CN212266914U - Waterproof and moisture permeable oxford for luggage - Google Patents
Waterproof and moisture permeable oxford for luggage Download PDFInfo
- Publication number
- CN212266914U CN212266914U CN201922494598.5U CN201922494598U CN212266914U CN 212266914 U CN212266914 U CN 212266914U CN 201922494598 U CN201922494598 U CN 201922494598U CN 212266914 U CN212266914 U CN 212266914U
- Authority
- CN
- China
- Prior art keywords
- layer
- permeable
- waterproof
- oxford
- moisture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a waterproof and moisture permeable oxford for bags and suitcases, which comprises a base cloth layer and a waterproof and moisture permeable film layer; the base cloth layer is made of oxford cloth formed by interweaving warps and wefts; the waterproof moisture-permeable film layer is a TPU/PAN double-component waterproof moisture-permeable film sprayed on the surface of the base cloth layer by adopting an electrostatic spinning method. The utility model relates to a case and bag are with waterproof moisture permeable oxford, including the base cloth layer that adopts elasticity covering yarn to prepare and adopt the waterproof moisture permeable membrane of electrostatic spinning method spraying on the base cloth layer, can make this surface fabric have good elasticity and waterproof moisture permeable effect. And TPU/PAN two-component waterproof moisture-permeable membrane, wherein TPU has good hydrophilicity and higher elasticity, PAN has good chemical corrosion resistance, and the fiber is thinner. So that the whole fabric has good protection function and moisture permeability function.
Description
Technical Field
The utility model belongs to the technical field of textile fabric technique and specifically relates to a waterproof moisture permeable oxford for case and bag.
Background
Oxford is a novel fabric with various functions and wide application, and mainly has the following components in the market: the varieties of the sheath lattice, the full-elastic, the chinlon, the jacquard lattice and the like originate from the United kingdom and are the traditional combed cotton fabric named by the Oxford university, the Oxford fabric starts about 1900 years, and the Oxford fabric is also widely used for manufacturing bags and cases. At present, the oxford used as a suitcase has poor moisture absorption effect and poor air permeability, cannot meet the daily use requirements of people, is inconvenient for people to use, and reduces the practicability of the polyester oxford.
SUMMERY OF THE UTILITY MODEL
The utility model aims at providing a case is with waterproof moisture permeable oxford can make this oxford have good waterproof moisture permeable's effect.
In order to solve the technical problem, the purpose of the utility model is to realize like this:
the utility model relates to a waterproof and moisture permeable oxford for bags and suitcases, which comprises a base cloth layer and a waterproof and moisture permeable film layer; the base cloth layer is made of oxford cloth formed by interweaving warps and wefts; the waterproof moisture-permeable film layer is a TPU/PAN double-component waterproof moisture-permeable film sprayed on the surface of the base cloth layer by adopting an electrostatic spinning method.
As a further explanation of the above scheme, the warp yarn used in the base fabric layer is an elastic core-spun yarn, which comprises a core layer and a cladding layer, wherein the core layer is an elastic filament.
As a further explanation of the scheme, the coating layer is terylene FDY 150D/36F; the weft yarn is terylene FDY 150D/36F.
As a further explanation of the scheme, the coating layer is 200D nylon air textured yarn, and the weft yarn is 160D nylon air textured yarn.
As a further illustration of the above solution, the elastic filament comprises a core-sheath inner layer and a sheath-sheath outer layer; the inner layer of the core sheath is made of polyurethane, and the outer layer of the sheath is made of PET.
As a further illustration of the above solution, the elastic filament comprises a core-sheath inner layer and a sheath-sheath outer layer; the inner layer of the core sheath is made of polyurethane, and the outer layer of the sheath is made of nylon 6 or nylon 66.
As a further illustration of the scheme, the thickness of the waterproof moisture-permeable film layer is 0.15-0.3 mm.
