CN211497863U - Crucible assembly for preparing single crystal by PVT method and crystal growth furnace - Google Patents

Abstract

The application discloses a crucible assembly and a crystal growth furnace for preparing single crystals by a PVT method, and belongs to the field of semiconductor material preparation. The crucible assembly for preparing the single crystal by the PVT method comprises a crucible and a seed crystal column arranged in the crucible; the side wall of the crucible comprises an interlayer, the interlayer comprises an inner side wall and an outer side wall, the inner side wall has higher porosity than the outer side wall, and the interlayer forms a raw material cavity; the seed crystal column and the extension direction of the central axis of the crucible are approximately same, and a long crystal cavity is formed between the seed crystal column and the inner surface of the inner side wall. The crucible assembly and the crystal growth furnace can efficiently and quickly prepare the silicon carbide single crystal with extremely low defect density and the substrate thereof, thereby laying a technical foundation for large-scale commercialization of the silicon carbide substrate with high quality and low cost.

Description

Crucible assembly for preparing single crystal by PVT method and crystal growth furnace

Technical Field

The application relates to a crucible assembly and a crystal growth furnace for preparing single crystals by a PVT method, belonging to the field of semiconductor material preparation.

Background

The existing silicon carbide preparation technology is mainly based on a physical vapor transport (PVT for short). The PVT method is formed by sublimating and decomposing a silicon carbide raw material placed at the bottom and transmitting the silicon carbide raw material to a seed crystal along an axial temperature gradient for crystallization. The sheet seed crystal used by the PVT method in the prior art is arranged at the top of the crucible, and the silicon carbide single crystal grows vertically and downwards along a certain radial direction of the single crystal.

Since the growth of the silicon carbide single crystal is limited by the distance from the growth surface of the single crystal and the surface of the raw material when growing downward, the crystal growth thickness is usually in the range of 20 to 50mm, and the yield of the substrate made of the silicon carbide single crystal is low. In addition, defects such as micropipes and dislocations in the silicon carbide seed crystal penetrate the silicon carbide single crystal and the seed crystal prepared therefrom in the <0001> direction in many cases. These defects will continue to be inherited into the newly grown single crystal and continue to form through defects during the growth of the single crystal, so that the control of the defect density in the single crystal and the substrate is difficult, the cost is high, and the improvement of the substrate quality is difficult.

Nature reports a silicon carbide single crystal preparation method for avoiding inheritance of defects such as micropipes and dislocation through cross section growth of a crystal, but the method has the disadvantages of complicated preparation process, high cost and inapplicability to industrial production process, and can reduce the defect density.

SUMMERY OF THE UTILITY MODEL

In order to solve the problems, the application provides a crucible assembly and a crystal growth furnace for preparing single crystals by a PVT method. The crucible assembly and the crystal growth furnace can efficiently and quickly prepare the silicon carbide single crystal with extremely low defect density and the substrate thereof, thereby laying a technical foundation for large-scale commercialization of the silicon carbide substrate with high quality and low cost.

According to an aspect of the present application, there is provided a crucible assembly for PVT method for manufacturing single crystal, which is capable of manufacturing single crystal having a large thickness when manufacturing single crystal by PVT method, so that a yield of a substrate manufactured from single crystal is high; when the method is used for preparing the silicon carbide single crystal, the efficiency is high, the defect density of the prepared silicon carbide single crystal is low, and the technical foundation is laid for large-scale commercialization of the silicon carbide single crystal substrate.

The crucible assembly for preparing the single crystal by the PVT method comprises a crucible and a seed crystal column arranged in the crucible; the side wall of the crucible comprises an interlayer, the interlayer comprises an inner side wall and an outer side wall, the inner side wall has higher porosity than the outer side wall, and the interlayer forms a raw material cavity; the seed crystal column and the extension direction of the central axis of the crucible are approximately same, and a long crystal cavity is formed between the seed crystal column and the inner surface of the inner side wall.

Optionally, the seed crystal column is obtained by cutting and polishing a single crystal column, and the surface of the seed crystal column is a smooth crystalline surface.

Optionally, the interlayer is arranged corresponding to the height of the seed crystal column, and the seed crystal column and the crucible share a central axis.

