Abstract

The utility model discloses a multi-functional corrosive wear multiphase flow erosion corrosion experimental device, which comprises an experimental cavity body of a sealed experimental cavity body cover, wherein a rotary main shaft connected with a motor is arranged on the experimental cavity body cover, a rotary sample plate fixedly connected with a sample is connected with the rotary main shaft and extends into the experimental cavity body, and a test system is arranged on the experimental cavity body cover and is communicated with the experimental cavity body; the control system is respectively connected with the test system, the motor and the heating integrated block, the drive motor drives the rotary sample plate to rotate, and the corrosion and erosion wear surface morphology of the oil gas corrosion test of the sample at the set temperature in the experiment cavity is obtained. The method can accurately simulate the corrosive wear rate and the morphological characteristics of the pipe and the coating sample under the conditions of different sand content ratios, different flow rates, no passing time and the like, and provides reliable data for the research on the corrosive wear rate, the morphological characteristics, the behaviors and the mechanism of the pipe and the coating under the condition of multiphase flow media.

Description

Multi-functional erosive wear multiphase flow erosion corrosion experimental apparatus

Technical Field

The utility model relates to a capability test field of tubular product such as oil gas development coating and plating layer, especially a heterogeneous class of flow erosion and corrosion experimental apparatus of multi-functional erosive wear.

Background

The pipe materials or equipment such as downhole tools, oil pipes, sucker rods, pipelines, reaction vessels and the like in the drilling, fracturing and development production of oil and gas fields can face the high-speed relative motion formed by natural gas carrying liquid or sand grains, an underground metal pipe column and the inner surface of a ground conveying metal pipeline, so that the inner wall of the gas production pipe column is washed to damage the metal surface, and meanwhile, the gas production pipe column is often subjected to corrosive medium CO in wet natural gas medium₂And H₂The corrosion of S is particularly obvious in the erosion damage of the reducing pipe, the elbow and the surface defect. In the oil extraction and oil transportation process, similar equipment, pipe columns and pipelines exist because the produced liquid contains a large amount of aggressive substances such as CO₂、H₂S, dissolving O₂、Cl^-And SRB bacteria and the like are seriously corroded, and the produced liquid contains sand and stone particles in some stratums, solid impurities brought by water injection and the like, so that the abrasion mechanical damage effect is formed on the surface of the inner wall of the material, the pipe is corroded and loses efficacy when the produced liquid is serious, accidents frequently occur, huge economic loss is brought, and the potential hazards of oil field safety and environmental protection are caused.

At present, a weight loss test of a hanging piece is generally carried out in a high-pressure reaction kettle or a corrosion loop experimental device for researching the erosion corrosion of the oil gas pipe, and the corrosion, wear rule and behavior are judged according to the morphological characteristics and the weight loss. Although the former can better simulate the test under the conditions of moving temperature and pressure, the inner wall of the kettle body is usually not a wear-resistant material, sand and stone particles cannot be effectively added to simulate the scouring phenomenon, and the flow state of fluid can be influenced because the kettle body is small; although the latter can meet the test conditions of certain temperature and pressure, has the characteristics of intuition and better accordance with actual conditions, the loop experiment device is often huge, the pipeline cannot adopt wear-resistant materials, the medium and energy consumption input in a single test are huge, the stability is poor, and finally, scientific research cannot be effectively carried out for a long time due to huge input.

Therefore, the erosion corrosion experimental device for developing the corrosion-resistant and wear-resistant multiphase flow of the material under the working condition production condition of the simulated oil and gas field is developed, and the test method is explained to obtain the corrosion and wear rate, the morphological characteristics, the behaviors and the mechanism of the pipe and the coating sample under each simulated condition, so that the erosion corrosion experimental device has extremely important academic value and engineering significance for developing the corrosion-resistant and wear-resistant performance of the pipe and the coating in the severe stratum environment and the ground conveying environment of the oil and gas field and providing effective erosion corrosion control measures.

SUMMERY OF THE UTILITY MODEL

For solving the above-mentioned defect that exists in the current test evaluation method, the utility model aims to provide a multi-functional heterogeneous class of erosive wear erodees corrosion test device for develop under the simulation oil gas drilling, fracturing, the development production operating mode condition and simulate different sand content and compare, different velocity of flow, not pass through the research of pipe material, coating sample's erosive wear rate, topography feature and action, mechanism under the condition such as time, thereby for metal pipe material in the oil gas production process, the erosive wear control of equipment and the screening aassessment of corrosion-resistant wear-resisting coating layer provide important reference foundation.

