CN218912043U - Honeycomb type interlayer high-strength aluminum veneer - Google Patents
Honeycomb type interlayer high-strength aluminum veneer Download PDFInfo
- Publication number
- CN218912043U CN218912043U CN202222982861.7U CN202222982861U CN218912043U CN 218912043 U CN218912043 U CN 218912043U CN 202222982861 U CN202222982861 U CN 202222982861U CN 218912043 U CN218912043 U CN 218912043U
- Authority
- CN
- China
- Prior art keywords
- aluminium
- honeycomb core
- aluminum
- aluminum alloy
- honeycomb
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model relates to a dalle technical field, and disclose a honeycomb intermediate layer high strength aluminium veneer, including aluminium veneer body, aluminium veneer body includes aluminum alloy panel, aluminum alloy bottom plate, two adhesive layer and aluminium system honeycomb core, two the adhesive layer is located the even coating setting of up and down terminal surface of aluminium system honeycomb core respectively, aluminum alloy bottom plate is through the fixed bonding setting of the lower terminal surface of homonymy adhesive layer and aluminium system honeycomb core, aluminum alloy panel passes through the fixed bonding setting of the up end of homonymy adhesive layer and aluminium system honeycomb core. This application is through compound cellular porous aluminium structure between panel and bottom plate, holistic quality is light, and structural strength is high to possess good thermal-insulated noise reduction performance, self weatherability, corrosion resistance, difficult ageing discoloration performance are better simultaneously.
Description
Technical Field
The application relates to the technical field of decorative boards, in particular to a honeycomb type interlayer high-strength aluminum veneer.
Background
The aluminum veneer is a building decoration material which is processed by chromizing and other treatments and then adopting a fluorocarbon spraying technology, and the fluorocarbon coating is mainly polyvinylidene fluoride resin and can be used for indoor and outdoor decoration plates.
In the process of realizing the application, the inventor finds that at least the following problems exist in the technology, the aluminum veneer is commonly used for curtain wall decoration, and the aluminum veneer after forming is relatively thin and low in strength because of the softer texture of the aluminum material, and the aluminum veneer is poor in heat insulation performance, high in use limitation and poor in effect because of the good heat conduction performance of the aluminum material, and the formed aluminum veneer is poor in sound absorption and noise reduction performance, so that the honeycomb interlayer high-strength aluminum veneer is provided.
Disclosure of Invention
The purpose of this application is in order to solve among the prior art because aluminum product itself texture is softer, so the aluminium veneer after the shaping is comparatively single thin, intensity is not high, and because the aluminum product possesses good heat conduction performance, so the thermal-insulated performance of aluminium veneer itself of formation is not good moreover, and it is also not good enough to inhale sound noise reduction performance, and the use is limited greatly, problem that the effect is not good, and a honeycomb intermediate layer high strength aluminium veneer is proposed.
In order to achieve the above purpose, the present application adopts the following technical scheme:
the utility model provides a honeycomb intermediate layer high strength aluminium veneer, includes aluminium veneer body, aluminium veneer body includes aluminum alloy panel, aluminum alloy bottom plate, two adhesive layer and aluminium system honeycomb core, two the adhesive layer is located the even coating setting of up and down terminal surface of aluminium system honeycomb core respectively, aluminum alloy bottom plate is fixed to bond the setting through the lower terminal surface of homonymy adhesive layer and aluminium system honeycomb core, aluminum alloy panel is fixed to bond the setting through homonymy adhesive layer and the up end of aluminium system honeycomb core.
Preferably, a plurality of regular hexagonal holes are formed in the end face of the aluminum honeycomb core, and the regular hexagonal holes are uniformly distributed on the aluminum honeycomb core.
Preferably, the thickness of the aluminum veneer body is 10mm, and the thicknesses of the aluminum alloy panel and the aluminum alloy bottom plate are 1.0mm.
Preferably, the shapes of the two adhesive layers are matched with the shapes of the aluminum honeycomb cores.
Preferably, the thickness of the two adhesive layers is set in the range of 0.2mm to 0.4 mm.
Preferably, the aluminum alloy panel, the aluminum alloy bottom plate and the aluminum honeycomb core are all made of 3003 aluminum alloy.
