CN216022316U - Medical polyurethane foam dressing - Google Patents
Medical polyurethane foam dressing Download PDFInfo
- Publication number
- CN216022316U CN216022316U CN202121484406.3U CN202121484406U CN216022316U CN 216022316 U CN216022316 U CN 216022316U CN 202121484406 U CN202121484406 U CN 202121484406U CN 216022316 U CN216022316 U CN 216022316U
- Authority
- CN
- China
- Prior art keywords
- polyurethane foam
- film
- layer
- medical
- foam dressing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a medical polyurethane foam dressing, which comprises: the polyurethane film, the hydrophilic polyurethane foam layer compounded on the polyurethane film, the release paper arranged on the hydrophilic polyurethane foam layer, and the soft silicone composite material layer positioned below the release paper; the polyurethane film consists of a release film and a PU resin layer or a TPU resin layer coated on the release film; the product can absorb wound exudate of pressure sores, can realize single-sided water resistance, has viscosity, can be stably fixed on the wound, cannot be easily displaced, and ensures continuous and stable imbibition.
Description
Technical Field
The utility model relates to a medical dressing, in particular to a medical polyurethane foam dressing.
Background
The patients who lie in bed for a long time, sit on a wheelchair for a long time or need to perform operations for a long time can not freely move, and the local skin is pressed for a long time, so that the blood circulation is not smooth, and the skin is necrotic and ulcerated after losing nutrients for a long time to form pressure sores/bedsores. Once pressure sores/bedsores are formed, long-term care is needed, and if the care is not carried out properly, the pain of patients is increased, and infection is possibly caused if the illness state is serious. Therefore, the patient who is easy to form pressure sores/bedsores needs to take protective measures in time.
Compared with the traditional gauze dressing, the medical polyurethane foam has better resilience, slow release pressure and absorption pressure, excellent absorption performance of seepage and good biological performance. Can be used for absorbing pus exuded from wounds after pressure sore/bedsore wounds occur to accelerate wound healing and reduce damage to skin around the wounds; however, the conventional polyurethane foam cannot realize single-sided waterproofing and is easy to shift on wounds, and the utility model solves the problem.
SUMMERY OF THE UTILITY MODEL
In order to solve the defects of the prior art, the utility model aims to provide a medical polyurethane foam dressing which can absorb wound exudate of pressure sores, can realize single-side water resistance, has viscosity, can be stably fixed on wounds, cannot be easily displaced, and ensures continuous and stable liquid absorption.
In order to achieve the above object, the present invention adopts the following technical solutions:
a medical polyurethane foam dressing comprising: the polyurethane film, the hydrophilic polyurethane foam layer compounded on the polyurethane film, the release paper arranged on the hydrophilic polyurethane foam layer, and the soft silicone composite material layer positioned below the release paper; the polyurethane film consists of a release film and a PU resin layer or a TPU resin layer coated on the release film.
In the medical polyurethane foam dressing, the roughness of the surface of the polyurethane film after corona treatment is 9-10.
In the medical polyurethane foam dressing, the soft silicone composite material layer is compounded on the hydrophilic polyurethane foam layer; the soft silicone composite material layer is provided with a through hole.
In the medical polyurethane foam dressing, the soft silicone composite material layer is compounded on the polyurethane film and is positioned on two sides of the hydrophilic polyurethane foam layer.
The medical polyurethane foam dressing further comprises: and the surface coating is coated on the surface of the release paper and is a silicon layer or a polymer material layer.
In the medical polyurethane foam dressing, the thickness of the polyurethane film is 15-18 mu m.
The medical polyurethane foam dressing has the thickness of 1.5-7 mm.
The medical polyurethane foam dressing has the thickness of 4-5 mm.
The utility model has the advantages that:
the structural design of the utility model can not only absorb wound exudate of pressure sores, but also realize single-side water prevention;
according to the utility model, the soft silicone composite material layer is arranged, so that the dressing has viscosity, can be stably fixed on a wound, cannot easily shift, and ensures continuous and stable liquid absorption;
the hydrophilic polyurethane foam of the utility model is single-sided waterproof.
Drawings
FIG. 1 is a schematic structural diagram of an embodiment of the present invention;
FIG. 2 is a schematic structural diagram of another embodiment of the present invention;
FIG. 3 is a schematic structural diagram of another embodiment of the present invention;
FIG. 4 is a schematic view of the contact surface between the upper platen and the upper release paper during the preparation process of the present invention;
FIG. 5 is a top view of one embodiment of the upper platen of the present invention;
FIG. 6 is a cross-sectional view of one embodiment of the upper platen of the present invention;
the meaning of the reference symbols in the figures:
1 polyurethane film, 2 hydrophilic polyurethane foam layers, 3 release paper, 4 soft silicone composite material layers, 401 through holes, 5 surface coatings, 601 shaping transition areas, 602 shaping areas and 603 benchmark.
