CN212288997U

CN212288997U - Infrared stealth cloth and infrared stealth clothes based on carbon nanotube structure

Info

Publication number: CN212288997U
Application number: CN201922374740.2U
Authority: CN
Inventors: 金元浩; 李群庆; 范守善
Original assignee: Tsinghua University; Hongfujin Precision Industry Shenzhen Co Ltd
Current assignee: Tsinghua University; Hongfujin Precision Industry Shenzhen Co Ltd
Priority date: 2019-12-25
Filing date: 2019-12-25
Publication date: 2021-01-05
Anticipated expiration: 2029-12-25

Abstract

An infrared stealth cloth based on a carbon nanotube structure, comprising: a cloth substrate; an infrared light absorber disposed on the cloth substrate; the infrared light absorber comprises a carbon nanotube structure, the carbon nanotube structure comprises a first layer of carbon nanotube drawing film, a second layer of carbon nanotube drawing film and a third layer of carbon nanotube drawing film, the first layer of carbon nanotube drawing film, the second layer of carbon nanotube drawing film and the third layer of carbon nanotube drawing film are arranged in a stacked mode, each of the first layer of carbon nanotube drawing film, the second layer of carbon nanotube drawing film and the third layer of carbon nanotube drawing film comprises a plurality of carbon nanotubes which are connected end to end and basically extend along the same direction, the extending directions of the carbon nanotubes in the first layer of carbon nanotube drawing film and the second layer of carbon nanotube drawing film form an included angle of 42-48 degrees, and the extending directions of the carbon nanotubes in the first layer of carbon nanotube drawing film and the third layer of carbon nanotube drawing film form an included angle of 84-96 degrees.

Description

Infrared stealth cloth and infrared stealth clothes based on carbon nanotube structure

Technical Field

The utility model relates to an infrared stealthy cloth and infrared stealthy clothes especially relate to an infrared stealthy cloth and infrared stealthy clothes based on carbon nanotube.

Background

Infrared radiation is electromagnetic waves with wavelengths between visible and microwave, and is imperceptible to the human eye. To detect the presence of such radiation and measure its intensity, it must be converted into other physical quantities that can be detected and measured. With the development of the photoelectric technology, the thermal infrared detection plays a crucial role in modern military reconnaissance and monitoring, and the thermal infrared threat is continuously upgraded. The infrared stealth technology reduces the infrared radiation characteristic difference between a target object and a complex environment by reducing the infrared radiation characteristic of the target object, so that the target object is difficult to find by a detection system or the detection effect of the detection system is reduced. However, the existing infrared stealth technology has low absorptivity to infrared radiation, resulting in poor stealth effect.

SUMMERY OF THE UTILITY MODEL

In view of this, it is necessary to provide an infrared stealth fabric and an infrared stealth garment with a good stealth effect.

An infrared camouflage fabric, comprising: a cloth substrate; an infrared light absorber disposed on the cloth substrate; the infrared light absorber comprises a carbon nanotube structure, the carbon nanotube structure comprises a first layer of carbon nanotube drawing film, a second layer of carbon nanotube drawing film and a third layer of carbon nanotube drawing film, the first layer of carbon nanotube drawing film, the second layer of carbon nanotube drawing film and the third layer of carbon nanotube drawing film are arranged in a stacked mode, each of the first layer of carbon nanotube drawing film, the second layer of carbon nanotube drawing film and the third layer of carbon nanotube drawing film comprises a plurality of carbon nanotubes which are connected end to end and basically extend along the same direction, the extending directions of the carbon nanotubes in the first layer of carbon nanotube drawing film and the second layer of carbon nanotube drawing film form an included angle of 42-48 degrees, and the extending directions of the carbon nanotubes in the first layer of carbon nanotube drawing film and the third layer of carbon nanotube drawing film form an included angle of 84-96 degrees.

An infrared stealthy clothing comprises a clothing body, wherein at least part of cloth of the clothing body is the infrared stealthy cloth.

Further, the infrared stealth fabric comprises two fabric substrates, and the infrared light absorber is arranged between the two fabric substrates.

Further, the extending directions of the carbon nanotubes in the first layer of carbon nanotube drawing film and the second layer of carbon nanotube drawing film form an included angle of 45 degrees.

Furthermore, the extending directions of the carbon nanotubes in the first layer of carbon nanotube drawing film and the third layer of carbon nanotube drawing film form an included angle of 90 degrees.

Further, the second layer of carbon nanotube drawn film is located between the first layer of carbon nanotube drawn film and the third layer of carbon nanotube drawn film, an included angle of 90 degrees is formed in the extending direction of the carbon nanotubes in the first layer of carbon nanotube drawn film and the third layer of carbon nanotube drawn film, and an included angle of 45 degrees is formed in the extending direction of the carbon nanotubes in the first layer of carbon nanotube drawn film and the second layer of carbon nanotube drawn film.

Further, the plurality of carbon nanotubes are connected end to end in the extending direction of the carbon nanotubes.

Further, the plurality of carbon nanotubes are parallel to the surface of the cloth substrate.

Further, the infrared light absorber further comprises a transparent coating layer, and the transparent coating layer is arranged on the surface of the carbon nano tube structure.

Further, the infrared light absorber has an absorption rate of 98.85% or more in a wavelength range of 250nm to 2 μm and an absorption rate of 98.975% or more in a wavelength range of 2 μm to 20 μm.

