CN215040939U - Composite carbon cloth - Google Patents
Composite carbon cloth Download PDFInfo
- Publication number
- CN215040939U CN215040939U CN202121688908.8U CN202121688908U CN215040939U CN 215040939 U CN215040939 U CN 215040939U CN 202121688908 U CN202121688908 U CN 202121688908U CN 215040939 U CN215040939 U CN 215040939U
- Authority
- CN
- China
- Prior art keywords
- layer
- carbon cloth
- cloth
- composite carbon
- tear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a composite carbon cloth, including the carbon fiber cloth main part, the carbon fiber cloth main part comprises fibrous layer and stand wear and tear layer, the fibrous layer with through making up mode fixed connection between the stand wear and tear layer, the fibrous layer is by outer to interior weaving layer, wire layer and the insulating layer of including in proper order, the weaving layer adopt the mode of longitude and latitude establishment with the wire layer is connected, the surface on stand wear and tear layer is provided with a plurality of bleeder vents. The utility model relates to a compound carbon cloth makes compound carbon cloth have stronger tensile properties through setting up the wire layer, can avoid compound carbon cloth to take place to warp.
Description
Technical Field
The utility model relates to a carbon cloth field, specific is a compound carbon cloth.
Background
The carbon fiber cloth has the characteristics of high strength, small density, thin thickness and the like, and the dead weight, the section size and the like of the reinforcing member are not basically increased, so the carbon fiber cloth is widely applied to the tensile, shear and seismic reinforcement of structural members at present. The reinforcement principle is that high-performance carbon fiber matched resin is used for impregnating and gluing the carbon fiber matched resin on the surface of the concrete member, and the purpose of enhancing the bearing capacity and strength of the member is achieved by utilizing the good tensile strength of the carbon fiber material. However, the existing carbon fiber cloth is easy to separate from sports equipment such as a badminton racket, and is easy to deform.
SUMMERY OF THE UTILITY MODEL
The weak point to existence among the above-mentioned technique, the utility model provides a compound carbon cloth has stronger stretch-proofing ability, can avoid compound carbon cloth to take place to warp.
In order to achieve the above purpose, the utility model adopts the following technical scheme: the utility model provides a composite carbon cloth, includes the carbon fiber cloth main part, the carbon fiber cloth main part comprises fibrous layer and stand wear and tear layer, the fibrous layer with through making up mode fixed connection between the stand wear and tear layer, the fibrous layer is by outer to interior weaving layer, wire layer and the insulating layer of including in proper order, the weaving layer adopt the mode of longitude and latitude establishment with the wire layer is connected, the surface on stand wear and tear layer is provided with a plurality of bleeder vents.
As a further elaboration, the woven layer is made of a nanofiber material.
As a further illustration, the metal wire layer is made of fine copper wires, and the thickness of the metal wire layer is 0.1mm-0.2 mm.
As a further illustration, the insulating layer is made of a polyurethane material, and the thickness of the insulating layer is 0.2mm-0.4 mm.
By way of further illustration, the abrasion-resistant layer is made of a thermoplastic resin material.
To sum up, the utility model discloses following beneficial effect has: the utility model relates to a compound carbon cloth makes compound carbon cloth have stronger tensile property through setting up the wire layer, can avoid compound carbon cloth to take place to warp, makes compound carbon cloth have stronger stand wear and tear performance through setting up stand wear layer, can improve compound carbon cloth's stand wear and tear ability, improves compound carbon cloth's life.
Drawings
Fig. 1 is a schematic view of the overall structure of a composite carbon cloth according to the present invention;
FIG. 2 is a schematic structural view of the fiber layer of the present invention;
fig. 3 is a top view of the composite carbon cloth of the present invention.
Reference numbers in the figures:
FIG. 1-wear resistant layer; 2-a fibre layer; 3-a carbon fiber cloth main body; 4-weaving layer; 5-a layer of wire strands; 6-an insulating layer; 7-air holes.
Detailed Description
The technical solutions in the embodiments of the present invention will be described clearly and completely with reference to the accompanying drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only some embodiments of the present invention, not all embodiments. Based on the embodiments in the present invention, all other embodiments obtained by a person skilled in the art without creative work belong to the protection scope of the present invention.