The utility model discloses a realize through following technical scheme.

According to the embodiment of the utility model, a multi-functional corrosive wear multiphase flow erosion corrosion experimental device is provided, which comprises an experimental cavity, a supporting frame, a rotary sample disc, a solid-liquid waste tray, a motor, a testing system and a control system; the experimental cavity is connected to the support frame in a sliding manner, and the solid-liquid waste tray is arranged below the experimental cavity;

an experiment cavity cover is sealed on the experiment cavity, a rotating main shaft connected with a motor is connected on the experiment cavity cover, a rotating sample plate fixedly connected with a sample is connected with the rotating main shaft and extends into the experiment cavity, and a heating integrated block for controlling the temperature of a test medium of the experiment cavity is arranged in the rotating sample plate; the test system is arranged on the experiment cavity cover and communicated with the experiment cavity;

the control system is respectively connected with the test system, the motor and the heating integrated block, drives the motor to drive the rotary sample plate to rotate, and obtains the surface appearance of corrosion and erosive wear of the sample in the oil-gas corrosion test at the set temperature in the experimental cavity.

In the above scheme, experiment cavity covers and is equipped with the connecting rod, connecting rod top and support frame fixed connection, and rotatory main shaft is connected to the bottom, and rotatory sample dish is connected to rotatory main shaft and is located the experiment cavity.

In the scheme, a plurality of arc-shaped sample tray notches which are distributed at equal intervals are arranged on the periphery of the rotary sample tray, and a plurality of notches with adjacent angles of 15 degrees are arranged on the inner arc surface of each sample tray notch.

In the above scheme, the sample corresponding to the notch of the sample disc is embedded in the notch of the sample disc, the sample notch is cut on the sample, and the sample and the rotary sample disc are fixedly connected through the notch of the sample disc and the notch of the sample disc through keys.

In the scheme, the sample working surface is arranged on the side surface of the sample cylinder and is smoothly connected with the peripheral arc surface of the rotary sample disc.

In the above scheme, the experiment cavity is installed on the support frame and is connected to the support frame through the movable slide rail in a sliding manner.

In the above scheme, the experiment cavity includes experiment chamber shell, experiment intracavity lining body and experiment cavity lid, and experiment intracavity lining body inside lining PVD rigid plastic board inlays installs in experiment chamber shell, and experiment cavity lid is sealed on experiment intracavity lining body.

In the scheme, the lining body in the experimental cavity is provided with a sealing ring, a positioning groove and a handle; the edge of the experimental cavity cover is provided with a plurality of sealing buckles which are uniformly distributed and connected with the lining body in the experimental cavity.

In the scheme, the test system comprises an air valve, a thermocouple, a pressure gauge and an electrochemical test electrode, wherein the electrochemical test electrode is formed by integrating a solid Ag/AgCl reference electrode and a Pt wire auxiliary electrode, and is wrapped by a corrosion-resistant and wear-resistant sheath.

The utility model discloses owing to take above technical scheme, it has following beneficial effect:

1) the utility model discloses owing to adopted metal laboratory cave inside lining PVD stereoplasm plastic slab, solved the easy wearing and tearing problem and the good weak acid resistance or the nearly neutral oil gas production fluid medium characteristics that directly adopt the metal laboratory cave under the simulation contains silt particle condition, realized simultaneously that the laboratory cave inner lining body in case can low cost and convenient change by the wearing and tearing inefficacy situation down, ensured that it develops corrosion-resistant wear-resisting test safely for a long time.

2) The utility model discloses owing to adopted the design of the sample keyway mouth of the many angles that erode such as 0, 30, 45, 60, the fluid that has solved conventional corrosion test equipment strikes sample angle design problem, has realized can simulating the erosion corrosion test under the different pipeline elbow conditions in the oil gas production, ensures the scientific nature of anticorrosive wear-resisting research.

3) The utility model discloses owing to installed electrochemistry test system modular design additional, solved conventional heterogeneous stream erosion corrosion test equipment and only carried out the weightless method of more singleness and corrode the lacing film problem, realized carrying out the online normal position electrochemical corrosion action research of material under the simulation oil gas environment, provide the basic research data of fitting reality for the protection technology development of oil gas tubular product.