Compared with the prior art, the utility model discloses utilize the carbon nanotube of the range upon range of setting of three-layer to draw the membrane as infrared absorber, because two-layer carbon nanotube draws the length extending direction vertical cross setting of carbon nanotube in the membrane, the third layer carbon nanotube draw the length extending direction of carbon nanotube in the membrane with two-layer carbon nanotube draws the membrane and forms 42 degrees to 48 degrees contained angles, therefore this infrared absorber not only has higher absorptivity, almost reaches 99%, has the omnidirectional absorption performance moreover, and its absorptivity is irrelevant with the polarization of infrared light, thereby makes infrared stealthy cloth and infrared stealthy clothes have better stealthy effect.

Drawings

Fig. 1 is a scanning electron microscope photograph of a carbon nanotube drawn film according to a first embodiment of the present invention.

Fig. 2 is a schematic diagram of a length extending direction of carbon nanotubes in two layers of carbon nanotube films (sample one) arranged perpendicularly in a crossing manner according to a first embodiment of the present invention.

Fig. 3 is a scanning electron micrograph of the first sample.

Fig. 4 is a schematic diagram illustrating a length extending direction of carbon nanotubes in a three-layer carbon nanotube drawn film (sample two) according to a first embodiment of the present invention.

Fig. 5 is a schematic diagram illustrating a length extending direction of carbon nanotubes in a four-layer drawn carbon nanotube film (sample three) according to a first embodiment of the present invention.

Fig. 6 is a scanning electron micrograph of sample three.

Fig. 7 is a schematic view of the extending direction of the carbon nanotubes in the three-layer carbon nanotube drawn film (sample four) according to the first embodiment of the present invention.

Fig. 8 is a schematic structural view of the sample four.

Fig. 9 is a scanning electron micrograph of the sample four.

FIG. 10 is a graph of the transmission spectrum of the sample in the Ultraviolet (UV) -Near Infrared (NIR) wavelength range.

Fig. 11 is a graph of the reflectance spectrum of the sample three in the Ultraviolet (UV) -Near Infrared (NIR) wavelength range.

Fig. 12 is a graph of the transmission spectrum of the sample four in the Ultraviolet (UV) -Near Infrared (NIR) wavelength range.

Fig. 13 is a graph of the reflectance spectrum of the sample four in the Ultraviolet (UV) -Near Infrared (NIR) wavelength range.

Fig. 14 is a graph of the absorption spectrum of sample four in the Ultraviolet (UV) -Near Infrared (NIR) wavelength range.

Fig. 15 is a graph of the transmission spectrum of sample four in the mid-infrared (MIR) wavelength range.

Fig. 16 is a graph of the reflectance spectrum of the sample four in the mid-infrared (MIR) wavelength range.

Fig. 17 is a graph of the absorption spectrum of sample four in the mid-infrared (MIR) wavelength range.

Fig. 18 is a graph of the spectrum of the sample four in the visible to near-infrared wavelength range measured at an incident angle of 0 ° to 60 °.

Fig. 19 is a spectrum diagram of the sample four in the mid-infrared wavelength range measured at an incident angle of 0 ° to 60 °.

Fig. 20 is a graph of the spectrum of the sample four in the visible-infrared wavelength range measured at an incident polarization degree of 0 ° to 90 °.

Fig. 21 is a spectrum of the sample four over the mid-infrared wavelength range measured at an incident polarization degree of 0 ° to 90 °.

Fig. 22 is a schematic structural diagram of an infrared detector according to a second embodiment of the present invention.

Fig. 23 is a schematic structural diagram of an infrared imager according to a third embodiment of the present invention.

Fig. 24 is a schematic structural view of an infrared stealth fabric according to a fourth embodiment of the present invention.

Fig. 25 is a schematic structural view of an infrared stealth garment according to a fifth embodiment of the present invention.

Description of the main elements

Sample No. 10

Sample No. two 20

Sample No. three 30

Sample No. four 40

First layer of carbon nanotube drawing film 12

Second layer carbon nanotube draw film 14

Third layer of carbon nanotube drawing film 16

Fourth layer carbon nanotube draw film 18

Infrared detector 100

Infrared absorber 110

Thermoelectric element 112

Electric signal detector 114

Infrared imager 200

Infrared receiver 210

Infrared detector assembly 220

Signal processor 230

Infrared display 240

Infrared stealth fabric 300

Cloth substrate 310

Infrared stealth garment 400

The following detailed description of the invention will be further described in conjunction with the above-identified drawings.

Detailed Description

The infrared stealth fabric and the infrared stealth garment provided by the present invention will be further described in detail with reference to the accompanying drawings and specific embodiments.

The first embodiment of the present invention provides an infrared absorber, which is a carbon nanotube structure formed by stacking a plurality of carbon nanotubes.

Referring to fig. 1, the drawn carbon nanotube film includes a plurality of carbon nanotubes connected end to end and extending substantially along a same direction. The carbon nanotubes include one or more of single-walled carbon nanotubes, double-walled carbon nanotubes, and multi-walled carbon nanotubes. The diameter of the single-walled carbon nanotube is 0.5 to 50 nanometers, the diameter of the double-walled carbon nanotube is 1.0 to 50 nanometers, and the diameter of the multi-walled carbon nanotube is 1.5 to 50 nanometers. The carbon nano tubes are uniformly distributed and are parallel to the surface of the carbon nano tube drawing film. The carbon nanotubes in the carbon nanotube drawn film are connected through Van der Waals force. On one hand, the carbon nanotubes connected end to end are connected through van der waals force, and on the other hand, the parallel carbon nanotubes are combined through van der waals force, so that the drawn carbon nanotube film has certain flexibility, can be bent and folded into any shape without breaking, and has good self-supporting performance. The carbon nanotube drawn film can be obtained by directly drawing a carbon nanotube array. It is understood that the carbon nanotubes extending in the same direction in the drawn carbon nanotube film are most of the carbon nanotubes extending in the same direction. Of course, a few carbon nanotubes randomly arranged exist in the drawn carbon nanotube film, and the carbon nanotubes do not have a significant influence on the overall alignment of most of the carbon nanotubes in the drawn carbon nanotube film. Therefore, "extending substantially in the same direction" may more accurately describe the internal structure of the carbon nanotube drawn film.

