CN2265283Y - Pad for high and low pressure press - Google Patents

Pad for high and low pressure press Download PDF

Info

Publication number
CN2265283Y
CN2265283Y CN 95228208 CN95228208U CN2265283Y CN 2265283 Y CN2265283 Y CN 2265283Y CN 95228208 CN95228208 CN 95228208 CN 95228208 U CN95228208 U CN 95228208U CN 2265283 Y CN2265283 Y CN 2265283Y
Authority
CN
China
Prior art keywords
metal
silk
group
forcing press
filament
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CN 95228208
Other languages
Chinese (zh)
Inventor
布鲁诺·亨内肯
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Rheinische Filztuchfabrik GmbH
Original Assignee
Rheinische Filztuchfabrik GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Rheinische Filztuchfabrik GmbH filed Critical Rheinische Filztuchfabrik GmbH
Priority to CN 95228208 priority Critical patent/CN2265283Y/en
Application granted granted Critical
Publication of CN2265283Y publication Critical patent/CN2265283Y/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

The utility model relates to a pressure pad for a high and low pressure device and is formed by the fact that a type of threads in group A and at least one type of threads in group B are interwoven, wherein, the definitions about the group A and group B follows the specification. The pressure pad of the invention has obvious and improved lining pad effect and favorable heat transferring capability which are can be kept for a long time under heavy pressure and high temperature.

Description

The forcing press pad that is used for high pressure and low pressure machine
The utility model relates to the forcing press pad that a kind of usefulness does not contain the material manufacturing of asbestos, it is used for various dissimilar high pressure and low pressure machine, for example be used for the short circulation and the multi-daylight press of the particle plate of lamination band melamine etc., be used to other forcing press of producing the high-pressure machine of high-pressure laminating thing and multiple other purposes being arranged.Listed herein only is exemplary, does not think that its claimed scope is completely.
Forcing press above-mentioned all is the mechanical system by different temperatures and pressure work.These forcing presses itself and downtrodden material all have bigger tolerance substantially.In this forcing press, the task of forcing press pad is to compensate these tolerances, and pressure is passed to equably on the whole surface of pressurized material.
In addition, the forcing press pad must have good thermal conductivity, can transmit with the possible loss of minimum so that make the required heat of final products.
The forcing press pad must can not only compensate above-mentioned tolerance and have good thermal conductivity, but also sizable pressure that must be able to stand on forcing press, to produce sometimes and quite high temperature, they also must can both keep these characteristics in long time simultaneously.
The following various forcing press pads of current main use: with comprising the thread mat that does not contain asbestos wiry, the mat made from the combination of same line and simple metal silk, the simple metal pad, the ox-hide paper washer has the forcing press pad (seeing GMG9203498.5) of wool surface layer.Listed herein only is exemplary, does not think completely.
The purpose of this utility model provides a kind of forcing press pad, and it has great liner effect and the good heat transfer ability improved, and also can keep these characteristics for a long time when being subjected to sizable pressure and quite high temperature sometimes.
In order to reach this purpose, of the present utility model being characterized as, the forcing press pad is interwoven by the line of at least a A group and the line of at least a B group.The line of described A group comprises:
(1) line formed of the filament made of filament of making by at least a aromatic polyamides and at least a metal material, described metal material comprises metal and metal alloy; And
(2) line that constitutes of the filament of being made by at least a metal material, described metal material comprises metal and metal alloy.
The line of described B group comprises:
(1) the heat-resisting silk of making by at least a rubber or mix the heat-resisting silk that constitutes by the fiber that rubber not of the same race is made;
(2) the heat-resisting silk of making by at least a polysiloxanes or mix the heat-resisting silk that constitutes by the fiber that different polysiloxanes is made;
(3) the heat-resisting silk of making by at least a flexiplast or mix and the heat-resisting silk that constitutes by the fiber that different flexiplasts is made;
(4) comprise an outer and metal-cored filament, described shell comprises the silk of being made by at least a following material, be that described material is from making B group (1), (2), select in the material of the silk (3), and the described metal-cored at least one silk made from at least a metal material that comprise, above-mentioned metal material comprises metal and metal alloy;
(5) filament that twines by wire, these filaments comprise the fiber made from at least a following material, and described material is from making B group (1), (2), select in the material of the silk (3) or in (4), described wire comprises the fiber of being made by at least a metal material, and described metal material comprises metal and metal alloy; And
(6) filament of making by at least a aromatic polyamides.
Described forcing press pad can be the individual layer braiding or multi-layer braided.
The present invention also provides a kind of forcing press pad, it is characterized in that, it is interwoven by filament made from at least a aromatic polyamides and at least a following fine rule, and described one group of fine rule comprises:
(1) the heat-resisting silk of making by at least a rubber;
(2) the heat-resisting silk of making by at least a polysiloxanes;
(3) the heat-resisting silk of making by at least a flexiplast;
(4) comprise an outer and metal-cored filament, described skin is made above-mentioned (1) by using, (2), (3) planting the filament that at least a material in the material of filament makes constitutes, and the described metal-cored silk that is made of at least one fiber made from at least a metal material constitutes, and described metal material comprises metal and metal alloy;
(5) by employing at least a manufacturing above-mentioned (1), (2), the fibrous filament that is wound that the material of (3) or (4) kind filament is made is the wire of being made by at least a metal material in order to what twine it, described metal comprises metal and metal alloy.
Described forcing press pad can be the individual layer braiding or multi-layer braided.
But, not claimed for the combination of the line of the 1st group of material and 2.6 groups, because it is open in based on the prior art of United States Patent (USP) 5298322.
People can select the diameter of the material of 2.1-2.6 group according to desired liner effect.If necessary, the thickness of forcing press pad thereby the liner effect just followed also can reach by the single or multiple lift braiding.
Sometimes, for example in long pressure process, the thermal conductivity of forcing press pad is less important. in this case, following combination of materials also can obtain useful result:
I) a kind of combination in the material of 2.6 groups material and 2.1-2.5 group
II) some kinds of combinations in the material of 2.6 groups material and 2.1-2.5 group
2.4 the metal-cored of material of group can be made up of monofilament or multifibres.
To illustrate in greater detail the utility model according to embodiment below, from these embodiment, also can obtain other key character.Among the figure:
Fig. 1 shows the cutaway view according to forcing press pad of the present invention,
Fig. 2 shows the view of line used herein,
Fig. 3 shows 2.4 groups metal-cored material of multifibres,
Fig. 4 shows 2.4 groups metal-cored material of monofilament.
Accompanying drawing only shows some material according to a forcing press pad embodiment of the present invention; Complete composition can be by further obtaining in above-mentioned data and the claim.
Forcing press pad 10 shown in Figure 1 has the line of being made by for example aromatic polyamide filament 20 that interweaves and the heat-resisting silk of for example being made by rubber, polysiloxanes or the mixture of the two 30 made.
As shown in Figure 2, line 40 comprises a core 41 and the silk thread 42 that is wrapped on this core.Core 41 can be metal-cored 41, and it is made by one or more filament.Silk thread 42 can be made with for example heat proof material of rubber, polysiloxanes or flexiplast, and they are wrapped on metal-cored 41.In addition, also can make core 41, and make silk thread 42 with metal material with the heat proof material of for example rubber, polysiloxanes or flexiplast.
Fig. 3 shows an embodiment of silk thread 60, and this silk thread 60 comprises one metal-cored 61 and one skin 62.Metal-cored 61 comprise the many wires made from fiber 61, and outer 62 by for example rubber, and the heat proof material of polysiloxanes or flexiplast is made, and this skin is provided with around metal-cored 61.
Fig. 4 shows a kind of modification embodiment illustrated in fig. 3, and this silk thread 70 comprises one metal-cored 71 and one skin 72, and wherein metal-cored 71 is to make with the single wire of for example copper or brass.
Example according to application or its combination of different silk thread materials of the present utility model is provided below.1. total situation
The forcing press pad wishes to have two key properties:
1. good liner effect (=tolerance compensating)
2. good thermal conductivity
In order to obtain good liner effect, people need a thick as far as possible forcing press pad.But when the thickness of forcing press pad increased, heat-transfer capability can degenerate in general.
In order to obtain good thermal conductivity, people need the material with good thermal conductivity as much as possible.But, if make the forcing press pad,, do not have the liner effect though this mat has optimal thermal conductivity with simple metal, this be because of, the mat of making of simple metal does not have recovery capability, this also just means does not have the liner ability.
Because the user has various plant equipment (forcing press), and produces various products, so the forcing press pad must satisfy the requirement that much has nothing in common with each other.With regard to certain customers, used new product usually requires to have corresponding adjustment and new development in the field of forcing press pad.Therefore, concerning various application scenarios, need between above-mentioned two kinds of extreme cases having found, try to achieve technology and the coordination of cost rationally.2. for example: I for example:
The mat that extraordinary liner effect is arranged: thermal conductivity is less important (very low).
The composition of mat: a kind of or some kinds of combinations of the material of 2.6 groups material and 2.1-2.3 group.Example II: the mat that has good thermal conductivity and good liner effect simultaneously.
The composition of mat: the combination of materials of 1.2 groups material and 2.5 groups.Example III: the mat of liner effect and thermal conductivity equilibrium.
The composition of mat: the combination of materials of 1.1 groups material and 2.4 groups.

