CN2143246Y - Decorative construction material of composite glass - Google Patents

Abstract

The utility model relates to a decorative composite glass tile for buildings, composed of a carrier layer 1 and a composite layer 2, wherein, the carrier layer is foam glass easy for paste, and the composite layer is beautiful glass or colored glass. The utility model which has the advantages of simple structure, easy paste, strong shock resistance and shapely configuration is especially suitable for various high-grade building decoration.

Description

Decorative construction material of composite glass

The utility model is a kind of building and ornament materials, particularly a kind of compound glass wall tile and floor brick.

Being used to the glass decoration material built in the market, all is monochromatic generally, not attractive in appearance, and because surface of ordinary glass is closely knit smooth, does not absorb water, and surperficial adsorption capacity is less, is difficult to bonding with the common building bonding agent.Therefore be used for the architectural decoration glass of bulk slightly, generally all be around this glass, inlay with other materials fixing, fritter resemble glass Mosaic, though can with cement add glue around inlay fixingly, often as seen it peels off vestige on building.Around fixedly the incrusted glass ornament is not owing to organically form an integral body with the matrix material of decorated thing (as wall etc.) with other materials, thereby impact resistance is poor, fragmentation easily.

The purpose of this utility model provides a kind of both bright and colourful, is convenient to again paste the compound glass wall tile and floor brick of strong shock resistance.

The utility model compound glass wall tile and floor brick is to be made of carrier layer and composite bed; 1. carrier is a kind of porous foam glass, and it is to add blowing agent and form in simple glass.2. composite bed is clear glass, colored glass, emulsion opal glass or aventurine glass.Take advantage of the glass of carrier compound last layer, two layers or multilayer other colors and purposes under the red heat state in process of production.

The compound glass wall tile and floor brick, because carrier is a porous foam glass, thereby solved the water imbibition problem of glass, increased surperficial adsorption capacity, can in the architectural decoration process, paste with common bonding agent, can form an organic whole with the matrix of decorated thing (as wall etc.), thereby improve impact resistance.Because composite bed is multiple stained glass, thereby it is bright and colourful.This ornament materials is owing to be the one deck very thin carrier glass is compound or the glass of other colors of multilayer.Thereby compare with the ceramic ornament materials, also have lightweight advantage; Though this ornament materials impact resistance, fold resistance be not as organic ornament materials (as Baoli polywood laminate, plastics etc.), its case hardness height, abrasion-resistance be strong, be difficult for wearing out, not burning, be not afraid of humidity.Directly water flushing, thereby be specially adapted to the senior building decoration.

Description of drawings of the present utility model is as follows:

Fig. 1 is a structural representation of the present utility model.

Among the figure: 1 carrier layer, 2 composite beds.

The utility model will be further described below in conjunction with drawings and Examples:

As shown in Figure 1: the utility model is to be composited by carrier layer 1 and composite bed 2, and wherein carrier layer is a foam glass, and composite bed is a glass, and composite bed can include stained glass layer and transparent glass layer.

The technological forming method of realizing the utility model compound glass wall tile and floor brick is as follows:

1. found glass with the simple glass kiln, the molten good glass as carrier is guided on the former by a longer supply channel as carrier.Agitator is installed on supply channel, before agitator, adds the glass blowing agent, glass is made the uniform foam glass of pore.

2, carrier glass is passed through carrier glass is squeezed into the carrier of desired thickness and width between the running roller of similar glass Mosaic forming machine equipment.

3. in the back upper place of former first road calendering running roller one or more vitreous electricity firing equipments (deciding according to the compound number of plies) are arranged.Vitreous electricity firing equipment bottom is the long and narrow seam of an adjustable width, and the required compound glass that gets on flows out from long and narrow seam, takes advantage of the glass of the carrier glass that comes out after the extruding compound last layer or multilayer required color under the red heat state.Join in the electric heating equipment after the glass of required color melts well by other glass melting equipment 8 and go.

4. compound good glass is taken advantage of the red heat state and is entered the second road running roller, and compacting cuts into the product of difformity and specification as required.

Well cutting product enter annealing furnace annealing, the reheating insulation crystallization of aventurine glass goods annealing back at once.

6. wash open with will the anneal sealed porosity of carrier glass of good product of sandblast technology, the concavo-convex hair side that this also increases carrier surface simultaneously increases surperficial adsorptivity.

According to purposes, require corner around the product is ground smooth, be finished product.

Claims (2)

1, a kind of compound glass wall tile and floor brick is characterized in that: it is to be composited by carrier layer 1 and composite bed 2, and wherein carrier layer is a foam glass, and composite bed is a glass.

2, compound glass wall tile and floor brick as claimed in claim 1, it is characterized in that: composite bed includes stained glass layer and transparent glass layer.