Preferably, fluorocarbon paint is sprayed on the opposite ends of the aluminum alloy panel and the aluminum alloy bottom plate.
Compared with the prior art, the application provides a honeycomb formula intermediate layer high strength aluminium veneer, possesses following beneficial effect:
1. this honeycomb intermediate layer high strength aluminium veneer through the aluminium alloy panel that is equipped with, aluminium alloy bottom plate, gluing agent layer and aluminium honeycomb core constitute's aluminium veneer body, through set up honeycomb between aluminium alloy panel and aluminium alloy bottom plate, can be lighter than traditional aluminium veneer etc. ornamental material on the one hand, utilizes honeycomb porous structure moreover, holistic structural strength is high, and the heat conduction performance of aluminium veneer body can be reduced to utilizing the porous moreover, in order to improve the thermal-insulated performance of aluminium veneer body, and pass through the wave of porous noise reduction, make aluminium veneer body possess certain sound insulation and fall the performance of making an uproar.
2. The honeycomb type interlayer high-strength aluminum veneer is made of 3003 aluminum alloy through the aluminum alloy panel, the aluminum alloy bottom plate and the aluminum honeycomb core, so that the aluminum veneer body after composite forming has higher strength and is not easy to deform and damage, and the performances of weather resistance, corrosion resistance, difficult aging, color change and the like of the aluminum veneer body can be improved through the sprayed fluorocarbon coating.
The device does not involve the part and all is the same with prior art or can adopt prior art to realize, and this application is through compound cellular porous aluminium structure between panel and bottom plate, and holistic structural strength is high to possess good thermal-insulated noise reduction performance, self weatherability, corrosion resistance, difficult ageing discoloration performance are better simultaneously.
Drawings
Fig. 1 is a schematic structural diagram of a honeycomb-type interlayer high-strength aluminum veneer proposed in the present application;
fig. 2 is a schematic top view of the aluminum honeycomb core of fig. 1.
In the figure: 1. an aluminum veneer body; 2. an aluminum alloy panel; 3. an aluminum alloy bottom plate; 4. an adhesive layer; 5. an aluminum honeycomb core; 6. a regular hexagonal hole; 7. fluorocarbon coating.
Detailed Description
The following description of the embodiments of the present application will be made clearly and fully with reference to the accompanying drawings, in which it is evident that the embodiments described are only some, but not all, of the embodiments of the present application.
Referring to fig. 1-2, a honeycomb type interlayer high strength aluminum veneer, which comprises an aluminum veneer body 1, wherein the aluminum veneer body 1 comprises an aluminum alloy panel 2, an aluminum alloy bottom plate 3, two adhesive layers 4 and an aluminum honeycomb core 5, wherein the two adhesive layers 4 are respectively positioned on the upper end face and the lower end face of the aluminum honeycomb core 5 and are uniformly coated, the aluminum alloy bottom plate 3 is fixedly adhered to the lower end face of the aluminum honeycomb core 5 through the adhesive layers 4 on the same side, the aluminum alloy panel 2 is fixedly adhered to the upper end face of the aluminum honeycomb core 5 through the adhesive layers 4 on the same side, and when the aluminum veneer body 1 is used, if cutting processing is carried out, common plate cutting equipment can be used, special equipment is not needed, and convenience in processing and use cannot be influenced.
The end face of the aluminum honeycomb core 5 is provided with a plurality of regular hexagon holes 6, each regular hexagon hole 6 is uniformly distributed on the aluminum honeycomb core 5, and the structural strength of the whole aluminum honeycomb core 5 can be ensured through the regular hexagon holes 6.
The thickness of the aluminum veneer body 1 is 10mm, the thicknesses of the aluminum alloy panel 2 and the aluminum alloy bottom plate 3 are 1.0mm, the thickness of the aluminum veneer body 1 can be adjusted according to the use requirement, and meanwhile, the thicknesses of the aluminum alloy panel 2 and the aluminum alloy bottom plate 3 also need to be adjusted along with the adjustment.
The shape of two gluing agent layers 4 all sets up with aluminium system honeycomb core 5's shape phase-match, through this kind of setting, even gluing agent 4 staggers a plurality of regular hexagon holes 6 on the aluminium system honeycomb core 5 to can pack and glue under the firm circumstances, can reduce the waste of gluing agent.
