CS199356B1 - Quick-drying alkaline bitumen emulsions,making protective layers,stable during storage - Google Patents
Quick-drying alkaline bitumen emulsions,making protective layers,stable during storage Download PDFInfo
- Publication number
- CS199356B1 CS199356B1 CS292476A CS292476A CS199356B1 CS 199356 B1 CS199356 B1 CS 199356B1 CS 292476 A CS292476 A CS 292476A CS 292476 A CS292476 A CS 292476A CS 199356 B1 CS199356 B1 CS 199356B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- protective layers
- quick
- bitumen emulsions
- weight
- during storage
- Prior art date
Description
Vynález se týká rychle schnoucích alkalických živičných emulzí vytvářejících hydrofobní ochranné vrstvy, stálých při skladování, a jejich kombinací s diperzemi alastomerů a plastomerů в přísadou nebo bez přísady polyglykoléterů a obvyklých plnidel· živičné emulze nabývají stále většího významu při stavbě silnic, ochraně staveb, v zemědělství a Jiných odvětvích hospodářství· Výhoda jejich používání spočívá, Jak známo, především ve zpracovatelnosti za studená a v bezepčné manipulaci s těmito produkty· Je známo, že živičné emulze lze Jednoduše míait s disperzemi elastomerd a plastomerů· Významu dosáhly především podobné kombinace s akučukovými latexy a polyvinylácetátovými disperzemi· Výhody těchto směsí se ukazují v jejich užitných hodnotách, to znamená po vyschnutí kombinací· Zde se sčítají vlastnosti živice a vlastnostmi plastomerd a elastomerů a rozšiřuje se tím značně aplikační oblast těchto látkových kombinací·FIELD OF THE INVENTION The present invention relates to quick-drying, alkaline bituminous emulsions forming storage-stable hydrophobic protective coatings, and combinations thereof with and without or without the addition of polyglycol ethers and conventional fillers with bitumen and plastomer dispersions. and other sectors of the economy · The advantage of their use lies, as is known, above all in the cold workability and in the safe handling of these products · It is known that bitumen emulsions can be easily mixed with dispersions of elastomers and plastomers. polyvinyl acetate dispersions · The advantages of these mixtures are shown in their utility values, that is to say after the combinations have dried up. Here, the properties of the resin and the properties of plastomers and elastomers are summed up, extending area of these substance combinations ·
Zvláštního významu dosáhly kombinace živičných emulzí s kaučukovým latexem, Jež se přednostně používají k prováděníizolace proti zemní vlhkosti, těsnění proti průsakové a tlakové vodě, izolace střech, vnitřní nátěry nádrží a podobné účely· Existuje řada aplikačních způosbů, Jež se zásadně dělí na Jednosložkové a dvousložkové postupy· PřiOf particular importance have been the combination of bitumen emulsions with rubber latex, which are primarily used for conducting insulation against ground moisture, leachate and pressure water sealings, roof insulation, tank interior coatings and similar purposes. There are a number of application ways that are fundamentally divided into one- and two-component Procedures · When
Jednosložkovém postupu se používají stabilní kombinace živičných emulzí s hlinitými a bentonitovými emulgátory в kaučukovým latexem· Film těchto kombinací se vytváří po odpařeníStable combinations of bituminous emulsions with alumina and bentonite emulsifiers in rubber latex are used in a one-component process · Film of these combinations is formed after evaporation
199 356199 356
199 359 emulzní vody·199 359 emulsion water ·
V dvousložkového postupu se používají nestabilní a polostabilní kombinace živičných emulzí e ani ot aktivní mi emulgátory a kaučukovými latexy, jež se při postupu nanášení vysrážejí roztokem chloridu vápenátého. Nevýhodou u dvousložkového postupu je příliš rychlé vytváření filmu, jež vyvolává zejména na středních plochách pozdější vznik puchýřů, velké náklady při provádění postupu a malá stabilita komerčních výrobků· Z toho důvodu nabývá jednoduchý jednosložkový postup stále většího významu· Zvláětní nedostatek uvedeného postupu spočívá ve velké citlivosti filmů a vrstev vůči vodě, jež je zejména v počáteční fázi po zpracování největší· Malá vzdornost filmů emulze proti vodě však zůstává i po odpaření emulzní vody· Vysušené filmy a vrstvy obsahují kromě základních složek Živice a plastomerů, popřípadě elastomeru, ještě 2načná množství netěkavých emulgátorů, stabilizátorů a zahuštovadel, nutných pro vznik, existenci a stálost emulze, jež však vevětšině případů zůstávají rozpustné nebo bobtnatelné ve vodě· Známými stabilizačními prostředky jsou bílkoviny, Jako kaseiny, proteiny a proteidy, uhlohydráty nebo synteticky vyrobené organické sloučeniny, především polyakryláty s volnými jarboxylovými skupinami nebo jejich ve vodě rozpustné soli alakalických kovů nebo amonné soli· Všechny tyto produkty mají ten nedostatek, že jsou bu3 rozpustné, nebo bobtnatelné ve vodě· Mají nepříznivý vliv na živičný film, zejména při přímém působení vody· Vznikají přitom puchýře, měknutí izolační vrstvy, netěsnosti