When at least two layers of the carbon nanotube drawn films are overlapped, the adjacent carbon nanotube drawn films are tightly combined through Van der Waals force. Furthermore, an included angle alpha is formed in the extending direction of the carbon nano tubes in the two adjacent layers of carbon nano tube drawing films, and the alpha is more than or equal to 0 and less than or equal to 90 degrees.

The self-supporting performance is that the carbon nanotube film drawing does not need large-area carrier support, but can be suspended integrally to keep a self film state as long as the two opposite sides provide supporting force, namely when the carbon nanotube film drawing is placed (or fixed) on two supporting bodies arranged at a fixed distance, the carbon nanotube film drawing positioned between the two supporting bodies can keep a self layer state. It will be appreciated that the infrared absorber also has self-supporting properties.

In order to research the absorption performance of the infrared absorber, the utility model discloses four kinds of different samples are prepared and are tested and compared, and these four kinds of samples are shown as figure 2 to figure 8 respectively. In order to clearly show the positions and arrangement relationships of the carbon nanotubes in the first sample, the second sample, the third sample and the fourth sample, only one carbon nanotube is drawn in each layer of the drawn carbon nanotube film in fig. 2, 4, 5 and 7 (actually, each layer of the drawn carbon nanotube film includes a plurality of substantially parallel carbon nanotubes), which should not be a limitation to the present invention.

Sample No. 10

Two layers of carbon nanotube films arranged perpendicularly across form sample one 10. Specifically, as shown in fig. 2 and 3, the sample one 10 is composed of two layers of carbon nanotube drawn films arranged in a perpendicular and crossed manner, the carbon nanotubes in each layer of carbon nanotube drawn film are connected end to end and extend along the same direction, and the length extending directions of the carbon nanotubes in the two layers of carbon nanotube drawn films form an included angle of about 90 degrees. That is, in sample one 10, two carbon nanotube films are stacked and formed in a cross shape.

Sample No. two 20

The three layers of carbon nanotube drawn films are stacked, and the length extension directions of the carbon nanotubes in the adjacent carbon nanotube drawn films form an included angle of about 60 degrees. Specifically, as shown in fig. 4, the second sample 20 is formed by sequentially stacking a first layer of drawn carbon nanotube film 12, a second layer of drawn carbon nanotube film 14, and a third layer of drawn carbon nanotube film 16 (in fig. 4, only one carbon nanotube is drawn on each of the first layer of drawn carbon nanotube film 12, the second layer of drawn carbon nanotube film 14, and the third layer of drawn carbon nanotube film 16 for clearly showing the positional relationship among the carbon nanotubes in the first layer of drawn carbon nanotube film 12, the second layer of drawn carbon nanotube film 14, and the third layer of drawn carbon nanotube film 16), the second layer of drawn carbon nanotube film 14 is located between the first layer of drawn carbon nanotube film 12 and the third layer of drawn carbon nanotube film 16, the extending direction of the carbon nanotubes in the first layer of drawn carbon nanotube film 12 and the extending direction of the carbon nanotubes in the second layer of drawn carbon nanotube film 14 form an included angle of about 60 degrees, and the extending direction of the carbon nanotubes in the second layer of drawn carbon nanotube film 14 and the extending direction of the carbon nanotubes in the third layer of drawn carbon nanotube film 16 are sequentially stacked carbon nanotubes in sequence The directions form an included angle of about 60 degrees.

Sample No. three 30

Four layers of carbon nano tube drawing films are stacked. Specifically, as shown in fig. 5 and 6, the sample three 30 is formed by sequentially stacking a first carbon nanotube drawn film 12, a second carbon nanotube drawn film 14, a third carbon nanotube drawn film 16, and a fourth carbon nanotube drawn film 18. In fig. 5, only one carbon nanotube is drawn on each of the first carbon nanotube drawing film 12, the second carbon nanotube drawing film 14, the third carbon nanotube drawing film 16, and the fourth carbon nanotube drawing film 18, so as to clearly show the position relationship among the carbon nanotubes in the first carbon nanotube drawing film 12, the second carbon nanotube drawing film 14, the third carbon nanotube drawing film 16, and the fourth carbon nanotube drawing film 18. The extending direction of the carbon nanotubes in the first carbon nanotube drawing film 12 and the extending direction of the carbon nanotubes in the second carbon nanotube drawing film 14 form an included angle of 45 degrees, and the extending direction of the carbon nanotubes in the second carbon nanotube drawing film 14 and the extending direction of the carbon nanotubes in the third carbon nanotube drawing film 16 form an included angle of 45 degrees. The carbon nanotubes in the fourth drawn carbon nanotube film 18 and the carbon nanotubes in the third drawn carbon nanotube film 16 form an included angle of 45 degrees, and the carbon nanotubes in the first drawn carbon nanotube film 12 and the extended length direction form an included angle of 90 degrees. That is, in sample three 30, four carbon nanotube drawn films are stacked and formed in a "rice" shape.