Optionally, the distance D1 between the inner side wall and the outer side wall is 50-300mm, and the distance D2 between the inner surface of the inner side wall and the surface opposite to the seed crystal column is 100-300 mm.

Optionally, the interlayer extends upward from the bottom of the crucible, and the seed column extends upward from the bottom of the crucible. Preferably, the interlayer extends from the bottom of the crucible to the top of the crucible, and the seed column extends from the bottom of the crucible to the top of the crucible.

Optionally, the bottom and/or the top of the crucible are distributed with slots for installing the seed crystal columns. Preferably, the clamping groove is in an equilateral hexagon corresponding to the seed crystal column.

Optionally, the seed crystal is a hexagonal seed crystal, and the single crystal is a hexagonal single crystal.

Alternatively, the seed column is configured as a hexagonal prism comprising six equivalent crystal planes.

Alternatively, the equivalent crystal plane has a width of 5 to 20 mm. Preferably, the width of the equivalent crystal plane is 7 to 15 mm.

Preferably, if the crystal face indexes of the long crystal faces are the same, the prepared single crystal is in the same shape as the crystal form of the seed crystal column.

Preferably, the six equivalent crystal planes of the seed column are <1120> <11-20> < -1120> <1-120> <1-1-20> respectively; or the six equivalent crystal planes of the seed column are <10-10> <01-10> < 1100> < 1010> <0-110> <1-100> respectively.

Optionally, the seed crystal column is a silicon carbide seed crystal column, and the single crystal is a silicon carbide single crystal. Preferably, the silicon carbide single crystal is an α silicon carbide single crystal, and has a hexagonal crystal structure.

Optionally, the crucible is a graphite crucible. Preferably, the crucible lateral wall is porous graphite plate, the porosity of inside wall is 40% -60%, the aperture of inside wall is not higher than 1 um. The porosity of lateral wall is not more than 10%, the aperture of lateral wall is not higher than 1 um.

Optionally, the seed crystal column is integrally arranged or spliced along the axial direction of the seed crystal column. The seed crystal columns can be directly stacked or bonded. Due to the limitation of seed crystal preparation, a plurality of seed crystal columns can be spliced axially to lengthen the length of the seed crystal columns, so that the thickness of the prepared silicon carbide single crystal is improved. The prepared single crystal is cut into a flaky single crystal substrate along the radial direction, so that the defects of the single crystal grown at the splicing part can be cut off; in order to improve the single crystal utilization rate, the cut defective single crystal may be used as a raw material for preparing the single crystal.

Optionally, the axial length of the seed crystal column is not less than 100mm, and the axial length of the single crystal is not less than 100 mm. Preferably, the axial length of the seed crystal column is not less than 120mm, and the axial length of the single crystal is not less than 120 mm. More preferably, the axial length of the seed column is not less than 150mm, and the axial length of the single crystal is not less than 150 mm.

According to one aspect of the application, a crystal growth furnace comprising any one of the crucible assemblies is provided, and the crystal growth furnace is heated in a mode that the side wall of the crucible generates heat, so that raw materials in the interlayer are heated to be sublimated to the seed crystal column for crystal growth, the thickness of the prepared single crystal is large, and the number of substrates prepared from the single crystal is large; when the method is used for preparing the silicon carbide single crystal, the efficiency is high, the defect density of the prepared silicon carbide single crystal is low, and the technical foundation is laid for large-scale commercialization of the silicon carbide single crystal substrate.

This contain long brilliant stove of any above-mentioned crucible subassembly, still include heating coil and insulation construction, insulation construction is established to the crucible overcoat, heating coil centers on insulation construction's lateral wall sets up. The induction coil is a medium-frequency induction coil.

Optionally, the crystal growth furnace comprises a furnace body, the furnace body is a quartz furnace, the crucible assembly is arranged outside the heat insulation structure and then placed in the furnace body, and the outer side wall of the furnace body is surrounded by the induction coil.

Benefits that can be produced by the present application include, but are not limited to:

1. the crucible assembly for preparing the single crystal by the PVT method has the advantages that the prepared single crystal can be in any size, particularly, the thickness is large and can be larger than 100mm, so that the number of substrates prepared from the single crystal is large, and a technical foundation is laid for large-scale commercialization of single crystal substrates.