The utility model has the advantages that: the utility model relates to a case and bag are with waterproof moisture permeable oxford, including the base cloth layer that adopts elasticity covering yarn to prepare and adopt the waterproof moisture permeable membrane of electrostatic spinning method spraying on the base cloth layer, can make this surface fabric have good elasticity and waterproof moisture permeable effect. And TPU/PAN two-component waterproof moisture-permeable membrane, wherein TPU has good hydrophilicity and higher elasticity, PAN has good chemical corrosion resistance, and the fiber is thinner. So that the whole fabric has good protection function and moisture permeability function.
Drawings
Fig. 1 is a schematic structural view of a waterproof moisture permeable oxford fabric according to the present invention;
FIG. 2 is a schematic structural view of the elastic core spun yarn used;
FIG. 3 is a schematic representation of the structure of the elastic filament used;
fig. 4 is a schematic structural view of a waterproof moisture-permeable oxford fabric according to example three.
The designations in the figures illustrate the following: 1-a base fabric layer; 2-waterproof moisture permeable film layer; 11-a core layer; 12-a coating layer; 111-core sheath inner layer; 112-sheath outer layer.
Detailed Description
The present invention will be further described with reference to the accompanying drawings and specific embodiments.
In order to make the objects, features and advantages of the present invention more obvious and understandable, the drawings in the embodiments of the present invention are combined below to clearly and completely describe the technical solutions in the embodiments of the present invention, and obviously, the embodiments described below are only some embodiments of the present invention, but not all embodiments. Based on the embodiments in the present invention, all other embodiments obtained by a person skilled in the art without creative efforts belong to the protection scope of the present invention.
The technical solution of the present invention is further explained by the following embodiments with reference to the accompanying drawings.
In the description of the present invention, it is to be understood that the terms "upper", "lower", "top", "bottom", "inner", "outer", and the like indicate orientations or positional relationships based on those shown in the drawings, and are only for convenience of description and simplicity of description, and do not indicate or imply that the device or element referred to must have a particular orientation, be constructed and operated in a particular orientation, and therefore should not be construed as limiting the present invention.
Example one
The present embodiment will be described in detail with reference to fig. 1, 2 and 3. The waterproof and moisture permeable oxford for the luggage comprises a base fabric layer 1 and a waterproof and moisture permeable film layer 2. The base cloth layer 1 is an oxford fabric formed by interweaving warps and wefts, and the waterproof moisture-permeable film layer 2 is a TPU/PAN double-component waterproof moisture-permeable film sprayed on the surface of the base cloth layer 1 by adopting an electrostatic spinning method. The thickness of the waterproof moisture-permeable film layer 2 is 0.15-0.3 mm.
The oxford used as the case sometimes drenches rainwater, and the rainwater can have certain erosion effect on the fabric, namely, how to make the used oxford capable of preventing water, moisture and rainwater during use. The waterproof moisture-permeable fabric mainly comprises three types of high-density fabrics, coating fabrics and laminated fabrics. In which a high-density fabric is poor in moisture permeability but water resistance. The laminated fabric has a waterproof moisture-permeable functional film, so that the laminated fabric has a good waterproof moisture-permeable function. But the conventional waterproof moisture-permeable film does not prevent the erosion of rainwater. The TPU/PAN two-component waterproof moisture-permeable membrane used in the embodiment contains two materials of TPU and PAN. The TPU has good hydrophilicity, higher strength and elasticity. PAN has good chemical corrosion resistance, can resist the corrosion of chemical components in rainwater after being wetted by rainwater, and ensures that the used oxford fabric has good protective performance on the premise of having good waterproof and moisture permeable effects.
In this embodiment, the warp yarn used in the base fabric layer 1 is an elastic core-spun yarn, and includes a core layer 11 and a covering layer 12. The core layer 11 is an elastic filament. The coating layer 12 is terylene FDY150D/36F, and the weft is terylene FDY 150D/36F. The warp and weft density was 360X 210 pieces per 10 cm.
