CS199073B1 - Mixture for hydroinsulating injections - Google Patents
Mixture for hydroinsulating injections Download PDFInfo
- Publication number
- CS199073B1 CS199073B1 CS445977A CS445977A CS199073B1 CS 199073 B1 CS199073 B1 CS 199073B1 CS 445977 A CS445977 A CS 445977A CS 445977 A CS445977 A CS 445977A CS 199073 B1 CS199073 B1 CS 199073B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- water
- bitumen
- pts
- parts
- weight
- Prior art date
Abstract
Description
Předmětem vynálezu Je směs pro,hyúroizolační injektáže na bázi živičných disperzí·SUMMARY OF THE INVENTION The subject of the invention is a mixture for
Pro utěsnění průsaků vody do vybudovaných podzemních staveb nebo ' ke zlepšení hydrogeologických podmínek kolem podzemního díla se použžvaJí různé druhy izolačních hmoo, které se do horniny injektují pomooí tlakových čerpadel· Pro vodotěsné injektáže Jsou používány hmoty jak anorganického původu, cement. Jíl, bentonit a jiné, tak organického původu, zejména směsi naVarious types of insulating materials are used to seal water leaks into the built underground structures or to improve the hydrogeological conditions around the underground works, which are injected into the rock by means of pressure pumps. Clay, bentonite and others of organic origin, in particular mixtures thereof
G'· - ' ' bázi pryskyřic nebo živic·G '· -' 'resin or resin based ·
V posledních letech se pro injektážní účely uplatňuje využívání živičných látek v disperzní formě olej ve vodě, známých pod názvem asfaltové emuuze, případně s příměsí latexu syntetického kaučuku, které Jsou . obecně nazývány asfaltolaeexové emuuze. Tyto emulze obsahují Jemně rozptýlený'asfalt ve vodě, do které jsou přidávány ernuugátory a stabilizátory· Pro injektáže Jsou používány emulze rychloštěpné o viskozitě 2,5 až 3 °E.In recent years, the use of bituminous substances in dispersed form oil-in-water, known as asphalt emulsions, possibly with admixture of synthetic rubber latex, which have been used, has been used for injection purposes. commonly called asphaltolaeex emulsions. These emulsions contain finely divided asphalt in water, to which are added erythropulants and stabilizers. · For grouting, quick-breaking emulsions with a viscosity of 2.5 to 3 ° E are used.
Podle známého stavu techniky se asfaltové nebo asfaltolaeexové emulze zpracovááaaí tak, že se k vy Štěpení asfaltu nebo asfaltaaučuku využívá moralizované vody, nebo v případech, kdy voda není dostatečně agresivní, aby způsoobla vy štěpení asfaltu nebo asfaltkaučuku, se souběžně do horniny vtlačuje vhodné srážedlo, například roztok chloridu vápenatého· Tato technologie je předmětem čs· patentu č· 122 312· Nevýhodou tohoto způsobu je především nedokonalé promísení emulze se srážedlem, takže štěpení neprobíhá v celém objemu· Další způsob zpracování asfaioových nebo asfaltdteeoových emuuzí pro injektáže spočívá v tom, že základní hydroAccording to the prior art, the asphalt or asphalt-laeex emulsions are processed by using moralized water to break up the asphalt or asphalt rubber, or in cases where the water is not aggressive enough to cause the asphalt or asphalt rubber to break down, for example calcium chloride solution · This technology is the subject of the patent · 122 312 · The disadvantage of this method is the imperfect mixing of the emulsion with the precipitant, so that the cleavage does not take place in its entirety. hydro
199 073199 073
199 073 izolační hmotě se těsně před aplikací homogenně promíaí s želatfriačním činidlem, kterým Je fluorokřemičitan sodný, přimíšený pro regulací rychlosti tuhnutí výsledné izolační hmoty v časově řiditelném rozmeeí, což Je předmětem čs. patentu Č. 176 30ti. Popsanou technologií Je zajištěno, že se živice vyátěpí v celém objemu a ve zvoleném časovém úseku.Nevýhodou je, že při injektéži značně rozrušených hornin nebo trhlin a spár ve stavebním díle v blízkosti injektážního vrtu dochází k vytlačování nevyštěpeného izolačního mateeiálu a v takových případech Je nutno injektáž přerušit do doby vy Štěpení účinkem želatinačního činidle. Krátí dobu než 5 minut nelze v praxi běžně pouuívat, aby nedošlo k vyštěpení asfaltu Ještě v ; injektážním zařízení·199 073 of the insulating material is mixed homogeneously with the gelling agent, which is sodium fluorosilicate, admixed to control the solidification rate of the resulting insulating material in a time-controllable range just prior to application. No. 176,306. The disadvantage is that when injecting severely disturbed rocks or cracks and joints in the building near the injection well, the uncleaved insulation material is displaced and in such cases it is necessary to interrupt injection until cleavage with gelling agent. Less than 5 minutes can not be used in practice to avoid asphalt splitting Still in ; grouting equipment ·
Popsané nevýhody odstraňuje směs pro hydroizolační injektáže podle vynálezu.The described disadvantages are overcome by the waterproofing grouting composition according to the invention.