Sample No. four 40

The three layers of carbon nano tube drawing films are arranged in a laminated mode. Specifically, as shown in fig. 7 and 8, in the sample four 40, a first layer of drawn carbon nanotube film 12, a second layer of drawn carbon nanotube film 14, and a third layer of drawn carbon nanotube film 16 are sequentially stacked, the second layer of drawn carbon nanotube film 14 is located between the first layer of drawn carbon nanotube film 12 and the third layer of drawn carbon nanotube film 16, a length extending direction of the carbon nanotubes in the first layer of drawn carbon nanotube film 12 and a length extending direction of the carbon nanotubes in the second layer of drawn carbon nanotube film 14 form an included angle of 45 degrees, and a length extending direction of the carbon nanotubes in the second layer of drawn carbon nanotube film 14 and a length extending direction of the carbon nanotubes in the third layer of drawn carbon nanotube film 16 form an included angle of 45 degrees. The extending direction of the carbon nanotubes in the first carbon nanotube drawing film 12 and the extending direction of the carbon nanotubes in the third carbon nanotube drawing film 16 form an included angle of 90 degrees.

In sample four 40, the extending direction of the carbon nanotubes in the first carbon nanotube drawn film 12 and the extending direction of the carbon nanotubes in the third carbon nanotube drawn film 16 form an included angle of 42 to 48 degrees with the extending direction of the carbon nanotubes in the second carbon nanotube drawn film 14, respectively, and the extending direction of the carbon nanotubes in the first carbon nanotube drawn film 12 and the extending direction of the carbon nanotubes in the third carbon nanotube drawn film 16 form an included angle of 84 to 96 degrees. Preferably, the extending direction of the lengths of the carbon nanotubes in the first carbon nanotube drawn film 12 and the extending direction of the lengths of the carbon nanotubes in the third carbon nanotube drawn film 16 form an included angle of 45 degrees with the extending direction of the lengths of the carbon nanotubes in the second carbon nanotube drawn film 14, respectively, and the extending direction of the lengths of the carbon nanotubes in the first carbon nanotube drawn film 12 and the extending direction of the lengths of the carbon nanotubes in the third carbon nanotube drawn film 16 form an included angle of 90 degrees.

The absorption properties of the above four samples are analyzed in comparison from the range of the absorption spectrum, the absorption spectrum at different incident angles, and the absorption spectrum at different polarization angles.

Fig. 9 is a graph of the transmission spectrum of the sample one 10 in the Ultraviolet (UV) -Near Infrared (NIR) wavelength range. As can be seen from fig. 9, the transmittance of sample one 10 is high, thus resulting in a low absorption rate. The reason is that: sample one 10 is too sparse in structure, has a large number and size of pores, and has a large amount of light passing through the pores of sample one 10, resulting in sample one 10 having a strong light transmittance of up to 2.6%, but a low light absorption.

Fig. 10 is a graph of the reflectance spectrum of the sample three 30 in the Ultraviolet (UV) -Near Infrared (NIR) wavelength range. As can be seen from fig. 10, the reflectance of sample three 30 is high, up to 3.3%, thus resulting in a low absorbance. The reason is that: the structure of sample three 30 is too compact and dense, and when light is irradiated to sample three 30, more light is reflected by sample three 30, resulting in sample three 30 having a strong light reflectivity, but a low light absorption. In addition, the absorption rate of sample two 20 is also low.

Further, the light transmittance and reflectance of the sample four 40 were measured using two independent optical measurement systems. Fig. 11 and 12 are a transmission spectrum and a reflection spectrum, respectively, of sample four 40 in the Ultraviolet (UV) -Near Infrared (NIR) wavelength range, i.e., in the 250 nanometer (nm) to 2 micrometer (μm) wavelength range. FIG. 13 is a spectral diagram measured in the UV-NIR wavelength range using a spectral luminance meter equipped with an integrating sphere, and the inset is an enlarged view of the high absorption region. As can be seen from fig. 11 to 13, the absorbance of sample four 40 in the UV-NIR wavelength range (250nm to 2 μm) was 98.85% or more.

FIGS. 14 and 15 are a transmission spectrum and a reflection spectrum, respectively, of sample four 40 measured in the mid-infrared (MIR) wavelength range (2 μm to 20 μm). Fig. 16 is a graph of a spectrum measured in the MIR wavelength range using a Fourier Transform Infrared (FTIR) spectrometer, with the inset being an enlarged view of the high absorption region. As can be seen from fig. 14 to 16, the absorbance of sample four 40 in the MIR wavelength range (2 μm to 20 μm) was 98.975% or more.

Fig. 17 is a spectral plot of the sample four 40 over the visible to NIR wavelength range measured at an angle of incidence of 0 ° to 60 °, the angle between the light ray and a normal to the surface of the sample four 40. That is, in sample four 40, the length extension direction of the carbon nanotube is parallel to the surface of sample four 40, and the light ray is irradiated to the surface of sample four 40, and the angle between the light ray and the normal line is the incident angle. As can be seen from fig. 17, the absorbance of sample four 40 remained stable in the wavelength range of 250nm to 2 μm, regardless of the incident angle of light, and the lowest absorbance of all incident angles was also greater than 98%. Therefore, sample four 40 can achieve omnidirectional absorption in the visible to NIR wavelength range of 250nm to 2 μm. The term "omnidirectional absorption" means that the sample four 40 has a high absorption rate at each angle of incidence.

