CS225580B1 - Pigment paste of water type made on the base of ferrugineous pigments - Google Patents
Pigment paste of water type made on the base of ferrugineous pigments Download PDFInfo
- Publication number
- CS225580B1 CS225580B1 CS731282A CS731282A CS225580B1 CS 225580 B1 CS225580 B1 CS 225580B1 CS 731282 A CS731282 A CS 731282A CS 731282 A CS731282 A CS 731282A CS 225580 B1 CS225580 B1 CS 225580B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- parts
- pigments
- aqueous
- pigment
- weight
- Prior art date
Description
Vynález se týká nových pigmentových past vodného typu na bázi železitých pigmentů obsahující anionaktivní anebo ionogenní tenzidy a případně další aditiva. Jsou především vhodné pro přípravu nátěrových hmot, zejména emailů a v celé řadě dalších specielních aplikacích.The present invention relates to novel aqueous pigments of the ferric pigment type comprising anionic and / or ionic surfactants and optionally further additives. They are especially suitable for the preparation of paints, especially enamels and in many other special applications.
V technické praxi i v širokém měřítku se používají výrobky, které se pro jednotlivé druhy aplikací vybarvují různými pigmenty, především pak železitými. Lze tak vybarvovat nátěrové vodou ředitelné hmoty, tmely na bázi vodných disperzí, mořidla na dřevo, azbestocementové výrobky, vápenatocementové omítkoviny apod. Zatímco nátěrové hmoty a tmely ve formě disperzí nebo ve vodě rozpustné se vybarvují přímo ve hmotě, jakož i omítkoviny, tak azbestocementové výrobky na rozdíl od nich lze vybarvovat jak ve hmotě tak i povrchově. K pigmentaci se mohou používat pigmenty v práškové nebo pastovité formě. Množství výrobků je vybarvováno železitými pigmenty v širokém rozsahu barevných odstínů, kde základní barvy jsou žlutá, červená, hnědá a černá. Jejich předností je vysoká odolnost proti povětrnosti i chemikáliím. Typy železitých pigmentů vyráběných kalcinací při vysokých teplotách mají velmi širokou distribuci velikosti částic od 1 do 70 ,«m a obsahují agregáty, což jsou vzájemně pevně spojené monočástice, které navzájem nelze oddělit běžným způsobem dispergace v pojivech. Tyto velké částice jsou značnou závadou při použití v nátěrových hmotách, zejména emailech. Pro snížení velikosti částic se provádí tzv. mikronizace, např. vzájemným obrušováním v jett-millech, to jest v zařízeních pracujících s přetlakem plynů. Pro zvýšení smáčivosti těchto pigmentů vodou se provádí jejich hydrofilizace. Pro pigmentaci i pro vybarvování je nejvýhodnější velikost částic od 0,01 do 1 μΐη. Částice pod 0,1 ,um zvyšují významně barvivost při snížené kryvosti, naopak částice nad 0,1 μηι do 1 ,um dávají vysokou kryvost nátěrů. Při přípravě pigmentových past z práškovitých pigmentů je třeba značného množství mechanické práce, a zároveň se zvyšuje prašnost pracovního prostředí atd. Jsou známy způsoby výroby železitých pigmentů srážením ve vodném prostředí, které se filtrací a sušením převádí do práškovité formy. Nevýhodou těchto postupů je značná spotřeba energie pro odstranění vody, reopexní chování těchto disperzí, které zhoršuje jejich čerpatelnost apod. Použití železitých pigmentů vyrobených srážením v práškovité formě je prakticky stejné, jako u typů vyrobených kalcinací. Pojivá nátěrových hmot jsou nejčastěji na bázi akrylátových anebo methakrylátových kopolymerů, oxidačně tvrditelné typy na bázi alkydů a epoxyesterů a podle typů těchto organických pojiv se rozlišují na typy na vzduchu zasychající fyzikálně nebo chemicky a na typy termoreaktivní vytvrzované při zvýšených teplotách.In technical practice and on a large scale, products are used that are colored with different pigments, especially ferric pigments, for individual applications. Water-based paints, water-based dispersion sealants, wood stains, asbestos-cement products, lime-cement renderings, etc. can be dyed. in contrast, they can be colored both in matter and surface. Pigments in powder or paste form can be used for pigmentation. Many products are colored with ferric pigments in a wide range of colors, where the basic colors are yellow, red, brown and black. Their advantage is high resistance to weathering and chemicals. The types of ferric pigments produced by calcination at high temperatures have a very wide particle size distribution of from 1 to 70 .mu.m and contain aggregates, which are firmly bonded monoparticles which cannot be separated by conventional dispersion in the binders. These large particles are a considerable problem when used in paints, especially enamels. In order to reduce the particle size, so-called micronization is carried out, e.g. To increase the wettability of these pigments with water, they are hydrophilized. A particle size of from 0.01 to 1 μΐη is most suitable for pigmentation and dyeing. Particles below 0.1 µm significantly increase coloration at reduced opacity, while particles above 0.1 µm to 1 µm give high coating opacity. The preparation of pigment pastes from powdered pigments requires a considerable amount of mechanical work, while increasing the dustiness of the working environment, etc. Methods for producing ferric pigments by precipitation in an aqueous medium are known, which are transformed into powder form by filtration and drying. The disadvantage of these processes is the considerable energy consumption for water removal, the reopex behavior of these dispersions, which impairs their pumpability, etc. The use of ferric pigments produced by precipitation in powder form is practically the same as for the types produced by calcination. The binders of paints are mostly based on acrylate or methacrylate copolymers, oxidatively curable types based on alkyds and epoxy esters and according to the types of these organic binders are differentiated into air-drying types physically or chemically and thermoreactive types cured at elevated temperatures.