The first embodiment is as follows: as shown in the following fig. 1-3, a composite carbon cloth, includes carbon fiber cloth main part 3, carbon fiber cloth main part 3 comprises fibrous layer 2 and wear-resistant layer 1, fibrous layer 2 with through making up mode fixed connection between the wear-resistant layer 1, fibrous layer 2 includes weaving layer 4, wire layer 5 and insulating layer 6 in proper order by outer to interior, weaving layer 4 adopt the mode of longitude and latitude establishment with wire layer 5 connects, wear-resistant layer 1's surface is provided with a plurality of bleeder vents 7, weaving layer 4 is made for nanofiber material, wire layer 5 is made for the thin copper wire, wire layer 5's thickness is 0.1mm, insulating layer 6 is made for the polyurethane material, insulating layer 6's thickness is 0.2mm, wear-resistant layer 1 is made for the thermoplastic resin material.
Example two: as shown in the following fig. 1-3, a composite carbon cloth, includes carbon fiber cloth main part 3, carbon fiber cloth main part 3 comprises fibrous layer 2 and wear-resistant layer 1, fibrous layer 2 with through making up mode fixed connection between the wear-resistant layer 1, fibrous layer 2 includes weaving layer 4, wire layer 5 and insulating layer 6 in proper order by outer to interior, weaving layer 4 adopt the mode of longitude and latitude establishment with wire layer 5 connects, wear-resistant layer 1's surface is provided with a plurality of bleeder vents 7, weaving layer 4 is made for nanofiber material, wire layer 5 is made for the thin copper wire, wire layer 5's thickness is 0.2mm, insulating layer 6 is made for the polyurethane material, insulating layer 6's thickness is 0.4mm, wear-resistant layer 1 is made for the thermoplastic resin material.
A method of making a composite carbon cloth comprising: firstly, uniformly coating the single surface of a wear-resistant layer 1, combining a coating surface with the smooth surface of a fiber layer 2 during winding to form two rolls, then placing the wear-resistant layer 1 with glue on an upper layer cloth placing frame, placing a shaped fiber layer 2 on a middle layer cloth placing frame, simultaneously pressing the fiber layer 2 and the wear-resistant layer 1 through two groups of hot press rollers, heating the hot press rollers to 180 ℃, adjusting the pressure of two groups of hot press roller cylinders, pressing the fiber layer 2 and the wear-resistant layer 1 into an integrated structure, and connecting the cooled composite cloth to a winding table through an air cooler to form the composite carbon cloth.
It is obvious to a person skilled in the art that the invention is not restricted to details of the above-described exemplary embodiments, but that it can be implemented in other specific forms without departing from the spirit or essential characteristics of the invention. The present embodiments are therefore to be considered in all respects as illustrative and not restrictive, the scope of the invention being indicated by the appended claims rather than by the foregoing description, and all changes which come within the meaning and range of equivalency of the claims are therefore intended to be embraced therein. Any reference sign in a claim should not be construed as limiting the claim concerned.
Furthermore, it should be understood that although the present description refers to embodiments, not every embodiment may contain only a single embodiment, and such description is for clarity only, and those skilled in the art should integrate the description, and the embodiments may be combined as appropriate to form other embodiments understood by those skilled in the art.
Claims (5)
1. A composite carbon cloth is characterized in that: including the carbon fiber cloth main part, the carbon fiber cloth main part comprises fibrous layer and stand wear and tear layer, the fibrous layer with through making mode fixed connection between the stand wear and tear layer, the fibrous layer is by outer to interior weaving layer, wire layer and the insulating layer of including in proper order, the weaving layer adopt the mode of longitude and latitude establishment with the wire layer is connected, the surface on stand wear and tear layer is provided with a plurality of bleeder vents.
2. The composite carbon cloth of claim 1, wherein: the woven layer is made of nanofiber materials.
3. The composite carbon cloth of claim 1, wherein: the metal wire layer is made of fine copper wires, and the thickness of the metal wire layer is 0.1mm-0.2 mm.
4. The composite carbon cloth of claim 1, wherein: the insulating layer is made of polyurethane materials, and the thickness of the insulating layer is 0.2mm-0.4 mm.
5. The composite carbon cloth of claim 1, wherein: the abrasion-resistant layer is made of a thermoplastic resin material.