The utility model discloses can be applicable to simulation oil gas drilling, fracturing, the tubular column in the pit of development production, collection such as ground pipeline, flowback, the oil of carrying, gas, water, under the heterogeneous flow medium operating mode condition of solid particle, all kinds of metals, tubular product such as organic polymer and coating layer are anticorrosive under oil field high temperature high pressure, high corrosivity ionic medium, sand grain impurity erodees the condition, wear-resisting performance test and research, this method can accurately simulate different sand-containing ratio, different velocity of flow, tubular product under the condition such as not passing time, the corrosive wear rate of coating sample, the appearance characteristic, for tubular product under the heterogeneous flow medium condition, the corrosive wear rate of coating, appearance characteristic and action, the research of mechanism provides reliable data.

Drawings

The accompanying drawings, which are included to provide a further understanding of the invention and are incorporated in and constitute a part of this application, do not constitute a limitation of the invention, and in which:

FIG. 1 is a schematic view of the whole structure of a multi-functional corrosive wear multi-phase flow erosion corrosion experimental apparatus;

FIG. 2 is a schematic structural diagram of a multi-functional corrosive wear multi-phase flow erosion corrosion experimental apparatus;

FIG. 3 is a schematic structural view of an experimental chamber cover and a rotary sample tray;

FIG. 4 is a schematic view of the distribution of sample notches of an experimental rotating sample disk;

FIG. 5 is a schematic view of a sample slot structure of an experimental rotating sample disk;

FIG. 6 is a schematic view of a sample structure;

FIGS. 7(a) and 7(b) are graphs comparing the erosion and wear rates of the simulation experiments under the influence of different sand content ratios and flow rates, respectively.

In the figure: 1-support frame, 2-solid-liquid waste tray, 3-experiment cavity, 4-movable slide rail, 5-main connecting rod, 6-inner lining body of experiment cavity, 7-rotary sample tray, 8-experiment cavity cover, 9-sealing buckle, 10-sealing connecting piece, 11-air valve, 12-thermocouple, 13-pressure gauge, 14-electrochemical testing electrode, 15-sealing ring, 16-positioning groove, 17-handle, 18-rotary main shaft, 19-positioning key, 20-heating integrated block, 21-notch of sample tray, 22-notch of sample tray, and 23-sample.

Detailed Description

The invention will be described in detail with reference to the drawings and specific embodiments, wherein the exemplary embodiments and descriptions are provided to explain the invention, but not to limit the invention.

As shown in fig. 1 and 2, the overall structure schematic diagram of the multi-functional corrosive wear multiphase flow erosion corrosion experiment device comprises a support frame 1, an experiment cavity, a rotary sample disc 7, a sample 23, an electrochemical test electrode system 14, a solid-liquid waste tray 2 and a control system. Among them, the rotary sample disk 7, the sample 23, and the electrochemical test electrode 14 are key test components of the apparatus.

The experiment cavity 3 is arranged on the support frame 1, and different height positions fixed on the support frame 1 can be adjusted through the movable slide rail 4, so that the operation of installing and unloading samples before and after testing is facilitated; a solid-liquid waste tray 2 is arranged below the test cavity 3 and is used for discharging solid-liquid materials in the cavity after the test is finished and then entering a waste collecting barrel.

Wherein, experiment cavity 3 includes experiment chamber shell, experiment intracavity lining body 6 and experiment cavity lid 8, and experiment intracavity lining body 6 inlays the dress in experiment chamber shell, and experiment cavity lid 8 seals on experiment intracavity lining body 6. The experiment cavity shell is made of Q235 structural steel and plays a role in bearing force, and the inner diameter of the cavity shell is phi 55cm so as to guarantee the stability of a fluid flow pattern and reduce the turbulence phenomenon of the fluid. The experiment cavity inner lining body 6 is made of PVC hard plastic, the inner diameter of the experiment cavity inner lining body is phi 50cm, the experiment cavity inner lining body is embedded into the experiment cavity shell, abrasion and corrosion of solid media containing sand and stone to the inner wall surface of the cavity under different simulation experiment environments are reduced, and meanwhile, the inner lining body is easy to disassemble and replace, and is economical and practical. The lining body 6 in the experimental cavity is provided with a sealing ring 15, a positioning groove 16 and a handle 17, wherein the sealing ring is made of nitrile rubber; the experiment cavity cover 8 is made of corrosion-resistant alloy 316L stainless steel, so that the corrosion influence of the experiment medium on the inner wall of the cover is ensured.

