CN213266860U - Cellulose fiber yarn, and fabric and product thereof - Google Patents
Cellulose fiber yarn, and fabric and product thereof Download PDFInfo
- Publication number
- CN213266860U CN213266860U CN202020986868.4U CN202020986868U CN213266860U CN 213266860 U CN213266860 U CN 213266860U CN 202020986868 U CN202020986868 U CN 202020986868U CN 213266860 U CN213266860 U CN 213266860U
- Authority
- CN
- China
- Prior art keywords
- cellulose fiber
- yarn
- cellulose
- fiber yarn
- hard
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model belongs to the technical field of the technique of yarn and specifically relates to a cellulose fiber yarn and surface fabric and goods thereof are related to, and the cellulose fiber yarn includes cellulose base fibre and stereoplasm filament, and the even parcel of cellulose base fibre forms the surrounding layer at the stereoplasm filament skin, and the thickness of stereoplasm filament is 50D ~ 600D, and the thickness of cellulose base fibre is 0.5D ~ 5.0D, and the weight of cellulose base fibre is more than 20% and 20% of the weight of cellulose fiber yarn. The fabric is formed by weaving the cellulose fiber yarns, and the product is formed by weaving the cellulose fiber yarns. The novel cellulose fiber yarn is formed by selecting the thicker hard filament and the thinner cellulose fiber, so that the yarn can not only ensure the texture of the cellulose fiber, but also improve the overall wear-resisting and durable performance of the yarn. The knitted glove also has the advantages of cellulose fiber texture and wear resistance and durability.
Description
Technical Field
The utility model belongs to the technical field of the technique of yarn and specifically relates to a cellulose fiber yarn and surface fabric and goods thereof.
Background
The labor protection gloves are important protection articles for workers during labor, and the cotton gloves are one of common gloves in the labor protection gloves. The knitting yarn of the cotton gloves is common cotton yarn.
The Chinese utility model with the publication number of CN210158069U discloses an abrasion-resistant cotton glove, which comprises a glove body, wherein five finger openings are uniformly formed in the left side of the outer surface of the glove body, a first latex layer is coated on the upper side of the outer surface of the glove body to improve the abrasion resistance of the glove, and a second latex layer is coated on the finger sleeves to improve the abrasion resistance of the finger sleeves; the glove is woven by cotton cloth.
However, the cotton gloves have the following defects in practical use: firstly, the gloves are easy to harden and have low softness after gum dipping, secondly, because the other sides of the gloves have no glue layers, in some special industries, such as express service industry, moving service industry, agricultural work and construction site work which need heavy carrying, the single-side damage rate of the cotton gloves is high, and workers usually need to replace one or two gloves one day.
In view of the above, it is desirable to provide a yarn and a glove that can improve abrasion resistance and durability without changing the softness of the yarn.
SUMMERY OF THE UTILITY MODEL
In view of the deficiencies of the prior art, it is an object of the present invention to provide a cellulose fiber yarn.
The above utility model discloses an above-mentioned utility model purpose can realize through following technical scheme: the cellulose fiber yarn comprises cellulose fibers and hard filaments, wherein the cellulose fibers are uniformly wrapped on the outer layer of the hard filaments to form an outer wrapping layer, the thickness range of the hard filaments is 50D-600D, and the thickness range of the cellulose fibers is 0.5D-5.0D.
By adopting the technical scheme, the novel cellulose fiber yarn is formed by selecting the thicker hard filament and the thinner cellulose fiber, so that the yarn can ensure the natural, comfortable and soft texture of the plant fiber, and can improve the integral wear-resisting and durable performance of the yarn by utilizing the high-modulus performance of the plant fiber. Therefore, the knitted gloves also have the advantages of soft texture and wear resistance and durability.
The present invention may be further configured in a preferred embodiment as: the weight of the cellulose fiber is 20 percent and more than 20 percent of the weight of the cellulose fiber yarn.
The present invention may be further configured in a preferred embodiment as: the weight of the cellulose fiber is 20-80% of that of the cellulose fiber yarn, and the weight of the hard filament is 20-80% of that of the cellulose fiber yarn.
