CN86106211A - Additive agent for underwater cement - Google Patents
Additive agent for underwater cement Download PDFInfo
- Publication number
- CN86106211A CN86106211A CN198686106211A CN86106211A CN86106211A CN 86106211 A CN86106211 A CN 86106211A CN 198686106211 A CN198686106211 A CN 198686106211A CN 86106211 A CN86106211 A CN 86106211A CN 86106211 A CN86106211 A CN 86106211A
- Authority
- CN
- China
- Prior art keywords
- cement
- mix
- polyacrylamide
- admixture
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of dabbling additive agent for underwater cement of water that is used for is to mix by polyacrylamide and shale ashes or with silica flour.Can contain anion surfactants such as β-naphthalene sulfonic acidformaldehyde condensation product.The cement, mortar or the concrete mix that mix this admixture therefrom freely fall when pouring into not to be emanated, does not disperse, and keeps the character of perfusion hardening thing constant, and cost is lower.Available general constructional method is carried out subaqueous concreting, is starched rapid constructions such as anchor, underwater grouting under water.
Description
The present invention relates to a kind of dabbling under water cement, mortar, concrete admixture.The cement, mortar or the concrete mix that mix this admixture freely fall when pouring into from water not to be emanated, does not disperse, and keeps the character of perfusion hardening thing constant.
The concrete mix of in the past cement, sand, stone, water etc. being mixed system falls in water in the dabbling process, and the grout in the mixture is just washed by water and runs off, and mixture produces segregation, and concrete hardening thing intensity obviously reduces.Japan publication 1983-49650 discloses a kind of employing sepiolite with flocculation agent (polyacrylamide etc.), also can mix the additive agent for underwater cement that water reducer (sodium alkyl naphthalene sulfonate etc.) etc. is prepared.Described in this patent, in concrete mix, only mix polyacrylamide,, can not fully prevent dispersion, the segregation of aggregate in the mixture though can prevent scattering and disappearing of grout in its mixture.For addressing this problem, adopted sepiolite to be used for preventing dispersion, the segregation of mixture aggregate in this patent.It is broken that but this sepiolite needs under certain liq, requires not damage its raphioid fiber structure in the fragmentation, so the requirement of sepiolite pulverizing complete processing is tighter, has sepiolite to be subjected to the restriction of China place of production and cost again, on using certain limitation arranged.
For solving the problem that above-mentioned sepiolite exists, adopt among the present invention shale ashes or silica flour both one of mix with polyacrylamide, wherein also can mix anion surfactants such as beta-naphthalenesulfonic-acid formaldehyde condensation compound again, its effect is better than sepiolite.Additive agent for underwater cement of the present invention shows through test of many times, the cement, mortar or the concrete mix that mix this admixture is freely fallen when pouring in water do not emanate, do not disperse, keep the dabbling homogeneity of mixture; Dabbling mixture can be full of model, levelling, closely knit voluntarily, need not vibrate; As be mixed with the low flow mixture and can support resisting moving water and wash away; Perfusion back mixture is not stratified, not laitance, not bleeding, inundation not, with extraneous water exchange interaction do not arranged, the proportioning of mixture when keeping initial perfusion; The hardening thing performance of mixture is identical with land construction almost; This admixture is to the effect of reinforcing bar non-corroding; The hardening thing performance is constant during with the seawater mix; Little in the construction to construction water pollution degree; Admixture of the present invention can reduce the consumption of the polyacrylamide that price is high in the admixture, reduces cement consumption, and the cost of this admixture is lower, and the cost of shale ashes only is 1/20 of a sepiolite.
Additive agent for underwater cement among the present invention is to be mixed by shale ashes and polyacrylamide or silica flour and polyacrylamide.Shale ashes main component wherein has SiO
2And Al
2O
3, be the hollow particle shape, have great specific surface area, mix in the cement and when with the water mix, can adsorb more moisture, make the multiviscosisty of grout dispersion, increase coherent structure, increase the anti-washing effect of cement; The Ca(OH that can produce with hydrated reaction of cement)
2Reaction generates hydrated calcium silicate and drated calcium aluminate with gelating property, can glued aggregate, and prevent the mixture segregation, disperse, improve hardening thing intensity.Shale ashes chemical ingredients (%) among the present invention is: SiO
256~60; Al
2O
319~24; Fe
2O
37~11; TiO
20.5~1; CaO 0.8~1.7; MgO 0.5~1.5; SO
30.5~2.0; K
2O 1.0~2.2; Na
2O 0.05~0.4; Loss on ignition 0.6~4.5.Proportion 2.2,200~400 kilograms/meter of unit weights
3, 5000~20000 meters of specific surface areas
2/ kilogram.Shale ashes volume among the present invention is 0.5~15% of a cement weight, and volume is little less than effect in 0.5% o'clock, and volume reduced the mixture bonding capacity and reduced hardening thing intensity greater than 15% o'clock.The optimum mix amount is 3.1%.As replace shale ashes wherein with silica flour, its silica flour has the similar effect of above-mentioned shale ashes among the present invention.This silica flour is mainly by amorphous Si O
2Form, its chemical ingredients (%) is: SiO
290~96; Al
2O
30.5~3.0; Fe
2O
30.2~0.8; CaO 0.1~0.5; MgO 0.5~1.5; K
2O 0.2~0.7; Na
2O 0.4~1.0; Loss on ignition 0.7~2.5.Proportion 2.1,200~300 kilograms/meter of unit weights
3, 19000~22000 meters of specific surface areas
2/ kilogram.The volume of this silica flour is 1~10% of a cement consumption, and volume is not obvious less than effect in 1% o'clock, and volume is greater than the intensity of bonding capacity that reduced mixture at 10% o'clock and reduction hardening thing.The optimum mix amount is 3.1%.
