CN216662956U - High-strength composite antibacterial breathable film - Google Patents
High-strength composite antibacterial breathable film Download PDFInfo
- Publication number
- CN216662956U CN216662956U CN202220300357.1U CN202220300357U CN216662956U CN 216662956 U CN216662956 U CN 216662956U CN 202220300357 U CN202220300357 U CN 202220300357U CN 216662956 U CN216662956 U CN 216662956U
- Authority
- CN
- China
- Prior art keywords
- layer
- breathable film
- woven fabric
- antibacterial
- melt adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model belongs to the technical field of breathable films, and particularly relates to a high-strength composite antibacterial breathable film which comprises a waterproof breathable film, non-woven fabric layers, antibacterial layers, reinforcing ribs, a hot melt adhesive layer and release paper. According to the utility model, the upper surface and the lower surface of the waterproof breathable film are respectively provided with the non-woven fabric layer, and the antibacterial layer and the reinforcing ribs are designed in the non-woven fabric layers, so that on one hand, the integral strength can be increased, the anti-tearing structure is not easy to tear, and on the other hand, the breeding of bacteria can be inhibited.
Description
Technical Field
The utility model relates to the field of breathable films, in particular to a high-strength composite antibacterial breathable film.
Background
Breathable films are used in a wide variety of sanitary products, such as diapers for babies, adult diapers, adult care products, sanitary napkins and panty liners. In these products, because the breathable film is directly contacted with the skin, but only has the breathable function and no antibacterial effect, bacteria are easy to grow after long-term use, a lot of discomfort is caused to the human body, and the overall strength is low, so that the breathable film is easy to tear. Therefore, improvements are needed.
SUMMERY OF THE UTILITY MODEL
The utility model aims to provide a high-strength composite antibacterial breathable film, which solves the problems that the existing breathable film only has a breathable function and does not have an antibacterial effect, so that bacteria are easy to breed after the breathable film is used for a long time, a plurality of discomfort is caused to a human body, the integral strength is low, and the breathable film is easy to tear.
In order to achieve the purpose, the utility model provides the following technical scheme: the utility model provides an antibiotic ventilated membrane of combined type of high strength, includes waterproof ventilated membrane, non-woven fabrics layer, antibiotic layer, strengthening rib, hot melt adhesive layer, leaves type paper, the upper and lower surface of waterproof ventilated membrane is provided with the non-woven fabrics layer, be provided with antibiotic layer and strengthening rib in the non-woven fabrics layer, the surface bonding on one of them non-woven fabrics layer has hot melt adhesive layer, hot melt adhesive layer's surface bonding has from type paper.
Preferably, the number of the reinforcing ribs is multiple, and the plurality of reinforcing ribs are uniformly distributed in the non-woven fabric layer.
Preferably, the surface of one of the non-woven fabric layers is provided with a sawtooth layer, and the sawtooth layer is bonded with the hot melt adhesive layer.
Preferably, the waterproof breathable film is a polyethylene breathable film, and the thickness of the waterproof breathable film is 0.1 mm.
Preferably, the antibacterial layer is made of nano silver, and the thickness of the antibacterial layer is 0.08 mm.
Preferably, the non-woven fabric layer is a needle-punched non-woven fabric, and the thickness of the non-woven fabric layer is 0.24 mm.
Compared with the prior art, the utility model has the following beneficial effects:
1. according to the utility model, the upper surface and the lower surface of the waterproof breathable film are respectively provided with the non-woven fabric layer, and the antibacterial layer and the reinforcing ribs are designed in the non-woven fabric layers, so that on one hand, the integral strength can be increased, the anti-tearing structure is not easy to tear, and on the other hand, the breeding of bacteria can be inhibited.
2. According to the utility model, the sawtooth layer is arranged on the surface of one of the non-woven fabric layers, so that the contact area between the non-woven fabric layers and the hot melt adhesive layer is larger, the connection between the non-woven fabric layers and the hot melt adhesive layer is further more stable, and the non-woven fabric layers and the hot melt adhesive layer are not easy to degum.
Drawings
FIG. 1 is a perspective view of the overall construction of the present invention;
FIG. 2 is a cross-sectional view of the structure of FIG. 1 in accordance with the present invention;
in the figure: 1. a waterproof breathable film; 2. a non-woven fabric layer; 21. an antibacterial layer; 22. reinforcing ribs; 23. a layer of serrations; 3. a hot melt adhesive layer; 4. and (4) release paper.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
Referring to fig. 1-2, a high-strength composite antibacterial breathable film includes a waterproof breathable film 1, a non-woven fabric layer 2, an antibacterial layer 21, a reinforcing rib 22, a hot-melt adhesive layer 3, and release paper 4, the non-woven fabric layer 2 is disposed on the upper and lower surfaces of the waterproof breathable film 1, the antibacterial layer 21 and the reinforcing rib 22 are disposed in the non-woven fabric layer 2, the hot-melt adhesive layer 3 is bonded on the surface of one of the non-woven fabric layers 2, and the release paper 4 is bonded on the surface of the hot-melt adhesive layer 3.