Detailed Description
The utility model is described in detail below with reference to the figures and the embodiments.
As shown in fig. 1, a medical polyurethane foam dressing includes: the polyurethane film comprises a polyurethane film 1, a hydrophilic polyurethane foam layer 2 compounded on the polyurethane film 1, release paper 3 arranged on the hydrophilic polyurethane foam layer 2, and a soft silicone composite material layer 4 positioned below the release paper 3; the polyurethane film 1 is composed of a release film and a PU resin layer or a TPU resin layer coated on the release film. As an embodiment, the release film material can be selected from PE, PET, PP and other materials.
A preparation method of a medical polyurethane foam dressing is characterized by comprising the following steps:
step one, preparing a polyurethane film:
coating PU/TPU resin on a release film material, wherein the coating amount is 15-30g/m2Drying to obtain a polyurethane film with the thickness of 15-18 mu m, and performing primary corona with the corona value of 1-4A and the equipment running speed of 5-10m/min to ensure that the roughness of the surface of the polyurethane film after corona treatment is 9-10 grade;
films with different light sensation textures can be manufactured according to the fog level degree of the surface of the release film, and the polyurethane film 1 can be obtained after the coated resin is dried by the solvent. The amount of the coating can be selected according to the requirements for the air-permeable strength of the film material, etc., and is preferably 15 to 30g/m at present2Preferably 23g/m for increasing the air permeability of the final product2More preferably 17g/m2The thickness of the polyurethane film 1 obtained at this time was 15 to 18 μm. In order to increase the surface roughness, corona can be carried out after coating is finished, and the roughness of the surface of the polyurethane film 1 after corona is 9-10 grades so as to increase the poly-urethane during the preparation of the waterproof film-coated polyurethane foamThe binding force between the polyurethane foam and the surface of the polyurethane film 1.
Step two, preparing hydrophilic polyurethane foam:
the formula of the hydrophilic polyurethane foam comprises the following components in parts by weight: 60-87.5 parts of isocyanate prepolymer, 12-36 parts of water, 0.16-2.8 parts of surfactant and 0.34-1.2 parts of sodium bicarbonate; as an example, the isocyanate prepolymer is toluene diisocyanate TDI, diphenylmethane diisocyanate MDI, hexamethylene diisocyanate HDI or a mixture of two or more thereof, which is not exhaustive, and any isocyanate prepolymer capable of obtaining a hydrophilic polyurethane foam is within the scope of the present invention. As an embodiment, the formula of the hydrophilic polyurethane foam comprises the following components in parts by weight: the mass parts of TDI prepolymer are as follows: 75 parts of water by mass: 23.75 parts, surfactant mass part: 0.75 portion of NaHCO3The mass portion is as follows: 0.5 part. As another example, the mass parts of the TDI prepolymer are as follows: 70 parts of water, by mass: 28.2 parts, surfactant mass part: 1.8 parts.
Mixing the prepolymer, water, a surfactant and a sodium bicarbonate water phase according to a formula, separately stirring the prepolymer at a stirring temperature of 25-35 ℃ and the water phase at a temperature of 15-25 ℃, pouring the materials on the manufactured polyurethane film, wherein the specific pouring method and parameters comprise that the prepolymer and the water phase are mixed by using a low-pressure foaming mixer at a rotating speed of 5000R/min, pouring is carried out by linking a conical plastic pouring head, the discharging size diameter of the pouring head can be cut according to the size of flow, the mixed materials are poured on the running polyurethane film, release paper is covered on the polyurethane film, the surface of the release paper is coated with a surface coating 5, and the polyurethane film is cured for 7-10min through leveling and normal temperature, and the specific leveling method comprises the following steps: the mixed liquid poured on the release paper passes through the upper pressing plate and the lower pressing plate, the gap range of the upper pressing plate and the lower pressing plate is 0.05mm-15cm, and the current application range is preferably 0.05 mm-8 mm according to the requirement. The upper pressing plate and the lower pressing plate are provided with a shaping transition area 601 and a shaping area 602, and the shaping transition area 601 and the shaping area 602 deform relative to a reference 603; the shaping transition area is in a two-way parabolic shape with a high middle part and two low sides, the shaping area is a flat plate, as shown in fig. 6, the shaping transition area adopts parabolic curvature over-shaping, so that uniform change in the shaping process and uniform stress process are ensured, and the shaping transition area is mainly used for shaping to a certain degree on the basis of dispersing liquid. The pressing plate is designed according to the foaming time of the formula, polyurethane foam products with different thicknesses can be produced, then the polyurethane foam products enter an oven to be dried, the dried polyurethane foam is the polyurethane foam of the single-sided composite waterproof breathable polyurethane film 1, and the production is finished through rolling; as an optimization, the material can carry out tension through the transfer roller and adjust, can rectify through deviation correcting device and make the foam rolling even, the off tracking does not, but during the rolling recombination from type paper reduces cohering between the two-layer foam, makes things convenient for the use of next process material, need not to carry out the secondary backrush.