The polyacrylamide that adopts among the present invention, its molecular weight is 2,000,000~9,000,000, degree of hydrolysis is below 30%, volume is 0.1~3% of a cement weight, volume is less than 0.1% o'clock, grout thickness DeGrain, and volume is greater than 3% o'clock mixture thickness too, can not use conventional facility construction, and reduce the intensity of hardening thing.The optimum mix amount be cement heavy 0.65%.
Admixture among the present invention can mix anion surfactants such as beta-naphthalenesulfonic-acid formaldehyde condensation compound, can make the polyacrylamide particle coat the diffluent tensio-active agent of one deck, makes polyacrylamide particle facile hydrolysis, and easily diffusion is difficult for conglomeration; In addition grout there is certain plastification, improves the degree of mobilization of mixture.The volume of this beta-naphthalenesulfonic-acid formaldehyde condensation compound is 0.1~3% of a cement consumption, and wherein little less than effect in 0.1% o'clock, volume is greater than the intensity that reduced hardening thing at 3% o'clock, and the optimum mix amount is 1.0%.Admixture among the present invention also can adopt shale ashes and silica flour certainly simultaneously, also can mix water reducer, adjustable solidification agent etc.
Admixture among the present invention can be mixed with admixture in advance by above-mentioned each component ratio, adds in cement, mortar, the concrete again.Specific implementation method is in conjunction with following embodiment explanation.
Embodiment: underwater grouting mortar test
(1) presses the listed proportioning weighing of table 1.Cement, admixture, sand dry mixing are evenly added in the GB177-77 cement mortar mixer blunge 6 minutes in the back.The GB177-77 cement mortar tryout is placed in the perfusion groove of 400 millimeters of the depth of waters, the mortar of mixing is irritated down from the water surface by funnel, keeping mixture free drop in water in the perfusion is 400 millimeters.Clip unnecessary mortar on the mould, form removal maintenance to regulated period makes, and presses the intensity that the GB177-77 prescriptive procedure is measured mortar specimen.
(2) in 1000 milliliters of graduated cylinders, add 1000 milliliters in water, irritate down from the graduated cylinder water surface, draw certain water gaging from 50 millimeters depths of the distance water surface with suction pipe after 5 seconds and put into the water sample cup, use than light turbidimeter and survey its turbidity with make new advances one spoonful in sand cutting slurry of stirring bale-out.
(3) press the GB2419-81 regulation, measure new sand cutting slurry degree of mobilization.
Test-results is listed in table 2.
Additive agent for underwater cement of the present invention is when being used for underwater concrete construction, and its implementation method is similar to above-mentioned mortar construction.At first take by weighing cement, admixture, sand, stone and put into the forced concrete mixer dry mixing 1 minute, water cement ratio (as 0.5) adds water and stirred discharging 3 minutes in accordance with regulations.Then concrete mix is carried out freely falling in the water perfusion.28 days ultimate compression strength of its concrete can reach 29.4 MPas.Additive agent for underwater cement of the present invention also can be used for starching anchor, underwater grouting etc. under water except that being used for underwater concrete construction.
The composition and the consumption of table 1 underwater grouting mortar
Annotate: (1) cement is 525 ordinary Portland cements.
The performance of table 2 underwater grouting mortar
Claims (4)
1, cement, mortar, the concrete admixture used of a kind of underwater construction contains polyacrylamide, it is characterized in that:
A. mix shale ashes;
B. or mix silica flour.
2, admixture according to claim 1 is characterized in that:
A. the specific surface area of shale ashes is 5000~20000 meters
2/ kilogram;
B. the specific surface area of silica flour is 19000~22000 meters
2/ kilogram.
3, admixture according to claim 1 also contains beta-naphthalenesulfonic-acid formaldehyde condensation compound, it is characterized in that the proportioning (percentage ratio of by mass of cement) of admixture is:
A. polyacrylamide: shale ashes: beta-naphthalenesulfonic-acid formaldehyde condensation compound=(0.1~3.0): (0.5~15): (0.1~3.0)
B. polyacrylamide: silica flour: beta-naphthalenesulfonic-acid formaldehyde condensation compound=(0.1~3.0): (1.0~10): (0.1~3.0).
4, admixture according to claim 3 is characterized in that optimum mix (percentage ratio of by mass of cement) is:
A. polyacrylamide: shale ashes: beta-naphthalenesulfonic-acid formaldehyde condensation compound=0.65: 3.1: 1.0
B. polyacrylamide: silica flour: beta-naphthalenesulfonic-acid formaldehyde condensation compound=0.65: 3.1: 1.0.