A kind of crease-resistant wear-resisting fabric
Technical field
The utility model belongs to fabric field more particularly to a kind of crease-resistant wear-resisting fabric.
Background technique
Fabric is the material for making clothes, and fabric is many kinds of, has dress mostly for making the fabric of clothes
Comfortably, the features such as sweat-absorbing breathable.With people to health and movement attention degree it is higher and higher, daily wear of clothes also by
Gradually aggravate;More especially have deep love for the consumer of body-building, outdoor sports, their requirements for the wearability of clothing fabric are more next
It is higher.But current wear-resisting fabric includes base fabric made of warp thread and weft yarns, the fabric poor air permeability of this structure,
It is easy to damage without elasticity.The especially fabric of trousers, not only wearability is undesirable, is easier to the case where wearing, and causes resistance to
It is undesirable with property, but also be easy to appear fold, influence using.Therefore, that there is wearabilities is undesirable, durable for existing fabric
Property it is undesirable and the problem of be easier to fold.
Utility model content
The technical issues of solution:, be easy to appear fold the shortcomings that undesirable for existing wear-resisting fabric abrasion resistant effect, this
Utility model provides a kind of crease-resistant wear-resisting fabric, using double rib air layer structure, using spandex composite yarn as fabric, with
Polyamide fibre composite yarn solves existing fabric there is wearabilities that undesirable, durability is undesirable and is easier to as outer shell fabric
The problem of fold.
Technical solution: a kind of crease-resistant wear-resisting fabric, including fabric body, the fabric body is by variation latitude plain and tuck
Organize compound double rib composite double layer institutional framework;The fabric of the fabric body is woven by spandex composite yarn,
Outer shell fabric is woven by polyamide fibre composite yarn, and fabric and outer shell fabric are connected by tuck stitch.
The thickness of fabric and outer shell fabric described above is 0.734mm.
Fabric body described above is a circulation with 10 tunnels, and the 1st road and the 2nd tunnel are called in person by dials and the high of syringe respectively
Needle knitting is respectively formed the variation latitude plain loop of 1 row in fabric body reverse side and front, the 3rd road and the 4th tunnel respectively by
The low heel needle knitting of dials and syringe is respectively formed other 1 variation latitude plain loop in the fabric body reverse side and front
Row carries out tuck by the low heel needle of dials and syringe on the 5th tunnel, by the 1st road to the 4th tunnel on dials and syringe respectively into
The row that row single side is knitted to form connects;6th road to the 9th tunnel repeats the braiding on the 1st road to the 4th tunnel, forms another
Row carries out tuck knitting by the high heel needle of dials and syringe, the row that the 6th road to the 9th tunnel is woven joins finally on the 10th tunnel
System gets up to form full wafer fabric body.
Spandex composite yarn described above is vortex spun core-spun yarn, is looping by yarn core, bamboo pulp fiber of polyurethane elastic filament
Fiber is made.
Polyamide fibre composite yarn described above is covering yarn, is made using PTT long filament by heart yarn, with polyamide fibre of fasciated yarn.
Tuck stitch described above is made of polyester elastic yarn.
Polyester elastic yarn described above is 11.11tex/48f terylene.
The outer surface of fabric body described above is coated with nano-aluminium oxide wear-resistant coating.
The utility model has the advantages that a kind of crease-resistant wear-resisting fabric provided by the utility model, has the advantages that the utility model
Using double rib air layer structure, there is good warmth retention property, gas permeability, the excellent feature of wrinkle resistance, with spandex composite yarn
Weaving fabric has the characteristics that elasticity is good, wrinkle resistance is good using spandex as heart yarn, uses bamboo pulp fiber for looping fibre
Dimension can improve the sense of touch of spandex, make fabric have the effect of soft comfortable, moisture absorption breathe freely, antibacterial bacteriostatic;And with polyamide fibre
Composite yarn woven outer layer fabric enables fabric body to have good wear-resisting, elastic recovery and anti-crease property.Therefore, this reality
Have the advantages that comfortable, elasticity is good, warmth retention property is good, moisture transported permeable is good, crease-resistant wearability is good with novel fabric.
Detailed description of the invention
Fig. 1 is the structural schematic diagram of the fabric body of the utility model.
In figure: 1, fabric;2, outer shell fabric;3, tuck stitch.