By adopting the technical scheme, the thickness selection can be confirmed through the weight ratio. The cellulose fiber yarn of the scheme preferably comprises 20-80% of the whole weight of the cellulose fiber, and the hard filament is 20-80% of the whole weight. The design is different from the cotton weight of common cotton threads. Such a ratio configuration can meet the requirements of softness and wear resistance.
The present invention may be further configured in a preferred embodiment as: the hard filaments comprise one or more of polyethylene, aramid 1414, terylene or nylon.
By adopting the technical scheme, the polyethylene as the hard filament has good wear resistance; the aramid fiber 1414 as a hard filament has high elongation, soft hand feeling and high strength; the terylene used as the hard filament has good wear resistance, high strength and toughness and good elasticity; the nylon as hard filament has good strength and fatigue resistance.
The present invention may be further configured in a preferred embodiment as: the connection form of the cellulose fibers and the hard filaments is that the cellulose fibers are distributed around the hard filaments in an agglomeration manner.
By adopting the technical scheme, the cellulose fibers and the hard filaments can be woven together by a double-twisting or cladding process to form a corresponding winding structure, so that the fastened cellulose fiber yarn is formed.
The present invention may be further configured in a preferred embodiment as: the twist of the cellulose fiber and the hard filament is 20-90 twist/10 cm.
Through adopting above-mentioned technical scheme, the twist of cellulose fibre and hard filament is high for ordinary cellulose fibre twist, and the degree of twining is high, and the exposed cellulose fibre is many in the unit length, and then the sense of touch of cellulose fibre yarn is good.
The second purpose of the utility model is to provide a fabric.
The above utility model discloses an above-mentioned utility model purpose can realize through following technical scheme: the fabric is woven by the cellulose fiber yarns.
By adopting the technical scheme, the fabric with soft texture, wear resistance and durability can be provided.
The third purpose of the utility model is to provide a product.
The above utility model discloses an above-mentioned utility model purpose can realize through following technical scheme: the product is woven by the cellulose fiber yarn.
By adopting the technical scheme, the product with soft texture, wear resistance and durability can be provided.
The present invention may be further configured in a preferred embodiment as: the article comprises a glove, cuff or protective garment.
By adopting the technical scheme, the special gloves, the special sleeves and the special protective clothes can have soft feeling of cotton and wear-resisting and durable performances.
To sum up, the utility model discloses a following at least one useful technological effect:
1. by selecting the thickness of the cellulose fiber and the hard filament, a brand new cellulose fiber yarn which has soft comfort and wear resistance and durability is provided;
2. through the selection of hard filament materials, the effect of yarn performance diversification is achieved, and different customer requirements can be met;
3. the cellulose fiber yarns are woven into fabrics, gloves, oversleeves, protective clothing and the like, so that the cellulose fiber yarns can be applied to special industries in a matching way, and related protective articles which have soft texture and wear resistance and durability are provided for the work of the special industries.
Drawings
FIG. 1 is a schematic structural view of example 1.
FIG. 2 is a schematic structural view of example 2.
FIG. 3 is a schematic structural view of example 3.
FIG. 4 is a schematic structural view of example 4.
In the figure, 1, cellulose fiber yarn; 2. cellulose fibers; 3. hard filaments; 4. fabric; 5. an article of manufacture; 6. cotton staple fibers; 7. and (4) a groove.
Detailed Description
The present invention will be described in further detail with reference to the accompanying drawings.
Example 1:
referring to fig. 1, a cellulose fiber yarn 1 disclosed in this embodiment includes cellulose fibers 2 and hard filaments 3, which are twisted together by a two-for-one twisting or coating process.
The hard filaments 3 may be of a thick variety, for example, the hard filaments 3 have a thickness in the range of 50D to 600D, and the cellulose fibers 2 may be of a thin variety, for example, the cellulose fibers 2 have a thickness in the range of 0.5D to 5.0D. Generally, the weight of the cellulose fiber 2 is 20% or more and 20% or more of the weight of the cellulose fiber yarn 1. Preferably, the weight of the cellulose fiber 2 should be 20% to 80% of the yarn, and the weight of the hard filament 3 should be 20% to 80% of the yarn. Thus, the cellulose fiber yarn 1 has high abrasion resistance and durability, and the outer layer can have a soft feeling of the plant fiber due to the cellulose fiber 2. Wherein, the hard filaments 3 can comprise one or more of polyethylene, aramid, terylene or nylon. The cellulose fibers 2 may be selected from short cotton fibers.