Podstata smmsi pro hydroizolační injektáže podle vynálezu spočívá v tom, že sestává ze 100 hmoo. dílů asfaltové nebo tsftltolatexovn emuuze, 5 až 15 hmot:· dílů' 40%iího vodního roztoku síranu amonného, 0,5 až 3 hmot dílů hydroxidu amonného, vztaženo na jeho roztok o koncctlгecl 26 % a 0,3 až 2 hmmo, dílů kysličníku zinečnatého.The essence of the smmsi for waterproofing grouting according to the invention is that it consists of 100 hmoo. 5 to 15% by weight of parts of a 40% by weight aqueous solution of ammonium sulfate, 0.5 to 3 parts by weight of ammonium hydroxide, based on its solution having a concentration of 26% and 0.3 to 2% by weight, parts of oxide zinc.
Směs pro hydroizolační injektáže podle vynálezu se připravuje homogenním promísením jednotlivých složek těsně před aplikací následujícím postupem. Eo asfaltové nebo tsftltoltttxové emulze se vmísí roztok síranu ι^ομ^ο, poté hydroxid amorný. Jako poslední složka kysličník zinečnatý. Pro snacdn!!Jší rozmíchání kysličníku zinečnatého do směsi je vhodné připravit z této látky suspenzi použitím malého množtví vody.The waterproofing injection composition according to the invention is prepared by homogeneously mixing the components just prior to application by the following procedure. Eo is added to the asphalt or ttltolyttx emulsion, followed by ammonium hydroxide solution. The last component is zinc oxide. For better mixing of the zinc oxide into the mixture, it is advisable to make a suspension of the zinc oxide using a small amount of water.
Obsah a skladba chemických látek směsi pro hydroizolační injektáže podle vynálezu způsobuje při styku s vodou oktDmžtn štěpení asfaltové nebo ttftltotatexovn emuuze, při němž se vylučuje její izolační složka, tj. asfalt nebo Důůežitou skutečnost je, že vodu, na rozdíl od popsaného stavu techniky, nemuuí být mineralizovaná. Voda snižuje koncentraci síranu amonného, čímž ve zředěném roztoku nastává úplná Sitrcitct jeho iontů, jejichž zvýšená aktivita způsobuje vy Štěpení izolační složky z živičné disperze. U směěi, která nepřijde v hornině nebo zemině do styku s vodou, se vyštěpí její izolační složka postupným účinkem vmíšených chemických látek, přičemž dobu štěpení je možno ovlivnit jejich vzáemmným poměrem.The water content and composition of the waterproofing injection composition of the present invention causes an octagonal breakdown of the asphalt or tertiarytatex emulsion in contact with water, which excludes its insulating component, i.e., asphalt or water. be mineralized. Water reduces the concentration of ammonium sulphate, whereby a complete Sitrcitct of its ions occurs in the diluted solution, the increased activity of which causes the isolation component to cleave from the bituminous dispersion. In the case of a mixture which does not come into contact with water in the rock or soil, its insulating component is split off by the gradual effect of the incorporated chemicals, the cleavage time being influenced by their relative ratio.
Příklady složení směsiExamples of composition
Příklad 1Example 1
100 hmot, dílů ttftltolatexovn em^uz^e, hmot, dílů 40%ního vodního roztoku (ΝΗ^^Ο^, hmoo;· díly NH^OH, vztaženo na jeho roztok o ^πκμΙ^οΙ 26 % a100 parts by weight of tertiary-latex resin, parts by weight of a 40% aqueous solution (ΝΗ ΝΗ ^ Ο Ο Ο Ο Ο Ο Ο Ο Ο Ο Ο Ο Ο Ο Ο Ο Ο Ο Ο),
0,4 hmot, díly ZnO.0.4 parts by weight of ZnO.
Zředěním smmsi vodou dochází k okamžitému štěpení izolační složky» bez zředění vodou dojde k úplnému vyštěpení v průběhu 60 minut.Dilution with smmsi water immediately cleaves the insulation component »without dilution with water, complete cleavage occurs within 60 minutes.
199 073199 073
Příklad 2Example 2
100 hmot, dílů asfaltolatexové emulze, hmot, dílů 4O%ního vodního roztoku (NH^^SO^,100 parts by weight of asphaltolatex emulsion, parts by weight of 40% aqueous solution (NH4 ^ SO4),
0,5 hmot, dílu NH^OH, vztaženo, na Jeho roztok o koncentraci 26 % a hmot, díl ZnO.0.5 parts by weight of NH4OH, based on its solution at 26%, and parts by weight of ZnO.
Zředěním směsi vodou dochází к okamžitému Štěpení izolační složky, bez zředění vodou dojde к úplnému vyštěpení v průběhu 25 minut.Dilution of the mixture with water leads to immediate cleavage of the insulating component, without dilution with water complete cleavage within 25 minutes.
Směs pro hydroizolační injektáže podle vynálezu je vhodná pro utěsnění průsaků nebo přítoků vody do podzemních stavebních děl, například do tunelů, šachetních jam, nebo к utěsnění vodonosných hornin nebo zemin zejména v hornictví a stavebnictví.The waterproofing grouting composition according to the invention is suitable for sealing leaks or inflows of water into underground structures, such as tunnels, shaft pits, or for sealing aquifers or soils, especially in mining and construction.
Claims (1)