2. The crucible assembly for preparing single crystal by PVT method provided by the application is high in efficiency when used for preparing silicon carbide single crystal, and the defect density of the prepared silicon carbide single crystal is small.

3. The heating mode of the crystal growth furnace for preparing the single crystal by the PVT method is that the side wall of the crucible generates heat, so that raw materials in the interlayer are sublimated to the seed crystal column to grow crystals, the prepared single crystal can be any size, particularly has large thickness, and the thickness can be larger than 100mm, so that the wafer yield of the substrate prepared from the single crystal is high, and a technical foundation is laid for large-scale commercialization of the silicon carbide single crystal substrate.

4. When the crystal growth furnace for preparing the single crystal by the PVT method is used for preparing the silicon carbide single crystal, the efficiency is high, the defect density of the prepared silicon carbide single crystal is low, zero micropipe is prepared, and the screw dislocation is lower than 100cm^-2And edge dislocation density of less than 220cm^-2The defect density of the high-quality silicon carbide single crystal can be close to zero.

Drawings

The accompanying drawings, which are included to provide a further understanding of the application and are incorporated in and constitute a part of this application, illustrate embodiment(s) of the application and together with the description serve to explain the application and not to limit the application. In the drawings:

fig. 1 is a schematic view of a crucible assembly according to an embodiment of the present application.

Detailed Description

In order to more clearly explain the overall concept of the present application, the following detailed description is given by way of example in conjunction with the accompanying drawings.

So that the manner in which the above recited objects, features and advantages of the present application can be understood in detail, a more particular description of the invention, briefly summarized above, may be had by reference to the embodiments thereof which are illustrated in the appended drawings. It should be noted that the embodiments and features of the embodiments of the present application may be combined with each other without conflict.

In the following description, numerous specific details are set forth in order to provide a thorough understanding of the present application, however, the present application may be practiced in other ways than those described herein, and therefore the scope of the present application is not limited by the specific embodiments disclosed below.

In addition, in the description of the present application, it is to be understood that the terms "center", "upper", "lower", "front", "rear", "left", "right", "vertical", "horizontal", "top", "bottom", "inner", "outer", "axial", "radial", "circumferential", and the like, indicate orientations and positional relationships based on those shown in the drawings, are only for convenience of description and simplicity of description, and do not indicate or imply that the referenced devices or elements must have a particular orientation, be constructed and operated in a particular orientation, and thus, are not to be construed as limiting the present application.

Furthermore, the terms "first", "second" and "first" are used for descriptive purposes only and are not to be construed as indicating or implying relative importance or implicitly indicating the number of technical features indicated. Thus, a feature defined as "first" or "second" may explicitly or implicitly include one or more of that feature. In the description of the present application, "a plurality" means two or more unless specifically limited otherwise.

In this application, unless expressly stated or limited otherwise, the terms "mounted," "connected," "secured," and the like are to be construed broadly and can include, for example, fixed connections, removable connections, or integral parts; the connection can be mechanical connection, electrical connection or communication; either directly or indirectly through intervening media, either internally or in any other relationship. The specific meaning of the above terms in the present application can be understood by those of ordinary skill in the art as appropriate.

In this application, unless expressly stated or limited otherwise, the first feature "on" or "under" the second feature may be directly contacting the first and second features or indirectly contacting the first and second features through intervening media. In the description herein, reference to the description of the term "one embodiment," "some embodiments," "an example," "a specific example," or "some examples," etc., means that a particular feature, structure, material, or characteristic described in connection with the embodiment or example is included in at least one embodiment or example of the application. In this specification, the schematic representations of the terms used above are not necessarily intended to refer to the same embodiment or example. Furthermore, the particular features, structures, materials, or characteristics described may be combined in any suitable manner in any one or more embodiments or examples.

The crucible assembly of the present application is used in the production of a single crystal by Physical Vapor Transport (PVT) method, and the kind of single crystal is not limited to a silicon carbide single crystal, and the crucible assembly can be used as long as a single crystal that can be produced by physical vapor transport can be used. The non-silicon carbide single crystal is not used in the crucible assembly with the silicon carbide single crystal in that the seed crystal column 6 has a shape of a crystal form of the non-silicon carbide single crystal, and if the non-silicon carbide single crystal is a cubic system, the seed crystal column 6 has a cubic shape.