Fig. 18 is a spectrum of the sample four 40 over the mid-infrared wavelength range measured at an incident angle of 0 ° to 60 °. As can be seen from fig. 18, the absorbance of sample four 40 remained stable in the wavelength range of 2 μm to 20 μm regardless of the incident angle of light, and the lowest absorbance of all incident angles was also greater than 98.5%. Therefore, sample four 40 also achieved omnidirectional absorption in the mid-infrared wavelength range of 2 μm to 20 μm.

Fig. 19 is a spectrum of the sample four 40 in the visible-infrared wavelength range measured at an incident polarization degree of 0 ° to 90 °. As can be seen from fig. 19, the absorption spectrum is almost the same regardless of the polarization of the incident light. Thus, the absorption of sample four 40 in the visible to NIR wavelength range of 250nm to 2 μm is independent of the polarization of the light.

Fig. 20 is a spectrum of the sample four 40 over the mid-infrared wavelength range measured at an incident polarization degree of 0 ° to 90 °. As can be seen from fig. 20, the absorption spectrum is almost the same regardless of the polarization of the incident light. Therefore, the absorption of sample four 40 in the mid-infrared wavelength range of 2 μm to 20 μm is also independent of the polarization of the light.

As can be seen from the test results of fig. 11-20, the absorption of sample four 40 in the uv to mid-ir wavelength range (250nm to 20 μm) is independent of both the incident angle and the polarization of light. Thus, sample four 40 has omnidirectional properties and is polarization independent for absorption of light in the ultraviolet to mid-infrared wavelength range (250nm to 20 μm).

In addition, the inventors found that in the sample four 10, the position of the second layer of drawn carbon nanotube film 14 is exchanged with the first layer of drawn carbon nanotube film 12 or with the third layer of drawn carbon nanotube film 16, which does not affect the absorption performance of the sample four 10. That is, in the sample four 10, the second layer of drawn carbon nanotube film 14, the first layer of drawn carbon nanotube film 12, and the third layer of drawn carbon nanotube film 16 are sequentially stacked; the first layer of carbon nanotube drawn film 12 is positioned between the second layer of carbon nanotube drawn film 14 and the third layer of carbon nanotube drawn film 16; the extending direction of the carbon nanotubes in the first carbon nanotube drawn film 12 and the extending direction of the carbon nanotubes in the second carbon nanotube drawn film 14 form an included angle of 42 degrees to 48 degrees, and the extending direction of the carbon nanotubes in the second carbon nanotube drawn film 14 and the extending direction of the carbon nanotubes in the third carbon nanotube drawn film 16 form an included angle of 42 degrees to 48 degrees. The extending direction of the carbon nanotubes in the first carbon nanotube drawing film 12 and the extending direction of the carbon nanotubes in the third carbon nanotube drawing film 16 form an included angle of 84 to 96 degrees. Preferably, the extending direction of the carbon nanotubes in the first carbon nanotube drawn film 12 and the extending direction of the carbon nanotubes in the second carbon nanotube drawn film 14 form an included angle of 45 degrees, the extending direction of the carbon nanotubes in the second carbon nanotube drawn film 14 and the extending direction of the carbon nanotubes in the third carbon nanotube drawn film 16 form an included angle of 45 degrees, and the extending direction of the carbon nanotubes in the first carbon nanotube drawn film 12 and the extending direction of the carbon nanotubes in the third carbon nanotube drawn film 16 form an included angle of 90 degrees.

The absorption rate of the first sample 10 is low, which may be because the two drawn carbon nanotube films in the first sample 10 are stacked alternately, the carbon nanotubes are sparse, and most of the light passes through the gaps between the sparse carbon nanotubes in the first sample 10, so the light transmittance of the first sample 10 is high, and the absorption rate is low.

In the third sample 30, four layers of carbon nanotube films are stacked in a shape like a Chinese character 'mi', and as the number of layers of the carbon nanotube films increases, gaps between the carbon nanotubes gradually decrease and light transmittance decreases, but as the carbon nanotubes are denser, more reflection is caused at the interface between the air and the carbon nanotubes, and most of light is reflected, so that the third sample 30 has a higher reflectivity and a lower absorption rate.

Therefore, as an infrared absorber, the three-layered drawn carbon nanotube film has a higher absorption rate than the two-layered drawn carbon nanotube film (sample one 10) and the four-layered drawn carbon nanotube film (sample three 30). Further, the inventors found that when two drawn carbon nanotube films are almost perpendicularly crossed and the remaining drawn carbon nanotube film is arranged at an angle of almost 45 degrees to the two drawn carbon nanotube films (sample four 40), the drawn carbon nanotube film has a higher absorption rate, almost as high as 99%, has an omnidirectional absorption performance, and has an absorption rate independent of the polarization of infrared light. This is not the case when the extending direction of the length of the carbon nanotube in the adjacent drawn carbon nanotube film forms an included angle of about 60 degrees (sample two 20).

Referring to fig. 22, a second embodiment of the present invention provides an infrared detector 100, wherein the infrared detector 100 includes an infrared light absorber 110, a thermoelectric element 112 and an electrical signal detector 114. The infrared light absorber 110 is disposed on the pyroelectric element 112, and is disposed in direct contact with the pyroelectric element 112. When the pyroelectric element 112 and the infrared light absorber 110 are stacked, the length extension direction of the carbon nanotubes in the infrared light absorber 110 is parallel to the contact surface between the pyroelectric element 112 and the infrared light absorber 110. The electrical signal detector 114 is electrically connected to the thermoelectric element 112 through a wire, and the electrical signal detector 114 is connected in series with the thermoelectric element 112 to form a loop for detecting the electrical signal change of the thermoelectric element 112.