Výše uvedené nedostatky odstraňuje předložený vynález, jehož předmětem jsou pigmentové pasty vodného typu na bázi želežitých pigmentů, obsahující anionaktivní anebo ionogenní tenzidy a případně další aditiva. Podstata tohoto vynálezu spočívá v tom, že pigmentové pasty sestávají hmotnostně ze 100 dílů vodné disperze železitých pigmentů získaných oxidačním srážením síranu železnatého z vodných roztoků vzduchem anebo kyslíkem za přítomnosti hydroxidu amonného o velikosti částic 0,001 až 15 fim a s obsahem vody 10 až 70 °/o, dále z 0,01 až 3 dílů tenzidu ze skupiny zahrnující etoxylované nonylfenoly o hodnotě hydrofilnělipofilní rovnováhy 8 až 14, fosfáty, sulfáty nebo sulfonové sloučeniny odvozené od alifatických alkoholů s počtem uhlíkových atomů 12 až 18, případně mono- a tetraetoxylovaných nebo od polyglykoletherů a až 100 dílů aditiv ze skupiny koloidních stabilizátorů typu kopolymerů kyseliny akrylové anebo methakrylové s vinylickými monomery, plniv, pigmentů, odpěňovačů a fungicidních látek.The above-mentioned drawbacks are overcome by the present invention, which are based on water-based pigment pastes based on iron pigments containing anionic and / or ionic surfactants and optionally other additives. SUMMARY OF THE INVENTION The pigment pastes consist of 100 parts by weight of an aqueous dispersion of ferric pigments obtained by oxidative precipitation of ferrous sulphate from aqueous solutions with air or oxygen in the presence of an ammonium hydroxide having a particle size of 0.001-15 µm and a water content of 10-70%. and from 0.01 to 3 parts of a surfactant selected from the group consisting of ethoxylated nonylphenols having a hydrophilic lipophilic balance of 8 to 14, phosphates, sulfates or sulfone compounds derived from aliphatic alcohols having a carbon number of 12 to 18, optionally mono- and tetraethoxylated or polyglycol ethers; up to 100 parts of additives from the group of colloidal stabilizers such as copolymers of acrylic or methacrylic acid with vinyl monomers, fillers, pigments, antifoams and fungicides.
Pigmentové pasty podle uvedeného vynálezu jsou ve vodě snadno dispergovatelné, čerpatelné a případně odsazené vodné podíly jsou redispergovatelné rozmícháním.The pigment pastes of the present invention are readily dispersible in water, pumpable, and optionally spaced aqueous fractions are redispersible by mixing.
Vodné disperze železitých pigmentů se připravují z vodných roztoků síranu železnatého oxidací vzduchem za přítomnosti hydroxidu amonného, kde teplotou a hodnotou pH se řídí barevný odstín vytvořené pigmentové složky. Promytím vodou se odstraní nežádoucí ve vodě rozpustné složky. Získá se pigmentová pasta železitých pigmentů o velikosti částic 0,001 až 15 μηι s obsahem 10 až 70 % hmot. vody. Obsah vody lze snížit i prostou sedimentací pasty a zároveň oddělit nejmenši částice a tím posunout distribuci velikostí částic až pod 1 μΐη, tedy do oblasti odpovídající mikronizovaným pigmentům. Srážené pigmenty mají v porovnání s pigmenty připravovanými vypalováním významně sníženou velikost částic, obvykle do 15 μΐη nebo v rozsahu 0,01 až 8 μΐη. Jsou tedy mimořádně vhodné pro přípravu nátěrových hmot, zejména emailů. Většina nátěr, hmot obsahuje mimo pigmentů i plniva. Železité pigmenty s vysokou barvivostí zvyšují významně i kryvost nátěr, filmů.Aqueous dispersions of ferric pigments are prepared from aqueous solutions of ferrous sulfate by oxidation with air in the presence of ammonium hydroxide, where the temperature and pH value of the pigment component formed is controlled. Washing with water removes undesirable water-soluble components. A pigment paste of ferric pigments having a particle size of 0.001 to 15 μηι containing 10 to 70% by weight is obtained. water. The water content can be reduced even by simple sedimentation of the paste, while at the same time separating the smallest particles and thus moving the particle size distribution below 1 μΐη, ie the area corresponding to the micronized pigments. The precipitated pigments have a significantly reduced particle size compared to the pigments prepared by firing, usually up to 15 μΐη or in the range of 0.01 to 8 μΐη. They are therefore particularly suitable for the preparation of paints, especially enamels. Most coatings, in addition to pigments contain fillers. Iron pigments with high coloring significantly increase the opacity of paints and films.