Referring to fig. 1 and 2, the number of the reinforcing ribs 22 is plural, and the plural reinforcing ribs 22 are uniformly distributed in the nonwoven fabric layer 2. Through the design of the reinforcing ribs 22, the strength of the non-woven fabric can be increased, and the non-woven fabric is not easy to tear.
Referring to fig. 1 and 2, a sawtooth layer 23 is disposed on a surface of one of the nonwoven fabric layers 2, and the sawtooth layer 23 is adhered to the hot melt adhesive layer 3. The design of the sawtooth layer 23 enables the contact area between the non-woven fabric layer 2 and the hot melt adhesive layer 3 to be larger.
Referring to fig. 1 and 2, the waterproof breathable film 1 is a polyethylene breathable film, and the thickness of the waterproof breathable film 1 is 0.1 mm. The waterproof breathable film 1 has both waterproof and breathable effects.
Referring to fig. 1 and 2, the antibacterial layer 21 is made of nano silver, and the thickness of the antibacterial layer 21 is 0.08 mm. The antibacterial layer 21 prevents bacteria from growing on the nonwoven fabric layer 2.
Referring to fig. 1 and 2, the nonwoven fabric layer 2 is a needle-punched nonwoven fabric, and the thickness of the nonwoven fabric layer 2 is 0.24 mm. The waterproof and breathable film 1 can be protected by the design of the non-woven fabric layer 2.
The specific implementation process of the utility model is as follows: during the use, all set up non-woven fabrics layer 2 at waterproof ventilated membrane 1's upper and lower surface, non-woven fabrics layer 2 adopts the acupuncture non-woven fabrics, and design antibiotic layer 21 and strengthening rib 22 in non-woven fabrics layer 2, can increase holistic intensity on the one hand like this, be difficult for tearing, on the other hand can restrain breeding of bacterium, then set up sawtooth layer 23 on the surface of one of them non-woven fabrics layer 2, make the area of contact between non-woven fabrics layer 2 and the hot melt adhesive layer 3 bigger like this, further make being connected more firm between non-woven fabrics layer 2 and the hot melt adhesive layer 3, be difficult for coming unstuck, later stage tears from hot melt adhesive layer 3 with release paper 4, can use.
Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the utility model, the scope of which is defined in the appended claims and their equivalents.
Claims (6)
1. The utility model provides an antibiotic ventilated membrane of combined type of high strength, includes waterproof ventilated membrane (1), non-woven fabrics layer (2), antibiotic layer (21), strengthening rib (22), hot melt adhesive layer (3), release paper (4), its characterized in that: the waterproof breathable film is characterized in that the upper surface and the lower surface of the waterproof breathable film (1) are provided with non-woven fabric layers (2), an antibacterial layer (21) and reinforcing ribs (22) are arranged in the non-woven fabric layers (2), a hot melt adhesive layer (3) is bonded on the surface of one of the non-woven fabric layers (2), and release paper (4) is bonded on the surface of the hot melt adhesive layer (3).
2. The high-strength composite antibacterial breathable film according to claim 1, wherein: the number of the reinforcing ribs (22) is multiple, and the plurality of the reinforcing ribs (22) are uniformly distributed in the non-woven fabric layer (2).
3. The composite antibacterial breathable film with high strength according to claim 1, wherein: the surface of one of the non-woven fabric layers (2) is provided with a sawtooth layer (23), and the sawtooth layer (23) is bonded with the hot melt adhesive layer (3).
4. The composite antibacterial breathable film with high strength according to claim 1, wherein: the waterproof breathable film (1) is a polyethylene breathable film, and the thickness of the waterproof breathable film (1) is 0.1 mm.
5. The composite antibacterial breathable film with high strength according to claim 1, wherein: the antibacterial layer (21) is made of nano silver, and the thickness of the antibacterial layer (21) is 0.08 mm.
6. The composite antibacterial breathable film with high strength according to claim 1, wherein: the non-woven fabric layer (2) is a needle-punched non-woven fabric, and the thickness of the non-woven fabric layer (2) is 0.24 mm.