The structures and the methods of use of the crucible assembly and the growth furnace will be described below by taking a silicon carbide single crystal as an example.

Referring to fig. 1, an embodiment of the present application discloses a crucible assembly for preparing a single crystal by a PVT process, which includes a crucible and a seed crystal column 6 disposed in the crucible; the side wall of the crucible comprises an interlayer, the interlayer comprises an inner side wall 8 and an outer side wall 2, the inner side wall 8 has higher porosity than the outer side wall 2, and the interlayer forms a raw material cavity 4; the axial direction of the seed crystal column 6 extends along the side wall of the crucible, and a long crystal cavity is formed between the seed crystal column 6 and the inner surface of the inner side wall 8. The crucible assembly can produce a single crystal having a large thickness when the single crystal is produced by the PVT method, so that the number of substrates produced from the single crystal is large; the method has high efficiency when used for preparing the silicon carbide single crystal, and the prepared silicon carbide single crystal has low defect density, thereby laying a technical foundation for large-scale commercialization of the silicon carbide single crystal substrate.

Alternatively, part or all of the height area of the sidewall is provided as an interlayer, and when part of the height area of the sidewall is provided as an interlayer, the interlayer may be provided at any height position of the sidewall.

In order to improve the crystal growth efficiency and make the shape of the single crystal uniform, the interlayer is arranged at a height corresponding to that of the seed crystal column 6, and the seed crystal column 6 has a crucible common axis, so that the side walls of the seed crystal column 6 are simultaneously subjected to crystal growth.

In an embodiment not shown, the interlayer extends upwards from the bottom of the crucible, i.e. the inner and outer side walls 8, 2 extend upwards from the bottom of the crucible and are connected to the remainder of the crucible side walls. Preferably, referring to fig. 1, the interlayer extends from the bottom of the crucible to the top of the crucible, and the seed crystal column 6 extends from the bottom of the crucible to the top of the crucible, the seed crystal column 6 being disposed corresponding to the interlayer. The interlayer arrangement mode can efficiently prepare large-volume single crystals, and the fixing mode of the seed crystal column 6 is simple.

As an embodiment, the sandwich layer including the inner side wall 8 and the outer side wall 2 forms a raw material chamber 4, and the raw material chamber 4 is used for containing raw materials such as silicon carbide powder used in the preparation of silicon carbide single crystal. Preferably, the distance D1 between inside wall 8 and the lateral wall 2 is 50-100mm, and D1's setting mode makes the crucible lateral wall generate heat when, can guarantee that the heat from lateral wall 2 to the high-efficient transmission of seed crystal post 6 direction, guarantees simultaneously that raw materials sublimation temperature and the long brilliant face's of seed crystal post 6 temperature is in the long brilliant temperature range of needs, low-power consumption, low cost.

As an implementation mode, a long crystal cavity is formed between the seed crystal column 6 and the inner surface of the inner side wall 8, and the distance D2 between the inner surface of the inner side wall 8 and the surface opposite to the seed crystal column 6 is 100-200 mm. The arrangement mode of the D2 can ensure the crystal growth quality, the crystal growth volume and the crystal growth efficiency of crystal growth. Preferably, the crucible is of a roughly cylindrical structure, the interlayer is of a cylindrical ring structure, and the combination of D1 and D2 can efficiently prepare large-volume high-quality single crystals.

In order to fix the seed crystal column 6 in the crucible, clamping grooves are distributed at the positions where the seed crystal column 6 needs to be fixed, such as the bottom and/or the top of the crucible, so that the seed crystal column 6 is inserted into the clamping grooves to be fixedly installed, and the shape of the clamping grooves is matched with the shape of the cross section of the seed crystal column 6. In one embodiment, when the seed column 6 has a hexagonal prism shape, the chucking groove is provided in an equilateral hexagon corresponding to the seed column 6. The clamping groove can be arranged in an upward protruding or concave structure relative to the inner side of the bottom wall of the crucible.