Pro přípravu pigmentových past lze použít přídavek tenzidu anionaktivního anebo ionogenního typu. Mezi neionogenní tenzidy patří zejména etoxylované alkylalkoholy a nonylfenoly o hodnotě hydrofilnělipofilní rovnováhy (HLB) 8 až 14, jako jsou např. trietoxylovaný laurylalkohol, pentaetoxylovaný nonylfenol, dekaetoxylovaný nonylfenol apod. Jako tenzidy anionaktivního typu se používají fosfáty, sulfáty či sulfonové sloučeniny odvozené od alifatických alkoholů s počtem uhlíkových atomů 12 až 18, případně monoa tetraetoxylovaných nebo od polyglykoletherů, ve formě solí jednomocných kaliontů, jako např. laurylfosfát či sulfát sodný, trietoxylovaná směs alkoholů C12 až C18, monofosfát amonný, ethylenpropylenglykolfosfát draselný apod. Přídavkem tenzldů, především hexametafosfátu se dosáhne změny Teologického charakteru disperze, kde reopexní charakter se převádí na tixotropní. To se projevuje snížením konzistence při míchání a tedy i čerpání.The addition of anionic or ionic surfactant surfactants can be used to prepare pigment pastes. Nonionic surfactants include, in particular, ethoxylated alkyl alcohols and nonylphenols having a hydrophilic lipophilic balance (HLB) value of 8 to 14, such as triethoxylated lauryl alcohol, pentaethoxylated nonylphenol, decethoxylated nonylphenol, and the like. Anionic-type surfactants include phosphates, sulfates or sulfonates having a carbon number of 12 to 18, optionally mono-tetraethoxylated or polyglycol ethers, in the form of monovalent cation salts such as lauryl phosphate or sodium sulfate, a triethoxylated mixture of C 12 to C 18 alcohols, ammonium monophosphate, ethylenopropylene glycol phosphate or the like; a change in the theological character of the dispersion is achieved, where the reopex character is converted to thixotropic. This results in a reduced consistency in mixing and thus pumping.
Podle způsobu aplikace se přidávají další složky. Z použitých aditiv jsou to především koloidní stabilizátory typu kopolymerů kyseliny akrylové anebo methakrylové s vinylickými monomery, jako např. akrylátové záhustky na bázi kyseliny methakrylové, ethylakrylátu styrenu a difumarátu o čísle kyselosti sušiny 250 až 350 mg KOH/g. Dále jako plniva se používají práškové anorganické látky, jako např. vápenec, mastek, slída apod., čímž lze značně snížit celkový obsah vody. Z pigmentů pak především titanová běloba pro dosažení pastelových odstínů.Depending on the method of application, additional ingredients are added. The additives used are, in particular, colloidal stabilizers of the type of copolymers of acrylic or methacrylic acid with vinyl monomers, such as methacrylic acid acrylate dyes, styrene ethyl acrylate and difumarate having a dry acid number of 250 to 350 mg KOH / g. Furthermore, powdered inorganic substances such as limestone, talc, mica and the like are used as fillers, whereby the total water content can be greatly reduced. The pigments are mainly titanium white to achieve pastel shades.
Z fungicidních látek se používají ty, které zlepšují skladovatelnost produktu, jako např. proti tvorbě plísní se do pigmentových past přidává dimethyllaurylamoniumbromid (ajatin) nebo ve vodě rozpustné sloučeniny Zn, Cu apod.Among the fungicides, those which improve the shelf-life of the product are used, for example dimethyllaurylammonium bromide (ajatin) or water-soluble compounds Zn, Cu and the like are added to the pigment pastes to prevent mold formation.