As shown in fig. 3, eight sealing buckles 9 are installed at the edge of the experiment cavity cover 8, and are uniformly distributed, and are used for being connected with the experiment cavity lining body 6, sealing and maintaining the experiment pressure of the simulated environment in the experiment cavity.

As shown in fig. 2, an air valve 11, a thermocouple 12, a pressure gauge 13 and an electrochemical testing electrode 14 are respectively arranged on the experimental cavity cover 8; wherein, the gas valve 11 is used for meeting the requirements of different oil gas corrosion test conditions, and generally before the test, a corrosion-resistant metal conduit is required to be connected with a gas cylinder, and CO with a certain content is introduced₂、H₂S、O₂And after the test is finished, the pressure in the experimental cavity is discharged, and the sample is discharged after the cavity reaches the normal pressure. Wherein the electrochemical test electrode 14 is a solid Ag/AgCl reference electrodeThe Pt wire auxiliary electrode is formed by integration and is wrapped by the corrosion-resistant and wear-resistant sheath, a test section probe of the Pt wire auxiliary electrode is close to the surface of the sample by about 1-2 mm, and the electrochemical characteristics of the sample at different corrosion and wear stages can be tested on line in real time in situ. The intra-chamber medium is controlled by thermocouple 12 to simulate the designed test temperature.

As shown in fig. 1 and 2, a main connecting rod 5 is arranged on the experimental cavity cover 8, the bottom of the main connecting rod 5 is connected with a rotating main shaft 18, and the main connecting rod 5 connects the rotating main shaft 18 to the experimental cavity cover 8 through a sealing connector 10; the lower part of the rotating main shaft 18 is connected with a rotating sample disc 7, the rotating sample disc 7 is positioned in a cavity of an inner lining body 6 of an experiment cavity, and the top of the connecting main rod 5 is fixedly connected with the support frame main body 1.

As shown in fig. 3, the experiment cavity cover 8 is provided with a positioning key 19 for matching with the positioning groove 16 on the inner liner 6, so as to achieve the stability of the experiment cavity of the device. The rotary sample tray 7 is made of 316L stainless steel, three groups of heating integrated blocks 20 are uniformly distributed on the lower surface of the rotary sample tray 7, the heating integrated blocks 20 are connected with a control system, and the control system controls the heating integrated blocks 20 to control the temperature of a test medium to a test design temperature value.

As shown in fig. 4, four sample tray notches 21 are arranged on the periphery of the rotary sample tray 7 at equal intervals, the sample tray notches 21 are four symmetrical arc-shaped sample mounting holes, and a plurality of notches with adjacent angles of 15 ° are processed on the arc surface in each sample keyway, as shown in fig. 5, so as to meet the experimental requirements of simulated production conditions of different fluid impact angles.

The test sample tray notch 21 is a half notch cut on the rotary test sample tray 7 of the experimental device, the test sample 23 corresponding to the test sample tray notch 21 is embedded on the test sample tray notch 21, as shown in fig. 6, the test sample notch 22 is cut on the test sample 23, and the test sample notch 22 and the test sample tray notch 21 connect and fix the test sample 23 and the rotary test sample tray 7 through keys, so that the test sample cannot deflect at angles when subjected to erosion actions at different angles, and the multi-angle erosion corrosion test for simulating production elbow pipelines such as 0 degrees, 30 degrees, 45 degrees, 60 degrees and the like is realized.

The sample used in the erosive corrosion wear device is made of metal or coating material used in an oil-gas field, a sample working surface is further arranged on the side surface of a sample cylinder, a plane is milled on one side of a cylinder with the diameter of phi 20mm to serve as the sample working surface for erosive corrosion research, and the rotation of the sample is realized by a driving motor connected with a rotating main shaft 18.

The sample is treated by adopting the wear-resistant and corrosion-resistant polymeric ceramic material coating except the working surface, so that the influence of the corrosion and wear on the rest surfaces on the accuracy of researching the corrosion and wear rate is prevented.

Software control system mainly does not reflect in the utility model discloses in the legend, the control module is loaded in the computer that experimental apparatus is connected, links to each other with it through the transmission line. The method mainly comprises the steps of controlling and recording working pressure, medium temperature, medium sand content ratio, sample rotating speed, test time and the like in an experimental cavity.

