CN2545021Y - Wheel spoke with color coatig and wheel spoke with multicolor coating - Google Patents
Wheel spoke with color coatig and wheel spoke with multicolor coating Download PDFInfo
- Publication number
- CN2545021Y CN2545021Y CN 02201360 CN02201360U CN2545021Y CN 2545021 Y CN2545021 Y CN 2545021Y CN 02201360 CN02201360 CN 02201360 CN 02201360 U CN02201360 U CN 02201360U CN 2545021 Y CN2545021 Y CN 2545021Y
- Authority
- CN
- China
- Prior art keywords
- spoke
- pigment
- wheel spoke
- wheel
- utility
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The surface of a bicycle wheel spoke is added with resin which contains common pigment, fluorescent pigment or phosphorescent pigment. Therefore, the spoke can be seen clearly no matter in the dark or in the day, which can prevent safety accidents from occurring. In addition, the spoke is anti-rust. The utility improves the support force, durability as well as the aesthetic value.
Description
Technical field
The utility model relates to a kind of improved wheel of taking turns spoke that is used for Bicycles and Motorcycles that has, and relates to the wheel spoke that the surface has common pigments, fluorescent pigment or phosphorescent pigment particularly.
Background technology
Generally, the wheel that is used for bicycle, motor bike or pony truck comprise wheel shaft, be rigidly connected to the annular wheel plate of wheel shaft side, fixedly wheel rim and a plurality of metal wheel spoke of the inner tube of a tyre.The wheel spoke is arranged on and is used for bearing load between wheel plate and the wheel rim.
The wheel spoke of bicycle has some shortcomings, and that is exactly to be covered by dust easily, has therefore weakened bearing force and durability; And not very showy in the dark, cause safety misadventure easily; Be exactly the outward appearance dullness in addition, therefore can not manifest the aesthetic values of high style.
Summary of the invention
Therefore, the utility model relates to a kind of improved bicycle quick of taking turns spoke that has, and thisly takes turns one or more problems that limitation and shortcoming caused that spoke has been avoided prior art.
The purpose of this utility model provides a kind of improved spoke of taking turns, its can be in the dark and daytime very showy.。
Another purpose of the present utility model provides a kind of improved spoke of taking turns, and it can prevent that corrosion is to improve bearing force and durability.
With other advantage, according to one side of the present utility model, provide a kind of spoke of taking turns to achieve these goals, spoke is included in the coating that the surface forms, and coating comprises resin and fluorescent pigment or phosphorescent pigment.
According on the other hand of the present utility model, a kind of spoke of taking turns is provided, described spoke is included in the coating that the surface forms, and coating comprises resin and common pigments.
Description of drawings
Merge to the accompanying drawing that becomes the application's part among the application and shown the utility model embodiment, and with introducing explanation principle of the present utility model is illustrated, accompanying drawing provides further understanding of the present utility model.Wherein:
Fig. 1 shows the bicycle transparent view comprise the wheel that has a plurality of spokes according to the utility model preferred embodiment;
Fig. 2 is a section drawing of taking turns spoke shown in Figure 1.
The specific embodiment
At length referring to preferred embodiment of the present utility model, its example shows in the accompanying drawings now.
According to explanation of the present utility model, the bicycle quick spoke forms the resin bed that has common pigments, fluorescent pigment or phosphorescent pigment by impregnation technology on its surface.So in the dark or by day all can be very showy, to prevent that safety misadventure from taking place.In addition, the wheel spoke has been avoided corrosion, has therefore improved bearing force and durability, and has improved aesthetic values.
Fig. 1 shows the bicycle transparent view comprise the wheel that has a plurality of spokes according to the utility model preferred embodiment.Fig. 2 is a section drawing of taking turns spoke shown in Figure 1.With reference to figure 1 and Fig. 2, bicycle quick 100 of the present utility model comprises a plurality of spokes of taking turns that are fixed on wheel rim with proportional spacing.Spoke forms coating 300 according to below the technology of introducing is applied the coating solution that has common pigments, fluorescent pigment or phosphorescent pigment on the surface.
After bicycle quick spoke 200 was put into temperature booster, spoke, immersed in the above-mentioned coating solution by 2 minutes then in about 100 to 500 degrees centigrade of preheatings 1.Coating solution mainly comprises resin, plasticizer, extending agent, stabilizer.Fluorescence or phosphorescent pigment have also been added in the coating solution.Coating solution preferably includes 100 weight portion polyvinylchlorides, the plasticizer of 0.5 to 2 weight portion, the extending agent of 0.05 to 0.1 weight portion, the fluorescence or the phosphorescent pigment of the stabilizer of 0.01 to 1.0 weight portion and 0.05 to 3.0 weight portion.