The implementation principle of the embodiment is as follows: the thickness of the hard filaments 3 and the cellulose fibers 2 is preferably selected to be controlled to be about 3-4: 6-7, the hard filaments 3 are heavier. If the hard filaments 3 are thin and thick, the weight ratio can be satisfied by increasing the number of the hard filaments 3. Finally, the cellulose fiber yarn 1 is formed through a double twisting or cladding process.
Example 2
Referring to fig. 2, the difference from embodiment 1 is that: the outer surface of the hard filament 3 is provided with cotton short fibers 6, the outer surface of the hard filament 3 is provided with a plurality of strip-shaped grooves 7, and part of the cotton short fibers 6 are embedded in the grooves 7.
The principle of the embodiment of the present embodiment is as follows: the hard filaments 3 are sequentially conveyed into a die with a plurality of strip-shaped pressing strips for punching to form a plurality of strip-shaped grooves 7, then the hard filaments 3 are conveyed into a glue box with glue, and are output and then enter a pile of cotton short fibers 6 in a subsection mode to bond the cotton short fibers 6. And shaking off the redundant cotton short fibers 6 after the bonding is finished. Cotton staple fibers 6 adhere to the surface of the hard filaments 3 and to the grooves 7. The dried hard filaments 3 and cellulose fibers 2 are processed into a cellulose fiber yarn 1.
Such exposed hard filaments 3 may also provide a soft hand to the cellulosic fiber yarn 1. The cotton short fibers 6 embedded in the groove 7 are not easy to be scratched and fall off because of being positioned in the canyon. The thickness of the short cotton fiber 6 is 0.5D-1D, and the length is 2-5 mm.
Example 3:
referring to fig. 3, in the fabric disclosed in this embodiment, the fabric 4 is woven by the cellulose fiber yarn 1.
The implementation principle of the embodiment is as follows: the cellulose fiber yarn 1 of example 1 was knitted alone or mixed with other yarns to form a new cotton fabric 4. The cotton fabric 4 has the advantages of good softness, wear resistance and durability.
Example 4:
referring to fig. 4, a product 5 is disclosed in this embodiment, and is woven from the cellulose fiber yarn 1. The article 5 may in particular comprise a glove, a cuff or a protective garment or the like.
The implementation principle of the embodiment is as follows: the cellulosic fiber yarn 1 of example 1 is knitted alone or in combination with other yarns to form a new glove, cuff or protective garment.
In some special industries, such as express service industry, moving service industry, agricultural work and construction site work which need to be carried again, the use time can be effectively prolonged by using the protective gloves, and the problem of high daily wear rate is solved.
The embodiment of this specific implementation mode is the preferred embodiment of the present invention, not limit according to this the utility model discloses a protection scope, so: all equivalent changes made according to the structure, shape and principle of the utility model are covered within the protection scope of the utility model.
Claims (7)
1. A cellulosic fiber yarn characterized by: the cellulose fiber yarn (1) comprises cellulose fibers (2) and hard filaments (3), the cellulose fibers are uniformly wrapped on the outer layers of the hard filaments to form outer wrapping layers, the thickness range of the hard filaments (3) is 50D-600D, and the thickness range of the cellulose fibers (2) is 0.5D-5.0D.
2. The cellulosic fiber yarn of claim 1, wherein: the hard filaments (3) are made of one of polyethylene, aramid 1414, polyester or nylon.
3. The cellulosic fiber yarn of claim 1, wherein: the connection form of the cellulose fibers (2) and the hard filaments (3) is that the cellulose fibers (2) are conglomerated and distributed around the hard filaments (3).
4. The cellulosic fiber yarn of claim 1, wherein: the twist of the cellulose fiber (2) and the hard filament (3) is 20-90 twist/10 cm.
5. A fabric is characterized in that: the fabric (4) is woven from the cellulosic fibre yarn (1) according to any one of claims 1 to 4.
6. An article characterized by: the article (5) is woven from the cellulosic fibre yarn (1) according to any one of claims 1 to 4.
7. An article according to claim 6, wherein: the article (5) comprises a glove, a cuff or a protective garment.