The seed crystal can be in any crystal form, the species and the crystal form of the seed crystal and the single crystal are the same, and the shape of the seed crystal column 6 can be in any columnar structure, such as a square prism, a cylinder or a hexagonal prism. Preferably, the seed crystal is a hexagonal system seed crystal, and the single crystal is a hexagonal system single crystal; more preferably, the seed column 6 is provided as a hexagonal prism including six equivalent crystal planes which are symmetrical, and the shape of the seed column 6 is set so that the single crystal produced grows uniformly to the periphery. Alternatively, the width of the equivalent crystal plane is 5 to 20 mm. Preferably, the width of the equivalent crystal plane is 7 to 15 mm. The width of the equivalent crystal face is set so that the crystal can grow equivalently at a constant speed in the transverse direction in a uniform thermal field taking the crucible axis as the symmetry center, and therefore the same axial position of the crystal is kept, namely the consistency and uniformity of the in-chip quality of the subsequently processed substrate are kept. The equivalent crystal face is used as a seed crystal growth face for growth, so that the inheritance of threading defects such as dislocation, micropipes and the like during the traditional growth along <000-1> can be avoided, and the dislocation density is effectively reduced; meanwhile, the thickness of the crystal during transverse growth is determined by the height of the seed crystal column, so that the preparation efficiency of the crystal is greatly improved.

In order to make the silicon carbide single crystal grow uniformly around the seed crystal column 6, when the seed crystal column 6 is prepared, the crystal face indexes of six equivalent planes of the seed crystal column 6 are respectively

<1120> <11-20> <1120> <1-120> <1-1-20 >; or the six equivalent crystal planes of the seed crystal column 6 are <10-10> <01-10> < 1100> < 1010> <0-110> <1-100 respectively, but the crystal is not limited to the six equivalent crystal planes, and other hexagonal symmetric crystal planes can be used as long as the crystal growth conditions are met.

In one embodiment, the seed crystal column 6 is a silicon carbide seed crystal column, and the single crystal is a silicon carbide single crystal. Preferably, the silicon carbide single crystal is an α silicon carbide single crystal, which has a hexagonal crystal structure. A hexagonal crystal column is used as a seed crystal column 6 for crystal growth, and the surfaces of the seed crystal column 6 are six equivalent crystal planes <1120> <11-20> <1120> <1-120> <1-1-20> respectively. The silicon carbide single crystal block is polished to prepare a smooth crystal surface suitable for the gas phase growth of the silicon carbide single crystal, and the six crystal faces are used for replacing the flaky wafer seed crystal in the conventional PVT method. The seed crystal column 6 can be processed by a silicon carbide crystal bar, the side length of the seed crystal column 6 is 5-20mm, and the length is determined by the initial silicon carbide crystal bar.

As an implementation mode, the crucible is a graphite crucible, the inner side wall 8 is a porous graphite plate, the porosity of the inner side wall 8 is 40% -60%, the pore diameter of the inner side wall 8 is not higher than 1um, the porosity of the outer side wall 2 is not more than 10%, and the pore diameter of the outer side wall 2 is not higher than 1 um. The inner side wall 8 has a porosity greater than that of the outer side wall 2, so that the inner side wall 8 serves as a gas phase transmission passage after decomposition and sublimation of the raw material.

In one embodiment, the seed column 6 is formed by cutting and polishing a single crystal column, for example, the seed column 6 is formed by processing a silicon carbide crystal bar, the width of the side edge of the seed column 6 is 5-20mm, and the length is determined by the original silicon carbide crystal bar.

In order to arrange the seed crystal column 6 with any length, the seed crystal column 6 is arranged to be integrated or spliced along the axial direction of the seed crystal column 6. The splicing mode comprises the following steps: the seed crystal columns 6 can be directly stacked or the seed crystal columns 6 can be bonded.

In order to obtain a high-length silicon carbide seed crystal column, a plurality of seed crystal columns 6 can be spliced in the axial direction to increase the length of the seed crystal column 6, thereby increasing the thickness of the obtained silicon carbide single crystal. For example, a plurality of identical silicon carbide seed columns 6 can be spliced together up and down, the spliced seed columns 6 are respectively connected and fixed with the hexagonal graphite hole clamping grooves in the center of the graphite cover body in the crucible through two ends of the uppermost and lowermost seed columns, and the height of the connected seed columns is the thickness of the silicon carbide crystal which can grow.

When the substrate is prepared by the single crystal, the substrate can be cut into a sheet-shaped single crystal substrate along the radial direction of the single crystal, and then the defect single crystal grown at the splicing part can be cut off; in order to improve the single crystal utilization rate, the cut defective single crystal may be used as a raw material for preparing the single crystal.