Plasticizer is from being called for short the DHP (d-2-hexyl phthalate) of DOP, selecting in the di 2 ethylhexyl isophthalate (d-iso-phthalate) of the dibutyl phthalate of abbreviation DBP and abbreviation DOA.
Calcium carbonate is as extending agent, and stabilizer comprises the compound of barium stearate or potassium zincate powder and liquid phase BC103 (barium-cadmium-zinc-base stabilizer).
Fluorescent pigment as pigment can show yellow, orange or green and have following physical property: mean particle size is 5N, and light resistance is 3, and heat stability is 110 to 230F, and oil absorption is 30 to 35%, and water capacity is 3.5%.Phosphorescent pigment as pigment shows general color in addition.Common pigments means universal pigment at this paper.
To be described in detail example of the present utility model.But scope of the present utility model is not subjected to the restriction of example.
Example 1
Coating solution is the polyvinylchloride with 100 weight portions, the DOP of 1.0 weight portions, and the calcium carbonate of 0.08 weight portion, the fluorescent pigment of the barium stearate of 0.07 weight portion and 1.0 weight portions mixes, and fluorescent pigment preferably has above-mentioned physical property.
Example 2
Coating solution is the polyvinylchloride with 100 weight portions, the DBP of 1.5 weight portions, and the calcium carbonate of 0.1 weight portion, the phosphorescent pigment of the potassium zincate of 0.05 weight portion and 3.0 weight portions mixes, and phosphorescent pigment preferably shows yellow.
Example 3
Coating solution is the polyvinylchloride with 100 weight portions, the DOA of 2.0 weight portions, and the calcium carbonate of 0.1 weight portion, the fluorescent pigment of the potassium zincate of 0.1 weight portion and 1.5 weight portions mixes, and fluorescent pigment preferably has above-mentioned physical property.
Example 4
Coating solution is the polyvinylchloride with 100 weight portions, the DOP of 2.0 weight portions, and the calcium carbonate of 0.1 weight portion, the fluorescent pigment of the potassium zincate of 0.1 weight portion and 3.0 weight portions mixes, and fluorescent pigment preferably has above-mentioned physical property.
Example 5
Coating solution is the polyvinylchloride with 100 weight portions, the DOP of 1.0 weight portions, and the calcium carbonate of 0.08 weight portion, the universal pigment of the barium stearate of 0.07 weight portion and 1.0 weight portions mixes, and universal pigment shows green.
Example 6
Coating solution is the polyvinylchloride with 100 weight portions, the DBP of 1.5 weight portions, and the calcium carbonate of 0.1 weight portion, the universal pigment of the potassium zincate of 0.05 weight portion and 3.0 weight portions mixes, and universal pigment shows yellow.
Example 7
Coating solution is the polyvinylchloride with 100 weight portions, the DOA of 2.0 weight portions, and the calcium carbonate of 0.1 weight portion, the common pigments of the potassium zincate of 0.1 weight portion and 1.5 weight portions mixes.
Example 8
Coating solution is the polyvinylchloride with 100 weight portions, the DOP of 2.0 weight portions, the calcium carbonate of 0.1 weight portion, the common pigments of the potassium zincate of 0.1 weight portion and 3.0 weight portions.
Example 9
Ordinary bicycle wheel spoke 200 immerses the coating solution of being made up of example 1-8 at about 100 to 500 degrees centigrade after preheating 1-2 minute.
Then, at once will through the spoke of above-mentioned processing about 100 to 500 degrees centigrade heat treatment 1-2 minute, put into ventilator again and at room temperature cool off, therefore form coating 300 in spoke surfaces, the thickness of coating is about 0.01 to 2 millimeter.
In above-mentioned utility model, because the surface of bicycle quick spoke has formed the resin bed that has in common pigments, fluorescent pigment or the phosphorescent pigment any.So spoke in the dark or daytime all very showy, can prevent the generation of safety misadventure.In addition, can also prevent that spoke from getting rusty.Therefore, improve bearing force and durability, and improved aesthetic values.
The foregoing description only is in order to illustrate, is not in order to limit the utility model.The utility model can easily be applied to the device of other type.Introduction of the present utility model is illustrative, this claim is not limited.Many variations, improvement and selection are conspicuous for the those skilled in the art.
Claims (4)
1. a spoke that is used for wheel is characterized in that, described spoke includes the coating that forms on the surface, and described coating is made of resin, fluorescent pigment or phosphorescent pigment.
2. spoke according to claim 1 is characterized in that described coating is made up of polyvinylchloride.
3. a spoke that is used for wheel is characterized in that, described spoke includes the coating that forms on the surface, and described coating is made of resin and common pigments.
4. spoke according to claim 3 is characterized in that described coating is made up of polyvinylchloride.