CS228182B1 - Structural part of an apparatus for metal coating by a dipping process of for metal dyeing,pickling and degreasing - Google Patents
Structural part of an apparatus for metal coating by a dipping process of for metal dyeing,pickling and degreasing Download PDFInfo
- Publication number
- CS228182B1 CS228182B1 CS184182A CS184182A CS228182B1 CS 228182 B1 CS228182 B1 CS 228182B1 CS 184182 A CS184182 A CS 184182A CS 184182 A CS184182 A CS 184182A CS 228182 B1 CS228182 B1 CS 228182B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- layer
- polyvinyl chloride
- pickling
- degreasing
- rigid foam
- Prior art date
Description
Vynále» se týká konstrukčních částí zařízení pro pokovování v roztocích, případně barvení, moření a odmašťování kovů, zejmána koster stolů, příček, výztuží, opláštění van, vanových zařízení, tvořených jádrem z tvrdé pěny, zejmána na bázi polyviřtylchloridu, polyuretanu, a polypropylenu, opatřeným alespoň na jedná straně chemicky odolnou vrstvou umělá pryskyřice, zejména na bázi polyesteru, epoxidu, nebo polyuretanu, případně vyztuženou skleněnými, uhlíkovými nebo syntetickými vlákny a na druhá straně vrstvou tvrdého termoplastu, zejmána polyvinylchloridu.The invention relates to components for metal plating or dyeing, pickling and degreasing equipment, in particular table skeletons, partitions, stiffeners, tub sheathing, bath tubs consisting of a rigid foam core, in particular based on polyvinyltyl chloride, polyurethane, and polypropylene, provided with at least on one side a chemically resistant layer of artificial resin, in particular based on polyester, epoxy or polyurethane, optionally reinforced with glass, carbon or synthetic fibers, and on the other side with a hard thermoplastic layer, in particular polyvinyl chloride.
Ke galvanizování se používá zařízení, zejména stolů, jejichž základem je kovová kostra, opatřená korozivzdornou úpravou, případně s opláštěním provedeným ze silnostěnných desek z plastické hmoty nebo sklolaminátu. Ani tato úprava nechrání všechny části konstrukce proti korozi, zejména výpary, které vnikají dovnitř konstrukčních částí a snižují jejich životnost.Equipment for galvanizing is used, especially of tables, which are based on a metal frame, provided with a corrosion-resistant treatment, possibly with a coating made of thick-walled plastic or fiberglass boards. Even this treatment does not protect all parts of the structure against corrosion, especially fumes that penetrate inside the components and reduce their service life.
V DOS 1 778 003 je popsáno a vyobrazeno materiálové složení stěny chemicky odolná nádoby větších rozměrů, která má jádro z tvrdá pěny, zejména na bázi polyvinylchloridu a tato vnitřní vrstva je po obou stranách zpevněna chemicky odolnou vrstvou z umělé pryskyřice, s výhodou vyztužené skleněnými vlákny.DOS 1 778 003 discloses and depicts the material composition of a wall of a larger size chemically resistant container having a rigid foam core, in particular based on polyvinyl chloride, and this inner layer is reinforced on both sides with a chemically resistant synthetic resin layer, preferably glass fiber reinforced .
Ze strany agresivní látky je navíc pokryta ochrannou vrstvou tvrdého termoplastu např. polyvinylchloridu nebo polypropylenu. Vrstva umělá pryskyřice zesílená skelným vláknem mezi vnitřním jádrem z tvrdé pěny a ochrannou vnější vrstvou tvrdého termoplastu slouží k jejich pevnému spojení, neboť přímé spojení není možné. Její zhotovení je pracné, zdlouhavé a nákladné.On the side of the aggressive substance, it is also covered with a protective layer of hard thermoplastic such as polyvinyl chloride or polypropylene. The fiberglass-reinforced synthetic resin layer between the hard foam inner core and the hard thermoplastic protective outer layer serves to firmly bond them since direct bonding is not possible. Its construction is laborious, lengthy and expensive.
Uvedené nevýhody se odstraní nebo podstatné omezí u konstrukčních částí podle vynálezu, jehož podstatě spočívá v tom, že mezi vrstvou tvrdého termoplastu s jádrem z tvrdé ptay je spojovací vrstva vzniklá stlačením jedné lepivé mezivrstvy na bázi polyvinylchloridu rozpuštěného v organickém rozpouštědle, narušujícím povrch tvrdého termoplastu a druhé lepivé vrstvy na bázi syntetického kaučuku, rozpuštěného v nejméně jednom aromatickém rozpouštědle, nanesená na zaschlou lepivou mezivrstvu a povrch jádra z tvrdé pěny, přičemž tloušíka spojovací vrstvy nepřesahuje 5 % celkové tloušlky stěny konstrukční části.These disadvantages are eliminated or substantially reduced by the components according to the invention, which consists in that between the hard thermoplastic layer and the hard ptay core there is a bonding layer formed by compressing one adhesive layer based on polyvinyl chloride dissolved in an organic solvent which disrupts the hard thermoplastic surface. a second synthetic rubber-based adhesive layer dissolved in the at least one aromatic solvent, applied to the dried adhesive interlayer and the surface of the rigid foam core, wherein the bonding layer thickness does not exceed 5% of the total wall thickness of the component.