The utility model discloses give below to the implementation process of the heterogeneous flow erosion corrosion experiment of erosive wear:

firstly, the experiment cavity shell 3 slides downwards along the support frame 1 to a certain position by moving the slide rail 4, and the processed four samples are fixedly connected with the sample notch 22 by keys according to a certain designed scouring angle, such as 0 degree, 30 degrees, 45 degrees, 60 degrees and the like; the sample 23 is fixed on the rotating sample plate 7.

After cleaning the lining body 6 in the experimental cavity, adding a solid-liquid medium with a certain sand content ratio into the lining body according to a designed amount, then placing the readjusting movable slide rail 4, and sealing the experimental cavity cover 8 through the sealing buckle 9.

Secondly, N is added₂The gas cylinder is communicated with a gas valve 11 on an experimental cavity cover 8, the closing state of the valve of the device is checked, and N is opened₂The gas cylinder pressure reducing valve is used for checking whether the installed experimental cavity has good air tightness or not and displacing air in the cavity; then according to the requirements of different oil gas corrosion test conditions, introducing CO with designed content through the gas cylinder₂、H₂S、O₂A small amount of corrosive gas is added, and N is introduced₂The total pressure requirement of the design simulation experiment is met, the working pressure of the experiment cavity is designed to be 1MPa, and the working temperature is designedAt 90 ℃, all valves were closed.

And thirdly, opening a software control system of the operating platform, inputting designed parameters such as experiment temperature values, sample rotating speed, test time and the like, starting a heating control key after setting, starting a driving motor after reaching a temperature design value, and ensuring that the sample operates at a determined rotating speed.

And finally, after the experiment is finished, closing the heating system, and after the experiment is naturally cooled for 1-2 hours, opening the air valve 11 to slowly discharge the gas in the experiment cavity into the tail gas absorption tank through the guide pipe. And opening the experimental cavity cover 8 to take out the four samples, immediately treating the samples to prevent the influence of secondary corrosion caused by exposed atmosphere, and then carrying out the analysis of the corrosive wear data and the standard analysis of the surface morphology. The solid-liquid medium in the experimental cavity is opened through a material port valve at the bottom of the experimental cavity and flows through the solid-liquid waste tray 2 to enter the waste collecting barrel.

The effect of the experimental method of the present invention is further illustrated by an example.

Taking the production conditions of oil pipelines on the surface of a certain oil field as an example, the materials of the samples are 20# and 3Cr steel grades, and the materials of 'water (after precipitation) produced by the certain oil field plus different amounts of fine sand and stones (with the particle size of 0.05-0.25 mm)' are used as experimental solid-liquid media. Experimental conditions for the effect of the first sand ratio: introducing CO into the experimental cavity₂Gas 0.05MPa, then N is introduced₂The total pressure in the cavity is 0.5MPa by gas, the cavity is heated to the experimental design temperature of 28 ℃, the rotating speed is 0.1m/s, the test period is 48h, and the sand content ratio is 0, 1:50 and 1:20 respectively. Second set of speed-influencing experimental conditions: introducing CO into the experimental cavity₂Gas 0.05MPa, then N is introduced₂The total pressure in the cavity is 0.5MPa by gas, the cavity is heated to the experimental design temperature of 28 ℃, the sand content ratio is 1:50, the test period is 48h, and the rotating speed is 0, 0.1m/s and 0.5m/s respectively. After the experiment, the corrosive wear rates of the 20# and 3Cr steel specimens under the two sets of simulated experimental conditions were calculated, as shown in FIGS. 7(a) and (b).

The experimental results of the above examples show that: in a first group of experiments influenced by the sand content ratio, the corrosion wear rates of two types of ground pipeline steel are increased along with the increase of the sand content ratio, and the increase is particularly obvious when the sand content ratio is 1: 20; in the second group of rotating speed influence experiments, the corrosive wear rates of the two types of ground pipeline steel are increased along with the increase of the rotating speed, and the corrosive wear rate at 0.5/m/s is greatly increased compared with that at 0.1m/s, which can show that when the corrosive wear of the samples by the fine sand and stone is synergistic, the wear effect of the solid-liquid medium is dominant when the samples reach a certain flow speed. Further studies can be characterized and analyzed by the erosive wear topography of the sample working face.

It can be seen from the above embodiment that the utility model discloses corrosive stratum aqueous medium environment that contains certain gravel and sand, stratum impurity down all kinds of tubular products corrosion-resistant wear resistance's basic research has important effect to in the oil gas.