a jevy odlupování· Rovněž přísady plnidel, jako Živičných a azbestových vláken, grafitu nebo křemeliny, popřípadě vysocedispegační kyseliny křemičité, nevedly ke zlepšení, protože právě proti sedimentaci těchto látek, většinou těžších oproti emulzi, je třeba použít větších množství uvedených stabilizačních prostředků· Dosažení hydrofobní vrstvy je proto spojeno в velkými obtížemi nebo je možné teprve po vymytí těchto látek několikerým oplachem nebo výměnou vody·The two-component process uses unstable and semi-stable combinations of bituminous emulsions or active emulsifiers and rubber latices, which are precipitated by the calcium chloride solution during the deposition process. The disadvantage of the two-component process is the too rapid film formation, which causes later blistering, particularly on medium surfaces, high process costs and low stability of commercial products. Therefore, the simple one-component process becomes more and more important. · Low resistance of the emulsion films to water even after evaporation of the emulsion water · Dried films and layers contain, in addition to the basic constituents of Resins and plastomers or elastomers, also considerable amounts of non-volatile emulsifiers , stabilizers and thickeners necessary for the formation, existence and stability of the emulsion, but in most cases remain soluble or swellable in water. · Well-known stabilizers are proteins, such as casein y, proteins and proteins, carbohydrates or synthetically produced organic compounds, in particular polyacrylates with free jarboxyl groups or their water-soluble salts of alkali metals or ammonium salts · All these products have the drawback that they are either soluble or swellable in water · They are unfavorable affects bituminous film, especially when exposed to water · Blistering, insulation layer softening, leakage and peeling effects occur · Additives of fillers such as bituminous and asbestos fibers, graphite or diatomaceous earth, or highly dispersible silicic acid, did not lead to improvement because sedimentation of these substances, usually heavier than emulsions, requires the use of larger amounts of the stabilizing agents mentioned above. currency Water ·
Z toho důvodu je použití dosud známých emulzí a jejich kombinací s disperzemi plastomerů a elastomerů, zejména pro vnitřní nátěry vodních nádrží a staveb pro zemědělské účely, velmi problematické· Při nedbání uvedených nedostatků může dojít к velkým škodám na stavebním díle následkem odlupování, nabobtnávání a netěsnosti ochranných vrstev·Therefore, the use of the known emulsions and their combinations with dispersions of plastomers and elastomers, especially for internal coating of water reservoirs and buildings for agricultural purposes, is very problematic. · Failure to observe these defects can result in major structural damage due to peeling, swelling and leakage protective layers ·
Úkolem vynálezu je vyvinout vhodným výběrem a vyzkoušením stabilizátorů ve směsi s živičnými emulzemi a jejich kombinacemi 8 disperzemi elastomerů a plastomerů rychle schnoucí nátěrové hmoty stálé při skladování, vytvářející hydrofobní ochranné vrstvy·SUMMARY OF THE INVENTION It is an object of the present invention to provide, by suitable selection and testing of stabilizers in admixture with bitumen emulsions and combinations thereof.
Uvedený úkol je řešen kombinacemi živičných emulzí a/nebo jejich kombinací s disperzemi elastomerů a plastomerů в případnou přísadou polyglykoléterů a obvyklých plnidel, ktoré podle vynálezu obsahují 0,1 až 10 hmot· %, s výhodou 1 až 3 hmot· 10 až 40 % vodné disperze kopolymerů, bobtnatelných alkáliemi, na bázi butadienu, styrenu a kyseliny metakrylové a produktu esterifikace Diels-Alderových aduktů z kyseliny maleinové s alkoholy z kopolymerů oxtylénoxidu, například altylfenoxypolyetylénoxyetanolu, se 4 až 20 moly etylénoxidu·This object is achieved by combinations of bitumen emulsions and / or combinations thereof with elastomer and plastomer dispersions, optionally with the addition of polyglycol ethers and customary fillers, which according to the invention contain 0.1 to 10% by weight, preferably 1 to 3% by weight, 10 to 40% aqueous dispersions of alkali-swellable copolymers based on butadiene, styrene and methacrylic acid and the esterification product of Diels-Alder adducts from maleic acid with alcohols from oxtylene oxide copolymers, for example altylphenoxypolyethyleneoxyethanol, with 4 to 20 moles of ethylene oxide ·
199 3S6 Přitom bylo 2jiáténof že. disperze kopolymerů na bázi butadienstyrenu, bobtnatelných alkáliemi, vyvolávají při přísadě živičných emulzí a jejich kombinací β disperzemi elastomerů a plastomerů v alkalické oblasti zahuštění celé směsi a tím větší stálost při skladování.3D6 199 It was 2jiáténo that f. dispersion copolymers based butadienst y Reno, swellable alkali induce additive in bitumen emulsions and dispersions of β combinations of elastomers and plastomers in the alkaline concentration of the entire mixture and the greater storage stability.