Specific embodiment
The following will be combined with the drawings in the embodiments of the present invention, carries out the technical scheme in the embodiment of the utility model
Clearly and completely describe, it is clear that the described embodiments are only a part of the embodiments of the utility model, rather than whole
Embodiment.Based on the embodiments of the present invention, those of ordinary skill in the art are without creative efforts
Every other embodiment obtained, fall within the protection scope of the utility model.
Embodiment 1
The present embodiment provides a kind of crease-resistant wear-resisting fabric, including fabric body, the fabric body by variation latitude plain with
The compound double rib composite double layer institutional framework of tuck stitch;The fabric 1 of the fabric body is woven by spandex composite yarn
It forms, outer shell fabric 2 is woven by polyamide fibre composite yarn, and fabric 1 and outer shell fabric 2 are connected by tuck stitch 3.Internal layer
The thickness of fabric 1 and outer shell fabric 2 is 0.734mm.
The fabric body is a circulation with 10 tunnels, and the 1st road and the 2nd tunnel are compiled by the high heel needle of dials and syringe respectively
It knits, is respectively formed the variation latitude plain loop of 1 row in fabric body reverse side and front, the 3rd road and the 4th tunnel are respectively by dials
The low heel needle knitting with syringe is respectively formed other 1 variation latitude plain loop row in the fabric body reverse side and front,
On the 5th tunnel, tuck is carried out by the low heel needle of dials and syringe, the 1st road is subjected to single side to the 4th tunnel respectively on dials and syringe
The row being knitted to form connects;6th road to the 9th tunnel repeats the braiding on the 1st road to the 4th tunnel, forms another row, most
Afterwards on the 10th tunnel, tuck knitting is carried out by the high heel needle of dials and syringe, the 6th road is connected to the row that the 9th tunnel weaves
Form full wafer fabric body.
Further, the spandex composite yarn is vortex spun core-spun yarn, is packet by yarn core, bamboo pulp fiber of polyurethane elastic filament
Fiber is twined to be made;The polyamide fibre composite yarn is covering yarn, is made using PTT long filament by heart yarn, with polyamide fibre of fasciated yarn;The tuck
Tissue 3 is made of polyester elastic yarn.
Further, the polyester elastic yarn is 11.11tex/48f terylene.
Embodiment 2
On the basis of embodiment 1, the outer surface of the fabric body is coated with nano-aluminium oxide wear-resistant coating.
The fabric of embodiment 1, embodiment 2 is detected below.
One, creasy recovery angle is tested
Referring to GB/T 3819-1997 " the test returns horn cupping of textile fabric wrinkle recovery property " in secondary standard atmosphere
Pressure carries out the test of wrinkle recovery angle of woven fabrics using viscoelasticity theory using I type Full automatic digital formula fabric crease elasticity test instrument of YG (B) 541D-.To reality
Testing result such as the following table 1 for applying example 1, to testing result such as the following table 2 of embodiment 2.
Table 1
Table 2
Two, wearability test
Referring to " the measurement part 2 of Martindale's method fabric abrasion resistance: the survey of sample breakage of GB/T 21196.2-2007
It is fixed " and GB/T 21196.4-2007 " the 4th part of measurement of Martindale's method fabric abrasion resistance: the evaluation of cosmetic variation " In
Under standard three-level atmospheric pressure, using YG401 type plain grinding instrument, wherein pressurize weight 250g, and 240/cm2Sand paper, revolution 300.It adopts
With the quality and thickness difference after mill before weighing mill with TG328A assay balance, quality and thickness loss rate are calculated.To embodiment 1
Testing result such as the following table 3, to testing result such as the following table 4 of embodiment 2.
Table 3
Table 4
By upper table 1, table 2 data it is found that the fabric have good wrinkle resistance.
By upper table 3, table 4 data it is found that the fabric have good wear-resisting property.
The foregoing description of the disclosed embodiments can be realized professional and technical personnel in the field or using originally practical new
Type.Various modifications to these embodiments will be readily apparent to those skilled in the art, and determine herein
The General Principle of justice can be realized in other embodiments without departing from the spirit or scope of the present utility model.Cause
This, the present invention will not be limited to the embodiments shown herein, and is to fit to and principles disclosed herein
The widest scope consistent with features of novelty.