Further, in this embodiment, the elastic filament includes a core-sheath inner layer 111 and a sheath outer layer 112, the core-sheath inner layer 111 is polyurethane, and the sheath outer layer 112 is PET. The ratio of the radius of the core-sheath inner layer 111 to the thickness of the sheath outer layer 112 is 5: 1-1: 5, in particular 1: 2. in this embodiment, since the weft yarn and the covering layer 11 are made of dacron, the sheath outer layer 112 of the elastic filament is also made of dacron, so that defects do not occur during dyeing.
Since the base fabric layer 1 has elasticity and the TPU/PAN bicomponent waterproof moisture-permeable film also has certain elasticity, when the TPU/PAN bicomponent waterproof moisture-permeable film is sprayed on the surface of the base fabric layer 1, the base fabric layer 1 needs to be sprayed in a stretched state, and the stretched elongation is half of the maximum elongation.
Example two
The present embodiment will be described in detail with reference to fig. 1, 2 and 3. The waterproof and moisture permeable oxford for the luggage according to the present embodiment is different from the first embodiment in that the covering layer 12 is 200D nylon air textured yarn, and the weft is 160D nylon air textured yarn in the present embodiment. The elastic filament comprises a core-sheath inner layer 111 and a sheath outer layer 112; the core-sheath inner layer 111 is made of polyurethane, and the sheath outer layer 112 is made of nylon 6 or nylon 66. The sheath 12, the weft and the sheath 112 of the elastic filaments are made of nylon so that no defects occur during dyeing.
EXAMPLE III
This embodiment will be described in detail with reference to fig. 4. In the waterproof moisture-permeable oxford for the case and bag related to the embodiment, the other side of the base fabric layer 1 is bonded with an elastic fabric layer 4 through a water-based polyvinyl chloride bonding layer 3, and the elastic fabric layer 4 is formed by interweaving cotton-ammonia core-spun yarns and pure cotton yarns. The cotton-ammonia core-spun yarn is warp yarn. The water-based polyvinyl chloride bonding layer 3 is in an array of dots.
The foregoing has described in detail preferred embodiments of the present invention. It should be understood that numerous modifications and variations can be devised by those skilled in the art in light of the present teachings without departing from the inventive concepts. Therefore, the technical solutions that can be obtained by a person skilled in the art through logic analysis, reasoning or limited experiments based on the prior art according to the concepts of the present invention should be within the scope of protection defined by the claims.
Claims (7)
1. The waterproof and moisture permeable oxford fabric for the luggage is characterized by comprising a base fabric layer (1) and a waterproof and moisture permeable film layer (2); the base cloth layer (1) is oxford formed by interweaving warp yarns and weft yarns; the waterproof moisture-permeable film layer (2) is a TPU/PAN double-component waterproof moisture-permeable film sprayed on the surface of the base fabric layer (1) by adopting an electrostatic spinning method.
2. The waterproof moisture-permeable oxford fabric for the luggage according to claim 1, wherein warp yarns used for the base fabric layer (1) are elastic core-spun yarns, and comprise a core layer (11) and a coating layer (12), wherein the core layer (11) is an elastic filament.
3. The waterproof moisture-permeable oxford fabric for the luggage according to claim 2, wherein the coating layer (12) is polyester FDY 150D/36F; the weft yarn is terylene FDY 150D/36F.
4. The waterproof moisture-permeable oxford fabric for the luggage according to claim 2, wherein the coating layer (12) is 200D nylon air textured yarn, and the weft yarn is 160D nylon air textured yarn.
5. The waterproof moisture-permeable oxford for bags according to claim 3, wherein the elastic filament comprises a core-sheath inner layer (111) and a sheath outer layer (112); the core-sheath inner layer (111) is made of polyurethane, and the sheath outer layer (112) is made of PET.
6. The waterproof moisture-permeable oxford for bags according to claim 4, wherein the elastic filament comprises a core-sheath inner layer (111) and a sheath outer layer (112); the core-sheath inner layer (111) is made of polyurethane, and the sheath outer layer (112) is made of nylon 6 or nylon 66.
7. The waterproof moisture-permeable oxford for bags according to claim 1, wherein the thickness of the waterproof moisture-permeable film layer (2) is 0.15-0.3 mm.