Výroba pigmentových past o daném složení se provádí tak, že základní disperze pigmentů vyrobených srážením se zbaví nadbytečné vody a to bud1 známými způsoby v kololisech, odstředivkách, nebo přídavkem tenzidů či práškovými plnivy. Po sedimentaci se horní vrstva vody odtáhne.Preparation of the pigment paste composition is carried out such that the base pigment dispersion prepared by precipitation was freed of excess water, either in one known methods kololisech, centrifuges, or by adding surfactants or powdered fillers. After sedimentation, the upper layer of water is drawn off.
Pigmentové pasty podle vynálezu jsou vhodné pro náročné aplikace, jako jsou antikorozní vodou ředitelné nátěrové hmoty akrylátové základní a vrchní, polotransparentní nátěry, vodná mořidla na dřevo. Ve vodných disperzích obsahujících cement, vápno popř. sádru dovolují již při sníženém obsahu dosáhnout dobrého vybarvení, což má příznivý vliv i na výsledné mechanické vlastnosti hotových výrobků, jako např. eternitů, omítkovin apod. Jsou v odstínech žluté, červené, červenohnědé, černé a hnědé.The pigment pastes according to the invention are suitable for demanding applications such as anti-corrosion water-borne acrylic primers and topcoats, semi-transparent coatings, aqueous wood stains. In aqueous dispersions containing cement, lime or. Gypsum allows good coloring even at a reduced content, which has a positive effect on the resulting mechanical properties of finished products such as eternites, plasters, etc. They are in shades of yellow, red, red-brown, black and brown.
Předmět vynálezu je dále doložen příklady provedení.The invention is further illustrated by the following examples.
Příklad 1Example 1
Pigmentová pasta pro vybarvování azbestocementových výrobků Kysličník železitý ěervenohnědý vyrobený srážením ve formě vodné disperze o sušině % hmot. o velikosti částic 0,01 až 5 μΐη 100 hmot. dílů hexamethafosfát sodný 0,9 hmot. díluPigment paste for dyeing asbestos-cement products Red-brown iron oxide produced by precipitation in the form of an aqueous dispersion with dry matter% wt. with a particle size of 0.01 to 5 μΐη 100 wt. 0.9 parts by weight of sodium hexamethaphosphate; part
V nádobě opatřené míchadlem se k pigmentové disperzi přidá hexamethafosfát sodný a míchá se do zřetelného snížení konzistence. Hmota se nechá odstát, až se rozdělí do dvou fází. Horní vodná fáze se odčerpá a zbytek se po rozmíchání čerpá do obalů. Vyrobená pigmentová pasta má sušinu 65 % hmot.In a flask equipped with a stirrer, sodium hexamethaphosphate is added to the pigment dispersion and mixed until the consistency is noticeably reduced. The mass is allowed to stand until it is separated into two phases. The upper aqueous phase is pumped off and the remainder is pumped into containers after mixing. The pigment paste produced has a dry matter content of 65% by weight.
Příklad 2Example 2
Pigmentová pasta pro disperzní lazurovací lakPigment paste for dispersion glazing varnish
Železitá žluť vyrobená srážením ve formě vodné disperze o sušině 45 °/o hmot. a velikosti částic 0,01 až 2 μΐη 98 hmot. dílů Pigmentová disperze černá na bázi kysličníků Fe vyrobených srážením o sušině 50 % hmot. a vel. částic 0,01 až 2,0 hmot. dílyFerric yellow produced by precipitation in the form of an aqueous dispersion having a dry weight of 45% by weight. and particle sizes of 0.01 to 2 μΐη 98 mass. parts Pigment dispersion black based on Fe oxides produced by coagulation with dry matter 50% wt. and particle sizes of 0.01 to 2.0 wt. parts
Hexamethafosfát sodný 0,78 hmot. dílu Oktylalkohol 0,5 hmot. díluSodium hexamethaphosphate 0.78 wt. 0.5 wt. part
Antiplísňové aditivurn dimethyllaurylbenzylamonlumbromid (Ajatin) 0,2 hmot. dílu Do disperze železité žlutí se za míchání přidá disperze železité černě, ve které je rozpuštěn hexamethafosfát a po homogenizaci se přidá antiplísňové aditivurn ajatin a nakonec se přidá oktylalkohol.Antifungal additive dimethyllaurylbenzylammonium bromide (Ajatin) 0.2 wt. To the ferric yellow dispersion is added, with stirring, a black iron dispersion in which hexamethaphosphate is dissolved and, after homogenization, an antifungal additive ajatin is added and finally octyl alcohol is added.
Příklad 3Example 3
Pigmentová pasta pro tónování disperzních nátěr, hmot vodou ředitelných Kysličník železitý hnědý vyrobený srážením ve formě vodné disperze o sušiněPigment paste for tinting of dispersion paints, water-soluble masses Iron oxide brown produced by precipitation in the form of an aqueous dispersion with dry matter
Claims (1)