The infrared light absorber 110 has a carbon nanotube structure identical to that of the sample four 40, that is, the infrared light absorber 110 is formed by sequentially stacking a first carbon nanotube drawn film 12, a second carbon nanotube drawn film 14, and a third carbon nanotube drawn film 16. The first layer of carbon nanotube drawn film 12, the second layer of carbon nanotube drawn film 14 and the third layer of carbon nanotube drawn film 16 all include a plurality of carbon nanotubes which are connected end to end in the extending direction of the carbon nanotubes and extend along the same direction. The second layer of carbon nanotube drawn film 14 is located between the first layer of carbon nanotube drawn film 12 and the third layer of carbon nanotube drawn film 16, and the first layer of carbon nanotube drawn film 12 and the third layer of carbon nanotube drawn film 16 are both in direct contact with the second layer of carbon nanotube drawn film 14. The extending direction of the carbon nanotubes in the first carbon nanotube drawn film 12 and the extending direction of the carbon nanotubes in the second carbon nanotube drawn film 14 form an included angle of 42 degrees to 48 degrees, and the extending direction of the carbon nanotubes in the second carbon nanotube drawn film 14 and the extending direction of the carbon nanotubes in the third carbon nanotube drawn film 16 form an included angle of 42 degrees to 48 degrees. The extending direction of the carbon nanotubes in the first carbon nanotube drawing film 12 and the extending direction of the carbon nanotubes in the third carbon nanotube drawing film 16 form an included angle of 84 to 96 degrees. Preferably, the extending direction of the carbon nanotubes in the first carbon nanotube drawn film 12 and the extending direction of the carbon nanotubes in the second carbon nanotube drawn film 14 form an included angle of 45 degrees, the extending direction of the carbon nanotubes in the second carbon nanotube drawn film 14 and the extending direction of the carbon nanotubes in the third carbon nanotube drawn film 16 form an included angle of 45 degrees, and the extending direction of the carbon nanotubes in the first carbon nanotube drawn film 12 and the extending direction of the carbon nanotubes in the third carbon nanotube drawn film 16 form an included angle of 90 degrees. The first layer of carbon nanotube drawn film 12, the second layer of carbon nanotube drawn film 14, and the third layer of carbon nanotube drawn film 16 are all self-supporting structures, and thus, the infrared light absorber 110 is also a self-supporting structure. The plurality of carbon nanotubes in the infrared light absorber 110 are parallel to the surface of the thermoelectric element 112.

The infrared light absorber 110 itself increases in temperature after absorbing infrared light, and since the carbon nanotubes have a high thermal conductivity, the infrared light absorber 110 can transfer heat to the thermoelectric element 112. When the thermoelectric element 112 absorbs heat, the temperature of the thermoelectric element 112 increases, so that the electrical properties of the thermoelectric element 112 change.

The thermoelectric element 112 may be a pyroelectric element, a thermistor, a thermocouple element, or the like. Specifically, the pyroelectric element is a material with a high thermoelectric coefficient, such as lead zirconate titanate ceramic, lithium tantalate, lithium niobate, titanium triethylammonium sulfate, and the like. The thermistor can be a semiconductor thermistor, a metal thermistor, an alloy thermistor, or the like. In this embodiment, the thermoelectric element 112 is a lead zirconate titanate ceramic.

Since the electrical signal detector 114 is used to detect a change in the electrical signal of the pyroelectric element 112, the kind of the electrical signal detector 114 differs according to the pyroelectric element 112. In one embodiment, the pyroelectric element 112 is a pyroelectric element, and the temperature of the pyroelectric element increases to generate a voltage or a current across the pyroelectric element, and the electrical signal detector 114 may be a current-voltage converter connected in series with the pyroelectric element to form a loop, so that the voltage or current change of the pyroelectric element can be detected. In another embodiment, the thermoelectric element 112 is a thermistor, the resistance of which changes when the temperature of the thermistor increases, and the electrical signal detector 114 includes a power source and a current detector, which are connected in series to form a loop, and the change of the current is measured by the current detector to detect the change of the resistance of the thermistor. In another embodiment, the pyroelectric element 112 is a thermocouple, the infrared light absorber 110 is disposed at one end of the thermocouple, and a temperature difference occurs at two ends of the thermocouple, that is, a potential difference occurs at two ends of the thermocouple, and in this case, the electrical signal detector 114 may be a voltage detector, which is connected in series with the thermocouple to form a loop, that is, a change in the potential of the thermocouple can be detected.

The working process of the infrared detector 100 is as follows: infrared light is radiated onto the infrared light absorber 110 (i.e., sample four 40), and the sample four 40 perfectly absorbs the infrared light and converts the absorbed infrared light into heat; the heat is transferred to the thermoelectric element 112; when the electrical signal detector 114 is electrically connected to both ends of the pyroelectric element 112 to form a loop, the electrical signal detector 114 can detect a change in the electrical signal of the pyroelectric element 112, thereby detecting the presence of infrared light in the detection region.