Claims (4)

1. a forcing press pad is characterized in that, it is interwoven by the line of at least a A group and the line of at least a B group.
2. forcing press pad as claimed in claim 1 is characterized in that, the line of described A group comprises:
(1) line formed of the filament made of filament of making by at least a aromatic polyamides and at least a metal material, described metal material comprises metal and metal alloy; And
(2) line that constitutes of the filament of being made by at least a metal material, described metal material comprises metal and metal alloy.
3. forcing press pad as claimed in claim 1 is characterized in that, the line of described B group comprises:
(1) the heat-resisting silk of making by at least a rubber or mix the heat-resisting silk that constitutes by the fiber that rubber not of the same race is made;
(2) the heat-resisting silk of making by at least a polysiloxanes or mix the heat-resisting silk that constitutes by the fiber that different polysiloxanes is made;
(3) the heat-resisting silk of making by at least a flexiplast or mix and the heat-resisting silk that constitutes by the fiber that different flexiplasts is made;
(4) comprise an outer and metal-cored filament, described shell comprises the silk of being made by at least a following material, be that described material is from making B group (1), (2), select in the material of the silk (3), and the described metal-cored at least one silk made from at least a metal material that comprise, above-mentioned metal material comprises metal and metal alloy;
(5) filament that twines by wire, these filaments comprise the fiber made from at least a following material, and described material is from making B group (1), (2), select in the material of the silk (3) or in (4), described wire comprises the fiber of being made by at least a metal material, and described metal material comprises metal and metal alloy; And
(6) filament of making by at least a aromatic polyamides.
4. forcing press pad as claimed in claim 1 is characterized by, and described forcing press pad can be the individual layer braiding or multi-layer braided.
CN 95228208 1994-11-25 1995-11-24 Pad for high and low pressure press Expired - Lifetime CN2265283Y (en)