The length of the seed crystal column 6 in the crucible assembly determines the length of the prepared single crystal, and the seed crystal column 6 can be spliced in multiple sections, so that the thickness obtained by one-time growth is not less than 100mm, 120mm and 150mm, the axial length of the single crystal is not less than 100mm, 120mm and 150mm, and the length of the prepared single crystal is far greater than the length of the single crystal prepared by the traditional disc seed crystal fixed on the top of the crucible, namely 20-50 mm. The length of the single crystal produced by the crucible assembly is large, so that the number of substrates produced from the single crystal is large.

As an implementation mode, the crystal growth furnace comprises any one of the crucible assemblies, and further comprises a heating coil, a furnace body and a heat preservation structure; after the crucible assembly is sleeved with the heat insulation structure, the crucible assembly is placed in the furnace body, and the outer side wall 2 of the furnace body is surrounded by the induction coil. Preferably, the furnace body is a quartz furnace, and the induction coil is a medium-frequency induction coil. The crystal growth furnace heats the side wall of the crucible through a heating coil, and then heats sublimation gas A after sublimation of the raw material in the raw material cavity 4 to flow to each surface of the seed crystal column 6 to carry out crystal growth after passing through the inner side wall 8; preferably, the long crystal planes have the same plane index. The thickness of the single crystal prepared by the crystal growth furnace is large, and the number of substrates prepared by the single crystal is large. When the crystal growth furnace is used for preparing the silicon carbide single crystal, the preparation efficiency is high, the defect density of the prepared silicon carbide single crystal is low, and a technical foundation is laid for large-scale commercialization of a silicon carbide single crystal substrate.

When the silicon carbide single crystal is prepared, the outer side wall 2 of the graphite is inductively heated through the intermediate frequency coil, heat is transmitted to the silicon carbide powder raw material in the interlayer, and the heat further flows to the inner side wall 8 of the porous graphite and the seed crystal column 6. Because the outer side wall 2 of the crucible generates heat, a certain temperature gradient exists along the radial direction of the crucible, the growth rate of the silicon carbide single crystal is determined by the inner side wall 8, the seed crystal column 6 and the outer growth surface of the grown single crystal, and the initial radial temperature gradient, namely the temperature difference between the inner side wall 8 of the crucible and the surface of the seed crystal column 6, is controlled between 50 ℃ and 300 ℃. Due to the existence of the radial temperature gradient, the powder in the raw material cavity 4 is transmitted to the crystal face of the seed crystal column 6 along the radial temperature gradient for recrystallization after decomposition and sublimation, and the surface of the single crystal expands towards the inner side wall 8 along the radial temperature gradient, so that the silicon carbide single crystal with the required size is grown.

The growth temperature of the silicon carbide single crystal is controlled at 2000-23000 ℃, the pressure is controlled at 5-50mbar, and inert gas such as argon or helium is introduced into the growth chamber to be used as protective gas; if a conductive N-type silicon carbide single crystal is produced, nitrogen gas may be introduced into the inert gas in an amount determined according to the actual resistivity to be required as a doping gas.

Due to the defects of micropipes, threading dislocations and the like in the silicon carbide single crystal or the silicon carbide seed crystal column 6 [0001 ]]The direction, therefore, the transverse growth can avoid the inheritance of defects such as micropipes, dislocation and the like, thereby obtaining the silicon carbide crystal ingot with extremely low defect density; preferably, zero micropipes, screw dislocations and knife edge dislocation densities below 50cm can be achieved^-2The defect density of the silicon carbide single crystal and the substrate is even close to zero.

Example 1

As a method for producing a silicon carbide single crystal from any of the above crucibles and a seed crystal column, comprising the steps of:

1) providing a crucible and a silicon carbide seed crystal column;

2) silicon carbide powder is filled into a raw material cavity formed by an interlayer on the side wall of the crucible, a silicon carbide seed crystal column is arranged in the crucible, and the silicon carbide seed crystal column is put into a crystal growth furnace after being assembled;

3) raising the temperature of the crystal growth furnace to 2000-2300 ℃, so that the sublimed gas after the raw material is sublimated passes through the inner side wall of the interlayer and is transmitted to the surface of the seed crystal column along the radial gas phase, and the temperature difference T between the inner surface of the inner side wall and the surface of the seed crystal is 50-300 ℃ for crystal growth, namely preparing the silicon carbide single crystal;

wherein, the D1 position is 50-300mm, the D2 is 100-300mm, the seed crystal column is a hexagonal prism comprising six symmetrical equivalent planes, the width D3 of the equivalent crystal plane is 5-20mm, and the axial length of the seed crystal column is not less than 100 mm.