Further, a transparent coating layer is provided on the infrared absorber 110, and since the coating layer is transparent, infrared light can pass through the coating layer and be absorbed by the infrared absorber 110. The coating does not affect the absorption of the infrared light absorber 110. The coating can improve the mechanical properties of the infrared light absorber 110 without affecting the absorption effect. The coating is disposed on the surface of the carbon nanotube structure, and preferably, the coating is disposed on the outer surface of each carbon nanotube. The coating may be a photoresist, a transparent polymer, or the like. Preferably, the material of the coating is ultraviolet photoresist which can be cured under the irradiation of ultraviolet light, and the ultraviolet photoresist can be polyvinyl alcohol cinnamic acid vinegar, cyclized rubber resist and the like. Specifically, an ultraviolet photoresist is deposited on the surface of the carbon nanotube in the infrared light absorber 110, and then the infrared light absorber 110 on which the ultraviolet photoresist is deposited is irradiated by ultraviolet light, so that the ultraviolet photoresist layer is tightly disposed on the infrared light absorber 110. The effect of the ultraviolet irradiation: not only the infrared light absorber 110 is tightly combined with the ultraviolet photoresist layer, but also the surface morphology of the carbon nanotube network in the infrared light absorber 110 is enhanced, thereby improving the wear resistance. The infrared light absorber 110 provided with the ultraviolet resist layer has good abrasion resistance and is not easily damaged regardless of being scratched by cloth or by a knife and a sandpaper.

The utility model discloses the infrared detector 100 that the second embodiment provided has following advantage: firstly, the infrared absorber 110 has good absorption effect on near infrared to mid infrared with the wavelength of 2 μm-20 μm, and improves the responsivity and sensitivity of the pyroelectric element 112, so that the infrared detector 100 has higher sensitivity; secondly, the infrared absorber 110 not only has omnidirectional absorption performance, but also has no relation with polarization, thereby expanding the application range of the infrared detector 100.

Referring to fig. 23, a third embodiment of the present invention provides an infrared imager 200, wherein the infrared imager 200 includes an infrared receiver 210, an infrared detector assembly 220, a signal processor 230, and an infrared display 240. The infrared receiver 210 is configured to receive a spectrum of infrared radiation and transmit the infrared light to the infrared detector assembly 220; the infrared detector assembly 220 is configured to convert the infrared radiation spectrum into an electrical signal, and transmit the electrical signal to the signal processor 230; the signal processor 230 is configured to process and calculate the electrical signal to obtain thermal field distribution data; the infrared display 240 displays an infrared thermography image based on the thermal field distribution data.

The infrared receiver 210 is used for receiving the infrared radiation spectrum emitted by the object, i.e. the infrared light emitted by the object. Further, the infrared receiver 210 may also converge the infrared radiation spectrum. In this embodiment, the infrared receiver 210 is an infrared lens. Specifically, the infrared radiation spectrum emitted by the object is received and converged by the infrared lens, and then directly transmitted to the infrared detector assembly 220. It is understood that the infrared receiver 210 may be omitted.

The infrared detector assembly 220 includes a plurality of infrared detectors 100 in the second embodiment, the plurality of infrared detectors 100 are uniformly distributed in a two-dimensional array, and each infrared detector 100 can convert an infrared radiation spectrum into an electrical signal change. It can be understood that each infrared detector 100 is equivalent to a pixel point, and each infrared detector 100 converts the infrared radiation spectrum of the position into an electrical signal, thereby implementing the detection of the infrared radiation spectrum emitted by the object by the infrared detector assembly 220. The spacing between any two adjacent infrared detectors 100 can be selected based on the resolution requirements of the thermal imaging.

The signal processor 230 is configured to process and calculate the electrical signal of each infrared detector 100, so as to obtain the thermal field distribution of the object. Specifically, the signal processor 230 calculates the temperature data of the object surface position corresponding to each infrared detector 100 according to the electrical signal variation of the infrared detector. That is, the signal processor 230 can calculate the thermal field distribution data of the object according to the electrical signal.

The infrared display 240 is used for displaying an infrared thermography of the object to be measured. The infrared thermography of the infrared display 240 is displayed according to the thermal field distribution data of the object, and different temperatures are displayed with different colors. Therefore, the infrared thermal image displayed by the infrared image display 240 corresponds to the temperature distribution of the object to reflect the temperature condition of each position of the object. For example, when the infrared imaging device 200 is used in the medical field, it can perform a whole-body thermal imaging on a human body, and a professional doctor can determine the disease properties and the pathological changes of different parts of the human body according to the thermal image, so as to provide a basis for clinical diagnosis.

When the infrared imager 200 is in operation, infrared light emitted by an object is received by the infrared receiver 210; the infrared receiver 210 receives and converges the infrared light, and then transmits the infrared light to the infrared detector component 220; the infrared detector assembly 220 converts infrared light into an electrical signal, and then transmits the electrical signal to the signal processor 230; the signal processor 230 processes and calculates the electrical signals to obtain temperature data of each position of the object, that is, thermal field distribution data of the object; the infrared display 240 displays an infrared thermography of the object according to the calculated thermal field distribution data.

The utility model discloses the infrared imager 200 that the third embodiment provided has following advantage: firstly, the infrared absorber 110 has good absorption effect on near infrared to mid infrared light with the wavelength of 2 μm-20 μm, and improves the responsivity and sensitivity of the pyroelectric element 112, so that the infrared imager 200 has higher sensitivity; secondly, the infrared absorber 110 not only has omnidirectional absorption performance, but also has no relation with polarization, thereby expanding the application range of the infrared imager 200.

Referring to fig. 24, a fourth embodiment of the present invention provides an infrared camouflage fabric 300, wherein the infrared camouflage fabric 300 includes a fabric substrate 310 and the infrared light absorber 110 disposed on the fabric substrate 310. The infrared absorber 110 has the same material and structure as those of the sample four 40, that is, the infrared absorber 110 is the sample four 40. The infrared absorber 110 may also be disposed between two cloth substrates 310 to form a sandwich structure. The carbon nanotubes are parallel to the surface of the infrared light absorber 110 near the cloth substrate 310.

