CS219498B1 - A method for reducing the alkali carbonate content of an insulating layer

Info

Publication number: CS219498B1
Application number: CS350780A
Authority: CS
Inventors: Frantisek Novak; Jan Novak
Original assignee: Frantisek Novak; Jan Novak
Priority date: 1980-05-20
Filing date: 1980-05-20
Publication date: 1983-03-25

Abstract

Odstranění škqdlivých alkalických uhličitanů ze: zdivá, vytvořených oxidací vodních skel ve zdivu, se dosáhne vtlačením kysličníku uhličitého CO2 infúzními vrty, které sloužily k zavedení vodních skel, do zdivá prosyceného vodními skly, a opakovaný výplach zdivá tlakovou vodou zaváděnou infúzními vrty.Removal of harmful alkaline carbonates from masonry, formed by oxidation of water glasses in the masonry, is achieved by injecting carbon dioxide CO2 through infusion wells, which were used to introduce water glasses, into the masonry saturated with water glasses, and repeated rinsing of the masonry with pressurized water introduced through infusion wells.

Description

Vynález se týká způsobu snížení obsahu alkalických uhličitanů v izolační vrstvě zdivá, vytvořené užitím vodního skla zaváděného infúzními vrty, jímž se zabraňuje jejich škodlivým účinkům na vlastnosti izolační vrstvy i zdivá a umožňuje použití méně nákladných hmot. Doposud se alkalické •uhličitany z izolační vrstvy neodštraňují, vyrážejí z povrchu infúzních vrtů a v případě jejich zaplněni putují až do omítek, nebo je vodní sklo nahrazeno nákladnými látkami.BACKGROUND OF THE INVENTION The present invention relates to a method for reducing the alkali carbonate content of a masonry insulating layer formed by the use of waterglass introduced by infusion boreholes, thereby avoiding their detrimental effects on the insulating layer and masonry properties and allowing the use of less expensive materials. Until now, alkaline carbonates • have not been removed from the insulating layer, are pumped out of the surface of the infusion wells and, if filled, travel to plaster or the water glass is replaced by expensive substances.

Uvedené nevýhody odstraňuje způsob snížení obsahu alkalických uhličitanů v izolační vrstvě zdivá, vytvořené užitím vodního skla, kterého podstata spočívá v tom, že po vpravení vodního skla nebo těsnící směsi vodní sklo obsahující, infúzními vrty do zdivá izolační vrstvy se vtlačí plynný kysličník uhličitý CO2 s vyšší koncentrací za přetlaku 0,2 MPa až 0,3 MPa, reakcí s vodním sklem se vytvoří polymerní kyselina křemičitá SÍO2 a alkalické uhličitany, které se rozpustí v záměsové vodě vodního skla, vypařující se rychle z povrchů infúzních vrtů, neboť její páry jsou vytlačovány přirozeným přetlakem vodních par v prostředí vzduchu a hmotnějšího kysličníku uhličitého CO2 v infúzních vrtech zbylého, se vyloučí na stěnách infúzních vrtů v podobě výjkvětů a krystalů, které se odstraní výplachy infúzních vrtů vodou nebo 2- až 5pro9 8 centním roztokem kyseliny, např. octofvé. Nový účinek vynálezu je dán odstraněním škodlivých účinků alkalických uhličitanů na vlastnosti izolační vrstvy zdivá s užitím vodního skla a na zdivo· samotné.The above-mentioned disadvantages are eliminated by the method of reducing the content of alkali carbonates in the masonry insulating layer formed by the use of water glass, which consists in injecting into the masonry insulating layer gaseous carbon dioxide CO2 with a higher water content. concentration at an overpressure of 0.2 MPa to 0.3 MPa, reaction with water glass forms polymeric silicic acid SiO2 and alkali carbonates, which dissolve in the mixing water of water glass, evaporating rapidly from the surfaces of infusion wells, because its vapors are displaced by natural by excess water vapor pressure in the air and more massive carbon dioxide CO2 remaining in the drilling wells, it is eliminated on the walls of the drilling wells in the form of efflorescence and crystals which are removed by drilling the drilling wells with water or 2 to 5 to 8 cent. The novel effect of the invention is due to the elimination of the harmful effects of alkali carbonates on the properties of the waterglass insulation layer and on the masonry itself.

PříkladyExamples

1. Při vytvoření nepropustné izolační vrstvy napříč zdí vpravením těsnicí směsi na bázi vodního skla do zdivá izolační vrstvy, se vtlačí dále do infúzních vrtů zia přetlaku 0,2 MPa až 0,3 MPa plynný kysličník uhličitý CO2 s vyšší koncentrací a po vyloučení solí alkalických uhličitanů po· stěnách imfúzních vrtů se tyto vypláchnou vodou, s výhodou tlakovou, nebo slabým 2 laž 5procentním roztokem kyseliny octové.1. To form an impermeable insulating layer across the wall by incorporating a water-based sealant into the masonry insulating layer, pressurized carbon dioxide gaseous CO2 with a higher concentration and after the addition of alkali salts are injected further into infusion boreholes at pressures of 0.2 MPa to 0.3 MPa. The carbonates on the walls of the wells are rinsed with water, preferably a pressurized or weak 2 to 5 percent acetic acid solution.

2. Při vytvoření svislé příčné izolační stěny za použití sodného vodního skla, se po vpravení těsnicí směsi se sodným vodním sklem po prosycení zdivá mezi vrty vtlačuje do infúzních vrtů plynný kysličník uhličitý CO2 s přetlakem do 0,3 MPa s vyšší koncentrací a po vyloučení výkvětů a krystalů alkalických uhličitanů v infúzních vrtech se tyto odstraní výplachem vodou nebo slabým roztokem kyseliny, např. octové.2. When creating a vertical transverse insulating wall using sodium water glass, after insertion of the sealing mixture with sodium water glass after saturation the masonry between boreholes is injected into infusion boreholes CO2 of carbon dioxide with overpressure up to 0,3 MPa with higher concentration and after efflorescence elimination and the alkali carbonate crystals in the infusion wells are removed by rinsing with water or a weak acid solution such as acetic.

Vynález se dá využít při vytváření izolačních chemických vrstev s užitím vodního skla pro vysoušení objektů všeho druhu.The invention can be used in forming insulating chemical layers using water glass for drying objects of all kinds.

Claims

SUBJECT

A method of reducing the content of alkali carbonates in a masonry insulation layer formed by a waterglass introduced into a masonry insulation layer by infusion wells, characterized in that after the waterglass or waterglass sealing compound is introduced, it is pressed into the infusion wells after

YNALEZU overpressure of carbon dioxide gas and, after covering the surfaces of the infusion wells, efflorescence of alkali carbonates, these are removed by flushing the infusion wells with water or a weak acid solution such as acetic.