Example 2

The preparation method was explained by taking the length of the seed column as an example of 150mm, and 1# -7# of the silicon carbide single crystal and D1# -D5# of the comparative silicon carbide single crystal were prepared according to the method of example 1, except for the methods of examples shown in Table 1.

TABLE 1

The 6-inch micropipes of the prepared silicon carbide single crystal 1# -7#, the comparative silicon carbide single crystal D1# -D5# were zero, the threading dislocation (TSD) density, The Edge Dislocation (TED) density and the XRD-characterized crystal quality were examined, and the examination results are shown in Table 2.

TABLE 2

From the above, when the silicon carbide single crystal grown laterally has a large radial temperature gradient, i.e., a large lateral driving force, a large loading amount of D1, i.e., a large loading amount, a moderate transmission distance of D2, and a long equivalent crystal plane of the seed crystal, a high-quality silicon carbide single crystal with excellent crystal quality and low dislocation density is easily obtained. This is because sufficient material quantity, large lateral growth driving force and proper transmission distance help to maintain C/Si ratio balance at crystal growth interface, and the large size of equivalent crystal plane avoids dislocation induced when atom step flows of polycrystalline plane are combined, thereby improving quality of silicon carbide single crystal.

The embodiments in the present specification are described in a progressive manner, and the same and similar parts among the embodiments are referred to each other, and each embodiment focuses on the differences from the other embodiments. In particular, for the system embodiment, since it is substantially similar to the method embodiment, the description is simple, and for the relevant points, reference may be made to the partial description of the method embodiment.

The above description is only an example of the present application and is not intended to limit the present application. Various modifications and changes may occur to those skilled in the art. Any modification, equivalent replacement, improvement, etc. made within the spirit and principle of the present application should be included in the scope of the claims of the present application.

Claims (10)

1. A crucible assembly for preparing a single crystal by a PVT method is characterized by comprising a crucible and a seed crystal column arranged in the crucible;

the side wall of the crucible comprises an interlayer, the interlayer comprises an inner side wall and an outer side wall, the inner side wall has higher porosity than the outer side wall, and the interlayer forms a raw material cavity;

the seed crystal column and the extension direction of the central axis of the crucible are approximately same, and a long crystal cavity is formed between the seed crystal column and the inner surface of the inner side wall.

2. The crucible assembly of claim 1, wherein the interlayer is disposed at a height corresponding to a height of the seed column, the seed column being concentric with the crucible.

3. The crucible assembly of claim 2, wherein the distance D1 between the inner and outer side walls is 50-300 mm;

the distance D2 between the inner surface of the inner side wall and the surface opposite to the seed crystal column is 100-300 mm.

4. The crucible assembly of claim 1, wherein the seed column is a hexagonal seed crystal and the single crystal is a hexagonal single crystal.

5. The crucible assembly of claim 4, wherein the seed column is configured as a hexagonal prism comprising six equivalent crystal planes.

6. The crucible assembly of claim 5, wherein the width of the equivalent lattice plane is 5-20 mm.

7. The crucible assembly of claim 5, wherein the crucible is a graphite crucible, the seed column is a silicon carbide seed column, and the single crystal is a silicon carbide single crystal.

8. The crucible assembly of claim 1, wherein the seed column is integrally formed or spliced along an axial direction of the seed column.

9. The crucible assembly of claim 1, wherein the axial length of the seed column is not less than 100mm and the axial length of the single crystal is not less than 100 mm.

10. The crystal growth furnace comprising the crucible assembly as claimed in any one of claims 1 to 9, further comprising a heating coil and a heat-insulating structure, wherein the crucible is externally provided with the heat-insulating structure, and the heating coil is arranged around the side wall of the heat-insulating structure.