CN212316007U - Printing-free warning adhesive tape - Google Patents
Printing-free warning adhesive tape Download PDFInfo
- Publication number
- CN212316007U CN212316007U CN202021305254.1U CN202021305254U CN212316007U CN 212316007 U CN212316007 U CN 212316007U CN 202021305254 U CN202021305254 U CN 202021305254U CN 212316007 U CN212316007 U CN 212316007U
- Authority
- CN
- China
- Prior art keywords
- warning
- yarn group
- free
- yarns
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses an exempt from to print warning sticky tape, wherein the sticky tape includes adhesive layer, gauze layer, thin layer in proper order and leaves the type layer, the gauze layer includes first warning yarn group and the second warning yarn group of cross arrangement, first warning yarn group and second warning yarn group comprise a plurality of warning yarns respectively. The utility model provides a printing-free warning sticky tape is implemented conveniently, and laminating is respond well in outdoor application and simulation test, and the weatherability is better, and production process does not have VOC and volatilizes almost, tears the terminal surface and levels and need not to cut with the stage property, and product tensile strength is higher, has the intensity of ordinary cloth base sticky tape, possesses the weatherability of oily acrylic acid glue, possesses the warning effect of printing cloth base. The volatilization of organic gas in the whole production process is close to zero.
Description
Technical Field
The utility model relates to an adhesive technical field especially relates to a printing-free warning sticky tape.
Background
The warning tape has the advantages of water resistance, moisture resistance, weather resistance, corrosion resistance, static electricity resistance and the like, and is suitable for the corrosion protection of underground pipelines such as air pipes, water pipes, oil pipelines and the like. The twill printing adhesive tape can be used for warning signs in areas such as ground, columns, buildings, traffic and the like. When the warning lamp is used for warning, red indicates the prohibition and prevention, the red and white alternate stripes indicate the prohibition of people from entering dangerous environments, the yellow and black alternate stripes indicate the attention of people, and the green and white alternate stripes indicate the more striking prompt of people.
Most of the warning tapes commonly used in the market at present are PVC printing forming coating solvent type acrylic glue, a large amount of plasticizer is used in the PVC generation process, the plasticizer gradually migrates out of a base material in the subsequent use process and goes to the environment, and the volatilization of a large amount of solvent and the generation of harmful substances exist in the production and manufacturing process of the solvent type acrylic glue. The PVC warning tape has the advantages that the damage to the environment is extremely large, the damage to the adhesive tape can be generated to the environment in the production, manufacturing and product aging processes, in addition, the PVC warning tape is uneven in tear opening and needs to be cut by a knife, and the strength is low. The other PET film-coated warning tape cannot be torn off by hands, so that the use experience is relatively influenced, and the residual adhesive exists after long-term use.
Therefore, in order to overcome the defects of the prior art, a completely new adhesive tape needs to be developed.
SUMMERY OF THE UTILITY MODEL
An object of the utility model is to provide a reliable, easy printing-free warning sticky tape.
In order to realize the purpose, the utility model provides an exempt from to print warning sticky tape includes adhesive layer, gauze layer, thin layer in proper order and leaves the type layer, the gauze layer includes first warning yarn group and the second warning yarn group of cross arrangement, first warning yarn group and second warning yarn group comprise a plurality of warning yarns respectively.
As a further improvement of the present invention, the first warning yarn set is composed of warning yarns of one or more than two different colors.
As a further improvement of the present invention, the second warning yarn group is composed of warning yarns of one or more than two different colors.
As a further improvement of the utility model, the thickness of the gauze layer is 80-120 μm, the tensile strength is 50-70N/cm, and the elongation is 8% -15%.
As a further improvement, the warning yarn parallel arrangement in the first warning yarn group, the warning yarn in the second warning yarn group also is parallel arrangement.
As a further improvement, the warning yarn in the first warning yarn group and the warning yarn in the second warning yarn group intersect perpendicularly.
As a further improvement of the utility model, the gauze layer is arranged into a mesh structure with 40-60 meshes.
As a further improvement of the utility model, the warning yarn is an elastic yarn.
The utility model also provides a preparation process of the printing-free warning adhesive tape, which comprises the following steps,
weaving 50-mesh gauze layer with different colors by using yarns with different colors of stretch yarn, coating the prepared polyethylene high polymer material on one side of the gauze layer, wherein the coating amount is 70-100g/m2(ii) a Then continuing to coat the non-silicon release agent, wherein the coating amount is 0.03-0.04g/m2Then drying is carried out, the drying temperature is 70-80 ℃, and the machine speed is 90-100 m/min; and coating an adhesive on the other side of the gauze layer, and curing by using a UV curing lamp after coating, wherein the light curing wavelength is 390-400 nm.
As a further improvement of the utility model, the formation of the gauze layer uses the weft insertion fine weaving mode, every 6 wefts are woven, and the interval is different colors.
The utility model discloses beneficial effect:
the utility model discloses regard the gauze layer as warning layer to reasonable arrange the yarn and weave, not only can guarantee reliable intensity during the use, tear the mouth moreover and level, need not to cut with the sword, tear after laminating for a long time and remove and can not have incomplete glue and the damaged phenomenon of substrate.
Drawings
Fig. 1 is a schematic structural view of the printing-free warning tape of the present invention.
Detailed Description
The present invention will be described in detail with reference to specific embodiments.
This embodiment provides a printing-free warning tape, like figure 1, include adhesive 1, gauze layer 2, thin layer 3 in proper order and leave type layer 4, the gauze layer warns yarn group and second including the first warning yarn group and the second of cross arrangement and warns yarn group, first warning yarn group and second warn yarn group and comprise a plurality of warning yarns respectively.