The surface coating 5 is a silicon layer or a polymer material layer, as shown in fig. 2 and 3, and is preferably coated with a polymer material; the square meter weight of the release paper 3 can be selected from 140-2. And then curing at normal temperature for 7-10min, and then drying in an oven, wherein the dried polyurethane foam is the polyurethane foam of the single-sided composite waterproof breathable polyurethane film 1. Medical polyurethane foam dressings of various thicknesses (1.5 to 7mm) can be manufactured according to the difference in flow rate and thickness of the squeegee, and it is preferable that the medical polyurethane foam dressing has a thickness of 4 to 5mm in view of use for pressure sore prevention.
As an example, the surfactant may be one or more of low-foaming nonionic active species such as PE800, PE6300, PE6200, PE6100, and the like, which are not exhaustive.
Step three, arranging a soft silicone composite material layer;
compounding the soft silicone composite material layer 4 and the hydrophilic polyurethane foam layer 2, wherein the compounding pressure range is 5-7Kpa, and the operation speed is 5-8m optimally; the soft silicone composite material layer 4 is provided with a through hole 401. The purpose of the soft silicone composite layer is to make the product sticky;
and step four, the prepared polyurethane foam dressing is subjected to the working procedures of slitting, forming, packaging, sterilizing and the like to obtain the medical polyurethane foam dressing.
The utility model solves the problems that the foam coiled material of the coiled material can not be continuously produced by block foam and the thickness is difficult to control, adopts the one-step forming method to produce the product, can realize the manufacture of the next procedure without secondary rewinding of the produced foam coiled material, and also solves the problem of air permeability loss caused by the gluing and film covering mode. The soft silicone material coated on the surface is not sticky to the skin and is friendly to the skin.
The thickness of the leveling part is controlled by the upper pressing plate and the lower pressing plate, the shape design of the upper pressing plate is designed according to the foaming speed, the thickness can be controlled more accurately, the dilemma that ultrathin materials are difficult to manufacture in the current production process is solved, the thinnest thickness can be 1mm, and the cutting thickness deviation is +/-0.2 mm.
The structural design of the utility model can not only absorb wound exudate of pressure sores, but also realize single-side water prevention; through setting up soft silicone composite material layer 4 for the dressing has viscidity, can be stable fix on the wound, can not shift easily, ensures lasting stable imbibition.
The foregoing illustrates and describes the principles, general features, and advantages of the present invention. It should be understood by those skilled in the art that the above embodiments do not limit the present invention in any way, and all technical solutions obtained by using equivalent alternatives or equivalent variations fall within the scope of the present invention.
Claims (8)
1. A medical polyurethane foam dressing, comprising: the polyurethane film, the hydrophilic polyurethane foam layer compounded on the polyurethane film, the release paper arranged on the hydrophilic polyurethane foam layer, and the soft silicone composite material layer positioned below the release paper; the polyurethane film consists of a release film and a PU resin layer or a TPU resin layer coated on the release film.
2. The medical polyurethane foam dressing as claimed in claim 1, wherein the roughness of the surface of the polyurethane film after corona treatment is 9-10.
3. The medical polyurethane foam dressing as claimed in claim 1, wherein the soft silicone composite layer is compounded on the hydrophilic polyurethane foam layer; the soft silicone composite material layer is provided with a through hole.
4. The medical polyurethane foam dressing as claimed in claim 1, wherein the soft silicone composite layer is compounded on the polyurethane film and positioned on both sides of the hydrophilic polyurethane foam layer.
5. The medical polyurethane foam dressing of claim 1, further comprising: and the surface coating is coated on the surface of the release paper and is a silicon layer or a polymer material layer.
6. The medical polyurethane foam dressing as claimed in claim 1, wherein the thickness of the polyurethane film is 15-18 μm.
7. The medical polyurethane foam dressing as claimed in claim 1, wherein the medical polyurethane foam dressing has a thickness of 1.5-7 mm.
8. The medical polyurethane foam dressing as claimed in claim 7, wherein the medical polyurethane foam dressing has a thickness of 4-5 mm.