Spojovací vrstva, vzniklá spojením dvou lepivých mezivrstev, zajišíuje dokonale pevný spoj mezi vrstvou z tvrdé pěny a vrstvou tvrdého termoplastu, přenášející a tlumící deformační síly především střižného charakterní. Přitom je méně hmotná než dosud používaná vrstva laminátu a její zhotovení je rychlé a levné.The bonding layer, formed by joining two adhesive interlayers, provides a perfectly strong bond between the rigid foam layer and the rigid thermoplastic layer, transmitting and damping the deformation forces, in particular, of shear. In doing so, it is less massive than the laminate layer used so far, and its production is quick and inexpensive.
Příkladná provedení jsou popsána dále a schématicky znázorněna na připojeném výkrese představujícím průřez stěnou konstrukční části zařízení pro pokovování, moření nebo barvení kovů.Exemplary embodiments are described below and schematically shown in the accompanying drawing, representing a cross-section through a wall of a structural part of a metal plating, pickling or dyeing device.
PřikladlHe did
Jádro 2 z tvrdé pěny je z polyvinylchloridu a je opatřeno na jedné straně vrstvou 2 umělé nenasycené polyesterové pryskyřice, zesílené rohoží ze skleněných vláken a z druhá strany vrstvou 2 tvrdého polyvinylchloridu, přilepeného k jádru 2 pomocí spojovací vrstvy 2 složené z jedné lepivé mezivrstvy 2 roztoku polyvinylchloridu v metylenchloridu a druhé lepivé vrstvy 6 z roztoku syntetického kaučuku ve směsi benzenu a xylenu. Toto složení je vhodné pro konstrukci zařízení pro pokovování, barvení nebo moření kovů, jehož tepelné zatíženi nepřekročí 40 °C.The rigid foam core 2 is made of polyvinyl chloride and is provided on one side with a layer of artificial unsaturated polyester resin reinforced with a glass fiber mat and on the other side with a layer 2 of hard polyvinyl chloride glued to the core 2 using a tie layer 2 composed of one adhesive interlayer 2 of polyvinyl chloride solution in methylene chloride and a second adhesive layer 6 of a synthetic rubber solution in a mixture of benzene and xylene. This composition is suitable for the construction of equipment for metal plating, dyeing or pickling, whose thermal load does not exceed 40 ° C.
Příklad 2Example 2
Jádro 2 1 tvrdé polyuretanové pěny a je z vnější strany opatřeno vrstvou 2 z epoxidové pryskyřice, zesílené rounem ze skleněných vláken a z vnitřní strany vrstvou J z tvrdého polxypropylenu, přilepeného k jádru 2 z tvrdé polyuretanové pěny jednou lepivou mezivrstvou 2 z roztoku polyvinylchloridu v metylenchloridu a druhou lepivou mezivrstvou 6 z roztoku syntetického kaučuku ve směsi benzenu a toluenu. Toto složení konstřukční části je vhodné např. pro vany odaašíovacích nebo barvicích lázní s trvalou provozní teplotou do 80 °C.Core 2 1 hard polyurethane foam and from the outside with a layer 2 of an epoxy resin reinforced with glass fiber fleece and the inside layer J hardwood polxypropylenu, adhered to the core 2 of hard polyurethane foam one adhesive intermediate layer 2 of a solution of polyvinyl chloride in methylene chloride a second adhesive interlayer 6 of a solution of synthetic rubber in a mixture of benzene and toluene. This composition of the construction part is suitable eg for bathtubs of degreasing or dyeing baths with a continuous operating temperature up to 80 ° C.
Příklad 3Example 3
Je obdobou konstrukčního dílu podle příkladu 1, s tím, rozdílem, že jádro 2 je 2 až 3krát silnější než u příkladu 1 a je opatřeno na jedné straně vrstvou 2 epoxidové pryskyřice zesílené uhlíkovými vlákny. Toto složení je vhodné pro· konstrukce, které jsou vystaveny nárazům nebo jsou jinak mechanicky namáhány. Složení je dále vhodné pro provozy, kde připadá v úvahu ehemické namáhání kyselinou fluorovodíkovou.It is similar to the component of Example 1, except that the core 2 is 2 to 3 times thicker than that of Example 1 and is provided with a carbon fiber reinforced epoxy resin layer 2 on one side. This formulation is suitable for structures that are subject to impact or otherwise mechanical stress. Furthermore, the composition is suitable for plants where the haemofluoric acid stress is considered.
Claims (1)