The first warning yarn group is composed of one or more than two warning yarns with different colors, the second warning yarn group is composed of one or more than two warning yarns with different colors, the thickness of the gauze layer is 80-120 mu m, the tensile strength is 50-70N/cm, the elongation is 8% -15%, the warning yarns in the first warning yarn group are arranged in parallel, and the warning yarns in the second warning yarn group are also arranged in parallel.
In a preferred embodiment, the warning yarns in the first warning yarn group are vertically crossed with the warning yarns in the second warning yarn group, the gauze layer is arranged into a mesh structure of 40-60 meshes, and the warning yarns are elastic yarns.
The gauze layer of the printing-free warning tape in the embodiment adopts film covering treatment, adopts high molecular polyethylene, then adds UV absorbent and anti-aging agent to play a role in good weather resistance, controls the film spraying temperature at 280-295 ℃, and controls the film covering amount to be 70-100g/m2The machine speed is controlled at 90-100m/min, and the machine speed and the coating amount can be adjusted according to the actual use requirement.
In the practical novel profile of the adhesive layer coating process, hot-melt glue is preferably coated in the embodiment, wherein the glue is preferably Pasteur acre resin @ A204UV, and the curing wave band is irradiated by light with the wave band of 390-. Meanwhile, the adhesive layer in the present embodiment may be generally mixed with conventional additives for improving pressure-sensitive adhesive properties, or with additives for improving other properties. Such as resins, particularly tackifying resins. All resins compatible with the binder can be used, in particular aliphatic, aromatic and alkylaromatic hydrocarbon resins, monomer-based hydrocarbon resins, hydrogenated hydrocarbon resins, functional hydrocarbon resins and natural resins, examples including terpene-phenolic resins, as well as C5, C9 and other hydrocarbon resins. In addition, a plasticizer, an aging inhibitor for fillers (non-covering fillers, hollow glass beads, etc.), and the like may be optionally added.
Specifically, the manufacturing process of the print-free warning tape in the embodiment is as follows:
weaving 50-mesh yellow-black gauze layer with elastic yarn yellow-black yarn, coating prepared polyethylene polymer material at 70-100g/m2(ii) a Then, a non-silicon release agent, preferably K100DI (Basff material), is applied in an amount of 0.03-0.04g/m2Then drying is carried out, the drying temperature is 70-80 ℃, and the machine speed is 90-100 m/min; an adhesive, preferably BASF acrein @ A204UV from Bass, is applied to the other side of the scrim layer and cured using a UV curing lamp at a photocuring wavelength of 390-400 nm.
In the above-mentioned manufacturing process, the gauze layer is formed by weft insertion fine weaving, and every 6 wefts are spaced by black and yellow.
In order to better embody the beneficial effects of the present invention, further verification is made through experimental tests below.
Test examples: and (5) preparing a sample after coating, and performing physical property test and application simulation.
The physical property test comprises the following steps: initial adhesion test (GB/T4852-; the test results obtained are shown in table 1.
TABLE 1
Simulation is applied: preparing a sample into a sample with the width of 25mm and the length of 30cm, attaching the sample to a part (a front bumper spray painting plate, a plastic arc material, a window rubber strip and the like) at a common position of an automobile bumper, and carrying out outdoor long-term simulation application after fixing; laminating open air glass panel, open air terrace finish, the various outer wall surfaces of open air building, simulation PE, PP, ABS panel, tear (remove) after 3 months of outdoor laminating and observe whether have cull and the damaged problem of substrate at applied position.
Through the experiment proof, the utility model provides a printing-free warning sticky tape is implemented conveniently, and laminating effect is good in outdoor application and simulation test, and the weatherability is better, and production process does not have VOC and volatilizes almost, tears the terminal surface and levels and need not to cut with the stage property, and product tensile strength is higher, has the intensity of ordinary cloth base sticky tape, possesses the weatherability of oily acrylic acid glue, possesses the warning effect of printing cloth base. The volatilization of organic gas in the whole production process is close to zero.
It should be understood that although the present description refers to embodiments, not every embodiment contains only a single technical solution, and such description is for clarity only, and those skilled in the art should make the description as a whole, and the technical solutions in the embodiments can also be combined appropriately to form other embodiments understood by those skilled in the art.
The above list of details is only for the practical implementation of the present invention, and they are not intended to limit the scope of the invention, and all equivalent implementations or modifications that do not depart from the technical spirit of the present invention should be included in the scope of the present invention.
Claims (8)
1. A printing-free warning adhesive tape is characterized in that: include adhesive layer, gauze layer, thin layer in proper order and leave the type layer, the gauze layer includes first warning yarn group and the second warning yarn group of cross arrangement, first warning yarn group and second warning yarn group constitute by a plurality of warning yarns respectively.
2. A print-free warning tape according to claim 1, wherein: the first warning yarn group is composed of one or more warning yarns with different colors.
3. A print-free warning tape according to claim 1, wherein: the second warning yarn group is composed of one or more warning yarns with different colors.
4. A print-free warning tape according to claim 1, wherein: the thickness of the gauze layer is 80-120 mu m, the tensile strength is 50-70N/cm, and the elongation is 8% -15%.
5. A print-free warning tape according to claim 1, wherein: the warning yarns in the first warning yarn group are arranged in parallel, and the warning yarns in the second warning yarn group are also arranged in parallel.
6. A print-free warning tape according to claim 5, wherein: and the warning yarns in the first warning yarn group are vertically crossed with the warning yarns in the second warning yarn group.
7. A print-free warning tape according to claim 6, wherein: the gauze layer is arranged into a mesh structure of 40-60 meshes.
8. A print-free warning tape according to claim 1, wherein: the warning yarn is an elastic yarn.