Překvapivě se dosahuje při vhodné kombinaci receptury zkrácení dobywysychání rychlejším vytvářením filmu· Filmyvykazují po vysušení při přídavku malých množství disperze butadienstyrenových kopolymerů, bobtnatelných alkáliemi, hydrofobní vlastnosti v důsledku zesílovacích reakcí. Zvláš? příznivě pťisobí přídavky 1 až 3 - hmot. % 10 až 40% disperzí. Jako kopolymery lze výhodně použít polymerátové latexy, vznikající polymerací vinylaromatických sloučenin dienů, nenasycených karboxylových kyselin a esterifikačfh produktů Diels-Alderových aduktů kyseliny maleinové.Surprisingly achieved in suitable combination formulation shortening dobywysychání faster film forming Filmyvykazují · after drying with the addition of small amounts of dispersion butadienstyrenových copolymers, alkali swellable hydrophobic properties due to crosslinking EDGINGPROFILE L I C h to a C rea. Zv láš ? pťisobí favorably at a dose of 1-3 - wt. % 10-40% erzí dis p. Polymer latexes resulting from the polymerization of vinylaromatic diene compounds, unsaturated carboxylic acids and esterification products of Diels-Alder maleic acid adducts can be advantageously used as copolymers.
Výsledné emulze nebo kombinace mají dobrou stálost při skladování, přičemž se téměř zabrání projevům usazování, popřípadě vysazování. Výrobky lze výtečně používat k opatřením k ochraně staveb, jako k izolaci proti zemní vlhkosti, těsnění proti tlakové vodě, nátěru střech nebo k ochraně betonových nádrží nebo kanálů proti vodě a agresivním vodným prostředím. přitom lze použít zvlášl výhodným postupů nanéáení stMMním. Výrobky v^/tv^ejí překvapivě velmi rychle hydrofobní filmy nebo ochranné vrstvy a jsou v krátké době odolné proti vodě a agresivním prostředím. Zesiloval reatoe . vytváří hydrofobní, velmi dobře přilnavý, nebobtnavý a nepropustný nátěr.The resulting emulsions or combinations have good storage stability while virtually avoiding deposition or withdrawal. The products can be used excellently for building protection measures such as ground moisture insulation, pressure water seals, roof coatings or for protection of concrete tanks or channels against water and aggressive aqueous environments. BC it th can be used to live from within Laslo advantageous post Pooh nanéáení stMMním. On the manufacture of ky ^ / t in an outwardly surprisingly fast hydrophobic films or protective layer and are shortly resistant P ro t i of water and aggressive grid of p m of copper. Reatoe magnified. DESIGNING Ar hydrates f b of the very id of Br- e adherent, impermeable coating and swell.
Zesilovací reakce lze zea^it přídavkem formaldehydových pryskyřic, jako například melaminrormaldehydové nebo močovinoformaldebydové pryskyřice. Urychlení zesílováni vyvolávají též přísady kysličníků nebo solí vicemocných kovů, jako například zinku nebo hořčíku. Jak uvedené pryskyřice, tak kysličníky nebo soli kovů - se používají v množství asi 10 %, vztaženo ' na sušinu disperze kopolyme.rů bobtnatelných alkáliemi na bázi butadienstyrenu použité podle vynálezu a půsoM jako katalyzátory při zes^ova^ reakci.Es il cheers from the rea tion can zea-IT by adding f d e hyd Ormala ovýc HP feature Kyr IC as melaminrormaldehy of ex and d d b b s not f orma of urea ld formaldehyde eb y p y y Kyr with ice. Uryc hl en s o l crosslinked and Ni also elicit additive oxides or salts of polyvalent metals such as zinc or magnesium. As the resin, and oxides or salts of metals - are used in amounts of about 10% based on dry weight basis dispersion copoly y me.rů alkali swellable butadiene styrene based ITE used in compliance p y n and l cut and the mouth of the I catalyzed by the multi ORY carboxylate p ^ s amp-ova response.
Vynález je blíže objasněn třemi příklady.Three examples illustrate the invention.
