CN218977759U - High-strength high-corrosion-resistance color fishhook - Google Patents

High-strength high-corrosion-resistance color fishhook Download PDF

Info

Publication number
CN218977759U
CN218977759U CN202320089329.4U CN202320089329U CN218977759U CN 218977759 U CN218977759 U CN 218977759U CN 202320089329 U CN202320089329 U CN 202320089329U CN 218977759 U CN218977759 U CN 218977759U
Authority
CN
China
Prior art keywords
coating layer
fishhook
coated
layer
resistance
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202320089329.4U
Other languages
Chinese (zh)
Inventor
占建飞
张恒
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Poyang Changming Fishing Gear Co ltd
Original Assignee
Poyang Changming Fishing Gear Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Poyang Changming Fishing Gear Co ltd filed Critical Poyang Changming Fishing Gear Co ltd
Priority to CN202320089329.4U priority Critical patent/CN218977759U/en
Application granted granted Critical
Publication of CN218977759U publication Critical patent/CN218977759U/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The utility model discloses a high-strength high-corrosion-resistance colored fishhook, which comprises a fishhook body, wherein the fishhook body comprises a polyimide coating layer, the bottom of the polyimide coating layer is coated with a cyanide coagulation coating layer, the bottom of the cyanide coagulation coating layer is coated with a polytetrafluoroethylene coating layer, the bottom of the polytetrafluoroethylene coating layer is coated with a modified polyphenylene sulfide coating layer, the modified polyphenylene sulfide coating layer comprises an epoxy zinc-rich primer layer, the bottom of the epoxy zinc-rich primer layer is coated with an epoxy iron red primer layer, and the bottom of the epoxy iron red primer layer is coated with red lead antirust paint. According to the utility model, through the arrangement of the polyimide coating layer, the cyanide coating layer, the polytetrafluoroethylene coating layer and the modified polyphenylene sulfide coating layer, the problems that the conventional fishhook does not have an anti-corrosion function, the service life of the fishhook is greatly reduced, the working efficiency is greatly reduced, the market share is reduced, and the use requirements of people cannot be met are solved.

