CS199480B1 - Paint based on polyesters modified with fatty acids for universal use - Google Patents
Paint based on polyesters modified with fatty acids for universal use Download PDFInfo
- Publication number
- CS199480B1 CS199480B1 CS684578A CS684578A CS199480B1 CS 199480 B1 CS199480 B1 CS 199480B1 CS 684578 A CS684578 A CS 684578A CS 684578 A CS684578 A CS 684578A CS 199480 B1 CS199480 B1 CS 199480B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- fatty acids
- universal use
- polyesters modified
- paint based
- coatings
- Prior art date
Description
(54)(54)
NÁTĚROVÁ HMOTA NA BÁZI POLYESTERU MODIFIKOVANÝCH ' MASTNÝMI KYSELINAMI PRO UNIVERSÁLNÍ POUŽITÍPOLYESTER-BASED PAIN modified with 'FATTY ACIDS' FOR UNIVERSAL USE
Vynález se týká nové formulace nátěrových hmot pro dekorační i ochranné účely na bázi alkydových pryskyřic a řeší problém stárnutí nátěrů při současné úspoře deficitních rostlinných olejů. ·The present invention relates to a new formulation of coating compositions for decorative and protective purposes based on alkyd resins and solves the problem of coating aging while saving vegetable oils deficient. ·
Pro přípravu syntetických nátěrových hmot se používají jako filmotvorná složka alkydové pryskyřice, což jsou polyestery kyseliny ftaloyé s vícemoenými alkoholy, např. glycerin, pentaeritrit, modifikované nenasycenými mastnými kyselinami o počtu 16 až 18 atomů uhlíka, např. kyselina linolová, linolěnová, olejová, nebo směsí těchto kyselin. Vlastnosti nátěrových hmot, tj. zasýchání, tvrdost, vláčnost a pevnost nátěru, jsou ovlivněny obsahem a druhem mastných kyselin. Tak pro dosažení vlastností požadovaných pro nátěry odolné povětrnostním vlivům je zpravidla obsah mastných kyselin 45 až 80 %. Všeobecnou nevýhodou těchto nátěrů je její křehnutí během stárnutí. Menšího křehnutí a tím vyšší odolnosti na povětrnosti se dosahuje zvýšeným obsahem mastných kyselin a použitím kyselin s menším počtem dvojných vazeb, ovšem za ceúu prodloužení zasychání a protvrdání nátěrů.Alkyd resins, which are polyesters of phthalic acid with polyhydric alcohols, e.g. glycerin, pentaeritrite, modified with unsaturated fatty acids of 16 to 18 carbon atoms, e.g. mixtures of these acids. The properties of paints, ie drying, hardness, suppleness and strength of the paint, are influenced by the content and type of fatty acids. Thus, in order to achieve the properties required for weather-resistant coatings, the fatty acid content is generally 45 to 80%. A general disadvantage of these coatings is their brittleness during aging. Less brittleness and thus higher weather resistance is achieved by the increased content of fatty acids and the use of acids with a lower number of double bonds, but with the aim of prolonging the drying and hardening of the coatings.
Používání zvláčfiovadel se v lekářské praxi uplatňuje hlavně u nátěrových hmot fyzikálně zasychajících, jako nitrocelulosovýéh, polymerétových. Přídavek těchto známých a běžných zvléčňovadel, např. esterů kys. ftalové a vyšších alkoholů, k alkydovým pryskyřicím přináší řadu nevýhod, které zá2 braňují jejich použití, jako je zpomalené zasychání, dolepování, menší přilnavost, termoplasticita.The use of emollients is mainly used in medical practice for physically drying coatings, such as nitrocellulose, polymeric coatings. The addition of these known and conventional emollients, such as phthalic acid esters and higher alcohols, to the alkyd resins presents a number of disadvantages that prevent their use, such as retarded drying, sticking, less adhesion, thermoplasticity.