Příklad 1Example 1
V rnícheičce se při 20 °C upraví pH 88 not. % s^taWlní živičné emu3.ze - s hlinRým emulgátorem na hodnotu 11 roztokem hydroxidu draselného. Za míchání se postupně přidá 1 hmot. % alkylfenolpolyglykotéru a 10 hmot. % butadienstyr nového latexu s 50 % sušiny. Kesměsi se vleje pozvolna za stálého míchání 1 hmot. % 33% disperze kopolymerů butadienu, styrenu, kyseliny metakiylové a produktu esterifikace Diels-Alderova aduktu kyseliny· maleinové e butadienem a dodecylfenolpolyetylénoxidetylalkoholem s 10 moly etylénoxidu. Celá směs přitom zhoustne a získá tixotropní vlastnosti. Po řádném promíchání se získá rychleschnoucí emulzní nátěrové hmoty, stálá při skladování, která po nanesení štětcem nebo stříkáním a po vysušení tytváří přilnavý , hydrofobní, nepropustný, chemicky odolný a nebobtnavý film nebo nános.In the rnícheičce p s at 20 ° C P P H Ravi 88 notes. % S ^ fo taWlní vičn Star emu3.ze - hlinRým with emulsifier to pH 11 with potassium hydroxide solution. While stirring, 1 wt. % alkylphenol polyglycerate and 10 wt. % butadiene styrene of the new latex with 50% dry matter. The mixture is poured slowly with stirring of 1 wt. % 33% dispersion of copolymers of butadiene, styrene, methiacylic acid and esterification product of Diels-Alder adduct · maleic acid with butadiene and dodecylphenolpolyethylene oxide ethyl alcohol with 10 moles of ethylene oxide. The whole mixture thickens and obtains thixotropic properties. After proper mixing, a fast-drying, stable storage emulsion is obtained which, when applied by brush or spraying and dried, forms an adhesive, hydrophobic, impermeable, chemically resistant and non-swellable film or coating.
1В9 эва1В9 эва
Oproti známé směsi, skládající se stejných'složek, popřípadě obsahující ještě plnidla, jako azbestová nebo čedičová vlákna, popřípadě křamelinu, a místo kopolymerů bobtnáte lných alkáliemi podle vynálezu obsahující ve vodě bobtnatelný polyakrylát, ae'získají následující vlastnosti:In contrast to the known mixture consisting of the same components, optionally containing fillers such as asbestos or basalt fibers or cramel, and instead of the copolymers swellable with the alkali according to the invention, comprising a water-swellable polyacrylate, the following properties are obtained:
Příklad 2Example 2
V níohaěoe ae amíaí 83,4 hmot* % matabilní nebo poloetabllní živičné emulze, 19 hmot, * butadianetyíanového latexu o aHně 35 * a 1,5 hmot* % 33(4 disperze kopolymru, bobtmtalného e^áHemi, na báal butadiaмtyrenu, . obdobného složení jako v příkladu 1, a 0,1 hael* * vodného roatoku mlaBlnformaldehydové pryakyřioo o 50* aHni. УвпПкХ* směs Je stálá při skladování a vytváří po naiwoonl stříkáním dvousložkovým postup hydrofobnt rychleaohnouoí fiOy· OppoU obvyklým eoOsío aa projevují výhody uvedená v příkladu 1«In this case, 83.4% by weight of a matt or semi-stable bitumen emulsion, 19% by weight of butadietylamine latex of at least 35% and 1.5% by weight of 33 (4 dispersions of copolymer, swellable, by weight, butadiene-ethylene). The composition is as in Example 1, and 0.1% by weight of the aqueous solution of 50% by weight of formaldehyde resin. «
Příklad 3Example 3
V míshadoe ae amaí stabilní Mionogenní živičná emulse a obsahem plnidel 6 hmoo. * a hodnotou pK 5 o 2 hrnci* * 8И disperse kopolymru, bobtmtolného o^áliemi, na běsi butodienetyránu, obdobného oldení jako v příkladu 1« . a 0,05 Ηβοϊ.* prálkového kysličníku aineenatáho* Vannklá amáa Je stálá při skladování a vytváří rychle aohnouoí hydrofobnt vrstvy a oohraroié filoy* Oj>rroi obvyklým směsím oo projevují výhody popsaná v příkladu 1.The mixer has a stable Mionogenic bitumen emulsion and a filler content of 6 hmoo. * and a pK of 5 by 2 pots * dispersion of copolymers, swellable with olives, on a butodienethane fraction, similar to the aging procedure of Example 1. and 0.05 Ηβοϊ. * aine-anaine oxide. * Stable in storage and form quickly and readily hydrophobic layers, and the film formulations of the conventional compositions exhibit the advantages described in Example 1.
199 3S9199 3S9
Claims (3)