

Polypropylénová na tlak citlivá páska tvo-řená vrstvou na tlak citlivého- lepidla hrůb-ky 25 /..;m na nosnom materiále tvorenompolypropylénovou vrstvou hrubky 40 ,«m o-rientovanou dlžením v pozdlžnom smerepásky v pomere 1: 2,2 a v priečnom smerepásky v pomere 1:11,7, teda v intenciáchpatentu US 4 137 3-82. Příklad 6 ’ Polypropylénová na tlak citlivá pá-ska tvo-řená vrstvou na tlak citlivého lepidla hrůb-ky 25 /tm na nosnom materiále tvorenompolypropylénovou vrstvou hrůbky 50 /tm o-rientovanou dlžením v pozdlžnom smere 24848a pásky v pomere 1:1,4 a v priečnom smerepásky v pomere 1: 6,2, teda v intenciáchpatentu US 4 1.37 362. Příklad 7Polypropylene pressure-sensitive tape formed by the pressure-sensitive adhesive layer of the crest on the carrier material formed by a polypropylene layer of 40 µm oriented in a longitudinal direction in a 1: 2.2 ratio and in the transverse direction bands in a ratio of 1: 11.7, i.e. in accordance with U.S. Pat. No. 4,137 3-82. EXAMPLE 6 Polypropylene pressure-sensitive tape formed by a pressure-sensitive adhesive layer of ridge 25 / tm on a backing material of polypropylene layer 50 / tm oriented in a longitudinal direction 24848a of the tape at a ratio of 1: 1.4 and in a cross section in a ratio of 1: 6.2, that is to say in U.S. Pat.

Polypropylénová na tlak citlivá páska tvo-řená vrstvou na tlak citlivého' lepidla hrůb-ky 24 |i(m .nanesenou na polypropylénovejstraně polypropylénového nosného materiá- lu tvořeného vrstvou koextrudovaného po-lypropylénu a polyetylénu, v ktorom torúbkapolypropylénové]' vrstvy činí 15 μία a hrúb-ka polyetylénové] vrstvy činí 10 um, orien-tovaného' dížením v pozdížnom smere pás-ky v pomere 1: '5,1 a v priečnom smere pás-ky v- pomere 1: 8,9.Polypropylene pressure-sensitive tape formed by a pressure-sensitive adhesive layer 24 µm thick (deposited on a polypropylene backing of a co-extruded polypropylene-polyethylene-polyethylene polypropylene backing material in which the tubular polypropylene layer is 15 µm) and the thickness of the polyethylene] layer is 10 µm, cut in a 1: 5.1 ratio in the longitudinal direction of the strip and in the transverse direction of the tape in a 1: 8.9 ratio.

Vysvetlenie výhod polypropylénové] natlak citlivé] pásky podl'a vynálezu poskytu-je nasledovná .tabulka.An explanation of the advantages of polypropylene pressure sensitive tape according to the invention provides the following table.

Polypropylé-nová na tlakcitlivá páskapodlá příkladuPolypropylene for pressure sensitive tape according to example

Pevnosť v ťahu(N/mm2) pozdížne priečneTensile strength (N / mm2) is laterally transverse

Prieťažnosť (%) pozdížne Rázová pevnosť(kg.cm/mm2)pozdížne priečne 1 150 300 2 165 . 254 3 196 201 4 116 347 5 74 36'3 6 42 117 7 144 271 130 85 165 122 91 154 74 137 12-8 107 67 191 246 38 197 340 24 142 133 78 157Elongation (%) lateral Impact strength (kg.cm/mm2) longitudinally transversal 1 150 300 2 165. 254 3 196 201 4 116 347 5 74 36'3 6 42 117 7 144 271 130 85 165 122 91 154 74 137 12-8 107 67 191 246 38 197 340 24 142 133 78 157