Tyto nevýhody nemají nátěrové hmoty podle vynálezu, jejichž podstata spočívá v tom, že obsahují jako filmotvornou složku 10 až 70 % hmotn. polyesteru modifikovaného 35 - 80 % mastných kyselin a 1 až 20 % externího zvláčftovadla, které tvoří epoxidovaný ester vyšších mastných kyselin, jehož jednou složkou je monotopický alifatický alkohol o 2 až 8 atomech uhlíku a druhou složku tvoří mastná kyselina s 16 - 22 atomy uhlíku. Tuto filmotvornou složku lze kombinovat s pigmenty, plnidly, aditivy podle požadovaných vlastností.These drawbacks do not have the coating compositions according to the invention, which consist in that they comprise from 10 to 70% by weight of the film-forming component. a polyester modified with 35-80% fatty acids and 1-20% of an external plasticizer which is an epoxidized ester of higher fatty acids, one component of which is a monotopic aliphatic alcohol of 2 to 8 carbon atoms and the other component is a fatty acid of 16-22 carbon atoms. This film-forming component can be combined with pigments, fillers, additives according to the desired properties.
Tímto postupem se dosáhne nátěrových hmot, jejichž nátěry rychle zasychají, jsou trvale pružné a vláčné a mají vysokou odolnost proti povětrnostním vlivům. Laboratorními zkouškami bylo prokázáno že běžný alkydový email bílého odstínu s obsahem 33 % alkydové pryskyřice (obsah mastných kyselin v alkydu je 60 %,) dává nátěry, které po 2 měsících vystavení na povětrnosti při ražení úderem dle ČSN 67 3082 praskají při pádu závaží s výše 0,05 m. Naproti tomu email podle tohoto vynálezu - obsah mastných kyselin 45 % při stejné rychlosti zasychání dává nátěry zcela odolné při ražení s výše 1 metru i po 12 měsících. Současně dochází k úspoře mastných kyselin.This process results in coatings whose coatings dry quickly, are permanently elastic and supple and have a high resistance to weathering. Laboratory tests have shown that conventional white alkyd enamel with 33% alkyd resin content (60% fatty acid content in alkyd) gives coatings that crack after 2 months of exposure to impact punching according to CSN 67 3082 when the weights fall above 0.05 m. In contrast, the enamel of the present invention - a fatty acid content of 45% at the same drying rate gives coatings completely resistant to embossing at a height of 1 meter even after 12 months. At the same time, fatty acids are saved.
Vynález je blíže vysvětlen na několika příkladech:The invention is explained in more detail in several examples:
Příklad 1 .Example 1.
Transparentní lak se vyrobí smíšením 50 hm.d. roztoku polyesteru, modifik. 40 % mastných kyselin, 38 hm.d. roztoku polyesteru modifik. 55 % mastných kyselin, 10 hm. d. epoxidovaného butylesteru mastných kyselin sojového oleje, 2 hm. d. sušidla, aditiva.The transparent lacquer is made by mixing 50 wt. polyester solution, mod. 40% fatty acids, 38 wt. Polyester Solution Mod. 55% fatty acids, 10 wt. d. epoxidized soybean oil fatty acid butyl ester, 2 wt. d. desiccants, additives.
Příklad 2Example 2
Bílá email pro nátěry vystavené povětrnosti se vyrobí snímáním 26 hm. d. roztoky polyester, pryskyřice modifik. 40 % mastných kysélin, 26 hm. d. roztoku polyester, pryskyřice modifik. 55 % mastných kyselin, 5 hm. d. epoxidovaného butylesteru mastných kyselin sojového oleje, .20 hm. d. titanové běloby, 20 hm. d. minerálních plnidel, 3 hm. d. aditiv a sikativů.White enamel for weathered coatings is produced by scanning 26 wt. d. polyester solutions, resin mod. 40% fatty acids, 26 wt. d. polyester solution, resin mod. 55% fatty acids, 5 wt. d. epoxidized soybean oil fatty acid butyl ester, .20 wt. d. titanium dioxide, 20 wt. d. mineral fillers, 3 wt. d. additives and siccatives.
Příklad 3Example 3
Zelený email pro nátěry vystavené povětrnosti ae připraví smíšením 58 hm. d. roztoku polyesteru modif. 45 % mastných kyselin, 8 hm. d. epoxidového isobutylesteru mast. kyselin lněného oleje, 6 hm. d. zeleného pigmentu, 25 hm. d. minerálních plnidel, 3 hm. d, aditiv a sikativů.Green enamel for weathered paints and prepared by mixing 58 wt. d. polyester solution modif. 45% fatty acids, 8 wt. d. an epoxy isobutyl ester ointment. of linseed oil, 6 wt. d. green pigment, 25 wt. d. mineral fillers, 3 wt. d, additives and siccatives.
Claims (2)