CN2769050Y - Organic antibiotic coating aluminium board - Google Patents
Organic antibiotic coating aluminium board Download PDFInfo
- Publication number
- CN2769050Y CN2769050Y CN 200520069003 CN200520069003U CN2769050Y CN 2769050 Y CN2769050 Y CN 2769050Y CN 200520069003 CN200520069003 CN 200520069003 CN 200520069003 U CN200520069003 U CN 200520069003U CN 2769050 Y CN2769050 Y CN 2769050Y
- Authority
- CN
- China
- Prior art keywords
- antibiotic
- layer
- coating
- aluminium plate
- organic antibacterial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model relates to an organic antibiotic coating aluminum board, which is characterized in that the utility model comprises a base material bottom layer (1), a liquid film middle layer (2) of the chrome-free purification of solvent, and a surface layer (3) of antibiotic coating materials. The utility model has the advantage of good antibiotic performance, and the environment can be effectively purified.
Description
Technical field:
The utility model relates to a kind of aluminium sheet, especially relates to a kind of organic antibacterial coating layer aluminium plate.Be mainly used in the desinfection chamber of medical treatment, hygiene department, the inner, external wall of the workshop of pharmaceutical factory, food factory, Cosmetics Plant etc. is decorated, and belongs to technical field of construction and decoration materials.
Background technology:
In the past in desinfection chamber medical, hygiene department, the workshop of pharmaceutical factory, food factory, Cosmetics Plant, the enforcement chamber of biochemistry, electron trade etc., the used ornament materials of its inside and outside metope is common sheet material or face brick, they are rough surface not only, easy binding dust, and grow harmful bacteria easily, pollute dirty border, be harmful to health, weather resistance is poor simultaneously, and service life is short, damage easily, fall flat.
Summary of the invention:
The purpose of this utility model is to overcome above-mentioned deficiency, and what a kind of effectively environment purification was provided has organic antibacterial coating layer aluminium plate of antibiotic property and preparation method thereof.
The purpose of this utility model is achieved in that a kind of organic antibacterial coating layer aluminium plate, is characterized in that it comprises aluminium sheet base material bottom, solvent Chrome-free purifying liquid film intermediate layer and antibiotic paint surface layer.
The utility model adopts the method for intending bacterium with bacterium, and thalline by cultivating in coating, is processed by coating baking, shaping then.Utilize the thalline of dense planting in the surface of aluminum plate coating that the harmful bacteria in the environment is killed, to reach the needs of environment purification and maintaining healthy.Coating of the present invention is adhered to closely, and the sense organ effect is splendid, has permanent weather resistance.Therefore be specially adapted to medical treatment, hygiene department's desinfection chamber, the workshop of pharmaceutical factory, food factory, Cosmetics Plant, the inner, external wall of the enforcement chamber of biochemistry, electron trade etc. is decorated.
Description of drawings:
Fig. 1 is embodiment one a section structure schematic diagram of the present utility model.
Fig. 2 is embodiment two section structure schematic diagrames of the present utility model.
The specific embodiment:
Embodiment one:
Referring to Fig. 1, the preparation of antibiotic polyester coating layer aluminium plate:
1), provide a continuous thin aluminum sheet 1, the surface of book aluminium sheet to coat solvent Chrome-free refined solution rete 2 earlier;
2), apply antibiotic polyester coating surface layer 3 again on above-mentioned thin aluminum sheet surface, this antibiotic polyester coating surface layer has 3.2 2 layers of priming coat 3.1 and finishing coats;
3), the above-mentioned coating layer aluminium plate that scribbles antibiotic polyester coating is entered baking oven, 200 ℃～220 ℃ down baking 45 "～60 " make antibiotic polyester coating layer aluminium plate manufactured goods.