The thickness of the two adhesive layers 4 is set in the range of 0.2mm to 0.4mm, ensuring that the adhesive layers 4 are not too thick under the condition that the adhesive layers 4 can provide sufficient tackiness.
The aluminum alloy panel 2, the aluminum alloy bottom plate 3 and the aluminum honeycomb core 5 are all made of 3003 aluminum alloy, and the 3003 aluminum alloy material has higher strength, so that the manufactured aluminum alloy panel 2 and aluminum alloy bottom plate 3 have higher strength.
The fluorocarbon coating 7 is sprayed on the opposite ends of the aluminum alloy panel 2 and the aluminum alloy bottom plate 3, and the fluorocarbon coating 7 can enable the aluminum veneer body 1 to have the characteristics of good finish, strong adhesive force, weather resistance, acid and alkali resistance, pulverization resistance, aging resistance, ultraviolet irradiation resistance and no color change.
In this application, during the use, through the aluminium veneer body 1 that comprises aluminium alloy panel 2, aluminium alloy bottom plate 3, gluing agent layer 4 and aluminium honeycomb core 5, through aluminium honeycomb core 5 that sets up between aluminium alloy panel 2 and aluminium alloy bottom plate 3, utilize porous honeycomb structure, on the one hand can be lighter than traditional decoration material such as aluminium veneer, utilize honeycomb porous structure moreover, holistic structural strength is high, and because porous structure can reduce the heat conduction contact surface, thereby can reduce the heat conduction performance of aluminium veneer body 1, in order to improve the thermal-insulated performance of aluminium veneer body 1, and absorb the reflection sound wave through the porous, thereby the wave transmission of noise reduction, make aluminium veneer body 1 possess certain sound insulation and fall the noise performance.
The foregoing is only a preferred embodiment of the present application, but the scope of the present application is not limited thereto, and any person skilled in the art, within the scope of the present application, should apply to the present application, and all equivalents and modifications as fall within the scope of the present application.
Claims (7)
1. The utility model provides a honeycomb intermediate layer high strength aluminium veneer, includes aluminium veneer body (1), its characterized in that, aluminium veneer body (1) include aluminum alloy panel (2), aluminum alloy bottom plate (3), two gluing agent layer (4) and aluminium system honeycomb core (5), two gluing agent layer (4) are located the even coating setting of up and down terminal surface of aluminium system honeycomb core (5) respectively, aluminum alloy bottom plate (3) are through homonymy gluing agent layer (4) and the fixed bonding setting of lower terminal surface of aluminium system honeycomb core (5), aluminum alloy panel (2) are through homonymy gluing agent layer (4) and the fixed bonding setting of up end of aluminium system honeycomb core (5).
2. The honeycomb sandwich high-strength aluminum veneer according to claim 1, wherein a plurality of regular hexagonal holes (6) are formed in the end face of the aluminum honeycomb core (5), and each regular hexagonal hole (6) is uniformly distributed on the aluminum honeycomb core (5).
3. A honeycomb sandwich high strength aluminium veneer according to claim 1, characterized in that the aluminium veneer body (1) has a thickness of 10mm, the aluminium alloy panel (2) and the aluminium alloy base plate (3) each having a thickness of 1.0mm.
4. A honeycomb sandwich high strength aluminium veneer according to claim 1, characterised in that both said adhesive layers (4) are shaped to match the shape of the aluminium honeycomb core (5).
5. A honeycomb sandwich high strength aluminium veneer according to claim 1, characterised in that the thickness of both said adhesive layers (4) is arranged in the range of 0.2mm to 0.4 mm.
6. A honeycomb sandwich high strength aluminium veneer according to claim 1, characterised in that the aluminium alloy panel (2), the aluminium alloy base plate (3) and the aluminium honeycomb core (5) are all made of 3003 aluminium alloy.
7. A honeycomb sandwich high strength aluminium veneer according to claim 1, characterized in that the opposite ends of the aluminium alloy panel (2) and the aluminium alloy bottom plate (3) are both coated with fluorocarbon paint (7).