The present invention is not limited to the above embodiments, and based on the technical solutions disclosed in the present invention, those skilled in the art can make some replacements and transformations for some technical features without creative labor according to the disclosed technical contents, and these replacements and transformations are all within the protection scope of the present invention.

Claims (9)

1. A multifunctional corrosive wear multiphase flow erosion corrosion experimental device is characterized by comprising an experimental cavity (3), a support frame (1), a rotary sample disc (7), a solid-liquid waste tray (2), a motor, a test system and a control system; the experimental cavity (3) is connected to the support frame (1) in a sliding manner, and the solid-liquid waste tray (2) is arranged below the experimental cavity (3);

an experiment cavity cover (8) is sealed on the experiment cavity (3), a rotating main shaft (18) connected with a motor is connected on the experiment cavity cover (8), a rotating sample plate (7) fixedly connected with a sample (23) through the rotating main shaft (18) extends into the experiment cavity (3), and a heating integrated block (20) for controlling the temperature of an experiment cavity testing medium is arranged in the rotating sample plate (7); the test system is arranged on the experiment cavity cover (8) and is communicated with the experiment cavity (3);

the control system is respectively connected with the test system, the motor and the heating integrated block (20), drives the motor to drive the rotating sample disc (7) to rotate, and obtains the surface appearance of corrosion and erosion wear of the sample (23) in the oil gas corrosion test at the set temperature in the experiment cavity (3).

2. The multifunctional multiphase flow erosive corrosion experimental device for corrosive wear according to claim 1, characterized in that a main connecting rod (5) is arranged on the experimental cavity cover (8), the top of the main connecting rod (5) is fixedly connected with the support frame (1), the bottom of the main connecting rod is connected with a rotating spindle (18), and the rotating spindle (18) is connected with a rotating sample plate (7) and is located in the experimental cavity (3).

3. The multi-functional erosive wear multiphase flow erosive corrosion experimental device according to claim 1, characterized in that a plurality of arc-shaped sample disk notches (21) are arranged on the outer periphery of the rotary sample disk (7) at equal intervals, and a plurality of notches with adjacent angles of 15 ° are arranged on the inner arc surface of each sample disk notch.

4. The multifunctional corrosive wear multiphase flow erosive corrosion experimental device according to claim 3, characterized in that a sample (23) corresponding to the sample plate notch (21) is embedded in the sample plate notch (21), a sample notch (22) is cut in the sample (23), and the sample notch (22) and the sample plate notch (21) fixedly connect the sample and the rotary sample plate (7) through a key.

5. The multi-functional erosive wear multiphase flow erosive corrosion experimental device according to claim 1, characterized in that a sample working surface is arranged on the side surface of the sample cylinder, and the sample working surface is smoothly connected with the outer circumference arc surface of the rotary sample disc (7).

6. The multifunctional erosive wear multiphase flow erosive corrosion experimental device according to claim 1, characterized in that the experimental cavity (3) is mounted on the support frame (1) and is slidably connected to the support frame (1) through a movable slide rail (4).

7. The multi-functional multiphase flow erosive corrosion experimental device for corrosive wear according to claim 1, characterized in that the experimental cavity (3) comprises an experimental cavity housing, an experimental cavity lining body (6) and an experimental cavity cover (8), wherein the experimental cavity lining body (6) is lined with a PVD rigid plastic plate and is embedded in the experimental cavity housing, and the experimental cavity cover (8) is sealed on the experimental cavity lining body (6).

8. The multifunctional erosive wear multiphase flow erosive corrosion experimental device according to claim 7, characterized in that the lining body (6) in the experimental cavity is provided with a sealing ring (15), a positioning groove (16) and a handle (17); a plurality of sealing buckles (9) which are uniformly distributed are arranged on the edge of the experiment cavity cover (8) and are connected with the experiment cavity lining body (6).

9. The multi-functional corrosive wear multiphase flow erosion corrosion experimental device according to claim 1, wherein the testing system comprises a gas valve (11), a thermocouple (12), a pressure gauge (13) and an electrochemical testing electrode (14), the electrochemical testing electrode (14) is formed by integrating a solid Ag/AgCl reference electrode and a Pt wire auxiliary electrode, and the electrochemical testing electrode (14) is wrapped by a corrosion-resistant and wear-resistant sheath.