Embodiment two:
Referring to Fig. 2, the preparation of antibiotic fluororine-carbon coating aluminium sheet:
1), provide a continuous thin aluminum sheet 1, the surface of book aluminium sheet to coat solvent Chrome-free refined solution rete 2 earlier;
2), apply antibiotic fluorocarbon coating surface layer 3 again on above-mentioned thin aluminum sheet surface, this antibiotic fluorocarbon coating surface layer has 3.2 2 layers of priming coat 3.1 and finishing coats, or 3.3 3 layers of priming coat 3.1, finishing coat 3.2 and surperficial layer of varnish are arranged;
3), the above-mentioned coating layer aluminium plate that scribbles antibiotic fluorocarbon coating is entered baking oven, 210 ℃～250 ℃ down baking 45 "～60 " make antibiotic fluororine-carbon coating aluminium sheet manufactured goods.
Wherein each material selection is as follows:
1) aluminium sheet base material:
Trade mark 1100-H18,3003-H14H24 or 3003H16H26;
Thickness 0.20mm～0.50mm; Width 970mm～1600mm;
Chemical analysis, mechanical property meet the GB/T3880 regulation.
2) chemical films: Chrome-free purifying liquid film
3) paint coatings thickness: Side fascia 〉=25 μ m, lining 〉=16 μ m.
Roller coat application condition sees Table one
Table one
| Coating | Coating | Application viscosity (No. 4 cups) | Baking condition (plate temperature) | Build | Remarks |
| Fluorocarbon coating (kynar500 | Primary coat | 40″～60″ | 210℃±10℃(45″～60″) | 5～8 | |
| Face is coated with | 90″～110″ | 250℃±10℃(45″～60″) | 22～25 | ||
| Varnish | 90″～110″ | 250℃±10℃(45″～60″) | 10～15 | The selectivity application | |
| Polyester coating (PE) | Primary coat | 40″～60″ | 200℃±10℃(45″～60″) | 5～8 | |
| Face is coated with | 60″～100″ | 220℃±10℃(45″～60″) | 14～18 |
The antimicrobial coating technical parameter sees Table two
Table two
| Project | Coating | Specification requirement |
| Sterilizing rate | More than 99.9% | |
| A rerum natura | 60 degree bright lusters | 30±5 |
| T bends (anti-bending) | ≤ | |
| 1/2inch*1kg*50cm is shock-resistant | Good | |
| Close work | Good | |
| Secondary rerum natura ( | Outward appearance | OK |
| 60 degree bright lusters | 28 | |
| T bends (anti-bending) | ≤ | |
| 1/2inch*1kg*50cm is shock-resistant | Good |
| Close work | Good | |
| The QUV aberration | Not obvious | |
| 100V*15W*20cm*6h light conservation rate | 100％ | |
According to the GB method of testing antimicrobial coating of embodiment is tested and the results are shown in following table:
| Testing time (hour) | 12 hours | 24 hours | 48 hours | |
| Sterilizing rate | Escherichia coli | 50％ | 85％ | 99.9％ |
| Staphylococcus | 50％ | 85％ | 99.9％ | |
Claims (4)
1, a kind of organic antibacterial coating layer aluminium plate is characterized in that it comprises aluminium sheet base material bottom (1), solvent Chrome-free purifying liquid film intermediate layer (2) and antibiotic paint surface layer (3).
2, a kind of organic antibacterial coating layer aluminium plate according to claim 1 is characterized in that the antibiotic paint that antibiotic paint surface layer (3) is adopted is antibiotic polyester coating, and (3.2) two layers of priming coat (3.1) and finishing coats are arranged.
3, a kind of organic antibacterial coating layer aluminium plate according to claim 1 is characterized in that the antibiotic paint that antibiotic paint surface layer (3) is adopted is antibiotic fluorocarbon coating, and (3.2) two layers of priming coat (3.1) and finishing coats are arranged.
4, a kind of organic antibacterial coating layer aluminium plate according to claim 3 is characterized in that antibiotic paint finishing coat surface scribbles layer of varnish (3.3).