Description

High-strength high-corrosion-resistance color fishhook
Technical Field
The utility model relates to the technical field of fishhooks, in particular to a high-strength high-corrosion-resistance colored fishhook.
Background
The utility model provides a fish hook (fish hook), is used for hanging bait in order to attract the instrument of fishhook on the fishing, and the development of present fish hook is very fast, and the type is various, has stainless steel, has carbon material's alloy steel, and size model classification is also more, and the fish hook (fish hook), and the fish hook comprises handle head, shank, hook bend, hook point, hook door, six parts at the bottom of the hook, and every part has its specific function, is the requisite tool when fishing, and perfect fishing tackle combination is the edge of helping you to become the high hand of fishing, and the fish hook is one of which the key, but current fish hook does not possess anticorrosive function, great reduction fish hook's life, great reduction work efficiency, reduced market share, unable satisfying people's user demand.
Disclosure of Invention
The utility model aims to provide a high-strength high-corrosion-resistance colored fishhook, which has the corrosion-resistance advantage, and solves the problems that the conventional fishhook does not have the corrosion-resistance function, the service life of the fishhook is greatly reduced, the working efficiency is greatly reduced, the market share is reduced, and the use requirement of people cannot be met.
In order to achieve the above purpose, the present utility model provides the following technical solutions: the utility model provides a high-strength high anticorrosive colored fishhook, includes the fishhook body, the fishhook body is including polyimide coating layer, the bottom coating of polyimide coating layer has the cyanogen congeal coating layer, the bottom coating of cyanogen congeal coating layer has polytetrafluoroethylene coating layer, the bottom coating of polytetrafluoroethylene coating layer has modified polyphenylene sulfide coating layer.
Preferably, the modified polyphenylene sulfide coating layer comprises an epoxy zinc-rich primer layer, and an epoxy iron oxide red primer layer is coated at the bottom of the epoxy zinc-rich primer layer.
Preferably, the bottom of the epoxy iron oxide red primer layer is coated with red lead antirust paint, and the bottom of the red lead antirust paint is coated with a polyethylene resin layer.
Preferably, the polyimide coating layer and the cyanide coating layer are connected through a PA coating layer, and the thickness of the polyimide coating layer is zero and three millimeters.
Preferably, the red lead antirust paint and the polyethylene resin layer are connected through the polyurethane resin layer, and the thickness of the red lead antirust paint is zero and three millimeters.
Compared with the prior art, the utility model has the following beneficial effects:
1. according to the utility model, through the arrangement of the polyimide coating layer, the cyanide coating layer, the polytetrafluoroethylene coating layer and the modified polyphenylene sulfide coating layer, the problems that the conventional fishhook does not have an anti-corrosion function, the service life of the fishhook is greatly reduced, the working efficiency is greatly reduced, the market share is reduced, and the use requirements of people cannot be met are solved.
2. The epoxy zinc-rich primer layer has the advantages of good mechanical property, high hardness, good plasticity, water resistance, rust resistance and corrosion resistance, and the epoxy iron oxide red primer layer has excellent rust resistance, water resistance and chemical corrosion resistance and has good adhesive force after coating.
Drawings
FIG. 1 is a schematic diagram of the structure of the present utility model;
FIG. 2 is a cross-sectional view of the body of the fishhook of the utility model;
FIG. 3 is a cross-sectional view of a modified polyphenylene sulfide coating layer of the present utility model.
In the figure: 1. a fishhook body; 101. a polyimide coating layer; 102. a layer of a cyanogen-curable coating; 103. a polytetrafluoroethylene coating; 104. a modified polyphenylene sulfide coating layer; 1041. an epoxy zinc-rich primer layer; 1042. an epoxy red primer layer; 1043. red lead antirust paint; 1044. a polyethylene resin layer.
Detailed Description
The following description of the embodiments of the present utility model will be made clearly and completely with reference to the accompanying drawings, in which it is apparent that the embodiments described are only some embodiments of the present utility model, but not all embodiments. All other embodiments, which can be made by those skilled in the art based on the embodiments of the utility model without making any inventive effort, are intended to be within the scope of the utility model.
Referring to fig. 1-3, a high-strength and high-corrosion-resistance colored fishhook comprises a fishhook body 1, wherein the fishhook body 1 comprises a polyimide coating layer 101, a cyanide coating layer 102 is coated at the bottom of the polyimide coating layer 101, a polytetrafluoroethylene coating layer 103 is coated at the bottom of the cyanide coating layer 102, a modified polyphenylene sulfide coating layer 104 is coated at the bottom of the polytetrafluoroethylene coating layer 103, and the fishhook has the advantages of good electrical insulation performance, good heat resistance, good mechanical property, irradiation resistance, good mechanical property, high tensile strength, organic solvent resistance, ozone resistance, mildew resistance and corrosion resistance, and has the advantages of long service life, weather resistance, aging resistance, oil stain resistance, water resistance and excellent corrosion resistance, and the advantages of acid and alkali resistance, corrosion resistance, various organic solvents and good high temperature resistance, and the advantages of high-temperature resistance, acid and alkali resistance and strong solvents are also realized through the arrangement of the modified polyphenylene sulfide coating layer 104.
The modified polyphenylene sulfide coating layer 104 comprises an epoxy zinc-rich primer layer 1041, wherein an epoxy iron oxide red primer layer 1042 is coated at the bottom of the epoxy zinc-rich primer layer 1041, and the modified polyphenylene sulfide coating layer has the advantages of good mechanical property, high hardness, good plasticity, water resistance, rust resistance and corrosion resistance through the arrangement of the epoxy zinc-rich primer layer 1041, and has excellent rust resistance, water resistance and chemical corrosion resistance through the arrangement of the epoxy iron oxide red primer layer 1042, and the adhesive force after coating is good.
The bottom of the epoxy red primer layer 1042 is coated with red lead rust inhibitive paint 1043, and the bottom of the red lead rust inhibitive paint 1043 is coated with a polyethylene resin layer 1044.
The polyimide coating layer 101 and the cyanide coating layer 102 are connected by a PA coating, and the thickness of the polyimide coating layer 101 is zero three millimeters.
The red lead antirust paint 1043 and the polyethylene resin layer 1044 are connected by a polyurethane resin layer, and the thickness of the red lead antirust paint 1043 is zero and three millimeters.
When in use, the polyimide coating layer 101 has the advantages of good electrical insulation performance, good heat resistance, good mechanical properties, high tensile strength, organic solvent resistance, ozone resistance, mildew resistance and good corrosion resistance, the cyanide coating layer 102 has the advantages of long service life, weather resistance, aging resistance, oil stain resistance, water resistance and excellent corrosion resistance, the polytetrafluoroethylene coating layer 103 has the advantages of acid resistance, alkali resistance, corrosion resistance, various organic solvents resistance and good high temperature resistance, and the modified polyphenylene sulfide coating layer 104 has the advantages of good impact resistance, high hardness, high temperature resistance, and corrosion resistance of non-oxidizing acid, concentrated alkali and solvents.
Although embodiments of the present utility model have been shown and described, it will be understood by those skilled in the art that various changes, modifications, substitutions and alterations can be made therein without departing from the principles and spirit of the utility model, the scope of which is defined in the appended claims and their equivalents.

Claims (5)

1. The utility model provides a high-strength high anticorrosive colored fishhook, includes fishhook body (1), its characterized in that: the fishhook comprises a fishhook body (1) and is characterized in that the fishhook body comprises a polyimide coating layer (101), a cyanide coating layer (102) is coated on the bottom of the polyimide coating layer (101), a polytetrafluoroethylene coating layer (103) is coated on the bottom of the cyanide coating layer (102), and a modified polyphenylene sulfide coating layer (104) is coated on the bottom of the polytetrafluoroethylene coating layer (103).
2. The high-strength high-corrosion-resistance colored fishhook of claim 1, wherein: the modified polyphenylene sulfide coating layer (104) comprises an epoxy zinc-rich primer layer (1041), and an epoxy iron red primer layer (1042) is coated at the bottom of the epoxy zinc-rich primer layer (1041).
3. The high-strength high-corrosion-resistance colored fishhook of claim 2, wherein: the bottom of the epoxy iron oxide red primer layer (1042) is coated with red lead antirust paint (1043), and the bottom of the red lead antirust paint (1043) is coated with a polyethylene resin layer (1044).
4. The high-strength high-corrosion-resistance colored fishhook of claim 1, wherein: the polyimide coating layer (101) and the cyanide coating layer (102) are connected through the PA coating, and the thickness of the polyimide coating layer (101) is zero and three millimeters.
5. A high strength, high corrosion resistance colored fish hook as defined in claim 3, wherein: the red lead antirust paint (1043) and the polyethylene resin layer (1044) are connected through the polyurethane resin layer, and the thickness of the red lead antirust paint (1043) is zero and three millimeters.
CN202320089329.4U 2023-01-31 2023-01-31 High-strength high-corrosion-resistance color fishhook Active CN218977759U (en)