The infrared absorber 110 may be provided directly on the fabric substrate 310, or may be fixed to the fabric substrate 310 by an adhesive. In this embodiment, after the infrared light absorber 110 is directly disposed on the fabric substrate 310, the infrared light absorber 110 and the fabric substrate 310 are wetted or soaked in an organic solvent, and the infrared light absorber 110 is tightly bonded to the fabric substrate 310 by using the surface tension generated by volatilization of the organic solvent. The material of the organic solvent is not limited as long as it is volatile and does not dissolve the cloth substrate 310. In this embodiment, the organic solvent is ethanol. Preferably, the cloth substrate 310 has a through hole, so that the infrared light absorber 110 is suspended on the cloth substrate 310. The material of the fabric substrate 310 is not limited, and may be an insulating material, a conductor, a flexible material, or a non-flexible material. In this embodiment, the material of the cloth substrate 310 is not limited, such as cotton, polyester, silk, wool, hemp, leather, etc. In another embodiment, the infrared absorber 110 is sewn between two layers of cloth.

When the infrared stealth fabric 300 covers the hand, the infrared emitted from the hand is absorbed by the infrared stealth fabric 300, and does not pass through the infrared stealth fabric 300 and is detected by other infrared detection systems. Therefore, the infrared camouflage fabric 300 has a good camouflage effect.

Referring to fig. 25, a fifth embodiment of the present invention provides an infrared camouflage garment 400, wherein the infrared camouflage garment 400 is at least partially made of the infrared camouflage fabric 300. That is, the infrared camouflage clothes 400 may be made of the infrared camouflage fabric 300 entirely or may be made of a part of the infrared camouflage fabric 300. The infrared camouflage clothes 400 is not limited to clothes, and may be gloves, masks, etc., which may be collectively referred to as infrared camouflage clothes. The infrared stealth garment comprises a garment body, and at least part of the fabric of the garment body is the infrared stealth fabric 300.

The utility model discloses the infrared stealth cloth 300 that the fourth embodiment provided and the infrared stealth clothes 400 that the fifth embodiment provided have following advantage: firstly, the infrared absorber 110 has a good absorption effect on near infrared light to intermediate infrared light with the wavelength of 2-20 μm, so that the stealth effects of the infrared stealth fabric 300 and the infrared stealth garment 400 are improved; secondly, the infrared absorber 110 has omnidirectional absorption performance and is independent of polarization, so that the application range of the infrared stealth fabric 300 and the infrared stealth garment 400 is expanded, and the stealth effect of the infrared stealth fabric and the infrared stealth garment is further improved.

In addition, other changes may be made by those skilled in the art without departing from the spirit of the invention, and it is intended that all such changes be considered within the scope of the invention as hereinafter claimed.

Claims

1. An infrared camouflage fabric, comprising:

a cloth substrate;

an infrared light absorber disposed on the cloth substrate;

the infrared light absorber is characterized by comprising a carbon nanotube structure, wherein the carbon nanotube structure comprises a first layer of carbon nanotube drawn film, a second layer of carbon nanotube drawn film and a third layer of carbon nanotube drawn film, the first layer of carbon nanotube drawn film, the second layer of carbon nanotube drawn film and the third layer of carbon nanotube drawn film are arranged in a stacked mode, each of the first layer of carbon nanotube drawn film, the second layer of carbon nanotube drawn film and the third layer of carbon nanotube drawn film comprises a plurality of carbon nanotubes which are connected end to end and basically extend along the same direction, the extending directions of the carbon nanotubes in the first layer of carbon nanotube drawn film and the second layer of carbon nanotube drawn film form an included angle of 42-48 degrees, and the extending directions of the carbon nanotubes in the first layer of carbon nanotube drawn film and the third layer of carbon nanotube drawn film form an included angle of 84-96 degrees.

2. The infrared camouflage fabric as recited in claim 1, wherein the infrared camouflage fabric comprises two fabric substrates, and the infrared light absorber is disposed between the two fabric substrates.

3. The infrared camouflage cloth according to claim 1, wherein the extending directions of the carbon nanotubes in the first drawn carbon nanotube film and the second drawn carbon nanotube film form an included angle of 45 degrees.

4. The infrared camouflage cloth according to claim 1, wherein the extending directions of the carbon nanotubes in the first drawn carbon nanotube film and the third drawn carbon nanotube film form an included angle of 90 degrees.

5. The infrared stealth fabric of claim 1, wherein the second drawn carbon nanotube film is located between the first drawn carbon nanotube film and the third drawn carbon nanotube film, the extending directions of the carbon nanotubes in the first drawn carbon nanotube film and the third drawn carbon nanotube film form an included angle of 90 degrees, and the extending directions of the carbon nanotubes in the first drawn carbon nanotube film and the second drawn carbon nanotube film form an included angle of 45 degrees.

6. The infrared camouflage cloth of claim 1, wherein the plurality of carbon nanotubes are connected end to end in the direction of elongation of the carbon nanotubes.

7. The infrared stealth fabric of claim 1, wherein the plurality of carbon nanotubes are parallel to a surface of the fabric substrate.

8. The infrared camouflage cloth of claim 7, wherein the infrared light absorber further comprises a transparent coating, and the transparent coating is disposed on the surface of the carbon nanotube structure.

9. The infrared camouflage fabric as set forth in claim 1, wherein the infrared absorber has an absorption rate of 98.85% or more in a wavelength range of 250nm to 2 μm and an absorption rate of 98.975% or more in a wavelength range of 2 μm to 20 μm.

10. An infrared stealth garment, which comprises a garment body and is characterized in that at least part of cloth of the garment body is the infrared stealth cloth according to any one of claims 1 to 9.