Pri praktickom použití polypropylénovýchna tlak citlivých pások popísaných vo vyš-šie uvedených příkladech na zatváranie le-penkových debien s klopami na páskovacomstroji sa ukázala ako nevyhovujúca, resp.čiastočne vyhovujúca pevnosť v ťahu v po-zdlžnom smere pásky v případe pások po-dlá příkladu 5 a příkladu 6, prieťažnosť amiera predíženia v pozdížnom smere páskyv případe pások podlá příkladu 3, příkladu5 a příkladu 6 a rázová pevnosť v priečnomsmere pásky v případe pásky podlá příkla-du 5 a rázová pevnosť v pozdížnom smerepásky v případe pásky podlá příkladu 3,příkladu 5 a příkladu 6. Pásky podlá pří-kladu 1, příkladu 2 a příkladu 4, teda páskypodlá vynálezu sa ukázali byť v každom zosledovaných znakov plné výhovu júce. Ďalšou, doteraz neuvedenou výhodou po-lypropylénové] na tlak citlivé] pásky podlávynálezu je možnosť zvýšenia pevnosti le-peného spoja vytváraného touto páskou da-ná možnosťou obsahu na tlak citlivého- le-pidla poskytujúceho zvýšenú pevnosť lepe-ného' spoja, ktorá je důsledkem zvýšenejpevnosti tejto pásky v ťahu v pozdížnomsmere pásky dané] zvýšenými pomermi dí-ženia v tomto smere. Ďalšou, doteraz neuvedenou výhodou po-lypropylénové] na tl-ak citlivé] pásky podťavynálezu je rozšíreinie možností je] použitiapomocou vysokovýkonných páskovacíchstrojov. V případe týchto- strojov je na tlakcitlivá páska odvíjaná z kotúča vysokourýchlosťou, následkom čoho sa lepený spojmedzi na tlak citlivým lepidlom a týmto le-pidlem nenatretou stranou nosného materiá- lu správa ako vysoko pevný, často pevnějšíako pevnosť na tlak citlivej pásky v ťahu vpozdížnom smere pásky, čo často v-edie kpretrhnutiu pásky pri je] odvíjaní z kotúča.Tomu zabraňuje zvýšená pevnosť v ťahu po-lypropylénové]' na tlak citlivej pásky pod-í-avynálezu v pozdížnom smere pásky.In practical use, the polypropylene pressure-sensitive tapes described in the above examples to close the pen-shaped flaps with the flaps on the strapping machine have proved to be unsatisfactory, or partially satisfactory, tensile strength in the tape length of the example 5 tape and Example 6, the elongation extensibility in the longitudinal direction of the tape in the case of the strips of Example 3, Example 5 and Example 6 and the impact strength in the tape cross-section of the tape according to Example 5 and the impact strength in the longitudinal tape of the tape of Example 3, Example 5 and Example 6. The tapes of Example 1, Example 2, and Example 4, i.e., the tapes of the present invention, have been shown to be fully satisfactory in each of the traits. Another advantage of the polypropylene pressure sensitive tape of the present invention, which is not yet mentioned, is the possibility of increasing the strength of the bonded joint formed by this tape by allowing the contents of the pressure sensitive agent to provide increased bonding strength resulting from increasing the tensile strength of the tape in the longitudinal ribbon portion given by the increased sizing ratios in that direction. Another advantage of the present invention is the use of high performance strapping machines. In the case of these machines, the pressure-sensitive tape is unwound from the roll with high velocity, and as a result, the glued bond between the pressure-sensitive adhesive and the non-wiped side of the carrier material is as high-strength, often stronger as the tensile strength of the sensitive tensile tape. this often prevents the tape from breaking when it is unwound from the roll. This prevents increased tensile strength of the polypropylene pressure-sensitive tape of the invention in the longitudinal direction of the tape.

Pre uskutečnemie nosného materiálu po-lypropylénovej na tlak citlivej pásky podťavynálezu možno využit polypropylén, -a tosamotný aleho v kombinácii s iným polymé-rom, resp. polymérmi vytvorenej lamináciou,natieraním, zmiešavaním aleb-o koextrúziou.Výhodné je použit polypropylén s percen-tom izotakticity vačším ako 90 °/o, sprav-idlavačším ako 95 %, s indexom toku taveninypodťa ČSN 64 08 61 rovným 1,9 -až 2,9 g/10minut, spravidla rovným 2,2 až 2,6 g/10 min. -Pre uskutočneinie polypropylénovej na tlakcitlivej pásky pod-ťa vynálezu možno využitrůzné typy na tlak citlivých lepidiel, akolepidiel na báze zrnesí základného elastomé-ru a živice na zvýše-nie lepkavosti, lepidieln-a báze vyšších akrylátov, pričom z hťadis-ka kohézie lepidla a jeho adhé-zie k nosné-mu materiálu je výhodný obsah karboxylo-vých skupím v lepidle.For the realization of the polypropylene pressure-sensitive tape support material, polypropylene can be used, but also in combination with another polymer, respectively. It is preferred to use a polypropylene having a percent isotacticity greater than 90%, more than 95%, with a melt flow index according to ČSN 64 08 61 equal to 1.9 to 2% by weight of polymers formed by lamination, coating, blending or coextrusion. , 9 g / 10 min, typically 2.2 to 2.6 g / 10 min. Various types of pressure-sensitive adhesives, base-elastomer-based adhesives, and tackifiers, adhesives and higher acrylate bases can be used to carry out the inventive polypropylene pressure-sensitive tape, wherein the adhesive cohesion criterion and the adhesive strength of the adhesive are based on the invention. its adhesion to the carrier material is the preferred content of carboxyl groups in the adhesive.

Možnosti uskutoičnenia polypropylénovejna tlak citlivej pásky podťa vynálezu sú rož-ne, pre předložený vynález však ostáv-a cha-rakteristické -a podstatné, že polypropylé-nová vrstva obsiahnutá v danej páske pod-ťavynálezu je orientovaná dížením v pozdíž-' nom smere pásky v pomere váčšom ako 1: 3a menšo-m ako 1:7 a v priečnom smerepásky v pomere vačšom ako 1:7a merišomako 1: 12.The possibilities of implementing the polypropylene pressure-sensitive tape according to the invention are, however, characteristic of and essential to the present invention that the polypropylene layer contained in the inventive tape is oriented in the longitudinal direction of the tape in the present invention. with a ratio greater than 1: 3a and less than 1: 7 and with a cross section of more than 1: 7 and 1: 12.

Claims

OBJECT (Polypropylene pressure-sensitive tape includes a pressure-sensitive adhesive layer and a polypropylene carrier material, characterized in that the polypropylene layer, also stretched therein, is oriented in the longitudinal

INVENTION the direction of the tape at a ratio greater than 1: 3 and less than 1: 7 and the transverse direction of the tape at a ratio greater than 1: 7 and less than 1: 12.